Abstract
Electrochemical water splitting is one of the most promising systems by which to store energy produced from sustainable sources, such as solar and wind energy. Designing robust and stable electrocatalysts is urgently needed because of the relatively sluggish kinetics of the anodic reaction, i.e. the oxygen evolution reaction (OER). In this study, we investigate the anomalous in situ activation behaviour of carbon-supported Ni2P nanoparticles (Ni2P/C) during OER catalysis in alkaline media. The activated Ni2P/C shows an exceptionally high activity and stability under OER conditions in which the overpotential needed to achieve 10 mA cm−2 was reduced from approximately 350 mV to approximately 300 mV after 8,000 cyclic voltammetric scans. In situ and ex situ characterizations indicate that the activity enhancement of Ni2P catalysts is due to a favourable phase transformation of the Ni centre to β-NiOOH, including increases in the active area induced by structural deformation under the OER conditions. These findings provide new insights towards designing transition metal/phosphide-based materials for an efficient water splitting catalyst.
Similar content being viewed by others
Introduction
The electrochemical splitting of water (H2O → H2 + 1/2O2) has been extensively studied given its promise towards achieving renewable solar-to-chemical fuel conversion1, 2. This process consists of two reactions: the hydrogen evolution reaction (HER) and the oxygen evolution reaction (OER), both of which require electrocatalysts that significantly reduce the overpotentials. This is particularly true for the OER, given its much more sluggish kinetics3, 4. Unfortunately, many OER catalysts that show the necessary performance are based on expensive precious metals, such as Ru and Ir3, 5. Other catalysts have been tested to reduce costs; these catalysts are based on more abundant metals but are nonetheless active and durable, and include first-row transition metal complexes centred on Ni6,7,8,9,10,11,12,13,14,15, Co16,17,18,19, Mn18, Ni-Fe20, 21, and Ni-Co-Fe22.
Ni-based electrocatalysts are among the most extensively studied materials given their high activity in alkaline media4. Under OER conditions, an active Ni centre changes oxidation states between Ni(OH)2 and NiOOH during the potential scans. According to the Bode diagram23, 24, the phase transformation among different Ni(OH)2 and NiOOH species could proceed in alkaline media (Fig. 1). One of the most important aspects of designing a robust catalyst is enhancing the intrinsic activity7, 8, 12, 13, 20,21,22. While still uncertain, the β-NiOOH phase is generally considered the most active towards the OER among the investigated Ni species19, 20, 25. The Bell group posited that the reaction rate is proportional to the β-NiOOH content and demonstrated a reduced overpotential in Ni-Fe oxide catalysts21. Meanwhile, Li and Selloni predicted that β-NiOOH-based structures would demonstrate smaller OER overpotentials than their γ-NiOOH equivalents26. The overall catalysis efficiency suggests that maximizing the active surface area is also an important parameter6, 7, 10. Recently, Nardi et al. exhibited that the OER electrocatalysis of a NiO film produced through atomic layer deposition can be improved by increasing the number of accessible Ni sites7. Likewise, Stern et al. found an enhanced catalytic activity for nano-sized NiO x and Ni(OH)2 with a higher number of active sites10.
A few studies concerning transition metal-P compounds as OER catalysts have been conducted. Kanan and Nocera reported in situ formation of a Co-Pi oxygen-evolving complex (OEC) film that was electrochemically active in an aqueous phosphate buffer solution19. Recently, nickel phosphides were used as efficient oxygen evolving catalysts11,12,13,14,15. In these cases, the formation of a NiO x layer on the surface, which contributes to the enhanced OER performance, might be associated with the underlying P. However, the mechanism of this enhancement is not yet fully understood.
Herein, we investigate the use of Ni2P nanoparticles on conductive carbon supports with a high surface area for OER catalysis. We observed anomalous in situ activation of the electrocatalyst, resulting in an exceptionally high activity and durability. We also revealed that these unique properties are related to the continuous phase transition of Ni species to β-NiOOH, including structural deformation. This finding provides a new method by which to produce a robust and durable Ni2P-based OER electrocatalyst starting from metal phosphide nanoparticles.
