Abstract
In order to effectively use glycerol as a fuel in direct glycerol fuel cells, a catalyst that can break the C–C bond and enhance the electro-oxidation of glycerol to CO2 is necessary. In this particular investigation, a palladium-nickel-tin nanocomposite electrodeposited on a glassy carbon electrode (PdNiSn/GC) exhibited excellent activity towards the electro-oxidation of glycerol, thanks to the synergistic effect of the catalyst composition. The PdNiSn/GC surface generated a peak current (Ip) that was 2.5 times higher than that obtained at a Pd/GC electrode, with a cathodic shift in the onset potential (Eonset) of approximately 300 mV. Additionally, the current obtained at the PdNiSn/GC surface remained stable during continuous electrolysis. Capacitance measurements were used to interpret the results of the electrocatalytic activity, and high-performance liquid chromatography indicated that the products of the glycerol electro-oxidation reaction were oxalic acid and formic acid, which were subsequently oxidized to CO2, as revealed by the charge calculations. The results depict that the synergy between Pd, β-Ni(OH)2, and SnO2 is crucial for boosting GEOR through enhancing the C–C bond cleavage and completely oxidize the reaction intermediates to CO2.
Similar content being viewed by others
Introduction
The continuous expansion in commercial activities and the gradual rising in population growth have directly increased the energy demand and necessitated finding alternative energy resources to fossil fuels. Amongst, the efficient utilization of chemical fuels in fuel cells has a great potential to contribute in an efficient and CO2-zero emission energy systems1.
Considering the different types of fuel cells, the polymer electrolyte membrane fuel cells offer numerous benefits over the other types of fuel cells, e.g.; high energy density, quick energy release; insensitivity to CO2 allowing the use of air as an oxidant, and operating at moderate temperatures (75–150 °C)2,3.
The use of alcohols, in particular glycerol, in the direct alcohol fuel cell is an interesting target for the fuel in such a scheme. Glycerol electrooxidation reaction (GEOR) could take place at the surface of electrocatalysts through the oxidation of its hydroxyl groups in order to generate electrical energy4. Furthermore, GEOR produces high theoretical energy density of 6 kWh kg−1, it is non-flammable and non-volatile5, and has low crossover rate through the membrane when compared to methanol6. In addition, the selective GEOR could produce value-added intermediates. Thus, another promising aspect of GEOR is the electrosynthesis of value-added molecules such as; glyceric acid, tartronic acid, mesoxalate, and 1,3-dihydroxyacetone7,8,9.
Glycerol is a common product from biodiesel industry which produces approximately hundreds of millions of kilograms of glycerol each year making it an available and low-price fuel10,11,12,13. In addition, glycerol is considered a good source for hydrogen production14,15. Thermodynamics depict that glycerol electro-oxidation reaction (GEOR) in the anodic compartment of DGFCs is energetically more efficient than oxygen evolution reaction (OER) in the electrolysis cell for the production of hydrogen9,10. GEOR takes place in the anodic compartment of the DGFCs producing protons and carbon dioxide while protons are reduced in the cathodic compartment producing hydrogen as shown in Eqns. 1–311.
However, the efficient and complete oxidation of glycerol into CO2 in the direct glycerol fuel cells (DGFCs) is still a great challenge as this process is multielectron and multiproton process which requires C–C bond cleavage (major challenge in electrocatalysis).
Pt electrocatalyst was considered to be the most efficient catalyst for the DGFC due to its high activity16,17,18,19, however, the production of the poisoning CO intermediate at its surface during the oxidation scheme of glycerol along with its high cost has limited its use16,20,21. This has motivated the use of alternative electrocatalysts, e.g., Pd, Ag, and Ni in order to boost the performance of the DGFC. In this regard, Pd-based electrocatalysts are considered a good candidate for the DGFC due to their advantages over the Pt-based electrocatalysts16. Pd shows better activity towards alcohols oxidation in the alkaline medium than Pt does22,23,24,25. In addition, the chance of the electrode poisoning by adsorbed carbon monoxide (COads) in alkaline medium is less than the acidic medium as the chemisorbed intermediates weakly bonds to the catalyst surface and the amount of poisoning species is less in alkaline medium26.
