Abstract
External fields are introduced to catalytic processes to improve catalytic activities. The light field effect plays an important role in electrocatalytic processes, but is not fully understood. Here we report a series of photo-coupled electrocatalysts for CO2 reduction by mimicking the structure of chlorophyll. The porphyrin-Au catalyst exhibits a high turnover frequency of 37,069 h−1 at −1.1 V and CO Faradaic efficiency (FE) of 94.2% at −0.9 V. Under visible light, the electrocatalyst reaches similar turnover frequency and FE with potential reduced by ~ 130 mV. Interestingly, the light-induced positive shifts of 20, 100, and 130 mV for porphyrin-Co, porphyrin-Cu, and porphyrin-Au electrocatalysts are consistent with their energy gaps of 0, 1.5, and 1.7 eV, respectively, suggesting the porphyrin not only serves as a ligand but also as a photoswitch to regulate electron transfer pathway to the metal center.
Similar content being viewed by others
Introduction
Converting CO2 to high-value chemicals is an ongoing challenge in the catalytic field1. Thermocatalysis2,3, photocatalysis4,5,6, and electrocatalysis7,8,9,10 are recognized as promising technologies for CO2 conversion. However, these catalytic routes still suffer from a series of issues, such as high temperature for thermal catalysis, low yield for photocatalysis, and high overpotential for electrocatalysis11,12,13,14.
In order to overcome such challenges, researchers propose that external field input can significantly improve intrinsic activity and energy efficiency. For example, a plasma field can vibrationally excite CO2 molecules into free radicals and excited species, which may largely reduce activation temperature in thermocatalytic process15. In addition, external bias is widely used in photocatalytic processes to facilitate charge separation16. It is worth mentioning that suitable light irradiation possibly interferes with electronic properties of electrocatalysts, such as electron transfer, band-bending, charge distribution, Fermi level, and desorption energy of intermediate, and all these factors can alter catalytic pathways and performance. However, there have been limited studies looking into the light field effect on electrocatalytic reduction of CO2. According to these limited studies, “photo-coupled electrocatalyst” is usually constituted with a ternary complex, including the dye as light harvester, semiconductor as charge transfer mediator, and metal nanoparticle as CO2 activator17,18. On the one hand, the hybrid system easily leads to complicated synthesis and poor durability; on the other hand, the high interior resistance causes the low efficiency.
As we all know, chlorophyll continuously provides energy and resources for the entire ecosystem by the photosynthetic conversion of CO2 to glucose. It is worth mentioning that porphyrin is the photosensitive core component of chlorophyll, whose porphyrinic ligand cooperates with a centrally bound Mg atom19,20. The electronic property is susceptible to conjugative perturbation of 18π aromatic macrocycle, thus utilizing rational external fine-turning (such as light irradiation) can drastically alter electronic performance21. Furthermore, extensive studies have indicated Au and single-Co-atom electrocatalysts display the best catalytic activity for CO production among metals and single-atom catalysts22,23, respectively, and Cu species are sole candidates for C2+ production. Therefore, synthetic mimics of chlorophyll may promote insight into the catalytic mechanism and development of “photo-coupled electrocatalyst” at the atomic level via replacing the central Mg of a chlorophyll molecule with Au, Cu, or Co24 (Fig. 1a).
Preparation and nanostructure characterization of HNTM-Au-SA. a Schematic illustration of photosynthesis and photoelectrochemical reduction of CO2 on chlorophyll and HNTM-Au-SA, respectively. b TEM image. c STEM image (inset is line-scanning spectrum for Au element). d HRTEM image. Each rhombus represents a porphyrin unit. e HAADF STEM image. Single Au atoms are highlighted in red circles. Scale bar: b is 1 μm, c is 50 nm, d, e is 5 nm
Here we synthesize zirconium porphyrinic metal-organic framework (MOF) hollow nanotubes (HNTMs) as supports to anchor Au, Cu, and Co (named as HNTM-Au-SA, HNTM-Cu-SA, and HNTM-Co-SA), respectively. In the dark, HNTM-Au-SA exhibits an ultrahigh turnover frequency (TOF) of 37,069 h−1 at −1.1 V. Motivated by light irradiation, a similar TOF value is obtained at a lower overpotential with a positive shift of 130 mV. Interestingly, we observed similar results on HNTM-Cu-SA and HNTM-Co-SA, suggesting that the light irradiation can easily facilitate electrochemical activation of CO2 molecule over single porphyrin-metal atom catalyst. Through both experimental tests and density functional theory (DFT) calculations, we have successfully demonstrated the feasibility of “photo-coupled electrocatalysis.” Thus, the application of a “photo-coupled electrocatalyst” that integrates electrocatalytic activity with light sensitivity provides an avenue to activate CO2 at a low overpotential.
Results
Characterization of single-Au-atom structure
As shown in Supplementary Fig. 1, HNTM could be synthesized via a solvothermal method with ZrCl4, tetrakis (4-carboxyphenyl)-porphyrin and benzoic acid. Transmission electron microscopy (TEM) images reveal the uniform HNTM morphology with a size of around 500 nm (Supplementary Fig. 2a, d). The inherent hollow interior of HNTM could serve as a collector for CO2 concentration and a microreactor for CO2 conversion simultaneously25.
