Abstract
Materials can be transformed from one crystalline phase to another by using an electric field to control ion transfer, in a process that can be harnessed in applications such as batteries1, smart windows2 and fuel cells3. Increasing the number of transferrable ion species and of accessible crystalline phases could in principle greatly enrich material functionality. However, studies have so far focused mainly on the evolution and control of single ionic species (for example, oxygen, hydrogen or lithium ions4,5,6,7,8,9,10). Here we describe the reversible and non-volatile electric-field control of dual-ion (oxygen and hydrogen) phase transformations, with associated electrochromic2 and magnetoelectric11 effects. We show that controlling the insertion and extraction of oxygen and hydrogen ions independently of each other can direct reversible phase transformations among three different material phases: the perovskite SrCoO3−δ (ref. 12), the brownmillerite SrCoO2.5 (ref. 13), and a hitherto-unexplored phase, HSrCoO2.5. By analysing the distinct optical absorption properties of these phases, we demonstrate selective manipulation of spectral transparency in the visible-light and infrared regions, revealing a dual-band electrochromic effect that could see application in smart windows2,9. Moreover, the starkly different magnetic and electric properties of the three phases—HSrCoO2.5 is a weakly ferromagnetic insulator, SrCoO3−δ is a ferromagnetic metal12, and SrCoO2.5 is an antiferromagnetic insulator13—enable an unusual form of magnetoelectric coupling, allowing electric-field control of three different magnetic ground states. These findings open up opportunities for the electric-field control of multistate phase transformations with rich functionalities.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on SpringerLink
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnature22389/MediaObjects/41586_2017_Article_BFnature22389_Fig1_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnature22389/MediaObjects/41586_2017_Article_BFnature22389_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnature22389/MediaObjects/41586_2017_Article_BFnature22389_Fig3_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnature22389/MediaObjects/41586_2017_Article_BFnature22389_Fig4_HTML.jpg)
Similar content being viewed by others
References
Tarascon, J. M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001)
Granqvist, C. G. Electrochromics for smart windows: oxide-based thin films and devices. Thin Solid Films 564, 1–38 (2014)
Steele, B. C. H. & Heinzel, A. Materials for fuel-cell technologies. Nature 414, 345–352 (2001)
Jeong, J. et al. Suppression of metal-insulator transition in VO2 by electric field-induced oxygen vacancy formation. Science 339, 1402–1405 (2013)
Katase, T., Suzuki, Y. & Ohta, H. Reversibly switchable electromagnetic device with leakage-free electrolyte. Adv. Electron. Mater. 2, 1600044 (2016)
Close, T., Tulsyan, G., Diaz, C. A., Weinstein, S. J. & Richter, C. Reversible oxygen scavenging at room temperature using electrochemically reduced titanium oxide nanotubes. Nat. Nanotechnol. 10, 418–422 (2015)
Ji, H., Wei, J. & Natelson, D. Modulation of the electrical properties of VO2 nanobeams using an ionic liquid as a gating medium. Nano Lett. 12, 2988–2992 (2012)
Shibuya, K. & Sawa, A. Modulation of metal–insulator transition in VO2 by electrolyte gating-induced protonation. Adv. Electron. Mater. 2, 1500131 (2016)
Llordés, A., Garcia, G., Gazquez, J. & Milliron, D. Tunable near-infrared and visible-light transmittance in nanocrystal-in-glass composites. Nature 500, 323–326 (2013)
Lu, Q. & Yildiz, B. Voltage-controlled topotactic phase transition in thin-film SrCoOx monitored by in situ X-ray diffraction. Nano Lett. 16, 1186–1193 (2016)
Schmid, H. Multi-ferroic magnetoelectrics. Ferroelectrics 162, 317–338 (1994)
