Abstract
In van der Waals epitaxial growth, the substrate plays a particularly important role in the crystal morphology. Here, we synthesized MoS2 by chemical vapour deposition on silicon carbide (SiC). The obtained MoS2 dendritic crystals show six-fold symmetry, which are different from the conventional triangular shapes on SiO2 substrate and from those with three-fold symmetry on SrTiO3 substrate. Interestingly, these MoS2 dendritic crystals on SiC exhibit an average fractal dimension 1.76, which is slightly larger than the classical Diffusion-limited-Aggregation fractal dimension 1.66. The first principle calculation indicates that the six-fold symmetry of the dendritic MoS2 is determined by the lattice symmetry of SiC. To further demonstrating the substrate effect, we break the natural six-fold lattice symmetry of SiC (0001) into groove arrays through etching the substrate. And then we successfully synthesized cross-type dendritic crystal MoS2 with two-fold symmetry. Its average fractal dimension 1.83 is slightly larger than the fractal dimension 1.76 of the previous MoS2 dendrite with six-fold symmetry. In a word, the symmetry of SiC substrate determined the symmetry and the fractal dimension of the dendritic MoS2. This work provides one possibility of inducing the growth orientation of dendritic crystals through controlling the substrate surface symmetry artificially.
Similar content being viewed by others
Introduction
In the past ten years, two dimensional (2D) transition-metal dichalcogenides (TMDs) materials have received considerable research interests in many fields for their wide range of potential applications, including optoelectronic devices1,2,3, capacitors4, hydrogen storage5, catalysis6, and solid lubricant7, because of their unique electrical, chemical and mechanical properties. Among many transition-metal dichalcogenides, one of the most promising representatives is molybdenum disulfide (MoS2). It has been expected as a candidate of flexible small quantum transistor materials8,9 in post-Moore era, due to its moderate direct band gap at few layers10,11,12 comparing to semi-metallic graphene. Until now, a variety of methods have been developed13,14,15,16 to fabricate a few layers or monolayer MoS2, including mechanically exfoliation, liquid exfoliation, thermal decomposition and chemical vapour deposition (CVD). Among them, the CVD method has been demonstrated as a promising method in producing large continuous MoS2 films17, thickness modulated MoS2 films18,19, and even large-area and highly quality monolayer MoS2 films20. In the CVD growth process, temperature, gas flow and substrate all play essential roles in determining the final film morphology, crystalline structure and quality of film. In the previous reports, the different substrates, such as amorphous SiO2/Si18,21,22, single-crystal mica19 and sapphire23, were adopted in MoS2 CVD growth. In these cases, the triangular MoS2 films were mainly synthesized due to the little influence of substrates. The synthesis of MoS2 film belongs to Van der Waals epitaxial growth and may be influenced by the symmetry of substrates. Such as, SrTiO3 with quartic symmetry, has been used to synthesize MoS2 dendritic flakes with three-fold symmetry6,24,25. In this regard, it is imperative to know the effect of substrate symmetry in MoS2 CVD growth process.
Though there is a paper about MoS2 synthesis by use of silicon carbide (SiC) as substrate, the MoS2 is a vertically standing triangles, and isn’t the dendritic morphology26. Here, we firstly synthesize dendritic MoS2 with six-fold symmetry and two-fold symmetry by use of single crystal SiC as a substrate, which is also different from that with three-fold symmetry on the SrTiO3 6,24,25. To explain the novel morphology formation, we adopt the diffusion limited aggregation (DLA) to reveal the reaction process of initial crystal growth. It has been observed that the symmetry of the single crystal SiC substrate played an irreplaceable role in dendritic crystal formation. In order to show the dominant role of the substrate symmetry further, we etched the SiC substrate into the grooves to break the substrate original six-fold symmetry artificially. This resulted in the cross-shaped dendritic MoS2 films, which is different from six-fold symmetry previously. This work provides not only one possibility of artificial induction of crystal growth orientation through controlling the substrate symmetry, but also provides a case for deeply understanding the detailed dynamics in non-equilibrium crystal growth of two-dimensional materials.
