Abstract
One-dimensional and two-dimensional materials are widely used to compose the conductive network atop soft substrate to form flexible strain sensors for several wearable electronic applications. However, limited contact area and layer misplacement hinder the rapid development of flexible strain sensors based on 1D or 2D materials. To overcome these drawbacks above, we proposed a hybrid strategy by combining 1D carbon nanotubes (CNTs) and 2D graphene nanoplatelets (GNPs), and the developed strain sensor based on CNT-GNP hierarchical networks showed remarkable sensitivity and tenability. The strain sensor can be stretched in excess of 50% of its original length, showing high sensitivity (gauge factor 197 at 10% strain) and tenability (recoverable after 50% strain) due to the enhanced resistive behavior upon stretching. Moreover, the GNP-CNT hybrid thin film shows highly reproducible response for more than 1000 loading cycles, exhibiting long-term durability, which could be attributed to the GNPs conductive networks significantly strengthened by the hybridization with CNTs. Human activities such as finger bending and throat swallowing were monitored by the GNP-CNT thin film strain sensor, indicating that the stretchable sensor could lead to promising applications in wearable devices for human motion monitoring.
Similar content being viewed by others
Introduction
Flexible electronics has become a hot area of research attracting extensive attention in recent years1,2,3,4. Flexible tactile sensor, as a significant subpart of wearable electronics, is usually mounted on wearable equipment to detect human body movement5,6,7,8,9. Specially, strain sensors with high sensitivity, stretchability, durability, and rapid response/recovery are essential in monitoring human motion10. However, traditional strain sensors based on metal foils or semiconductor films possess unsatisfying flexibility and poor stretchability (ε < 5%) due to the brittleness of sensing materials11,12,13. Therefore, these sensors are not suitable for occasions where both high sensitivity and large stretchable range are required. In order to fabricate high-performance strain sensors, researchers have made tremendous efforts by utilizing various kinds of conductive materials such as silver nanowires7, carbon nanotubes (CNTs)14,15,16, CVD graphene17, and reduced graphene oxide18,19, as the sensing elements.
Networks of overlapping graphene nanoplatelets (GNPs) have been reportedly used in piezoresistive strain sensors, owing to superior stretchability, chemical stability, and economic/scalable synthesis10,19. Each GNP is few-layer graphene with thickness of few nanometers. When these platelets connect with each other to form a thin film, the resistance could be influenced by the contact resistances between GNPs. Upon mechanical loading, the change in film resistance originates from the disconnection, cracking, and tunneling effect between GNPs in the film plane10. To date, a large variety of flexible strain sensors with large workable strain range and/or high sensitivity have been reported. For example, Wang et al. reported a strain sensor based on buckled graphene film deposited on polydimethylsiloxane (PDMS). The sensor was able to be stretched up to ~ 30%, but showing a small GF of ∼220. Graphene-based strain sensor has been reported with a high gauge factor (GF) of 1000 in the strain range of 2–6%17. However, the graphene conductive network could be irreversibly broken, when the applied strain is larger than 7%, leading to the destruction of sensors under deformation. For better practical applications, it’s a significant task to obtain both large workable strain range and high sensitivity. In addition, the fabrication processes of nanomaterials and the strain sensors are generally complicated and costly, possibly generating by-products hazardous to environment. Cost-effective, scalable, and biocompatible approaches are highly demanded for fabricating strain sensors with high sensitivity and large workable strain range.
In this work, we present a strain sensor based on hybridized film of GNPs and CNT, prepared by spray-coating method. CNTs joined GNPs by the van der Waals force to form entangled networks. For comparison, strain sensors based on sole GNPs and sole CNTs thin films were also prepared by similar method. The characteristics of thin films and the sensing performance of proposed strain sensors were investigated. Besides, the application of GNP-CNT hybrid thin film strain sensor as a wearable device was demonstrated by mounting it on human finger and front neck to monitor body-motion. It is revealed that CNTs hybridization greatly improves the sensitivity of GNPs and the proposed strain sensor has a promising perspective in applications of human body monitoring.