Then the HNTM were treated with HAuCl4·4H2O (CoCl2, CuCl2·2H2O) in N,N-dimethylformamide (DMF) at 80 °C for 4 h to immobilize corresponding metal atoms (HNTM-M-SA) (Fig. 1b and Supplementary Fig. 2b, e). The HNTM loaded with metal nanoparticles (HNTM-M-NP) were also prepared for comparison (Supplementary Fig. 2c, f). The TEM and scanning tunneling electron microscopy (STEM) images exhibit that HNTM-Au-SA retains its initial nanostructure after metal atom immobilized (Supplementary Fig. 3a, b). Neither sub-nanometer clusters nor nanoparticles are detected, indicating Au species possibly exist as single atoms. The line-scanning spectra and energy dispersive spectroscopy (EDS) mapping images indicate that C, N, O, Zr, and Au elements are well-dispersed over the entire nanostructure (Fig. 1c and Supplementary Fig. 3c, d). Low loading amount of gold (0.07% by optical emission spectrometry-inductively coupled plasma (OES-ICP)) results in weak Au element signal. As shown in Fig. 1d, clearly observed porphyrin units on HNTM-Au-SA surface are marked by red rhombus. Aberration-corrected high-angle annular dark-field imaging (HAADF)-STEM images confirm that the Au species are in single atom form, which are presented as bright dots in the center of red circles (Fig. 1e). As for HNTM-Au-NP, the TEM and STEM images prove the existence of Au nanoparticles with a size distribution between 5 and 10 nm (Supplementary Fig. 4). Due to the insufficient anchoring sites, excessive addition of metal salt would result in the formation of nanoparticles.
As shown in Fig. 2a, N2 adsorption–desorption isotherms of HNTM and HNTM-Au-SA exhibit similar type IV curves. The H3-type hysteresis loops indicate the existence of abundant mesopores with the sizes of 2–5 nm, which is also confirmed by pore size distribution in Supplementary Fig. 5. Compared with HNTM with the specific surface area of 894 m2 g−1, the incorporation of Au atoms and Au nanoparticles result in lower value of 384 and 31 m2 g−1 for HNTM-Au-SA and HNTM-Au-NP, respectively.
Single-Au-atom structure characterization. a Nitrogen adsorption–desorption isotherms and b XRD curves of HNTM, HNTM-Au-SA, and HNTM-Au-NP. c Au 4 f XPS spectra of HNTM-Au-SA and HNTM-M-NP. d The normalized XANES spectra. e FT-EXAFS spectra of HNTM-Au-SA, HNTM-Au-NP, HAuCl4, and Au foil at Au L3 edge. f The FT-EXAFS space-fitting curve of HNTM-Au-SA. Inset shows schematic models of HNTM-Au-SA, Au (yellow), N (green), C (gray), and H (white)
Both of HNTM and HNTM-Au-SA show the X-ray diffraction (XRD) patterns in consistence with PCN-22526 (Fig. 2b), indicating the well-maintained crystallinity after single Au atom immobilized. An apparent diffraction peak located at 6–7° is observed in HNTM-Au-NP, which may be ascribed to the high degree of ordered Au plane within MOF framework27.
X-ray photoelectron spectroscopy (XPS) was used to investigate the oxidation state of Au in HNTM-Au-SA and HNTM-Au-NP. The survey XPS spectrum reveals the predominant presence of Zr, C, O, N, and Au elements, and no other hetero-elements (Cl) are detected (Supplementary Fig. 6). The Au 4 f XPS spectrum of HNTM-Au-SA displays two peaks at binding energies (BEs) of 92.0 eV (Au 4f5/2) and 88.2 eV (Au 4f7/2), corresponding to Au3+, which could be ascribed to Au-N coordination28 (Fig. 2c).
To further confirm the single-Au-atom structure, X-ray absorption fine structure (XAFS) spectroscopy was conducted (Fig. 2d). The Au L3-edge in the X-ray absorption near edge structure (XANES) curve of HNTM-Au-SA is almost the same as HAuCl4·4H2O, suggesting the oxidation state of Au atom is around +3, which is in good accordance with XPS results. Meanwhile, the XANES curves of HNTM-Au-NP and Au foil are approximately the same, implying Au species mainly exist as metallic nanoparticles.
The coordination information of single-atom structure was indicated by the extended XAFS (EXAFS). Figure 2e shows the Fourier transform (FT) k3-weighted EXAFS spectra of HNTM-Au-SA at Au L3-edge. In contrast to reference samples (Au foil and HAuCl4·4H2O), no obvious peaks of Au-Au (2.1 and 2.7 Å), Au-H (0.9 Å), and Au-Cl (1.8 Å) coordination are detected. Only a prominent peak at 1.5 Å is observed, corresponding to Au-N coordination28. As a comparison, the EXAFS spectra of HNTM-Au-NP exhibits strong Au-Au peaks, in good agreement with XANES results. Wavelet transform was also conducted to search the atomic dispersion of Au atom. The intensity maximums of Au foil and HNTM-Au are 2.6 Å and 1.5 Å, corresponding to Au-Au and Au-N contributions, respectively28 (Supplementary Fig. 7).
Figure 2f shows the fitting curve of single-Au-atom structure, which is perfectly reproduced by the experimental FT-EXAFS data. As shown in Supplementary Table. 1, the coordination number (Au-N) is 4, the bond length is 1.52 Å, and the disorder is 0.00785 Å2. Based on the above results and previous study24, we propose the schematic model of HNTM-Au-SA in the inset of Fig. 2f. A single Au atom is coordinated with four N atoms and anchored in the center of square-planar porphyrin unit to form a catalytic active site.
