Abstract
We have created a new architected material, which is both highly deformable and ultra‐resistant to dynamic point loads. The bio-inspired metallic cellular structure (with an internal grid of large ceramic segments) is non-cuttable by an angle grinder and a power drill, and it has only 15% steel density. Our architecture derives its extreme hardness from the local resonance between the embedded ceramics in a flexible cellular matrix and the attacking tool, which produces high-frequency vibrations at the interface. The incomplete consolidation of the ceramic grains during the manufacturing also promoted fragmentation of the ceramic spheres into micron-size particulate matter, which provided an abrasive interface with increasing resistance at higher loading rates. The contrast between the ceramic segments and cellular material was also effective against a waterjet cutter because the convex geometry of the ceramic spheres widened the waterjet and reduced its velocity by two orders of magnitude. Shifting the design paradigm from static resistance to dynamic interactions between the material phases and the applied load could inspire novel, metamorphic materials with pre-programmed mechanisms across different length scales.
Similar content being viewed by others
Introduction
Nature uses hierarchical structures for protection from extreme loads. The freefall of grapefruit from 10 m does not damage the pulp1 because pomelo peel consists of vascular bundles and an open-pored cellular structure with the struts made of parenchymatic cells. Arapaimas fish living in the Amazon resist the attack of piranhas’ triangular teeth arrays through the hierarchical design of their scales2. The highly mineralized external layer of each scale has sinusoidal grooves, with a periodicity that is out-of-phase with that of piranha teeth spacing. The external interface is strengthened by an underlying hierarchical structure consisting of a cross-lamellar arrangement of collagen fibers. Biological shells also owe their hardness to hierarchical structures3, which evolved over hundreds of millions of years. Nacre of Abalon is made of hard aragonite tiles with an organic, flexible interlayer. Its fracture toughness is 3000 times higher than that of single aragonite crystals4. Gao et al.5,6 proposed a one-dimensional model to study the interplay between high volume fraction of mineral tiles and flexible protein layers. Metals, which require processing temperatures in excess of 300 °C are largely absent in biological structures; i.e., nature has only been able to create materials and architectures prone to transformations at earthbound environmental conditions.
Multi-scale material manufacturing technologies have benefited from recent developments such as self-propagating photopolymer waveguides to achieve unprecedented properties7. Pham et al.8 translated the known benefits of dislocations (local imperfections) in metals into 3D printed, polymeric lattices with unit cells at millimeter scale. Their work demonstrated that one needs to consider the system level interactions and that focusing only on a repetitive unit cell may be self-limiting. Shape-reconfigurable materials (SRMs) were developed to allow for significant morphological changes upon application of relatively small loads and the maintenance of the desired shape when the loading was removed9. Novel architectures were proposed to convert the energy of the incoming mechanical waves into a local resonance. Embodiments of that concept range from the atomistic scale10, through 3D printed structures11 up to infrastructure level, such as seismic metabarriers12. Topology optimization algorithms have produced material patterns capable of focusing, turning or dispersion of blast waves13. Our recent work has shown that locally self-impacting structures can excite natural frequencies of the material to interfere with the oscillatory loads and consequently minimize vibrations14,15.
Results
Metallic-ceramic hierarchical material
Our study created a new metallic-ceramic, hierarchical structure (Fig. 1), which is susceptible to internal vibrations under localized loads. These oscillations are designed to occur when a rotating cutting tool encounters a ceramic sphere on its path. The contact with the ceramic segment produces a localized load on the rim of a rotating disc, which leads to high-frequency, out-of-plane vibrations16. The second aspect of the resistance mechanism was inspired by the vision of Francis Bacon17, who wrote ‘this Proteus of Matter, being held by the Sleeves, will turn and change into many Metamorphoses.’ He believed that matter could not be destroyed or annihilated but only reshaped, reformed or transformed into a new geometry, state, or composition. Thus, we did not attempt to prevent fragmentation of the ceramic segments through the use of the hardest available material (i.e. with the highest purity). Conversely, we employed alumina spheres with suboptimal densification of the grains to promote the fragmentation into fine particulate matter because particles are useful for abrasion of the cutting disc. Notably clusters of small particles become more resistant to penetration under fast moving load due to the increase of their system level resistance under high strain rates18. In other words, our design did not attempt to prevent the material transformations but embraced them and selected the base materials to achieve the most favorable evolution of the constituents.
We produced sandwich plate specimens made of a cellular aluminum core (EN AW-6060) with an orthogonal layout of ceramic spheres (Fig. 1a,b,e,f) with steel alloy (DC01) faceplates. The ceramic spheres had 13 mm mean diameter, while aluminum foam had on average 2.1 mm pore size only and the wall thickness ranging from 30 µm to about 1000 µm. Thus, the ceramic inclusions were an order of magnitude larger than ceramic particulate matter or whiskers used for reinforcement of metallic foams. The ceramic spheres were sufficiently large to interact with a drill or a cutting blade and occupied only 14% volume fraction of the cellular core.
The aluminum foam matrix had a density of ρf = 730 kg/m3 and 73% porosity (air content), which ensured sufficient flexibility of the matrix. Our metallic-ceramic hierarchical structure had ρf = 1140 kg/m3 density. Sandwich panels with two 2 mm steel face plates had 1780 kg/m3 density in a 40 mm thick panel configuration. We also manufactured cylindrical specimens to demonstrate that our technology can achieve high aspect ratio components such as beams or columns (Fig. 1c,d,g and CT scans in Supplementary Information). The cylinders were ideal for computed tomography (CT) because the X-ray travel path through the foam was equal around the circumference, which reduced measuring artifacts. See Methods, section 7 for the description of our CT setup.