Results and discussion
Fabrication process and device structure
The strain sensors were prepared via a simple spray-coating process. Figure 1 shows schematically the solution-based fabrication of the GNP-CNT hybrid thin film strain sensor. To prepare the hybrid thin films, the GNP-CNT mixed dispersion was made, following the procedure detailed in “Experimental methods” section. Using the sonicated GNP-CNT mixed solution, a spray coating technique was carried out to fabricate the GNP-CNT hybrid thin films. In brief, the GNP-CNT mixed solution was first deposited onto a PDMS substrate at an elevated temperature (controlled at 90 °C) to facilitate solution evaporation. After the spray-coating process, the GNP-CNT/PDMS film was peeled off from the glass slide substrate. Then, silver paste was applied on the two ends of the film to form the electrodes. Finally, the device was covered by a layer of PDMS for encapsulation. Similar procedure was carried out to fabricate strain sensors based on sole GNPs and sole CNTs thin films.
Figure 2 shows the working mechanism of three types of strain sensors. Neat CNTs networks are easily destroyed under repeated mechanical load. CNTs bend and buckle upon the release of loads due to the flexibility of 1D nanostructure, which results in wavy structures in the network (Fig. 2a). The generation of nanotube buckles prevents the restoration of conductive paths in the network after releasing of the strain, leading to permanent loss in network conductivity21,22. GNPs are loosely connected with each other forming some microcracks and micropores in the 2D nanostructure (Fig. 2b). Under plane strain, GNPs have chances to arrange themselves to maintain connection by reducing overlapped area. Therefore, the connection resistance of GNPs does not change obviously under strain and the GF value is relatively small10. Compared with the pristine CNTs network and pristine GNPs network, a GNP-CNT hybrid network is mechanically stronger and more flexible to respond plane strain (Fig. 2c). GNPs are stacking in the dispersion network formed by entangled CNTs, the hybrid network demonstrating properties of both 1D and 2D nanostructure. Due to the weak interactions at the nanotube joints, the networks respond to tensile loads through interfacial sliding between the neighboring nanotubes23. Under the same tensile strain, the CNTs show much smaller deformation (slide instead of bending and buckling) than the pristine CNTs network, demonstrating an enhanced strength and better stability. Besides, the flexibility improves because the resistance change of strain sensor based on the GNP-CNT hybrid thin film is not only due to the fracture or crack propagation of GNPs. Figure 2d shows the measurement scheme of a strain sensor based on GNP-CNT hybrid. As demonstrated in Fig. 2e, from relaxed state (Fig. 2eI) to tensile state (Fig. 2eII), GNPs and CNTs slide by the deformation of the PDMS matrix so that the number of disconnection gradually increases by higher tensile strain, causing the resistance of the strain sensor to increase11.
Characterization
The morphology and structure of CNT, few-layer graphene, and the GNP-CNT hybrid material were measured using AFM, TEM, and Raman spectroscopy to demonstrate the percolation theory in thin film. The GNP-CNT hybrid material was fabricated with 5 ml GNPs dispersion and 2 ml CNTs dispersion. Figure 3a shows the AFM image of the GNP-CNT hybrid material acquired in a liquid cell. The whiter boxes in Fig. 3a mark the locations of large GNPs. With AFM imaging, we estimated the lateral dimension (50–2500 nm) and the thickness (~ 4.5 nm) of GNPs. The average bundle length and diameter of the CNTs in GNP-CNT hybrid thin films were determined to be 2000 nm and 5 nm, respectively. It can be seen that the CNTs are intertwined with each other in a mixed structure, while GNPs stacking in the hybrid dispersion network. Raman spectrum of few-layer graphene, CNT, and GNP-CNT hybrid materials are presented in Fig. 3b. Figure 3bI presents a strong G band at 1578 cm−1 but rather weak D band at 1349 cm−1, suggesting that the few-layer graphene is mainly constituted of sp2 hybridized carbon24. The 2D band (2714 cm−1 in Fig. 3bI) of few-layer graphene has been regarded as a sensitive indication of the number of layers25,26,27,28,29. The radial breathing mode (RBM) as well as the G and D band on the spectrum (Fig. 3bII) is markers for determining the diameters of the CNT30,31. Focusing on the RBM of the spectrum, the Raman shift at 68.6 cm−1, 157.7 cm−1, 191.2 cm−1 and 270.5 cm−1 respectively correspond to CNTs approximately 3.98 nm, 1.54 nm, 1.25 nm and 0.87 nm in diameter32. Raman spectroscopy unambiguously corroborates the presence of GNP-CNT hybrid material as shown in Fig. 3bIII. The connections between GNPs and CNTs are important for achieving hybrid materials with good performance. Microstructures and morphology of the GNP-CNT hybrid material imaged at different magnifications were investigated by TEM. TEM and HRTEM images of GNP-CNT hybrid material are shown in Fig. 3c,d, respectively. From the TEM image, the junctions between GNPs and CNTs are clearly observed. The HRTEM image (Fig. 3d) confirms that small lattice fringes with an interlayer thickness of 0.34 nm, which belongs to sp2 bonded graphite carbon. The diameter of the carbon nanotubes is about 5 nm, which is consistent with the AFM result. Both images clearly reveal that GNPs and CNTs are uniformly dispersed to form the mixed structures of CNTs entangled network stacking by GPNs in the hybrid dispersion.