The single-atom structure of HNTM-Cu-SA and HNTM-Co-SA was also corroborated by HADDF-STEM and EXAFS analysis. As shown in Supplementary Fig. 8 and 9, no nanoparticles are detected on the MOF framework, implying the single-atom structure of Co and Cu. The aberration-corrected HAADF STEM images and EDS mapping display Cu and Co atoms are well-dispersed over the entire structure (Supplementary Fig. 8–10). XPS and EXAFS analysis further confirm their single-atom structure (Supplementary Fig. 11), indicating Co and Cu atoms in the oxidation state of +2. The ICP-OES results show the single atom loadings are 0.35% and 0.59% on HNTM-Cu-SA and HNTM-Co-SA, respectively (Supplementary Table 2).
Photo-coupled electrocatalytic performances of CO2 reduction
To evaluate the CO2 catalytic reduction performance of porphyrin-metal center structure, the photoelectrochemical reduction of CO2 was carried out in a transparent H-cell equipped with a 300 W Xe lamp (with > 420 nm cutoff filter, 67% solar intensity). The distance between the light source and H-cell was about 30 cm to keep electrolyte (0.1 M KHCO3 without a sacrificial regent) temperature stable at 25 °C. The gas and liquid products were analyzed by gas chromatography (GC) and 1H NMR, respectively. Notably, no gas and liquid product signals were detected during photocatalytic process, as the absence of sacrificial agent cannot trap the photogenerated holes for CO2 activation29,30.
Figure 3a presents the linear sweep voltammograms (LSVs) of HNTM-Au-SA scanned at 5 mV s−1 in N2- and CO2-saturated 0.1 M KHCO3. HNTM-Au-SA exhibits a very small cathodic current density in a N2 atmosphere and only H2 is detected at all potential range, conversely verifying that the products are originated from the reduction of CO2 (Supplementary Fig. 12). To further verify the origin of the products, we performed isotope labeling experiments by using 13CO2 as a carbon source. The generated CO and HCOOH were analyzed by GC-mass spectrometry (MS) and 1H NMR, respectively. As shown in Supplementary Fig. 13a, b, only the 13CO signal (m/z = 29) is observed in analysis of gas mixture, which is different from the 12CO (m/z = 28) when 12CO2 was used. For liquid product, the 1H NMR spectrum of the electrolyte exhibits a doublet after 13CO2 electrocatalysis, which is attributed to the methine proton of H13COO− (Supplementary Fig. 13c). In contrast, H12COO− is observed as a singlet at 8.3 p.p.m. after 12CO2 electrocatalysis. These results clearly prove that both CO and HCOOH are originated from CO2 reduction and not from the organic residue in the electrolyte or MOF material.
Photo-coupled electrochemical and electrochemical performance of CO2 reduction. a LSV curves of HNTM-Au-SA scanned at 5 mv s−1 in N2-saturated (black line) and CO2-saturated 0.1 M KHCO3 under visible light (red line)/dark (blue line). b LSV curves of HNTM, HNTM-Au-SA, and HNTM-Au-NP in CO2-saturated 0.1 M KHCO3 under visible light. c FECO on HNTM-Au-SA at the potentials of −0.6 V to −1.1 V under visible light (red line)/dark (black line). d TOF curves of HNTM-Au-SA under visible light (red line)/dark (black line). Error bars are ± s.d.
With the assistance of visible light, the current density of HNTM-Au-SA significantly increases from 10 to 13 mA cm−2 at −1.1 V in CO2-saturated electrolyte (Fig. 3b). It is evident that the porphyrin can utilize solar light to transfer more electron for CO2 reduction. As reference, the current densities of HNTM are negligible and almost overlapped in N2- and CO2-saturated electrolyte, revealing the inactivity for CO2 reduction (Supplementary Fig. 14a). Furthermore, the current density on HNTM shows negligible increase under visible light, suggesting the entwined orbitals of porphyrin-Au unit can transfer more electrons from porphyrin under visible light.
The effect of visible light on Faradaic efficiency (FE) at different potentials was also investigated. As expected, the sole reaction product for HNTM is H2, indicating Au is the active site for CO2 reduction (Supplementary Fig. 14c). As for HNTM-Au-SA, the FECO reaches a maximum of 94.2% at 0.9 V in dark condition as well as 95.2% at 0.8 V under visible light (Fig. 3c). Therefore, it is reasonable to infer that the visible light could interfere the electronic property of porphyrin to enhance atomic activity, which benefits CO2 reduction occurred at a relatively low potential. It is also worth mentioning that the higher FECO of HNTM-Au-SA than HNTM-Au-NP can be attributed to a more suitable chemical bond between intermediate and Au3+ single site than Au nanoparticle (Supplementary Fig. 14d).
TOF results can help us clearly understand the light field effect in CO2 activation (Fig. 3d). As expected, HNTM-Au-SA shows a maximum of 37,069 h−1 at −1.1 V under dark condition, much higher than those previously reported electrocatalysts31,32. When coupled with light, a similar TOF curve of HNTM-Au-SA is obtained with a positive shift about 130 mV, indicating visible light can easily disturb electronic property of catalysts and reduce the overpotential for CO2 activation.
