Abstract
We investigated the band gap of SiZnSnO (SZTO) with different Si contents. Band gap engineering of SZTO is explained by the evolution of the electronic structure, such as changes in the band edge states and band gap. Using ultraviolet photoelectron spectroscopy (UPS), it was verified that Si atoms can modify the band gap of SZTO thin films. Carrier generation originating from oxygen vacancies can modify the band-gap states of oxide films with the addition of Si. Since it is not easy to directly derive changes in the band gap states of amorphous oxide semiconductors, no reports of the relationship between the Fermi energy level of oxide semiconductor and the device stability of oxide thin film transistors (TFTs) have been presented. The addition of Si can reduce the total density of trap states and change the band-gap properties. When 0.5 wt% Si was used to fabricate SZTO TFTs, they showed superior stability under negative bias temperature stress. We derived the band gap and Fermi energy level directly using data from UPS, Kelvin probe, and high-resolution electron energy loss spectroscopy analyses.
Similar content being viewed by others
Introduction
Amorphous oxide semiconductors (AOSs) have gained much attention over the past decades as candidate materials for next-generation thin film transistors (TFTs). These materials have applications in integrated multilayered microelectronics, flat panel displays, and flexible displays1,2,3. Currently, great efforts have been made to enhance the performance and the stability of oxide TFTs by optimising the gate insulator, electrode, active channel layers, and TFT structure4,5,6,7,8. In particular, amorphous InGaZnO (a-IGZO) has been extensively investigated due to its favourable properties, including high field effect mobility, large area uniformity, and long-term stability9,10,11. Numerous studies have reported AOS TFTs with several multicomponent oxide semiconductors, such as InGaZnO, ZnSnO, and HfGaZnO12,13,14. Recently, indium free materials, like zinc-tin oxide (ZTO), have been extensively studied for the use of active channel layer of TFTs. Oxide-based multicomponent semiconductors have several advantages over conventional Si-based semiconductors, such as visible light transparency, large area deposition at low temperature, and high carrier mobility. For ZTO TFTs, the high mobility comes from an increase in the population of charge carriers (electrons) originating from oxygen vacancies. However, too many deep trap levels within the band gap can lead to instability of the device during operation15,16, such as large off currents and a depletion mode with a large threshold voltage shift17,18,19.
For high performance and stable device operation, it is important to optimize the O-deficiency and deep state formation20,21,22,23. In a previous study, it was found that the Si atoms could suppress the oxygen deficiency, due to the high bonding strength with oxygen17. Therefore, doping with Si atoms can be a strategy to enhance the electrical characteristics as well as the device stability. However, the role of the Si dopant atoms in the ZTO films regarding TFT device performance and stability is not yet clear. Investigation of the basic semiconducting properties, such as the Fermi-level and energy band gap configuration, including the position of the valence band maximum (VBM) and the conduction band minimum (CBM) are key properties related to the carrier concentration and the mobility of the films for AOS TFT operation. In this study, we examined Si doped ZTO TFTs in which the active semiconductor layers were AOS thin films and the Fermi energy level could be controlled by changing the Si doping ratio. To investigate the effect of Si doping on the ZTO semiconductor, the energy band diagrams were carefully derived by combining the results of Kelvin probe microscopy (KP), ultraviolet photoelectron spectroscopy (UPS), and high-resolution electron energy loss spectroscopy (HR-EELS) measurements. In addition, to investigate the effect of Si doping of ZTO on the electrical characteristics of SZTO TFTs, a series of TFTs with different Si ratios were fabricated and characterized in terms of the Si doping concentration.
