Abstract
The strengthening of metallic biomaterials, such as Co–Cr–Mo and titanium alloys, is of crucial importance to the improvement of the durability of orthopedic implants. In the present study, we successfully developed a face-centered cubic (fcc) Co–Cr–Mo alloy with an extremely high yield strength (1400 MPa) and good ductility (12%) by multipass hot-rolling, which is suitable for industrial production, and examined the relevant strengthening mechanisms. Using an X-ray diffraction line-profile analysis, we revealed that a substantial increase in the number of stacking faults (SFs) in the fcc γ-matrix occurred at a greater height reduction (r), while physical modeling demonstrated that the contribution of the accumulated SFs (i.e., the reduction in SF spacing) with an increase in r successfully explains the entire strengthening behavior of the hot-rolled alloy. The present study sheds light on the importance of the SF strengthening mechanism, and will help to guide the design and manufacturing strategy for the high-strength Co–Cr–Mo alloys used in highly durable medical devices.
Similar content being viewed by others
Introduction
Given their superior corrosion and wear resistance, Co–Cr–Mo alloys are widely used in orthopedic implants such as total hip replacements and spinal systems1,2,3,4. Recently, much attention has been paid to the strengthening of these alloys to improve the durability of such implants because existing metallic biomaterials often fail during clinical use5, 6. Furthermore, high-strength materials open avenues for novel designs of biomedical devices to improve patients’ quality of life (QOL); for instance, low-profile spinal-system devices with a reduced rod diameter may potentially be realized with high-strength Co–Cr–Mo alloys.
Thermomechanical processing to control the microstructure is one approach to the strengthening of Co–Cr–Mo alloys; therefore, many studies have addressed the hot deformation processing of these alloys7,8,9. Notably, we previously discovered dynamic recrystallization (DRX), which occurs in these alloys during hot deformation at temperatures of more than 1273 K10,11,12. It was revealed that DRX significantly reduces the grain size of the face-centered cubic (fcc) γ-matrix phase to a minimum grain size of 0.6 µm10, resulting in a very high tensile yield strength of 1400 MPa, which is much higher than that reported in the literature11.
The anomalously low stability of the γ-phase in Co–Cr–Mo alloys is the origin of the significant grain refinement due to DRX. The stacking fault energy (SFE) (γ SFE ) is known to be closely related to the Gibbs energy difference between the fcc γ- and hexagonal close-packed (hcp) ε-phases13:
where ΔG γ → ε is the molar Gibbs energy change of the γ → ε phase transformation, ρ is the molar surface density along the {111} planes in the fcc structure, and σ γ/ε is the interfacial energy between the γ- and ε-phases. Because the equilibrium temperature between the γ- and ε-phases (T 0 at ΔG γ → ε = 0) is relatively high (around 1173 K) compared to that of other metallic materials, Co–Cr–Mo alloys undergo a peculiar hot deformation under a considerably low SFE of approximately 50 mJ m−2, which is comparable to or slightly higher than the room-temperature SFE (e.g. 20.5–42 mJ m−2) of austenitic twinning-induced plasticity (TWIP) steels14, or typical low-SFE alloys (the SFE generally increases with temperature and reaches sufficiently high values at hot-deformation temperatures, e.g., > 200 mJ m−2 for TWIP steels14). This leads to strain accumulation due to the presence of highly planar dislocation structures even at elevated temperatures, which leads to DRX with significant grain refinement12. However, relatively large strains are necessary to obtain homogeneous UFG microstructures via DRX, which is the main obstacle preventing the application of a DRX-dominated strategy to industrial production using actual manufacturing processes (forging, rolling, drawing, etc.).
In this work, we focus on multipass thermomechanical processing, which involves the repeated introduction of relatively small amounts of deformation (strain) at elevated temperatures and which is suitable for industrial production. Owing to the anomalously low SFE of these alloys, we can expect a remarkable increase in the dislocation density as a result of the process. Furthermore, strengthening due to planar defects is anticipated with this process. It was recently reported that, in some Mg alloys with an hcp structure, the tensile strength can be improved by introducing stacking faults (SFs) with nanoscale spacing on their basal (0001) plane15,16,17,18. The following model was proposed to account for the contributions of the SFs (σ SF )15, 16:
where k SF is a constant and L SF is the interspacing between SFs. Basal-SF-driven ultra-high strength was also reported in hcp titanium at the nanoscale19. For fcc metals and alloys, which include biomedical Co–Cr–Mo alloys, however, very few studies for quantitatively and directly evaluating the correlation between the SF formation and strength have been reported20, 21, although the strain-hardening behavior during tensile deformation has been well described in terms of SFE22,23,24,25,26. Moreover, unlike room-temperature deformation, a complicated microstructural evolution, which involves not only the introduction of lattice defects (dislocations/SFs) but also thermally activated processes such as DRX with grain refining, would occur at high temperatures. Therefore, a comprehensive study examining the microstructure development and its effect on the overall strengthening would be highly desirable to optimize its processing and properties and to obtain a deeper understanding of its microstructure–property relationships.
In this study, we performed multipass hot-rolling of a Co–Cr–Mo alloy and examined the tensile properties and hot-rolled microstructures in terms of the accumulated strain. It is difficult to quantitatively characterize the behaviors of dislocations and SFs in highly deformed microstructures by transmission electron microscopy (TEM). X-ray diffraction (XRD) line-profile analyses were therefore employed to study the evolution of the dislocation density and the number of SFs present during the process. On the basis of the generated data, we analyzed the contributions of the relevant strengthening mechanisms to illustrate how SFs add to the overall strength (in combination with other strengthening mechanisms) so that they may be used in an even wider application range in fcc alloys.
