Abstract
Conducting organic metal chalcogenides (OMCs) have attracted considerable interest for their superior electrical properties and fascinating functions. However, the electronic structural and functional regulation of OMCs are typically limited to the combination of monometallic nodes and graphene-like ligands. Here, we report a family of bimetallic OMCs ([CuAgx(C6S6)]n, x = 4 or 2) synthesized via selective metal metathesis and oxidation transformation. Both OMCs have alternatively stacked one-dimensional (1D) copper-dithiolene chains and 2D Ag-S networks, which can synergistically serve as charge transport pathways, rendering these bimetallic materials highly conductive. The incorporation of heterometallic nodes turned nonmagnetic [Ag5(C6S6)]n into paramagnetic metallic [CuAg4(C6S6)]n, which exhibited a coherence-incoherence crossover in magnetic susceptibility measurements and an unusually large Sommerfeld coefficient, reminiscent of the characteristics of Kondo lattice. This work opens up an avenue for tailoring the electronic structures of OMCs and provides a platform for studying the dichotomy between electronic localization and itinerancy.
Similar content being viewed by others
Introduction
Organic metal chalcogenides (OMCs) represent a burgeoning class of organic–inorganic hybrid materials constructed with continuous M-X (X = S, Se, Te) networks that are further covalently connected by organic ligands and extend into periodic one-dimensional (1D), two-dimensional (2D), or three-dimensional (3D) frameworks1,2,3,4. Conducting OMCs have currently received significant attention for their tailorable structures5,6 and superior electrical properties6,7,8 as well as fascinating features of quantum phenomena9,10. Growing efforts have been dedicated to exploring conducting OMCs by varying the organic and metal building blocks. To date, by combining single-metal nodes (e.g., Fe, Ni, Cu, or Ag, etc.) and highly symmetrical aromatic ligands, a large number of conductive OMCs with varying structural topologies have been produced11,12. However, these monometallic OMCs generally impose some unavoidable disadvantages in manipulating their electronic structures and regulating the functions of interest, thus limiting the maximal potential of this emerging class of organic–inorganic hybrid materials.
From the structural perspective, the integration of bimetallic nodes inside OMCs could be an effective method to tailor the targeting structural topologies and introduce additional functionalities. However, the kinetic inertness and fast reaction rate of the metal–chalcogen bond formation reaction13 make the direct synthesis impractical, since the reaction of ligands with different metal ions would inevitably suffer from the separate growth of OMCs in solution. Encouragingly, post-synthetic modification provides an alternative scheme for accessing materials when the direct synthesis route fails14,15. For example, in analogous systems like transition metal dichalcogenides (TMD), doping of TM (Fe, Co, and Ni) atoms has been experimentally demonstrated to be a promising way to achieve functional programming16,17. However, unlike the ionic TMD, OMC is a covalent compound and its skeleton is maintained by robust covalent M-X bonds12,18, which makes the energy barrier of embedding a second metal atom into pristine OMC lattices very steep. Consequently, the synthesis of bimetallic OMCs has been challenging and has not been reported hitherto.
Here, the original bimetallic OMC, [CuAg4(C6S6)]n (CuAg4BHT, BHT = benzenehexathiol), was synthesized via selective metal metathesis of Ag5BHT, wherein only the square-planar Ag ions were precisely substituted by Cu ions. In particular, under the delicate oxidation regulation, CuAg4BHT can be converted to another bimetallic species, CuAg2BHT. The crystal structures of both OMCs were solved with atomic resolution, revealing 3D lamellar structures composed of alternatively stacked 1D copper-dithiolene chains and 2D Ag-S networks. Significantly, ultraviolet-photoelectron spectroscopy (UPS) and band structure calculations evidence the intrinsic metallic character of both materials. In addition, combining magnetic susceptibility and specific heat measurements, a coherence-incoherence crossover was observed in CuAg4BHT, suggesting that this OMC would be an unprecedented candidate for a heavy Fermi liquid with Kondo lattice behavior. Our findings open up an avenue for the design of bimetallic OMCs with unusual structural topologies and tailor-made functionalities, and provide an attractive platform to search for exotic states of matter.
Results
Synthesis and structural characterization
As shown in Fig. 1, both the direct synthesis and post-synthetic metathesis were attempted to synthesize heterometallic OMCs. Under homogeneous solution condition, when BHT reacted with a mixture of the two metal ions, no crystalline product could be isolated (Supplementary Table 1 and Supplementary Fig. 1), due to the divergent OMC formation kinetics of two metal ions with BHT. To achieve controlled incorporation of two metal nodes, we envisioned that the post-synthetic metathesis approach with highly crystalline Ag5BHT (ref. 19) and Cu4BHT (ref. 20) as the parent frameworks might work, since these two well-defined OMCs possess similar building blocks and coordination geometries (Fig. 1). We screened various synthetic parameters, including temperature, reaction time, stoichiometry, and metal salt types to find optimal conditions. However, due to the appearance of silver metal, the transmetalation reactions of Cu4BHT are always unsuccessful (Supplementary Note 1). Under optimized conditions, the reaction of Ag5BHT with Cu(NO3)2·3H2O could afford a highly crystalline product, CuAg4BHT (Supplementary Table 2 and Supplementary Fig. 2).