A lot of work was done to improve the effectiveness of Pd catalyst towards glycerol electro-oxidation, this includes adding another metal to Pd surface in order to increase its activity. It also includes, the employment of high surface area carbon materials as electrode material, e.g., carbon nanotubes (CNTs), activated carbon, and carbon nanofibers due to their good physiochemical properties and good resistance to corrosion27.
The current study focuses on tailoring and designing an efficient electro-catalyst for GEOR. Employing noble metal-based materials for GEOR could subject them to be compromised by the strongly adsorbed CO poison28,29. Thus, adding other catalysts is intended to increase the catalyst’s tolerance towards CO poisoning based on bifunctional and electronic effects30.
In this study, PdNiSn nanocomposite is electrodeposited at the glassy carbon (GC) electrode surface utilizing a simple electrochemical method then examined towards GEOR. The synergy between the component of the catalyst is believed to introduce a uniform dispersion of the nanoparticles and thus increase the number of active sites available for OH− adsorption/desorption, GEOR, and the oxidation of CO. This work will highlight the role of Pd in offering a suitable surface for the glycerol molecules adsorption and oxidation, and the role of Sn in making the Ni quickly restore its highly active state.
The selection of the catalyst and the preparation method are believed to introduce a structural organization that facilitates the oxidation of the glycerol and the reaction intermediates to CO2 and suppress the formation of the poisoning CO. It is aimed to evaluate the effect of incorporating Ni and Sn atoms/oxides in the catalyst structure on the performance of GEOR. Not only that, the catalyst surface will be proved to be suitable for energy storage applications through evaluating its real capacitance.
Experimental
Electrodes, pre-treatments, and measurements
In this study, a three-electrode electrochemical cell was utilized. The working electrode was a glassy carbon electrode (diameter = 3.0 mm), while the reference electrode was Ag/AgCl/KCl (saturated), and a spiral Pt wire was used as the counter electrode. Prior to use, the GC electrode was smoothed using alumina (0.5 μm down to 0.05 μm), then rinsed successively with distilled water and sonicated in ethanol and water31,32,33,34. It is important to note that all potentials were converted from Ag/AgCl to RHE using the following equation:
where Eo(Ag/AgCl) = 0.1976 V at 25° C and E(Ag/AgCl) is the working potential.
The chemicals used were supplied from Sigma-Aldrich and the solutions were prepared using double distilled water.
A VersaSTAT 4 potentiostat operated with VersaStudio software was used for the electrochemical measurements which were all performed at room temperature. The electrochemical measurements of glycerol electro-oxidation reaction (GEOR) were performed in 0.1 M KOH containing 0.3 M glycerol (no iR-correction).
Electrochemical impedance spectroscopy (EIS) measurements were conducted at open circuit potential within the frequency range from 100 to 30 mHz. Then, EIS curves (Zre − Zim) were turned into capacitance curves (Cre − Cim) using VersaStudio software. The equivalent circuit diagram for this system is shown in Fig. 4, with the inset indicating the charge transfer resistance (Rct) of the electrode/electrolyte interface associated with GEOR, the solution resistance (Rs), and constant phase element (CPE) of the double layer capacitance, respectively.
Electrode’s modification
To deposit the PdNiSn nanocomposite on the surface of the GC electrode, potential step electrolysis was used, with the potential ranging from 0 to − 1 V vs. Ag/AgCl/KCl (saturated) for a duration of 3 min. The electrolysis was performed using a solution of 50 mM of NaNO3 (purged with N2), which contained 1 mM of each metal ion salt35. It should be noted that SnCl2 can slowly hydrolyze to form Sn(OH)Cl, resulting in a slightly milky appearance of the solution, indicating the formation of Sn(OH)Cl.
Materials characterization
The characterization of the morphology and composition of the prepared catalysts were performed using a field-emission scanning electron microscope (FE-SEM, FEGESEM, model Quattro S, supplied by Thermo Scientific USA) joined with energy dispersive X-ray spectroscopy (EDS, EDAX genitive). The structures of Pd and PdNiSn nanocomposite crystals were characterized using X-ray diffraction (XRD, PANalytical, X’Pert PRO) operated with Cu target, l = 1.54 Å, and scan speed = 0.05°/s. The products formed as a result of GEOR at PdNiSn/GC electrode were identified utilizing a high performance liquid chromatography (HPLC, Aglient 1100) integrated with a diode array detector at wavelength of 228 nm. The incorporated column was μ Bondapak C18 10 μm 125 A with an eluent 0.1% phosphoric acid (flow rate = 0.5 mL min−1).
