Abstract
We present a spectroscopic ellipsometry study of Mo-doped VO2 thin films deposited on silicon substrates for the mid-infrared range. The dielectric functions and conductivity were extracted from analytical fittings of Ψ and Δ ellipsometric angles showing a strong dependence on the dopant concentration and the temperature. Insulator-to-metal transition (IMT) temperature is found to decrease linearly with increasing doping level. A correction to the classical Drude model (termed Drude-Smith) has been shown to provide excellent fits to the experimental measurements of dielectric constants of doped/undoped films and the extracted parameters offer an adequate explanation for the IMT based on the carriers backscattering across the percolation transition. The smoother IMT observed in the hysteresis loops as the doping concentration is increased, is explained by charge density accumulation, which we quantify through the integral of optical conductivity. In addition, we describe the physics behind a localized Fano resonance that has not yet been demonstrated and explained in the literature for doped/undoped VO2 films.
Similar content being viewed by others
Introduction
Vanadium dioxide (VO2) undergoes a first-order insulator-to-metal transition (IMT) at a critical temperature (\({T}_{c}\)) around 68 °C1,2, which is accompanied by a structural transformation of a low-temperature monoclinic (M, insulator) to high-temperature tetragonal rutile (R, metal) phase. This transition is fully reversible and is a result of an interplay between Mott and Peierls mechanisms3,4, whereas the relative contributions are still a subject of debate5. The monoclinic to rutile or intermediate monoclinic phase transitions coincide with large changes in the optical6, electrical7, thermal8, and magnetic properties9, making VO2 one of the most intensively studied phase change materials due to its unique temperature-dependent physicochemical properties and, at the same time, opens exciting new opportunities for the development of novel functional materials with a wide range of technological and industrial applications such as radiative thermal memristors10, ultrafast tunable nanoplasmonics11,12, uncooled bolometers13, energy-efficient smart windows14,15,16,17, heat storage devices18, temperature sensors19, ultrafast tunable opto-electronic nano-gating20, room temperature hydrogen nanosensors21, infrared optical limiters22, memory and neuromorphic devices4, and tunable terahertz metamaterials23, among others.
Some of the above applications critically rely on the performance of the VO2 IMT close to ambient conditions. To enhance the application of VO2 in thermally-triggered optical and electrical switching devices, for instance, the shifting and effective control of its phase transition temperature to around room temperature is highly desirable. Faced with this challenge, it is important to highlight that the critical temperature at which VO2 phase transition occurs, is substantially affected by the degree of impurities embedded in the bulk of the material as dopants which, for a few percent concentration can induce an appreciable change of \({T}_{c}\). For example, a conventional approach to regulate the VO2 IMT is controlling the carrier concentration in the material, that is, by selectively choosing the type and level of dopant element, an electron- or hole-injection can be built up into the bulk material. Thus, doping the VO2 lattice with high-valence metal transition ions such as W6+, Mo6+, or Nb5+ effectively decreases the \({T}_{c}\), whereas low-valence metal ions such as Cr3+, Al3+, Fe3+, or Ga3+ are found to severely increase it24,25,26,27,28,29.
Moreover, the fabrication of VO2 crystalline thin films has been carried out by different techniques such as pulsed laser deposition30,31,32, sputtering16,33, molecular beam epitaxy34, dip-coating35, chemical vapor deposition36, spin coating19, etc. In particular, the fabrication of VO2 thin films by spin coating deposition of a sol-gel precursor is one of the easiest and low cost techniques to produce reasonably high quality films, with an additional advantage of not requiring sophisticated equipment. The latter opens the possibility to scale up the fabrication process of VO2 coatings enabling, thus, the practical application in industrial fields by developing an efficient and straightforward synthesis method19. Moreover, it has been demonstrated that only minor discrepancies appear in the optical properties of samples fabricated by spin coating deposition as compared to the samples prepared with the sputtering technique37.
On the other hand, the strongly correlated conducting state of VO2 has been associated to nanoscale metallic puddles that percolate at the IMT38. Near-field microscopy observations along with infrared spectroscopic ellipsometry (IRSE), show that the coalescence of metallic puddles are directly related to the significant increment of the optical conductivity, and the divergence of the real part of the dielectric function in the low frequency limit, when the percolation is taking place39. In parallel to these findings, Walther et al.40, interpret the terahertz conductivity of ultrathin metallic gold films at the percolation transition in terms of the carrier backscattering Drude-Smith model41. The extracted parameters of the Drude-Smith model, namely, the plasmon frequency \({\omega }_{p}\), collision-modified lifetime, \(\tau \), and persistence of original velocity after collisions \(c\), provide a reasonable explanation for the percolative behavior of gold thin films at the IMT, as compared to the unflexible Drude model40,41. Consequently, the Drude-Smith model can be applied to describe temperature-dependent optical ellipsometry measurements in order to elucidate the electronic correlations around the percolation threshold of Mo-doped VO2 thin films.
As an optical technique, spectroscopic ellipsometry has proved to be a non-invasive and non-destructive powerful probe for monitoring the optical properties of VO2 thin films through IMT, e.g. Kana et al., studied the thermally tunable optical constants of VO2 thin films in the visible to near infrared (NIR) range42. Lafort et al., determined the refractive indices of sputtered films of VO2 deposited on stainless steel substrates33. Huang et al., carried out an analysis of the phase transition of VO2 thin films by combining Raman scattering and ellipsometry for visible and NIR range43. More recently, Wan et al., reported the influence of substrate and fabrication method on the complex refractive index of VO2, along with Looyenga mixing rule fittings at the IMT, in oder to describe the coexistence of insulating and metallic domains as an effective medium37. Furthermore, the Bruggeman effective medium theory, successfully used to obtain the response of inclusions in media, has been reported to fail in the regime near the percolation transition (for the mid-IR range44) and also has been inconsistent with optical measurements in the far IR range40. While effective medium theories are useful to describe the dielectric function of mixtures, they do not explain some fundamental phenomena that occur in the microstructure of VO2.