Results and Discussion
Before researching the substrate effect on film growth properties in MoS2 CVD synthesis, we used the common silicon substrate with 285 nm insulating SiO2 as a monitor of growth conditions. Through optimizing the growth conditions, ~300 μm triangular MoS2 crystal (Fig. 1b) has been achieved in a CVD setup (Fig. 1a) at atmospheric pressure. Raman spectroscopy was performed on this sample and relative Raman peak intensities and peak positions of the E1 2g and A1g modes of the MoS2 have been acquired. As shown in Fig. 1c, this MoS2 crystal grown on SiO2 shows the frequency difference (∆ν) of 19.3 cm−1, less than 20 cm−1, which is a monolayer in nature27,28,29,30. Additionally, many secondary nucleation sites on top of the big triangle monolayer film can be easily observed, which is similar to other reports31. However, their formation mechanism in the final film morphology is beyond this paper’s scope.
The MoS2 crystal grown on SiC substrate has shown clearly dendritic form as shown in Fig. 2, instead of compact triangular structure obtained on SiO2/Si substrate. The optical image recorded over a large region with plentiful MoS2 dendritic crystal, like snowflakes, on the SiC substrate, as shown in Fig. 2a. Most of the islands’ sizes are around 100 μm. The area within the red rectangular region of Fig. 2a was zoomed in and shown in Fig. 2b. In the image, it can be observed clearly that two hexagonal dendritic crystals have same six-fold symmetric backbones, extending with many hierarchical branches harbouring similar angle. In some regions on SiC wafer, the backbones only extend a few secondary branches, while in other regions, the continuous films were observed, which may be due to different local growth conditions. The inset in Fig. 2b is the MoS2 flakes grown on SiO2 substrate in the same batch growth as a comparison. The scale bar is 10 μm. The X-ray photoelectron spectroscopy (XPS) data of the dendritic crystals grown on SiC reveals the occurrence of Mo 3d3/2 and 3d5/2 states at binding energies of 232.7 eV and 229.6 eV, and 2p1/2 and 2p3/2 states of S at 163.7 eV and 162.4 eV respectively (Fig. 2e). These are typical signs for MoS2 films32,33,34. To characterize the flakes’ structure in more details, a high resolution scanning electron microscope (SEM) image was taken in Fig. 2c. Similar to the optical images, it also shows the backbones and many hierarchical branches. While, there is no any hierarchical branch in some backbones. From the morphology comparison, we can found clearly that the MoS2 grown on SiO2 in the same batch growth is the compact triangle crystal, which suggests that the substrate affects the final film morphology of MoS2. Even though various shapes with or without additional branches can be observed, all of them exhibit the basic triangle shapes or their combining forms, which is similar to previous reports of MoS2 grown on SiO2/Si substrate20,21,35.
Micro-Raman spectroscopy has been widely utilized to characterize the 2D materials. The native MoS2 grown on SiC and SiO2 was scanned by 518 nm wavelength laser, and their Raman spectra were shown in Fig. 2f. It can be observed that two samples grown on SiC and SiO2 all show typical characteristic Raman modes of MoS2, E1 2g and A1g peaks, around 380 and 402 cm−1. Their frequency difference (∆ν) for the MoS2 on SiO2 is 18.9 cm−1 which is a monolayer in nature27,28,29,30. But their frequency difference is 24.8 cm−1 in MoS2 on SiC, corresponding to a thicker film. The Atomic Force Microscope (AFM) image (Fig. 2d) reveals more details about the morphology and thickness of the snow-like MoS2 dendrite. It indicates that the thickness of the dendritic MoS2 flakes is at most 3 nm, approximate 5 layers.
The two-dimensional crystal growth mechanism of MoS2 can usually be described by following process: 1) nucleation, 2) diffusion and growth, 3) formation of crystals. The symmetry of substrate dominates the nucleation process and plays a critical role in determining whether a compact or fractal growth. In other words, the substrate with triangular or hexagonal geometry is easier to have extended fractal growth than square lattice36,37,38. To obtain the symmetry of the MoS2 film morphology in more detail via CVD growth method, we carried out the angular distribution of the dendritic morphology of MoS2 on SiC statistically. The orientation of backbones of dendrites were illustrated by the blue arrows, between which are 60° angles usually, shown in Fig. 3a. And the angle between the subsequent hierarchical branches and the main backbones is also about 60°, seen in Fig. 3c. It has been confirmed that both angle distributions are centred at 60°, shown in Figs 3b and d, by the angle statistics from 200 flakes of backbone and 140 flakes of hierarchical branches.