Results
Tensile properties of prepared hot-rolled specimens
Figure 1(a) shows the tensile stress–strain curves of the initial solution-treated specimen and those specimens that were hot-rolled to a cumulative height reduction (r) of up to 90%. They were obtained by tensile loading along the rolling direction (RD). The specimens exhibited apparent strain hardening and subsequent fractures without any clear macroscopic necking, which is typical of Co–Cr–Mo alloys. Figure 1(b) shows the corresponding strain-hardening behavior with respect to the true strain. Interestingly, the r = 30% and r = 60% specimens show almost identical strain-hardening rates, these being significantly higher than that of the initial specimen over the entire loading range. The strain-hardening rate of the r = 90% specimen, despite the remarkable increase in strength, was still higher than that of the initial specimen, although it decreased slightly from those of the hot-rolled specimens processed with the lower value of r. Figure 1(c,d) plots the tensile strength and elongation-to-failure of the prepared specimens as functions of equivalent strain (ε eq ) imposed during the multipass hot-rolling process. The initial specimen had a 0.2% proof stress of 485 MPa and a large elongation-to-failure of approximately 40%. The 0.2% proof stress increased monotonically with ε eq , while the ultimate tensile strength became saturated at higher ε eq values. The elongation-to-failure (uniform elongation) was found to decrease with an increase in ε eq , although those specimens that were hot-rolled up to ε eq = 1.06 (r = 60%) exhibited an almost identical ductility. However, a remarkably high 0.2% proof stress of around 1400 MPa and a good elongation-to-failure of 12% were obtained at ε eq = 2.66 (r = 90%). These results demonstrate that the present industrially feasible multipass processing method can realize a superior strength-ductility balance that is comparable to that of DRX-mediated UFG materials11.
Microstructural development during processing
The scanning electron microscopy-backscattered electron (SEM-BSE) image of the initial microstructure prior to hot-rolling, shown in Fig. 2(a), reveals a uniform equiaxed grain structure with annealing-twin boundaries (ATBs). In contrast, the morphology of the grains became unclear with an increase in r and was difficult to identify beyond r = 90% (Fig. 2(b–d)). We did not find precipitates (e.g., σ-phase and M23C6 carbide) in any of the specimens.
Figure 3 shows the results of the electron backscatter diffraction (EBSD) analysis of the specimens before and after multipass hot-rolling. Because 0.13 wt% of nitrogen incorporated into the alloy as a γ-phase stabilizing element sufficiently suppressed the athermal γ → ε martensitic transformation upon cooling after hot rolling27, only the fcc γ-phase was indexed in all the specimens, irrespective of the imposed r. The inverse pole figure (IPF) map of the initial microstructure exhibits uniform crystallographic orientations in each grain (Fig. 3(a1)). In contrast, in-grain misorientation was observed in the IPF maps of the hot-rolled specimens, and the degree of misorientation increased with r (Fig. 3(b1–d1)). The boundary maps and corresponding misorientation distributions are shown in Fig. 3(a2–d2) and Fig. 3(a3–d3), respectively. The initial specimen (Fig. 3(a2)) had many ATBs. The peak intensity at a misorientation of 60° in the misorientation distribution in Fig. 3(a3) indicates that approximately 55% of the boundaries in the initial sample corresponded to twin boundaries (TBs). The fraction of TBs significantly decreased upon hot-rolling; in contrast, the quantity of low-angle boundaries (LABs) increased upon hot-rolling, as shown in Fig. 3(e). A TB fraction of only 5% or less and a significant fraction of LABs (i.e., > 30%) were observed at ε eq = 2.66 (r = 90%). Figure 3(a4–d4) shows the grain-size distributions of the specimens at each r. Figure 3(f) shows the average grain size (d) for each specimen, determined by log-normal fitting of the EBSD data without considering TBs. Grain refinement with increasing ε eq was identified: the initial grain size of 128 μm was decreased to 53 μm at ε eq = 0.41 (r = 30%) and then gradually decreased to 39 μm at ε eq = 2.66 (r = 90%). A similar tendency was observed when TBs were taken into account in the grain-size calculations. These results indicate that grain refinement due to DRX and the development of deformation structures occurred simultaneously during the multipass hot-rolling.
Figure 4(a) shows a TEM bright-field image of the r = 90% specimen. A large number of planar defects, which intersect with each other, were found inside the γ-grains. High-resolution TEM (HRTEM) images and the corresponding fast Fourier transform (FFT) images (with the zone axis parallel to the [\(\bar{1}\text{10}\)]γ direction) of the same specimen are shown in Fig. 4(b,c). The planar defects observed in Fig. 4(b1) produced streaks formed along the <111> γ direction in the FFT image (Fig. 4(b2)), indicating the formation of SFs in the γ-matrix during the process. The interspacing of SFs was approximately 10 nm. In contrast, the interface shown in Fig. 4(c1,c2) showed extra diffraction spots, which arise from TB, in the corresponding FFT image (Fig. 4(c3). This indicates that deformation twinning (DT) occurred during the multipass hot-rolling, although EBSD could not index these nano-spaced twins owing to the resolution limit (Fig. 2(d2)). This is reasonable because the hot deformation of the present alloy occurs at an SFE comparable to those of TWIP steels at room temperature, as described in the Introduction.
X-ray diffraction (XRD) line-profile analysis
Figure 5(a) shows the XRD patterns obtained from the specimens before and after hot-rolling. Similar to the EBSD results, all of the specimens exhibited only fcc γ-peaks. The peak broadening induced by hot-rolling was clearly observed (see inset). XRD line-profile analysis based on the extended convolutional whole profile (eCMWP) fitting28, 29 was performed on the measured profiles. The eCMWP method was developed based on the conventional CMWP fitting method30, 31, and can be used to examine the evolution of the “SF probability” (SFP), in addition to dislocation structures. Figure 5(b) shows a typical example of the eCMWP fitting results for the initial specimen. The eCMWP fitting was conducted for the 111, 200, 220, 311, and 222 peaks of the γ-phase of each specimen. Although the initial specimen without deformation had very narrow diffraction peaks, which often made the fitting procedure difficult, the measured line profile (open symbols) fitted the eCMWP procedure (solid line) well.
