Abstract
Two-photon polymerization (TPP) is capable of fabricating 3D structures with dimensions from sub-µm to a few hundred µm. As a direct laser writing (DLW) process, fabrication time of 3D TPP structures scale with the third order, limiting its use in large volume fabrication. Here, we report on a scalable fabrication method that cuts fabrication time to a fraction. A parallelized 9 multi-beamlets DLW process, created by a fixed diffraction optical element (DOE) and subsequent stitching are used to fabricate large periodic high aspect ratio 3D microstructured arrays with sub-micron features spanning several hundred of µm2. The wall structure in the array is designed with a minimum of traced lines and is created by a low numerical aperture (NA) microscope objective, leading to self-supporting lines omitting the need for line-hatching. The fabricated periodic arrays are applied in a cell – 3D microstructure interaction study using living HeLa cells. First indications of increased cell proliferation in the presence of 3D microstructures compared to planar surfaces are obtained. Furthermore, the cells adopt an elongated morphology when attached to the 3D microstructured surfaces. Both results constitute promising findings rendering the 3D microstructures a suited tool for cell interaction experiments, e.g. for cell migration, separation or even tissue engineering studies.
Similar content being viewed by others
Introduction
3D fabrication approaches including electro-spinning, nano-imprinting, additive 3D printing of ceramics, metals and plastics together with other forms of bottom-up techniques, have revolutionized tissue and organ engineering, cell migration research and other applications in biomedical research1,2,3,4,5,6. Additionally, advanced light-induced material processing techniques have been developed including mask-less and rapid micro-fabrication and -machining, e.g. for surface structuring, ablation and modifications7,8,9,10. Belonging to this class of methods is direct laser writing (DLW) based micro-fabrication, where single-photon DLW can fabricate 2D and 2.5D type structures, while the inherent sectioning capability of multi-photon based DLW allows the fabrication of 3D microstructures11,12,13,14. DLW has shown versatility in the fabrication of high-quality micro-optical elements12, waveguides15, and micro-machines16. Laser-based manufacturing is capable of processing bio-compatible materials17,18,19. As an optical technique DLW is limited by optical diffraction. Therefore, achievable feature sizes relate to the wavelength of the light source used. The microfabrication resolution furthermore is governed by the material properties, including the polymerization or ablation thresholds. The combination of these two aspects ultimately may allow for fabricating feature sizes well below the optical diffraction limit20,21,22. The DLW-based polymerization fabrication process is based on tracing the contours of the structure design in a photosensitive material, followed by a development step to remove the developed/undeveloped polymer to obtain the final microfabricated structure. As a serial process, the fabrication time of DLW power scales with the dimensionality of the structure, i.e. to the third power in 3D. This might not present a limiting factor in case of small – high quality structure fabrication, but can hinder upscaling, when considering fabrication of large volume structures. Even though as a benchmark study, recently centimeter size structure fabrication using multi-photon DLW has been demonstrated23,24. For the fabrication of small features high NA optics are chosen, which create the needed small writing voxels. Large volume structures are therefore associated with long fabrication times requiring multiple tracing of closely spaced lines in X and Y, called hatching, as well as close layer separation in Z, called slicing. To compensate for the increase in fabrication time for the DLW process at high resolution/small feature size, two strategies can be employed. First, the writing speed, translation of the voxel through the photosensitive material, could be increased. Second, the light field at the focus, could be modified in a way that several voxels are created, thereby effectively transforming the serial into a parallel fabrication process.
For increased voxel movement speed the translation speed of stage scanning systems is typically the limiting factor for this approach, while inside the field-of-view (FOV) of the focusing objective the voxel speed can significantly be increased by using galvo-scanning mirrors12. Though, for larger structures extending beyond a single FOV stitching of structural elements becomes necessary25.
The parallelization of the DLW process can be achieved using holographic methods, either based on using a fixed diffractive optical element (DOE) or adaptive optical elements such as a spatial light modulators (SLMs) or micro-mirror arrays, or via splitting the excitation beam via lenselets into multiple excitation beamlets13,26,27,28,29,30.
A SLM or micro-mirror array gives the benefit of changeable patterns, even allowing for dynamic pattern changes during the fabrication process. However pattern quality is limited by the SLM pixel or mirror number, shape and density.
Common for DLW-based microfabrication, and especially important for TPP-DLW, where each photon carries energy below the polymerization threshold, is that the energy in each beamlet or pixel, is above the polymerization threshold. The writing speed and especially the maximum number of active voxels is therefore limited by the available laser power. Recent developments in high pulse power kHz repetition rate lasers and micro-mirror arrays have made it possible to reach massive parallelization of the TPP process with up to a million pixels29,30.
