Abstract
In this study, hybrid graphene-Pt/TiO2 nanostructure were synthesized by single-step, inexpensive and surfactant/organic solvent free route; hydrothermal technique. The physicochemical properties of hybrid graphene-Pt/TiO2 nanostructure were carefully analyzed by multiple techniques, including X-ray diffractometer (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). The synthesized hybrid nanostructures were utilized as photocatalyst for the degradation of methylene blue (MB) dye under natural environment at average ambient temperature and mean daily global solar radiation, of about 22–25 °C and 374.9 mWh/cm2, respectively. The activity performance indicated considerable degradation of methylene blue (MB) dye and was in the following order Gr (13%), TiO2 (60%) and hybrid graphene-Pt/TiO2 nanostructure (90%) over 21 min under the natural light illumination. The physiochemical characterization suggests that, the tightly attached metalized TiO2 nanoparticles (Pt-TiO2) on the high surface area graphene sheets improved utilization of visible light and increased separation and transfer of photo-excited electron (ē) hole (h+) pairs. Notably, the hybrid graphene-Pt/TiO2 nanostructure exhibited an excellent cyclic stability for methylene blue (MB) dye removal. Finally, the kinetic behavior indicated that the photocatalytic degradation reaction of the dye obeyed the pseudo-first order (Langmuir-Hinshelwood) kinetics model.
Similar content being viewed by others
Introduction
The global textile industries are forced to be great, as these are fulfills the clothing requirement of the human being and the synthetic dyestuffs are one of the most common requirements for the textile industry1,2. Consequently, the synthetic dyestuffs have become typical industrial organic pollutants during textile dyeing and printing processes3. One of these dyes, Methylene blue (MB) is a photoactive basic aniline dye that is not only toxic but also causes serious ecological problems and damage the marine life4. Therefore, the removal or degradation of heterocyclic organics pollutants has gradually become hot topics for textile industrialists. Among numerous degradation techniques suitable for dye removal, the heterogeneous photocatalytic process is an efficient and economic technique, which can be successfully used to degrade the organic pollutants and transform them into benign substances5,6.
In particular, visible light photocatalysis has appealed great interest because visible light energy takes up more than 80% of the solar energy. Thus the visible light photocatalysis is one of the most promising techniques used to solve environmental remediation7,8. However, it remains great challenge to find appropriate photocatalyst that can yield maximum solar light9. Among different semiconductors, titanium dioxide have been attracted much attention as a photocatalyst due to its high photosensitivity, nontoxicity and biological and chemical stability10,11.
Unfortunately, the photocatalytic activity of TiO2 is mainly confined to the UV light due to its wide band gap (3.20 eV). Moreover, easy recombination of photo-induced electron and holes also leads to reduce their quantum yield. Therefore, there is a need to find a solution to activate TiO2 under visible light and improve its overall photocatalytic efficiency. To address these technological challenges, defect engineering through metal doping on TiO2 and introducing carbonaceous nanomaterials including carbon nanofibers(CNFs), carbon nanotubes (CNTs) and activated carbon (AC) strategy have been applied to fabricate promising photocatalyst to enhance the utilization of visible light for environmental remediation12,13,14,15,16,17.
Graphene, known as two-dimension sp2-hybridized carbon atoms, have a bright future in photocatalysis due to its appealing electronic, thermal and mechanical properties. In addition, graphene has wide surface area (2600 m2/g), and high transparency with strong adsorption properties18,19,20,21,22,23. Consequently, the coupling of graphene and TiO2 may improve the surface area and light harvesting properties of TiO2.
Recently, the incorporation of noble metal nanoparticles into TiO2 has gained widespread attention, because it could greatly reduce the recombination rate of photoexcited electrons and holes24,25,26. Therefore, the combination of these three (TiO2, graphene and Pt) nanomaterials may become a new type of hybrid nanostructure having high photocatalytic activities. Accordingly, in this study visible light active hybrid graphene-Pt/TiO2 nanostructure was synthesized by the hydrothermal technique.