Figure 6 shows the results of the eCMWP fitting analysis of the prepared specimens, plotted as a function of ε eq . As shown in Fig. 6(a), the dislocation density (ρ dis ) for Shockley partial dislocations was 1.2 × 1014 m–2 for the initial solution-treated specimen. The ρ dis value first strongly increased with ε eq and then became saturated at higher values of r. However, a very high dislocation density of 8.5 × 1015 m−2, which is almost two orders of magnitude higher than that of the initial specimen, was obtained for ε eq = 2.66 (r = 90%).
Figure 6(b) shows the evolution of the mean crystallite size (D), which defines the size of domains that coherently diffract incident X-rays30 during the hot-rolling process. The crystallite size for the initial specimen (D = 1462 nm) significantly decreased at the beginning of the hot-rolling (i.e., ε eq = 0.41 (r = 30%)), which correlates to the increase in the dislocation density. The D value then decreased slightly to approximately 50 nm via further deformation.
Figure 6(c) shows the dislocation arrangement parameter M as a function of ε eq . M values that are smaller or larger than unity indicate a strong or weak interaction between dislocations, respectively32. The initial specimens had an M value well above 1, while M decreased to less than 1 at ε eq = 0.41 (r = 30%). A similarly low M value was obtained at ε eq = 1.06 (r = 60%). The decrease in M indicates that the dislocations introduced during hot-rolling were rearranged into low-energy configurations. This may be explained by the development of LABs, as captured with EBSD analyses (Fig. 3). Further deformation (i.e., r = 90%) slightly increased M, indicating that newly formed excess lattice defects were introduced in the interiors surrounded by LABs in the later stage of the multipass hot-rolling process.
Finally, Fig. 6(d) shows the variation in the SFP (P SF ) as a function of ε eq . The eCMWP fitting procedure clearly captured the evolution of the SFs during the multipass hot-rolling process. P SF was almost zero up to ε eq = 0.41 (r = 30%), at which point it increased sharply with further increase in ε eq . P SF was substantially higher at ε eq = 2.66 (r = 90%), reaching approximately 1.6%, which indicates its dramatic influence on the mechanical behavior of the alloy. This result quantitatively demonstrates our hypothesis that a significant accumulation of SFs occurs even at high temperatures (e.g., 1473 K) if the alloy has a sufficiently low SFE.
Discussion
In general, there are four strengthening mechanisms at work in metallic materials33: solid-solution hardening, precipitation hardening, dislocation hardening, and grain refinement. The contributions of grain refinement (σ gb ) and dislocation density (σ dis ) are expressed by the Hall–Petch and Bailey–Hirsch (or Taylor) relationships, respectively:
where k is the Hall–Petch coefficient, d is the grain size, M Taylor is the Taylor factor, α is a constant, G is the shear modulus, and b is the value of the Burgers vector. In the present study, the hot-rolled specimens were prepared from the same alloy ingot, and we did not identify the secondary phase precipitation in any of the specimens (Fig. 2). Therefore, it is likely that the solid-solution hardening and precipitation hardening do not create a significant difference in the strengths of the prepared specimens. Thus, we defined the “calculated yield stress” (σ y,calc ) as follows:
where σ 0 is the friction stress. By summing the obtained results, σ y,calc for the prepared hot-rolled specimens was calculated and is plotted as a function of ε eq in Fig. 7(a). Table 1 presents the parameters used in the calculations34,35,36,37. The value of the Burgers vector (b p ) for Shockley partial dislocation was employed to determine the σ dis values. The σ 0 values (around 120 MPa) can be calculated using the Taylor factor (M Taylor ) and the critical resolved shear stress (τ CRSS = 54 MPa36), where σ 0 = M Taylor • τ CRSS . The M Taylor value was obtained for each specimen based on the results of the EBSD measurements; thus, the effect of the hot-rolling texture on the strength of the specimens could be incorporated into the analyses, although negligible anisotropy was found in the prepared specimens. These results indicate that the contribution of the grain-boundary (GB) strengthening increased from 35 MPa for the initial specimen to 64 MPa for ε eq = 2.66 (r = 90%). The increased dislocation density plays a more significant role in the overall strength, and its contribution increases remarkably with ε eq ; σ dis was calculated to be 455 MPa at ε eq = 2.66 (r = 90%). However, the obtained σ y,calc values were still much lower than the experimentally measured 0.2% proof stresses (σ 0.2). Therefore, we defined this discrepancy as the “extra strengthening” (σ extra ).
Interestingly, the σ extra values show an accelerated increase with an increase in ε eq (Fig. 7(b)). σ extra was approximately 743 MPa for the r = 90% (ε eq = 2.66) specimen, which is quite significant relative to the corresponding σ 0.2. Therefore, we can conclude that the strengthening obtained by the multipass hot-rolling process cannot be explained only in terms of the grain refinement and accumulated dislocations.
In contrast, in the present study, we discovered that the SFP (P SF ) dramatically increased, particularly at greater values of r (Fig. 6(d)). This indicates that plastic deformation in multipass hot rolling was predominantly accommodated by Shockley partial dislocations to generate SFs. A transition from perfect to partial dislocations was previously reported when the grain sizes and/or plastic deformation lie on nanoscale regimes38,39,40. In the present study, however, we used Co–Cr–Mo alloys with grain sizes of at least several tens of micrometers. Therefore, we were not able to clarify such a transition. Here, the relationship between the “extra strengthening” and the accumulated SFs is discussed. The P SF value, which was obtained by the eCMWP fitting procedure, can be defined as the frequency of SFs formed along the {111} plane of the γ-phase. Therefore, the “average value” of L SF can be determined using P SF (in percentage):
where d 111 is the interspacing between the {111}γ planes.