Results
The Ni2P nanoparticles were loaded onto the catalyst (Ni2P/C) to achieve a sufficient dispersity and conductivity. The total phosphide loading was set to 50 wt% (which was the highest possible value) to minimize carbon corrosion reactions under the OER conditions by decreasing the exposure of bare carbon surfaces. As shown in Fig. 2a, the Ni2P loading on the carbon supports was successful; the high-resolution transmission electron microscopy (HR-TEM) image clearly shows a lattice distance typical of the Ni2P (001) plane13. Meanwhile, energy dispersive X-ray spectroscopy (EDS) under scanning TEM (STEM) mode demonstrated a good dispersion in the bulk particles (Fig. 2b). The X-ray diffraction (XRD) pattern (Fig. 2c) also confirms the formation of a typical Ni2P structure, with peaks at 40.8°, 44.6°, 47.3°, 54.2°, and 54.4° corresponding to the (111), (021), (210), (300), and (002) planes, respectively (JCPDS 03-0953). Overall, the as-prepared particulate-shaped Ni2P/C and Ni2P were clearly present on the carbon surface.
The OER electrocatalytic activities of Ni2P/C, NiO/C, and IrO x /C were investigated using a glassy carbon electrode (area: 0.196 cm2) in a 0.1 M KOH aqueous solution. Commercial carbon-supported NiO and IrO x nanoparticles (hereafter denoted as NiO/C and IrO x /C, respectively) were used for comparisons to our materials. Interestingly, the oxygen production currents increased with consecutive cyclic voltammetric (CV) scans, as shown in the OER polarization curves (Fig. 3a). For example, the initial OER activity at j = 10 mA cm−2 was measured at about 350 mV, which is slightly more sluggish than the value of 340 mV for IrO x /C (one of the most active OER catalysts in basic aqueous solutions)3, 5. However, the enhanced OER activity was observed over time, even while the electrocatalytic activity of IrO x /C and NiO/C significantly slowed (Supplementary Figs S1 and S2). After 8,000 CV scans, an overpotential of about 300 mV was needed to achieve a current density of 10 mA cm−2 with the Ni2P/C electrocatalyst (E = 1.53 VRHE; RHE = reversible hydrogen electrode), while IrO x /C and NiO/C initially demanded values of 340 and 420 mV, respectively. According to Ni2p XPS spectra of Ni2P and Ni2P/C as shown in Supplementary Fig. S12, both spectra showed almost identical peak position. Therefore, supported carbon does not affect to the active materials and there is no synergistic effect between carbon and Ni2P. Further, the mass-normalized current density of the Ni2P/C electrocatalyst (64.9 A g−1 at 1.53 VRHE) was improved by factors of about 2 and 19 with respect to that of IrO x /C (30.5 A g−1) and NiO/C (3.4 A g−1), respectively (Supplementary Fig. S2). Note that the observed overpotentials for the activated Ni2P/C electrocatalysts are among the lowest values reported under these conditions (Supplementary Table S1)6, 9, 14, 16,17,18, 20, 22, 27,28,29.