Results and discussion
Materials characterization
Figure 1A and 1A’ show the FE-SEM images of PdNiSn/GC electrode before and after the reaction. They show that the particles are uniformly distributed at the GC electrode surface and the particle size is ranging between 70 and 90 nm.
On the other side, the exact composition of the catalyst and the relative surface composition are confirmed by EDS analysis (Fig. 1B and the table inserted therein). In this figure, the characteristic peaks of Pd, Ni, and Sn appear in their position which emphasises that all the components of the nanocomposite are effectively deposited at the GC electrode surface.
Additionally, the crystallographic structure of the prepared nanocomposite is identified using XRD (Fig. 1C). The figure illustrates the XRD patterns of Pd/GC (Fig. 1C, curve a) and PdNiSn/GC (Fig. 1C, curve b). In both curves, a broad peak is observed that extends from 2θ of 20° to 28° which corresponds to C(002) of GC electrode36. Moreover, four peaks of Pd metal are obtained at 2θ of ca. 39.7°, 43.2°, 67.2° and 78° related to Pd(111), Pd(200), Pd(220) and Pd(311) planes of face centred cubic (FCC) structure, respectively33,34. At PdNiSn/GC electrode (Fig. 1C, curve b), the same peaks appeared at Fig. 1C, curve a are observed in addition to other peaks at 2θ of 19.2°, 33.4°, and 59.4° assigned for Ni(001), Ni(100), and Ni(110) planes of \(\beta \)-Ni(OH)2 of the Ni-containing catalyst1,37,38, in addition, one more peak at 2θ of 51.7° related to Sn(211) plane of SnO2 is observed. The other three planes of SnO2; Sn(110), Sn(101), and Sn(301) appear at 2θ of 26.5°, 33.8°, and 65.8° and overlap with the C(002) peak of carbon, Ni(100) plane of \(\beta \)-Ni(OH)2, and Pd(220) plane of Pd metal, respectively1.
Glycerol Electro-oxidation reaction (GEOR) and capacitance correlation
Figure 2A and Table 1 compare the electrocatalytic activity obtained at Pd/GC (Fig. 2A., curve a) and PdNiSn/GC with molar ratio of Pd:NiSn = 1:1:1 (Fig. 2A. curve b) towards GEOR. The figure and the table illustrate that the peak current (Ip) of GEOR obtained at PdNiSn/GC (Pd:Ni:Sn = 1:1:1) surface is 1.6 times of that obtained at Pd/GC surface plus cathodic shift in the onset potential (Eonset) of GEOR of ca. 200 mV. These results highlight the role of Ni and Sn oxides (\(\beta \)-Ni(OH)2 and SnO2) in boosting the ability of Pd to enhance the oxidation of glycerol and the reaction intermediates by increasing the charge transfer in the media.
Moreover, the optimization of the molar ratio of Pd:Ni:Sn in PdNiSn nanocomposite was crucial. Figure 2B shows the LSVs obtained at PdNiSn/GC with molar ratio of Pd:Ni:Sn = 1:1:1 (curve a), 1:1:2 (curve b), 1:2:1 (curve c), and 2:1:1 (curve d) electrodes in 0.1 M KOH containing 0.3 M glycerol. Figure 2B and Table 1 disclose that the highest electrocatalytic activity of GEOR is obtained when the molar ratio of Pd:Ni:Sn = 2:1:1 (Fig. 2B, curve d), where the Ip of GEOR is 2.5 of that obtained at Pd/GC plus cathodic shift in Eonset of GEOR = 300 mV.