Although some studies of IRSE have been carried out in vanadium oxide33,37,42,43,44,45,46, to the best of our knowledge, the influence of dopants on the optical properties of VO2 through the IMT has not yet been analyzed by Drude-Smith model. In this article, we study the temperature-dependent mid-infrared optical properties of Mo-doped VO2 thin films across the IMT using the spectroscopic ellipsometry technique. From our measurements, we are able to determine the complex dielectric functions and optical conductivities of Mo-doped samples throughout the thermally induced transition. We show that the parameters, as extracted from the Drude-Smith model and the changes of the phase of a Fano resonance, provide a consistent description of the most pronounced infrared optical effects carried out at the percolation transition of Mo-doped and undoped VO2 layers.
Materials and Methods
Synthesis of Mo-doped VO2 thin films
All the reagents were of analytical grade and used as obtained commercially without further purification. Vanadium pentoxide (V2O5) was selected as the starting material, oxalic acid (H2C2O4 · 2H2O) as the reducing agent and ethanol as the solvent. Ammonium molybdate tetrahydrate ((NH4)6Mo7O24 · 4H2O) was used as the dopant supplier substance to decrease \({T}_{c}\). Substrates were prepared from (001)-oriented, boron doped p-type silicon wafer (1–5 mΩ · cm). Piranha solution was used for cleaning and pre-treating the silicon surface.
VO2 thin films were prepared using a chemical-based fabrication method19,47. Briefly, vanadium pentoxide V2O5 and H2C2O4 · 2H2O were mixed in ethanol in a molar ratio of 1:3, respectively. A transparent blue vanadyl oxalate (VOC2O4 · xH2O) precursor solution was obtained after refluxing at 120 °C for 10 h, followed by the filtration of the precursor (to remove any unreacted chemicals) and storage under an inert atmosphere to avoid further oxidation. Substrates were immersed for 24 h into a solution of H2SO4:H2O2 in a volumetric ratio of 3:1, in order to remove residual organic contamination and improve the hydrophilicity of the silicon surface (hazards of working with piranha solution can be found in ref. 48). Mo-doped VO2 thin films were synthesized by the addition of (NH4)6Mo7O24 · 4H2O (initially dissolved in few drops of deionized water) to achieve the dopant levels (1% and 2% with respect to vanadium) and then, slowly added to the VOC2O4 · xH2O precursor under vigorous stirring followed by ultra-sonication during 2.5 h to obtain a homogeneous precursor solution. Along with the control sample (0% dopant), Mo-doped VO2 thin films were deposited by spin coating the precursor solution at 3000 rpm for 30 s over the pre-treated silicon substrate in a nitrogen atmosphere. After drying at 100 °C to remove the excess solvent, the prepared samples were thermally annealed in a tube furnace at 450 °C for 60 min at a heating rate of 10 °C/min in nitrogen atmosphere to form a crystalline VO2 thin film. The morphological properties and thickness of the films were observed through field emission scanning electron microscopy (SEM, Hitachi SU5000).
Optical characterization
A commercial variable-angle infrared spectroscopic ellipsometer IR-VASE from J.A. Woollam Co. Inc, equipped with a Peltier-based homemade temperature control system, was used to characterize the optical properties of VO2 thin films as a function of temperature. The ellipsometer consists of an infrared source (BOMEM MB102), a positionable polarizer, a high precision \(\theta -2\theta \) sample stage, a rotating compensator, and an analyzer, with computerized controls. This configuration is known as PSCRA49. A paraboloidal mirror (with a 50 cm focal length) focuses the beam to an 8 mm spot diameter on the surface of the sample. Spectral intensity is acquired with a DTGS detector. The signal is then automatically reduced to the ellipsometric angles Ψ and Δ, defined below, as functions of frequency from 300 to 6000 cm−1 (1.5–33 μm). For the experiment, we set an angle of incidence of 67° with a nominal spectral resolution of 16 cm−1. These experimental settings were considered sufficient to permit synchronization along with the temperature control with reasonable scanning and thermal stabilization times. Furthermore, the temperature control was implemented to work in setting-only mode, i.e., without feedback cycles, such as e.g., PID, which would have induced undesired hysteresis sub-loops within the main loop, that would have distorted the final results. On the other hand, due to the heavily doped substrates used in the present study, the absorption contribution of free-charge carriers impedes the IR radiation to reach the backside of the samples; thus no backside surface treatment was required for our samples as it is needed for intrinsic silicon to avoid spurious reflections37.
Ellipsometry measures the changes in the polarization state of linearly polarized incident light upon reflection off the sample surface. This change is expressed as the ratio of the complex Fresnel reflection coefficients \({r}_{p}\) and \({r}_{s}\) for light polarized parallel and perpendicular to the plane of incidence, that is to say49,50
where tan(Ψ) is the ratio of the magnitudes of \({r}_{p}\) and \({r}_{s}\) and Δ is the relative phase difference between those coefficients. The measured ellipsometric spectra, expressed in terms of Ψ and Δ values as a function of the frequency, are then fitted with the aid of commercial software to obtain the temperature-dependent optical parameters.