The SEM images of surface morphology and the cross-section of the GNP-CNT hybrid thin film were shown in Fig. 4a,b, respectively. CNTs are uniformly dispersed within the network of percolating GNPs as seen in Fig. 4a. The thickness of the hybrid thin film is estimated to be ~ 3.25 μm from Fig. 4b. From the SEM results, it suggests that the CNTs rope entangled network structures stacking mosaic morphology of GNPs in the as-prepared thin film. Figure 4c,d are photographs of a strain sensor made of GNP-CNT hybrid thin film at its original length and with over 50% strain, respectively, showing the stretchability and bendability of the sensor. Figure 4e shows the photographs of the sensors under bending stress with ultra-softness. The sensors can be directly mounted on human skin or attached to complex surfaces with perfect contact and negligible slippage.
Piezoresistive characteristics analysis
The GNP-CNT hybrid thin film sensor was clamped to a motorized moving controller (WNMC 400 Motion Controller) to characterize its electromechanical behavior. Multiple strain/release cycles with different strain levels were applied to the sensor, while the resistance changes were measured. The gauge factor (GF) was evaluated according to the coupled electrical-cyclic tensile testing results:
\(\Delta R\) is the relative change in resistance. \({R}_{0}\) is initial resistance without applying strain. \(\Delta L/L\) is the displacement variation of the sensing film. The I–V curves (Fig. 5a) at different strain levels indicate that the response of the sensor based on GNP-CNT hybrid thin film to strain is steady, and the resistance (slope of I–V curves) under each applied strain is constant. The slope of the curve under strain conditions is much smaller than that of the curve when no strain is present, indicating a significant increase in the resistance.
When the strain sensor was held at various levels of strain, the resistance changes were recorded to evaluate the stability of output signal. During each period, the signals remained stable without distinct drifts, as shown in Fig. 5b, the Gauge Factors of strain sensor are 116 under 7.5% strain and 197 under 10% strain, respectively. The GF values, calculated to be 10–197, were superior to those of previously reported stretchable sensors (GF: 0.5–69)7,33,34 and some other graphene/CNTs based strain sensors (GF 0.54 at 90% strain, GF 15 at 206% strain)35,36.
Our sensor also showed long-time stability, little hysteresis, and high durability. Figure 5c shows the response of the sensor to 1000 times cyclic loading of 10% strain, indicating its remarkable stability. For comparison, strain sensors based on sole GNPs and sole CNTs thin films were prepared and measured by similar method. Figure 5d compares the GF values of sole CNTs thin film sensors (sprayed with 4 mL or 5 mL CNTs dispersion, sensing layer thickness ~ 2.0 μm or ~ 2.1 μm) with those of sole GNPs thin film sensors (sprayed with 8 mL or 11 mL GNPs dispersion, sensing layer thickness ~ 2.9 μm or ~ 3.1 μm). Figure 5e compares the GF values of GNP-CNT hybrid thin films fabricated with altered GNP/CNTs ratio under different strain levels. The sensitivity of strain sensors fabricated with optimal GNP-CNT volume ratio 5:2 is much better than that of sole CNTs and sole GNPs thin films sensors. Besides, consistent with the mechanism described in Fig. 2, after the experimental strain/release cycles, the resistance of strain sensor made of sole CNTs failed reverting to initial value and that of strain sensor made of CNT/GNP or sole GNPs was able to resume to initial value.