Results and Discussion
The diffraction patterns of the SZTO layers revealed typical amorphous behaviour, as shown in Fig. 1; A (undoped ZTO), B (0.3 wt% SZTO), and C (0.5 wt% SZTO). The ZTO and SZTO thin films directly deposited on the SiO2 layer on the substrate showed an amorphous phase (no peaks were observed). In addition, the addition of Si atoms increased the average crystallite size of SZTO films, resulting in an increased surface roughness24. The root-mean-square surface roughness of films A, B, and C were 0.38, 0.46, and 0.48 nm, respectively. Figure 2 shows the electrical properties of undoped and doped SZTO TFTs with different amounts of Si from current-voltage (I-V) curves. The field effect mobility of samples A, B, and C decreased from 14.9 cm2/V s to 7.9 cm2/V s, respectively. Table 1 summarizes the electrical characteristics of Si doped ZTO TFTs depending on various Si ratio. The dependence of the electrical properties on the silicon ratio could be related to the defect concentration in the thin films. Oxygen vacancies, acting as trap states in the oxide materials, deteriorate the electrical properties, leading to a large shift in the threshold voltage, low mobility, and high sub-threshold swing25. Typically, the addition of Si atoms decreases the carrier concentration of an oxide semiconductor due to the high bond strength of Si-O (799.6 kJ/mol) compared with those of Sn-O (531.8 kJ/mol) and Zn-O (395 kJ/mol)10. In previous work, we investigated the electronic structure of the present SZTO compound and the energetic formation of the oxygen deficient state through first principles calculations26. The effective mass of an electron carrier (m*) tends to increase with increasing Si concentration, meaning that the electronic structure sensitively responds to any lattice fluctuation related with a change in the conduction band position. To understand the origin of the change in the electrical properties, the chemical states of the films were examined by X-ray photoemission spectroscopy (XPS). Figure 3(a) shows the O1s XPS spectra for films A, B, and C. The binding energy of photoelectrons was calibrated using the C1s peak at 284.25 eV as a reference. The O1s peak on the surface was fitted by three Gaussians peaks; labelled (OI), (OII), and (OIII). The lowest energy sub-peak (OI) at 530.25 eV was assigned to the oxygen-binding region of the matrix without oxygen vacancies, and the medium energy sub-peak (OII) at 531.62 eV is associated with the oxygen-deficient regions27,28. The highest energy sub-peak (OIII) at 532.5 eV is related to the metal hydroxide peak29. The density of the oxygen-deficient bonding state (OII) decreased with increasing Si ratio, as shown by the relative ratios of the OII peak in Fig. 3(b). The relative ratio of the OII peaks of films A, B, and C decreased from 46.4% to 39.5%, respectively. This result clearly indicates that the concentration of oxygen vacancies (VO) decreased, probably resulting in a decrease in the carrier concentration with increasing Si content. Even though the individual contribution of VO to the electrical performance was not quantified precisely, the formation of VO results in the generation of charge carriers due to the increase of free electrons, explained by the electron charge trapping model. Figure 4 shows the evolution of the transfer curves over time obtained at a drain-to-source voltage (VDS) of 5 V for films A, B, and C under negative bias temperature stress (NBTS). The NBTS was kept at a gate-to-source voltage (VGS) of −20 V and VDS of 10.1 V over 7,200 s at 60 °C. The formation of O-deficient states is easily suppressed by Si-doping due to the strong binding energy with oxygen30,31. SZTO TFT (0.5 wt%) showed a threshold voltage shift (ΔVth) of 0.9 V. The strong bonding strength of silicon suppressed VO formation, resulting in a decrease in the carrier concentration. However, there are problems explaining the behaviour of the electrical characteristics of oxide semiconductors using only the O1s peak mechanism. The O1s peak analysed by XPS can only explain the oxygen related defects in the metal-oxide structure, such as the occupied electron trap states in the oxide semiconductor. It has been proposed that the oxygen deficiency generated by the removal of oxygen atoms separated from the lattice primarily produces deep and localized states near the VBM32. Moreover, Duke et al.32,33,34,35 suggested a reconstructed model of the prism face. In addition, it could be expected that we could control the electrical performances and the stability of TFTs by changing the band offset. This implies that the addition of Si atoms can control the Fermi level related with the change in carrier concentration in amorphous oxide n-type semiconductors. Therefore, it is very important to derive the energy band diagram to investigate any changes in the electron carrier concentration and explain the behaviour of the electrical characteristics. To obtain further insight into the band gap structure of SZTO TFTs with different Si ratios, a typical valence band was measured by UPS. He (II) UPS spectra are shown in Fig. 5. The secondary electron cut-off energy (SC) and the valence band edge energy (EVBE) were derived using a linear extrapolation of the leading edges to the backgrounds of the spectra. From these extracted values, the valence band energies were obtained analogously using equation (1)36,