In order to describe the morphology of MoS2 flakes in more detail, the fractal dimension is calculated statistically, presented in Fig. 3e. Thirty-four flakes on the same sample was comprehensively estimated by use of a standard box-counting evaluation. The left inset is a contrast-enhanced SEM image of a typical snow-like MoS2 dendrite crystal; while the right inset is a box-counting estimation of the fractal dimension for the left flake. These flakes exhibit an average fractal dimension of 1.76 ± 0.01. This fractal dimension is in good agreement with the classical DLA dimension of 1.66. This also demonstrates the natural fractal property of the snow-like MoS2 dendrite indirectly.
Whether the six-fold symmetry observed in the dendritic morphology is influenced by the substrate surface symmetry or not? In order to reply the question, the density functional theory (DFT) calculations were performed. The binding energies of a MoS x monomer on various configurations on the Si-terminated SiC (0001) surface are computed. Here the molecular MoS3 was assumed to be the representative monomer precursor for the final MoS2 film because it is the dominate phase in the low-temperature and excess sulphur regime, according to the Mo-S phase diagram39. In the DFT model, the SiC substrate with Si-terminated surface was modelled by a three layers 5 × 5 superlattice with total 150 atoms as shown in Fig. 4a. And a vacuum space of 10 Å along the direction perpendicular to the surface was used to avoid interactions between adjacent layers. Six absorption sites of MoS3 molecule on SiC surface were calculated and the corresponding bonding energy to the lowest energy mode (Fig. 4g) were shown under each image, respectively (Fig. 4b–g). Note that the most energetically favourable adsorption site for MoS3 is for the Mo atom sitting above the centre of the hexagonal lattice while the S atom locating on top of Si atoms, as shown in Fig. 4g, where the unsaturated S and Si atoms could form effective bonding with each other. Because of the natural hexagonal symmetry of SiC, it is obvious that there are six closest equal adsorption sites near the energetically favourable adsorption site and six preferential equal diffusion pathways oriented 60 degree to each other as shown in Fig. 4h. This is in agreement well with the statistical results about the 60 degree angle between the backbones of dendritic MoS2 flakes.
The formation of the dendritic morphology could be inferred by the DLA mechanism36,40,41. When the MoS3 molecule was adsorbed onto substrate, it might have some energy to move around on the surface. According to our calculation, the molecule prefer the position energetically on where the Mo atom is rest upon the centre of the hexagonal lattice because this configuration has the lowest binding energy, and thus it serves as an nucleation site. This nucleation on SiC substrate doesn’t like the previous SiO2, sapphire and Mica substrate, on which it prefers to happen on impurity or defects.
Subsequent adsorbed atoms (ad-atoms) deposit onto the substrate and diffuse in a certain way. They might hopping around onto different sites but the configuration with Mo sitting at the centre of Si-C hexagon is energetically favoured and will serve with stronger sticking coefficient. When the ad-atoms encounter those nucleation centres, three situations might happen, which is determined by the difference between particle diffusing and bonding energy. The first is that the particles don’t diffuse and become attached to the nucleation centre and being part of cluster. The second is that the ad-atoms continue walking on the substrate surface and not adsorbed with any cluster. The third is that they become one part of the cluster, but continue to diffuse along the cluster edges. With the increasing of the cluster size, more and more ad-atoms have the chance to meet the island and the cluster continues to grow. It suggests that the first and the second situations would always happen until there are no ad-atom left on the surface. What is interesting is the third case, the ad-atoms with proper energy diffuse limitedly along the edge so that they couldn’t cross the corner to make the edge relaxing and new corners would be generated. Subsequent ad-atoms follow the former atoms and more edge are generated. With the increasing of edges and corners, the ad-atoms have less chance to fill the vacancy sites and relax along the edge36,37. In our case, it suggests that because the SiC substrate has strong dangling bond42,43, comparing to amorphous SiO2, the MoS x molecule need higher energy to diffuse along the edge so that it prefers to stick to the nucleation sites, according to the DFT calculation, leading to more edges and insufficient edges relaxation once they encounter a cluster. In a word, whether precursors could diffuse freely or form dendrite in the substrate surface