Trace amounts of Fe incorporated into the Ni(OH)2 catalysts can enhance the OER electrocatalysis in the first few potential cycles through the formation of highly active Ni-Fe-O species, as previously reported30. Because the removal of a trace amount Fe in the electrolyte is almost impossible in practical applications, we now clarify that the prominent OER activity of Ni2P/C is derived from either incorporation of Fe in oxygenated Ni species or is an intrinsic property of Ni2P/C itself. In fact, NiO/C also showed an improved performance with overpotentials decreasing from about 420 to 360 mV after 500 cycles, as shown in Fig. 3 and Supplementary Fig. S2. However, this improvement was not sustained over additional cycles in the harsh electrochemical environment employed for testing; the NiO/C overpotential later increased to 390 mV after 3,000 scans, which is in sharp contrast to the continued decrease in the corresponding Ni2P/C value up to 8,000 trials. Once the trace Fe was removed, the enhanced activation behaviour for Ni2P/C was only detectable over an extended period of time, whereas the NiO/C performance decreased immediately (Supplementary Fig. S3 and Supplementary Fig. S4), which is consistent with the literature7, 10, 21, 30. Considering that the effect of Fe incorporation is eliminated by the experiments using purified solutions, the activation process would be explained only by changes in the inherent properties of Ni2P/C, such as in situ activation during the electrochemical cycles derived from continuous structural modifications, as discussed later.
Discussion
We analysed the catalyst after the electrochemical measurements to clarify the source of the anomalous activation behaviour. As shown in the TEM images in Fig. 4a, the Ni2P nanoparticles were deformed during the OER, coating a film-like structure onto the carbon support. This is a marked difference from the original composite displayed in Fig. 2a. The high-resolution images show very thin, small crystalline structures, as indicated by the FFT patterns of NiO and Ni(OH)2. Meanwhile, the high-angle annular dark field (HAADF) images using STEM show that relatively heavy atoms are still placed on the carbon supports (Fig. 3b). Likewise, the EDS data indicate that Ni, P, and O are well dispersed on the carbon surface. Thus, the very thin, newly evolved Ni-O-P layer on the carbon supports resulted from electrocatalysis. In Ni2P/C, because the carbonaceous materials with high surface were used as supports, the exact active surface area cannot be measured by conventional physicochemical methods such as Brunauer–Emmett–Teller (BET) measurements. Alternatively, we used the area of reduction peak of Ni(II)/Ni(III), directly associated with the active surface of nickel-based materials. The corresponding increase in the surface area likely accounts for the improved electrochemical performance, a conclusion that was confirmed by observing the rapid growth in electrochemical performance after 500 CV scans, as estimated by the area of characteristic Ni(II)/Ni(III) peaks (Fig. 5a and b)7. In addition, the outstanding OER activity might be attributed to the improved conductivity and charge transfer capability because of the incorporation of carbon supports into nickel phosphides during the structural deformation14.
Next, X-ray absorption and emission spectroscopy was used to gather detailed structural information (Fig. 6). The initial Ni2P/C structure was completely deformed after five CV scans. X-ray absorption near-edge spectroscopy (XANES) showed that the Ni K edge shifted largely in the positive direction during the first five scans, with additional changes through 1,000 scans (Fig. 6a). This demonstrates progressive oxidation, especially when combined with the X-ray photoelectron spectroscopy (XPS) measurements of the Ni 2p core-level (Fig. 6b). The initially prepared Ni2P/C showed a typical Ni-P peak (orange) and a surface Ni-O peak (yellow)31, 32. After repeated OER cycles, a new main peak (violet) assigned to Ni-OH appeared33, 34. To clarify the oxidation state of Ni, the valence state was examined by linear combination fitting method assuming the cycled Ni2P samples include Ni2P and NiO components (inset in Fig. 6a). The valence states of as-prepared Ni2P and NiO were set to be +1.5 and +2. The XANES spectrum of 5 cycle was composed of 42% Ni2P and 58% NiO while the spectrum of 1000 cycle was composed of 100% NiO, which gives +1.8 and +2 valence states for 5 cycle and 1000 cycle, respectively. Similarly, the reduced FFT TEM patterns corresponding to Ni(OH)2(101) and NiO(200) show nickel phosphide oxidation. Microstructural analysis using extended X-ray fine structure (EXAFS) analysis of the Ni K edge (Fig. 6c) reinforced these observations; after deformation, the FFT signal changed completely, with Ni-O and Ni-Ni peaks developing in a manner consistent with the Ni(OH)2 phase31, 32. After five cycles, the Ni-P signal dropped dramatically and almost diminished through 3,000 CV scans (Supplementary Fig. S5). We carefully suggested that P species should have a role to promote deformation of Ni2P and formation of the film-like oxidized Ni species. Again, this indicates that the surface P species dissolved into the solution through consecutive cycles. In addition, the crystallinity of Ni-O and Ni-Ni was enhanced, as observed by the increasing FFT magnitude. Previous research has shown that α-Ni(OH)2 spontaneously converts to β-Ni(OH)2 under alkaline conditions23, particularly in electrochemical potential cycles33,34,35,36. During this process, the Ni(OH)2 crystallinity improves as stacking faults in the oxy-hydroxides disappear34, 37,38,39. According to the reported transformation of Ni(OH)2 and our observed EXAFS signals, the Ni2P/C structural changes must also involve the transformation to a highly ordered β-Ni(OH)2 phase. Furthermore, this transformation did not occur in NiO/C, as shown in Supplementary Fig. S6, indicating that Ni2P/C is a unique precursor for OER catalysis. More detailed discussions concerning these changes encompassing the improved OER activity of Ni-based electrocatalysts are given below.