where hv is the incident He (II) line energy at 40.813 eV37 and EVBE is defined as the energy separation between the VBM edge and the Fermi level. It is clear that the valence band spectra changed with Si doping of the SZTO system. In order to elucidate the origin of the observed band-gap changes, HR-EELS spectra were obtained using a 1.5 keV exciting electron beam, as shown in Fig 6(a). HR-EELS is capable of analysing electronic and optical properties of oxide materials because the low-energy-loss region reflects the valence and conduction band structures of solids. All spectra showed a strong elastic peak, followed by a flat and featureless region and then a broad energy loss peak. The onset of the energy loss peak in the spectrum gives the energy gap corresponding to that particular scattering geometry. The band-gaps of films A, B, and C were estimated by the linear fit method (Fig. 6(b)), yielding values of 3.88, 4.11, and 4.21 eV, respectively. As the Si ratio increased, the bandgap widened. We also used KP to measure the work function of SZTO thin films, where the measured contact potential difference was calibrated using an in situ sputtered Au reference sample38,39. The valence band and band gap values calculated from UPS and HR-EELS allowed us to estimate the position of the conduction band (Ec)40. The experimentally determined band gaps are shown in Fig. 7. Thecorresponding values of the band gaps of ZTO and SZTO (0.3, 0.5 wt %) thin films were 3.88, 3.82, and 4.09 eV, respectively. The band gap and energy level values are reported in Table 2 for each oxidethin film. The field effect mobility decreased from 14.9 to 7.9 cm2/V s with doping mainly caused by the decrease of the electron carrier concentration at 0.3 and 0.5 wt% Si content. It has been reported that a low carrier concentration can lead to low mobility in oxide TFTs due to the suppression and passivation of oxygen vacancies41. However, it is still uncertain why the addition of Si changed the electrical characteristics. After adding Si atoms (0.3 and 0.5 wt %), a drastic increase in the ΔECB from 0.467 to 0.897 eV was observed42. The wave function of the CBM is characterized mainly by Sn-5s and Zn-4s orbitals in the ZTO thin film. That is, increasing the CBM relative to the vacuum level will lead to an increase in the work function, provided that the Fermi level stays close to the CBM. Actually, the Si4+ ions incorporated in the ZTO matrix do not generate carriers in the SZTO, because the Si4+ ions substituted into the Sn4+ ion sites may work as oxygen binders for oxygen out-diffusion, thereby suppressing the formation of oxygen vacancies. This oxygen-related defect model has usually been explained as the electron charge trapping mechanism in oxide TFTs43,44. The carrier transport is governed by percolation conduction over trap states and is enhanced at high carrier concentrations by filling the trap states. The decrease in the carrier concentration is explained by the increase in ΔECB. Therefore, the role of Si ions as oxygen binders in the SZTO materials is the reason for the stability improvement and band edge changes in the SZTO TFT.
In conclusion, the control of the carrier concentration and mobility in SZTO TFTs has been demonstrated, where the incorporation of Si suppresses the carrier concentration. However, a small amount of Si doping in SZTO TFTs improves the electrical properties due to a decrease in ΔECB. We observed that the Si atoms in SZTO TFTs significantly affected the electrical properties. This investigation of the band gap characteristics of SZTO TFTs through UPS, KP, and EELS analyses provided a sufficient guideline for determining favourable oxide TFT characteristics leading to improved electrical properties.
Conclusion
In summary, the relationship between the change of the energy band gap due to doping suppressors and the stability of TFTs due to oxygen vacancy has been verified. We have derived energy band diagrams for ZTO and SZTO thin films using EELS, UPS, and KP measurements. The effect of Si on the device performance of ZTO and SZTO TFTs has been systematically investigated. Increasing the Si content resulted in a change in the electrical conduction properties due to changes in the band structure. The work function of ZTO TFTs was found to be strongly dependent on the Si content. As the Si concentration increased, the Fermi level of the SZTO TFTs decreased. In addition, widening of the ΔECB relative to the vacuum level resulted in an increase in the work function. Si doping affected the band alignments including the band gap and CBM, VB, and Ef, which in turn changed the electrical characteristics. Direct derivation of the energy band diagram could explain the enhancement of the stability of the TFTs due to the suppression of oxygen vacancies, resulting in a decrease in the defects in the band gap and carrier generation.
