Abstract
Innovations in nanostructuring of inorganic crystalline solids are often limited by prerequisite critical nucleation energy and solute supersaturation for formation of a phase. This research provides direct evidence supporting the viability of an unconventional irradiation-induced nanostructuring process, via transmission electron microscopy, that circumvents these preconditions. Using polymorphic silicon carbide (SiC) as a prototype, a surprising two-step nucleation route is demonstrated through which nanoscale distribution of the second phase is achieved by reaction of solutes with neutron irradiation-induced precursors. In the first step, nanoscale α–SiC precipitates in a β–SiC matrix unexpectedly nucleate heterogeneously at structural defects. This occurs at significantly lower temperatures compared with the usual β→α transition temperature. Subsequently, α–SiC precipitate acts as a surrogate template for its structural and compositional transition into a fission product precipitate, palladium silicide. These discoveries provide a modern view of irradiation engineering in polymorphic ceramics for advanced applications.
Similar content being viewed by others
Introduction
Diverse aspects of science, ranging from organic to inorganic to mineral crystallization, have examined the nucleation process. Classical nucleation theory explains that the emergence of a stable cluster of a new, distinct second phase is dependent on overcoming critical nucleation energy1. It is well known that this activation energy is partially abated in metals and ceramics by heterogeneous precipitation of the second phase at structural defects such as grain boundaries2 or interphase interfaces3. Exploiting metallurgical principles for controlled distribution of intragranular nanoscale precipitates, particularly in ceramics, is an attractive prospect4.
Silicon carbide (SiC)—a polymorphic material—is known to exist in more than 250 polytypes5. Apart from electronic applications6, it is being considered as a radiation-tolerant material in nuclear fission and fusion reactors7,8 due to the isotropic nature of the 3 C β-SiC polytype. The irradiation of materials is widely observed to bring microstructural changes due to unexpected phase transformations9,10,11,12,13,14. Such irradiation engineering for nanostructured SiC can be useful for electronic or spintronic applications15,16.
This article describes a counterintuitive intragranular nucleation process in SiC that indirectly avoids the critical nucleation energy barrier. To the best of the research team’s knowledge, it cannot be explained completely by any known nucleation mechanism. This process provides a means for precipitating out a second phase in a rather incompliant matrix under neutron irradiation. This phase transition has been observed in neutron irradiated SiC utilized as a fission product barrier in TRISO (tristructural-isotropic) coated nuclear fuel particles7.
Although transport of fission products along grain boundaries of the β-SiC layer in TRISO coated fuel is most probable from a metallurgical perspective17,18, the intragranular nanoscale precipitation of fission products, mainly palladium silicide, has raised questions regarding their transport mechanisms19,20. The near homogenous distribution of these nanoscale Pd rich precipitates in β-SiC matrix19,20 has led to obvious conclusion based on classical nucleation theory to date that Pd interacts with β-SiC to form these precipitates. Hence, there have been numerous modeling effort to simulate the intragranular Pd transport in TRISO fuel by studying the interaction of Pd with β-SiC21,22,23. However, Gentile et al. has experimentally demonstrated that α-SiC is more susceptible than β-SiC to react with Pd24. The present novel dual-step nucleation mechanism of Pd silicide in SiC certainly gives light to these experimental-theoretical controversies of intragranular transport of fission products and has been demonstrated and explained in rest of the paper.
Results and Discussion
Transmission electron microscopy (TEM) of unirradiated SiC layer of TRISO fuel in Fig. 1(a) shows the presence of stacking faults but no apparent dislocation loops or precipitates are observed. TEM was consistently carried out here along the <011> direction of β-SiC as shown in the inset in Fig. 1(b). Irradiation-induced voids25 about 2–4 nm in diameter are visible in a scanning transmission electron microscopy (STEM) image in Fig. 1(b). Apart from these voids, polygonal-shaped precipitates with edge lengths of about 20–30 nm are mostly observed on Frank loops on {111} planes. The approximate volume fraction of these precipitates is less than one percent of the entire grain of β-SiC under study. Although these precipitates have similar size and morphology, some of them appear to possess strong mass contrast as shown in Fig. 1(c). Their chemical identities are revealed by the energy dispersive spectroscopy (EDS) analysis in TEM. While the precipitate indicated by the blue box in Fig. 1(d) did not contain any element other than Si and C, a significant amount of Pd (a fission product) was found along with Si and C in the precipitate indicated by the red box. The presence of a fission product other than Pd in these precipitates was not observed in this study, but the possibility of Pd-assisted transport of other elements cannot be ruled out26.