Results and Discussion
Figure 1 shows the ellipsometric Ψ (Fig. 1(a)) and Δ (Fig. 1(b)) spectra corresponding to Mo-doped VO2 films for three doping percentages from 0 to 2%. The spectra are displayed for initial (blue circles/triangles/diamonds) and saturation temperatures (red circles/triangles/diamonds), along with fittings of experimental data performed through a sum of oscillators (black solid lines), as discussed in the latter part of this paper. The fits were obtained by employing the CompleteEASE ellipsometry software from J.A. Woollam, considering a multilayered system composed of the VO2 layer, a native silicon oxide layer, and a semi-infinite p-type \(\mathrm{(001)}\) silicon substrate (schematically shown in the inset of Fig. 1(b)). A good agreement between experimental spectra and modeled line shapes can be observed. Additionally, temperature-dependent experimental runs and spectra calculations for the bare SiO2/Si substrate were performed separately in order to leave the dielectric functions and thicknesses corresponding to VO2 films as unique goals of the fitting procedure. The thicknesses of VO2 films and native silicon oxide layer, determined from spectroscopic ellipsometry measurements (dIRSE and dOx, respectively) and scanning electron microscopy (dSEM), are shown in Table 1. The difference in the thicknesses determined by ellipsometry from those obtained by SEM, can be attributed to the following factors: (i) the area of the light spot of the ellipsometer of ~1 cm2, being much larger than the SEM observation zone (<400 nm) leads, thus, to an average measurement with different thicknesses over the sample; (ii) the modeled dielectric function can be the result of a non-uniform mixing of different dielectric functions of different regions of the film, whereby an effective dielectric function of the film can produce a different optical thickness, resulting in a mismatch of optical and SEM widths; and (iii) the surface roughness of the film is not considered in this study.
Figure 2 shows selected experimental spectra of the pseudo-refractive index \(\langle n\rangle \) (also termed pseudo-transform) of Mo-doped VO2 thin films for the different doping percentages. The plots show the evolution of \(\langle n\rangle \) from initial lower temperature, (chosen to be close the IMT), gradually increasing and changing its spectral line shape up to finally reaching an unchanging state at a particular saturation temperature (solid lines). To complete the measurement cycle by decreasing temperature, the \(\langle n\rangle \) spectra gradually decrease to reach again the initial state (dashed lines). The symbol \(\langle n\rangle \) corresponds to the effective refractive index obtained from inversion of Ψ and Δ angles, using an expression that provides reliable dielectric functions only for bulk-like samples (see Eq. 1 in the Supplementary Information). In the case of stacked media, \(\langle n\rangle \) has contributions from the complete layered structure schematically shown in the inset of Fig. 1(b), i.e., it is a convolution of optical properties and thicknesses of individual layers that must be revealed through a model. The justification for showing these pseudo transforms is rooted in a couple of practical reasons. First, among the available representations of ellipsometric data, \(\langle n\rangle \) spectra provided the best way to monitor changes during experimental thermal runs, due to their qualities of being always positive and growing nearly monotonically for the present system throughout the complete working spectral range, and second, the line shape of this representation is found to have a nice resemblance (except for the broad dip at ~1500 cm−1 produced by the substrate), to the optical conductivity extracted from the model (the results of optical conductivity and a further justification for using \(\langle n\rangle \) are presented below). For the sake of clarity, we only show the real part of the pseudo-refractive index, whereas the imaginary part \(\langle k\rangle \) and pseudo-dielectric transforms are shown in the Supplementary Information (Figs. S1 and S2). As the temperature is increased, the \(\langle n\rangle \) spectrum rise with a marked hump (observed between 2000 and 2400 cm−1, depending on dopant concentration) suggesting collision-rich percolative conductivity, which can be modelled by the Drude-Smith characteristic line shape41. Furthermore, the dip at around 1000 cm−1 which appears to be more pronounced as the conductivity is increased, implies the presence of an asymmetric Fano-like resonance51. The variation of the refractive index of Si substrate, as a function of the temperature, is negligible as compared to the change of VO2 layer (see Fig. S3 of Supplementary Information), therefore, the huge variation of \(\langle n\rangle \) has been mainly attributed to the contribution of thermochromic changes in VO2, which are also affected by the doping level. For VO2 films, a series of phonon resonances are present in the region below 1000 cm−1 52, however, in this work phonon effects (although important for the determination of the crystallographic phase), are not considered in the extraction of the dielectric function, since we are interested in the very broad conductivity spectral contribution. Moreover, none of the reported vibrational modes coincides with our so-assigned Fano-like resonance. In fact, with the sharpening of the Fano structure, the phonon resonances tend to smear out.
Figure 3 shows the hysteresis loops for different doping levels, constructed from the pseudo-refractive index functions, by extracting data of traces corresponding to the frequency where the maximum value of \(\langle n\rangle \) is located at saturation temperature (vertical dashed lines in Fig. 2). The experimental data, i.e., each individual symbol in Fig. 3, corresponds to an average taken over eleven neighboring spectral points around the trace frequency. The selection of \(\langle n\rangle \)max as a representative of experimental spectra as a function of the temperature over other visualizations of ellipsometric data demands a justification besides its resemblance to optical conductivity: it is also more sensitive to temperature-driven changes even from the onset of the IMT as compared to hystereses of e.g., \(\langle {\varepsilon }_{1}\rangle \), which show a delayed response to temperature, at least for the present system. We elaborate on this result in the context of Figs. S4 and S5 of Supplementary Information. The continuous black lines correspond to fitted line shapes, performed separately for increasing and decreasing temperatures, via Gompertz53 (characterized by its asymmetric “S”-shape, used here for the ascending temperature of 0% and 1%, and descending temperature of 0% of Mo-doping) and logistic54 (of symmetric “S”-shape, used for both, ascending and descending temperatures for the rest of the data) growth laws, which are non-linear models to predict e.g., population growth in confined spaces, or with some other restrictions are widely used in the fields of marketing, insurance, health and biology (for instance for populations of plants55 and and bacteria56). On comparing different samples, apart from the shift in the hysteresis loops to lower temperatures with increasing doping level, the slopes at the inflection temperature are found to decrease, i.e., a higher amount of Mo-dopant leads to a more gradual IMT (data from the quantitative analysis are presented in the Supplementary Information). Transition temperatures exhibit a linear diminution with increasing Mo concentration. Concerning the morphology, it is observed (see right panels in Fig. 3) that both, the doped and undoped VO2 films present uniform coverage of the substrate and a homogeneous, granular texture whose average grain size seems to depend on the percentage of dopant19. As the growth conditions for all the samples were kept the same, the observed differences in the morphology of the films have been attributed to the variation in the dopant concentration. Although, the present results are in conformity with some reported observations46,57,58, nevertheless we do not discard some slight contributions due to variations associated to thermal gradients (along the furnace during the annealing process) and/or to different thicknesses observed in the layers that in turn could lead to the formation of different crystallization morphologies induced by strain relaxation37.