Here, we use a fixed beamlet pattern, which is well-suited for the fabrication of repetitive periodic structures with constant pitch, as these can be optimized to achieve high beamlet uniformity and quality. We demonstrate a scalable fast fabrication strategy for large volume continuous 3D structures containing sub-micrometer features. Such feature sizes are found in biology, where extracellular matrices contain networks with few micrometer fibrous structures31, while individual cells typically reach length scales of tens of micrometers. It has been shown that microstructured surfaces have an impact on cell polarization, motility, morphology and proliferation32. Importantly, 3D polymer microstructures may act as scaffolds for tissue engineering33. Various emerging research approaches make use of 3D polymer microstructures to develop an increased understanding via in vitro studies in various areas of medical research relevance, concretely in the area of cancer31,34,35, neuronal25,36,37,38, primary/stem cell research39,40,41,42,43,44,45 and even reached in vivo applications46.
Typically, extended structures – covering several FOV – are needed to host a relevant number of cells interacting with the 3D microstructures under identical conditions. Therefore, the fabrication time of microstructures for cell motility/interaction studies can be considered a relevant factor and reducing it may be considered important for a widespread technology uptake in cellular biology research and bioengineering.
Our approach relies on the combination of a fixed DOE for parallelized multi-beamlet writing with a relatively low NA microscope objective, to allow unit structure fabrication without hatching and reduced slicing.
We aim to reduce fabrication duration by 9 times using a fixed DOE designed to create 9 identical beamlets in a 3 × 3 pattern with a 50 µm pitch, matching to the size of the designed unit structures. We characterize the polymer microstructures using confocal fluorescence microscopy and high-resolution SEM imaging. Stitching of the 3 × 3 patterns is used to create large continuous structure arrays suited for cell scaffolds or tissue engineering and we show initial cell – 3D microstructure interaction results.
Results
We fabricate 3D microstructures using a custom-designed TPP setup, based on a femtosecond laser guided into a stage scanning microfabrication work station. The custom design and accessible beam path allows the insertion of additional optical components, such as a DOE (see scheme in Fig. 1). The DOE creates 9 beamlets and the positioning and beam paths are indicated in an additional scheme, while 3D visualization indicates the writing process inside of a photosensitive polymer. First, we determine the voxel size based on the used microscope objective and fabrication parameters like stage scanning velocity and laser power, to be able to predict the resulting 3D polymer microstructures.
(a) Schematic representation of the TPP experimental setup based on a stage scanning system and a femtosecond laser; an enlarged cross section view of the beamlet-creating DOE and microscope objective as well as a 3D visualization of the parallelized writing using the 9 beamlets in the polymer. (b) SEM micrograph of a 3D structure detail, featuring a vertical line with a diameter of 1.047 µm (Z-direction), the dimension in the XY-plane is indicating that the lateral voxel size is well below 1 µm. (c,d) Study of voxel extend in the Z-direction. The horizontal line separation is changed from 7 µm (c) to 10 µm (d). For 7 µm the wall is nearly intact, while for a separation of 10 µm the wall becomes fully porous. We can estimate the voxel in Z-direction extension to be approx. 7 µm.
Determination of the voxel size
The vertical and lateral dimension of the voxel are determined from fabricated vertical and horizontal lines for selected experimental parameters: a writing speed of 15 µm/s, a laser power of 11.5 mW and the SZ2080 bio-compatible photosensitive polymer.
We determine the lateral voxel size to be <1 µm for single traced lines in the XY- plane, while in vertical traced lines the voxel size reaches approximately 1 µm, as indicated by a marker in Fig. 1b. The slightly larger diameter of the vertical lines stems from additional polymerization caused by the comparatively larger vertical voxel extension leading to increased dose at same fabrication speed.
The vertical dimension of the voxel can be estimated from a 3D microfabricated structure that contains horizontal lines (see Fig. 1c,d). The chosen microstructure for voxel determination, contains a grid of vertical and horizontal lines connecting two larger towers. From the free hanging horizontal lines we can estimate the voxel in Z-direction. The line separation was varied from 5 (not shown) to 7 and 10 µm (see Fig c,d respectively) to identify the situation, when the lateral lines are no longer connected, resulting in small openings and horizontal cracks. This occurs at a separation of 7 µm, while at a separation of 10 µm between the horizontal lines, clear openings and a porous structure appears. Therefore, it is concluded that 7 µm is the vertical voxel size.
To test DOE created multi bealet based parallelization of the microfabrication process for large continuous arrays, we compare two different 3D designs. In both designs, the dimension of the unit structure is accurately matching the distance between the beamlets, created by the fixed DOE. Both 3D microstructure arrays consist of a single layer of unit structures with an XY extension of 450 × 450 µm2, created by stitching several 3 × 3 microstructures. The two designs of stitched structures can be divided into two broad categories of designs; structures with supported or unsupported stitching between individual structures. While different in height and number of walls, the two designs are such that they have the same wall surface area per unit structure.