In order to better study the light field effect, CO2 reduction performance was also recorded on HNTM-Cu-SA and HNTM-Co-SA. Similar to HNTM-Au-SA, both HNTM-Cu-SA and HNTM-Co-SA deliver larger current densities under visible light, whereas the nanoparticle counterparts perform lower activities, proving that single atom is much more active than nanoparticle due to specific valence state and maximum atom efficiency33 (Supplementary Fig. 15). As depicted in Fig. 4a, FECO of HNTM-Co-SA shows a maximum of 82.9% at −0.7 V under dark condition. Under visible light, all the FECO exceed 85.0% from −0.6 to −0.8 V and a maximum of 90.4% is achieved at −0.8 V. As for HNTM-Cu-SA, only HCOOH and H2 are detected with a total FE of nearly 100%. FEHCOO− attains a maximum of 77.2% at −0.7 V under visible light, higher than that without light irradiation (58.3% at −0.8 V) (Fig. 4b). As expected, both HNTM-Cu-NP and HNTM-Co-NP exhibit low FE, reconfirming lower activity of metal nanoparticles (Supplementary Fig. 16). Only a weak signal of formate is detected on HNTM-Cu-NP, with a relatively low FEHCOO− below 22% at all potential range.
Photo-coupled electrochemical and electrochemical reduction of CO2. a FECO on HNTM-Co-SA under visible light (red line)/dark (black line). b FEHCOO− on HNTM-Cu-SA under visible light (red line)/dark (black line). c TOF curves of HNTM-Co-SA under visible light (red line)/dark (black line). d TOF curves of HNTM-Cu-SA under visible light (red line)/dark (black line). Error bars are ± s.d.
The calculated TOF of HNTM-Cu-SA and HNTM-Co-SA at fixed potentials is plotted in Fig. 4c, d. A general trend is obtained as the peak position of TOF curves positively shifted ~ 100 mV for HNTM-Cu-SA and ~ 20 mV for HNTM-Co-SA. The shifts demonstrate once again that visible light can alter catalytic activity of different metal atoms.
The observed product and corresponding FE maximum on each catalyst are compared in Fig. 5a. HNTM-M-SA always show the highest FEmax under visible light. To further evaluate the photo-coupled system, the mass-specific, area-specific, and charge-specific rate of CO and HCOO− on each catalyst are presented in Supplementary Fig. 17–19. All of HNTM-M-SA exhibit significant improvement under visible light, verifying the light field effect. Furthermore, HNTM-Cu-SA and HNTM-Co-SA show similar performance with reported porphyrin complex; however, TOF value of HNTM-Au-SA shows at least one order of magnitude larger than them (Supplementary Table. 3). Reported photoelectrocatalysts are also listed, while they usually show complicated structures with low FE and reaction rate, which limit their practical application. Thereby, how to design and synthesize photo-coupled electrocatalysts with high performance remains the central challenge in this field.
Density functional theory calculations. a FE maximum and product observed on each catalyst. Red and black color bars represent FE under light/dark conditions, respectively. Error bars are ± s.d. b Calculated free energy profile of electrochemical reduction of CO2 to CO. c The synergistic catalysis mechanism of CO2 reduction on HNTM-Au-SA
Photo-coupled electrocatalytic mechanism
To understand the observed high selectivity and activity on the porphyrin-based catalysts, we performed DFT calculations of the free energy landscape for the CO pathway of CO2 reduction with computational hydrogen electrode model34. The conversion of CO2 to CO is an overall two-electron two-proton process. As demonstrated by the energy profile (Fig. 5b), the rate-determining step in this process is the first proton-coupled electron-transfer step in which the adsorbed *CO2 is transformed to *COOH, and the corresponding free energy changes are 1.2 eV, 0.6 eV, and 2.8 eV, respectively, on HNTM-Au-SA, HNTM-Co-SA, and HNTM-Cu-SA catalysts, which is qualitatively consistent with previous computational studies of CO2RR on Co and Cu phthalocyanine and porphyrin monolayers, despite differences in model designs and material structures35,36,37,38. The energy required for the CO2-to-COOH conversion on HNTM-Cu-SA is so high that it is not an active catalyst for CO production. It is further noted that different from the regular 5-coordination single-atom catalysts with only one active site23, the metal atom in HNTM-M-SA is anchored in the porphyrin plane and coordinated by four N atoms, so that it may simultaneously adsorb two CO2 molecules and catalyze the reduction reaction on both sides of the porphyrin plane. As illuminated in Fig. 5b, ΔG of the rate-limiting step is reduced from 1.2 eV to 0.8 eV on HNTM-Au-SA when one of the adsorbed *CO2 has been reduced to *COOH, whereas it is increased from 0.6 eV to 0.8 eV on HNTM-Co-SA, suggesting the CO2 activation on both sides of porphyrin plane may be synergic for HNTM-Au-SA. This synergistic catalysis mechanism for HNTM-Au-SA is illustrated in Fig. 5c, in which each Au atom has two active sites and it adsorbs two CO2 molecules and catalyzes their reduction synergistically. The proposed mechanism for the CO formation on HNTM-Au-SA gives rise to the lower potential of −0.9 V in corroboration with the experimental observation and the improved efficiency of CO2 reduction compared with HNTM-Co-SA with non-synergistic mechanism. It has thus explained the much higher TOF observed for CO production on HNTM-Au-SA than HNTM-Co-SA (25,425 h−1 vs. 1847 h−1 at −0.9 V under dark).