Jeen, H. et al. Reversible redox reactions in an epitaxially stabilized SrCoOx oxygen sponge. Nat. Mater. 12, 1057–1063 (2013)
Muñoz, A. et al. Crystallographic and magnetic structure of SrCoO2.5 brownmillerite: neutron study coupled with band-structure calculations. Phys. Rev. B 78, 054404 (2008)
Tsujimoto, Y. et al. Infinite-layer iron oxide with a square-planar coordination. Nature 450, 1062–1065 (2007)
Zhou, Y. et al. Strongly correlated perovskite fuel cells. Nature 534, 231–234 (2016)
Hayward, M. et al. The hydride anion in an extended transition metal oxide array: LaSrCoO3H0.7 . Science 295, 1882–1884 (2002)
Kobayashi, Y. et al. An oxyhydride of BaTiO3 exhibiting hydride exchange and electronic conductivity. Nat. Mater. 11, 507–511 (2012)
Yoon, H. et al. Reversible phase modulation and hydrogen storage in multivalent VO2 epitaxial thin films. Nat. Mater. 15, 1113–1119 (2016)
Simon, P. & Gogotsi, Y. Materials for electrochemical capacitors. Nat. Mater. 7, 845–854 (2008)
Ueno, K. et al. Electric-field-induced superconductivity in an insulator. Nat. Mater. 7, 855–858 (2008)
Yamada, Y. et al. Electrically induced ferromagnetism at room temperature in cobalt-doped titanium dioxide. Science 332, 1065–1067 (2011)
Yuan, H. T. et al. Electrostatic and electrochemical nature of liquid-gated electric-double-layer transistors based on oxide semiconductors. J. Am. Chem. Soc. 132, 18402–18407 (2010)
Mitra, C., Meyer, T., Lee, H. N. & Reboredo, F. A. Oxygen diffusion pathways in brownmillerite SrCoO2.5: influence of structure and chemical potential. J. Chem. Phys. 141, 084710 (2014)
Karvonen, L. et al. O-K and Co-L XANES study on oxygen intercalation in perovskite SrCoO3-δ . Chem. Mater. 22, 70–76 (2010)
Bora, D. K. et al. Influence of crystal structure, ligand environment and morphology on Co L-edge XAS spectral characteristics in cobalt compounds. J. Synchrotron Radiat. 22, 1450–1458 (2015)
Liu, X. S. et al. Why LiFePO4 is a safe battery electrode: Coulomb repulsion induced electron-state reshuffling upon lithiation. Phys. Chem. Chem. Phys. 17, 26369–26377 (2015)
Shan, X. Q. et al. Bivalence Mn5O8 with hydroxylated interphase for high-voltage aqueous sodium-ion storage. Nat. Commun. 7, 13370 (2016)
Katayama, T. et al. Topotactic synthesis of strontium cobalt oxyhydride thin film with perovskite structure. AIP Adv. 5, 107147 (2015)
Chen, C. T. et al. Experimental confirmation of the x-ray magnetic circular dichroism sum rules for iron and cobalt. Phys. Rev. Lett. 75, 152–155 (1995)
Zhao, T. et al. Electrical control of antiferromagnetic domains in multiferroic BiFeO3 films at room temperature. Nat. Mater. 5, 823–829 (2006)
Zhou, Y. & Ramanathan, S. Relaxation dynamics of ionic liquid-VO2 interfaces and influence in electric double-layer transistors. J. Appl. Phys. 111, 084508 (2012)
Nakano, M. et al. Collective bulk carrier delocalization driven by electrostatic surface charge accumulation. Nature 487, 459–462 (2012)
Li, Q. et al. Quantitative probe of the transition metal redox in battery electrodes through soft x-ray absorption spectroscopy. J. Phys. D 49, 413003 (2016)
Wernet, Ph . et al. The structure of the first coordination shell in liquid water. Science 304, 995–999 (2004)
Smith, J. D. et al. Energetics of hydrogen bond network rearrangements in liquid water. Science 306, 851–853 (2004)
de Groot, F. M. F. et al. Oxygen 1s x-ray-absorption edges of transition metal oxides. Phys. Rev. B 40, 5715 (1989)
Kim, Y.-M. et al. Probing oxygen vacancy concentration and homogeneity in solid-oxide fuel-cell cathode materials on the subunit-cell level. Nat. Mater. 11, 888–894 (2012)
Marrocchelli, D. et al. Understanding chemical expansion in non-stoichiometric oxides: ceria and zirconia case studies. Adv. Funct. Mater. 22, 1958–1965 (2012)
Ohta, H. et al. Field-induced water electrolysis switches an oxide semiconductor from an insulator to a metal. Nat. Commun. 1, 118 (2010)