The structural analysis by high resolution (HR) TEM imaging further unveils the identities of these precipitates. Figure 2(a) shows a precipitate of Si and C only, with an average edge length of nearly 15 nm, in the β-SiC matrix at the edge of a Frank loop. While the fast Fourier transforms (FFT) of the matrix show only the principal reflections of the cubic β-SiC phase, the FFT of the precipitate corresponds to the 6 H variant of the α-SiC phase. The expected orientation relation between α-SiC and β-SiC, which is {111}β || {0001}α, is observed, since the lattice plane spacing d(111) of β-SiC and d0006 of 6 H α-SiC are both 0.25 nm27. The usual transformation of β-SiC into α-SiC takes place at 2,000 °C or higher27. The presence of the α variant of SiC has been observed to nucleate at an irradiation temperature of 1,000–1,200 °C, which is nearly 50 percent lower than the transformation temperature28. This unusual behavior can be attributed to accelerated diffusion in Si and C that facilitates reconstructive transformation of β-SiC into α-SiC heterogeneously at linear and planar defects28. The structural defect assisted reconstructive transformation is expected to lower the nucleation energy barrier associated with α-SiC formation. Figures S1 and S2 shows the same transformation in SiC subjected to different experimental conditions. Similarly, HRTEM of another polygonal precipitate at a Frank loop is shown in Fig. 2(b). The FFT corresponding to the polygonal structure shows the superlattice diffraction spots, apart from the principal β-SiC spots, corresponding to a primitive L12 cubic structure. It has been reported that Pd can react with Si within SiC to form ordered L12 Pd3Si-type structures (space group Pnma)21. There are many other possibilities for structure and stoichiometry21,29. Previously, similar intergranular precipitates have been observed, but their structural identification has not been done26. Graphite, the byproduct of this solid state reaction, was not observed in this microscopic investigation.
Unlike the isolated α-SiC and Pd-rich precipitates presented in Figs 1 and 2, an interesting feature in Fig. 3(a) is a nanoscale region that resides in β-SiC and has varied contrast within its own periphery. The image not only shows the contrast in mass of the two regions confined in a hexagonal periphery, but also the appearance of different crystallography. This precipitate appears to be isolated from any structural defects from the two-dimensional perspective of TEM, but the possibility of a defect out of the TEM foil cannot be denied. The linear chemical analysis along Line 1-2, normal to the phase transition front shown in Fig. 3(b), indicates that only the brighter region in the STEM image is chemically rich with Pd. A different region of β-SiC in Fig. 3(c) captures all three kinds of precipitates encountered in this study. In the magnified image of the semi-transformed region, indicated by the green box, it clearly appears that the Pd and α-SiC regions are associated with two Frank loops terminating in opposite directions. From this evidence, it appears that the diffusional transformation of α-SiC into Pd3Si is aided by the intragranular transport of Pd via linear or planar defects. However, there is possibility of Pd transport in the bulk β-SiC matrix20,26. These results lead to the intriguing puzzle of why Pd reacts with the α variant of SiC only. Interestingly, the presence of nanoscale α–SiC variant avails the readiness of Pd reaction with SiC as compared with that with a single phase, β-SiC24. It can be extrapolated that α-SiC precipitates potentially accelerated the Pd silicide formation. It is probably energetically expensive for Pd silicide to create new semi-coherent or incoherent interfaces with the β-SiC phase, together with the fact that it has a lower chemical affinity with β-SiC. This allows Pd3Si precipitates to be metamorphosed upon the surrogate α-SiC phase without movement of any phase boundary. Hence, this process uniquely circumvents the nucleation barrier by adopting the morphology of parent α-SiC rather than creating new interfaces with β-SiC. Also, the accelerated solute diffusion along structural defects does not require a conventional solute supersaturation for second phase precipitation. Though only one type of Pd silicide was found here, there is the possibility of formation of other types depending upon the processing conditions21,29.
The structural analysis of such a semi-transformed region in β-SiC is shown in Fig. 4. The FFT of the β-SiC matrix shows the characteristic diffraction pattern of cubic-SiC along the [110] zone axis. The FFT corresponding to the top part of the structure nucleated at a Frank loop indicates a 6 H variant of SiC, and the expected α–β orientation relationship, {111}β ||{0001}α, is observed. The FFT of the bottom part of the structure shows the superlattice spots, apart from the principal β-SiC spots, corresponding to a primitive L12 cubic structure.
A comparison of neutron irradiated TRISO fuel with out-of-pile experiments, as reported by van Rooyen et al.30, suggests that the out of pile experiments do not simulate the relevant diffusion coefficient of fission products in SiC. Although Pd silicide formation in SiC has also been observed in other type of irradiations such as swift heavy ions (SHI)29, there is no microscopy data available that can ensure the applicability of SHI to induce such nanostructuring in polymorphic ceramics. The comparison of microstructure under neutron and proton irradiation reports that proton irradiation can likely reproduce the microstructure evolution of neutron irradiation since the average size and number density of dislocation loops and voids are similar31. Hence, similar nanostructuring remains a possibility in various polymorphic ceramics such as ZrO2 32 and ZrC33 by various irradiation sources.
