Abstract
Polarization of electromagnetic waves plays an extremely important role in interaction of radiation with matter. In particular, interaction of polarized waves with ordered matter strongly depends on orientation and symmetry of vibrations of chemical bonds in crystals. In quantum technologies, the polarization of photons is considered as a “degree of freedom”, which is one of the main parameters that ensure efficient quantum computing. However, even for visible light, polarization control is in most cases separated from light emission. In this paper, we report on a new type of polarization control, implemented directly in a spintronic terahertz emitter. The principle of control, realized by a weak magnetic field at room temperature, is based on a spin-reorientation transition (SRT) in an intermetallic heterostructure TbCo2/FeCo with uniaxial in-plane magnetic anisotropy. SRT is implemented under magnetic field of variable strength but of a fixed direction, orthogonal to the easy magnetization axis. Variation of the magnetic field strength in the angular (canted) phase of the SRT causes magnetization rotation without changing its magnitude. The charge current excited by the spin-to-charge conversion is orthogonal to the magnetization. As a result, THz polarization rotates synchronously with magnetization when magnetic field strength changes. Importantly, the radiation intensity does not change in this case. Control of polarization by SRT is applicable regardless of the spintronic mechanism of the THz emission, provided that the polarization direction is determined by the magnetic moment orientation. The results obtained open the prospect for the development of the SRT approach for THz emission control.
Similar content being viewed by others
Introduction
Generation of terahertz (THz) radiation is of great technological importance for many current and future applications, such as non-destructive diagnostics, ultra-fast computing, wireless communications1,2,3,4, as well as direct control of the materials order parameters5.
During the last decade enormous work has been done to verify materials and mechanisms providing THz radiation with required characteristics. Among THz-materials are semiconductors ZnTe6, GaP7, GaSe8, GaAs9, organic crystals10, metals11,12, in which either optical rectification or photocurrents induced by a short optical pulse are the sources of THz radiation. Recently, not only charge but spin has been taken into consideration in spintronic THz emitters (STE), where ultrafast spin photocurrent can convert into a transverse charge current. Using STE, new applications such as near-field THz microscope have been suggested13,14.
The conventional STE is a bilayer made of ferromagnetic and nonmagnetic metal thin films stack15,16. In a ferromagnetic layer, magnetization lies in the film plane. An optical femtosecond pump pulse incident on the ferromagnetic/nonmagnetic structure generates a nonequilibrium electronic state. Since in a ferromagnetic layer with uncompensated magnetization, the mobility of spin-up (majority) electrons is significantly higher than that of spin-down (minority) electrons, the current appearing along the normal to the stack surface is spin-polarized. The inverse spin-Hall effect (ISHE) transforms the out-of-plane spin current into the desired sub-picosecond in-plane charge current. The latter gives rise to the emission of a THz electromagnetic pulse. The spectral range of the emitted radiation in such materials is from 0.5 to 15 THz (two orders of the dynamical range magnitude) with signal amplitude compared with that of ZnTe or InP15. The magnetic field value controls magnetization value and hence the amplitude of THz radiation. By changing magnetic field direction, polarization plane of THz wave can be controlled16.
New way for THz emission polarization control was demonstrated in Ref.17. In a Co/Pt heterostructure with in-plane magnetization of Co layer, not only a linearly polarized, but also a circularly polarized femtosecond laser pulse launches a spin-current from Co to Pt. In the Pt-layer, the spin current is subsequently converted into a charge current due to the ISHE. For circularly polarized optical pulse used for excitation, the THz emitted pulse is linearly polarized, with polarization plane being helicity dependent. Polarization control of THz wave by spatially varying magnetic field (quadrupole-like in a demonstrator18) was suggested in Ref.16. Similar approach was used in THz near-field microscope13.
Spin-reorientation transition (SRT) is known as a bright example of the order-order type phase transitions in magnets19,20. These transitions appear as a change in orientation of magnetic moment under variation of the external parameters such as temperature, magnetic field strength, stress, etc. At the critical point of the first order SRT, the spin orientation changes abruptly. In the second order SRT, orientation changes continuously, but near the critical point the susceptibility of the spin system increases anomalously.