depends on the competition among its energy, the temperature, the interaction between the precursor and the substrate, and the interaction between the precursor and the established island or cluster. In our case, since the strong dangling bond of the SiC substrate, the more compact dendritic MoS2 film was formed and its fractal dimension is bigger than the classical one. Furthermore, due to the natural hexagonal symmetry of those nucleation sites on SiC (0001) surface, the dendritic edges prefer arranging along the centre of hexagonal Si-C ring to form a unique dendritic shape with six-fold symmetry. About the dendritic shape with six-fold symmetry in two dimension, there is another material, graphene dendritic on copper44. MoS2 dendritic with six-fold symmetry is different from the graphene one because the former owns three atoms layer structure, while the latter is only one atom layer structure. The most important is that the morphology of graphene dendritic is determined by itself symmetry, not by the substrate, copper. MoS2 dendritic is fully determined by the symmetry of the SiC substrate44. Furthermore, from DLA mechanism, we can know that another energy term in first principle calculation, a stick potential barrier works in MoS2 dendritic growth.
To further demonstrate that the SiC surface symmetry determines the final dendritic morphology of MoS2 film in CVD, we created an artificial surface structure on substrate to change the nucleation sites symmetry. The chemical etching process is presented to accomplish the aim. Prior to MoS2 growth, the SiC substrate was immersed in hydrofluoric acid (HF, 1%) for 24 h before washing. Artificial grooves with about 3 nm depth and 100 nm width was created, shown in Fig. 5e. The MoS2 film grown on the etched SiC shows a cross-type dendrite with two-fold symmetry, as shown by the optical and SEM images of Figs 5a–c. Most of the island’s size are around 20 μm, much smaller than 100 μm crystals on native SiC. As a comparison, the MoS2 on SiO2 under the same batch growth is shown in the inset of Fig. 5b (the scale bar is 10 μm). By comparing these images, it is obvious that the new two-fold symmetry MoS2 dendrite is different from the six-fold MoS2 on native SiC and from the compact crystal on SiO2. Furthermore, the orientation of the two-fold dendrites are aligned with the long axis along roughly the same direction of the grooves. This has been suggested by the statistics of main axis orientation for the dendritic flakes, seen in Fig. 5d. To confirm the crystal grown on etched SiC is still MoS2, XPS was also collected, and the result is shown by Fig. 5f: the occurrence of Mo 3d3/2 and 3d5/2 states at binding energies of 232.7 eV and 229.6 eV, and 2p1/2 and 2p3/2 states of S at 163.7 eV and 162.4 eV, which are typical signs for MoS2 film. Furthermore, the SEM and AFM images have shown more morphology details (Figs 5c,e). Wavy MoS2 flakes with groove arrays can be observed, which indicates again that the long axis of cross-type dendrite is along the groove direction. Comparing to the six-fold MoS2, the fractal dimension of two-fold MoS2 is around 1.83 by statistics for twenty-one cross-type dendritic MoS2 flakes (Fig. 5g). The fractal dimension is slightly bigger than that of the six-fold one, so we can infer the two-fold dendritic MoS2 is more compact than six-fold one. It is attributed to a potential barrier. On the etched SiC substrates, the precursor should overcome an additional potential barrier across artificial groove arrays to diffuse on the surface, than on the native SiC substrate.
The details of the two-fold dendrite growth should be further understood under DLA mechanism as well. On the etched SiC substrates, the artificial grooves create an anisotropy diffusion potential barrier, which induces an anisotropy sticking energy. Therefore, the energy should hinder diffusion of the precursor molecule across the groove direction, comparing to direction along the groove. During growth, the ad-atoms have much higher probability stuck to those sites at edge of grooves, causing faster growth of crystal along the groove direction than across it. Comparing the native SiC substrate, the hexagonal symmetry of the diffusion paths have been broken, which are replaced by insufficient diffusion across the grooves and faster diffusion along to the grooves. This suggests that two orthometric pathways in the etched SiC substrate lead to the novel cross-type shape dendrites under the DLA mechanism. Therefore, we conclude that the dendritic morphology of MoS2 grown on SiC substrate can be modified to the desired morphology through artificially constructing special substrate surface in the CVD growth process. This also inspires us to explore novel symmetry of dendrite, different from its natural, by the use of special substrate or the special symmetry structure on surface of substrate.