There are already lots of research and development work is done regarding synthesis of graphene-Pt/TiO2 nanostructure, but herein, we demonstrate innovative single-step synthesis via surfactant/organic solvent free method.
After carefully studying the physiochemical properties, we investigated the photocatalytic properties of hybrid graphene-Pt/TiO2 nanostructure as visible light active photocatalyst by methylene blue degradation.
Results and Discussion
The phase and structure of as synthesized hybrid graphene-Pt/TiO2 nanostructure was observed by X-ray powder diffraction (XRD). In Fig. 1, the diffraction peaks located at 2θ value could be well indexed to the anatase phase of TiO2 (JCPDS no. 21–1272) and cubic crystalline phase of the Pt (JCPDS; #04-0802). There was no detectable peak of graphene, which suggests that, the overlap of characteristic one at 2θ ~ 25° with 101 reflection plane of TiO2 at around same 2θ value27. Moreover, as expected, the SEM image with its corresponding EDX elemental analysis Fig. 3(A and B) confirms the appearance of carbon (C), oxygen (O), titanium (Ti) and platinum (Pt) atoms.
The morphology of the hybrid graphene-Pt/TiO2 nanostructure was observed by field emission scanning electron microscopy (FESEM). Figure 2 indicated that natural graphite was successfully converted to graphene. The image (Fig. 2(A)) showed that hybrid nanostructure is mainly consisting of large amount of wrinkled nanosheets which are interconnected to each other’s with slightly curled edges. It can be observed from the high magnification image (Fig. 2(B)) that the Pt/TiO2 nanoparticles were heavily dispersed on the surface of graphene.
Further detailed structure has been observed by transmission electron microcopy (TEM). Figure 4(A and B) showed the low and high magnification images of hybrid graphene-Pt/TiO2 nanostructure, respectively. The low magnification image showed that the nanocomposite exhibited the transparent morphology with some folded surface, which suggested the stacking of numerous pieces of graphene, which shows strong π-π interaction on the surface. Moreover, it can be clearly observed from the high magnification image that there are two different kinds of crystalline nanoparticles and their measured planar distance (d = 0.23 nm and 0.34 nm) quite similar with the crystallographic planes of Pt (111) and TiO2 (101) confirmed that these nanoparticles are Pt and TiO2, respectively.
The surface composition and the valence state of the hybrid graphene-Pt/TiO2 nanostructure were investigated using XPS analysis technique. Figure 5(A), displays the corresponding spectrum of synthesized hybrid nanostructure. As expected, in the survey scan the peaks laying at 532.8, 455.6, 314.9, 284.8, and 70.5 eV corresponding to of OIs, Ti2p, Pt4d, CIs and Pt4f, respectively confirms the presence of oxygen (O), titanium (Ti), platinum (Pt) and carbon (C) atoms. As shown in Fig. 5(B), deconvolution peaks of the C1s spectrum suggested three peaks. The Peak at 284.0 eV corresponding to C-C bond were generally reflects the sp2 hybridized graphitic carbon atoms28,29 while the peak observed at 285.9 eV corresponding to the C-O bond and the peak located at 288.0 eV corresponding to C=O bond were assigned to the oxygen bound species30. Plus, the O1s spectrum in Fig. 5(C) confirms the presence of oxygen in metal oxide at the peaks of 530.2 and 533.11 eV corresponding to the Ti-O-Ti and Ti-O-C bonds, respectively in a hybrid graphene-Pt/TiO2 nanostructure31,32. Deconvolution of Ti2p in hybrid nanostructure (Fig. 5(D)) showed the presence of two set of characteristic peaks, one set centered at 464.5 and 458.9 eV which were assigned to the Ti2p1/2 and Ti2p3/2 spin-orbital splitting photoelectrons, respectively31,33. The observed spin-orbit splitting of Ti2p1/2 and Ti2p3/2 (5.9 eV) can prove the presence of Ti4+ chemical state in the hybrid nanostructure. This indicates that titanium exists in the form of TiO2.34. While other set of peaks centered at 465.8 and 463.0 eV were attributed to Ti2p1/2 and Ti2p3/2 spin-orbital splitting photoelectrons, respectively confirm the