The effects induced near SRT by ultrafast optical excitation attract special attention. It was reported an enhancement of the spin precession amplitude and of the intensity of THz emission excited by femtosecond pulse in the vicinity of SRT temperature21,22,23. The latter effect provides a THz emitter with new mechanism, which is mostly attractive and economically viable if operates at room temperature. In most cases (Terbium–Yttrium Iron Garnets, Intermetallic Compounds RFe2, DyFeO3 type orthoferrites, etc.) the SRT occurs at low temperature. Some special materials like heterostructures24,25,26,27 or very thin films28 have been developed which exhibit SRT at room and even higher temperatures. So far, the light induced effects have been demonstrated only near SRT induced by temperature.
The first observation of the spin dynamics excited by femtosecond laser pulse in the vicinity of SRT induced at room temperature by magnetic field has been reported in Refs.29,30. The experiments were carried out on the intermetallic TbCo2/FeCo heterostructure with uniaxial in-plane magnetic anisotropy.
In this paper, we report on THz emission in the TbCo2/FeCo heterostructure. The experimental method makes it possible to indicate a most probable mechanism of the emission as optically induced ISHE. ISHE in this structure was observed previously using direct spin current injection from YIG film at ferromagnetic resonance31. In the area of SRT we demonstrate manipulation of THz wave polarization by variation of magnitude of the DC magnetic field while its direction is fixed. Manipulation is made without losing the generated total THz field. Intriguingly, the whole scenario unfolds for the magnetic field strength below the SRT critical value.
Results
THz signal hysteresis
THz emission was generated by linearly polarized femtosecond laser pulse incident normally on a multilayer TbCo2/FeCo structure with in-plane magnetization. A detailed sample description and the schematic of the optical experiment are presented in the “Method” section.
The emission was studied for two characteristic orientations of magnetizing field relatively to the axis of the uniaxial magnetic anisotropy of the structure: the magnetic field vector either parallel to the easy axis (“easy axis” geometry) or normal to it (“hard axis” geometry). Time domain profile of the THz signal ΔS in the “hard axis” geometry is shown in Fig. 1a and appropriate spectra is shown in Fig. 1b (for exact definition of ΔS see Supplementary Information S5). A change in the sign of the magnetizing field inverts the THz pulse, that is reversing the phase of the pulse.
The dependences of the maximum of the THz signal \(\Delta S\) (that is at \(t = 0\)) on magnetic field strength in the “easy axis” and “hard axis” geometries (THz hysteresis loops) are presented in Fig. 2a. The obtained dependences coincide with the corresponding magnetization curves (Fig. 2b) measured by VSM technique. In the “easy axis” geometry, the THz signal possesses almost rectangular hysteresis loop with the coercive field about 0.1 kOe. In the “hard axis” geometry, the field dependence of the THz signal reproduces magnetization curve typical for SRT. The saturation along magnetic field occurs at about 1,2 kOe when magnetizing field achieves the value of the anisotropy field \({H}_{A}\). The field strengths \(H=\pm {H}_{A}\) correspond to the critical points of the SRT. A decrease in the field strength is accompanied by a tilt of magnetic moment towards the “easy axis”, which represents a transition from saturation to the angular (canted) magnetic phase. In the interval − \({{H}_{A}}<H<+{{H}_{A}}\), the magnetic moment gradually rotates from negative to positive orientation, and its projection onto the "hard axis" linearly depends on \(H\) value. The amplitude of the emission does not depend on magnetic field when magnetic states are saturated along \(H\).
THz polarization rotation
To study the effect of the magnetic field strength on the polarization of generated THz pulses, a THz polarizer was installed in the path between the ZnTe crystal detector and the sample. The principle of polarization determination by rotation of the polarizer when optical axis of the detector is fixed is described in the “Method” section. The experimental dependences of the THz signal peak-to-peak amplitude (as shown in Fig. 1a) on the angle of rotation of the polarizer in the “hard axis” geometry are shown in Fig. 3. The dependences reflect THz polarization rotation during spin reorientation controlled by magnetic field strength in the SRT area.