Actually, the Ip value (17.5 mA cm−2) obtained at PdNiSn/GC with molar ratio of Pd:Ni:Sn = 2:1:1 towards GEOR is higher than that obtained at similar electro-catalysts in the literature (Table 2). It is about 4 and 3 times of that obtained at polycrystalline Pt incorporated with Pb and Bi (Ptp-Pb, Ptp-Bi), respectively39. Moreover, Ip obtained at PdNiSn/GC is 15 times of that obtained at 10% Pt/WC and 19 times of that obtained at 10% Pt/TaC40. In addition, Ip obtained at PdNiSn/GC is 7 times of that obtained at PdFe/rGO41. On the other hand, it is 35 and 12.5 times of that obtained at Pd/C and PdCu/C, respectively42. Furthermore, the electrocatalytic activity obtained at PdNiSn/GC is 13 and 6.5 times of that obtained at Pt and Pd electrodeposited on carbon paper (Pt/CP and Pd/CP), respectively 43.
The results of the electrocatalytic activity obtained at the ternary structures of PdNiSn towards GEOR were interpreted by correlating this activity with the results of the capacitance obtained at the same electrodes in the same solution. Figure 3 (curves a-e) shows the capacitance curves of Pd/GC (curve a), PdNiSn/GC (molar ratio = 1:1:1, curve b), PdNiSn/GC (molar ratio = 1:1:2, curve c), PdNiSn/GC (molar ratio = 1:2:1, curve d), and PdNiSn/GC (molar ratio = 2:1:1, curve e) in 0.1 M KOH containing 0.3 M glycerol. The figure reveals that the real capacitance (Cre) values obtained at these electrodes are compatible with the values of the electrocatalytic activity of GEOR and the increase in Ip values (Fig. 2A and B) is consistent with the increase in Cre values (Fig. 3). For instance, both, Ip and Cre values obtained at PdNiSn (2:1:1) is about 2.5 times of those obtained at Pd/GC electrode.
These results clarify that the reason behind the obtained catalysis is due to the catalyst composition and the solution content. In other words, PdNiSn (with molar ratio = 2:1:1) offers a favourable conditions for the adsorption of glycerol molecules at its surface, then, the number of the charged adsorbed species is increased consequently (Fig. 3, curve e), leading to a significant enhancement in GEOR at its surface (Fig. 2B, curve d).
Stability of PdNiSn/GC electrode towards GEOR
Furthermore, PdNiSn/GC (molar ratio = 2:1:1) shows an excellent repeatability and reproducibility. Figure 4A shows that the Ip of GEOR obtained at its surface remained at almost the same value after 300 potential cycle. In addition, the current transient curves (Fig. 4B) were obtained at Pd/GC (curve a), PdNiSn/GC (molar ratio = 1:1:1, curve b), PdNiSn/GC (molar ratio = 1:1:2, curve c), PdNiSn/GC (molar ratio = 1:2:1, curve d), and PdNiSn/GC (molar ratio = 2:1:1, curve e) electrodes in 0.1 M KOH containing 0.3 M glycerol. They disclose that the overall stability in the current followed similar behaviors among the first four systems studied (Fig. 4B, curves a-d), where the currents obtained at their surfaces diminished to more than half of their initial values at the first 30 min. of the experiment and continued to decay until the end of the hour-long experiment. However, the current obtained at PdNiSn/GC (molar ratio = 2:1:1, curve e) electrode shows a very high stability with just a slight decay in the current obtained at its surface. This reflects the high tolerance of PdNiSn/GC (molar ratio = 2:1:1, curve e) electrode against the poisoning intermediate species by preventing their adsorption or facilitating their oxidation to a final product. The catalyst composition and ingredients’ ratio are believed to be the reason behind the obtained reinforcement in the stability of the current at the electrode surface (Fig. 4B, curve e).
Discussion
Figure 5 identifies the oxidation products obtained from GEOR at PdNiSn/GC electrode after 6 h of accumulation of the products at E = 0.77 vs. RHE. It depicts that only two products are obtained; oxalic acid (C2 species, 68%) and formic acid (C1 species, 32%) which highlights the high selectivity of the prepared catalyst to produce two products of interest from GEOR. This result discloses the following: (i) PdNiSn catalyst could efficiently oxidize all the glycerol molecules in the sample, (ii) there are two possible reaction pathways for GEOR at PdNiSn catalyst (Fig. 6), starting from glyceric acid (glcerate); the first one proceeds via the consecutive electro-oxidation of the functional groups without breaking or attacking the C–C bond producing glycolic acid (glycolate) through two electron transfer reaction, then, glycolic acid is further oxidized to oxalic acid (oxalate) through four electron transfer reaction 41,44 and the second one proceeds via the cleavage of the C–C bond and the electro-oxidation of the C1 fragments producing formic acid (formate) through two electron transfer reaction41,44.