Previous studies have shown that the structural transformation achieved by chemical oxidation was a synthetic shortcut to prepare OMCs21. To testify the universality of this chemical transformation strategy for OMCs, valence-variable cerium ammonium nitrate ((NH4)2Ce(NO3)6, CAN) was employed as the oxidizing reagent here (Methods, Supplementary Fig. 6). When two equivalents of CAN were added to CuAg4BHT, we found that CuAg4BHT can be completely transformed into another bimetallic species, CuAg2BHT (Fig. 1), which is evidenced by powder X-ray diffraction (PXRD) and other structural characterizations (see the following section for details).
X-ray photoelectron spectroscopy (XPS) reveals that C, S, Cu, and Ag present within both samples (Supplementary Fig. 7), indicating the absence of solvent molecules or other counterions. The thermogravimetric analysis shows that CuAgxBHTs are stable up to 300 °C and solvent molecules are absent in the final products (Supplementary Fig. 8). The energy dispersive spectroscopy disclosed the uniform distribution of S, Cu, and Ag across the samples (Supplementary Fig. 9), suggesting that the samples prepared herein were not physical mixtures of two monometallic OMCs. The inductively coupled plasma optical emission spectrometry (ICP-OES) and Electron Probe Micro-analyzer (EPMA) results indicated that the atomic ratios of Cu:Ag:S in CuAg4BHT and CuAg2BHT are close to 1:4:6 and 1:2:6, respectively (Supplementary Fig. 4). Consequently, their chemical formulas can be estimated as [CuAg4(C6S6)]n and [CuAg2(C6S6)]n, respectively.
Both CuAgxBHT samples display rod-like morphologies with lengths varying from 500 nm to over 2 µm and widths around 50 nm, as shown in scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images (Fig. 2c–f). In the high-resolution TEM images of CuAg4BHT and CuAg2BHT nanorods (Fig. 2g, h), two series of lattice fringes with interlayer distances of 4.4 and 4.1 Å were clearly discerned, suggesting the high crystallinity of CuAgxBHT nanorods, which is verified by the PXRD observations (Fig. 2a, b).
a, b Rietveld refinement of PXRD patterns for CuAg4BHT (a) and CuAg2BHT (b) from a synchrotron source (λ = 0.69003 Å). c–f The SEM images of CuAg4BHT (c) and CuAg2BHT (d). The TEM images of CuAg4BHT (e) and CuAg2BHT (f). g, h HRTEM images of CuAg4BHT (g) and CuAg2BHT (h). Source data are provided as a Source Data file.
The high-resolution PXRD data of CuAg4BHT obtained with synchrotron radiation displayed sharp diffraction peaks from 2θ = 5° to 30° with the d spacings similar to what observed in Ag5BHT (Supplementary Table 3), showing that these two materials are structurally similar. As the PXRD data show a lot of possibilities for the space group of this material, rotation electron diffraction (RED) was performed on CuAg4BHT microcrystals to determine the cell parameter and space group accurately. First, a set of initial unit cells was obtained from the 3D reciprocal lattice reconstructed from the RED data (Supplementary Fig. 10). The results show that CuAg4BHT crystallizes in the monoclinic P21/c space group with cell parameters of a = 4.28 Å, b = 8.75 Å, c = 14.48 Å, and β = 94.3°. Based on this initial unit cell parameters and synchrotron PXRD data, the structure of CuAg4BHT was solved with the charge flipping algorithm (a detailed description of the structure-solving process is presented in Supplementary Note 2). The final Rietveld refinement converges with Rp = 3.57%, Rwp = 4.64%. The crystal structure of CuAg2BHT was directly solved based on synchrotron PXRD data with the final Rietveld refinement converging with Rp = 2.21%, Rwp = 2.62%. CuAg2BHT crystallizes in a triclinic P−1 space group with cell parameters of a = 3.58 Å, b = 8.43 Å, c = 8.80 Å, α = 62.1°, β = 86.1°, and γ = 80.8°. The small differences between the experimental PXRD patterns and the simulated ones (Fig. 2a, b) confirm the accuracy of the crystal structures of CuAgxBHT. The detailed crystallography data are provided in Table 1 and Supplementary Table 4. In Fig. 2a, b, no diffraction peaks belonging to crystalline impurities could be observed, and the calculated results are in good agreement with the experimentally observed PXRD data, verifying the phase purity of CuAgxBHT samples. In addition, the EPMA, ICP-OES and elemental analysis results of CuAgxBHT powder samples are highly consistent with the formulas obtained based on crystal structure analysis and further confirmed the purity unambiguously (Supplementary Table 5).