presence of C-Ti bonds in between TiO2 and graphene28,33. At last, deconvolution of Pt4f in the hybrid nanostructure (Fig. 5(E)) showed the existence of two pairs of doublets of 7/2 and 5/235. The binding energies of Pt4f 7/2 at 73.3 and of Pt4f5/2 at 74.8 eV were attributed to metallic Pt. The binding energy of Pt°4f was slightly higher than the reported value36,37 which referred to the small particle size and the attachment of Pt° with the TiO2/graphene support. The binding energies of Pt4f5/2 at 72.6 and of Pt4f7/2 at 76.3 eV could be corresponded to Pt2+ and Pt4+, respectively, thereby indicates that the mixed-valance Pt nanoparticles coexist in the hybrid graphene-Pt/TiO2 nanostructure. The formation of mixed-valance Pt nanoparticles indicates the decomposition of H2PtCl6 in the hybrid nanostructure as follows.
In addition, the existence of Pt2+ states indicating Pt-O bond which anchored on the surface of TiO2/graphene network38,39.
Photocatalytic degradation of methylene blue (MB) using hybrid graphene-Pt/TiO2 nanostructure was carried out under natural light illumination, and their comparative studies have been performed with the pristine TiO2 and graphene. In addition the experiment on controlled sample without photo-catalyst was also carried out under the identical conditions. Figure 6(A) shows the relationship between absorbance and exposure time of methylene blue (MB) dye solution over hybrid nanostructure. In presence of hybrid graphene-Pt/TiO2 nanostructure, the absorption peak intensity of methylene blue (MB) dye solution at λ = 664 nm has noticeably decreased upon increasing the exposure time and it is observed that the most of methylene blue (MB) dye molecules decomposes after 21 min of irradiation time. No further shifting of absorption peak of methylene blue (MB) dye solution can be understood by the decomposition of chromophores40. Additionally, Fig. 6(B) shows the comparative study of the degradation of methylene blue (MB) dyes over the blank, TiO2, graphene and hybrid graphene-Pt/TiO2 nanostructure. The photocatalytic degradation efficiency was calculated using the following formula4.
where C0 and Ct are the initial and final concentration based on the absorbance intensity of the sample at a specific time interval. Graphene, TiO2 and synthesized hybrid graphene-Pt/TiO2 nanostructure exhibits photocatalytic ability for MB dyes solution degradation under natural light illumination in comparison to controlled sample. As shown, the degradation efficiency for pristine TiO2 increased slightly compared to those for the pristine graphene sample. However, low photocatalytic efficiency of pristine TiO2 is understandable due to its large band gap and partial utilization of visible light energy41,42. In contrast, hybrid graphene-Pt/TiO2 nanostructure had very high photocatalytic efficiency for MB dyes solution degradation. The decomposition of MB by graphene, TiO2 and hybrid graphene-Pt/TiO2 nanostructure over 21 min under illumination of natural light were found to be 13%, 60% and 90%, respectively. The observed high photocatalytic efficiency of hybrid graphene-Pt/TiO2 nanostructure is understandable because of high surface area which provides more active sites for photocatalytic reactions43, additionally graphene could accelerate migration rate of the photoexcited charges therefore helping faster availability to the reaction channels and improving the initiation of the photocatalytic reaction44. Moreover, tightly attached metalized TiO2 nanoparticles (Pt-TiO2) could not only help to activate the hybrid nanostructure under the irradiation of natural light but it can played main function in the separation of photo-excited electron hole pair. In addition, the interfacial region between the metal (Pt) and semiconductors (TiO2), which is known as Schottky barrier also attribute to the high photocatalytic activity because it would be beneficial for providing efficient channeling of excited electrons and helps to lower the electron density in the semiconductors (TiO2) nanoparticles45,46,47. Subsequently, prevent the electron-hole pair recombination.