The skin deformation combines stretching and bending37, which could lead to the structural changes of these microcracks and micropores38, thus the film could be used as a skin-mountable strain sensor to detect human motion. In comparison to the traditional strain sensors based on metal foil or silicon, the unique feature of GNP-CNT hybrid thin film strain sensors is their remarkable extensibility and durability20,39. In combination with the high sensitivity and ease of fabrication, these properties make the strain sensor highly promising for applications in human–machine interactions and body motion monitoring. To demonstrate the potential and applicability, the GNP-CNT hybrid thin film strain sensor was mounted on the finger and the front neck to monitor body motion. We fixed the strain sensor on a middle finger to see its resistance response to the bending of the finger (Fig. 6a). When the middle finger slowly bended toward the palm to a certain angle (30°, 45°, and 90°) and subsequently released repeatedly, the finger motion was faithfully registered by the continuous increase and decrease of the resistance. The greater the bending angle is, the more the resistance increases. The resistance almost doubles when the middle finger bends to an angle of 90°. By mounting the strain sensor on human finger, the GNP-CNT hybrid thin film strain sensors could potentially be useful for a broad range of applications in human–machine interactions, such as making phone calls, clicking the mouse, typing on the keyboard, playing piano and remotely controlling the operation of vehicles. Moreover, the strain sensors based on GNP-CNT hybrid thin film can be used for body monitoring. Figure 6b shows a GNP-CNT hybrid thin film strain sensor attached onto skin of the neck to noninvasively monitor the muscle movement during pronouncing ‘a’ and swallowing. The strains induced by the motion of surficial skin along a human neck were clearly sensible with reproducible signals in resistance. The GNP-CNT hybrid thin film strain sensor exhibited high sensitivity and distinct current curves while pronouncing ‘a’ or swallowing. This further demonstrated the excellent performance of the strain sensor in voice recognition.
Conclusion
In summary, we demonstrate a simple, cost-effective, and scalable approach for the implementation of highly sensitive and stretchable strain sensors based on GNP-CNT hybrid thin films. Strain sensors with high sensitivity (GF ~ 197 under 10% strain), high stretchability (ε ≥ 50%) and a reproducible response over 1000 loading cycles (including stretching and bending) can be achieved by incorporating CNTs into GNPs networks to form 1D-2D hybrid microstructure. The devices can be used for strain and vibration sensing in a variety of applications ranging from human physiological activity monitoring to soft robotics.
Experimental methods
Ethical approval
The study was approved by the Ethics Committee of University of Electronic Science and Technology of China. All procedures performed in this study involving human participants were carried out in compliance with the Declaration of Helsinki. The informed consent was obtained from all the human participants in the study.
Materials and chemicals
Graphite powder (≥ 325 mesh, 99.95% metals basis) was purchased from Aladdin Biochemical Technology Co. Ltd. TNWDIS (90 wt%) and single-walled carbon nanotubes with an average length of 5–30 μm and average diameter of 1–2 nm were purchased from Chengdu Organic Chemicals Co. Ltd, Chinese Academy of Sciences. N-Methylpyrrolidone (NMP, 99.13 (MW), analytical pure) was purchased from Kelong Chemical Reagents Factory. The PDMS monomer and curing agent were provided by Sylgrad-184, Dow Corning. All the materials and chemicals were used as received without further purification.