Figure 4 shows the THz polarization angle as a function of the magnetic field strength measured stroboscopically in the “hard axis” geometry (see the “Method” section). As can be seen, the result completely matches the field dependence of the THz signal shown in Fig. 2a.
Similar studies were carried out in the “easy axis” geometry, the results are presented in Fig. 5. A sharp change in the phase of generated THz pulses did not allow for measurements in intermediate states between positive and negative magnetic phases in the given geometry. In this case, a phase change means a 180-degree THz polarization rotation relative to the X laboratory frame.
Model and discussion
The observed effect of magnetic field on the amplitude of generated THz pulses in the TbCo2/FeCo heterostructure reveals ISHE mechanism of the THz emission similar to that described in Refs.15,32. Light-induced demagnetization in the FeCo layer launches a pulse of spin current into the TbCo2 and Ru layers (see Fig. 6). In the framework of ultrafast demagnetization mechanism, the direction of spin current is determined by asymmetric position of the Ru cap and by the gradient of magnetization quenching induced by laser irradiation. The spin current is normal to the structure surface \(\overrightarrow{{J}_{s}}||\overrightarrow{z}\). Spin polarization the majority of electrons is antiparallel to magnetization \(\overrightarrow{\sigma }||-\overrightarrow{M}\).
Strong spin–orbit interaction in TbCo2 splits electron flows with opposite spins, generating a charge current \({\overrightarrow{J}}_{c}\), according to ISHE spin-charge conversion:
where \({\theta }_{ISHE}\) is electron deflection angle.
The basic scheme of measurements (presented in Fig. 7 of the “Method” section) detects \({E}_{\mathrm{x}}\)—component of THz electric field, that is normal to the optical axis [001] of ZnTe nonlinear crystal. Since polarization of the emitted wave is parallel to \({\overrightarrow{J}}_{c},\) the measured amplitude of THz pulses is proportional to the Y-component of magnetization: \({E}_{\mathrm{x}}\propto {M}_{y}\) . In the scheme given in Fig. 7, the magnetizing field is parallel to y-axis, for this reason THz amplitude dependences on magnetic field reproduce magnetization curves \({M}_{y}\left(H\right)\) in both the “easy axis” and in the “hard axis” geometries. According to the ISHE mechanism, THz polarization direction should follow variations of magnetic moment orientation. In the angular (canted) phase of SRT, the orientation of the magnetic moment is controlled by the strength of magnetic field directed normally to the easy axis20.
The SRT in a uniaxial magnetic film arises in the canted state as pure rotation of saturated magnetization by 90° from hard to easy axis when magnetic field value \(H\) decreases from \({H}_{A}\) to 0. After changing the sign of the magnetic field, the magnetization continues to rotate up to 180° when negative value of \(H\) decreases down to − \({H}_{A}\). In the framework of ISHE mechanism such a pure rotation of magnetization is accompanied only by the change of the current direction without changes of its value. Thus, THz polarization can rotate at fixed intensity of the emission. This opens a way for control of THz polarization without rotation of the magnetic field.
Conclusions
We presented the results of a study of THz emission generated by femtosecond laser pulses in the spintronic TbCo2/FeCo heterostructure. The THz pulses generated in these structures show linear polarization. The total intensity of THz emission depends only on the optical pump intensity and does not depend on the magnetic field. Magnetic field provides control over polarization of THz wave by its strength: a fairly small field within the range \({H}_{A}\) rotates polarization within entire angular range of ± 180°. For our samples \({H}_{A}\) = 1.2 kOe and can be significantly reduced for the specially fabricated samples25. Continuous polarization control can be achieved for the “hard axis” configuration, i.e. when magnetic field is applied perpendicularly to the magnetization axis of the sample. In the “easy axis” configuration, changing magnetic field results only in reversing the phase of the THz pulse.