Manufacturing of the material
Our material consists of metallic and ceramic ingredients and consequently requires metallurgical processes to manufacture the end parts. Firstly, the aluminum powder is mixed with titanium dihydride, TiH2 (foaming agent) utilizing a rotating impeller to ensure a uniform mixture (Fig. 2). After the mixing stage, the powder mixture is consolidated via cold compaction in a compressor and then extruded through an extrusion die resulting in dense rods of material, which are cut into smaller pieces. Next, ceramic spheres and compressed aluminum powder rods are stacked in an orthogonal, grillage pattern and enclosed in a steel box using spot welds. The structure is then heated in a furnace to ca. 760 °C (depending on the melting range of the used aluminum alloy) for between 15 and 20 minutes. The titanium dihydride begins to decompose at approximately 470 °C, releasing hydrogen gas. The release of the high-pressure hydrogen expands the molten aluminum, creating voids. The components are subsequently cooled in calm air to produce a stable cellular structure with embedded ceramic components.
Mechanical properties
We subjected cylindrical samples (60 mm diameter × 150 mm height) to compressive loading in order to characterize mechanical properties of our meta-material (Fig. 3). The Young’s modulus, from loading-unloading tests, was E = 5.5 GPa and yield stress, σy = 8.1 MPa (measured according to ISO/DIS 13314 standard). The Poisson’s ratio of the material was approximately 0.0 in the early stages of the loading and began ascending toward 0.5 from 10% engineering strain onward (see Methods, section 1). The cellular structure showed significant deformability, exceeding 20% of engineering strain as expected from previous studies of cellular metals19,20,21,22,23 with the densification strain of εd ≈ 0.25. The inclusion of ceramic spheres did not have a significant effect under static loading because the deformations followed the paths of the least resistance via the cellular matrix in-between the spheres.
Resistance to angle grinder cutting
Relatively low plateau stress (compared to solid steel) and ability for large compressive deformations is excellent for energy dissipation under extreme loads. However, protective systems usually also require hardness to withstand point loads. Ballistic resistance is often achieved with ceramic materials such as high-purity alumina (Al2O3) or high-hardness, armor steels. The multiplicity of the hardness measuring instruments with various indenter shapes and test protocols24 indicate that hardness may not be a fundamental property of a material but rather a composite one including yield strength, work hardening, true tensile strength, modulus of elasticity, and micro properties such as strength of atomic bonds. We were not aiming in our study at low depths of Brinell, Rockwell or Knoop indentations but at resistance to penetration under real-life extreme loads. We concentrated on developing resistance to the severe localized loads such as an angle grinder, power drill, and water jet cutter, which are examples of extreme loads. Focusing on these specific, end-user features allowed us to depart from the established paradigm of designing for the high hardness, i.e. low indentation resistance.
The angle grinder attack represented the first highly localized load applied to penetrate our architected material. We used 115- and 125-mm diameter cutting discs with a sapphire finish to cut our panel samples (see Fig. 4 and Methods section 2 for disc descriptions). The angle grinder revolved at up to 180 revolutions per second, with rim velocity of up to 80 m/s. The angle grinder achieved only a partial incision and subsequently experienced high wear. Its external diameter reduced rapidly from 115 mm to 44 mm (Marcrist disc) and from 125 mm to 100 mm (Tyrolit disc) after 60–65 sec. At that point, the cutting discs became ineffective (Fig. 4b and Movie S1). Exact cutting attack times for the performed tests are tabulated in Methods, section 2. To compare our results with existing armor materials, we also tested one of the best currently available rolled-homogeneous armor (RHA) steels, distributed under MARS 220 trademark. The steel is quenched and tempered at temperatures below 200 °C to give it 440 Brinell hardness. The angle grinder completely penetrated the 10 mm MARS 220 plate in 45 sec (see Methods section 2 and Movie S2).
The resistance mechanism of our architected material exploited the contrast in stiffness between the ceramic spheres and the flexible aluminum cellular structure. Thereby, the energy of the rotating angle grinder was partially transferred into the mechanical vibrations of the spinning disc (Fig. 5) and subsequently into vibrations of the ceramic sphere (nested in the flexible cellular matrix), which interacted with the cutting disc (Fig. 5b,c). The tool operator reported vibrations, and they are also evident in Movie 1. Computed tomography scans also detected cracks in the aluminum foam structure (Fig. 5c,e, Supplementary Information A and Movies 3–5). The working principle of the vibrational interface is shown schematically in Fig. 5b. Localized contact of the rotating disc with the ceramic sphere (blue) generated broadband vibrations. Such behavior is consistent with previous work by Campbell16, who measured multiple vibrational modes, including four nodal waves, after application of a rubbing contact to a rim of a rotating disc.
Dynamic vibrations had not been effective when the disc only touched the external surface of the ceramic sphere because the contact area on the sides of the cutting disc was insufficient to excite considerable disc oscillations. However, as the cutting progressed, it increased the contact region with the disc’s rim (Fig. 5f). Consequently, lateral disc vibrations were generated, which created a dynamic interface with the partially cut ceramic sphere. In addition to the case where the cutting discs were applied to the equator of the sphere, we also tested cases, where the angle grinder cut on the side of a sphere, in the proximity of the equator and closer to the sphere’s pole (see SI with CT scans of these cases and Movies 6–9). We observed the same outcome, i.e., the cutting disc diameter reduced rapidly in just over a minute, and the angle grinder became inoperative. Interestingly, the vibrational mechanism was equally effective against the power drill, where the geometry of the drill bits differed significantly from the flat, cutting discs of angle grinders. In all instances when a drill encountered a ceramic sphere, the drilling progress was arrested (see Movie 10). Hence, the vibrational interface mechanism did not appear sensitive to the aspect ratio of the rotating cutting tools. The experimental procedure and detailed results of cutting and drilling tests are explained in Methods, section 2. The CT-scans of these tests are included in Supplementary Information C.
Theoretical modes of vibrations25,26 consist of shape variations along the angular direction, with waveform denoted by n (see Fig. 6). The first angular wave corresponds to a single sinusoidal wave along the circumference of the disc denoted with n = 1. For n = 2 deflections form a train of two waves, for n = 3 a train of three waves and so on. In addition to circumferential modes, waveforms can also propagate radially from the center of the disc. Such waves are like ripples observed after dropping a pebble into a lake. The fundamental radial mode, corresponding to s = 0, resembles deflection under uniform pressure (see Fig. 6a). Higher radial modes with s = 1, 2, etc form ‘sinusoidal’ waves in the radial direction.