The first design, categorized as structures with unsupported stitching, contains towers and walls, and stitching is meant to occur at the end facets of the walls. A perspective view of a 3D visualization of the expected microfabricated structures, which takes into account the determined lateral and vertical voxel dimensions, that govern the feature size of the resulting microfabricated structures, can be seen in Fig. 2a. Each of the walls are constructed by merely tracing 4 lines, 2 horizontal and 2 vertical lines (green). The horizontal lines form a wall due to the extended voxel in vertical direction, created by using a low NA microscope objective.
3D unsupported test structure for multi-beam writing. (a) 3D visualization of the unit structure, showing traced lines in green and voxel extension in the Z-direction in red. (b) 3D representation of the DOE replication of 9 identical unit structures. (c) Confocal fluorescence image of the full structure, where white arrows indicate the stitching between different fabrication replications. A white dotted square indicates the highlighted region in (e) where white numbers (1–9) indicates structures from one DOE replication, while red numbers (1–3) are unit structures from another DOE replication. (d) Tilted 3D confocal fluorescence image with arrows indicating error -free stitching in green and incomplete stitching in red. (e) Tilted-view SEM micrograph of the unsupported stitching. Green arrows indicate complete stitching inside the same DOE replication, while orange and red arrows indicate complete and incomplete stitching between structures from different DOE replications, respectively. One example of the sub-micrometer feature created by the difference between horizontal and vertical lines is indicated by the blue arrow.
The unit structure shall be replicated in parallel 9 times by the DOE inside the FOV to create a multiplet structure. In Fig. 2b, we visualize the multiplet taking into account the voxel dimensions.
To achieve homogeneous features for all 9 beamlets for the parallelized TPP microfabrication process, the alignment between the laser excitation beam and the DOE was first optimized (Fig. S1).
The fabricated wall structure has an aspect ratio of more than 15, with a height of >15 µm and a thickness of <1 µm. The additional vertical lines seem to improve mechanical stabilization and provide anchoring of the wall to the sample surface, thereby strengthening the otherwise weakly bound wall structures. We observe that without addition of these lines, the wall segments collapse or move and bend during the development phase (data not shown). Secondly, the vertical lines create sub-micrometre features on the otherwise smooth wall surface, potentially interesting for cell interaction studies. While the walls and vertical pillars are fabricated by the same voxel at the same power and stage moving speed, the asymmetric voxel geometry with a 11 times increased extension in vertical direction causes a higher excitation dose deposited in the polymer positions of the vertically fabricated pillars.
The design of unsupported high aspect ratio single line interconnections demands very high precision in the stitching fabrication step. To evaluate the stitching quality throughout the full array confocal microscopy imaging, based on the autofluorescence signal of the SZ2080 polymer, and higher resolution SEM was used. In the confocal images incomplete stitching leads to discontinuity in the fluorescence from the structures as seen in Fig. 2c,d. The SEM image in Fig. 2d further emphasizes this, where several stitching mismatches, leading to breaks at the stitching position, are highlighted. We define two kinds of stitching results in the periodic structure. One where the resulting walls are intact (green and orange arrows) and a second, where the wall is broken (red arrows). Between structures created within a single FOV with the beamlets in parallel, only intact stitching is observed even if the wall segments seems to buckle, e.g. different orientations of the wall segments seem to occur between the stabilizing vertical pillars or towers. This is especially observable in Fig. 2e, when following the contact line between the polymer and substrate in the bottom of the SEM image.
This indicates that the matching between the structure design and the DOE pitch are perfectly matched and that the 50 µm travel of the stages does not introduce enough misalignment to compromise the single line stitching. Less accurate stitching is observed when multiplets are stitched. Then, both incomplete (red arrows) and complete (orange arrows) stitching results are observed. This indicates that the 150 µm long travel of the stages between different replications can introduce a small misalignment, and fusing extended <1 µm thin wall segments reveals to be difficult.
In Fig. 3 we show a 3D confocal micro-fluorescence (a) and a SEM image (b) of the full structure covering an area of 450 × 450 µm2 containing 81 unit structures. The 3D sectioning confocal imaging allows to assess the 3D nature of the array and all structural features are well resolved.
Array of unsupported stitched parallel fabricated unit structures. (a) Confocal fluorescence image of the full structure (20× objective). (b) SEM micrograph of the full structure covering an area of 450 × 450 µm, covered by a thin 10nm layer of gold. Fabrication time is 37 min for the full array where each individual unit structure takes 246 s.
To produce this extended array, only 9 unit structures are traced, and replicated 9 times. The parallel writing, using the 9 beamlets created by a fixed DOE, results in a 9 times shorter fabrication time.
Depending on the application of the microstructure stitching imperfection may hamper the intended functionality of the structure. One example would be the case of a photonic structure, where stitching discontinuities and structure imperfections would modify the periodicity or waveguiding properties and possibly render the structure non-functional. For most bio-applications the 3D microstructure requirements are expected to be less severe. Therefore, we conclude that using parallelized microfabrication reducing the fabrication time to a fraction via a holographic approach, paves the way for high throughput fabrication of 3D microstructures with bio-applications.