Preparation of GNPs dispersion and CNTs dispersion
Graphene dispersion was obtained from exfoliation of natural graphite powder based on Chiang’s liquid exfoliation method40,41. Graphite dispersions were prepared by dispersing natural graphite in N-Methylpyrrolidone (with the mass fraction 0.2 of deionized water) at an initial concentration of 5 mg/ml. These dispersions were sonicated in a pulse operation mode (on 2 s, off 3 s) with the power set at 60 W for 15 h, followed by standing for 24 h to allow the formation of any unstable aggregates in the bottom. The dispersion was then centrifuged at a speed of 3000 rpm for 15 min. The supernatant obtained was the graphene dispersion. The CNTs dispersion (0.3 mg/ml) was prepared by sonicating a mixture of 30 mg CNTs and 105 mg TNWDIS in 100 g deionized water. The sonication conditions, except the sonication duration (2.5 h), were the same as those of preparing GNPs dispersion. The dispersion was then centrifuged at a speed of 2000 rpm for 15 min. The supernatant obtained was the CNTs dispersion.
Fabrication of GNP-CNT hybrid nanomaterials
The GNP-CNT hybrid nanomaterials were prepared by introducing CNTs solution into GNPs dispersion. To make the hybrid mix uniformly, the mixture was sonicated for 2.5 h under stirring with the speed of 1000 rpm/min to form a homogeneous suspension.
Fabrication of strain sensor
The strain sensor was fabricated by spraying 10 ml diluted GNP-CNT hybrid mixed dispersion (7 ml dispersion with 3 ml DI water) onto an elastomeric polydimethylsiloxane (PDMS) substrate. Spray coating was carried out with a commercial airbrush (ACG model HD-130, Taiwan). In the spray process, the PDMS substrate was heated by a hot plate set at 90 °C to accelerate the solvent evaporation and facilitate thin film formation. The GNP-CNT hybrid coating film was gradually formed by controlling the spraying speed to balance the spraying and solvent evaporation time. For all the thin film sensors, silver paste was applied on the two ends of the film to form a two-electrode configuration for the afterward sensing performance evaluation.
Characterization
Scanning electron microscopy (SEM) was performed with Hitachi S-4800 at 5.0 kV for examining the morphologies and thicknesses of different sensors. The tapping mode AFM (Veeco Digital Instruments by Bruker Dimension D3100) was used to acquire images of GNP-CNT hybrid nanomaterials deposited on silicon wafer for thickness measurement. Structural and morphological characterization of the material was performed on a FEI Tecnai G2 F20 TEM operated at 200 kV of accelerating voltage. The two ends of the sensor were mounted on a customized micrometer moving stage, and the sensing film can be bent and stretched by moving the stage closer. Electrical properties of the sensor were collected by a source measurement unit (SMU) instrument (Keithley 2400).
References
Rogers, J. et al. Materials and mechanics for stretchable electronics. Science 327, 1603–1607. https://doi.org/10.1126/science.1182383 (2010).
Gupta, S. et al. Ultra-thin chips for high-performance flexible electronics. npj Flexible Electron. 2, 8. https://doi.org/10.1038/s41528-018-0021-5 (2018).
Khan, S. et al. Recent advances of conductive nanocomposites in printed and flexible electronics. Smart Mater. Struct. 26, 8. https://doi.org/10.1088/1361-665X/aa7373 (2017).
Xue, J. et al. Nanowire-based transparent conductors for flexible electronics and optoelectronics. Sci. Bull. 62(2), 143–156. https://doi.org/10.1016/j.scib.2016.11.009 (2017).
Khan, H. et al. Sensitive and flexible polymeric strain sensor for accurate human motion monitoring. Sensors 18, 418. https://doi.org/10.3390/s18020418 (2018).
Zhou, H. et al. Wearable, flexible, disposable plasma-reduced graphene oxide stress sensors for monitoring activities in austere environments. ACS Appl. Mater. Interfaces. https://doi.org/10.1021/acsami.8b22673 (2019).
Roh, E. et al. Stretchable, transparent, ultrasensitive, and patchable strain sensor for human-machine interfaces comprising a nanohybrid of carbon nanotubes and conductive elastomers. ACS Nano 9, 6252–6261. https://doi.org/10.1021/acsnano.5b01613 (2015).
Li, X. et al. Highly sensitive flexible tactile sensors based on microstructured multiwall carbon nanotube arrays. Scripta Mater. 129, 61–64. https://doi.org/10.1016/j.scriptamat.2016.10.037 (2017).
Quan, Y. et al. Highly sensitive and stable flexible pressure sensors with micro-structured electrodes. J. Alloy. Compd. 699, 824–831. https://doi.org/10.1016/j.jallcom.2016.12.414 (2017).