Interestingly, the reduction peaks of the reacted Ni2P/C surfaces, which are associated with Ni(OH)2 + ne− → NiOOH, are clearly separated into two peaks at 1.27 and 1.37 VRHE after consecutive CV scans (Fig. 5a). The reduction characteristics continued to decrease after 500 CV scans, occurring at the same time as the discussed structural and chemical transformations (inset in Fig. 5b). Furthermore, the area of the two peaks exhibited an inverse trend after repeated scans (Fig. 5c), with the peak at 1.27 V decreasing and the one at 1.37 V increasing up to 6,000 scans. However, the ratio between the two peaks approached approximately 0.3. The OER activity also reached a maximum at 6,000 CV scans (Fig. 3e), suggesting that the anomalous activation and in situ structural changes of Ni2P/C are introduced during the electrochemical redox reactions.
The changes of the NiOOH phase affect its catalytic activity at the potential range of the OER. NiOOH can exist as either the β- or γ-phase in an alkaline aqueous solution40,41,42,43. Subbaraman et al. demonstrated that the OER activity of M-OOH (M = Ni, Co, Fe, or Mn) in alkaline solution is determined solely by the energetics of the OH-MOOH species25. An interaction that is too strong might slow the OER rate because of the excessive stabilization of the reaction intermediates. Our calculations clearly show that the binding energy of OH (E B(OH)) for β-NiOOH (4.90 eV) was relatively small compared to that of γ-NiOOH (1.57 eV) (Fig. 5c). Likewise, the two different peaks at 1.37 and 1.27 VRHE correspond to the β- and γ- phase of NiOOH, respectively40,41,42,43. As shown in Fig. 6b, the β-phase portion steadily increases and saturates through 6,000 CV scans and is accompanied by an improved OER performance and a drastic reduction in peaks assigned to γ-NiOOH. Recall that we predicted increases of the β-Ni(OH)2 phase from EXAFS signals, suggesting that formation of β-NiOOH is favourable according to Fig. 1. Although some studies have demonstrated that the NiP x @NiO y core-shell structure formed during electrocatalysis can enhance OER activity11,12,13, 15, the source of this superior activity is not yet known. Herein, the results of physicochemical characterizations imply that the anomalous activation behaviours of Ni2P/C electrocatalysts towards the OER are derived from the facile formation of nickel phosphide to β-NiOOH with a high surface area in repeated CV scans, probably by the aid of underlying P (Fig. 7). Therefore, this spontaneous phase transformation during the OER circumstance leads to such a high activity and stability.