In the following, we aim to optimize the design of the unit structure for optimal stitching and chose extended features to be positioned at the stitching interface to overall reduce the number and extend of stitching errors.
Optimizing 3D design for defect-free stitching
The second unit structure design for the stitching into a large area periodic structure is based on the conclusions made on the first design. The unsupported stitching between structures is changed to a supported structure. We exchange the single central tower with two towers, one at each end of a wall segment. Towers from two unit structures will fully overlap thereby creating a support between wall segments. The towers are 30 µm and the wall segments 27 µm tall, again fabricated by single line tracing. The distance between the horizontal lines is increased to 10 µm exceeding the vertical extension of the voxel. Therefore a porous structure emerges, as can be seen in the 3D visualization of the resulting unit structure in Fig. 3a. The size of the pores in the walls provides openings which lead to the possibility of potential cell passage and hence interesting opportunities for cell migration and cell separation studies31.
The unit structure is replicated in parallel 9 times by the fixed DOE shown in Fig. 4b, the wall segments are fabricated in one direction creating an open scaffold.
3D supported test structure for multi-beam writing. (a) 3D visualization of the unit structure, showing traced lines in green and voxel extension in the Z-direction in red. (b) 3D representation of the DOE replication of 9 identical unit structures. (c) 3D visualization highlighting the stitching between wall segments. (d) Tilted-view SEM image showing the towers with internal stitching positions, highlighted by white arrows. (e) Confocal fluorescence image of the extended array. (f) Tilted-view SEM micrograph of the DOE-written structure, across a larger area of the sample.
Stitching between wall elements from different structures occurs at the inside of the towers, as seen in the 3D visualization in Fig. 4c, and in the SEM micrograph of the fabricated structure shown in Fig. 4d,f. We do not observe stitching errors using confocal fluorescence microscopy (see Fig. 4e), where continuous fluorescence signal is observed along the walls connecting the towers for both type of stitching – either the stitching between the beamlets or the 3 × 3 multiples. Similarly, the high resolution SEM micrograph shown in Fig. 4f does not show fabrication errors due to stitching positioning mismatch.
The full array of 81 unit structures is fabricated in the same way as for the first design. The multiplication of the beam into the 9 beamlets allows the parallel fabrication of the unit structure, such that single tracing of the unit structure results in 9 seemingly identical replica.
In the confocal microscopy image in Fig. 5a the fluorescence from the polymer is again used to map the 3D nature of the array and even details such as the porous wall can be characterized, which can also be observed in the tilted perspective SEM micrograph shown in Fig. 5b.
Array of supported stitched parallel fabricated unit structures. (a) Confocal fluorescence image of the full structure. (b) SEM micrograph of the full structure covering an area of 450 × 450 µm2 and with added thin 10 nm gold layer. Fabrication time is 56 min for the full array where each individual unit structure takes 373 s.
A small part of the array is collapsed, which happens occasionally in the development and subsequent drying process, especially for high aspect ratio structures. Each wall segment is straight, indicating that the supporting tower structures are indeed stabilizing the wall segments, leading to straight 40 µm spanning wall connections between the towers. The wall continues into the tower for another 5 µm, therefore after stitching of the unit structures an extended wall with a total length of 440 µm in the periodic array shown in Fig. 5 is obtained.
We show that parallelized TPP fabrication based on a holographic approach can be used for faster fabrication of extended 3D periodic structure arrays, while additionally we find that it is advisable to optimize the unit structure design for error-free stitching.
To demonstrate the potential of these extended 3D microstructure arrays for bioassays, and to provide an insight on the obtained feature sizes compared to live cells, we perform microstructure – cell interaction studies using confocal and optical transmission microscopy.
Cell – 3D microstructure interaction studies
To evaluate the application of the periodic structures in the area of bioengineering and cell biology, we analyze the live cell – microstructure interaction over several days. We use HeLa cells, which are incubated on both structure arrays, and record confocal and transmission images after 24 and 120 h of incubation (see Figs. 6 and S2), respectively. For SEM characterization and to create a homogenous surface on the substrate, a 10 nm thin pure gold coating was added on the microstructured substrates. A thin continuous gold layer has been reported to be biocompatible and does not show inhibitory effects on cell growth after 72 h using fibroblast cells47.
Combined confocal and optical transmission microscopy images of HeLa cells incubated on gold-coated 3D microstructures after 24 h (a), and zoom images in (a1,a2) and after 120 h in (b) with zoom into selected areas given in (b1,b2). We highlight areas in purple and yellow, where at 24 h of incubation no cells are present, while after additional 96 h of incubation, individual cells attach to walls or edges, respectively. The red circle indicates the opposite situation, where cells are attached to walls at 24 h of incubation, that relocate during the following 96 h leaving empty wall segments behind.
Cultured cells in 2D receive different environmental cues compared to cells in natural tissues, and the potentially beneficial effect of 3D scaffolds to support mimic real tissue has been analyzed in various studies comparing 2D and 3D cell cultures48,49. To study the effect of 3D microstructures on HeLa cell behavior, we compare the cell population and morphology close to the 3D microstructures and on the 2D flat areas of the same sample (see Fig. S3).