In order to determine the kinetic behavior of photocatalyst, the variation of −ln Ct/C0 was plotted versus irradiation time, it was turns out that the photodegradation of the dye obeys the pseudo-first order (Langmuir-Hinshelwood) kinetics model:
where C is the concentration of MB dye solution with respect to time and k (min−1) is the observed rate constant, and after doing the integration following relationship will be obtained
From Fig. 7(B), it was found that the degradation rate constant obtained for hybrid graphene-Pt/TiO2 nanostructure was comparatively very high. Further, the cyclic stability of hybrid graphene-Pt/TiO2 nanostructure was evaluated by repeated photodegradation of MB dye solution (three times). The results from Fig. 7(A), demonstrates almost similar photocatalytic behavior of the nanocomposite. The possible mechanism of photocatalytic degradation of methylene blue under irradiation of natural light can be described as follows (Fig. 7(C)). The TiO2 nanoparticles absorb visible light, resulting the electrons (e−) in the valence band (VB) of TiO2 nanoparticles can be excited to conduction band (CB) of TiO2 nanoparticles. As a result, electron hole (h+) is generated in valance band (VB). Due to good electrical conductivity of graphene the excited electron (e−) can moved freely to the graphene through interface48,49,50,51. Further the electron (e−) may be trapped by the Pt nanoparticles and contributed to the improving separation of photoexcited electron-hole pairs12. On the other hand, due to the synergistic effect of mixed-valance Pt nanoparticles, the electron (e−) from the Pt nanoparticles where also excited from conduction band (CB) and creating hole (h+)25. Moreover, the recombination rate of charge pairs can be diminished by Pt nanoparticles. Finally, the electron can react with O2 and generate super oxide (\({O}_{2}^{.-}\)) radicals while remaining holes (h+) can react with water or OH− ions to generate an extremely oxidizing radical (\(O{H}^{.}\)) which was mainly responsible for degradation of methylene blue dye.
Conclusions
Hybrid graphene Pt/TiO2 nanostructure can be successfully synthesized using single-step, low-cost and environment friendly hydrothermal technique. The hybrid nanostructure was well characterized by XRD, SEM, TEM and XPS techniques. Single-step without use of organic solvents/surfactant synthesis and effectively utilization of synthesized hybrid graphene Pt/TiO2 nanostructure as a natural light sensitive photocatalyst was the main objective of the work. Therefore, the decomposition of model pollutant (methylene blue) using synthesized hybrid nanostructure reaches 90% just over a 19 min of irradiation. It is suggested that the robust synergetic interaction between metalized semiconductor (Pt-TiO2) and graphene contribute to the enhancement of photocatalysis. More importantly, as compared bare TiO2 and graphene, synthesized hybrid graphene Pt/TiO2 nanostructure exhibit high rate constant with good stability over three cycles. Finally, synthesized hybrid graphene Pt/TiO2 nanostructure can be a potential photocatalyst for environmental remediation.
Experimental
Synthesis of Graphene
Graphene oxide was prepared by the following procedure using the modified Hummers method through oxidation of natural graphite52. Firstly, 100 ml of previously cooled concentrated sulphuric acid (H2SO4) and 5 gm of natural graphite powder was taken in a round bottom flask under vigorous stirring until the homogeneous dispersion is obtained. Secondly, 12 g of potassium permanganate (KMnO4) was added slowly into the solution under the stirring for 2 h, followed by addition of 150 ml DI water into the dispersion under the stirring for another 1 h. Then above dispersion was treated with 45 ml of 30wt. % hydrogen peroxide (H2O2) so as to terminate the reaction. Then, as prepared product was filtered and washed repeatedly with dilute hydrochloric acid (HCl) and deionized water to neutralize the pH. The resulting product was dispersed in water to give a brown dispersion. Finally, the dispersion was filtered and dried in vacuum oven for overnight at 60 °C.