Conclusion
In summary, we have achieved the MoS2 dendritic in CVD on single-crystal SiC. The obtained MoS2 flakes show a special snow-shaped dendritic morphology with six-fold symmetry, in contrast with the traditional sharp-edged triangular compact flakes grown on conventional SiO2 substrate. The growth dynamics of this morphology can be readily explained by the classical Diffusion-Limited-Aggregation mechanism. Additionally, we find the intrinsic lattice symmetry of the SiC substrate can be broken by etching, and obtained cross-shaped dendritic MoS2 films, further suggesting that the substrate plays a crucial role in dendritic growth process. Furthermore, by comparing the two kind of fractal dimension of dendrite with the classical one, we found that the substrate effect on the MoS2 dendrite would be enhanced due to the additional potential barrier. This work could contribute to further in-depth understanding of the detailed dynamics in non-equilibrium crystal growth of two-dimensional materials and provides one possibility of artificially inducing the growth orientation of crystals through controlling the substrate surface symmetry.
Methods
The MoS2 flakes were produced utilizing the facile CVD technique. High purity MoO3 (99.5%, Alfa Aesar) and sulphur powder (99.9%, Alfa Aesar) were used as precursors. The MoO3 powder (less than 1 mg) was sowed directly on the substrate which was placed at the centre of a 4-inch diameter CVD furnace by a flat quartz board. The sulphur powder was kept in a quartz boat placed upstream at a lower temperature zone out of the furnace. The distance between sulphur boat and the substrate was maintained to be ~50 cm.
We used single crystal 4H-SiC wafers as substrates, where the crystal orientation is <0001> and 4° toward <112(−)0>. All substrates were first immersed in a freshly prepared piranha solution (H2SO4:H2O2, 7:3) for 24 h. Then they were washed with de-ionized (DI) water two times, repeatedly, and sonicated in acetone and subsequently in isopropyl alcohol (IPA) for 5 min each before blow-dried by nitrogen. In addition, when it needs etching, the SiC substrate was etched by immersing in hydrofluoric acid (HF, 1%) for 24 h. And all other processes were then completed repeatedly.
Prior to the growth, the quartz tube of CVD furnace was cleaned completely. The furnace was then heated to 300 °C for 60 min under Ar gas. Then the temperature was ramped up to 700 °C at a rate of 10 °C/min. At this stage, the sulphur boat was pushed into heated zone to a suitable position. Then the furnace was kept in 700 °C for 20 min before cooled naturally. In the whole process, the gas flow rate was kept at 500 sccm.
The SEM measurements were done using a Zeiss Ultra 55 FESEM system. The Raman spectroscopy were executed at room temperature in back scattering geometry using a Renishwa’s Invia confocal Raman spectrometer with argon ion laser (514 nm excitation). The size of the focused laser spot on the sample was ~1um. The laser power was kept at 12 μW for all the measurements. The X-ray photoelectron spectroscopy (XPS Thermo Fisher K-Alpha) measurements were done with standard Al Kα (1486.7eV) x-ray source. The binding energies were calibrated with respect to the signal from the adventitious carbon (binding energy =284.5eV). AFM measurement was performed on an Asylum Research Company Cypher-ES system.
References
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Baugher, B. W. H., Churchill, H. O. H., Yang, Y. & Jarillo-Herrero, P. Optoelectronic devices based on electrically tunable p-n diodes in a monolayer dichalcogenide. Nat. Nanotechnol. 9, 262–267 (2014).
Ugeda, M. M. et al. Giant bandgap renormalization and excitonic effects in a monolayer transition metal dichalcogenide semiconductor. Nat. Mater. 13, 1091–1095 (2014).
Pumera, M., Sofer, Z. & Ambrosi, A. Layered transition metal dichalcogenides for electrochemical energy generation and storage. J. Mater. Chem. A 2, 8981–8987 (2014).