The strong fluorescence from the SZ2080 photosensitive polymer is easily detected, while the positions and morphology of the cells is determined from the simultaneously recorded bright field images. The gold coating on the other hand ensures that the incubated cells experience no surface difference between the polymer structures and the glass substrate and the effect of the 3D microstructuring compared to flat 2D surfaces on cell behavior should therefore be directly observable from the experiments. For the first design, the interaction of the incubated HeLa cells and the 3D microstructure after 24 and 120 h of incubation is shown in Fig. 6. We highlight cells attaching to the scaffold after 24 h or 120 h of incubation, respectively and highlight specific dynamic changes, indicated by circles.
In the zoom areas shown in Fig. 6a1,a2 it is observed, that HeLa cells attach to both wall and corner segments, shown in yellow and purple, respectively. The cells change their morphology when interacting with the 3D microstructures and appear elongated between towers and even adopt triangular shape in the corners. We conclude that cells in the proximity of the 3D microstructures can alter their overall morphology compared to the typically more rounded or elliptically stretched cellular shapes present on the planar 2D surface (see Fig. S3a). Only a few cells in the area are not in direct contact with the scaffold, indicating a good affinity of the cells to the 3D microstructures. After 24 h of incubation, the number of cells inside the area of the scaffold is roughly the same as in a similar area on the planar 2D gold surface, indicating similar growth conditions.
The situation changes after 120 h of incubation (see Fig. 6b), where the number of cells inside the area of the scaffold is observably higher, compared to the number of cells in a similar area on the planar surface (see Fig. S3b). Some morphological changes occur for cells in contact with the scaffold (see Fig. 6b1,b2). The area highlighted by a red circle shows cells attached to the scaffold at the 24 h time point, which are not present at these locations after additional 96 h of incubation, indicating that these cells are alive and mobile. The higher number of cells in the 3D microstructured area hints towards two possible mechanisms; either increased cell affinity towards 3D microstructured surfaces, such that cells are attracted from the flat 2D areas into the 3D pattered areas, and/or an effect of the 3D microstructured environment on increased cell proliferation. Quantifying and separating these effects of the 3D microstructures on cell populations could be the aim of future dedicated cell interaction studies.
Discussion
We analyzed the ability to speed up a nonlinear microfabrication process using a multi-beamlets generating DOE structure in the excitation beam path. For a first design without support structures at stitching positions, high similarity is observed between the individual unit structures inside each repetition (see Fig. 2e, green arrow), while at the stitching positions between different repetitions discrepancies are observed leading to gaps in the overall periodic pattern (see Fig. 2e, red arrows). The gaps arise from contraction of the polymer material during the development and subsequent drying process. It is related to large leapfrog movement of the stage system (>150 µm) between repetitions. In the second design, additional support structures at stitching positions were added to overcome this problem. Using this strategy, no gaps are observed and any remaining mismatch is less than 100 nm at the stitching positions. Cell interaction studies with the 3D microstructured arrays show cellular affinity, changed cell morphologies and potentially enhanced cell proliferation.
Conclusions
In summary, we have demonstrated a scalable method for fast fabrication of large volume scaffold structures with the potential for cell and tissue engineering. We demonstrate how parallelization of the DLW process by a fixed DOE cuts the fabrication time to a fraction for large unit structures, while maintaining sub-micrometer features in each unit structure. To further lower fabrication time, each individual unit structure is designed to minimize the number of traced lines by omitting hatching. Large continuous 3D microstructures composed of stitched unit structures with supported and unsupported interconnections were fabricated with the parallelized TPP method. Unsupported stitching between unit structures leads to incomplete connections, while for supported stitching of unit structures, the extension from multiplets to extended periodic arrays is defect-free. While important for photonic structures, for bio-applications the advantages of fast fabrication may outweigh the need for high precision periodicity. The initial cell interaction studies indicate high cell affinity. Several locations around 3D TPP-fabricated features show the accumulation of cells that form contact with the 3D microstructures leading to small cell aggregates. These suggest the 3D TPP microstructures are promising as a tissue engineering scaffolding system.
Materials and Methods
DOE fabrication
The binary phase Fourier DOE generates a 3 × 3 array of spots designed using an in-house Iterative Fourier Transform Algorithm (IFTA), with a three-stage optimization procedure to improve spot array uniformity50. The 10 × 10 mm DOE was fabricated in a 630 nm layer of S1800 series photoresist (MicroChem) on a glass substrate using a custom parallel direct-write photoplotter. The glass substrate was then laser scribed to dice it to dimensions compatible with the multi-photon system microscope.
Two-photon polymerization (TPP) - based micro-fabrication
Structure design in 3D software
All presented structures are designed directly in the μFAB software from Newport. Since the design and fabrication software is the same, no additional software is used for slicing and hatching.