Figure 4 shows the extracted dielectric function and conductivity spectra of Mo-doped VO2 thin films, for different temperatures across the IMT. We note that by dielectric function we are referring to the relative, adimensional one throughout this article. The extraction of the dielectric function was carried out by fitting of experimental data via a sum of oscillators. In the case of VO2 layers, we did not consider the granular structure of the films, thus, the extracted dielectric functions correspond to effective media composed of air and VO2 grains. To ensure consistency of the modeled optical response across samples with different doping values, the dielectric function was fitted with the same set of oscillators only employing different values for the fitting parameters. For temperatures across the IMT, Fano and Drude-Smith oscillators were employed due to the inverted asymmetric line-shape resonance observed around 1000 cm−1 and the strong absorption of the layer in the metallic phase characterized by a broad peak with maximum, depending on Mo concentration, between 2000 and 3000 cm−1 (improperly fitted by the classical Drude theory), respectively41 (see Fano and Drude-Smith equations along with a selected deconvolved spectrum in Fig. S5 in Supplementary Information). The silicon substrate dielectric function used in the model for fitting all \(\langle n\rangle \) was independently adjusted from a reference sample subjected to a temperature cycle as done for the VO2 main samples. For its optical model, we employed temperature-dependent Drude oscillators to emulate the overall line shape and a small correction with a Fano resonance, characteristic of heavily p-type doped Si59, while the native oxide dielectric function was fitted with two (temperature independent) Gaussian oscillators.
Figure 4(a) displays modeled \(\tilde{\varepsilon }={\varepsilon }_{1}+i{\varepsilon }_{2}\) spectra for selected temperatures from 30 to 100 °C. For the undoped sample (top panel, 0%), the real part, \({\varepsilon }_{1}\) is observed to abruptly increase as a function of temperature for some fixed frequencies at the lower spectral end, followed by a subsequent decrease while crossing the \({T}_{c}\), in agreement with the first order transition divergence reported by Qazilbash et al.38, however, we were unable to reproduce the complete behavior due to the lack of data in the low frequency terahertz range. In contrast, for doped samples (middle and bottom panels, 1% and 2% of Mo-doping, respectively) we observe a more gradual transition close to zero frequency, but similar line shapes for the rest of the spectra, with a clear metallic behavior characterized by negative values of \({\varepsilon }_{1}\) for a broad range of frequencies with (nearly) monotonic trend. The imaginary part (\({\varepsilon }_{2}\)) reveals a gradual increment with increasing temperature for whole spectral range (insets). The real part of the conductivity, in S.I. units, related to the imaginary part of dielectric function via
is shown in Fig. 4(b). For all the samples, an increase in temperature reveals a huge increment of more than two orders of magnitude in the conductivity values, with respect to its value at low temperature. Moreover, the Fano structure (at 1000 cm−1) and a clearly Drude-Smith line shape (hump between 2000–3000 cm−1) become appreciable with the rise of temperature as metallic phase is reached. Drude-Smith model takes into account carrier localization through enhanced carrier backscattering41, and has been reported as an excellent model to describe photoconductivity in InP nanoparticles60, ZnO-based nanowires, nanoparticles/thin films61, and metal-insulator percolation transitions40. Although the Drude-Smith theory has been improved by Cocker et al.62, we observed excellent fits of our spectra employing the generalization of Smith theory41. Additionally, Drude-Smith conductivity displays a maximum value for non-zero frequency, which can not be obtained from Drude model41.
Based on reports that the phase of Fano resonance can be modulated for controlled fraction of vacancies between dielectric particles63,64, in the present case the origin of the Fano resonance has been attributed to the voids between VO2 particles. Here, we can consider that the conducting state contributes to the continuum state and the charges at walls polarizing the voids contribute to the discrete coupling state required by Fano theory63,64. In spite of the fact that voids fraction and distances between grains remain constant, the electronic interaction of the walls changes with temperature, resulting in a temperature-dependent Fano response. The right panels of Fig. 4(b), show the shifting \(q\) phase of the resonance from negative to near to zero values as the temperature is increased, suggesting an approximation to percolation. In analogy with the report from Pariente et al.63, we consider the granular VO2 structure as quasi-disordered photonic crystals percolating through interactions of polarization charges on its walls, and so interconnecting the different dielectrics. For the partially conducting VO2 particles the Fano phase \(q\approx 0\) is reached when approaching saturation independently of Mo concentration, which suggests that voids and continuum, although both excited by light are finally decoupled64. The variation of parameter q as a function of the temperature is shown in Supplementary Information (Fig. S7). This observation is supported by the temperature, morphology and dopant-dependent varying positions of the Fano resonance, whose q-phases reach all the same close-to-zero value at saturation and whose line shapes show a pure Lorentz-like, but inverted, resonance independently of doping level and morphology. Furthermore, the larger size of grains and their better interconnection, and the larger sizes of voids for the 0% VO2 film (see Fig. 3), may explain the smaller size of its corresponding Fano resonance (reduced wall interactions), its flatter Drude-Smith contribution (more room to extend puddles, slight enhancement in probability of forming connections), and its broader range of negative \({\varepsilon }_{1}\) as compared with the doped (more granular) films. Supporting thus, our interpretation of the origin of the Fano peak in terms of film morphology.