Moreover, the amount of charge (Q) consumed during GEOR to oxalic acid (Qoxalic acid) and to formic acid (Qformic acid) was calculated using their relative peak areas in the HPLC pattern. These values were estimated as 1.38 and 0.6 C for Qoxalic acid and Qformic acid, respectively. The addition of the two values (1.98 C) is below that recorded for GEOR (Qglycerol) during glycerol electrolysis (3.6 C). This difference highlights that there is other oxidation product was formed, e.g., formic acid could further been oxidized to CO2 which consumes a part of (Qglycerol). N.B., the percentage (%) of the two acids (oxalic acid and formic acid) in the above calculations were probed using their relative peak intensities in the HPLC pattern for the products of GEOR.
The HPLC results (Fig. 5) together with the charge calculations show that PdNiSn catalyst has high selectivity to CO2 through enhancing the electro-oxidation of formic acid and oxalic acid to CO2.
These results point towards the synergistic effect between Pd, Ni(OH)2, and SnO2 in PdNiSn nanocomposite. This synergy enhanced the ability of Pd to cleave the C–C bond and completely oxidize the reaction intermediates.
Conclusion
The surface of PdNiSn nanocomposite electrodeposited at GC electrode (PdNiSn/GC) offered an efficient electro-oxidation of glycerol in this study. PdNiSn/GC (with a molar ratio of Pd:Ni:Sn = 2:1:1) exhibited both the highest capacitance and the highest electrocatalytic activity towards glycerol electrooxidation reaction (GEOR), when compared to Pd/GC, PdNiSn/GC (molar ratio of Pd:Ni:Sn = 1:1:1), PdNiSn/GC (molar ratio of Pd:Ni:Sn = 1:1:2), and PdNiSn/GC (molar ratio of Pd:Ni:Sn = 1:2:1) electrodes. Furthermore, PdNiSn/GC (molar ratio of Pd:Ni:Sn = 2:1:1) offered the highest current stability among all of the aforementioned electrodes. HPLC analysis revealed that GEOR resulted in the production of two products, oxalic acid (C2 species) and formic acid (C1 species). The results of the HPLC analysis, as well as the charge calculations, indicated that the synergistic effect between Pd, β-Ni(OH)2, and SnO2 played an essential role in promoting GEOR by enhancing C–C bond cleavage and completely oxidizing the reaction intermediates to CO2.
Data availability
All data generated or analysed during this study are included in this published article.
References
Jongsomjit, S., Prapainainar, P. & Sombatmankhong, K. Synthesis and characterisation of Pd–Ni–Sn electrocatalyst for use in direct ethanol fuel cells. Solid State Ionics 288, 147–153 (2016).
Li, Q., Aili, D., Hjuler, H. A. & Jensen, J. O. High Temperature Polymer Electrolyte Membrane Fuel Cells 1st edn. (Springer, 2015).
Silva, R. G. D., Neto, S. A., Kokoh, K. B. & Andrade, A. R. D. Electroconversion of glycerol in alkaline medium: From generation of energy to formation of value-added products. J. Power Sources 351, 174–82 (2017).
Zhang, Z., Xin, L. & Li, W. Electrocatalytic oxidation of glycerol on Pt/C in anion-exchange membrane fuel cell: Cogeneration of electricity and valuable chemicals. Appl. Catal. B Environ. 119–120, 40–48 (2012).
Arechederra, R. L., Treu, B. L. & Minteer, S. D. Development of glycerol/O2 biofuel cell. J. Power Sources 173, 156–161 (2007).
Livshits, V. & Peled, E. Progress in the development of a high-power, direct ethylene glycol fuel cell (DEGFC). J. Power Sources 161, 1187–1191 (2006).