Timoshenko26 expressed free vibrations of a rotating disc as a product of both radial and angular components varying in time, as:
where ωns = 2π fns is the natural frequency of vibrations corresponding to the superposition of angular, n and radial, s modes. Using trigonometric identities, equation (1) can be simplified to:
One should note that natural frequency of the disc depends on the spinning speed, namely ωns = f(ωdisc) is a function of the disc rotational velocity because spinning produces centrifugal tension in the disc, and consequently stiffens it. A careful reader might also recognize that the modal shapes are given in the disc frame of reference, which is rotating with the disc. An external observer measuring deflections of a fixed point in the contact with the rim, such as an embedded ceramic sphere, traces a point moving counterclockwise relatively to the disc spinning clockwise. The coordinate of such a point in the spinning frame of reference is θpoint (t) = θ0 − ωdisct, where θ0 is the initial angular position. Thus, a point, with Rpoint, θpoint coordinates in the stationary frame of reference, experiences the following excitation:
Thereby, a stationary point in space such as a ceramic sphere at the rim of the rotating disc senses two waves, namely the (B)ackward and the (F)orward travelling waves, with rotational frequencies:
where \(\frac{{\omega }_{ns}}{n}\) is the speed of the forward and backward moving wave in the disc frame of reference. Although both waves have the same speed, they move in the opposite directions, and their overlap produces a standing wave in the disc frame of reference. Whereas ωdisc is the spinning velocity of the disc, and n is a number of angular waves in the fundamental modes as shown in Fig. 6a. The number of the angular waveforms, n increases the frequency of the wave contact with the stationary ceramic sphere. This result is consistent with independent derivation by Campbell16 (see Eqs. 6 and 7 of the seperate Campbell derivations, based on the requirements for standing waves, attached in Supplementary Information B).
Number of waves, n has an effect on the excitation frequency experienced by a ceramic sphere. For example, two waves, n = 2 in a train of waves increase the excitation frequency applied to the ceramic sphere by the factor of two. It is useful to note that (4) can also be written in terms of frequencies in cycles per second [Hz], and for the (F)orward travelling wave it is:
Similarly, the (B)ackward travelling wave, which travels against the direction of the disc rotation, has a frequency of:
The analytical time history produced by the first mode of forward and backward moving disc waves is shown in Fig. 6b (see Methods, section 3 for the numerical calculations). Campbell16 measured disc vibrations with both stationary electromagnetic sensors and the probes rotating with the disc. His stationary sensors recorded the forward (higher frequency) and backwards (lower frequency) waves travelling in the opposite directions. The oscillograph record shown in Fig. 33 of Campbell’s article (in Supplementary Information B) resembles Fig. 6b derived from the analytical considerations shown here. While inspecting Campbell’s results, it is necessary to keep in mind, however, that in an oscillograph record the amplitude is dependent on the induced voltage, which, in turn, depends on both the amplitude and the frequency of the vibration. Thus, higher frequencies have magnified amplitudes in proportion to the frequency. Campbell’s experimental work also demonstrated that a prolonged resonance with the backward travelling wave led to disc failure. These observations established that disc vibrations can be destructive. Irregular contact of the cutting disc with the sphere, due to manual operation of the angle grinder, compounded by potential interactions between the forward travelling waves and higher natural modes of the disc, may excite a couple of the natural frequencies at the same time. Multiple natural modes are usually observed during impact tests27. Cumulative excitation produced by the three lowest modes (see Methods, section 3 for the values of the natural frequencies) form a more complicated signal (shown with bold green color in Fig. 6c).
On the one hand, the analytical natural frequencies for the idealized disc (without any central hole) range from 231 Hz to 3341 Hz for the first eight modes (see Methods, section 3). The frequencies with circumferential waveform(s), i.e. with \(n\ge 1\), generate forward and backward travelling waves. Numerical natural frequencies for a composite disc corresponding to dimensions and material properties of 125 mm Tyrolit disc were also computed using ANSYS software (see Methods, section 4). These models include a central opening for fixing the disc to the shaft of the angle grinder. The first 6 natural frequencies produced backward and forward travelling waves in the range from 246 Hz to 2991 Hz (see Fig. 6d). On the other hand, analysis of natural frequencies of the sphere embedded in a continuum with mechanical properties corresponding to our metallic foam resulted in the range of natural frequencies from 5300 Hz to 9300 Hz (Fig. 6e).
Thus, one can expect the vibrational interaction between higher disc frequencies (with n > 5) and local oscillations of the ceramic sphere, which is embedded in a flexible, cellular matrix. These vibrations can be local, or if enough energy is injected, they can encompass more spheres (Fig. 6f). Interestingly, fixing a point on a rim during an eigenanalysis (to approximate the effect of the locally applied load) results in more irregular eigenmodes, as shown in Movie 11. Since the disc is rotating, the contact point is moving across the circumference of the disc (as noted above). Such modal analysis cannot be performed using an eigensolver because the boundary conditions are changing with time. It would require a transient, time history analysis with post-processing of the time signals to identify the natural frequencies and their corresponding waveforms, which is beyond the scope of this article. Irrespectively of the modelling nuances, it is broadly clear that forward and backward moving components of the higher natural disc frequencies will interact with the embedded spheres. Such higher order waves are consistent with the gradual grinding of the discs as opposed to their catastrophic failure into a few, large pieces, which would be more consistent with lower vibrational modes.
The interface between the disc and the ceramic spheres was not only oscillating but also very abrasive due to the fragmentation of the alumina spheres into particulate matter (see Figs. 5c–e, 7). The ceramic spheres exhibited a very rough surface (Fig. 7c), consistent with a low densification morphology, which promoted the fragmentation into particulate matter shown in Fig. 7d–f. The particles created a sandpaper-like, vibrating interface with the cutting disc. We extracted the powder following the cutting tests for further inspection as explained in Methods, section 6 and Supplementary information C. Scanning electron microscopy (SEM) images revealed a variety of particles with a myriad of compositions and shapes (Fig. 7d–f). The size distribution of the particulate matter (50–500 µm) from both the cutting disc (such as fiberglass fragments or iron shards) and ceramic sphere (aluminum oxide) confirmed the abrasive wear of the cutting disc, rather than a fragmentation caused by dynamic cracking of the disc into large fragments.