Due to the shorter Cu-S bond lengths (2.247(8), 2.214(8) Å) in CuAg4BHT, the substitution of the square-planar Ag atoms leads to an obvious shrink in cell volume for CuAg4BHT (540.9 Å3) compared to that of Ag5BHT (551.7 Å3) (Table 1). This also results in a reduction in the crystal symmetry from the I2/m space group to P21/c, while the structural topology is almost intact. Thus, similar to that observed in Ag5BHT, CuAg4BHT exhibits alternatively stacked 2D Ag-S networks and 1D copper-dithiolene chains (Fig. 3a). Moreover, a graphene-like layer structure formed by the connection of Ag atoms is preserved in the transmetalation product (Fig. 3b), which is further confirmed by the characteristic symmetric vibration signal of Ag-Ag bond in Raman spectrum (Supplementary Fig. 12). In contrast, CuAg2BHT exhibits a Kagome-like lattice when viewed along the a-axis (Fig. 3c), in which the six-coordinated Ag atoms lied between the mean planes defined by the two square-planar metal ions and ligand moieties (Fig. 3d). It is worth noting that the Ag atoms with high coordination numbers are critical for extending bimetallic OMCs into 3D networks (Supplementary Fig. 13 and Fig. 1).
a Crystal structure of CuAg4BHT viewed along the a-axis direction. b Honeycomb-like lattice formed by adjacent Ag atoms in CuAg4BHT (viewed along the c-axis). c Top view of the Kagome-like lattice in CuAg2BHT (viewed along the a-axis). d Side view of the layered structure formed by the metals ions with square-planar geometry and the C6S6 moieties in CuAg2BHT (gray: carbon atoms, red: sulfur atoms, blue: copper atoms, violet: silver atoms).
Electrical transport characterizations
The electrical conductivities of Ag5BHT and CuAgxBHT samples were measured on pressed pellets via the four-probe method. At 300 K, all these OMCs exhibited high conductivities, ranging from 10 S cm−1 for Ag5BHT and 0.13 S cm−1 for CuAg2BHT to 3 S cm−1 for CuAg4BHT (Fig. 4a–c and Supplementary Table 6). These conductivities are among the highest values ever reported for conductive coordination polymers (Supplementary Table 7). The conductivity is positively correlated with temperature, suggesting the thermally activated transport. The plot of ln(σ) versus T−0.25 in the temperature range of 100–250 K is well fitted to the 3D Mott variable-range hopping model (Fig. 4a–c, inset)22. This behavior is very similar to what is observed in other granular conductors where inter-grain hopping dominates the charge transport19,23. Given that all three samples are composed of highly crystalline nanorods, the observed behaviors reflect interparticle rather than intraparticle (i.e., intrinsic) transport behavior.
a–c Electrical conductivities of three materials as a function of temperature from 2 to 400 K. Inset, plots of ln(σ) versus T−1/4 over the temperature region of 100–250 K. d UPS data for the valence band region of three samples acquired at 300 K, and the Fermi edge was shown by the pink dotted line. Source data are provided as a Source Data file.
UPS indicated that the Fermi levels of all three samples cut the valence bands (Fig. 4d), which is an inherent character for metallic states, similar to conducting Ni3BHT2 and Cu3(HIB)2 (HIB = hexaiminobenzene)6,24. Density functional theory (DFT) calculations were performed to probe their electronic structures and Density of States (DOS) near the Fermi level. As shown in Fig. 5, they all exhibit wide energy band dispersions and salient features with bands crossing the Fermi level, further showing the metallic character of these materials.
a–c Calculated band structures and DOS for Ag5BHT (a), CuAg4BHT (b), and CuAg2BHT (c). The high-symmetry K-points in the first Brillouin zone are provided in Supplementary Table 8. d Seebeck coefficients of three materials as a function of temperature from 300 to 400 K. Source data are provided as a Source Data file.
The Seebeck coefficients of all three materials displayed a positive sign (Fig. 5d), indicating that hole-type conduction is dominant25,26. The room-temperature Seebeck coefficient of CuAg4BHT is ~74 μV K−1, which is more than ten times larger than those of CuAg2BHT (~6 μV K−1) and Ag5BHT (~5 μV K−1). According to Mott’s formula, the Seebeck coefficient is connected with the variation of the DOS at the Fermi level27,28, which means that the steeper varying DOS around the Fermi level will result in a larger Seebeck coefficient. Thus, for CuAg2BHT, the observed small Seebeck coefficient could be attributed to its smoothly changing DOS near the Fermi level, while the DOS is close to its minimum (Fig. 5c). Compared to Ag5BHT, the DOS of CuAg4BHT displays a steeper curve around the Fermi level (Supplementary Fig. 15), consistent with the markedly larger Seebeck coefficient of CuAg4BHT. Besides, we carried out theoretical calculations of the Seebeck coefficients using the Boltzmann transport theory with the constant scattering approximation as implemented in the BoltzTrap code29,30,31. With the constant scattering approximation, the Seebeck coefficients are estimated based on the band structures. The simulation results show that the exact Seebeck values are slightly different from the experimental ones, but the trend is consistent with what observed that the Seebeck value of CuAg4BHT is significantly higher than that of the other two materials (Supplementary Fig. 16). Furthermore, the valence bands of Ag5BHT and CuAg2BHT are mostly parabolic bands, while CuAg4BHT displays nearly flat band along the E–Z–C2 vectors, which is also a tag for the higher Seebeck coefficient. Notably, a bipolaron effect32 could be observed in CuAg4BHT, with the Seebeck coefficient reaching a maximum value (~81 μV K−1) at 350 K and decreasing in the temperature range from 350 to 400 K, suggesting the contribution of the minority carriers increased with raising temperature.