In summary, Ni2P/C was synthesized and subjected to electrochemical testing, ultimately forming a robust OER electrocatalyst because of the structural transformation. This enhanced performance resulted from the formation of a Ni-O-P film-like structure with a high surface area that was layered onto the carbon support and the preferential growth of β-NiOOH, providing highly active sites for OER. This favourable transition to the β-phase proceeds up to 6,000 CV scans, resulting in continuous enhancement of the OER. After completing this transformation, the outstanding OER activity is stably maintained. These results offer new methods for the initial preparation of OER electrocatalysts that provide excellent catalytic performances.
Methods
Synthesis of the Electrocatalysts
Carbon-supported Ni2P nanoparticles were prepared by thermal decomposition following a previously reported method31. First, nickel(II) acetylacetonate (Ni(acac)2) and (CH3(CH2)7)3P were mixed and stirred at 90 °C in an inert atmosphere. Then, the solution was quickly added to (CH3(CH2)7)3PO, heated to 310 °C, and stirred for 2 h. After the precipitates formed, the reactor was cooled to room temperature and the Ni2P nanoparticles were collected. The Ni(acac)2:(CH3(CH2)7)3P:(CH3(CH2)7)3PO molar ratio was 1:15:20. To acquire 50 wt% Ni2P/C, the nanoparticles were mixed with Vulcan XC-72 carbon black in CH3CON(CH3)2 using a wand-sonicator for 1 h. Then, the prepared catalyst was washed several times and used without further purification. For comparison, carbon-supported NiO nanoparticles were prepared by simple mixing of NiO nanoparticles (<50 nm) and carbon black. The typical preparation method was as follows: NiO nanoparticles and carbon black were sonicated in dimethylacetamide for 1 h. Then, the precipitates were filtered and washed in ethanol several times. The collected powder was dried in a vacuum oven at 60 °C. These particles were denoted as NiO/C.
Electrochemical Measurements
To evaluate the electrochemical properties, we performed half-cell measurements using a three-electrode system, consisting of a working electrode (glassy carbon electrode, diameter = 5 mm), reference electrode (saturated calomel electrode), and counter electrode (Pt wire). The catalyst ink was prepared by mixing Ni2P/C, NiO/C, or IrOx/C (10 mg), a Nafion perfluorinated resin solution (57.2 μL), and CH3CON(CH3)2 (1.6 mL). The ink was transferred onto a rotating glassy carbon electrode (diameter = 5 mm). The catalyst loading was set at 0.15 mg cm−2. CV (1.0 to 1.8 VRHE) was used to measure the OER at a scan rate of 5 mV s−1 in 0.1 M KOH with saturated O2 at room temperature. For consecutive CV scans, the applied potentials were swept from 1.0 to 1.8 VRHE at a faster scan rate of 100 mV s−1. During oxygen evolution, the working electrode was rotated with a rotation speed of 1,600 rpm to remove the oxygen bubbles on the surface. All measurements were standardized vs. RHE and were compensated for the solution resistance, which was obtained from electrochemical impedance spectroscopy. The frequency range was 0.5–200 kHz with an amplitude of 0.025 V. Commercial IrOx/C and NiO/C were used as reference catalysts for comparisons.
Characterization
We used various physicochemical techniques to perform ex situ characterizations of the Ni-P-O electrocatalyst. HR-TEM images were obtained using a Titan 80–300 microscope (FEI) with an acceleration voltage of 300 kV. Spherical aberration (Cs)–corrected STEM images were also acquired using the same equipment. Elemental analysis was conducted by EDS using a Titan 80–300 microscope. Crystallographic information was obtained from XRD patterns (D/Max 2500/PC, Rigaku). The operating conditions were 40 kV and 200 mA with a scan range (2θ) between 30° and 80° at 0.5 ° min−1. X-ray absorption spectroscopy was performed using the 10 C beamline at the Pohang Accelerator Laboratory (PAL). The Ni K edge was collected in fluorescence mode at room temperature. The absorption edge of Ni K (E 0 = 8,333 eV) was calibrated using Ni foil. X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) were analysed by the IFEFFIT software package using ATHENA and ARITEMIS. The experimental details were previously described44. X-ray photoelectron spectroscopy (XPS) was performed using a Theta Probe AR-XPS system (Thermo Fisher Scientific) to compare the surface compositions of the nanoparticles. Monochromatic Al K α (1486.6 eV) radiation was used as an X-ray source. All spectra were obtained at 15 kV and 150 W with a spot size of 400 μm and calibrated with respect to the C 1 s peak at 284.6 eV.