Shi, G. et al. Highly sensitive, wearable, durable strain sensors and stretchable conductors using graphene/silicon rubber composites. Adv. Funct. Mater. 26, 7614–7625. https://doi.org/10.1002/adfm.201602619 (2016).
Amjadi, M. et al. Highly stretchable and sensitive strain sensor based on silver nanowire-elastomer nanocomposite. ACS Nano 8, 5154–5163. https://doi.org/10.1021/nn501204t (2014).
Yan, C. et al. Highly stretchable piezoresistive graphene-nanocellulose nanopaper for strain sensors. Adv. Mater. 26, 2022–2027. https://doi.org/10.1002/adma.201304742 (2014).
Zhou, J. et al. Flexible piezotronic strain sensor. Nano Lett. 8, 3035–3040. https://doi.org/10.1021/nl802367t (2008).
Shi, J. et al. Graphene reinforced carbon nanotube networks for wearable strain sensors. Adv. Funct. Mater. 26, 2078–2084. https://doi.org/10.1002/adfm.201504804 (2016).
Park, S. et al. Highly flexible wrinkled carbon nanotube thin film strain sensor to monitor human movement. Adv. Mater. Technol. https://doi.org/10.1002/admt.201600053 (2016).
Michelis, F. et al. Highly reproducible, hysteresis-free, flexible strain sensors by inkjet printing of carbon nanotubes. Carbon 95, 1020–1026. https://doi.org/10.1016/j.carbon.2015.08.103 (2015).
Wang, Y. et al. Wearable and highly sensitive graphene strain sensors for human motion monitoring. Adv. Funct. Mater. 24, 4666–4670. https://doi.org/10.1002/adfm.201400379 (2014).
Liu, Q. et al. High-quality graphene ribbons prepared from graphene oxide hydrogels and their application for strain sensors. ACS Nano 9, 12320–12326. https://doi.org/10.1021/acsnano.5b05609 (2015).
Gong, T. et al. Highly responsive flexible strain sensor using polystyrene nanoparticle doped reduced graphene oxide for human health monitoring. Carbon 140, 286–295. https://doi.org/10.1016/j.carbon.2018.09.007 (2018).
Wang, Y. et al. Super-elastic graphene ripples for flexible strain sensors. ACS Nano 5, 3645–3650. https://doi.org/10.1021/nn103523t (2011).
Cai, L. et al. Highly transparent and conductive stretchable conductors based on hierarchical reticulate single-walled carbon nanotube architecture. Adv. Funct. Mater. 22, 5238–5244. https://doi.org/10.1002/adfm.201201013 (2012).
Zhang, Y. Y. et al. Polymer-embedded carbon nanotube ribbons for stretchable conductors. Adv. Mater. 22, 3027–3031. https://doi.org/10.1002/adma.200904426 (2010).
Kanoun, O. et al. Flexible carbon nanotube films for high performance strain sensors. Sensors 14, 10042–10071. https://doi.org/10.3390/s140610042 (2014).
Chen, J. et al. A binary solvent system for improved liquid phase exfoliation of pristine graphene materials. Carbon 94, 405–411. https://doi.org/10.1016/j.carbon.2015.07.006 (2015).
Hernandez, Y. et al. High-yield production of graphene by liquid-phase exfoliation of graphite. Nat. Nanotechnol. 3, 563–568. https://doi.org/10.1038/nnano.2008.215 (2008).
Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710. https://doi.org/10.1038/nature07719 (2009).
Ferrari, A. C. et al. Raman spectroscopy as a versatile tool for studying the properties of graphene. Nat. Nanotechnol. 8, 235. https://doi.org/10.1038/nnano.2013.46 (2013).
Tung, V. C. et al. High-throughput solution processing of large-scale graphene. Nat. Nanotechnol. 4, 25. https://doi.org/10.1038/nnano.2008.329 (2008).
Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401. https://doi.org/10.1103/PhysRevLett.97.187401 (2006).
Dresselhaus, M. S. et al. Raman spectroscopy of carbon nanotubes. Phys. Rep. 409, 47–99. https://doi.org/10.1016/j.physrep.2004.10.006 (2005).