In conclusion, the present study reports a heterogeneous nucleation process in a simple polymorphic crystalline solid that involves two discrete reconstructive and diffusive transformations in a sequence. The phase formed upon the irradiation-induced reconstructive transformation subsequently acts as a surrogate phase and facilitates its reaction with a fission product that is transported in the microstructure via linear and planar defects. The fission product precipitates adopt the exact morphology of the parent phase without movement of any phase boundary and bypass the activation energy otherwise required for its nucleation. These exemplary results challenge the conventional wisdom of precipitation in a nuclear reactor environment. They provide a new view of irradiation-induced nanostructuring in ceramics for advanced applications.
Methods
TRISO coated nuclear fuel was fabricated under standard conditions and subjected to irradiation under the AGR-1 and AGR-2 experimental programs in the Advanced Test Reactor at Idaho National Laboratory. The irradiation conditions for these two programs are reported in Table 1. Samples for TEM were prepared by a dual-beam Quanta 3D focused ion beam instrument. STEM and conventional TEM analysis were conducted on an FEI Tecnai F30 microscope operated at 300 kV. STEM images were obtained using different camera focal lengths, ranging from 80 mm to 4.5 m, for better visualization of nanoscale features in β-SiC. Chemical analyses on TEM samples were carried out using the EDAXTM energy dispersive spectroscopy (EDS) system. Gatan Digital micrograph and TIATM (TEM imaging and analysis) software were used for post-processing of TEM data. The simulations of diffraction patterns were carried out using JEMSTM software.
Data availability statement
The datasets generated during the current study are available from the corresponding author on reasonable request.
References
Karthika, S., Radhakrishnan, T. K. & Kalaichelvi, P. A Review of Classical and Nonclassical Nucleation Theories. Crystal Growth & Design 16, 6663–6681 (2016).
Porter, D. A. & Easterling, K. E. Phase Transformations in Metals and Alloys, Third Edition (Revised Reprint). (Taylor & Francis, 1992).
Ricks, R. A. & Howell, P. R. The formation of discrete precipitate dispersions on mobile interphase boundaries in iron-base alloys. Acta Metallurgica 31, 853–861 (1983).
Cain, M. & Morrell, R. Nanostructured ceramics: a review of their potential. Applied Organometallic Chemistry 15, 321–330 (2001).
Jepps, N. W. & Page, T. F. Polytypic transformations in silicon carbide. Progress in Crystal Growth and Characterization 7, 259–307 (1983).
Nakamura, D. & Gunjishima, I. et al. Ultrahigh-quality silicon carbide single cyrstals. Nature 430, 1009–1012 (2004).
Snead, L. L. et al. Handbook of SiC properties for fuel performance modeling. Journal of Nuclear Materials 371, 329–377 (2007).
Zinkle, S. J. & Busby, J. T. Structural materials for fission & fusion energy. Materials Today 12, 12–19 (2009).
Zhang, Y. et al. Ionization-induced annealing of pre-existing defects in silicon carbide. Nature Communications 9049 (2015).
Baumgardner, W. J. et al. Nanoparticle Metamorphosis: An in Situ High-Temperature Transmission Electron Microscopy Study of the Structural Evolution of Heterogeneous Au:Fe2O3 Nanoparticles. ACS Nano 8, 5315–5322 (2014).
Jin, R. et al. Photoinduced conversion of silver nanospheres to nanoprisms. Science 294, 1901–1903 (2001).
Hayashi, N. & Takahashi, T. Irradiation‐induced phase transformation in type 304 stainless steel. Applied Physics Letters 41, 1100–1101 (1982).
Valdez, J. A., Chi, Z. & Sickafus, K. E. Light ion irradiation-induced phase transformation in the monoclinic polymorph of zirconia. Journal of Nuclear Materials 381, 259–266 (2008).
Naito, M., Ishimaru, M., Valdez, J. A. & Sickafus, K. E. Electron irradiation-induced phase transformation in α-FeSi2. Journal of Applied Physics 104, 073524 (2008).
Falk, A. L. et al. Polytype control of spin qubits in silicon carbide. Nature Communications 4, 1819 (2013).
Castelletto, S. et al. A silicon carbide room-temperature single-photon source. Nature Materials 13, 151–156 (2014).
van Rooyen, I. J., Lillo, T. M. & Wu, Y. Q. Identification of silver and palladium in irradiated TRISO coated particles of the AGR-1 experiment. Journal of Nuclear Materials 446, 178–186 (2014).