Bonaccorso, F. et al. Graphene, related two-dimensional crystals, and hybrid systems for energy conversion and storage. Science 347, 1246501 (2015).
Zhang, Y. et al. Dendritic, transferable, strictly monolayer MoS2 flakes synthesized on SrTiO3 single crystals for efficient electrocatalytic applications. ACS nano 8, 8617–8624 (2014).
Chhowalla, M. & Amaratunga, G. A. J. Thin films of fullerene-like MoS2 nanoparticles with ultra-low friction and wear. Nature 407, 164–167 (2000).
Ponomarev, E., Gutierrez-Lezama, I., Ubrig, N. & Morpurgo, A. F. Ambipolar light-emitting transistors on chemical vapor deposited monolayer MoS2. Nano Lett. 15, 8289–8294 (2015).
Sangwan, V. K. et al. Gate-tunable memristive phenomena mediated by grain boundaries in single-layer MoS2. Nat. Nanotechnol. 10, 403–406 (2015).
Splendiani, A. et al. Emerging photoluminescence in monolayer MoS2. Nano Lett. 10, 1271–1275 (2010).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).
Liu, Q. et al. Tuning electronic structure of bilayer MoS2 by vertical electric field: a first-principles investigation. J. Phys. Chem. C 116, 21556–21562 (2012).
Wang, F. et al. Recent advances in transition-metal dichalcogenide based nanomaterials for water splitting. Nanoscale 7, 19764–19788 (2015).
Gan, X., Zhao, H. & Quan, X. Two-dimensional MoS2: A promising building block for biosensors. Biosens. Bioelectron. 89, 56–71 (2016).
Tan, C. & Zhang, H. Two-dimensional transition metal dichalcogenide nanosheet-based composites. Chem. Soc. Rev. 44, 2713–2731 (2015).
Coleman, J. N. et al. Two-dimensional nanosheets produced by liquid exfoliation of layered materials. Science 331, 568–571 (2011).
Liu, K. K. et al. Growth of large-area and highly crystalline MoS2 thin layers on insulating substrates. Nano Lett. 12, 1538–1544 (2012).
Choudhary, N., Park, J., Hwang, J. Y. & Choi, W. Growth of large-scale and thickness-modulated MoS2 nanosheets. ACS Appl. Mater. Inter. 6, 21215–21222 (2014).
Xu, Y. Y. et al. Layer-controlled large area MoS2 layers grown on mica substrate for surface-enhanced Raman scattering. Appl. Surf. Sci. 357, 1708–1713 (2015).
van der Zande, A. M. et al. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 12, 554–561 (2013).
Ji, Q., Zhang, Y., Zhang, Y. & Liu, Z. Chemical vapour deposition of group-VIB metal dichalcogenide monolayers: engineered substrates from amorphous to single crystalline. Chem. Soc. Rev. 44, 2587–2602 (2015).
Lin, Z. et al. Controllable growth of large-size crystalline MoS2 and resist-free transfer assisted with a Cu thin film. Sci. Rep. 5, 18596 (2015).
Wu, C. R. et al. Multilayer MoS2 prepared by one-time and repeated chemical vapor depositions: anomalous Raman shifts and transistors with high ON/OFF ratio. J. Phys. D: Appl. Phys. 48, 435101 (2015).
Ji, Q. et al. Morphological engineering of CVD-grown transition metal dichalcogenides for efficient electrochemical hydrogen evolution. Adv. Mater. 28, 6207–6212 (2016).
Zhang, Y. et al. Monolayer MoS2 dendrites on a symmetry-disparate SrTiO3 (001) substrate: formation mechanism and interface interaction. Adv. Fun. Mater. 26, 3299–3305 (2016).
Lan, F. F. et al. Synthesis of Vertically Standing MoS2 Triangles on SiC. Sci. Rep. 6, 31980 (2016).
Windom, B. C., Sawyer, W. G. & Hahn, D. W. A Raman spectroscopic study of MoS2 and MoO3: applications to tribological systems. Tribol. Lett. 42, 301–310 (2011).