The density of charge carriers, for a given temperature, can be quantified by means of the \(f\)-sum rule, which states that
where \(N(T)\) is the (history-dependent) free charge density at \(t\). Equation 3 is valid for both, the classical Drude and the Drude-Smith conductivity approaches (this is shown in the Supplementary Information), indicating that the same charge density is only differently distributed, concerning its response to frequency, forming thus the mid infrared peak41. Within the limited spectral range of the present work, we attempted to quantify the fraction of carriers resonating in the mid-infrared range. This can be justified by the presence of the broad bump of \({\sigma }_{1}\) as seen in Fig. 4(b). The integrals of \({\sigma }_{1}\) are presented as symbols in Fig. 4(c), where it can be observed that they also present a trend similar to that shown in Fig. 3. In fact, in Fig. 4(c) we reproduce (scaled) the hysteresis curves already shown in Fig. 3. The match indicates that the above employed growth laws describe quite well, and thus validate their employment to fit each branch of the hysteresis loops, the variations of charge density as a function of temperature: for the undoped film the very slow, nearly imperceptible growth of \(N\) at the beginning of the cycle may indicate that there are not enough electrons to screen excitons65. As the temperature increases the free charges start to accumulate in spatial puddles producing the very fast rise at the bottom of the hysteresis curve. The interconnection of puddles and the concomitant reduction of space to grow explain the subsequent increment of conductivity and its asymptotic approach to saturation. For the doped samples, the extra electron provided by the Mo atom very likely facilitates a more rapid formation of conducting puddles leading to an initially faster, logistic-like growth (see e.g. 2% Mo film at ~40 °C in Fig. 4(c)).
Figure 5 displays the parameters extracted from the adjustments through Drude-Smith model for doped/undoped samples. Figure 5(a) shows the persistence velocity parameter \(c\) changing from −1 before percolation transition to −0.65, −0.85, and −0.82 for 0%, 1% and 2%, respectively, in saturation temperature with intermediate values along the IMT range. The negative values of \(c\) indicate carrier backscattering, and a clearly non-Drude behavior41,62. As the temperature increases, the \(c\) value gets closer to zero, indicating a free carrier conduction similar to that of Drude, though never reached. As a comparison, Walther et al., reported the change of \(c\) parameter for an insulator to metal transition with a clear change from −1 to \(0\) in gold films40, however, a complete Drude-like behavior (\(c=0\)) is not observed in our results due to a grain morphology which induces lower values of optical conductivity of VO2 in the metallic phase (~103 S/cm) as compared with those of gold (~104–105 S/cm)40. Figure 5(b) shows the inverse of scattering time as a function of frequency. Extreme values of \({\tau }^{-1}\) are observed for all doped/undoped samples around the percolation transition. Such divergence indicates a discontinuity of a macroscopic property40. For undoped VO2, Peterseim et al., suggest that while the metallic islands percolate, charges are able to cross the phase borders in the metallic network, but correlations become strong enough to prevent metallic conduction driving the system towards a Mott insulator6. We speculate that this divergence can be interpreted as a signature of the first order transition in a Mott semiconductor. Figure 5(c) shows the plasmon frequency parameter changing from 200 to 2000 THz while crossing IMT temperature. The large increment of the plasmon frequency throughout the IMT indicates a more metallic behavior, which is in agreement with the current observations. According to Walther et al., plasmon frequency of percolating gold metallic islands can be scaled by \({\omega }_{p}\propto |d-{d}_{c}{|}^{t/2}\), where d accounts for the thickness of the layer with a critical value \({d}_{c}\), and \(t\) is the critical exponent for a two dimensional system with a value of 1.366,67; SEM observations of gold metallic islands show that the mean diameter proportionally increase with d40. On the other hand, Qazilbash et al., showed near field microscopy direct observations, where the VO2 metallic islands grow and coalesce as the temperature increases38. Therefore, the mean diameters of VO2 metallic islands should be proportional to the temperature, which we can associate, by analogy, to a power law for the plasmon frequency as \({\omega }_{p}\propto |T-{T}_{c}{|}^{t/2}\). Continuous lines in Fig. 5(c) show power fits after percolation threshold with critical exponents of \(t/2=0.60\), 0.54 and 0.64 for 0%, 1%, and 2% of Mo-doping, respectively, which are in agreement with reported value of 0.65 for a two dimensional percolative system and supports the electronic correlation assumption for doped and undoped VO2 films.
Conclusions
Mid-infrared spectroscopic ellipsometry measurements were carried out to determine the effective optical constants of Mo-doped VO2 thin films, across the IMT. The measured parameters Ψ and Δ angles are fitted by a sum of oscillators as a function of the frequency for different temperatures. For all the doped/undoped films, although unflexible Drude model fails to adjust the experimental data, Drude-Smith model is found to be in good agreement for the complete transition temperature range. While doped samples apparently show a smoother transition as compared to pristine control film, the set of extracted parameters show significant changes involved in the IMT and the discontinuity of a macroscopic property for all doped/undoped films, which are features of a percolation transition. Moreover, the asymmetry of a Fano resonance appearing with increasing temperature, supports the idea of a high electric field emerging in the frontier of the VO2 grains due to the percolation in all the proposed (doped/undoped) VO2 structures deposited over silicon substrates. The temperature and doping concentration dependent line shapes of thermo-optical hysteresis loops are quantitatively described in terms of growth laws, and are associated to accumulating charge density. As this percolation dependent Fano response is known to be very sensitive to environmental changes and can be tuned with the help of synthesis parameters/temperature, the proposed analysis open new avenues towards a simple and sensitive detection system.