Min, H., Wettmarshausen, S., Friedrich, J. F. & Unger, W. E. S. A ToF-SIMS study of the deuterium-hydrogen exchange induced by ammonia plasma treatment of polyolefins. J. Anal. At. Spectrom. 26, 1157–1165 (2011)
Bouilly, G. et al. Electrical properties of epitaxial thin films of oxyhydrides ATiO3-xHx (A = Ba and Sr). Chem. Mater. 27, 6354–6359 (2015)
Denis Romero, F. et al. Strontium vanadium oxide-hydrides: “square-planar” two-electron phases. Angew. Chem. Int. Ed. 53, 7556–7559 (2014)
Tassel, C. et al. Direct synthesis of chromium perovskite oxyhydride with a high magnetic-transition temperature. Angew. Chem. Int. Ed. 53, 10377–10380 (2014)
Ichikawa, N. et al. Reduction and oxidation of SrCoO2.5 thin films at low temperatures. Dalton Trans. 41, 10507–10510 (2012)
Nakano, M. et al. Infrared-sensitive electrochromic device based on VO2 . Appl. Phys. Lett. 103, 153503 (2013)
Mercier, V. M. & Slius, P. Toward solid-state switchable mirrors using a zirconium oxide proton conductor. Solid State Ion. 145, 17–24 (2001)
Dahlman, C. J. et al. Electrochemically induced transformations of vanadium dioxide nanocrystals. Nano Lett. 16, 6021–6027 (2016)
Li, Z. Y. et al. Correlated perovskites as a new platform for super-broadband-tunable photonics. Adv. Mater. 28, 9117–9125 (2016)
Wang, Q. et al. Vacancy induced semiconductor-insulator-metal transitions in nonstoichiometric nickel and tungsten oxides. Nano Lett. 16, 7067–7077 (2016)
Sato, T. et al. Electrochemical properties of novel ionic liquids for electric double layer capacitor applications. Electrochim. Acta 49, 3603–3611 (2004)
Acknowledgements
This study was financially supported by the National Basic Research Program of China (grants 2015CB921700, 2016YFA0301004 and 2015CB921002); the National Natural Science Foundation of China (grants 11274194, 51561145005, 51332001 and 11334006); the Initiative Research Projects of Tsinghua University (grant 20141081116); and the Beijing Advanced Innovation Center for Future Chip (ICFC). L.G. acknowledges support from the National Program on Key Basic Research Project (2014CB921002) and the Strategic Priority Research Program of Chinese Academy of Sciences (XDB07030200) and National Natural Science Foundation of China (grants 51522212, 51421002 and 51672307). The Advanced Light Source is supported by the US Department of Energy under contract no. DE-AC02-05CH11231.
Author information
Authors and Affiliations
Contributions
P.Y. conceived the project and designed the experiments. N.L., Y.W., Z.D. and Z.L. fabricated the thin films. N.L. performed the ILG, X-ray diffraction, magnetic and optical measurements, with H.-B.L. Y.W., S.Y. and M.W. P.Z. performed the theoretical analysis and calculations, under the supervision of J.W. Q.Z. performed the scanning transmission electron microscopy measurements, under the supervision of L.G. and C.-W.N. R.Q., J.G. and M.Y. performed the room-temperature soft X-ray absorption measurements, under the supervision of S.Z. and W.Y. Q.H., J.G. and E.A. performed the low-temperature soft X-ray magnetic circular dichroism measurements. D.Z., H.-B.L. and N.L. performed the electrical transport measurements. Y.T. discussed the results. N.L. and P.Y. wrote the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Reviewer Information Nature thanks D. Milliron, S. Ramanathan and the other anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Figure 1 XRD results for the three distinct phases.
a, c, e, Reciprocal space mapping of thin films of a, SrCoO2.5, c, SrCoO3−δ and e, phase A (HSrCoO2.5) in the (103) crystalline plane of the LSAT substrate. Å−1 represents the reciprocal space units, and Q100 and Q001 represent projected directions in the reciprocal space. b, d, f, XRD rocking curves around the peaks of b, SrCoO2.5 (008), d, SrCoO3−δ (002) and f, phase A (HSrCoO2.5) (008).
Extended Data Figure 2 ILG-induced phase transformations.