References
Walter, M. G. et al. Solar Water Splitting Cells. Chem. Rev. 110, 6446–6473 (2010).
Cook, T. R. et al. Solar Energy Supply and Storage for the Legacy and Nonlegacy Worlds. Chem. Rev. 110, 6474–6502 (2010).
McCrory, C. C. L. et al. Benchmarking Hydrogen Evolving Reaction and Oxygen Evolving Reaction Electrocatalysts for Solar Water Splitting Devices. J. Am. Chem. Soc. 137, 4347–4357 (2015).
Man, I. C. et al. Universality in oxygen evolution electrocatalysis on oxide surfaces. ChemCatChem 3, 1159–1165 (2011).
McCrory, C. C. L., Jung, S., Peters, J. C. & Jaramillo, T. F. Benchmarking Heterogeneous Electrocatalysts for the Oxygen Evolution Reaction. J. Am. Chem. Soc. 135, 16977–16987 (2013).
Ren, J., Antonietti, M. & Fellinger, T. P. Efficient Water Splitting Using a Simple Ni/N/C Paper Electrocatalyst. Adv. Energy Mater. 5 (2015).
Nardi, K. L., Yang, N., Dickens, C. F., Strickler, A. L. & Bent, S. F. Creating Highly Active Atomic Layer Deposited NiO Electrocatalysts for the Oxygen Evolution Reaction. Adv. Energy Mater. 5 (2015).
Bediako, D. K. et al. Structure–Activity Correlations in a Nickel–Borate Oxygen Evolution Catalyst. J. Am. Chem. Soc. 134, 6801–6809 (2012).
Zhao, Y., Nakamura, R., Kamiya, K., Nakanishi, S. & Hashimoto, K. Nitrogen-doped carbon nanomaterials as non-metal electrocatalysts for water oxidation. Nat. Commun. 4, 2390 (2013).
Stern, L.-A. & Hu, X. Enhanced oxygen evolution activity by NiOx and Ni(OH)2 nanoparticles. Faraday Discuss. 176, 363–379 (2014).
Ledendecker, M. et al. The Synthesis of Nanostructured Ni5P4 Films and their Use as a Non‐Noble Bifunctional Electrocatalyst for Full Water Splitting. Angew. Chem. Int. Ed. 54, 12361–12365 (2015).
Stern, L.-A., Feng, L., Song, F. & Hu, X. Ni2P as a Janus catalyst for water splitting: the oxygen evolution activity of Ni2P nanoparticles. Energy Environ. Sci. 8, 2347–2351 (2015).
Han, A., Chen, H., Sun, Z., Xu, J. & Du, P. High catalytic activity for water oxidation based on nanostructured nickel phosphide precursors. Chem. Commun. 51, 11626–11629 (2015).
Li, Z., Dou, X., Zhao, Y. & Wu, C. Enhanced oxygen evolution reaction of metallic nickel phosphide nanosheets by surface modification. Inorg. Chem. Front. 3, 1021–1027 (2016).
Yu, X.-Y., Feng, Y., Guan, B., Lou, X. W. & Paik, U. Carbon coated porous nickel phosphides nanoplates for highly efficient oxygen evolution reaction. Energy Environ. Sci. 9, 1246–1250 (2016).
Zhao, Y. et al. Graphene-Co3O4 nanocomposite as electrocatalyst with high performance for oxygen evolution reaction. Sci. Rep. 5, 7629 (2015).