The suggested way of polarization control is based on the magnetic-field induced spin-reorientation phase transitions in the TbCo2/FeCo heterostructure. The SRT provides magnetization rotation when magnetic field is changed by its value only, giving rise to polarization rotation of the THz pulse. This makes the SRT multilayers very different from the magnetic/nonmagnetic structures. In the latter, the polarization rotation can be achieved by rotation magnetic field around them, that is much less technologically justified.
It is worth noting that in the studied magnet/magnet structures, THz generation is provided by inversed spin-Hall effect, analogously to that in the commonly used magnet/nonmagnet structures. However, in our work we show that this mechanism can be generalized to a magnet/magnet multilayer structure as well.
Spin reorientation phase transitions that have proven to be the basis for creating innovative spintronic and straintronic functional materials and devices are applied here to generation of controllable THz emission. The proposed THz polarization control by SRT is applicable independently on mechanism of the THz emission proved that polarization direction is determined by the magnetic moment orientation.
The results obtained allow us to consider SRT as a promising approach for elaboration of THz emitters with controllable parameters.
Method
The sample
The multilayer film FeCo 2 nm/TbCo2 4.8 nm/FeCo 4 nm/TbCo2 4.8 nm/FeCo 4 nm/TbCo2 4.8 nm/FeCo 2 nm/Ru 4 nm was deposited on a glass substrate by RF sputtering technology (Fig. 6). Ruthenium is non-magnetic cap layer. The sputtering was carried out under the static magnetic field that allows for fabrication of heterostructure with controllable uniaxial in-plane magnetic anisotropy25.
The sample was mounted on a non-magnetic holder between two electromagnet poles, which allowed applying fields up to 5 kOe in the plane of the sample along Y axis of the laboratory frame (Fig. 7). A GMW electromagnet (Model 3470) was used as the source of the magnetic field.
Rotation of the sample around the normal to its surface made it possible to set the sample with the easy axis of magnetization directed either parallel or perpendicular to the magnetic field: “easy axis” geometry (e.a.) or “hard axis” geometry (h.a.), respectively.
Optical geometry
The THz emission characteristics were studied using a time-domain spectroscopy scheme, for details see Supplementary information (SI).
For pumping, an amplified Titanium:Sapphire based femtosecond laser system (TiF-20F, Avesta project, Russia) was used provided a 35 fs laser pulse with a repetition rate of 3 kHz at a central wavelength of 800 nm. The output optical radiation was split into two beams: an optical pump pulse and an optical probe pulse. An optical pump pulse was focused onto the sample surface, the energy density being ~ 1 mJ/cm2. The generated in the sample THz radiation was collimated by a parabolic mirror into a parallel beam and then, by the second parabolic mirror, was focused onto the surface of the ZnTe crystal detector. The optical pump radiation was cut off by a filter. The probing beam, passing through the delay line, was focused onto the surface of the ZnTe crystal detector as well and was spatially overlapped with the THz pulse. After interacting with the detector crystal, the probe beam passed through a polarizer, the optical plane of which was crossed with the probe beam polarization plane (zero-point electro optical regime measurements33).
To study the polarization characteristics of the generated THz radiation, a wire-grid polarizer (WGP) was used, which could be rotated through an angle \({\varphi }_{2}\) (For geometry, see Fig. 7). The polarization of the pump and probe beams was rigidly fixed, so that the pump polarization was oriented horizontally in the laboratory axis X, and the polarization of the probe beam was vertical in the laboratory axis Y. In accordance with Ref.34, the polarization of the probe beam was set parallel to the [001] axis of the ZnTe detector crystal, which allows to detect the X-component of the THz field (\({E}_{\mathrm{x}}\)). For details of the method for determining the direction of the emitted THz pulse polarization can be found in SI.
Optical measurements
The following types of measurements have been performed.
-
(1)
Time-domain profiles of THz pulses generated by the spintronic structures in a pump-probe configuration (by changing the delay time between the pump and probe pulses with and without a magnetic field application): Fig. 1a.
-
(2)
Stroboscopic measurements of the THz pulse amplitude at the fixed delay time during magnetic field sweep (THz amplitude hysteresis): Fig. 2a.