The contrast between the stiffness of the ceramics and cellular metallic foam matrix as well as the susceptibility of the ceramic spheres to fragmentation were also effective against the waterjet cutter. The abrasive jet cut through the metallic foam but was deflected from the first encountered ceramic sphere (Fig. 8a,b) and accompanied by reverse splashing toward the nozzle. We also conducted tests on a cylindrical sample to enable examination of the sphere erosion (Fig. 8c,d). The curvature of the ceramic obstacle was maintained as the sphere was eroding and it was responsible for widening the jet, which slowed its velocity by two orders of magnitude.
Scrutiny of the final eroded geometry revealed that the jet diameter increased from djet = 1.0 mm to dwake = 5.3 mm when exiting the material sample (Fig. 8d). Considering mass flow rate as constant, m = const, the velocity in the wake, Vwake can be computed from:
where the Vjet is the initial, optimal cutting velocity of the jet and it is given by the manufacturer, while cross-sectional areas Ajet and Awake are measured following a series of cutting tests.
If one assumes that the density of the jet is constant (despite the debris), the wake velocity is:
Thus, the cutting speed in the wake dropped off 50 times from the jet velocity of 821 m/s at the nozzle to 19 m/s inside our architected material. The cutting progress slowed considerably due to the limited abrasive effectiveness of the much slower jet. The velocity, Vwake appeared to be below the limit of active, fast abrasion. It was closer to the regime of slow erosion approaching geological time scales observed in riverbeds and rocks.
We used cut area per unit time to quantify the resistance to waterjet cutting experimentally. The spherical segment (shown in Fig. 8c,d, with 15 mm depth) was cut over 60 s, which corresponded to a cutting rate of ratehierarch = 5.5 cm2/min. We compared that cutting rate with a stainless steel plate with 20 mm thickness and areal density, ρsteel = 157 kg/m2, which was more than double that of our 40 mm metallic foam ceramic structure with ρhierarch = 71 kg/m2. In spite of the higher areal density, the water jet cutting rate of the solid steel plate was two orders of magnitudes faster than that of our metallic foam ceramic sphere architecture at ratesteel = 170 cm2/min. Considering the waterjet cutter effectively stopped at the 15 mm incision, our architected material can be considered non-cuttable by a waterjet cutter.
Discussion
Our experimental observations are consistent with previous studies of waterjets impacting convex obstacles by Wilson and Goldstein28 and later Fujisawa and Kobayashi29. The interaction of the mean flow and the turbulence strengthened as a function of djet/(2R), where djet was the diameter of the jet, and R was the radius of the circular obstacle, but more importantly the measure of its curvature29. The ratio of our jet diameter to the sphere radius was approximately 0.15 and corresponded to case No 2 in their experimental work on cylindrical obstacles. Fujisawa and Kobayashi reported that upon contact with the curved surface the jet diameter increased largely. We also noticed the waterjet widening as a result of the contact with a strongly convex ceramic sphere in our tests. The waterjet resembled an inverted funnel-shape, which abraded the sphere such that the cut geometry maintained the convex curvature in the wake region throughout the cutting (Fig. 8d). That convex curvature in the lee side of the eroded sphere continued to widen the jet during the cutting due to a stable, funnel shape cut plane.
The angle grinder and power drill were also defeated, even though ceramic spheres were partially cut before the cutting attacks were stopped. Thus, we created a resistance mechanism, which is not based on the hardness of the ceramic segments but on vibrations induced in the cutting discs, which have a complex nature and consist of both forward and backward travelling waves, across a broad range of frequencies. Considering the vibrations from the perspective of a ceramic sphere (Fig. 5f), both radial and traveling waves impact the sphere, whenever they pass through the cut. Thus, several natural frequencies of the disc might interact with the metallic foam ceramic material. We expect higher natural frequencies of the disc to interact with the fundamental, natural frequency of the sphere nested in the cellular metal. However, it might be also possible for several frequencies to interact simultaneously as the point load from the sphere is moving around the disc with a noticeable rotational velocity.
Varying the cutting disc diameter, its thickness, and the rotational speed of the disc are expected to produce a range of vibrational responses. At the same time, we have experimentally shown efficacy against cutting discs of various diameters (115 mm and 125 mm) as well as against power drills, which might indicate that the dynamic resistance mechanism is not sensitive to variations in disc geometries. In other words, application of a point load to a rim of a rotating disc always induces vibrations in the disc, irrespectively of its diameter and material. Once travelling waves are present in the disc, they interact with a ceramic sphere in the metallic foam leading to the gradual destruction of the cutting disc. The multitude of waves traveling with various radial and angular frequencies overlay or diverge in time, depending on their relative phase lags and the movement of the point load on the rim. Thus, an irregular wave with varying amplitude is expected, which might help to explain sudden jolts experienced by an angle grinder operator, which occurred at apparently aberrant intervals during the cutting tests (as seen in the Movie 1). Thus, the contact between the disc and the ceramic sphere might get tighter or looser, and considering the variability of the applied pressure by a human operator, varying inclination angle and other real-life random imperfections, the contact forces and vibration waves are expected to contain significant, non-vanishing transient components and exhibit a stochastic nature.
Our resistance mechanism was also likely benefiting from the strain rate effects of granular matter, which are known to increase the fracture toughness of particulate matter exponentially. The tensile strength of sand grains has been shown to double already at 15 m/s loading velocity18. Sandbags that are encountered in conflict zones are effective in stopping bullets mainly due to the strain rate enhancement. Thus, we expect the contact stresses between the vibrating disc and the particles in the cut to increase largely with the rotational velocity of the cutting blade and the frequencies of the disc vibrations because faster loading rates increase strain rate related fracture toughness of the particulate matter.
Significantly, the eroded geometry of a ceramic sphere under the waterjet abrasion was different from the partially cut sphere with an angle grinder, which was accompanied by particulate matter. Thus, our material ‘metamorphosed’ differently under different cutting loads to render them ineffective in all cases. Additionally, local changes in the microstructure of the ceramic sphere material resulting from localized heating (due to friction with the cutting blade) could enable a phase change and densification of alumina under certain conditions. Such material hardening on the surface of the spheres is likely to further enhance the cutting resistance of our architected material and should be investigated in future studies.