Zhuang, Z., Sheng, W. & Yan, Y. Synthesis of Monodispere Au@Co3O4 Core‐Shell Nanocrystals and Their Enhanced Catalytic Activity for Oxygen Evolution Reaction. Adv. Mater. 26, 3950–3955 (2014).
Masa, J. et al. MnxOy/NC and CoxOy/NC Nanoparticles Embedded in a Nitrogen‐Doped Carbon Matrix for High‐Performance Bifunctional Oxygen Electrodes. Angew. Chem. Int. Ed. 53, 8508–8512 (2014).
Kanan, M. W. & Nocera, D. G. In situ formation of an oxygen-evolving catalyst in neutral water containing phosphate and Co2+. Science 321, 1072–1075 (2008).
Friebel, D. et al. Identification of highly active Fe sites in (Ni, Fe) OOH for electrocatalytic water splitting. J. Am. Chem. Soc. 137, 1305–1313 (2015).
Louie, M. W. & Bell, A. T. An Investigation of Thin-Film Ni–Fe Oxide Catalysts for the Electrochemical Evolution of Oxygen. J. Am. Chem. Soc. 135, 12329–12337 (2013).
Qian, L. et al. Trinary Layered Double Hydroxides as High‐Performance Bifunctional Materials for Oxygen Electrocatalysis. Adv. Energy Mater. 5 (2015).
Bode, H., Dehmelt, K. & Witte, J. Zur kenntnis der nickelhydroxidelektrode—I. Über das nickel (II)-hydroxidhydrat. Electrochim. Acta 11, 1079–IN1071 (1966).
Van der Ven, A., Morgan, D., Meng, Y. & Ceder, G. Phase stability of nickel hydroxides and oxyhydroxides. J. Electrochem. Soc. 153, A210–A215 (2006).
Subbaraman, R. et al. Trends in activity for the water electrolyser reactions on 3d M(Ni,Co,Fe,Mn) hydr(oxy)oxide catalysts. Nat. Mater. 11, 550–557 (2012).
Li, Y.-F. & Selloni, A. Mechanism and Activity of Water Oxidation on Selected Surfaces of Pure and Fe-Doped NiOx. ACS Catal. 4, 1148–1153 (2014).
Ma, T. Y., Dai, S., Jaroniec, M. & Qiao, S. Z. Graphitic Carbon Nitride Nanosheet–Carbon Nanotube Three‐Dimensional Porous Composites as High‐Performance Oxygen Evolution Electrocatalysts. Angew. Chem. Int. Ed. 53, 7281–7285 (2014).
Gao, M.-R. et al. Nitrogen-Doped Graphene Supported CoSe2 Nanobelt Composite Catalyst for Efficient Water Oxidation. ACS Nano 8, 3970–3978 (2014).
Gao, M. et al. Efficient water oxidation using nanostructured α-nickel-hydroxide as an electrocatalyst. J. Am. Chem. Soc. 136, 7077–7084 (2014).
Trotochaud, L., Young, S. L., Ranney, J. K. & Boettcher, S. W. Nickel–Iron Oxyhydroxide Oxygen-Evolution Electrocatalysts: The Role of Intentional and Incidental Iron Incorporation. J. Am. Chem. Soc. 136, 6744–6753 (2014).
Seo, H.-R., Cho, K.-S. & Lee, Y.-K. Formation mechanisms of Ni2P nanocrystals using XANES and EXAFS spectroscopy. Mater. Sci. Eng., B 176, 132–140 (2011).
Zhu, Y. et al. Ultrathin Nickel Hydroxide and Oxide Nanosheets: Synthesis, Characterizations and Excellent Supercapacitor Performances. Sci. Rep. 4, 5787 (2014).
Kamath, P. V. et al. Stabilized α‐Ni(OH)2 as Electrode Material for Alkaline Secondary Cells. J. Electrochem. Soc. 141, 2956–2959 (1994).
Tessier, C. et al. Structural and textural evolution of zinc-substituted nickel hydroxide electrode materials upon ageing in KOH and upon redox cycling. Solid State Ionics 133, 11–23 (2000).