References
Shao, Z., Cao, X., Luo, H. & Jin, P. Recent progress in the phase-transition mechanism and modulation of vanadium dioxide materials. NPG Asia Mater. 10, 581–605, https://doi.org/10.1038/s41427-018-0061-2 (2018).
Zhang, Z. et al. Thermochromic VO2 thin films: Solution-based processing, improved optical properties, and lowered phase transformation temperature. Langmuir 26, 10738–10744, https://doi.org/10.1021/la100515k (2010).
Weber, C. et al. Vanadium dioxide: A Peierls-Mott insulator stable against disorder. Phys. Rev. Lett. 108, 256402, https://doi.org/10.1103/PhysRevLett.108.256402 (2012).
Zhou, Y. & Ramanathan, S. Mott memory and neuromorphic devices. Proc. IEEE 103, 1289–1310, https://doi.org/10.1109/JPROC.2015.2431914 (2015).
Liu, K., Lee, S., Yang, S., Delaire, O. & Wu, J. Recent progresses on physics and applications of vanadium dioxide. Mater. Today 21, 875–896, https://doi.org/10.1016/j.mattod.2018.03.029 (2018).
Peterseim, T., Dressel, M., Dietrich, M. & Polity, A. Optical properties of VO2 films at the phase transition: Influence of substrate and electronic correlations. J. Appl. Phys. 120, 075102, https://doi.org/10.1063/1.4961406 (2016).
Del Valle, J. et al. Subthreshold firing in Mott nanodevices. Nature 569, 388–392, https://doi.org/10.1038/s41586-019-1159-6 (2019).
Hamaoui, G. et al. Thermophysical characterisation of VO2 thin films hysteresis and its application in thermal rectification. Sci. reports 9, 8728, https://doi.org/10.1038/s41598-019-45436-0 (2019).
Liu, L. et al. New-phase VO2 micro/nanostructures: investigation of phase transformation and magnetic property. New J. Chem. 36, 619–625, https://doi.org/10.1039/c1nj20798a (2012).
Ordonez-Miranda, J., Ezzahri, Y., Tiburcio-Moreno, J. A., Joulain, K. & Drevillon, J. Radiative thermal memristor. Phys. Rev. Lett. 123, 025901, https://doi.org/10.1103/PhysRevLett.123.025901 (2019).
Maaza, M., Nemraoui, O., Sella, C., Beye, A. C. & Baruch-Barak, B. Thermal induced tunability of surface plasmon resonance in Au–VO2 nano-photonics. Opt. Commun. 254, 188–195, https://doi.org/10.1016/j.optcom.2004.08.056 (2005).
Maaza, M., Nemraoui, O., Sella, C. & Beye, A. C. Surface plasmon resonance tunability in Au-VO2 thermochromic nano-composites. Gold Bull. 38, 100–106, https://doi.org/10.1007/BF03215243 (2005).
Chen, C., Yi, X., Zhao, X. & Xiong, B. Characterizations of VO2-based uncooled microbolometer linear array. Sensors Actuators A: Phys 90, 212–214, https://doi.org/10.1016/S0924-4247(01)00495-2 (2001).
Madida, I. G. et al. Submicronic VO2–PVP composites coatings for smart windows applications and solar heat management. Sol. Energy 107, 758–769, https://doi.org/10.1016/j.solener.2014.06.025 (2014).
Zhang, D. et al. High performance VO2 thin films growth by dc magnetron sputtering at low temperature for smart energy efficient window application. J. Alloy. Compd. 659, 198–202, https://doi.org/10.1016/j.jallcom.2015.11.047 (2016).
Sun, G. et al. Multi-nanolayered VO2/sapphire thin film via spinodal decomposition. Sci. reports 8, 5342, https://doi.org/10.1038/s41598-018-23412-4 (2018).
Zhou, Q. et al. Boron doped M-phase VO2 nanoparticles with low metal-insulator phase transition temperature for smart windows. Ceram. Int., https://doi.org/10.1016/j.ceramint.2019.10.211 (2019).
Muramoto, K. et al. VO2-dispersed glass: A new class of phase change material. Sci. reports 8, 2275, https://doi.org/10.1038/s41598-018-20519-6 (2018).
Antunez, E. E. et al. Porous silicon-VO2 based hybrids as possible optical temperature sensor: Wavelength-dependent optical switching from visible to near-infrared range. J. Appl. Phys. 118, 134503, https://doi.org/10.1063/1.4932023 (2015).
Maaza, M. et al. Phase transition in a single VO2 nano-crystal: potential femtosecond tunable opto-electronic nano-gating. J. Nanoparticle Res. 16, 2397, https://doi.org/10.1007/s11051-014-2397-z (2014).
Simo, A. et al. VO2 nanostructures based chemiresistors for low power energy consumption hydrogen sensing. Int. J. Hydrog. Energy 39, 8147–8157, https://doi.org/10.1016/j.ijhydene.2014.03.037 (2014).
Maaza, M. et al. Optical limiting in pulsed laser deposited VO2 nanostructures. Opt. Commun. 285, 1190–1193, https://doi.org/10.1016/j.optcom.2011.09.057 (2012).
Wang, S., Kang, L. & Werner, D. H. Hybrid resonators and highly tunable terahertz metamaterials enabled by vanadium dioxide (VO2). Sci. Reports 7, 4326, https://doi.org/10.1038/s41598-017-04692-8 (2017).