Methods
Device fabrication
First, a typical ultrasonic wafer cleaning process was used. SZTO films were deposited on Si wafers with a 200 nm thickness of SiO2 by radio frequency (RF) magnetron sputtering at room temperature followed by a standard lithography and wet etching process to pattern the film. Ceramic targets of SZTO (diameter of 2 in) were prepared by sintering mixtures of Si, Zn and Sn powders. The Si contents of the sputtering targets were 0, 0.3, and 0.5 wt.%, where the Zn: Sn ratio was fixed at 1:1. SZTO films of 50 nm thickness were deposited by RF magnetron sputtering at a processing pressure of 0.6 Pa and a sputtering power of 50 W. Photolithography and wet-etching was then performed and the width/length (W/L) of the active layer was patterned with 250/50 μm. After developing the photoresist, the source and drain electrodes were deposited using Ti/Au (10/50 nm) using an e-beam or thermal evaporation process, respectively. Annealing of the fabricated devices was carried out in N2 at 500 °C for 2 h. A poly methyl-methacrylate (PMMA) layer was deposited as a passivation layer over the channel layer by spin coating.
Characterisation
All current-voltage (I-V) measurements were conducted using a semiconductor parameter analyser (EL423, ELECS Co.) at room temperature in a dark box. The crystallinity of the SZTO films was analysed using X-ray diffraction (XRD, modified Philips-1880) using CuKα radiation. The film morphology was observed using a JEOL JSPM-5200 atomic force microscope (AFM). UPS measurements were conducted in ultra-high vacuum (~10−10 mbar) where the samples were irradiated with 40.813 eV photons (He II line). For each sample, the work function was calculated from the UPS spectrum by subtracting the energy of the incident beam from the difference between the Fermi edge and the low-energy cut-off of secondary electrons. A commercial Kelvin probe system was used to measure the work function changes of the SZTO films. This apparatus measures the contact potential difference between a reference plate and the surface of silicon indium zinc oxide (SIZO). The 10 mm diameter probe plate was made of stainless steel and was electrically connected via ground to the sample during the measurement.
Additional Information
How to cite this article: J. Y. Choi et al. Engineering of band gap states of amorphous SiZnSnO semiconductor as a function of Si doping concentration. Sci. Rep. 6, 36504; doi: 10.1038/srep36504 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Nomura, K. et al. Room-temperature fabrication of transparent flexible thin-film transistors using amorphous oxide semiconductors. Nature. 432, 488–492 (2004).
Hosono, H., Nomura, K., Ogo, Y., Uruga, T. & Kamiya, T. Factors controlling electron transport properties in transparent amorphous oxide semiconductors. J. Non-Cryst. Solids. 354, 2796–2800 (2008).
Barquinha, P. et al. Toward high-performance amorphous GIZO TFTs. J. Electrochem. Soc. 156, H161–H168 (2009).
Park, S.-H. K. et al. Transparent ZnO thin film transistor array for the application of transparent AM-OLED display. SID Int. Symp. Digest Tech. 37, 25–28 (2006).
Hirao, T. et al. Distinguished paper: High mobility top-gate zinc oxide thin-film transistors (ZnO-TFTs) for active-matrix liquid crystal displays. SID Int. Symp. Digest Tech. Papers. 18–20 (2006).
Dehuff, N. L. et al. Transparent thin-film transistors with zinc indium oxide channel layer. J. Appl. Phys. 97, 064505 (2005).
Liu, P. T., Chou, Y. T., Teng, L. F., Li, F. H. & Shieh, H. P. Nitrogenated amorphous InGaZnO thin film transistor. Appl. Phys. Lett. 98, 052102 (2011).
Chiu, C. J., Chang, S. P. & S. J. Chang, High-performance a-IGZO thin-film transistor using Ta2O5 gate dielectric. IEEE Electron Device Lett. 31, 1245–1247 (2010).
Fortunato, E. M. C. et al. High mobility indium free amorphous oxide thin film transistors. Appl. Phys. Lett. 92, 222103 (2008).