Palma, L. M. et al. Effect of co-catalyst on the selective electrooxidation of glycerol over ruthenium-based nanomaterials. ChemElectroChem 4, 39–45 (2017).
Kwon, Y., Thomas, J. P. & Hersbach, Koper MTM. Electro-oxidation of glycerol on platinum modified by adatoms: Activity and selectivity effects. Top. Catal. 57, 1272–6 (2014).
Simões, M., Baranton, S. & Coutanceau, C. Electrochemical valorisation of glycerol. Chemsuschem 5, 2106–2124 (2012).
Santos, E. C. et al. Efficient screening of Bi–metallic electrocatalysts for glycerol valorization. Electrochim Acta 398, 139283 (2021).
Houache, M. S. E., Hughesa, K. & Baranova, E. A. Study on catalyst selection for elec- trochemical valorization of glycerol. Sustain. Energy Fuels 3, 1892–1915 (2019).
Huang, L. et al. Co-generation of electricity and formate in glycerol fuel cells with a bifunctional PdPtAg alloy nanowire electrocatalyst. Green Chem. 24, 9721–9733 (2022).
Sun, H. et al. Boosting ethanol oxidation by NiOOH-CuO nano-heterostructure for energy-saving hydrogen production and biomass upgrading. Appl. Catal. B Environ. 325, 122388 (2023).
Ambat, I., Srivastava, V. & Sillanpää, M. Recent advancement in biodiesel produc- tion methodologies using various feedstock: A review. Renew. Sustain. Energy Rev. 90, 356–369 (2018).
Budžaki, S., Miljic, G., Tišma, M., Sundaram, S. & Hessel, V. Is there a future for enzymatic biodiesel industrial production in microreactors?. Appl Energy 201, 124–34 (2017).
Klaas, L., Modibedi, M., Mathe, M., Su, H. & Khotseng, L. Electrochemical studies of pd-based anode catalysts in alkaline medium for direct glycerol fuel cells. Catalysts. 10, 968 (2020).
Alvarez, G. F. A., Mamlouk, M. & Scott, K. An investigation of palladium oxygen reduction catalysts for the direct methanol fuel cell. Int. J. Electrochem. 2011, 684535 (2011).
He, Q. et al. Dramatically enhanced cleavage of the C–C bond using an electrocatalytically coupled reaction. J. Am. Chem. Soc. 134, 8655–8661 (2012).
Ribeiro, J. et al. Carbon-supported ternary PtSnIr catalysts for direct ethanol fuel cell. Electrochim Acta 52, 6997–7006 (2007).
Xue, X. et al. Enhancement of the electrooxidation of ethanol on Pt-Sn-P/C catalysts prepared by chemical deposition process. J. Power Sources 172, 560–569 (2007).
Jiang, L., Colmenares, L., Jusys, Z., Sun, G. Q. & Behm, R. J. Ethanol electrooxidation on novel carbon supported Pt/SnOx/C catalysts with varied Pt: Sn ratio. Electrochim Acta 53, 377–389 (2007).
Geraldes, A. N. et al. Palladium and palladium-tin supported on multi-wall carbon nanotubes or carbon for alkaline direct ethanol fuel cell. J. Power Sources 275, 189–199 (2015).
Yi, Q., Chu, H., Chen, Q., Yang, Z. & Liu, X. High-performance Pd, PdNi, PdSn and PdSnNi nanocatalysts supported on carbon nanotubes for electrooxidation of C2–C4 alcohols. Electrocatalysis 27, 388–397 (2015).
Waje, M. M., Li, W., Chen, Z. & Yan, Y. Durability investigation of cup-stacked carbon nanotubes supported Pt as PEMFC catalyst. ECS Trans. 3, 677–683 (2006).
Yuan, X.-Z., Song, C., Wang, H. & Zhang, J. Electrochemical Impedance Spectroscopy in PEM Fuel Cells (Springer, 2010).
Yu, E. H., Krewer, U. & Scott, K. Principles and materials aspects of direct alkaline alcohol fuel cells. Energies 3, 1499–1528 (2010).
Hernandez, R., Dunning, C. Direct methanol fuel cells. In Electrocatalysts for Direct Methanol Fuel Cells. New York: Nova Science Publishers (2017).