In summary, we created a hierarchical architected material by combining hard ceramic spheres and highly compressible aluminum foam matrix and called it ‘Proteus’ due to its metamorphic nature. Ceramic inclusions had no detrimental effect on compressibility under quasi-static load. However, their spatial hierarchy had significant ramifications on performance under dynamic load. In the case of an angle grinder attack, vibrations of the disc, manifested as contact pressure oscillations, coupled with the abrasive action of ceramic particles resulted in extraordinary cutting resistance, consistent with a non-cuttable material. The waterjet cutter was rendered equally ineffective by the curvature of the spheres in the lee side region, which widened the jet cross-section and consequently reduced the jet velocity fifty times according to our estimate.
The configuration of our new architected material can be tailored to a broad range of applications. One can tune foam porosity, alter base materials, adjust the size of spheres, and their packing pattern. We can also modify the thickness of the sandwich panels, the diameter of the cylinders, the thickness of faceplates and manufacture curvilinear geometries effectively. The demonstrated components can be welded and bonded with other materials to form larger structural systems. Security applications such as doors or barriers (as protection from forcible entry attacks) are obvious ones. However, our material technology could also be useful for enhancing the cutting resistance of shoe soles or protective clothing. Workers could benefit from non-cuttable elbow pads or forearm guards in environments with industrial tools. In addition to vibrational inputs, wave propagation via multiple media and chemical transformations at the metallic-ceramic interfaces require further investigation.
Methods
Section 1. mechanical testing of material properties
We manufactured six cylindrical compression specimens with 150 mm height and 60 mm diameter. From these, three aluminum foam baseline specimens and three samples with ceramic spheres embedded in the foam were compressed axially. Three strain gauges spaced equally around the circumference of each of these specimens (120 degrees apart) and placed at mid-height measured the strains. Multiple loading-unloading cycles gave information on Young’s modulus. The same cylindrical samples that were used in the determination of the elastic modulus were loaded to failure to determine the stress-strain response of the material. The data logged from the testing included the compressive force, the readings from each of the applied strain gauges and the crosshead displacement of the testing machine. Yield stress values were determined from the procedure described in ISO/DIS 13314 standard titled “Mechanical testing of materials – Ductility testing – Compression test for porous and cellular materials.” The testing demonstrated that the inclusion of the ceramic spheres did not have a significant effect on the mechanical properties of the foam composite as compared to pure aluminum foam. The loads followed the path of least resistance via the foam matrix, which controlled the compliance. Evolution of material compressibility as manifested by its Poisson ratio is shown in Fig. 9.
Section 2. angle grinder cutting and power drill tests
We tested the resistance of the panels against an angle grinder and a power drill. Three timed attacks were performed with an angle grinder for a duration of one minute. After the time limit had been achieved, the damage was assessed in each case. If complete penetration of the material was seen then the time at which this occurred was noted, in other cases the depth of the final penetration was measured. The test results of the angle grinder attacks are given in Table 1 for our material.
We have also tested resistance of our material samples to a 36 V cordless drill (see Table 2). When the drill encountered a ceramic sphere on its path, the drilling stopped to progress indefinitely. The power drill missed a ceramic sphere in only one case. Whereas it is much harder for the angle grinder to miss a ceramic sphere because it cuts a line segment through the material, it is possible for the drill bit not to encounter a ceramic sphere when their packing is imperfect or only one layer of ceramics is used. If the ceramic spheres are not packed sufficiently tightly, it might be possible for a 10 mm drill to find a spot between the spheres, and drill through the metallic foam easily. One way to ensure that does not happen is to have many layers of the spheres, which are offset relative to each other. Thereby, even if one layer is missed, there is another layer or two behind the first one to ensure that there are no gaps. If the structure is stochastic, it becomes a statistical problem. If the structure is strictly architected, it is a matter of quality control and precision of the manufacturing. In our initial configuration we only had two sparse layers with associated likelihood of ‘missing’ a sphere approximately 1/9 based on our limited tests.
Addition of metallic short fibers (NiCr) in order to reinforce the cellular matrix (as shown in Fig. 10) improved both the cutting and drilling resistance considerably. Embedded wires improved tensile resistance of the cellular material under vibrational load imparted by the rotating disc. Cutting and drilling resistance improved as shown in Tables 3 and 4.
We compared the cutting resistance of our hierarchical structure with a state-of-the-art armor steel plate distributed by ArcelorMittal under Mars 220 trade name. The rolled-homogeneous armor (RHA) steel has 440 Brinell hardness according to the manufacturer data sheet and is used in protective structures and military hardware. We selected 10 mm thick plate with an areal density of \({\rho }_{Mars}^{areal}\) = 78.5 kg/m2, which was comparable to the areal density of our material, \({\rho }_{Proteus}^{areal}\) = 71 kg/m2. Whereas our hierarchical structure was effectively non-cuttable by an angle grinder and wore the cutting discs extensively (see Fig. 11), Mars 220 steel plates were penetrated relatively quickly, within 20 seconds typically (see Fig. 12 and Table 5).
We also carried out cutting experiments on cylindrical samples of our material to enable computed tomography (CT) imaging of the partial incisions. We performed cutting tests with the disc aligned with the sphere center, a sphere side, and in-between two closely spaced spheres (see Supplementary Information A for CT images). The cylindrical samples were non-cuttable, and significant disc wear was observed, which rendered the cutting discs ineffective within one minute. We used premium Tyrolit and Marcrist 850 cutting discs, with 115 mm and 125 mm diameters respectively. Marcrist specify that their discs can be used for cutting and grinding metals, concrete, masonry and building materials.
Section 3. Analytical considerations of vibrations of a rotating disc
Southwell25 and Timoshenko26 derived an analytical solution for the natural frequencies of a circular disc. The solution gives a lower bound on the natural frequencies of the rotating disc and consists of two components. Firstly, natural frequencies of a stationary, non-rotating disc are computed. Next, one accounts for the centrifugal forces, which make the disc stiffer during the disc rotation because centrifugal inertia is stretching/tensioning the disc.