As shown in Supplementary Fig. 17a–d, for monometallic Ag5BHT, the DOS near the Fermi level mainly derived from the Ag-d orbitals and S-p orbitals, suggesting that the 2D Ag-S network is the preferred charge transport route. Due to the different coordination geometries and chemical environments of Ag1 and Ag2 in Ag5BHT (Ag1 refers to the six-coordinated Ag atoms with distorted octahedron geometry and Ag2 features a square-planar coordination mode), the d-orbitals splitting of Ag1 and Ag2 is expected to be different, which makes the orbital compositions of Ag1 and Ag2 different in PDOS. The \({{{{{\rm{Ag}}}}}}{1}_{{d}_{xz}+{d}_{{x}^{2}-{y}^{2}}}\) and \({{{{{\rm{Ag}}}}}}{2}_{{d}_{xy}+{d}_{yz}}\) orbitals contribute the most to PDOS near the Fermi level (Supplementary Fig. 17c, d), whereas for CuAgxBHTs, due to copper incorporating into the framework matrix, the PDOS near the Fermi level is dominated by contributions from the d orbitals of Cu and Ag and p orbitals of S. It should be noted that for CuAg4BHT, the PDOS derived from Ag d-orbitals is different from that of Ag1 in Ag5BHT, while the PDOS contribution from \({{{{{{\rm{Cu}}}}}}}_{{d}_{xy}+{d}_{yz}}\) orbitals is similar to that of Ag2 in Ag5BHT. The p-orbital composition of S atoms also changes after the metal atom substitution (Supplementary Fig. 17b, f), which is ascribed to the charge redistribution in this M5BHT system (M refers to the metal ions). After the chemical oxidation transformation, significant variations in the PDOS composition of the d orbitals of metal atoms and the p orbitals of C and S atoms can be observed near the Fermi level (Supplementary Fig. 17i–l). All these results elucidate that the introduction of bimetallic nodes can synergistically tailor the electronic structures of the OMCs, thereby modulating the corresponding charge transport behavior.
EPR and magnetic studies
Electron paramagnetic resonance (EPR) measurements were performed to investigate electron configurations of these materials. For Ag5BHT, no EPR signal was detected even when cooled down to 10 K, suggesting its diamagnetic nature. After metal metathesis, a nearly isotropic signal contributed by the Cu2+ with g = 2.053 was observed (Fig. 6a), which is consistent with the Cu 2p XPS analysis in CuAg4BHT (Supplementary Fig. 18). As for CuAg2BHT, only a very weak EPR signal was observed (Supplementary Fig. 19). The signal intensity is temperature dependent and almost diminishes at room temperature, which indicates that it does not originate from an organic radical. As this EPR signal was broad and asymmetrical, it can be attributed to a small amount of leftover Cu2+ during oxidation, while the dominant Cu ions became EPR silent, supporting that the oxidation state of Cu in CuAg2BHT was +1 (Supplementary Fig. 18).
a Temperature variable EPR spectrum. b M(H)|T isotherm measurements performed at various temperatures. As argued by Johnston, M(H)|T = χ(T)H + Mi(H)|T, where χ(T) and Mi(H)|T are the intrinsic susceptibility of CuAg4BHT and the impurity contribution to M(H)|T, respectively. c Measured magnetic susceptibility M/H of CuAg4BHT (red solid line). The blue symbols show the intrinsic susceptibilities χ(T) of CuAg4BHT derived from magnetic isotherms. The upper inset shows M/H versus T plot below 20 K. d Cp/T-T2 plot of CuAg4BHT in the temperature range of 2–20 K. The dashed line represents a fit using the equation, Cp = γT + βT3. Source data are provided as a Source Data file.
From the first generation of Ag5BHT (coordination assembly), to the second generation of CuAg4BHT (metal metathesis), and then to the third generation of CuAg2BHT (oxidation regulation) (Fig. 1), the non-innocent ligand shows multiple accessible redox states that are responsible for electrically neutral networks. During the metathesis process, we found that only the square-planar Ag atoms of Ag5BHT could be replaced by Cu(II) ions, even by raising the reaction temperature or prolonging the duration. Generally, longer bond length refers to lower bond energy, so it can be expected that the bond energy of Ag-S bond (231.3–202.1 KJ mol−1) is lower than that of Cu-S bond (274.5 KJ mol−1)33. Thus, the precise exchange result can be attributed to the labile tetra-coordinated [AgS4] cores (Supplementary Fig. 13), which has also been verified by other studies34,35, whereas Ag atoms with non-coplanar coordination geometry were stabilized by the formation of Ag-Ag bond, preventing their substitution by Cu atoms. Furthermore, the total energy of Ag5BHT (−122.4 eV) calculated with DFT method is higher than that of CuAg4BHT (−125.6 eV), indicating this selective metal metathesis reaction is a thermodynamically favored process.