Figure 8(a) summarizes the L SF values determined from P SF as a function of ε eq . L SF was more than several tens of micrometers in the initial and r = 30% (ε eq = 0.41) specimens, indicating that very few SFs existed at the early stage of the multipass processing. However, the L SF value decreased dramatically with an increase in ε eq , and a very small L SF of approximately 10 nm was obtained after the 90% hot-rolling. The L SF value obtained here is in good agreement with that obtained from TEM observations (Fig. 4(b)), indicating that the present eCMWP method can provide reasonable quantitative evaluations of the L SF values.
Figure 8(b) plots the extra strengthening (σ extra ) as a function of 1/L SF in accordance with Eq. (2). A linear relationship was obtained, indicating that the extra strengthening defined above can be well described in terms of the model proposed by Jian et al.15, 16. Therefore, we can conclude that the SFs introduced during multipass hot-rolling contribute to the evolution of the extra strengthening. The intercept at 1/L SF = 0 is not zero (around 250 MPa), indicating that the extra strengthening does not originate solely from the accumulated SFs and that there are contributions from other than the above-mentioned mechanisms. Nitrogen doping may be a dominant contributing factor for this because it can increase the yield stress by 100–200 MPa27. Thus, the contribution of the SF strengthening is as high as 500 MPa at ε eq = 2.66 (r = 90%), which is quite significant relative to the overall strengthening due to multipass hot-rolling.
The physical model described by Eq. (2) was originally proposed for hcp Mg alloys with parallelly spaced SFs on their basal planes15, 16. To the best of our knowledge, the present study is the first to demonstrate that the model is applicable to fcc metals and alloys. It is interesting to note that the slope of the linear relationship (k SF ) in Fig. 8(b) is 6537 ± 342 MPa nm, which is of the same order but much larger than that obtained for a Mg alloy (k SF = 3780 MPa nm). In the model, k SF can be expressed as a function of the extra energy consumed by cutting through SFs when dislocations are impinged at the SFs16. Therefore, the large k SF value of the present alloy indicates that, compared with Mg alloys, SFs in fcc metals and alloys can act as a strong obstacle for dislocation gliding. Because SFs in the fcc crystals can form on all four {111} planes (i.e., (111), \((\overline{1}11)\), \((1\overline{1}1)\), and \((11\overline{1})\)), intersecting SFs occur during plastic deformation, as shown in Fig. 4(a). It was suggested from geometric arguments that the intersection of two SFs acts as a “dislocation dipole”41, providing a strong obstacle to dislocation, whereas SFs themselves are not strong barriers42. Therefore, the SF intersections resulting from multiple activations of SFs on different {111} planes during the process would play a considerable role in this strengthening mechanism compared with Mg alloys, in which SFs form almost parallel to each other on the basal (0001) plane. Further investigations are required to clarify these interactions.
Using the k SF value determined here, we ascertained the contributions of grain refinement (σ gb ), dislocations (σ dis ), and SFs (σ SF ), all of which were achieved by multipass hot-rolling, in the prepared specimens at different values of r (Fig. 9(a)). The σ gb values were as high as 50 MPa, irrespective of r. The increased dislocation density contributed to the yield stress significantly; the σ dis values increased steeply between the initial condition and r = 30%, and dislocations accounted for more than 80% of the strengthening effect caused by multipass hot-deformation in the specimens deformed up to r = 60% (Fig. 9(b)). In contrast, the SF strengthening was not evident in the initial and r = 30% specimens, but became significant at greater r. Surprisingly, the contribution of the SFs at r = 90% (around 500 MPa) is comparable or even superior to that from the dislocations. Thus, the increase in the SF width, which is preferred under a large external stress43, suitably explains the r-dependence of σ SF . These results shed light on the importance of the SF strengthening, which has not yet been directly considered, and will help in guiding the design and manufacturing strategy for high-strength fcc alloys using lattice defects. Furthermore, the eCMWP-based XRD line-profile analysis employed in this study is a powerful technique capable of statistically determining SF densities and modeling the contribution to the strength.
It is also noteworthy that the formation of ATBs and DTs was observed in the initial solution-treated (Fig. 3(a2)) and hot-rolled specimens (Fig. 4(c1–c3)), respectively. Recent studies have reported that TBs play an important role in the strengthening of metals33, 44,45,46,47. It was shown that the twin thickness (i.e., the spacing between two adjoining TBs) affects the yield strength in the same way as the grain boundaries, i.e., they conform to a Hall–Petch relationship33, 46. Although the Hall–Petch coefficient for TBs, which is similar to33 or often one order of magnitude smaller than that for grain boundaries48, 49, in these alloys is unknown at present, the contribution of ATBs was found to be minimal (no more than around 10 MPa) when ATBs were taken into account in the grain-size calculation using the EBSD results. Furthermore, careful TEM observations identified that the fraction of nanoscale DTs was not high in the present hot-rolled specimens; the fact that the extra strengthening defined above fully complied with Eq. (2), as shown in Fig. 8(b), implies that the formation of SFs was dominant over DT and that the effect of DTs on the strength is almost negligible in the present hot-rolled specimens. It is well known that there are critical stresses leading to the initiation of DT43, 50, 51 as well as DRX52,53,54. The critical stress for DT is regarded as being higher than that for DRX, as grain refinement due to DRX occurred during the multipass hot-rolling process (Fig. 3(f)). The occurrence of DRX is involved in flow softening, which also inhibits DT. The higher frequency of SFs, relative to DTs, is thus likely related to the competitive behavior between DT and DRX. Because the flow stress at high temperatures is highly dependent on the deformation conditions, optimizing the processing parameters (e.g., using a lower deformation temperature and a higher strain rate) may lead to an increase in the number of SFs and nanotwins, while manipulating the state of the lattice defects within the fcc γ-matrix may yield a more suitable balance of the multiple strengthening mechanisms for overcoming the strength–ductility tradeoff.