The natural frequencies of a stationary disc, according to Southwell25 are:
where the bending plate rigidity is denoted as:
and the remaining parameters describe the material properties and geometry of a disc. We used the values below to represent a typical cutting disc:
Parameter αns gives the natural frequency for each mode, consisting of n angular and s radial waves (see Fig. 13) as shown in Table 6.
The natural frequencies in cycles per second for a stationary, circular disc, using material properties and geometry from (11), are shown in Table 7:
One should note that the lowest natural frequency is associated with n = 1 and s = 0, and not n = 0 and s = 0. The rotation of the disc adds centrifugal forces, which stretch the disc and increase its natural frequencies. The effect is similar to tensioning a string in a musical instrument, which increases the frequency of its free vibrations and, consequently, its pitch. In order to incorporate that effect, frequencies of a rotating, flexible disc with no appreciable bending rigidity need to be computed first. Southwell25 and Timoshenko26 reported the formula for free vibrations of a flexible disc as:
where ωdisc is the rotational velocity of disc in [rad/sec] and λns corresponds to the modes of vibrations explained above and is given as shown in Table 8:
Thereby, the frequencies of a flexible disc rotating at a typical rotational velocity of a cutting disc, namely ωdisc = 11000 rpm, are shown in Table 9:
The lower bound on natural frequencies of a rotating disc, considering the actual disc material properties and the effect of the centrifugal forces can be approximated as a geometric average of the frequencies of a stationary disc and natural frequencies of a rotating flexible disc, namely:
Therefore, the natural frequencies of our rotating disc have lower bounds given by:
With the fundamental natural frequency of:
Considering the rotation of the disc at:
The excitation experienced by the sphere from the forward and backward travelling waves of the fundamental mode, using Table 9 for n = 1 and s = 0 and referring to Eq. (5) are:
Analogously for the next analytical mode (n = 2 and s = 0), the frequencies of the forward and backward travelling waves are:
One can observe that a higher order wave (with n = 2, 3, …), when coupled with the disc rotations, can produce a forward travelling wave with a significantly higher frequency, and consequently higher frequency vibrations applied to the embedded sphere than the baseline natural frequency of the disc, for example:
Section 4. Finite element analysis of the cutting disc vibrations
ANSYS software was used to calculate the natural frequencies of the used disc. A finite element model of the actual cutting disc was created (Fig. 14). The disc was modelled as 8 layers because the cutting blade is made of a layered glass fiber reinforced composite. We modelled the disc with 115 mm diameter and 25 mm cylindrical hole in the center. We applied the boundary conditions by restraining out of plane deflections and out of plane rotations of the region in the range of 25 mm < d < 40 mm to represent the clamping applied to the disc in the angle grinder. The model was meshed using thin solid elements (SOLID 186 from ANSYS library of elements). Orientation of the coordinate system and application of the boundary conditions are shown in Fig. 14. We used material properties of the disc as given below:
Ex = 52 GPa (Young modulus in x-direction)
Ey = 14 GPa
Ez = 14 GPa
νxy = 0.28 (Poisson ratio in x-y plane)
νyz = 0.30
νxz = 0.28
ρ = 1.85 g cm3.
The orientation of the composite layers employed in the model is shown in Table 11. Note that the material properties are given in the local coordinate system and are rotated in each layer to produce relatively axi-symmetric material properties.
A rotational velocity of 11,000 rpm or 1152 rad/s was applied to the disc. In the first step a static-structural simulation allowed us to compute the stresses produced by the centrifugal force. The resulting maximum stresses are in the range of 5 MPa (Fig. 15).
In the second step the centrifugal stresses were used to setup eigenmode analysis to find the natural frequencies and vibration modes of the rotating disc as shown in Fig. 16.
The results of the modal analysis are listed in Fig. 17. Modes and shapes of vibrations differ from the theoretical solution because the numerical model accounts for a large circular opening in the center of the disc. It also used the orthotropic composite material properties. The backward and forward travelling waves are of primary importance for our analysis. These frequencies are summarized in Tables 12 and 13. For the sake of completeness, frequencies of the radial modes are given in Table 14.
Section 5. Natural frequencies of ceramic sphere(s) embedded in cellular aluminum
The model was created in ANSYS Workbench. Firstly, we considered the vibration of a single ceramic sphere with a diameter of 13 mm placed in the center of the cube (400 mm × 400 mm × 400 mm). The ceramic sphere and the surrounding media shared nodes (Fig. 18). Thereby, contact elements were not needed. The bodies (ceramic sphere and the surrounding solid material representing metallic foam) were meshed with 72,400 elements. The aluminum foam body was fixed on the outer boundaries.
The natural vibrations of a ceramic sphere embedded in metallic foam depend on the proximity of the boundaries such as our faceplates (see Fig. 19). Bringing the boundaries closer to the sphere increases its natural frequency. We have also analyzed the effect of multiple ceramic spheres by computing natural frequencies for cases with a row of ceramic spheres and an array of spheres (Fig. 20) and a grid of spheres (Fig. 21). The presence or absence of the ceramic spheres in the surrounding material influences the natural frequencies. The inclusion of the ceramic material increases the density of the surrounding media because alumina has a greater density of ρAl203 = 3950 kg/m3, then aluminum foam at ρf = 730 kg/m3. At the same time, the spatial grid of the ceramic spheres has a minor effect on the homogenized material stiffness because it is controlled by the compressibility of the compliant foam in between ceramic spheres as shown in our mechanical tests (see Fig. 3). Increased mass density reduced the natural vibrational frequencies, which is consistent with the results shown in Figs. 20 and 21.
We can conclude that the computed frequencies of our models range from \({f}_{single}^{sphere}=5352\,Hz\) to \({f}_{single}^{sphere}=7621\,Hz\) depending on the proximity of the boundaries. Packing the cellular structure with three multiple layers of ceramic spheres would give \({f}_{grid}^{sphere}=5961\,Hz\), which is likely to be in line with the fundamental frequency of our metamorphic material, ‘Proteus’. Interestingly, a multitude of higher modes of vibrations is also possible, because they are closely spaced, with frequency gaps in the range of hundreds of Hz only see (Fig. 19).