Synthesis of hybrid graphene-Pt/TiO2 nanostructure
Hybrid graphene-Pt/TiO2 nanostructure was synthesized by hydrothermal method. Firstly, 1 gm of previously synthesized graphene oxide (GO) was exfoliated in 150 mL deionized water by ultrasonication for 1 to 1.5 h. Secondly, 75 µL of 8% hydrogen hexachloroplatinate (H2PtCl6) solution and 125 µL titanium chloride (TiCl3) solution was added into the above suspension by ultrasonication for 30–45 min in a water bath, followed by addition of 200 µL of 98% hydrazine monohydrate (NH2NH2.H2O) solution into the mixture. Then, the reaction mixture was treated in a Teflon vessel sealed in an autoclave equipped with microwave heating system at 150 °C for 8 h. After naturally cooling the prepared hybrid nanostructure was washed, filtered and dried in vacuum oven for overnight at 60 °C. The final product, hybrid graphene-Pt/TiO2 nanostructure was collected and characterized. Figure 8 shows a schematic illustration for the synthesis procedure and the final product.
Characterization and photocatalytic investigations
The physicochemical properties of the final product were analyzed by powder X-ray diffraction (XRD, Rigaku Japan), field-emission scanning electron microscopy (FESEM, Hitachi S-7400, Japan), transmission electron microscope (TEM, JEOL JEM-2200FS, Japan) and X-ray photoelectron spectroscopy (XPS, AXIS-NOVA, Krotas Analytical, UK) techniques. While photocatalytic activity investigation of synthesized hybrid graphene-Pt/TiO2 nanostructure was evaluated under natural environment on sunny day at average ambient temperature and mean daily global solar radiation, of about 22–25 °C and 374.9 mWh/cm2, respectively in January between 12:00 p.m. to 02:00 p.m. by degradation of methylene blue (MB) dye solution. The procedure used for photocatalytic investigation of synthesized hybrid graphene-Pt/TiO2 nanostructure in this study has followed according to our previous studies4,5,6.
Change history
22 May 2019
A correction to this article has been published and is linked from the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Mouni, L. et al. Removal of Methylene Blue from aqueous solutions by adsorption on Kaolin: Kinetic and equilibrium studies. Applied Clay Science 153, 38–45, https://doi.org/10.1016/j.clay.2017.11.034 (2018).
Castro-Beltrán, A. et al. Titanium butoxide molar ratio effect in the TiO2 nanoparticles size and methylene blue degradation. Optik 157, 890–894, https://doi.org/10.1016/j.ijleo.2017.11.185 (2018).
El-Moselhy, M. M., Kamal & Soha, M. Selective removal and preconcentration of methylene blue from polluted water using cation exchange polymeric material. Groundwater for Sustainable Development 6, 6–13, https://doi.org/10.1016/j.gsd.2017.10.001 (2018).
Al-Meer, S. et al. Engineering of magnetically separable ZnFe2O4@ TiO2 nanofibers for dye-sensitized solar cells and removal of pollutant from water. Journal of Alloys and Compounds 723, 477–483, https://doi.org/10.1016/j.jallcom.2017.06.211 (2017).
Saud, P. S., Ghouri, Z. K., Hassan, M. K., Barakat, N. A. & Kim, H. Y. Nano-designed λ-CaCO3@ rGO photo-catalyst for effective adsorption and simultaneous removal of organic pollutant. Journal of Materials Science: Materials in Electronics 27, 9593–9598 (2016).
Saud, P. S. et al. Photocatalytic degradation and antibacterial investigation of nano synthesized Ag3VO4 particles@ PAN nanofibers. Carbon letters 18, 30–36 (2016).
Liu, J. et al. Metal-free efficient photocatalyst for stable visible water splitting via a two-electron pathway. Science 347, 970–974 (2015).
Cao, S., Low, J., Yu, J. & Jaroniec, M. Polymeric photocatalysts based on graphitic carbon nitride. Advanced Materials 27, 2150–2176 (2015).