The precise substitution of the Ag+ ions by Cu2+ ions turns the nonmagnetic Ag5BHT into a paramagnetic conducting material. The coexistence of local spins and conducting electrons reminds us of the research on molecular Kondo system36. Remarkably, searching for Kondo systems in 3d-electron compounds has attracted immense interest in condensed matter physics37. Considering that Cu2+ ions with localized magnetic moments are periodically arranged in the network having itinerant d-p-π electrons, Kondo lattice scenario arising from the interaction between localized spins and conduction electrons in CuAg4BHT could be expected.
Thus, the magnetic susceptibility measurements were carried out first. As shown in Fig. 6c, M/H increases with decreasing temperatures and displays a broad peak around 12 K. A significant downward trend occurs as the temperature decreases, and the M(T)|H curve starts to increase again below 5 K. This upturn is typical of heavy Fermi liquids and reveals the presence of a small amount of magnetic or paramagnetic impurities/defects38,39. Actually, we noticed such paramagnetic impurities originating from the surface contamination or defects, and a calibration procedure was carried out to eliminate the interference signal. Meanwhile, in order to ensure the dominant source of magnetic properties of CuAg4BHT, the possible influence of extrinsic oxides was excluded by synchrotron PXRD and temperature variable EPR measurements (Supplementary Figs. 19 and 20). Therefore, the intrinsic magnetic susceptibility of CuAg4BHT was precisely determined by analyzing the magnetic isotherms M(H)|T at different temperatures (Fig. 6b) instead of M(T)|H curve40. The derived intrinsic susceptibilities were represented by the blue symbols in Fig. 6c, and followed the Curie–Weiss law in the high T region. The Curie–Weiss fitting from 100 to 300 K afforded a Curie constant of C = 0.376 emu K mol−1 and Curie–Weiss temperature of θ = −5.6 K. The calculated effective moment (µeff) for each Cu ion in the formula CuAg4C6S6 equals 1.74 μB, which was reasonably close to that expected for Cu(II) (S = 1/2, μeff = 1.73 μB). The negative Curie–Weiss temperature indicated the presence of antiferromagnetic interactions between the magnetic moments. Besides, the measured susceptibility shows no signature of a magnetic ordering transition down to 2 K, but a clear deviation from Curie–Weiss behavior appears below T <12 K. As the temperature decreases, the intrinsic susceptibility of CuAg4BHT reaches a broad hump around 10 K and then decreases when T <8 K, while its intrinsic susceptibility remains quite large, equal to 1.8 × 10−2 emu mol−1 toward the T = 0 limit. Such magnitude and T dependence of susceptibility39,41 provides a crude estimation of the coherence temperature T* (refs. 42, 43). Below the T* of ~8–10 K, the susceptibility evolving becomes visible, indicating the emergence of the interaction of local Cu2+ spins and conduction d-p-π electrons. Therefore, the observable decrease in intrinsic susceptibility when T <8 K is attributed to the Kondo scenario, in which localized magnetic moments are screened by itinerant electrons. Thus, with decreasing temperature, a crossover from a paramagnetic state with localized moments to renormalized Fermi liquid state with coherent Kondo lattice was suggested in CuAg4BHT.
In addition, since CuAg4BHT is isostructural with Ag5BHT, the comparison of their specific heat data can reveal the influence of Cu ion introduction. In the temperature range from 2 to 8 K, the specific heat data are well represented by the relation of Cp = γT + βT3 (Fig. 6d). A linear fit of Cp/T to T2 plot yields a Sommerfeld coefficient (γ) of 82.2 mJ K−2 mol−1 for CuAg4BHT, which is more than ten times higher than that of Ag5BHT (Supplementary Fig. 21). Such unusually large γ value also proves the existence of heavy-mass quasiparticle states44,45, supporting the observed susceptibility anomaly. Furthermore, anomalously large Seebeck coefficient in metallic CuAg4BHT provides another hint for the existence of a large effective electron mass. Finally, we realized that CuAg4BHT has a triangular lattice of Cu(II) cations (Supplementary Fig. 22), the origin of the heavy quasiparticle mass could be closely linked with the geometrical frustration, as also demonstrated in d-electron LiV2O4 spinel41. To gain in-depth insight into the complex Kondo physics, the preparation of bulk single-crystal sample (>50 μm) and ultralow temperature measurements are further demanded, and will be performed on this OMC in the near future.