The SF strengthening mechanism discussed here assumes the cutting of SFs by dislocations, assuming its contribution to be proportional to 1/L SF 16. In contrast, the GB or TB strengthening mechanisms are explained in terms of dislocation pile-ups, resulting in the Hall-Petch relationship33, 46. That is, the interaction with the dislocations differentiates the SF strengthening from the GB and TB strengthening mechanisms. From a practical viewpoint, it is generally difficult to attain homogeneous ultrafine-grained microstructures or nanostructures through conventional manufacturing procedures. Therefore, severe plastic deformation (SPD) techniques, such as equal channel angular pressing (ECAP) and high-pressure torsion (HPT)55,56,57,58, are generally employed. Similarly, nanotwinned metals are produced by means of electrodeposition47, 59, sputtering60, 61, or dynamic plastic deformation62. Therefore, it is still difficult to fully employ these two mechanisms in bulk forms via industrial production. The SF strengthening, in contrast, can be applied to conventional manufacturing processes and realizes significant strengthening, as demonstrated in the present study. Applicability to industrial production is a major advantage of SF strengthening.
Nanostructured materials often exhibit unusual deformation behaviors, such as large elastic strain63 and grain-boundary-mediated plasticity64, 65. It is well known that lattice defects in the parent γ-matrix can act as precursors of ε-martensite. Because this strain-induced γ → ε martensitic transformation is responsible for the strain-hardening behavior of biomedical Co–Cr–Mo alloys66,67,68,69, these lattice defects in the parent γ-phase might enhance the strain-hardening ability of an alloy (see Fig. 1(b)), thus avoiding the early onset of plastic instability and leading to good ductility. Furthermore, SFs themselves act as a barrier against gliding dislocations, in the same was as TBs20. The dislocation–SF interactions and the correlation between the preexisting lattice defects and tensile deformation behavior will be described in a follow-up paper.
In conclusion, we conducted multipass hot-rolling of a biomedical Co–Cr–Mo alloy with a single fcc structure and investigated the origin of its significant strengthening based on a quantitative examination of microstructure evolution by electron microscopy and XRD. The strength after multipass hot-rolling linearly increased with r and eventually reached approximately 1400 MPa for the 0.2% proof stress at r = 90% while maintaining a large elongation of 12%. Grain refinement due to DRX and the development of deformation structures occurred simultaneously during the multipass hot-rolling, although the observed reduction in grain size had much less influence on the overall strength. XRD line-profile analyses revealed that the dislocation density of the initial solution-treated specimen (1.2 × 1014 m−2) first strongly increased with r and then became saturated at a very high dislocation density of 8.5 × 1015 m−2. The increased dislocation density caused the significant strengthening observed in the hot-rolled specimen. Notably, by using eCMWP analysis, we demonstrated a dramatic increment in the SFP during the multipass hot-rolling process. This corresponds to the significant reduction in L SF to approximately 10 nm at r = 90%. Consequently, the contribution of SFs to overall strengthening became significant at greater values of r, although it was not evident at lower r. The quantitative evaluation of strengthening mechanisms revealed the first direct evidence of “stacking fault strengthening” in biomedical Co–Cr–Mo alloys and described the manipulation of SFs via thermomechanical processing, which will help in guiding the design and manufacturing strategy for high-strength Co–Cr–Mo alloys.
Methods
Sample preparation
A biomedical Co–28Cr–6Mo–0.13 N (Cr: 28.20, Mo: 5.92, N: 0.126, C: 0.04, Mn: 0.62, Si: 0.50, Co: bal. (wt%)) alloy, which satisfies the specifications of the ASTM F1537 standard, was prepared by conventional high-frequency induction melting. An ingot of the alloy weighing around 30 kg (around 150 mm in diameter) was subjected to homogenizing heat treatment and then hot-forged at 1473 K. The alloy was then solution-treated at 1473 K for 15 min, followed by forging at 1473 K to produce a plate specimen with a thickness (t) of 15 mm. The specimens for hot-rolling (25 mm in width, 35 mm in length, and 15 mm in thickness) were cut from the plates with an electric discharge machine (EDM) and subjected to solution heat treatment at 1473 K for 10 min. Multipass hot-rolling was conducted with the solution-treated specimens. The specimens were heated to 1473 K and then rolled to produce a height reduction of around 1 mm per pass. This process was repeated to obtain cumulative height reductions (r) of 30%, 60%, and 90%. The r values were converted to equivalent strains (ε eq ) by using the following equation:
To maintain a sufficiently high specimen temperature to prevent fractures during deformation, interval heating was performed at 1473 K for 5 min every two passes (plate thickness t ≥ 10 mm) or every pass (t ≤ 10 mm). The specimens were air-cooled after the hot-rolling.
Tensile tests
Uniaxial tensile tests of the initial and hot-rolled specimens were performed at room temperature. Flat samples with a gauge section of 2.0 × 1.0 mm2 and gauge length of 10.5 mm were prepared by EDM with the longitudinal axis parallel to the rolling direction (RD). The specimens were strained to failure at a nominal strain rate of 1.6 × 10−4 s−1. At least three samples for each material were subjected to the tensile test to confirm reproducibility.