Cushing, S. K. et al. Photocatalytic activity enhanced by plasmonic resonant energy transfer from metal to semiconductor. Journal of the American Chemical Society 134, 15033–15041 (2012).
Li, F.-t et al. In-situ one-step synthesis of novel BiOCl/Bi24O31Cl10 heterojunctions via self-combustion of ionic liquid with enhanced visible-light photocatalytic activities. Applied. Catalysis B: Environmental 150, 574–584 (2014).
Pouran, S. R., Bayrami, A., Aziz, A. A., Daud, W. M. A. W. & Shafeeyan, M. S. Ultrasound and UV assisted Fenton treatment of recalcitrant wastewaters using transition metal-substituted-magnetite nanoparticles. Journal of Molecular Liquids 222, 1076–1084 (2016).
Pan, X., Chen, X. & Yi, Z. Defective, porous TiO2 nanosheets with Pt decoration as an efficient photocatalyst for ethylene oxidation synthesized by a C3N4 templating method. ACS applied materials & interfaces 8, 10104–10108 (2016).
Zhu, Q. et al. Stable blue TiO2−x nanoparticles for efficient visible light photocatalysts. Journal of Materials Chemistry A 2, 4429–4437 (2014).
Zheng, Z. et al. Metallic zinc-assisted synthesis of Ti3+ self-doped TiO2 with tunable phase composition and visible-light photocatalytic activity. Chemical Communications 49, 868–870 (2013).
Zhang, Y., Tang, Z.-R., Fu, X. & Xu, Y.-J. TiO2− graphene nanocomposites for gas-phase photocatalytic degradation of volatile aromatic pollutant: is TiO2− graphene truly different from other TiO2− carbon composite materials? ACS nano 4, 7303–7314 (2010).
Chen, Z., Zhang, N. & Xu, Y.-J. Synthesis of graphene–ZnO nanorod nanocomposites with improved photoactivity and anti-photocorrosion. CrystEngComm 15, 3022–3030 (2013).
Han, C., Zhang, N. & Xu, Y.-J. Structural diversity of graphene materials and their multifarious roles in heterogeneous photocatalysis. Nano Today 11, 351–372 (2016).
Lee, K.-R., Jang, S. H. & Jung, I. Analysis of acoustical performance of Bi-layer graphene and graphene-foam-based thermoacoustic sound generating devices. Carbon 127, 13–20 (2018).
Zhang, N., Yang, M.-Q., Liu, S., Sun, Y. & Xu, Y.-J. Waltzing with the versatile platform of graphene to synthesize composite photocatalysts. Chemical reviews 115, 10307–10377 (2015).
Zhang, N., Yang, M.-Q., Tang, Z.-R. & Xu, Y.-J. Toward improving the graphene–semiconductor composite photoactivity via the addition of metal ions as generic interfacial mediator. ACS nano 8, 623–633 (2013).
Lu, K.-Q., Xin, X., Zhang, N., Tang, Z.-R. & Xu, Y.-J. Photoredox catalysis over graphene aerogel-supported composites. Journal of Materials Chemistry A 6, 4590–4604 (2018).
Zhang, N., Zhang, Y. & Xu, Y.-J. Recent progress on graphene-based photocatalysts: current status and future perspectives. Nanoscale 4, 5792–5813 (2012).
Quan, Q., Lin, X., Zhang, N. & Xu, Y.-J. Graphene and its derivatives as versatile templates for materials synthesis and functional applications. Nanoscale 9, 2398–2416 (2017).
Cui, Y., Huang, J., Fu, X. & Wang, X. Metal-free photocatalytic degradation of 4-chlorophenol in water by mesoporous carbon nitride semiconductors. Catalysis Science & Technology 2, 1396–1402 (2012).
Maeda, K. et al. Photocatalytic activities of graphitic carbon nitride powder for water reduction and oxidation under visible light. The Journal of Physical Chemistry C 113, 4940–4947 (2009).