a–d, In situ XRD results obtained near the LSAT(002) peak during phase transformations from: a, SrCoO2.5 to phase A (HSrCoO2.5); b, phase A (HSrCoO2.5) to SrCoO2.5; c, SrCoO2.5 to SrCoO3−δ; and d, SrCoO3−δ to SrCoO2.5, with fixed gating voltages of +3.5 V, −2.3 V, −2.7 V and +1.8 V, respectively. The dashed horizontal lines indicate when the phase transformation occurred. e–h, Summarized gating durations for transformations from: e, SrCoO2.5 to phase A (HSrCoO2.5); f, phase A (HSrCoO2.5) to SrCoO2.5; g, SrCoO2.5 to SrCoO3−δ; and h, SrCoO3−δ to SrCoO2.5, with different gating voltages. The gating duration is defined as the time required for the phase transformation to complete. All gating durations of less than 2,000 minutes were obtained from the in situ XRD measurements shown in a–d; for extended gating durations (more than 2,000 minutes), the data were obtained from the ex situ gating experiments (e, g). The black squares in e and g indicate that the initial SrCoO2.5 phase remains unchanged even after a gating duration of 2,880 minutes. Red and blue points correspond to negative and positive gating voltages, respectively. The vertical dashed lines indicate the electrolysis voltage of water. i, X-ray photoelectron spectroscopy measurements of the as-grown SrCoO2.5 (green) and ILG-induced SrCoO3−δ (red) and HSrCoO2.5 (blue) phases, grown on LSAT(001) substrate. The peaks represent the electron-binding energy of the specific atomic orbitals in selected elements. LMM and KLL refer to states in Auger electron spectroscopy. j, k, Reversible electric-field-induced, well defined transformations between SrCoO2.5 and phase A (HSrCoO2.5) (j) and between SrCoO2.5 and SrCoO3−δ (k) at selected gating voltages. The films of material were 50 nm thick. The gating experiments were performed in air with the as-received ionic liquid DEME-TFSI.
Extended Data Figure 3 Thickness and strain dependence of the phase transformations.
a, In situ XRD measurements of phase transformations in films with thicknesses of 20 nm, 50 nm and 100 nm, grown on LSAT(001) substrate. The top and bottom panels show ILG with positive and negative voltages, respectively. b, Thickness dependence of gating durations for films grown on the LSAT(001) substrate. c, In situ XRD measurements during phase transformations for films with different strain states. The compressive strain is calculated on the basis of the difference in lattice constant between the substrates (LaAlO3, LSAT and SrTiO3) and the bulk SrCoO2.5 phase. d, Strain dependence of gating durations.
Extended Data Figure 4 Structural and compositional analysis of the three phases.
a, HAADF-STEM results with the calculated lattice structures (shown in the insets) of SrCoO2.5 and SrCoO3−δ. The zone axis is along the [110] direction of the LSAT substrate. b, Statistical analysis of the in-plane strontium–strontium interatomic distances for the three phases, and their comparison with theoretical calculations. c, Chemical expansion during phase transformations. d, Energy-dispersive X-ray spectroscopy results for as-grown SrCoO2.5 (green) as well as ILG-induced SrCoO3−δ (red) and HSrCoO2.5 (blue), grown on LSAT(001) substrate. Error bars represent the standard deviation of the measurements.
Extended Data Figure 5 Calculated crystalline lattice configurations.
a–c, Three possible lattice configurations for SrCoO2, based on first-principle calculations, with: a, parallel oxygen-vacancy channels; b, orthogonal oxygen-vacancy channels; or c, infinite planar lattice structure. Calculated lattice constants and total energies are also given. For reference, the lattice constants and total energy of SrCoO2.5 are: a = 5.65 Å; b = 5.51 Å; c = 15.76 Å; Etotal = −218.30 eV. d–g, Calculated crystalline lattice configurations for HySrCoO2.5 when y equals: d, 0.125; e, 0.25; f, 0.5; and g, 1.0.
Extended Data Figure 6 Stability tests for HSrCoO2.5 and SrCoO3−δ.
a, b, XRD θ–2θ scans for thin films of a, HSrCoO2.5 and b, SrCoO3−δ grown on LSAT(001) substrate, as a function of time after ILG-induced formation followed by storage at room temperature (25 °C) and in a 1 atm air environment with relative humidity of 40%. The diffraction peaks of HSrCoO2.5 remain nearly unchanged even after 11 days, suggesting that this phase is a robust equilibrium state. Meanwhile, for SrCoO3−δ, a negligible shift in the peak position (of about 0.1°) was observed after 11 days, suggesting that this phase still holds the structure of perovskite, with the occurrence of a tiny amount of oxygen vacancies. (Interestingly, with a similar hydrogenated system (HVO2), the structure gradually returns to that of the dehydrogenated VO2 phase after 8 days at room temperature, owing to the slow release of hydrogen18.) c, d, In situ temperature-dependent XRD θ–2θ scans for thin films of c, HSrCoO2.5 and d, SrCoO3−δ around the LSAT(002) peak, annealed in a 1 atm oxygen gas (oxidizing) or a 1 atm argon gas (reducing) environment, respectively. The crystalline structures of both phases remain stable up to 175–195 °C, above which they change into the brownmillerite SrCoO2.5. The SrCoO2.5 phase is a thermodynamic equilibrium state, which is stable at temperatures up to 350 °C in mild oxidizing or reducing environments, owing to the robustness of the Co3+ valence state.