Microstructure observations
Scanning electron microscopy (SEM) observations and electron backscatter diffraction (EBSD) analyses were conducted with a JEOL JSM-7100F and an FEI XL30S-FEG operated at 15 kV and 20 kV, respectively. EBSD data were collected with a step size of 0.2 µm and analyzed using a TSL OIM system. The observations were made on the planes parallel to the rolling plane and at the middle thickness of the rolled specimens. Samples for the above microstructural analyses were ground with emery paper, polished with a 1-µm alumina suspension, and then finished with a 0.04-µm colloidal silica suspension. Transmission electron microscopy (TEM) observations were made using an FEI TITAN3 G2 60-300 S/TEM operating at 300 kV with a double spherical aberration (Cs) corrector. The TEM samples were prepared by cutting a 3-mm-diameter disk from each alloy specimen and then grinding it to form a thin film using a dimple grinder (Gatan Model 656). Next, we prepared thin foils through ion-beam milling of the disks (Gatan Model 691, PIPS).
X-ray diffraction (XRD) line-profile analyses
XRD measurements were performed on the initial and hot-rolled specimens by using an X-ray diffractometer (D8 ADVANCE, Bruker AXS) equipped with a Cu-Kα radiation source. The Bragg–Brentano (2θ–θ) geometry was employed for obtaining line profiles for the eCMWP analyses. Because both the X-ray scattering of white X-rays and the Cu-Kα2 component distort the line profile, incident X-rays were monochromated to the Cu-Kα1 line (0.15406 nm) with a Johansson-type monochromator having a quartz-101 reflection. Instrumental line profiles (I i ) were obtained from an annealed copper specimen70. The eCMWP fitting was performed using CMWP-fit, an open-source software package. The details of the eCMWP method are briefly described in the Supplementary Information.
References
Ashman, R. B. et al. Mechanical testing of spinal instrumentation. Clin. Orthop. Relat. Res. 227, 113–25 (1988).
Buford, A. & Goswami, T. Review of wear mechanisms in hip implants: Paper I - General. Mater. Des. 25, 385–393 (2004).
Chiba, A., Kumagai, K., Nomura, N. & Miyakawa, S. Pin-on-disk wear behavior in a like-on-like configuration in a biological environment of high carbon cast and low carbon forged Co–29Cr–6Mo alloys. Acta Mater. 55, 1309–1318 (2007).
Niinomi, M., Nakai, M. & Hieda, J. Development of new metallic alloys for biomedical applications. Acta Biomater. 8, 3888–3903 (2012).
Gilbert, J. L., Buckley, C. A., Jacobs, J. J., Bertin, K. C. & Zernich, M. R. Intergranular corrosion-fatigue failure of cobalt-alloy femoral stems. A failure analysis of two implants. J Bone Jt. Surg Am 76, 110–115 (1994).
Yamanaka, K. et al. Analysis of the fracture mechanism of Ti–6Al–4V alloy rods that failed clinically after spinal instrumentation surgery. Spine (Phila. Pa. 1976). 40, E767–E773 (2015).
Shi, L., Northwood, D. O. & Cao, Z. Alloy design and microstructure of a biomedical Co–Cr alloy. J. Mater. Sci. 28, 1312–1316 (1993).
Saldívar-García, A. J. & López, H. F. Microstructural effects on the wear resistance of wrought and as-cast Co–Cr–Mo–C implant alloys. J. Biomed. Mater. Res. - Part A 74, 269–274 (2005).
Lippard, H. E. & Kennedy, R. L. in Cobalt-Base Alloys for Biomedical Applications (eds. Disegi, J. A., Kennedy, R. L. & Pilliar, R.) 98–107 (American Society for Testing and Materials, 1999).
Yamanaka, K., Mori, M., Kurosu, S., Matsumoto, H. & Chiba, A. Ultrafine grain refinement of biomedical Co–29Cr–6Mo alloy during conventional hot-compression deformation. Metall. Mater. Trans. A 40, 1980–1994 (2009).
Yamanaka, K., Mori, M. & Chiba, A. Enhanced Mechanical Properties of As-Forged Co–Cr–Mo–N Alloys with Ultrafine-Grained Structures. Metall. Mater. Trans. A 43, 5243–5257 (2012).
Yamanaka, K., Mori, M. & Chiba, A. Origin of significant grain refinement in Co–Cr–Mo alloys without severe plastic deformation. Metall. Mater. Trans. A 43, 4875–4887 (2012).
Olson, G. B. & Cohen, M. A General Mechanism of Martensitic Nucleation: Part I. General Concepts and the FCC → HCP Transformation. Metall. Trans. A 7, 1897–1904 (1976).
Curtze, S., Kuokkala, V.-T., Oikari, A., Talonen, J. & Hänninen, H. Thermodynamic modeling of the stacking fault energy of austenitic steels. Acta Mater. 59, 1068–1076 (2011).
Jian, W. W. et al. Ultrastrong Mg Alloy via Nano-spaced Stacking Faults. Mater. Res. Lett. 1, 61–66 (2013).
Jian, W. W. et al. Physics and model of strengthening by parallel stacking faults. Appl. Phys. Lett. 103, 133108 (2014).
Jiao, Y. et al. Enhancing the performance of Mg-based implant materials by introducing basal plane stacking faults. J. Mater. Chem. B 3, 7386–7400 (2015).
Xu, C. et al. Microstructure, mechanical and damping properties of Mg–Er–Gd–Zn alloy reinforced with stacking faults. Mater. Des. 79, 53–59 (2015).
Yu, Q., Li, S., Minor, A. M., Sun, J. & Ma, E. High-strength titanium alloy nanopillars with stacking faults and enhanced plastic flow. Appl. Phys. Lett. 100, 63109 (2012).
Tian, Y. Z. et al. Significant contribution of stacking faults to the strain hardening behavior of Cu-15%Al alloy with different grain sizes. Sci. Rep. 5, 16707 (2015).
Otto, F. et al. The influences of temperature and microstructure on the tensile properties of a CoCrFeMnNi high-entropy alloy. Acta Mater. 61, 5743–5755 (2013).
Rohatgi, A., Vecchio, K. S. & Gray, G. T. The influence of stacking fault energy on the mechanical behavior of Cu and Cu-Al alloys: Deformation twinning, work hardening, and dynamic recovery. Metall. Mater. Trans. A 32, 135–145 (2001).