Di, Y., Wang, X., Thomas, A. & Antonietti, M. Making Metal Carbon Nitride Heterojunctions for Improved Photocatalytic Hydrogen Evolution with Visible Light. ChemCatChem 2, 834–838 (2010).
Chen, L., Yang, S., Mu, L. & Ma, P.-C. Three-dimensional titanium dioxide/graphene hybrids with improved performance for photocatalysis and energy storage. Journal of Colloid and Interface Science 512, 647–656, https://doi.org/10.1016/j.jcis.2017.10.103 (2018).
Huang, Q. et al. Enhanced photocatalytic activity of chemically bonded TiO2/graphene composites based on the effective interfacial charge transfer through the C–Ti bond. Acs Catalysis 3, 1477–1485 (2013).
Chen, C. et al. Synthesis of visible-light responsive graphene oxide/TiO2 composites with p/n heterojunction. Acs Nano 4, 6425–6432 (2010).
Yu, H., Xu, P., Lee, D.-W. & Li, X. Porous-layered stack of functionalized AuNP–rGO (gold nanoparticles–reduced graphene oxide) nanosheets as a sensing material for the micro-gravimetric detection of chemical vapor. Journal of Materials Chemistry A 1, 4444–4450 (2013).
Zhang, X.-Y., Li, H.-P., Cui, X.-L. & Lin, Y. Graphene/TiO 2 nanocomposites: synthesis, characterization and application in hydrogen evolution from water photocatalytic splitting. Journal of Materials Chemistry 20, 2801–2806 (2010).
Gu, L. et al. Glucosamine-induced growth of highly distributed TiO 2 nanoparticles on graphene nanosheets as high-performance photocatalysts. RSC Advances 6, 67039–67048 (2016).
Akhavan, O. & Ghaderi, E. Photocatalytic reduction of graphene oxide nanosheets on TiO2 thin film for photoinactivation of bacteria in solar light irradiation. The Journal of Physical Chemistry C 113, 20214–20220 (2009).
Zhang, M. et al. Hierarchical nanostructures of copper (II) phthalocyanine on electrospun TiO2 nanofibers: controllable solvothermal-fabrication and enhanced visible photocatalytic properties. ACS applied materials & interfaces 3, 369–377 (2011).
Shen, Y., Xiao, K., Xi, J. & Qiu, X. Comparison study of few-layered graphene supported platinum and platinum alloys for methanol and ethanol electro-oxidation. Journal of Power Sources 278, 235–244 (2015).
Nakamura, J. & Kondo, T. Support effects of carbon on Pt catalysts. Topics in Catalysis 56, 1560–1568 (2013).
Stakheev, A. Y. et al. Particle Size Effect on CH4 Oxidation Over Noble Metals: Comparison of Pt and Pd Catalysts. Topics in Catalysis 56, 306–310, https://doi.org/10.1007/s11244-013-9971-y (2013).
Zhang, J., Sasaki, K., Sutter, E. & Adzic, R. Stabilization of platinum oxygen-reduction electrocatalysts using gold clusters. Science 315, 220–222 (2007).
Kim, S., Hwang, S.-J. & Choi, W. Visible light active platinum-ion-doped TiO2 photocatalyst. The Journal of Physical Chemistry B 109, 24260–24267 (2005).
Xia, S., Zhang, L., Pan, G., Qian, P. & Ni, Z. Photocatalytic degradation of methylene blue with a nanocomposite system: synthesis, photocatalysis and degradation pathways. Physical Chemistry Chemical Physics 17, 5345–5351 (2015).
Zhang, Q. et al. Advanced fabrication of chemically bonded graphene/TiO 2 continuous fibers with enhanced broadband photocatalytic properties and involved mechanisms exploration. Scientific reports 6, 38066 (2016).
Chen, X., Shen, S., Guo, L. & Mao, S. S. Semiconductor-based photocatalytic hydrogen generation. Chemical reviews 110, 6503–6570 (2010).