TPP setup
A stage scanning microfabrication writing station (µFAB, Newport), with a fixed focused laser beam is used. Translation stages in XY have a travel range of 100 mm with 1 nm resolution and minimum step size of 10 nm, while in the Z-direction the travel range is 4.8 mm with 20 nm resolution and minimum step size of 60 nm. The movement of the translation stages to trace the lines of the structures is controlled by a Newport XPS controller. A femtosecond laser (Tsunami, Spectra Physics, repetition rate 80 MHz) tuned to 795 nm with a pulse length of approximately 100 fs after the external prism compressor was used as light source for nonlinear polymerization. For power control a combined half-wave plate and Glan-laser polarizer is used. A fast shutter is used to control the beam on/off during the fabrication process. A beam expander is used to fully illuminate the DOE and also to overfill the back aperture of the microscope objective. All the presented structures are fabricated with a 40× Nikon air microscope objective (N40×-PF) with a NA of 0.75. The field-of-view (FOV) for the DOE is chosen to be a 150 µm square to limit optical distortion. The DOE mask is inserted in the excitation beam path at a distance of 15 mm from the back aperture of the microscope objective. Sample focusing and process inspection during fabrication was monitored via a CCD camera protected by a BG39 filter.
Experimental procedure for 3D microfabrication
Cleaned 1 mm thick glass microscope slides are heated to 100 °C for about 30 min on a hotplate to remove eventual water and solvent residues. 20 µL of the SZ2080, low-shrinkage hybrid organic-inorganic zirconium containing sol-gel polymer, is drop-casted on the glass slide and subsequently baked for another 30 min at 100 °C51. After baking, the sample is mounted in the µFAB writing station and the 3D microstructure designs are traced in the polymer layer. For both of the presented scaffolds fabrication speed is set to 15 µm/s. The laser power was set to 148 mW before the DOE element. With a ~70% efficiency of the DOE element, a power of 11.5 mW is estimated for each of the 9 individual beamlets. Development of the fabricated 3D polymer microstructures involves washing with a 1:2 solution of 4-Methyl-2-pentanone and 2-Propanol for 45 min and subsequent air drying.
Confocal microscopy imaging
Confocal imaging was performed with a Zeiss LSM 780 confocal microscope with the 488 nm excitation line of an Ar+ laser. In parallel, transmission bright field images were recorded. Experiments were performed with a 20× dry objective for the developed polymer structures, mounted pointing downwards to allow 3D sectioning of the structures within the working distance of the objective.
For in vitro cell bioimaging studies a 10× dry objective was used and imaging was performed through the 1 mm microscope glass slide.
SEM imaging
A thin 10 nm layer of gold was sputtered on the samples with a Kenosistec - UHV multitarget confocal sputter and SEM micrographs were collected with a FEI NovaNanoSEM 650.
Cell culture
The Penicillin-Streptomycin 100 × solution, 0.25% Trypsin-EDTA, and Phosphate-Buffered Saline (PBS) were supplied from Corning Cellgro. HyClone Fetal Clone III serum was obtained from GE Healthcare and Modified Eagle’s Medium (MEM) was purchased from Biowest. HeLa cell line was purchased from ECACC (Cat. No. 93021013), grown under standard culture conditions and seeded inside of two silicone insert wells on the TPP functionalized microscope slide in MEM culture media supplemented with 10% serum, 1% of penicillin-streptomycin, incubated under 5% of CO2 at 37 °C.
References
Khajavi, R., Abbasipour, M. & Bahador, A. Electrospun biodegradable nanofibers scaffolds for bone tissue engineering. J. Appl. Polym. Sci. 133, 3 (2016).
Cai, Y. Z. et al. Novel biodegradable three-dimensional macroporous scaffold using aligned electrospun nanofibrous yarns for bone tissue engineering. J. Biomed. Mater. Res. - Part A 100A, 5 (2012).
Cipitria, A., Skelton, A., Dargaville, T. R., Dalton, P. D. & Hutmacher, D. W. Design, fabrication and characterization of PCL electrospun scaffolds - A review. J. Mater. Chem. 21, 9419–9453 (2011).
Nandakumar, A. et al. A fast process for imprinting micro and nano patterns on electrospun fiber meshes at physiological temperatures. Small 9, 20 (2013).
Eckel, Z. C. et al. Additive manufacturing of polymer-derived ceramics. Science 351, 6268 (2016).
Ngo, T. D., Kashani, A., Imbalzano, G., Nguyen, K. T. Q. & Hui, D. Additive manufacturing (3D printing): A review of materials methods, applications and challenges. Compos. B. Eng 143, 172–196 (2018).
Truby, R. L. & Lewis, J. A. Printing soft matter in three dimensions. Nature 540, 371–378 (2016).
Kuang, Z. et al. Fast parallel diffractive multi-beam femtosecond laser surface micro-structuring. Appl. Surf. Sci. 255, 13–14 (2009).