Frommeyer, G., Brüx, U. & Neumann, P. Supra-Ductile and High-Strength Manganese-TRIP/TWIP Steels for High Energy Absorption Purposes. ISIJ Int. 43, 438–446 (2003).
Curtze, S. & Kuokkala, V.-T. Dependence of tensile deformation behavior of TWIP steels on stacking fault energy, temperature and strain rate. Acta Mater. 58, 5129–5141 (2010).
Dumay, A., Chateau, J. P., Allain, S., Migot, S. & Bouaziz, O. Influence of addition elements on the stacking-fault energy and mechanical properties of an austenitic Fe–Mn–C steel. Mater. Sci. Eng. A 483–484, 184–187 (2008).
Lee, T.-H., Shin, E., Oh, C.-S., Ha, H.-Y. & Kim, S.-J. Correlation between stacking fault energy and deformation microstructure in high-interstitial-alloyed austenitic steels. Acta Mater. 58, 3173–3186 (2010).
Yamanaka, K., Mori, M. & Chiba, A. Effects of nitrogen addition on microstructure and mechanical behavior of biomedical Co–Cr–Mo alloys. J. Mech. Behav. Biomed. Mater. 29, 417–426 (2014).
Balogh, L., Tichy, G. & Ungár, T. Twinning on pyramidal planes in hexagonal close packed crystals determined along with other defects by X-ray line profile analysis. J. Appl. Crystallogr. 42, 580–591 (2009).
Balogh, L., Ribárik, G. & Ungár, T. Stacking faults and twin boundaries in fcc crystals determined by x-ray diffraction profile analysis. J. Appl. Phys. 100, 23512 (2006).
Ungár, T., Gubicza, J., Ribárik, G. & Borbély, A. Crystallite size distribution and dislocation structure determined by diffraction profile analysis: Principles and practical application to cubic and hexagonal crystals. J. Appl. Crystallogr. 34, 298–310 (2001).
Ribárik, G., Gubicza, J. & Ungár, T. Correlation between strength and microstructure of ball-milled Al–Mg alloys determined by X-ray diffraction. Mater. Sci. Eng. A 387–389, 343–347 (2004).
Wilkens, M. The determination of density and distribution of dislocations in deformed single crystals from broadened X-ray diffraction profiles. Phys. Status Solidi A 2, 359–370 (1970).
Lu, K., Lu, L. & Suresh, S. Strengthening materials by engineering coherent internal boundaries at the nanoscale. Science 324, 349–352 (2009).
Mori, M., Yamanaka, K., Sato, S., Wagatsuma, K. & Chiba, A. Microstructures and Mechanical Properties of Biomedical Co–29Cr–6Mo–0.14N Alloys Processed by Hot Rolling. Metall. Mater. Trans. A 43, 3108–3119 (2012).
Kamikawa, N., Huang, X., Tsuji, N. & Hansen, N. Strengthening mechanisms in nanostructured high-purity aluminium deformed to high strain and annealed. Acta Mater. 57, 4198–4208 (2009).
Hagihara, K., Nakano, T. & Sasaki, K. Anomalous strengthening behavior of Co–Cr–Mo alloy single crystals for biomedical applications. Scr. Mater. 123, 149–153 (2016).
Yamanaka, K., Mori, M. & Chiba, A. Mechanical properties of as-forged Ni-free Co–29Cr–6Mo alloys with ultrafine-grained microstructure. Mater. Sci. Eng. A 528, 5961–5966 (2011).
Wang, L. et al. In Situ Observation of Dislocation Behavior in Nanometer Grains. Phys. Rev. Lett. 105, 135501 (2010).
Wang, L., Zhang, Z. & Han, X. In situ experimental mechanics of nanomaterials at the atomic scale. NPG Asia Mater. 5, e40 (2013).
Wang, L., Zheng, K., Zhang, Z. & Han, X. Direct atomic-scale imaging about the mechanisms of ultralarge bent straining in Si nanowires. Nano Lett. 11, 2382–2385 (2011).
Ashbee, K. H. G. Intersecting stacking faults in face-centered cubic lattices. Acta Metall. 15, 1129–1131 (1967).
Rajan, K. & Vander Sande, J. B. Room temperature strengthening mechanisms in a Co–Cr–Mo–C alloy. J. Mater. Sci. 17, 769–778 (1982).
Byun, T. S. On the stress dependence of partial dislocation separation and deformation microstructure in austenitic stainless steels. Acta Mater. 51, 3063–3071 (2003).
Yue, Y., Zhang, Q., Yang, Z., Gong, Q. & Guo, L. Study of the Mechanical Behavior of Radially Grown Fivefold Twinned Nanowires on the Atomic Scale. Small 12, 3503–3509 (2016).
Yue, Y. et al. In Situ Observation of Twin Boundary Sliding in Single Crystalline Cu Nanowires. Small 13, 1604296 (2017).
Shen, Y. F., Lu, L., Lu, Q. H., Jin, Z. H. & Lu, K. Tensile properties of copper with nano-scale twins. Scr. Mater. 52, 989–994 (2005).
Lu, K. Stabilizing nanostructures in metals using grain and twin boundary architectures. Nat. Rev. Mater. 1, 16019 (2016).
Liang, Z. Y., Li, Y. Z. & Huang, M. X. The respective hardening contributions of dislocations and twins to the flow stress of a twinning-induced plasticity steel. Scr. Mater. 112, 28–31 (2016).
Zhou, P., Liang, Z. Y., Liu, R. D. & Huang, M. X. Evolution of dislocations and twins in a strong and ductile nanotwinned steel. Acta Mater. 111, 96–107 (2016).