Saito, R. et al. Raman spectroscopy of graphene and carbon nanotubes. Adv. Phys. 60, 413–550. https://doi.org/10.1080/00018732.2011.582251 (2011).
Bachilo, S. M. et al. Structure-assigned optical spectra of single-walled carbon nanotubes. Science 298, 2361–2366. https://doi.org/10.1126/science.1078727 (2002).
Trung, T. Q. & Lee, N. E. Flexible and stretchable physical sensor integrated platforms for wearable human-activity monitoringand personal healthcare. Adv. Mater. 28, 4338–4372. https://doi.org/10.1002/adma.201504244 (2016).
Lipomi, D. J. et al. Skin-like pressure and strain sensors based on transparent elastic films of carbon nanotubes. Nat. Nanotechnol. 6, 788–792. https://doi.org/10.1038/nnano.2011.184 (2011).
Zhao, X. et al. Highly conductive multifunctional rGO/CNT hybrid sponge for electromagnetic wave shielding and strain sensor. Adv. Mater. Technol. 4(9), 1900443. https://doi.org/10.1002/admt.201900443 (2019).
Pan, S. et al. A highly stretchable strain sensor based on CNT/graphene/fullerene-SEBS. RSC Adv. 10, 11225–11232. https://doi.org/10.1039/D0RA00327A (2020).
Jung, S. et al. Reverse-micelle-induced porous pressure-sensitive rubber for wearable human-machine interfaces. Adv. Mater. 26, 4825–4830. https://doi.org/10.1002/adma.201401364 (2014).
Zhang, Q. et al. Highly sensitive and stretchable strain sensor based on Ag@CNTs. Nanomaterials 7(12), 424. https://doi.org/10.3390/nano7120424 (2017).
Luo, S. & Liu, T. Structure–property–processing relationships of single-wall carbon nanotube thin film piezoresistive sensors. Carbon 59, 315–324. https://doi.org/10.1016/j.carbon.2013.03.024 (2013).
Manna, K. et al. Graphene and graphene-analogue nanosheets produced by efficient water-assisted liquid exfoliation of layered materials. Carbon 105, 551–555. https://doi.org/10.1016/j.carbon.2016.04.065 (2016).
Luo, S. & Liu, T. SWCNT/graphite nanoplatelet hybrid thin films for self-temperature-compensated, highly sensitive, and extensible piezoresistive sensors. Adv. Mater. 25, 5650–5657. https://doi.org/10.1002/adma.201301796 (2013).
Acknowledgements
This work was supported by, National Natural Science Foundation of China (Nos. 61971108, 61804023, 61905035), Sichuan Provincial Department of Science and Technology (2020YJ0015, 2019YJ0198, 2019YFG0222), Natural Science Foundation of Tianjin (18JCYBJC41500) and LY acknowledged China National Funds for Distinguished Young Scientists (No. 61825102).
Author information
Authors and Affiliations
Contributions
Y. Li and Q.A. planned and supervised the study. Y. Li and L.M. fabricated the strain sensor. SEM image and AFM image were acquired by Q.A. and Y. Liu. J.G. and T.G. carried out the Raman spectroscopy measurements and analysis. W.H., Y. Lin and X.Z. provided materials, laboratory tools and facility. Y. Li and Q.A. carried out the electromechanical experiment, the experimental data analysis and image graphics. The manuscript writing and preparation was done by Y. Li and W.H. All authors read and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, Y., Ai, Q., Mao, L. et al. Hybrid strategy of graphene/carbon nanotube hierarchical networks for highly sensitive, flexible wearable strain sensors. Sci Rep 11, 21006 (2021). https://doi.org/10.1038/s41598-021-00307-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-00307-5
This article is cited by
-
High-density, highly sensitive sensor array of spiky carbon nanospheres for strain field mapping
Nature Communications (2024)
-
Harnessing NaNH2 as a dual-function activator for synthesis of porous carbon and its impact on enhanced supercapacitor performance: a review
Chemical Papers (2024)
-
Carbon nanotube-graphene hybrids for soft electronics, sensors, and actuators
Micro and Nano Systems Letters (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.