UV-vis diffuse reflection was performed to better understand the optical properties. All samples show strong absorption in the range of 200–800 nm, which is ascribed to photon absorption ability of porphyrin39. After single Au atom immobilized, HNTM-Au-SA exhibits higher visible light absorption (Supplementary Fig. 20a). Furthermore, the HNMT-Au-SA shows a lowest photoluminescence (PL) intensity, suggesting the most efficient charge separation occurred on coordinated single atom than encapsulating nanoparticles (Supplementary Fig. 20b). To compare the photo-induced electron transfer efficiency, the difference value between photocurrent respond at −0.8 and 0 V was calculated. HNTM-Au-SA shows the highest value of 0.50 mA, more than five times higher than HNTM-Au-NP, confirming that visible light can accelerate electron transfer to single Au atom than nanoparticles (Fig. 6a). More importantly, Fig. 6b clearly reveals that HNTM-Co-SA shows a higher Tafel slope of 1.21 V dec−1 under dark at the overpotential rang of 0.6–0.8 V, whereas it decreases to 0.78 V dec−1 under visible light, indicating visible light can facilitate a faster 1e− transfer from CO2 to CO2•−. We also measured the electrochemical impedance spectroscopy (EIS) to investigate the effect on the charge transfer resistance (Rct). As presented in Fig. 6c, EIS results show the Rct is 7.8 ohms under visible light vs. 8.5 ohms under dark condition, indicating the photoexcited porphyrin can efficiently facilitate charge transfer.
Mechanism for photo-coupled electrochemical and electrochemical CO2 reduction. a The difference between photocurrent response at −0.8 V and 0 V on HNTM-Au-SA, HNTM-Au-NP, and HNTM. b Tafel plots of HNTM-Co-SA under visible light (red line)/dark (black line). c EIS spectra of HNTM-Co-SA in Ar-(blue line)/CO2-saturated 0.1 M KHCO3 under visible light (red line)/dark (black line). d The electron transfer pathways under visible light and dark are shown in the left and right parts, respectively. e Transition orbital of T1 state under visible light. f Schematic representation of the excited states of porphyrin-Au
As illuminated by the frontier orbital analysis of porphyrin-Au, the electron of the vacant highest occupied molecular orbital (HOMO) is mostly localized on the porphyrin ligand, and that of the lowest unoccupied molecular orbital (LUMO) is mainly localized on the central metal atom. Under dark condition, external electrons can only flow to the LUMO, which need a high overpotential to excite across the HOMO-LUMO gap (in the right part of Fig. 6d). To illustrate the mechanism of photoelectrocatalysis and the effect of visible light, we further calculated the electronic properties of S1 and T1 excited states of these porphyrin-based catalysts. Both S1 and T1 exhibit clearly the ligand-to-metal charge-transfer excitation characteristic, which apparently facilitates the electron-flow and CO2 activation occurring on the single-Au-site (Fig. 6e). Upon the light absorption, porphyrin is first excited from the S0 ground state to the S1 state, and then undergoes fast relaxations to the ground state as well as the T1 triplet state through the intersystem crossing process. The spin-orbital coupling in heavy metal elements is so strong that the relaxation to this long-lived T1 state after the visible light irradiation is prominent. As all the photophysical processes occur much faster than the electrocatalysis process, we expect the photo-coupled electrocatalysis of CO2 proceeds mainly from the T1 state of porphyrin-Au instead of the S0 state, with the same mechanism proposed above (Fig. 5c). In addition, the energy required for T1 state is taken from the light absorption and no electricity is needed (Fig. 6f). The energy of T1 is 1.7 eV higher than the S0 state, which may result in the reduction of overpotential by ~ 130 mV (Fig. 6e). To our delight, the T1 states of HNTM-Cu-SA and HNTM-Co-SA are 1.5 eV and 0 eV, respectively, consistent with the overpotential shift of ~ 100 mV and 20 mV observed in experiment.
Discussion
In summary, we have successfully synthesized a series of photo-coupled electrocatalysts (HNTM-Au-SA, HNTM-Cu-SA, and HNTM-Co-SA) based on the structure of chlorophyll. When coupled with light, HNTM-Au-SA and HNTM-Co-SA achieve high FECO of 95.2% and 92.6%, as well as FEHCOO− of 77.2% on HNTM-Cu-SA. HNTM-Au-SA presents a volcano TOF curve with a maximum of 37,069 h−1 at −1.1 V under dark condition, whereas it positively shifts ~ 130 mV under visible light. The light-assisted TOF results show a positive shift of 20, 100, and 130 mV for HNTM-Co-SA, HNTM-Cu-SA, and HNTM-Au-SA, respectively, consistent with the calculated energy gaps of 0, 1.5, and 1.7 eV. Coupled with light field, the porphyrin ligand serves as a photoswitch to collect photons and motivate external electron transfer from ground state to T1 state. On the contrary, electrons can only transfer from the high-energy LUMO under dark conditions, resulting in high overpotential. This work provides a blueprint for the design of photo-coupled electrocatalysts at the atomic scale, utilizing porphyrin ligand as photosensitizer and coordinated metal atom as catalytic site.