Section 6. Chemical composition of the cutting discs, metallic foam and ceramic spheres
Typical cutting discs are made of proprietary fiber glass reinforced composites. Marcrist supplied us with Material Safety Data Sheet (no M SDS-02-0001-2), which disclosed the chemical components in the cutting disc (Table 15). It contains up to 20% of fiberglass reinforcement and significant proportions of ceramics such as aluminum oxide, silicon carbide and zirconium oxide. We also extracted particulate matter from the incision in plate panes shown in Fig. 22. Microscopic analysis of the geometrical shapes and size of the particles is shown in Fig. 7(d–f).
We also carried out energy-dispersive X-ray spectroscopy (EDX) to shed light on the chemical elements in the extracted particulate matter. Based on the images in Fig. 23, we estimated the content of chemical elements in the individual powder particles. EDX analysis of the powder (Table 16) was consistent with the datasheet supplied by the cutting disc manufacturer, Marcrist (Table 15). We also found particles originating from our cellular aluminum foam matrix and alumina oxide ceramic spheres.
Section 7. Computer tomography of material samples
Computed tomography (CT) is used increasingly in material science, as it enables a fast and non-destructive visualization of internal structures. CT is based on the collection of X-ray absorption images of a specimen from different rotational angles. In the reconstruction process, the 3D volume is calculated from the X-ray images. It consists of so-called voxels, whose edge length mainly defines the resolution of the measurement. The grey value of each voxel reflects the local X-ray absorption characteristic. A high grey value represents a high X-ray absorption. This representation enables one to distinguish different materials in the CT measurement.
CT was especially suitable for the inspection of the metallic foam specimens because the exact interaction of our meta-material and an angle grinder was not externally observable. Due to the highly wear-resistant nature of our hierarchical structure, preparation of microsections would be very difficult, if not impossible to achieve. A cylindrical specimen was manufactured for the CT measurements (150 mm tall with 60 mm diameter as shown in Fig. 1c and in Fig. 24 below). The CT measurement (Fig. 25) allowed us to uncover the 3-dimensional structure of the material in the cutting region, including the course of the cuts, the distribution of powder in the foam structure, and the presence of defects such as cracks following the cutting attacks.
The spatial resolution is dependent on the measuring geometry. A small distance between the focal point and the rotation axis is often desirable for a high magnification. When the specimen itself is larger than the scanning volume – the region of interest (ROI) – the outer dimensions of the specimen can physically prevent the scanning volume from being located as close to the focal point as desired. Furthermore, material outside the ROI, which has to be penetrated by the X-rays, reduces scan quality due to the additional absorption of X-rays and reconstruction artefacts. The cylindrical shape of the specimen reduced the specimen volume to the ROI, enabling a positioning close to the focal point and avoiding specimen material outside the ROI as would be the case for a rectangular plate specimen. In addition, the CT measurement relies on the partial penetration of the X-rays through the specimen in every rotational stage. Complete absorbance can occur for example when a wall, consisting of a highly absorptive material like steel, is oriented parallel to the beam path. This can cause massive reconstruction artefacts and is prevented by the cylindrical geometry. The thin metallic face sheet on the cylindrical sample also acted as an X-ray filter reducing the X-ray beam hardening inside the specimen.
Fraunhofer Wilhelm-Klauditz-Institut WKI in Hannover, Germany performed the scans on a Procon X-Ray CT-AlphaDuo device. To maximize the resolution, while capturing the complete region of interest (a cylinder with a height of 70 mm and a diameter of 60 mm), the CT scan was conducted in helix mode combined with a measuring field extension. Focus-object-distance and focus-detector-distance were set to 188 mm and 1300 mm respectively. X-ray parameters were a voltage of 230 kV and a current of 100 µA. 4161 projections averaging 6 images with an integration time of 450 ms each were collected. The voxel resolution of the reconstructed volume amounts to 19.9 µm. For visualization of the volume data VGSTUDIO MAX 3.0 was used.
Change history
30 October 2020
An amendment to this paper has been published and can be accessed via a link at the top of the paper.
References
Bührig-Polaczek, A. et al. Biomimetic cellular metals—using hierarchical structuring for energy absorption. Bioinspir. Biomim. 11, 045002 (2016).
Meyers, M. A., Chen, P.-Y., Lopez, M. I., Seki, Y. & Lin, A. Y. M. Biological materials: A materials science approach. Journal of the Mechanical Behavior of Biomedical Materials 4, 626–657 (2011).
Barthelat, F. Architectured materials in engineering and biology: fabrication, structure, mechanics and performance. International Materials Reviews 60, 413–430 (2015).
Li, X. W., Ji, H. M., Yang, W., Zhang, G. P. & Chen, D. L. Mechanical properties of crossed-lamellar structures in biological shells: A review. Journal of the Mechanical Behavior of Biomedical Materials 74, 54–71 (2017).
Gao, H., Ji, B., Jäger, I. L., Arzt, E. & Fratzl, P. Materials become insensitive to flaws at nanoscale: Lessons from nature. PNAS 100, 5597–5600 (2003).
Gao, H. Application of Fracture Mechanics Concepts to Hierarchical Biomechanics of Bone and Bone-like Materials. Int J Fract 138, 101 (2006).
Schaedler, T. A. et al. Ultralight Metallic Microlattices. Science 334, 962–965 (2011).
Pham, M.-S., Liu, C., Todd, I. & Lertthanasarn, J. Damage-tolerant architected materials inspired by crystal microstructure. Nature 565, 305 (2019).
Haghpanah, B., Salari-Sharif, L., Pourrajab, P., Hopkins, J. & Valdevit, L. Multistable Shape-Reconfigurable Architected Materials. Adv. Mater. 28, 7915–7920 (2016).
Liu, Z. et al. Locally Resonant Sonic Materials. Science 289, 1734–1736 (2000).
Matlack, K. H., Bauhofer, A., Krödel, S., Palermo, A. & Daraio, C. Composite 3D-printed metastructures for low-frequency and broadband vibration absorption. PNAS 113, 8386–8390 (2016).