Lillo, T. M. & van Rooyen, I. J. Associations of Pd, U and Ag in the SiC layer of neutron-irradiated TRISO fuel. Journal of Nuclear Materials 460, 97–106 (2015).
van Rooyen, I. J., Olivier, E. J. & Neethling, J. H. Fission products silver, palladium, and cadmium identification in neutron-irradiated SiC TRISO particles using a Cs-Corrected HRTEM. Journal of Nuclear Materials 476, 93–101 (2016).
Olivier, E. J. & Neethling, J. H. Palladium transport in SiC. Nuclear Engineering and Design 244, 25–33 (2012).
Turchi, P. E. A. & Ivashchenko, V. I. First-principles study of the Pd–Si system and Pd(001)/SiC(001) hetero-structure. Journal of Nuclear Materials 454, 308–314 (2014).
Rabone, J. & Kovács, A. A DFT investigation of the interactions of Pd, Ag, Sn, and Cs with silicon carbide. International Journal of Quantum Chemistry 114, 1534–1545 (2014).
Schuck, P. C. & Stoller, R. E. Ab initio study of the adsorption, migration, clustering, and reaction of palladium on the surface of silicon carbide. Physical Review B 83, 125303 (2011).
Gentile, M., Xiao, P. & Abram, T. Palladium interaction with silicon carbide. Journal of Nuclear Materials 462, 100–107 (2015).
Kondo, S., Katoh, Y. & Snead, L. L. Microstructural defects in SiC neutron irradiated at very high temperatures. Journal of Nuclear Materials 382, 160–169 (2008).
Olivier, E. J. & Neethling, J. H. The role of Pd in the transport of Ag in SiC. Journal of Nuclear Materials 432, 252–260 (2013).
Harris, G. L. INSPEC, Properties of Silicon Carbide. (INSPEC, Institution of Electrical Engineers, 1995).
Parish, C. M., Koyanagi, T., Kondo, S. & Katoh, Y. Irradiation-induced β to α SiC transformation at low temperature. Scientific Reports 7, 1198 (2017).
Njoroge, E. G. et al. Interface reactions between Pd thin films and SiC by thermal annealing and SHI irradiation. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms 371, 263–267 (2016).
van Rooyen, I. J. et al. Progress in Solving the Elusive Ag Transport Mechanism in TRISO Coated Particles: What Is New? Paper HTR2014-31261, Proceedings of the HTR 2014 Conference, Weihai, China (2014).
Swenson, M. J. & Wharry, J. P. The comparison of microstructure and nanocluster evolution in proton and neutron irradiated Fe–9%Cr ODS steel to 3 dpa at 500 °C. Journal of Nuclear Materials 467, 97–112 (2015).
Chan, S. K. The polymorphic transformations of zirconia. Physica B + C 150, 212–222 (1988).
Katoh, Y., Vasudevamurthy, G., Nozawa, T. & Snead, L. L. Properties of zirconium carbide for nuclear fuel applications. Journal of Nuclear Materials 441, 718–742 (2013).
Hunn, J. D. & Lowden R. A. ORNL/TM-2006/019: Data compilation for AGR-1 baseline coated particle composite LEU01-46T, US Government Publication.
Hunn, J. D., Montgomery, F. C. & Pappano, P. J. ORNL/TM-2010/017: Data Compilation for AGR-2 UCO variant compact lot LEU09-OP2-ZR1, US Government Publication.
Acknowledgements
This work was sponsored by the U.S. Department of Energy, Office of Nuclear Energy, under U.S. Department of Energy Idaho Operations Office Contract DE-AC07-05ID14517, as part of the Advanced Reactor Technology Program. The United States Government retains and the publisher, by accepting the article for publication, acknowledges that the United States Government retains a nonexclusive, paid-up, irrevocable, world-wide license to publish or reproduce the published form of this manuscript, or allow others to do so, for United States Government purposes. The authors would like to acknowledge the efforts of Mr. James Madden in the focused ion beam fabrication of the transmission electron microscope samples, as well as other staff at the Materials and Fuels Complex at Idaho National Laboratory. Transmission electron microscopy work was carried out at the Center for Advanced Energy Studies-Microscopy and Characterization Suite.
Author information
Authors and Affiliations
Contributions
S.M., I.V.R., T.M.L. generated the idea and designed the experiments. S.M. performed TEM and analyzed the results. All the authors discussed and contributed to the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Meher, S., van Rooyen, I.J. & Lillo, T.M. A Novel Dual-Step Nucleation Pathway in Crystalline Solids under Neutron Irradiation. Sci Rep 8, 98 (2018). https://doi.org/10.1038/s41598-017-18548-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-18548-8
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.