Discussion
In summary, we have rationally designed and synthesized a family of bimetallic OMCs, CuAgxBHTs, via selective metal metathesis and delicate oxidation regulation. Both crystal structures have been well characterized by PXRD and RED techniques, revealing atomically precise structures composed of alternatively stacked 1D copper-dithiolene chains and 2D Ag-S networks. As suggested by band structure calculations, the bimetal-bis(dithiolene) moieties can synergistically regulate the electronic structures of these OMCs, which accounts for the high electrical conductivity observed in 3D OMCs. In addition, the susceptibility anomaly and other measurements suggested that CuAg4BHT was a candidate for a heavy Fermi liquid with Kondo lattice. We expect that our experimental results will motivate theoretical efforts on this intriguing subject in the future. More importantly, the development of bimetallic OMCs may effectively avoid the “Buckets Effect” caused by the unbalanced properties of their monometallic counterparts. Our results pave the way for constructing organic–inorganic hybrid materials with unique structural topologies, and unlock more opportunities for condensed matter physics as well as electronics, catalysis, and energy-related applications.
Methods
Synthesis of CuAg4BHT
Under argon atmosphere, Cu(NO3)2•3H2O (470 mg, 1.94 mmol) was dissolved in 160 mL degassed ethanol, and then Ag5BHT (100 mg, 0.124 mmol) was added. The mixture was sonicated for 5 min, and subsequently heated to 80 °C with constant stirring for 72 h to form a gray-black powder, followed by natural cooling to room temperature. The obtained power was filtered, washed with water, ethanol, acetone, and diethyl ether in sequence, and then dried at 80 °C under vacuum for 24 h. Yield: 82 mg (87%). Elem. Anal. Calcd. for CuAg4C6S6: C, 9.49; S, 25.33; Cu, 8.37, Ag, 56.81. Found: C, 9.79; S, 25.46; Cu, 9.20, Ag, 55.55.
Trials for the oxidation regulation of CuAg4BHT
Under argon atmosphere, different amounts of Ce(NH4)2(NO3)6 (0.5–6 equiv. to CuAg4BHT) were dissolved in 100 mL degassed acetonitrile, and then CuAg4BHT (76 mg, 0.1 mmol) was added. The mixture was stirred at room temperature for 12 h. The obtained power was filtered, washed with water, CH3CN, acetone, and diethyl ether in sequence, and then dried at 80 °C under vacuum for 24 h.
Optimized synthetic condition of CuAg2BHT
Under argon atmosphere, Ce(NH4)2(NO3)6 (220 mg, 0.4 mmol) was dissolved in 150 mL degassed acetonitrile, and then CuAg4BHT (152 mg, 0.2 mmol) was added. The mixture was stirred at room temperature for 24 h. The obtained power was filtered, washed with water, CH3CN, acetone, and diethyl ether in sequence, and then dried at 80 °C under vacuum for 24 h. Yield: 48 mg (88%). Elem. Anal. Calcd. for CuAg2C6S6: C, 13.25; S, 35.38; Cu, 11.69, Ag, 39.68. Found: C, 14.53; S, 36.16; Cu, 10.23, Ag, 38.48.
SEM and TEM characterizations
SEM images were obtained using a Toshiba SU8000-SEM with an acceleration voltage of 10 kV. TEM images were acquired using a JEOL 2100F-TEM with an acceleration voltage of 120 kV. About 1 mg of the sample was dispersed in 4 mL of absolute ethanol, and after ultrasonic dispersion for 30 min, 5 µL of the suspension was dropped on a copper grid coated with a carbon film to perform TEM characterizations. The 3D RED data were collected on a Themis 300 TEM by a BM-Ceta camera with an acceleration voltage of 300 kV. One typical set of RED data was collected by combing specimen tilt and electron-beam tilt in the range of −65° to +70° with a beam-tilt step of 1°. The nanocrystal selected for data collection was isolated by the selected area aperture, and calibrated to a concentric height to stay within the aperture over the entire tilt range. During continuous rotation, the dose rate was calibrated to <0.03 e-/Å2 s. Altogether, 137 frames were obtained, and the reflection intensities and unit parameters were extracted with the software Pets2.0.
Electrical property measurement
The electrical conductivities were measured on the pelletized samples via a four-probe method in a Physical Property Measurement Systems (PPMS-9, Quantum design). About 5 mg samples were compressed into a cuboid pellet under a pressure of 10 MPa. Then four parallel gold electrodes were deposited on the pellet by vacuum evaporation to form a four-electrode device. The Seebeck coefficients were measured using the SB-100 Seebeck Measurement System (MMR Tech.) under a vacuum environment below 18 mTorr.
Details of physical property measurements
The DC magnetic susceptibility measurement under 2–300 K was conducted in a Superconducting Quantum Interference Device (SQUID) magnetometer (Quantum Design). Zero field cooling and field cooling measurements were performed under an applied field of 1000 Oe. Diamagnetic correction was applied using Pascal’s constant. The temperature variable EPR spectrum were collected using a Bruker ElexSys E580 spectrometer, operating at the X-band (ω = 9.37 GHz). The center field was set to 300 mT, and the scanning range was 100 mT. A low-temperature environment was achieved by using an Oxford Instruments ESR900 liquid helium cryostat. The low-temperature heat capacity measurements were also performed in PPMS.