Methods
Synthesis of HNTM-M-SA (Au, Co, Cu)
In a typical procedure, 2 mL DMF, 10 mg ZrCl4, 250 mg benzoic acid, and 200 μL H2O were added to 10 mL capacity Teflon-lined autoclave in sequence. After stirring for 5 min, 10 mg TCCP (detail synthetic process is shown Supplementary Methods) was further added in the above-mentioned solution and stirred for 10 min at room temperature. The autoclave was sealed and then heated at 120 °C for 18 h. The products were collected via centrifugation at 6000 r.p.m. for 3 min and further washed with ethanol for three times. HNTM was obtained after drying in vacuum drying oven at room temperature overnight.
In a typical procedure, 4 mL DMF, 20 mg HNTM, and 200 μL HAuCl4·4H2O aqueous solution (20 mg Au per mL) were added to a 10 mL Teflon-lined autoclave and then stirred for 10 min at room temperature. Next, the mixture was heated at 80 °C for 4 h. After cooling down, HNTM-Au-SA was separated via centrifugation at 10,000 r.p.m. for 3 min and further washed with ethanol for three times. For HNTM-Co-SA and HNTM-Cu-SA, the same concentration of CoCl2 and CuCl2·2H2O replaced HAuCl4·4H2O, respectively. HNTM-M-NP was also obtained by adding doubling dose of metal salts.
Material characterization
The as-prepared samples were characterized by TEM (HITACHI H-7700), high-resolution TEM (HRTEM, FEI Tecnai G2 F20), XRD (Bruker D8-advance), and XPS (PHI Quantera SXM), respectively. The BEs were corrected by the C1s peak at 284.8 eV. All the single atom catalysts were performed on HAADF-STEM (Titan 80–300). Metal loading was measured by ICP-OES (IRIS Intrepid II XSP, ThermoFisher). UV-vis diffuse reflectance spectra were obtained using a UV-vis spectrophotometer (UV-3600, Shimadzu). The PL spectra were carried out on a Varian Cary Eclipse Fluorescence spectrophotometer in a range of 420–850 nm. The CO and HCOOH produced from the 13CO2 labeling experiments were analyzed by GC-mass spectrometer (GC/MS-QP2010, Shimadzu) and 1H NMR, respectively.
The XAFS spectra were measured at 1W1B station in Beijing Synchrotron Radiation Facility. XAFS measurements at the Au L3-edge, Co K-edge, and Cu K-edge were conducted in fluorescence mode using a Lytle detector. The energy was calibrated using corresponding metal foil as references. The acquired EXAFS data were processed according to the standard procedures using the Athena program.
Photoelectrochemical measurements
Electrochemical measurements were carried out in a transparent H-cell with an electrochemical station (CHI 660E). Photoelectrochemical measurements were performed in the above-mentioned electrochemical system equipped with a 300 W Xe lamp (with > 420 nm cutoff filter, 67% solar intensity). The distance between the light source and H-cell was about 30 cm to keep electrolyte (0.1 M KHCO3 without a sacrificial regent) temperature stable at 25 °C. Five milligrams of catalyst and 5 mg Vulcan XC-72 were dispersed in 2 ml water–isopropanol solution with a volume ratio of 1:1. Nafion (20 μL; 5 wt%) was further added in the mixture and kept sonicating for 30 min to form a homogeneous ink. Then, 400 μL link was uniformly dropped onto the gas diffusion electrode (area: 1 cm × 2 cm) at room temperature, giving a catalyst loading of 0.5 mg cm−2. The gas diffusion electrode, Pt wire, and Ag/AgCl were used as working electrode, the counter electrode, and reference electrode, respectively. Reversible hydrogen electrode (RHE) potentials were calculated by the Nernst equation, ERHE = EAg/AgCl + 0.197 V + 0.0591 × pH.
Before measurements, CO2 gas (99.99%) was purged into the cathodic electrolyte at a rate of 20 s.c.c.m. for 30 min. During electrochemical and photoelectrochemical process, the flow rate of CO2 was controlled at 7 s.c.c.m. The LSVs scanned at 5 mv s−1 in N2- and CO2-saturated 0.1 M KHCO3. Collected gas products and liquid products were qualitatively and quantitatively analyzed by GC and 1H NMR. The mole number of gas products and liquid products were calculated from GC peak areas and 1H NMR peak areas based on standard curves of pure samples, respectively. The FE was calculated according to the following equation (1):
Where 96,485 is Faraday constant (C/mol), n is the amount of products per milliliter (mol/ml), 2 is the electron transfer number (CO, HCOOH, and H2), 7 is the flow rate of CO2 (mL min−1), 60 is reaction time (min), and Q is total charge obtained from chronoamperometry.
The TOF value of catalysts was calculated by the equation (2):
Where TOF is TOF (h−1), Iproduct is the partial current density of products (A), 2 is the electron transfer number for CO and HCOOH production, F is faraday constant (96,485 C mol−1), m is catalyst mass in the electrode (g), w is metal loading (Au, Co, Cu) on HNTM, and M is atomic mass.