Extended Data Figure 7 Mechanism underlying ILG-induced phase transformations.
a, Proposed origin of H+ and O2− ions during ILG: the water inside the ionic liquid is decomposed into negatively charged O2− and positively charged H+ ions through electrolysis. b, Gating current (IG) as a function of gating voltage (VG). c, Comparison of SIMS spectra around m/z ≈ 2.0 for samples gated with the as-received ionic liquid DEME-TFSI containing water (H2O), or the developed ionic liquids EMIM-BF4 and DEME-TFSI containing heavy water (D2O). d, Depth profiles of the D+ ions in films gated with the developed ionic liquids containing heavy water.
Extended Data Figure 8 Universal proof of ILG-induced phase transformations.
a–d, XRD θ–2θ scans for typical as-grown SrCoO2.5 samples (green), and after positive (blue) and negative (red) voltage gating using the following hydrophobic ionic liquids: a, EMIM-TFSI, and b, HMIM-TFSI; also with c, the hydrophilic EMIM-BF4; as well as with d, the aqueous electrolyte NaOH (1 mol per litre). e, Residual water concentrations of ionic liquids, determined by the Karl Fischer titration method. Quoted errors represent the standard deviation of the measurements. The results show that the ILG-induced phase transformations occur with all of these ionic liquids, and that even the hydrophobic ionic liquids have enough residual water to achieve the phase transformation, confirming the generic nature of the ILG-induced phase transformations.
Extended Data Figure 9 Transient optical transmission spectra during phase transformations.
a, b, Time evolution of optical transmission spectra from 50-nm-thick SrCoO2.5 films grown on double-sided polished LSAT(001) substrate, with gating voltages of a, +3.5 V and b, −2.7 V. The results show clear phase transformations from SrCoO2.5 to HSrCoO2.5 (a), and from SrCoO2.5 to SrCoO3−δ (b). VIS, visible light; NIR, near-infrared.
Extended Data Figure 10 Comparison of the optical absorptions and calculated densities-of-states for the three phases.
a, Optical absorptions of the three phases, plotting α (the optical absorption) versus ħω (the photon energy). Below a photon energy of 4.0 eV, there are two main absorption features in all three phases, which can be attributed to the intraband d–d transition (lower-energy end; the absorption peaks α, σ and δ) and interband p–d transition (higher-energy end; the absorption peaks β, ε and γ). Consistent with our electrical transport studies, we find that the SrCoO3−δ is metallic, with strong absorption among the whole optical range studied here. However, both SrCoO2.5 and HSrCoO2.5 show insulating behaviour, with strong absorption spectra emerging around the interband transitions (β and ε). Furthermore, the absorption by SrCoO2.5 is even greater than that of the metallic SrCoO3−δ phase at higher energies (greater than 2.5 eV), owing to the large p–d excitation. However, the absorption by HSrCoO2.5 is strongly suppressed compared with that by SrCoO2.5, owing to enhancement of the direct bandgap. b–d, Calculated total and projected density of states (DOS) onto oxygen 2p, CoT (tetragonal layer) and CoO (octahedral layer) orbitals for: b, SrCoO2.5; c, HSrCoO2.5; and d, SrCoO3. In comparison with SrCoO2.5, the bandgap of HSrCoO2.5 becomes larger, owing to the ascension of the unoccupied cobalt 3d state. For SrCoO3, the Fermi energy level cuts into the oxygen 2p and cobalt 3d DOS, consistent with the metallic nature of this phase suggested by our electrical transport studies.
Rights and permissions
About this article
Cite this article
Lu, N., Zhang, P., Zhang, Q. et al. Electric-field control of tri-state phase transformation with a selective dual-ion switch. Nature 546, 124–128 (2017). https://doi.org/10.1038/nature22389
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nature22389
This article is cited by
-
On-device phase engineering
Nature Materials (2024)
-
Reconfigurable optoelectronic transistors for multimodal recognition
Nature Communications (2024)
-
Dynamic-to-static switch of hydrogen bonds induces a metal–insulator transition in an organic–inorganic superlattice
Nature Chemistry (2024)
-
Effect of Ni doping on the microstructure and electrical properties of Ba–Co–O NTC ceramics
Journal of Materials Science: Materials in Electronics (2024)
-
Electrolyte-gated SrCoOx FET sensor for highly sensitive detecting pH in extreme alkalinity solution
Nano Research (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.