Asayesh-Ardakani, H. et al. Atomic origins of monoclinic-tetragonal (rutile) phase transition in doped VO2 nanowires. Nano Lett. 15, 7179–7188, https://doi.org/10.1021/acs.nanolett.5b03219 (2015).
Chae, B. G., Kim, H. T. & Yun, S. J. Characteristics of W- and Ti-doped VO2 thin films prepared by sol-gel method. Electrochem. Solid-State Lett. 11, D53–D55, https://doi.org/10.1149/1.2903208 (2008).
Batista, C., Ribeiro, R. M. & Teixeira, V. Synthesis and characterization of VO2-based thermochromic thin films for energy-efficient windows. Nano Express 6, 301, https://doi.org/10.1186/1556-276X-6-301 (2011).
Tan, X. et al. Unraveling metal-insulator transition mechanism of VO2 triggered by tungsten doping. Sci. Reports 2, 466, https://doi.org/10.1038/srep00466 (2012).
Zhao, L., Miao, L., Liu, C., Li, C. & Cheng, H. Facile solution-grown Mo-doped vanadium dioxide thermochromic films with decreased phase transition temperature and narrowed hysteresis loop width. Mater. Sci. Forum 787, 23–30, https://doi.org/10.4028/www.scientific.net/MSF.787.23 (2014).
Gomez-Heredia, C. L. et al. Measurement of the hysteretic thermal properties of W-doped and undoped nanocrystalline powders of VO2. Sci. Reports 9, 14687, https://doi.org/10.1038/s41598-019-51162-4 (2019).
Narayan, J. & Bhosle, M. V. Phase transition and critical issues in structure-property correlations of vanadium oxide. J. Appl. Phys. 100, 103524, https://doi.org/10.1063/1.2384798 (2006).
Genchi, S. et al. Growth of vanadium dioxide thin films on hexagonal boron nitride flakes as transferrable substrates. Sci. reports 9, 2857, https://doi.org/10.1038/s41598-019-39091-8 (2019).
Moatti, A., Sachan, R., Cooper, V. R. & Narayan, J. Electrical transition in isostructural VO2 thin-film heterostructures. Sci. reports 9, 3009, https://doi.org/10.1038/s41598-019-39529-z (2019).
Lafort, A. et al. Optical properties of thermochromic VO2 thin films on stainless steel: Experimental and theoretical studies. Thin Solid Films 519, 3283–3287, https://doi.org/10.1016/j.tsf.2010.12.122 (2011).
Fan, L. L. et al. Growth and phase transition characteristics of pure m-phase VO2 epitaxial film prepared by oxide molecular beam epitaxy. Appl. Phys. Lett. 103, 131914, https://doi.org/10.1063/1.4823511 (2013).
Dou, S. et al. Facile preparation of double-sided VO2 (m) films with micro-structure and enhanced thermochromic performances. Sol. Energy Mater. Sol. Cells 160, 164–173, https://doi.org/10.1016/j.solmat.2016.10.025 (2017).
Wang, S. et al. Recent progress in VO2 smart coatings: Strategies to improve the thermochromic properties. Prog. Mater. Sci. 81, 1–54, https://doi.org/10.1016/j.pmatsci.2016.03.001 (2016).
Wan, C. et al. On the optical properties of thin-film vanadium dioxide from the visible to the far infrared. Annalen der Physik 531, 1900188, https://doi.org/10.1002/andp.201900188 (2019).
Qazilbash, M. M. et al. Mott transition in VO2 revealed by infrared spectroscopy and nano-imaging. Science 318, 1750–1753, https://doi.org/10.1126/science.1150124 (2007).
Qazilbash, M. M. et al. Infrared spectroscopy and nano-imaging of the insulator-to-metal transition in vanadium dioxide. Phys. Rev. B 79, 075107, https://doi.org/10.1103/PhysRevB.79.075107 (2009).
Walther, M. et al. Terahertz conductivity of thin gold films at the metal-insulator percolation transition. Phys. Rev. B 76, 125408, https://doi.org/10.1103/PhysRevB.76.125408 (2007).
Smith, N. V. Classical generalization of the Drude formula for the optical conductivity. Phys. Rev. B 64, 155106, https://doi.org/10.1103/PhysRevB.64.155106 (2001).
Kana Kana, J. B., Ndjaka, J. M., Vignaud, G., Gibaud, A. & Maaza, M. Thermally tunable optical constants of vanadium dioxide thin films measured by spectroscopic ellipsometry. Opt. Commun. 284, 807–812, https://doi.org/10.1016/j.optcom.2010.10.009 (2011).
Huang, Y. et al. Phase transition analysis of thermochromic VO2 thin films by temperature-dependent Raman scattering and ellipsometry. Appl. Surf. Sci. 456, 545–551, https://doi.org/10.1016/j.apsusc.2018.06.125 (2018).
Ramirez-Rincon, J. A. et al. Thermal hysteresis measurement of the VO2 dielectric function for its metal-insulator transition by visible-ir ellipsometry. J. Appl. Phys. 124, 195102, https://doi.org/10.1063/1.5049747 (2018).
Voloshenko, I. et al. Microscopic nature of the asymmetric hysteresis in the insulator-metal transition of VO2 revealed by spectroscopic ellipsometry. Appl. Phys. Lett. 113, 201906, https://doi.org/10.1063/1.5055296 (2018).
Nagashima, M. & Wada, H. Near infrared optical properties of laser ablated VO2 thin films by ellipsometry. Thin Solid films 312, 61–65, https://doi.org/10.1016/S0040-6090(97)00360-X (1998).
Zhao, L. et al. Solution-processed VO2-SiO2 composite films with simultaneously enhanced luminous transmittance, solar modulation ability and anti-oxidation property. Sci. Reports 4, 7000, https://doi.org/10.1038/srep07000 (2014).