Choi, J. Y., Kim, S. S. & Lee, S. Y. Effect of hafnium addition on Zn-Sn-O thin film transistors fabricated by solution process. Appl. Phys. Lett. 100, 022109 (2012).
Narushima, S. et al. A p-type amorphous oxide semiconductor and room temperature fabrication of amorphous oxide p–n heterojunction diodes. Adv. Mater. 15, 1409–1413 (2003).
Mo, Y. G. et al. Amorphous-oxide TFT backplane for large-sized AMOLED TVs J. Soc. Inf. Display. 19, 1 (2011).
Yabuta, H. et al. High-mobility thin-film transistor with amorphous InGaZnO4 channel fabricated by room temperature rf-magnetron sputtering. Appl. Phys. Lett. 89, 112123 (2006).
Park, J. S., Maeng, W.-J., Kim, H.-S. & Park, J.-S. Review of recent developments in amorphous oxide semiconductor thin-film transistor devices. Thin Solid Films. 520, 1679–1693 (2012).
Shin, J.-H. et al. Light effects on the bias stability of transparent ZnO thin film transistors. ETRI J. 31, 62–64 (2009).
Lee, K.-H. et al. The effect of moisture on the photon-enhanced negative bias thermal instability in Ga–In–Zn–O thin film transistors. Appl. Phys. Lett. 95, 232106 (2009).
Chong, E., Kang, I., Park, C. H. & Lee, S. Y. First-principle study of amorphous SiZnSnO thin-film transistor with excellent stability. Thin Solid Films. 534, 609–613 (2013).
Kang, I., Park, C. H., Chong, E. & Lee, S. Y. Role of Si as carrier suppressor in amorphous Zn–Sn–O. Curr. Appl. Phys. 12, S12–S16 (2012).
Jeong, S. et al. Role of gallium doping in dramatically lowering amorphous-oxide processing temperatures for solution-derived indium zinc oxide thin-film transistors. Adv. Mater. 22, 1346–1350 (2010).
Yin, W. J., Wei, S. H., Al-Jassim, M. M. & Yan, Y. Prediction of the chemical trends of oxygen vacancy levels in binary metal oxides. Appl. Phys. Lett. 99, 142109 (2011).
Kamiya, T. & Hosono, H. Material characteristics and applications of transparent amorphous oxide semiconductors. NPG Asia Mater. 2, 15–22 (2010).
Kamiya, T., Nomura, K. & Hosono, H. Origins of high mobility and low operation voltage of amorphous oxide TFTs: Electronic structure, electron transport, defects and doping. J. Disp. Technol. 5, 273–288 (2009).
Yu, Y.-J. et al. Tuning the graphene work function by electric field effect. Nano Lett. 9, 3430–3434 (2009).
LiBassi, A. et al. Density, sp3 content and internal layering of DLC films by X-ray reflectivity and electron energy loss spectroscopy. Diam. Relat. Mater. 9, 771–776 (2000).
Wu, C. et al. Characterization of amorphous Si-Zn-Sn-O thin films and applications in thin-film transistors. Appl. Phys. Lett. 103, 082109 (2013).
Chong, E., Kim, S. H. & Lee, S. Y. Role of silicon in silicon-indium-zinc-oxide thin-film transistor. Appl. Phys. Lett. 97, 252112 (2010).
Lee, D.-H., Park, K.-H., Kim, S. & Lee, S. Y. Effect of Ag doping on the performance of ZnO thin film transistor. Thin Solid Films. 520, 1160–1164 (2011).
Rim, Y. S., Kim, D. L., Jeong, W. H. & J. Kim, H. Effect of Zr addition on ZnSnO thin-film transistors using a solution process. Appl. Phys. Lett. 97, 233502 (2008).
Terrier, C., Chatelon, J. P., Berjoan, R. & Roger, J. A. Sb-doped SnO2 transparent conducting oxide from the sol-gel dip-coating technique. Thin Solid Films. 263, 37–41 (1995).
Hansen, W. N. & Johnson, K. B. Work function measurements in gas ambient. Surf. Sci. 316, 373–382 (1994).
Song, H. et al. Stabilization of oxygen-deficient structure for conducting Li4Ti5O12 by molybdenum doping in a reducing atmosphere. Sci Rep. 4, 4350 (2014).