Morales-Torres, S., Pastrana-Martínez, L. M., Figueiredo, J. L., Faria, J. L. & Silva, A. M. Design of graphene-based TiO2 photocatalysts—a review. Environmental Science and Pollution Research 19, 3676–3687 (2012).
Quan, Q., XIE, S.-J., WANG, Y. & XU, Y.-J. Photoelectrochemical Reduction of CO2 Over Graphene-Based Composites: Basic Principle, Recent Progress, and Future Perspective. Acta Physico-Chimica Sinica 33, 2404–2423 (2017).
Hufschmidt, D., Bahnemann, D., Testa, J. J., Emilio, C. A. & Litter, M. I. Enhancement of the photocatalytic activity of various TiO2 materials by platinisation. Journal of Photochemistry and Photobiology A: Chemistry 148, 223–231 (2002).
Taft, S. A unique metal-semiconductor interface and resultant electron transfer phenomenon. arXiv preprint arXiv 1202, 5771 (2012).
Hope, G. A. & Bard, A. J. Platinum/titanium dioxide (rutile) interface. Formation of ohmic and rectifying junctions. The Journal of Physical Chemistry 87, 1979–1984 (1983).
Fattakhova-Rohlfing, D., Zaleska, A. & Bein, T. Three-dimensional titanium dioxide nanomaterials. Chemical reviews 114, 9487–9558 (2014).
Luo, W. B., Chou, S. L., Wang, J. Z., Zhai, Y. C. & Liu, H. K. A Metal‐Free, Free‐Standing, Macroporous Graphene@ g‐C3N4 Composite Air Electrode for High‐Energy Lithium Oxygen Batteries. Small 11, 2817–2824 (2015).
Mao, S., Lu, G. & Chen, J. Three-dimensional graphene-based composites for energy applications. Nanoscale 7, 6924–6943 (2015).
Tong, Z. et al. Three-dimensional porous aerogel constructed by g-C3N4 and graphene oxide nanosheets with excellent visible-light photocatalytic performance. ACS applied materials & interfaces 7, 25693–25701 (2015).
Ghouri, Z. K. et al. Synthesis and characterization of Nitrogen-doped &CaCO3-decorated reduced graphene oxide nanocomposite for electrochemical supercapacitors. Electrochimica Acta 184, 193–202, https://doi.org/10.1016/j.electacta.2015.10.069 (2015).
Acknowledgements
Dr. Zafar Khan Ghouri gratefully acknowledges the support of Chemical Engineering Program, Texas A&M University at Qatar and Central laboratories Unit, Qatar University.
Author information
Authors and Affiliations
Contributions
Z.K.G. conceived the idea, designs the experiments, wrote the manuscript and followed up the experimental work; K.A. and S.A.M. contributed photocatalytic characterization, analyzed data and discussed the results. A.A. and N.A.M.B. helped in the analysis and experimental work and revised the manuscript to improve the language. All authors reviewed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ghouri, Z.K., Elsaid, K., Abdala, A. et al. Surfactant/organic solvent free single-step engineering of hybrid graphene-Pt/TiO2 nanostructure: Efficient photocatalytic system for the treatment of wastewater coming from textile industries. Sci Rep 8, 14656 (2018). https://doi.org/10.1038/s41598-018-33108-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-33108-4
Keywords
This article is cited by
-
Enhanced visible-light-triggered photocatalytic characteristics of GNPs/CeO2 nanocomposites towards hazardous organic pollutants
Bulletin of Materials Science (2022)
-
Fabrication of stable superhydrophobic bismuth material on the aluminum substrate with high photocatalytic activity
Journal of Nanoparticle Research (2021)
-
Ultrathin Assembles of Porous Array for Enhanced H2 Evolution
Scientific Reports (2020)
-
Synthesis and degradation kinetics of TiO2/GO composites with highly efficient activity for adsorption and photocatalytic degradation of MB
Scientific Reports (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.