Internet archive, W. M. Piranha, https://web.archive.org/web/20100718162251/http://www.seas.upenn.edu/~nanofab/chemicals/Piranha.html (2010).
Fujiwara, H. Spectroscopic Ellipsometry: Principles and Applications (John Wiley & Sons, Ltd, 2007).
Tiwald, T. E., Thompson, D. W., Woollam, J. A., Paulson, W. & Hance, R. Application of ir variable angle spectroscopic ellipsometry to the determination of free carrier concentration depth profiles. Thin Solid Films 313–314, 661–666, https://doi.org/10.1016/S0040-6090(97)00973-5 (1998).
Gallinet, B. & Martin, O. J. F. Ab initio theory of fano resonances in plasmonic nanostructures and metamaterials. Phys. Rev. B 83, 235427, https://doi.org/10.1103/PhysRevB.83.235427 (2011).
Barker, A. S. Jr., Verleur, H. W. & Guggenheim, H. J. Infrared optical properties of vanadium dioxide above and below the transition temperature. Phys. Rev. Lett. 17, 1286–1289, https://doi.org/10.1103/PhysRevLett.17.1286 (1966).
Gompertz, B. On the nature of the function expressive of the law of human mortality, and on a new mode of determining the value of life contingencies. Philos. Trans. R. Soc. 115, 513–585, https://doi.org/10.1098/rstl.1825.0026 (1825).
Bacaër, N. A Short History of Mathematical Population Dynamics. (Springer, London, 2011).
Archontoulis, S. V. & Miguez, F. E. NonlinearRegression Models and Applications in Agricultural Research. Agron. J. 107, 786–798, https://doi.org/10.2134/agronj2012.0506 (2015).
Zwietering, M. H., Jongenburger, I., Rombouts, F. M. & Van’t Riet, K. Modeling of the Bacterial Growth Curve. Appl. Environ. Microbiol. 56, 1875–1881 (1990).
Wu, Y. F. et al. Spectroscopic analysis of phase constitution of high quality VO2 thin film prepared by facile sol-gel method. AIP Adv. 3, 042132, https://doi.org/10.1063/1.4802981 (2013).
Panagopoulou, M. et al. Thermochromic performance of mg-doped VO2 thin films on functional substrates for glazing applications. Sol. Energy Mater. Sol. Cells 157, 1004–1010, https://doi.org/10.1016/j.solmat.2016.08.021 (2016).
Humlicek, J. Ellipsometric study of Fano resonance in heavily doped p-type Si and SiGe alloys. Thin Solid Films 313–314, 656–660, https://doi.org/10.1016/S0040-6090(97)00972-3 (1998).
Beard, M. C. et al. Electronic coupling in InP nanoparticle arrays. Nano Lett. 3, 1695–1699, https://doi.org/10.1021/nl0346777 (2003).
Baxter, J. B. & Schmuttenmaer, C. A. Conductivity of ZnO Nanowires, Nanoparticles, and Thin Films Using Time-Resolved Terahertz Spectroscopy. J. Phys. Chem. B 110, 25229–25239, https://doi.org/10.1021/jp064399a (2006).
Cocker, T. L. et al. Microscopic origin of the Drude-Smith model. Phys. Rev. B 96, 205439, https://doi.org/10.1103/PhysRevB.96.205439 (2017).
Pariente, J. A. et al. Percolation in photonic crystals revealed by fano resoance, http://arXiv.org/abs/1607.08890 (2016).
Limonov, M. F., Rybin, M. V., Poddubny, A. N. & Kivshar, Y. S. Fano resonances in photonics. Nat. Photonics 11, 543–554, https://doi.org/10.1038/NPHOTON.2017.142 (2017).
Mott, N. F. Metal-insulator transitions. Contemp. Phys. 14, 401–413, https://doi.org/10.1080/00107517308210764 (1973).
Clerc, J. P., Giraud, G., Laugier, J. M. & Luck, J. M. The electrical conductivity of binary disordered systems, percolation clusters, fractals and related models. Adv. Phys. 39, 191–309, https://doi.org/10.1080/00018739000101501 (1990).
Yagil, Y., Yosefin, M., Bergman, D. J., Deutscher, G. & Gadenne, P. Scaling theory for the optical properties of semicontinuous metal films. Phys. Rev. B 43, 11342–11352, https://doi.org/10.1103/PhysRevB.43.11342 (1991).
Acknowledgements
We are grateful for the technical support provided by J.E. Madrigal-Sustaita, F. Ramírez-Jacobo and E. Ontiveros-Hernández during the course of this research. J.M.-M., V.A. and D.A.-F. acknowledge the partial financial support from grants CB-2015-01-259278, A-1S-30393, and CB-256243-2015, respectively, and IRSE equipment through grant 206298, all provided by Consejo Nacional de Ciencia y Tecnología.
Author information
Authors and Affiliations
Contributions
S.A.-A., J.O.-G. and A.S.-Z. carried out the ellipsometric measurements, J.O.-G. and A.S.-Z. designed the thermal part of the experiment. S.A.-A., V.A. and E.A. contributed in the synthesis of the samples and the discussion of the results, S.A.-A., R.C.-G., J.S.P.-H., J.M.-M., J.M.F.-C. and D.A.-F. analysed the results and developed the manuscript. D.A.-F. and J.M.F.-C. conducted and supervised the whole project. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Amador-Alvarado, S., Flores-Camacho, J.M., Solís-Zamudio, A. et al. Temperature-dependent infrared ellipsometry of Mo-doped VO2 thin films across the insulator to metal transition. Sci Rep 10, 8555 (2020). https://doi.org/10.1038/s41598-020-65279-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-65279-4
This article is cited by
-
Reconfigurable image processing metasurfaces with phase-change materials
Nature Communications (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.