Hasegawa, S., Shiono, K. & Hayasaki, Y. Femtosecond laser processing with a holographic line-shaped beam. Opt. Express 23, 18 (2015).
Jenness, N. J., Hill, R. T., Hucknall, A., Chilkoti, A. & Clark, R. L. A versatile diffractive maskless lithography for single-shot and serial microfabrication. Opt. Express 18, 11 (2010).
Vaezi, M., Seitz, H. & Yang, S. A review on 3D micro-additive manufacturing technologies. Int. J. Adv. Manuf. Technol. 67, 1721–1754 (2013).
Gissibl, T., Thiele, S., Herkommer, A. & Giessen, H. Two-photon direct laser writing of ultracompact multi-lens objectives. Nat. Photonics 10, 554 (2016).
Gittard, S. D. et al. Fabrication of microscale medical devices by two-photon polymerization with multiple foci via a spatial light modulator. Biomed. Opt. Express 2, 3167–3178 (2011).
Stankevicius, E. et al. Fabrication of micro-tube arrays in photopolymer SZ2080 by using three different methods of a direct laser polymerization technique. J. Micromech. Microeng. 22, 065022 (2012).
Duc Nguyen, H. H. et al. Freeform three-dimensional embedded polymer waveguides enabled by external-diffusion assisted two-photon lithography. Appl. Opt. 55, 8 (2016).
Power, M., Thompson, A. J., Anastasova, S. & Yang, G. Z. A Monolithic Force-Sensitive 3D Microgripper Fabricated on the Tip of an Optical Fiber Using 2- Photon Polymerization. Small 14, 16 (2018).
Zhu, W. et al. 3D printing of functional biomaterials for tissue engineering. Curr. Opin. Biotech. 40, 103–112 (2016).
Kufelt, O., El-Tamer, A., Sehring, C., Schlie-Wolter, S. & Chichkov, B. N. Hyaluronic acid based materials for scaffolding via two-photon polymerization. Biomacromolecules 15, 2 (2014).
Qin, X. H., Wang, X., Rottmar, M., Nelson, B. J. & Maniura-Weber, K. Near-Infrared Light-Sensitive Polyvinyl Alcohol Hydrogel Photoresist for Spatiotemporal Control of Cell-Instructive 3D Microenvironments. Adv. Mater. 30, 10 (2018).
Zhou, X., Hou, Y. & Lin, J. A review on the processing accuracy of two-photon polymerization. AIP Adv. 5, 030701 (2015).
Xing, J. F. et al. Improving spatial resolution of two-photon microfabrication by using photoinitiator with high initiating efficiency. Appl. Phys. Lett. 90, 131106 (2007).
Emons, M. et al. Two-photon polymerization technique with sub-50 nm resolution by sub-10 fs laser pulses. Opt. Mater. Express 2, 7 (2012).
Obata, K., El-Tamer, A., Koch, L., Hinze, U. & Chichkov, B. N. High-aspect 3D two-photon polymerization structuring with widened objective working range (WOW-2PP). Light Sci. Appl. 2, e116 (2013).
Chu, W. et al. Centimeter-Height 3D Printing with Femtosecond Laser Two-Photon Polymerization. Adv. Mater. Technol. 3, 5 (2018).
Accardo, A. et al. Multiphoton Direct Laser Writing and 3D Imaging of Polymeric Freestanding Architectures for Cell Colonization. Small 13, 27 (2017).
Obata, K., Koch, J., Hinze, U. & Chichkov, B. N. Multi-focus two-photon polymerization technique based on individually controlled phase modulation. Opt. Express 18, 16 (2010).
Kato, J. I., Takeyasu, N., Adachi, Y., Sun, Hong-Bo & Kawata, S. Multiple-spot parallel processing for laser micronanofabrication. Appl. Phys. Lett. 86, 044102 (2005).
Vizsnyiczai, G., Kelemen, L. & Ormos, P. Holographic multi-focus 3D two-photon polymerization with real-time calculated holograms. Opt. Express 22, 24217–24223 (2014).
Saha, S. K. et al. Scalable submicrometer additive manufacturing. Science 366, 6461 (2019).
Geng, Q., Wang, D., Chen, P. & Chen, S. C. Ultrafast multi-focus 3-D nano-fabrication based on two-photon polymerization. Nat. Commun. 10, 2179 (2019).
Spagnolo, B. et al. Three-dimensional cage-like microscaffolds for cell invasion studies. Sci. Rep. 5, 10531 (2015).
Huang, G. et al. Functional and Biomimetic Materials for Engineering of the Three-Dimensional Cell Microenvironment. Chem. Rev. 117, 12764–12850 (2017).
Farsari, M. & Chichkov, B. N. Materials processing: Two-photon fabrication. Nat. Photonics 3, 450–452 (2009).
Lemma, E. D. et al. Tunable mechanical properties of stent-like microscaffolds for studying cancer cell recognition of stiffness gradients. Microelectron. Eng. 190, 11–18 (2018).