-
(3)
Peak-to-peak measurements are the result of hardware and software processing of time domain dependences, measured as in item 1) at different values of magnetic field (see also SI). For each \(H\), peak-to-peak value (see Fig. 1a) was extracted.
-
(4)
THz emission angular measurements. Peak-to peak measurements were performed with a chosen position \({\varphi }_{2}\) of WGP; \({\varphi }_{2}\) was varied from 0° to 360° with 10°—step. In this way, angular dependences as in Figs. 3 and 5 were obtained.
-
(5)
THz pulse polarization angle \({\varphi }_{1}\) determination: as a fit of angular efficiency measurements (from Figs. 3, 5, the result is shown in Fig. 4).
All experiments were carried out at room temperature.
References
Tonouchi, M. Cutting-edge terahertz technology. Nat. Photon. 1, 97 (2007).
Yang, Y. et al. Terahertz topological photonics for on-chip communication. Nat. Photon. 14, 446 (2020).
Schlauderer, S. et al. Temporal and spectral fingerprints of ultrafast all-coherent spin switching. Nature 569, 383 (2019).
Vetter, E. et al. Observation of carrier concentration dependent spintronic terahertz emission from n-GaN/NiFe heterostructures. Appl. Phys. Lett. 117, 093502 (2020).
Kimel, A. V., Kalashnikova, A. M., Pogrebna, A. & Zvezdin, A. K. Fundamentals and perspectives of ultrafast photoferroic recording. Phys. Rep. 852, 1 (2020).
Blanchard, F. et al. Generation of 1.5 μJ single-cycle terahertz pulses by optical rectification from a large aperture ZnTe crystal. Opt. Express 15, 13212 (2007).
Chang, G. et al. GaP waveguide emitters for high power broadband THz generation pumped by Yb-doped fiber lasers. Opt. Express 15, 16308 (2007).
Sell, A., Leitenstorfer, A. & Huber, R. Phase-locked generation and field-resolved detection of widely tunable terahertz pulses with amplitudes exceeding 100 MV/cm. Opt. Lett. 33, 2767 (2008).
Blanchard, F. et al. Terahertz pulse generation from bulk GaAs by a tilted-pulse-front excitation at 1.8 μm. Appl. Phys. Lett. 105, 241106 (2014).
Hauri, C. P., Ruchert, C., Vicario, C. & Ardana, F. Strong-field single-cycle THz pulses generated in an organic crystal. Appl. Phys. Lett. 99, 161116 (2011).
Kadlec, F., Kužel, P. & Coutaz, J.-L. Study of terahertz radiation generated by optical rectification on thin gold films. Opt. Lett. 30, 1402 (2005).
Welsh, G. H., Hunt, N. T. & Wynne, K. Terahertz-pulse emission through laser excitation of surface plasmons in a metal grating. Phys. Rev. Lett. 98, 026803 (2007).
Chen, S.-C. et al. Ghost spintronic THz-emitter-array microscope. Light Sci. Appl. 9, 99 (2020).
Bai, Z. et al. Near-field terahertz sensing of hela cells and pseudomonas based on monolithic integrated metamaterials with spintronic terahertz emitter. ACS Appl. Mater. Interfaces 12, 35895–35902 (2020).
Seifert, T. et al. Efficient metallic spintronic emitters of ultrabroadband terahertz radiation. Nat. Photon. 10, 483–488 (2016).
Fülöp, J.-A., Tzortzakis, S. & Kampfrath, T. Laser-driven strong-field terahertz sources. Adv. Opt. Mater. 8, 1900681 (2019).
Li, G. et al. THz emission from Co/Pt bilayers with varied roughness, crystal structure, and interface intermixing. Phys. Rev. Mater. 3, 084415 (2019).
Hibberd, M. T. et al. Magnetic-field tailoring of the terahertz polarization emitted from a spintronic source. Appl. Phys. Lett. 114, 031101 (2019).