Wendt, H., Spinacé, E. V., Neto, A. O. & Linardi, M. Electrocatalysis and electrocatalysts for low temperature fuel cells: Fundamentals, state of the art, research and development. Quim Nova. 28, 1066–1075 (2005).
Antolini, E. Catalysts for direct ethanol fuel cells. J. Power Sources 170, 1–12 (2007).
Holade, Y., Servat, K., Napporn, T. W. & Kokoh, K. B. Electrocatalytic properties of nanomaterials synthesized from “Bromide Anion Exchange” method-Investigations of glucose and glycerol oxidation. Electrochim Acta 162, 205–214 (2015).
Cui, F. & Zhang, X. A method based on electrodeposition of reduced graphene oxide on glassy carbon electrode for sensitive detection of theophylline. J. Solid State Electrochem. 17, 167–173 (2013).
El-Deab, M. S., El-Nowihy, G. H. & Mohammad, A. M. Synergistic enhancement of the electro-oxidation of methanol at tailor-designed nanoparticle-based CoOx/MnOx/Pt ternary catalysts. Electrochim. Acta 165, 402–409 (2015).
El-Nowihy, G. H. & El-Deab, M. S. Boosted electrocatalytic oxidation of formic acid at CoOx/Pd/Au nanoparticle-based ternary catalyst. Int. J. Hydrog. Energy 45, 21297–21307 (2020).
El-Nowihy, G. H. & El-Deab, M. S. Smart selection of fuel blends: Robust oxidation of formic acid in its blend with urea at NiOx/Pd nanoparticles-based binary anodes. Renew. Energy 167, 830–840 (2021).
Roy, N. et al. Facile deposition of Cu-SnOx hybrid nanostructures on the lightly boron-doped diamond electrodes for CO2 reduction. ChemElectroChem 5, 2542–2550 (2018).
Wang, L. et al. One-step synthesis of Pt–NiO nanoplate array/reduced graphene oxide nanocomposites for nonenzymatic glucose sensing. J. Mater. Chem. A. 3, 608 (2015).
Narayan, R. T. Effect of crystallinity of B- and Bbc-nickel hydroxide samples on chemical cycling. Indian J. Eng. Mater. Sci. 2015, 1–7 (2015).
Wu, Z. et al. Electrostatic induced stretch growth of homogeneous β-Ni(OH)2 on graphene with enhanced high-rate cycling for supercapacitors. Sci. Rep. 4, 3669 (2014).
de Matheus, B. C. S. et al. Pb- and Bi-modified Pt electrodes toward glycerol electrooxidation in alkaline media. Activity, selectivity, and the importance of the Pt atoms arrangement. ACS Catal. 10, 2131–7 (2020).
Mou, H. et al. Enhancing glycerol electrooxidation from synergistic interactions of platinum and transition metal carbides. Appl. Catal. B Environ. 316, 121648 (2022).
Cassani, A. et al. Fe-Modified Pd as an effective multifunctional electrocatalyst for catalytic oxygen reduction and glycerol oxidation reactions in alkaline media. ACS Appl. Energy Mater. 4, 9944–9960 (2021).
Maya-Cornejo, J. et al. Synthesis of Pd-Cu bimetallic electrocatalyst for ethylene glycol and glycerol oxidations in alkaline media. Procedia Chem. 12, 19–26 (2014).
Arjona, N. et al. Glycerol electro-oxidation in alkaline media using Pt and Pd catalysts electrodeposited on three-dimensional porous carbon electrodes. New J. Chem. 41, 1854 (2017).
Han, X. et al. Electrocatalytic oxidation of glycerol to formic acid by CuCo2O4 spinel oxide nanostructure catalysts. ACS Catal. 10, 6741–6752 (2020).
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
G.H.El-N.: Conceptualization, Methodology, Investigation, Formal analysis, Writing – review & editing.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
El-Nowihy, G.H. Tailor-designed nanoparticle-based PdNiSn catalyst as a potential anode for glycerol fuel cells. Sci Rep 13, 13244 (2023). https://doi.org/10.1038/s41598-023-40374-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-40374-4
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.