Hussain, S. et al. Controlled synthesis and optical properties of polycrystalline molybdenum disulfide atomic layers grown by chemical vapor deposition. J. Alloys Compd. 653, 369–378 (2015).
Li, H. et al. From bulk to monolayer MoS2: evolution of Raman scattering. Adv. Fun. Mater. 22, 1385–1390 (2012).
Najmaei, S., Liu, Z., Ajayan, P. M. & Lou, J. Thermal effects on the characteristic Raman spectrum of molybdenum disulfide (MoS2) of varying thicknesses. Appl. Phys. Lett. 100, 013106 (2012).
Han, G. H. et al. Seeded growth of highly crystalline molybdenum disulphide monolayers at controlled locations. Nat. Com. 6, 6128 (2015).
Qiu, D., Lee, D. U., Pak, S. W. & Kim, E. K. Structural and optical properties of MoS2 layers grown by successive two-step chemical vapor deposition method. Thin Solid Films 587, 47–51 (2015).
Yang, Z. et al. Realization of high Curie temperature ferromagnetism in atomically thin MoS2 and WS2 nanosheets with uniform and flower-like morphology. Nanoscale 7, 650–658 (2015).
Shi, J. et al. Monolayer MoS2 growth on Au foils and on-site domain boundary imaging. Adv. Fun. Mater. 25, 842–849 (2015).
Wang, S. et al. Shape evolution of monolayer MoS2 crystals grown by chemical vapor deposition. Chem. Mater. 26, 6371–6379 (2014).
Zhang, Z. & Lagally, M. G. Atomistic processes in the early stages of thin-film growth. Science 276, 377–383 (1997).
Zhang, Z., Chen, X. & Lagally, M. G. Bonding-geometry dependence of fractal growth on metal surfaces. Phys. Rev. Lett. 73, 1829–1832 (1994).
Ghosh, A., Batabyal, R., Das, G. P. & Dev, B. N. An extended fractal growth regime in the diffusion limited aggregation including edge diffusion. AIP Adv. 6, 015301 (2016).
Feldman, Y., Wasserman, E., Srolovitz, D. J. & Tenne, R. High-rate, gas-phase growth of MoS2 nested inorganic fullerenes and nanotubes. Science 267, 222 (1995).
Witten, T. A. & Sander, L. M. Diffusion-limited aggregation, a kinetic critical phenomenon. Phys. Rev. Lett. 47, 1400–1403 (1981).
Honjo, H., Ohta, S. & Sawada, Y. New experimental finding in two-dimensional dendritic crystal growth. Phys. Rev. Lett. 55, 841–844 (1985).
Starke, U. et al. Novel reconstruction mechanism for dangling-bond minimization: combined method surface structure determination of SiC(111)-(3 × 3). Phys. Rev. Lett. 80, 758–761 (1998).
Bekaroglu, E., Topsakal, M., Cahangirov, S. & Ciraci, S. First-principles study of defects and adatoms in silicon carbide honeycomb structures. Phys. Rev. B 81, 075433 (2010).
Hao, Y. F. et al. The Role of Surface Oxygen in the Growth of Large Single-Crystal Graphene on Copper. Sciencce 342, 720–723 (2013).
Acknowledgements
This work is partially supported by “Shaanxi Province Science and Technology Innovation Project of China” (2015ZS-02) and that for “National Science and Technology Major Project of China” (2016YFA0300702). M. G. Xia also thanks to the supports by State Key Laboratory for Mechanical Behaviour of Materials (Grant No. 20131311), and the Fundamental Research Funds for Central Universities (2012jdgz04). Prof. Gu want to acknowledge funding from the National Natural Science Foundation of China (51672125, 51472114).
Author information
Authors and Affiliations
Contributions
M.X., Z.G. and T.M. conceived the idea and supervised the project. D.W., T.M., G.L. and M.X. designed research method, analysed data and conducted the material growth. D.W., J.Z., C.L., and G.M. conducted the material characterization and theoretical calculation. All authors contributed to the writing and editing.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wu, D., Min, T., Zhou, J. et al. Effect of Substrate symmetry on the dendrite morphology of MoS2 Film synthesized by CVD. Sci Rep 7, 15166 (2017). https://doi.org/10.1038/s41598-017-13238-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-13238-x
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.