Laplanche, G., Kostka, A., Horst, O. M., Eggeler, G. & George, E. P. Microstructure evolution and critical stress for twinning in the CrMnFeCoNi high-entropy alloy. Acta Mater. 118, 152–163 (2016).
Cao, Y. et al. Applied stress controls the production of nano-twins in coarse-grained metals. Appl. Phys. Lett. 101, 231903 (2012).
Poliak, E. I. & Jonas, J. J. A one-parameter approach to determining the critical conditions for the initiation of dynamic recrystallization. Acta Mater. 44, 127–136 (1996).
Poliak, E. I. & Jonas, J. J. Initiation of Dynamic Recrystallization in Constant Strain Rate Hot Deformation. ISIJ Int. 43, 684–691 (2003).
Najafizadeh, A. & Jonas, J. J. Predicting the Critical Stress for Initiation of Dynamic Recrystallization. ISIJ Int. 46, 1679–1684 (2006).
Valiev, R. Z., Islamgaliev, R. K. & Alexandrov, I. V. Bulk nanostructured materials from severe plastic deformation. Prog. Mater. Sci. 45, 103–189 (2000).
Valiev, R. Z. et al. Producing Bulk Ultrafine-Grained Materials by Severe Plastic Deformation: Ten Years Later. JOM 68, 1216–1226 (2016).
Estrin, Y. & Vinogradov, A. Extreme grain refinement by severe plastic deformation: A wealth of challenging science. Acta Mater. 61, 782–817 (2013).
Azushima, A. et al. Severe plastic deformation (SPD) processes for metals. CIRP Ann. - Manuf. Technol. 57, 716–735 (2008).
Lu, L. et al. Ultrahigh Strength and High Electrical Conductivity in Copper. Science 304, 422–426 (2004).
Bufford, D. C., Wang, Y. M., Liu, Y. & Lu, L. Synthesis and microstructure of electrodeposited and sputtered nanotwinned face-centered-cubic metals. MRS Bull. 41, 286–291 (2016).
Zhang, X. et al. High-strength sputter-deposited Cu foils with preferred orientation of nanoscale growth twins. Appl. Phys. Lett. 88, 173116 (2006).
Qin, E. W., Lu, L., Tao, N. R., Tan, J. & Lu, K. Enhanced fracture toughness and strength in bulk nanocrystalline Cu with nanoscale twin bundles. Acta Mater. 57, 6215–6225 (2009).
Wang, L. et al. In situ atomic-scale observation of continuous and reversible lattice deformation beyond the elastic limit. Nat. Commun. 4, 2413 (2013).
Shan, Z. et al. Grain Boundary-Mediated Plasticity in Nanocrystalline Nickel. Science 305, 654–657 (2004).
Wang, L. et al. Grain rotation mediated by grain boundary dislocations in nanocrystalline platinum. Nat. Commun. 5, 4402 (2014).
Salinas-Rodriguez, A. & Rodriguez-Galicia, J. L. Deformation behavior of low-carbon Co–Cr–Mo alloys for low-friction implant applications. J. Biomed. Mater. Res. 31, 409–419 (1996).
Huang, P. & López, H. F. Strain induced ε-martensite in a Co–Cr–Mo alloy: Grain size effects. Mater. Lett. 39, 244–248 (1999).
Koizumi, Y. et al. Strain-induced martensitic transformation near twin boundaries in a biomedical Co–Cr–Mo alloy with negative stacking fault energy. Acta Mater. 61, 1648–1661 (2013).
Mani, A. & Lopez, H. F. Deformation induced FCC to HCP transformation in a Co–27Cr–5Mo–0.05C alloy. Mater. Sci. Eng. A 528, 3037–3043 (2011).
Sato, S., Kwon, E. P., Imafuku, M., Wagatsuma, K. & Suzuki, S. Microstructural characterization of high-manganese austenitic steels with different stacking fault energies. Mater. Charact. 62, 781–788 (2011).
Acknowledgements
We thank Professor Tadashi Furuhara at the Institute for Materials Research, Tohoku University, for his fruitful discussions. The authors thank Yuichiro Hayasaka for help with the TEM observations. This research was supported by the Grant-in-Aid for Young Scientists (A) [No. 17H04957] and (B) [No. 26870050, 16K21567] from the Japan Society for the Promotion of Science (JSPS); the Amada Foundation [No. AF-2016034]; and Tohoku University microstructural characterization platform as a program of "Nanotechnology Platform" of the Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan.
Author information
Authors and Affiliations
Contributions
K.Y. and M.M. conceived and designed the experiments and contributed to the preparation of the alloy, performed the experimental analysis, and wrote the manuscript. S.S. performed the XRD measurements and analyzed the data. A.C. provided technical support and conceptual advice. All the authors contributed to the interpretation of the experimental data, discussed the results, and commented on the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yamanaka, K., Mori, M., Sato, S. et al. Stacking-fault strengthening of biomedical Co–Cr–Mo alloy via multipass thermomechanical processing. Sci Rep 7, 10808 (2017). https://doi.org/10.1038/s41598-017-10305-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-10305-1
This article is cited by
-
Hot Deformation Behavior and Microstructure of Cast Ni-Based Superalloy IN-100 Based on the Processing Map
Metallurgical and Materials Transactions A (2023)
-
Development of Low-Yield Stress Co–Cr–W–Ni Alloy by Adding 6 Mass Pct Mn for Balloon-Expandable Stents
Metallurgical and Materials Transactions A (2021)
-
Co–Cr–Mo alloy fabricated by laser powder bed fusion process: grain structure, defect formation, and mechanical properties
The International Journal of Advanced Manufacturing Technology (2021)
-
Correlating work hardening with co-activation of stacking fault strengthening and transformation in a high entropy alloy using in-situ neutron diffraction
Scientific Reports (2020)
-
Strain-induced martensitic transformation in biomedical Co–Cr–W–Ni alloys
Rare Metals (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.