DFT calculations
All the calculations including structural optimization, vibrational, and thermochemistry analysis were carried out using DFT with the Gaussian 16 package40. The PBE0 functional was used to treat the exchange-correlation energy and the long-range dispersion interaction was taken into account by Grimme’s D3 parameters. The 6–31 G* basis set was applied for the light elements including H, C, N, and O, and the LANL2DZ basis set and pseudopotential were used for the heavy metal elements such as Co, Cu, and Au. All the metal porphyrin complex structures were first fully optimized and then fixed with only adsorbed species relaxed in the later computations. The free energies of reactants, CO2 and H2, were corrected to reproduce ΔG298 = 0.208 eV for CO2RR to produce CO: CO2(g) + H2(g) → CO(g) + H2O(l).
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request. The source data underlying Figs. 2–4, 6a–c and Supplementary Figs 5–6, 11–19 are provided as a Source Data file at https://doi.org/10.6084/m9.figshare.8845793.v1 (https://doi.org/10.6084/m9.figshare.8845793)41.
References
Le Quér, C. et al. Global carbon budget 2014. Earth Syst. Sci. Data. 7, 47–85 (2015).
Wang, W., Wang, S., Ma, X. & Gong, J. Recent advances in catalytic hydrogenation of carbon dioxide. Chem. Soc. Rev. 40, 3703–3727 (2011).
Wesselbaum, S., Vom Stein, T., Klankermayer, J. & Leitner, W. Hydrogenation of carbon dioxide to methanol by using a homogeneous ruthenium-phosphine catalyst. Angew. Chem. Int. Ed. 51, 7499–7502 (2012).
Yu, J., Low, J., Xiao, W., Zhou, P. & Jaroniec, M. Enhanced photocatalytic CO2 reduction activity of anatase TiO2 by coexposed {001} and {101} facets. J. Am. Chem. Soc. 136, 8839–8842 (2014).
Yan, Z. H. et al. Photo-generated dinuclear {Eu(II)}2 active sites for selective CO2 reduction in a photosensitizing metal-organic framework. Nat. Commun. 9, 3353 (2018).
Habisreutinger, S. N., Schmidt-Mende, L. & Stolarczyk, J. K. Photocatalytic reduction of CO2 on TiO2 and other semiconductors. Angew. Chem. Int. Ed. 52, 7372–7408 (2013).
Qiao, J., Liu, Y., Hong, F. & Zhang, J. A review of catalysts for the electroreduction of carbon dioxide to produce low-carbon fuels. Chem. Soc. Rev. 43, 631–675 (2014).
Zhang, L., Zhao, Z. J. & Gong, J. Nanostructured materials for heterogeneous electrocatalytic CO2 reduction and their related reaction mechanisms. Angew. Chem. Int. Ed. 56, 11326–11353 (2017).
Reske, R., Mistry, H., Behafarid, F., Roldan Cuenya, B. & Strasser, P. Particle size effects in the catalytic electroreduction of CO2 on Cu nanoparticles. J. Am. Chem. Soc. 136, 6978–6986 (2014).
Hori, Y., Murata, A. & Takahashi, R. Formation of hydrocarbons in the electrochemical reduction of carbon dioxide at a copper electrode in aqueous solution. J. Chem. Soc. 85, 2309 (1989).
Zhu, D. D., Liu, J. L. & Qiao, S. Z. Recent advances in inorganic heterogeneous electrocatalysts for reduction of carbon dioxide. Adv. Mater. 28, 3423–3452 (2016).
Zheng, X. et al. Theory-guided Sn/Cu alloying for efficient CO2 electroreduction at low overpotentials. Nat. Catal. 2, 55–61 (2018).
Jiang, K. et al. Metal ion cycling of Cu foil for selective C–C coupling in electrochemical CO2 reduction. Nat. Catal. 1, 111–119 (2018).
De Luna, P. et al. Catalyst electro-redeposition controls morphology and oxidation state for selective carbon dioxide reduction. Nat. Catal. 1, 103–110 (2018).
Neyts, E. C., Ostrikov, K., Sunkara, M. K. & Bogaerts, A. Plasma catalysis: synergistic effects at the nanoscale. Chem. Rev. 115, 13408–13446 (2015).
Jang, J. W. et al. Aqueous-solution route to zinc telluride films for application to CO2 reduction. Angew. Chem. Int. Ed. 53, 5852–5857 (2014).
Wang, L. et al. Ni-foam-supported and amine-functionalized TiO2 photocathode improved photoelectrocatalytic reduction of CO2 to methanol. J. Catal. 349, 1–7 (2017).
Xu, Y. et al. Photoelectrocatalytic reduction of CO2 to methanol over the multi-functionalized TiO2 photocathodes. Appl. Catal. B 205, 254–261 (2017).
Johnson, D. G. et al. Photochemical electron transfer in chlorophyll-porphyrin-quinone triads: the role of the porphyrin-bridging molecule. J. Am. Chem. Soc. 115, 5692–5701 (1993).
Gale, P. A., Sessler, J. L., Král, V. & Lynch, V. Calix[4]pyrroles: old yet new anion-binding agents. J. Am. Chem. Soc. 118, 5140–5141 (1996).
Tanaka, T. & Osuka, A. Conjugated porphyrin arrays: synthesis, properties and applications for functional materials. Chem. Soc. Rev. 44, 943–969 (2015).
Kuhl, K. P. et al. Electrocatalytic conversion of carbon dioxide to methane and methanol on transition metal surfaces. J. Am. Chem. Soc. 136, 14107–14113 (2014).
Pan, Y. et al. Design of single-atom Co-N5 catalytic site: a robust electrocatalyst for CO2 reduction with nearly 100% CO selectivity and remarkable stability. J. Am. Chem. Soc. 140, 4218–4221 (2018).