Data availability
The crystallographic information obtained by Rietveld refinement of PXRD data has been deposited in the Cambridge Crystallographic Data Centre under accession codes CCDC 2143107 (CuAg4BHT) and CCDC 2143106 (CuAg2BHT) [https://www.ccdc.cam.ac.uk/structures/?]. All data generated and analyzed in this study are included in the article and its Supplementary Information, and are also available from the authors upon request. The source data generated in this study are provided in the Source Data file. Source Data are provided with this paper.
References
Paritmongkol, W. et al. Size and quality enhancement of 2D semiconducting metal–organic chalcogenolates by amine addition. J. Am. Chem. Soc. 143, 20256–20263 (2021).
Xing, G. et al. Copper(I)-based flexible organic–inorganic coordination polymer and analogues: high-power factor thermoelectrics. ACS Appl. Mater. Interfaces 12, 53841–53851 (2020).
Li, Y. et al. Coordination assembly of 2D ordered organic metal chalcogenides with widely tunable electronic band gaps. Nat. Commun. 11, 261 (2020).
Yan, H. et al. Hybrid metal–organic chalcogenide nanowires with electrically conductive inorganic core through diamondoid-directed assembly. Nat. Mater. 16, 349–355 (2017).
Banda, H. et al. High-capacitance pseudocapacitors from Li+ ion intercalation in nonporous, electrically conductive 2D coordination polymers. J. Am. Chem. Soc. 143, 2285–2292 (2021).
Kambe, T. et al. Redox control and high conductivity of nickel bis(dithiolene) complex π-nanosheet: a potential organic two-dimensional topological insulator. J. Am. Chem. Soc. 136, 14357–14360 (2014).
Huang, X. et al. A two-dimensional π-d conjugated coordination polymer with extremely high electrical conductivity and ambipolar transport behaviour. Nat. Commun. 6, 7408 (2015).
Clough, A. J. et al. Room temperature metallic conductivity in a metal-organic framework induced by oxidation. J. Am. Chem. Soc. 141, 16323–16330 (2019).
Huang, X. et al. Superconductivity in a copper(II)-based coordination polymer with perfect kagome structure. Angew. Chem. Int. Ed. 57, 146–150 (2018).
Takenaka, T. et al. Strongly correlated superconductivity in a copper-based metal-organic framework with a perfect kagome lattice. Sci. Adv. 7, eabf3996 (2021).
Wang, M., Dong, R. & Feng, X. Two-dimensional conjugated metal-organic frameworks (2D c-MOFs): chemistry and function for MOFtronics. Chem. Soc. Rev. 50, 2764–2793 (2021).
Veselska, O. & Demessence, A. d10 coinage metal organic chalcogenolates: from oligomers to coordination polymers. Coord. Chem. Rev. 355, 240–270 (2018).
Deng, X. et al. Conductive MOFs based on thiol-functionalized linkers: challenges, opportunities, and recent advances. Coord. Chem. Rev. 450, 214235 (2022).
Mandal, S. et al. Post-synthetic modification of metal–organic frameworks toward applications. Adv. Funct. Mater. 31, 2006291 (2021).
Tanabe, K. K. & Cohen, S. M. Postsynthetic modification of metal–organic frameworks—a progress report. Chem. Soc. Rev. 40, 498–519 (2011).
Duan, H. et al. Beating the exclusion rule against the coexistence of robust luminescence and ferromagnetism in chalcogenide monolayers. Nat. Commun. 10, 1584 (2019).
Ahmed, S. et al. Magnetic properties of Co doped WSe2 by implantation. J. Alloy. Compd. 731, 25–31 (2018).
Ananikov, V. P. et al. Catalytic adaptive recognition of thiol (SH) and selenol (SeH) groups toward synthesis of functionalized vinyl monomers. J. Am. Chem. Soc. 134, 6637–6649 (2012).
Huang, X. et al. Highly conducting neutral coordination polymer with infinite two-dimensional silver-sulfur networks. J. Am. Chem. Soc. 140, 15153–15156 (2018).
Huang, X. et al. Highly conducting organic-inorganic hybrid copper sulfides CuxC6S6 (x = 4 or 5.5): Ligand-based oxidation-induced chemical and electronic structure modulation. Angew. Chem. Int. Ed. 59, 22602–22609 (2020).
Jin, Y. et al. Facile synthesis, precise species control and chemical transformation of highly conducting organic metal chalcogenides CuxBHT (BHT = benzenehexathiol; x = 3, 4, and 5.5). J. Mater. Chem. C. 10, 2711–2717 (2022).
Mott, N. F. Conduction in non-crystalline materials. Philos. Mag. 19, 835–852 (1969).
Beloborodov, I. S. et al. Granular electronic systems. Rev. Mod. Phys. 79, 469–518 (2007).
Dou, J. H. et al. Signature of metallic behavior in the metal-organic frameworks M3(hexaiminobenzene)2 (M = Ni, Cu). J. Am. Chem. Soc. 139, 13608–13611 (2017).
Park, J. et al. High thermopower in a Zn-based 3D semiconductive metal–organic framework. J. Am. Chem. Soc. 142, 20531–20535 (2020).