Krödel, S., Thomé, N. & Daraio, C. Wide band-gap seismic metastructures. Extreme Mechanics Letters 4, 111–117 (2015).
Le, C., Bruns, T. E. & Tortorelli, D. A. Material microstructure optimization for linear elastodynamic energy wave management. Journal of the Mechanics and Physics of Solids 60, 351–378 (2012).
Ryan, S. M. et al. Damping behavior of 3D woven metallic lattice materials. Scripta Materialia 106, 1–4 (2015).
Salari-Sharif, L. et al. Damping of selectively bonded 3D woven lattice materials. Scientific Reports 8 (2018).
Campbell, W. Protection of Steam Turbine Disk Wheels from Axial Vibration. ASME Transactions 46, 31–160 (1924).
Bacon, F. Sylva sylvarum; or, A natural history, in ten centuries. Whereunto is newly added the History natural and experimental of life and death, or of the prolongation of life. (London, Edited by W. Rawley and printed by J. R. for William Lee., 1627).
Druckrey, A., Casem, D., Alshibli, K. & Huskins, E. Influence of Loading Rate on Fracture Strength of Individual Sand Particles. In Dynamic Behavior of Materials, Volume 1 (eds Casem, D., Lamberson, L. & Kimberley, J.) 75–80, https://doi.org/10.1007/978-3-319-41132-3_11 (Springer International Publishing, 2017).
Gibson, L. J., Ashby, M. F. & Ashby, M. Cellular Solids: Structure and Properties. (Cambridge University Press, 1999).
Ashby, M. Metal foams: a design guide. (Butterworth-Heinemann, 2000).
Ashby, M. F. Materials selection in mechanical design. (Butterworth-Heinemann, 2011).
Smith, B. H., Szyniszewski, S., Hajjar, J. F., Schafer, B. W. & Arwade, S. R. Steel foam for structures: A review of applications, manufacturing and material properties. Journal of Constructional Steel Research 71, 1–10 (2012).
Smith, B. H., Szyniszewski, S., Hajjar, J. F., Schafer, B. W. & Arwade, S. R. Characterization of Steel Foams for Structural Components. Metals 2, 399–410 (2012).
LaSalvia, J. C., Campbell, J., Swab, J. J. & McCauley, J. W. Beyond hardness: Ceramics and ceramic-based composites for protection. JOM 62, 16–23 (2010).
Southwell, R. V. On the Free Transverse Vibrations of a Uniform Circular Disc Clamped at Its Centre; and on the Effects of Rotation. Proceedings of the Royal Society of London. Series A, Containing Papers of a Mathematical and Physical Character 101, 133–153 (1922).
Timoshenko, S. Vibration Problems in Engineering. (D. Van Nostrand Company, 1937).
Szyniszewski, S., Akada, T., Masuya, H. & Kajikawa, Y. Numerical Simulation of a Concrete Plate subjected to Impact Load. JSCE Journal of Applied Mechanics 7, 635–42 (2004).
Wilson, D. J. & Goldstein, R. J. Turbulent Wall Jets With Cylindrical Streamwise Surface Curvature. Journal of Fluids Engineering 98, 550 (1976).
Fujisawa, N. & Kobayashi, R. Turbulence characteristics of wall jets along strong convex surfaces. International Journal of Mechanical Sciences 29, 311–320 (1987).
Acknowledgements
This study was funded by the Research Framework of the European Commission under METFOAM Career Integration Grant 631827 with support from program manager Dr. Ing. Antonio Cipollaro. The project was also funded by the Home Office in the UK with the support from the program officer, Jess Sorrell. The work was also supported by the impact acceleration grant no EP/P511456/1, provided by the Engineering and Physical Science Council (EPSRC) in the UK. Support of Dr. Sue Angulatta, a local program manager, is genuinely appreciated. Any opinions, findings, and conclusions expressed in this article are those of the authors and do not necessarily reflect the views of the European Commission, the Home Office nor EPSRC. We are indebted to Dr. Mavrogordato and Prof. Sinclair from µ-VIS X-Ray Imaging Centre at the University of Southampton for performing CT scans of our early material samples. Mr. Peter Haynes, Mr. David Jones, and Dr. David Jesson were invaluable during mechanical testing of our specimens. Mr. Lee Ramsdale and his team machined testing fixtures, which enabled our mechanical tests. We are grateful to Dr. Łukasz Rogal from Polish Academy of Sciences for fruitful discussions and benchmarks against high entropy alloys. We would like to thank: Kilian Fivaesh, Izzuan Bin Sa’adon, Pablo Álvarez del Río and Ioannis Antonakos for their involvement in metallic foam ceramic composite testing and characterization as part of their undergraduate and MSc projects. We are also indebted to Prof. Alan Robins, Dr. Marco Placidi, and Dr. Paul Hayden for insightful discussions about the resistance mechanism to waterjet cutting.
Author information
Authors and Affiliations
Contributions
S.S. designed the material architecture and carried out analytical work on disc vibrations, natural frequencies of ceramic spheres in a continuum media, and waterjet cutting resistance. S.S. guided the overall study. R.V. produced material samples, carried out waterjet and angle grinder cuttings tests. R.V. also performed finite element analysis of disc vibrations and natural frequencies of ceramic spheres nested in a metallic foam block. F.B. carried out computed tomography (CT) tests and assisted in characterization of the cutting resistance as well as material properties such as average pore size and wall thickness. E.J. performed microscopic and chemical analysis of particulate matter extracted from partial incisions of our metamorphic material samples. M.A. synthesized the findings of the study. M.P. explained the resistance mechanism to waterjet cutting. A.C. prepared and processed components for manufacturing of our material samples. H.J.E. brought to light biological links and background to our metamorphic material design. T.H. aided in experimental and computational work at Fraunhofer Institute in Chemnitz. All authors contributed to writing manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Szyniszewski, S., Vogel, R., Bittner, F. et al. Non-cuttable material created through local resonance and strain rate effects. Sci Rep 10, 11539 (2020). https://doi.org/10.1038/s41598-020-65976-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-65976-0