He, T. et al. Zirconium-porphyrin-based metal-organic framework hollow nanotubes for immobilization of noble-metal single atoms. Angew. Chem. Int. Ed. 57, 3493–3498 (2018).
Yang, H. & Wang, X. Secondary-component incorporated hollow MOFs and derivatives for catalytic and energy-related applications. Adv. Mater. 30, 1800743 (2018).
Jiang, H. L. et al. An exceptionally stable, porphyrinic Zr metal-organic framework exhibiting pH-dependent fluorescence. J. Am. Chem. Soc. 135, 13934–13938 (2013).
Huo, Z., Tsung, C. K., Huang, W., Zhang, X. & Yang, P. Sub-two nanometer single crystal Au nanowires. Nano lett. 8, 2041–2044 (2008).
Chen, Z. et al. Single-site Au(I) catalyst for silane oxidation with water. Adv. Mater. 30, 1704720 (2018).
Zhao, G. et al. Co-porphyrin/carbon nitride hybrids for improved photocatalytic CO2 reduction under visible light. Appl. Catal. B 200, 141–149 (2017).
Morris, A. J., Meyer, G. J. & Fujita, E. Molecular approaches to the photocatalytic reduction of carbon dioxide for solar fuels. Acc. Chem. Res. 42, 1983–1994 (2009).
Zhao, C. et al. Ionic exchange of metal-organic frameworks to access single nickel sites for efficient electroreduction of CO2. J. Am. Chem. Soc. 139, 8078–8081 (2017).
Smith, P. T. et al. Iron porphyrins embedded into a supramolecular porous organic cage for electrochemical CO2 reduction in water. Angew. Chem. Int. Ed. 57, 9684–9688 (2018).
Yang, H. B. et al. Atomically dispersed Ni(I) as the active site for electrochemical CO2 reduction. Nat. Energy 3, 140–147 (2018).
Zhu, W. et al. Monodisperse Au nanoparticles for selective electrocatalytic reduction of CO2 to CO. J. Am. Chem. Soc. 135, 16833–16836 (2013).
Xu, L., Yang, L. & Ganz, E. Mn–graphene single-atom catalyst evaluated for CO oxidation by computational screening. Theor. Chem. Acc. 137, 98 (2018).
Liu, J., Yang, L. & Ganz, E. Efficient and selective electroreduction of CO2 by single-atom catalyst two-dimensional TM–Pc monolayers. ACS Sustain. Chem. Eng. 6, 15494–15502 (2018).
Liu, J., Yang, L. & Ganz, E. Electrochemical reduction of CO2 by single atom catalyst TM–TCNQ monolayers. J. Mater. Chem. A 7, 3805–3814 (2019).
Liu, J., Yang, L. & Ganz, E. Electrocatalytic reduction of CO2 by two-dimensional transition metal porphyrin sheets. J. Mater. Chem. A 7, 11944–11952 (2019).
Li, L. L. & Diau, E. W. Porphyrin-sensitized solar cells. Chem. Soc. Rev. 42, 291–304 (2013).
Frisch, M. J. et al. Gaussian 16, Revision. A.03 (2016).
Yang, D. Source Data figure share https://doi.org/10.6084/m9.figshare.8845793.v1 (2019).
Acknowledgements
This work was supported by National Key R & D Program of China (2017YFA0700101 and 2016YFA0202801) and NSFC (21431003). We thank Beijing Synchrotron Radiation Facility (BSRF) for providing the EXAFS tests in 1W1B station. We thank Dr. Haifang Li for providing GC-MS tests.
Author information
Authors and Affiliations
Contributions
X.W. led the whole project. D.Y. synthesized the catalysts, performed TEM, XRD, XPS, XAFS, ICP, UV-vis, PL, and electrochemical and photoelectrochemical measures, data analysis, and wrote the manuscript. H.Yu performed DFT calculation and edited the manuscript. T.H. guided synthetic process. S.Z. performed XAFS measurements and analysis. X.L. and L.G. performed HAADF-STEM measurements. B.N. guided the usage of GC and performed HRTEM measurements. H.Yang and H.L. edited the manuscript. D.W. guided DFT calculation and edited the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information: Nature Communications thanks the anonymous reviewers for their contributions to the peer review of this work. Peer review reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, D., Yu, H., He, T. et al. Visible-light-switched electron transfer over single porphyrin-metal atom center for highly selective electroreduction of carbon dioxide. Nat Commun 10, 3844 (2019). https://doi.org/10.1038/s41467-019-11817-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-11817-2
This article is cited by
-
Developing silicon-based photocathodes for CO2 conversion
Science China Chemistry (2024)
-
Rational design of ZnCdS/TpPa-1-COF heterostructure photocatalyst by strengthening the interface connection in solar hydrogen production reactions
Nano Research (2023)
-
Dynamically modulated synthesis of hollow metal-organic frameworks for selective hydrogenation reactions
Nano Research (2023)
-
Sub-nanomaterials for Photo/Electro-catalytic CO2 Reduction: Achievements, Challenges, and Opportunities
Chemical Research in Chinese Universities (2023)
-
Ultrathin zirconium-porphyrin based nanobelts as photo-coupled electrocatalysis for CH4 oxidation to CO
Nano Research (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.