Chen, C., Cheng, K.-C., Chagarov, E. & Kanicki, J. Crystalline In–Ga–Zn–O Density of States and Energy Band Structure Calculation Using Density Function Theory. Jap. J. Appl. Phys. 50, 091102 (2011).
Duke, C. B. et al. Low-energy-electron-diffraction analysis of the atomic geometry of ZnO (10 0). Phys. Rev. B. 15, 4865 (1977).
Duke, C. B., Lubinsky, A. R., Lee, B. W. & Mark, P. Atomic geometry of cleavage surfaces of tetrahedrally coordinated compound semiconductors. J. Vac. Sci. Technol. 13, 761 (1976).
Duke, C. B., Meyer, R. J., Paton, A. & Mark, P. Calculation of low-energy-electron-diffraction intensities from ZnO (10 0). II. Influence of calculational procedure, model potential, and second-layer structural distortions. Phys. Rev. B. 18, 4225 (1978).
Moormann, H., Kohl, D. & Heiland, G. Variations of work function and surface conductivity on clean cleaved zinc oxide surfaces by annealing and by hydrogen adsorption. Surf. Sci. 100, 302–314 (1980).
Scanlon, David O. et al. Band gap engineering of In2O3 by alloying with Tl2O3 . Appl. Phys. Lett. 103, 262108 (2013).
Rangan, S. et al. Energy alignment, molecular packing, and electronic pathways: Zinc(II) tetraphenylporphyrin derivatives adsorbed on TiO2(110) and ZnO(11–20) Surfaces. J. Phys. Chem. C. 116, 23921–23930 (2012).
Kim, J. S. et al. Kelvin probe and ultraviolet photoemission measurements of indium tin oxide work function: a comparison. Synthetic Metals. 111–112, 311–314 (2000).
Veronica Ganduglia-Pirovano, M., Hofmann, A. & Sauer, J. Oxygen vacancies in transition metal and rare earth oxides: Current state of understanding and remaining challenges. Surf. Sci. Rep. 62, 219–270 (2007).
Chen, Y., Barnard J. C. & Palmer R. E. Indirect band gap of light-emitting BC2N. Phys. Rev. Lett. 83, 12 (1999).
Kim, H.-S. et al. Anion control as a strategy to achieve high-mobility and high-stability oxide thin-film transistors. Sci. Rep. 3, 1459 (2013).
Park, J. et al. Molecular orbital ordering in titania and the associated semiconducting behavior. Appl. Phys. Lett. 99, 142104 (2011).
Hosono, H. Ionic amorphous oxide semiconductors: Material design, carrier transport, and device application. J. Non-Cryst. Solids. 352, 851–858 (2006).
Acknowledgements
This work was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (NRF-2013R1A2A2A03069155) and the “Sensitivity touch platform development and new industrialization support program” through the Ministry of Trade, Industry & Energy (MOTIE) and the Korea Institute for Advancement of Technology (KIAT).
Author information
Authors and Affiliations
Contributions
S.W.H., S.K. and S.Y.L. designed the study; K-S C. performed the experiments and band gap calculations using UPS, EELS, and KP; J.Y.C. and K.H. analysed the data and co-wrote the main manuscript text. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Choi, J., Heo, K., Cho, KS. et al. Engineering of band gap states of amorphous SiZnSnO semiconductor as a function of Si doping concentration. Sci Rep 6, 36504 (2016). https://doi.org/10.1038/srep36504
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep36504
This article is cited by
-
Work function effect of metal electrodes on the performance of amorphous Si–Zn–Sn–O thin-film transistors investigated by transmission line method
Journal of Materials Science: Materials in Electronics (2024)
-
Channel thickness effect on the performance of amorphous SiZnSnO semiconductor thin-film transistor with metal capping structure
Journal of Materials Science: Materials in Electronics (2024)
-
RETRACTED ARTICLE: Effect of oxygen concentration in ZnO-based transparent flexible memristor synapse
Journal of Materials Science: Materials in Electronics (2023)
-
Exploratory study of potential usefulness of cost-effective composites thin films for energy device
Materials for Renewable and Sustainable Energy (2023)
-
Significant enhancement of the bias stability of Zn-O-N thin-film transistors via Si doping
Scientific Reports (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.