Belov, K. P., Zvezdin, A. K., Kadomtseva, A. M. & Levitin, R. Z. Spin-reorientation transitions in rare-earth magnets. Uspekhi Fizicheskikh Nauk 119, 447–486 (1976).
Millev, Y. T. et al. Influence of external field on spin reorientation transitions in uniaxial ferromagnets. Phys. Rev. B 57, 5837–5847 (1998).
Kimel, A. et al. Laser-induced ultrafast spin reorientation in the antiferromagnet TmFeO3. Nature 429, 850 (2004).
Mikhaylovskiy, R. et al. Ultrafast optical modification of exchange interactions in iron oxides. Nat. Commun. 6, 8190 (2015).
Guyader, L. L. et al. Dynamics of laser-induced spin reorientation in Co/SmFeO3 heterostructure. Phys. Rev. B 87, 054437 (2013).
Tiercelin, N., Ben-Youssef, J., Preobrazhensky, V., Pernod, P. & Le-Gall, H. Giant magnetostrictive superlattices: From spin reorientation transition to MEMS. Static and dynamic properties. J. Magn. Magn. Mater. 249, 519–523 (2002).
Klimov, A., Tiercelin, N., Preobrazhensky, V. & Pernod, P. Inhomogeneous spin reorientation transition (SRT) in giant magnetostrictive TbCo2/FeCo multilayers. IEEE Trans. Magn. 42, 3090–3092 (2006).
Tiercelin, N. et al. Thin film magnetoelectric composites near spin reorientation transition. J. Magn. Magn. Mater. 321, 1803–1807 (2009).
Joly, L. et al. Spin-reorientation in the heterostructure Co/SmFeO3. J. Phys. Condens. Matter 21, 446004 (2009).
Kronseder, M., Buchner, M., Bauer, H. G. & Back, C. H. Dipolar-energy-activated magnetic domain pattern transformation driven by thermal fluctuations. Nat. Commun. 4, 2054 (2013).
Ovcharenko, S. et al. Photoinduced spin dynamics in a uniaxial intermetallic hetrostructure TbCo2/FeCo. Sci. Rep. 10, 15785 (2020).
Ilyin, N. et al. Dynamics of magnetization in multilayer TbCo/FeCo structures under the influence of femtosecond optical excitation. Russ. Technol. J. 3, 50 (2019).
Shaikhulov, T. A. et al. Ferromagnetism in the ferromagnetic yttrium iron garnet film/ferromagnetic intermetallic compound heterostructure. Phys. Solid State 62, 1653 (2020).
Matthiesen, M. et al. Temperature dependent inverse spin Hall effect in Co/Pt spintronic emitters. Appl. Phys. Lett. 116, 212405 (2020).
Kovalev, S. P. & Kitaeva, GKh. Terahertz electro-optical detection: Optical phase or energy measurements. J. Opt. Soc. Am. 30, 2650 (2013).
Planken, P., Nienhuys, H.-K., Bakker, H.-J. & Wenckebach, T. Measurement and calculation of the orientation dependence of terahertz pulse detection in ZnTe. J. Opt. Soc. Am. 18, 313 (2001).
Acknowledgements
The work of Russian side is mainly supported by Russian Science Foundation (Grant 20-12-00276). The work of A. Buryakov is supported by Ministry of Science and High Education of RF (State task for the Universities No. FSFZ-0706-2020-0022). Sample fabrication is supported by French RENATECH network.
Author information
Authors and Affiliations
Contributions
N.T. and P.P.—sample fabrication and VSM measurements; M.G., S.O., D.K. and A.B.—THz experiments and numerical simulation; A.K.—static magneto-optical measurements; V.N.—the grid polarizer adaptation for the experiment, E.M.—experimental work supervising and data acquisition; A.S. and V.P.—theory and numerical simulation. The paper was written by V.P., E.M. and A.S. with feedback from all co-authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Khusyainov, D., Ovcharenko, S., Gaponov, M. et al. Polarization control of THz emission using spin-reorientation transition in spintronic heterostructure. Sci Rep 11, 697 (2021). https://doi.org/10.1038/s41598-020-80781-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-80781-5