Sun, L. et al. A microporous and naturally nanostructured thermoelectric metal-organic framework with ultralow thermal conductivity. Joule 1, 168–177 (2017).
Barnard, R. Thermoelectricity in Metals and Alloys (Taylor &. Francis Ltd., London, 1972).
Cutler, M. & Mott, N. F. Observation of Anderson localization in an electron gas. Phys. Rev. 181, 1336–1340 (1969).
Madsen, G. K. H. & Singh, D. J. BoltzTraP. A code for calculating band-structure dependent quantities. Comput. Phys. Commun. 175, 67–71 (2006).
Yang, J. et al. Evaluation of half-heusler compounds as thermoelectric materials based on the calculated electrical transport properties. Adv. Funct. Mater. 18, 2880–2888 (2008).
Gorai, P. et al. Computationally guided discovery of thermoelectric materials. Nat. Rev. Mater. 2, 17053 (2017).
Ravich Yu, I., Efimova, B. & Smirnov, I. Semiconducting Lead Chalcogenides (Plenum, New York, 1970).
Luo, Y.-R. Comprehensive Handbook of Chemical Bond Energies (CRC Press, 2007).
Young, A. G. & Hanton, L. R. Square planar silver(I) complexes: a rare but increasingly observed stereochemistry for silver(I). Coord. Chem. Rev. 252, 1346–1386 (2008).
Chowdhury, S., Drew, M. G. B. & Datta, D. A case of four-coordinate silver(I) adopting a high energy planar geometry. Exp. Theory N. J. Chem. 27, 831–835 (2003).
Idobata, Y., Zhou, B., Kobayashi, A. & Kobayashi, H. Molecular alloy with diluted magnetic moments-molecular Kondo system. J. Am. Chem. Soc. 134, 871–874 (2012).
Zhao, M. et al. Kondo holes in the two-dimensional itinerant Ising ferromagnet Fe3GeTe2. Nano Lett. 21, 6117–6123 (2021).
Hardy, F. et al. Evidence of strong correlations and coherence-incoherence crossover in the iron pnictide superconductor KFe2As2. Phys. Rev. Lett. 111, 027002 (2013).
Kondo, S. et al. LiV2O4: a heavy Fermion transition metal oxide. Phys. Rev. Lett. 78, 3729–3732 (1997).
Johnston, D. C. The puzzle of high temperature superconductivity in layered iron pnictides and chalcogenides. Adv. Phys. 59, 803–1061 (2010).
Urano, C. et al. LiV2O4 spinel as a heavy-mass Fermi liquid: anomalous transport and role of geometrical frustration. Phys. Rev. Lett. 85, 1052–1055 (2000).
Continentino, M. A., Japiassu, G. M. & Troper, A. Critical approach to the coherence transition in Kondo lattices. Phys. Rev. B 39, 9734–9737 (1989).
Yang, Y.-f et al. Scaling the Kondo lattice. Nature 454, 611–613 (2008).
Zhu, J.-X. et al. Electronic correlation and magnetism in the ferromagnetic metal Fe3GeTe2. Phys. Rev. B 93, 144404 (2016).
Zhang, Y. et al. Emergence of Kondo lattice behavior in a van der Waals itinerant ferromagnet, Fe3GeTe2. Sci. Adv. 4, eaao6791 (2018).
Acknowledgements
The authors acknowledge the financial support from the National Key R&D Program of China (Grant No. 2017YFA0204701), the National Natural Science Foundation of China (Grant 22071256), and the Chinese Academy of Sciences (QYZDY-SSW-SLH024). The authors also appreciate the crew of the BL14B1 beamline at the Shanghai Synchrotron Radiation Facility (SSRF) for their assistance in synchrotron PXRD data collection.
Author information
Authors and Affiliations
Contributions
W.X. planned and designed the research project. Y.G.J. executed the syntheses, chemical, spectroscopic and electrical characterization. Y.H.F. performed and analyzed temperature variable EPR data. X.H. and B.G. obtained and analyzed the transmission electron microscopy data. C.M.L. performed and analyzed the magnetic susceptibility measurements. Y.L., Z.L., and S.W. collected the PXRD data. Y.M.S. contributed to the Seebeck coefficient measurements and analysis. X.J.D. and Y.Z. performed and analyzed electrical conductivity experiments and UPS characterizations. D.W.W. performed and analyzed the specific heat data. F.H. and W.X. performed the DFT calculation and crystal structure-solving works. Y.G.J. and W.X. wrote the manuscript. All authors participated in the discussion and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jin, Y., Fang, Y., Li, Z. et al. Construction of conducting bimetallic organic metal chalcogenides via selective metal metathesis and oxidation transformation. Nat Commun 13, 6294 (2022). https://doi.org/10.1038/s41467-022-34118-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-34118-7
This article is cited by
-
Efficient first-principles electronic transport approach to complex band structure materials: the case of n-type Mg3Sb2
npj Computational Materials (2024)
-
Thermoelectric Transport Properties of Co0.5Fe0.5Se2, Co0.5Fe0.5Te2, and Their Solid-Solution Compositions
Electronic Materials Letters (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.