Marino, A. et al. Two-Photon Lithography of 3D Nanocomposite Piezoelectric Scaffolds for Cell Stimulation. ACS Appl. Mater. Interfaces 7, 46 (2015).
Timashev, P. S. et al. 3D in vitro platform produced by two-photon polymerization for the analysis of neural network formation and function. Biomed. Phys. Eng. Express 2, 035001 (2016).
Marino, A. et al. Two-Photon Polymerization of Sub-micrometric Patterned Surfaces: Investigation of Cell-Substrate Interactions and Improved Differentiation of Neuron-like Cells. ACS Appl. Mater. Interfaces 5, 13012–13021 (2013).
Soman, P. et al. Three-dimensional scaffolding to investigate neuronal derivatives of human embryonic stem cells. Biomed. Microdevices 14, 829–838 (2012).
García-González, A. et al. The Effect of Cell Morphology on the Permeability of the Nuclear Envelope to Diffusive Factors. Front. Physiol 9, 925 (2018).
Trautmann, A., Rüth, M., Lemke, H.-D., Walther, T. & Hellmann, R. Two-photon polymerization based large scaffolds for adhesion and proliferation studies of human primary fibroblasts. Opt. Laser Technol. 106, 474–480 (2018).
Nava, M. M. et al. Two-photon polymerized ‘nichoid’ substrates maintain function of pluripotent stem cells when expanded under feeder-free conditions. Stem Cell Res. Ther. 7 (2016).
Su, P.-J. et al. Mesenchymal Stem Cell Interactions with 3D ECM Modules Fabricated via Multiphoton Excited Photochemistry. Biomacromolecules 13, 2917–2925 (2012).
Suter, M. et al. Superparamagnetic microrobots: fabrication by two-photon polymerization and biocompatibility. Biomed. Microdevices 15, 997–1003 (2013).
Timashev, P. et al. Novel biodegradable star-shaped polylactide scaffolds for bone regeneration fabricated by two-photon polymerization. Nanomedicine 11, 1041–1053 (2016).
Ricci, D. et al. Scaling-up techniques for the nanofabrication of cell culture substrates via two-photon polymerization for industrial-scale expansion of stem cells. Materials 10(1), 66 (2017).
Mačiulaitis, J. et al. Preclinical study of SZ2080 material 3D microstructured scaffolds for cartilage tissue engineering made by femtosecond direct laser writing lithography. Biofabrication 7, 015015 (2015).
Selvakumaran, J., Hughes, M. P., Keddie, J. L. & Ewins, D. J. Assessing biocompatibility of materials for implantable microelectrodes using cytotoxicity and protein adsorption studies. 2nd Annual International IEEE-EMBS Special Topic Conference on Microtechnologies in Medicine and Biology. Proceedings (Cat. No.02EX578), Madison, WI, USA, pp. 261–264 (2002).
Mirbagheri, M. et al. Advanced cell culture platforms: a growing quest for emulating natural tissues. Mater. Horiz. 6, 45–71 (2019).
Kapałczyńska, M. et al. 2D and 3D cell cultures – a comparison of different types of cancer cell cultures. Arch. Med. Sci. 14(4), 910–919 (2018).
Kettunen, V. Review of iterative Fourier-transform algorithms for beam shaping applications. Opt. Eng. 43, 11 (2004).
Ovsianikov, A. et al. Ultra-low shrinkage hybrid photosensitive material for two-photon polymerization microfabrication. ACS Nano 2, 2257–2262 (2008).
Acknowledgements
This work was supported by the CCDR-N via the project “Nanotechnology based functional solutions” (grant no.: NORTE-01-0145-FEDER-000019) and from the ERDF via the INTERREG POCTEP programme via the grant no: 0181_NANOEATERS_1_EP, O.F.S. received a fellowship from the EC via the project NanoTRAINForGrowth, FP7-PEOPLE-COFUND-FP programme (grant no: 600375).
Author information
Authors and Affiliations
Contributions
J.N., C.M. and K.H. conceived and designed the research. C.M. designed and fabricated the TPP structures. O.S. cultivated and incubated the HeLa cells. O.S. and C.M. made the confocal images. M.S. and K.H. designed and fabricated the DOE. J.B. performed the metal deposition and SEM imaging of the structures. J.N. supervised the project. All authors contributed to the writing of the manuscript and have given their approval.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Maibohm, C., Silvestre, O.F., Borme, J. et al. Multi-beam two-photon polymerization for fast large area 3D periodic structure fabrication for bioapplications. Sci Rep 10, 8740 (2020). https://doi.org/10.1038/s41598-020-64955-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-64955-9
This article is cited by
-
The physics of 3D printing with light
Nature Reviews Physics (2023)
-
Development of the multi-directional ablation process using the femtosecond laser to create a pattern on the lateral side of a 3D microstructure
Scientific Reports (2023)
-
Light-based vat-polymerization bioprinting
Nature Reviews Methods Primers (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.