Godwin, I. & Lyons, M. Enhanced oxygen evolution at hydrous nickel oxide electrodes via electrochemical ageing in alkaline solution. Electrochem. Commun. 32, 39–42 (2013).
Desilvestro, J., Corrigan, D. A. & Weaver, M. J. Characterization of redox states of nickel hydroxide film electrodes by in situ surface Raman spectroscopy. J. Electrochem. Soc. 135, 885–892 (1988).
Ramesh, T. & Kamath, P. V. Synthesis of nickel hydroxide: effect of precipitation conditions on phase selectivity and structural disorder. J. Power Sources 156, 655–661 (2006).
Deabate, S., Fourgeot, F. & Henn, F. X-ray diffraction and micro-Raman spectroscopy analysis of new nickel hydroxide obtained by electrodialysis. J. Power Sources 87, 125–136 (2000).
Barde, F., Palacin, M., Chabre, Y., Isnard, O. & Tarascon, J.-M. In situ neutron powder diffraction of a nickel hydroxide electrode. Chem. Mater. 16, 3936–3948 (2004).
Hall, D. S., Bock, C. & MacDougall, B. R. The electrochemistry of metallic nickel: oxides, hydroxides, hydrides and alkaline hydrogen evolution. J. Electrochem. Soc. 160, F235–F243 (2013).
Marioli, J. M. & Sereno, L. E. The potentiodynamic behavior of nickel-chromium (80: 20) alloy electrodes in 0.10 N sodium hydroxide. Electrochim. Acta 40, 983–989 (1995).
Barnard, R., Randell, C. & Tye, F. Studies concerning charged nickel hydroxide electrodes I. Measurement of reversible potentials. J. Appl. Electrochem. 10, 109–125 (1980).
Jović, B., Lačnjevac, U., Jović, V. & Krstajić, N. Kinetics of the oxygen evolution reaction on NiSn electrodes in alkaline solutions. J. Electroanal. Chem. 754, 100–108 (2015).
Yoo, S. J. et al. Enhanced stability and activity of Pt-Y alloy catalysts for electrocatalytic oxygen reduction. Chem. Commun. 47, 11414–11416 (2011).
Acknowledgements
This work is supported by supported financially by Global Frontier R Program on Center for Multiscale Energy System (NRF-2016M3A6A7945505), the NRF grant funded by MSIP (2017R1A2B2003363), the KIST Institutional Program, the New and Renewable Energy Core Technology Program of KETEP grant funded by MOTIE (20133030011320, 20143030031340), and the KCRC grant funded by MSIP (2014M1A8A1049349).
Author information
Authors and Affiliations
Contributions
Y.-H.C., I.J. and S.J.Y. developed the idea and conceived the experiments. Y.-H.C., J.-H.J., and conducted experiments and analyses. H.C.H. carried out DFT calculations. Y.-H.C., H.S.P., J.H.J., Y.-K.L. and S.J.Y. discussed the physical and electrochemical data. Y.-H.C. and H.S.P. co-wrote the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Chung, YH., Jang, I., Jang, JH. et al. Anomalous in situ Activation of Carbon-Supported Ni2P Nanoparticles for Oxygen Evolving Electrocatalysis in Alkaline Media. Sci Rep 7, 8236 (2017). https://doi.org/10.1038/s41598-017-08296-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-08296-0
This article is cited by
-
Interfacial electronic structure engineering on molybdenum sulfide for robust dual-pH hydrogen evolution
Nature Communications (2021)
-
Synthesis of Iron Phosphide Nanoclusters by an Electroless Plating Method for Enhanced Oxygen Evolution Reaction
Journal of Electronic Materials (2021)
-
Recent Trends in Synthesis and Investigation of Nickel Phosphide Compound/Hybrid-Based Electrocatalysts Towards Hydrogen Generation from Water Electrocatalysis
Topics in Current Chemistry (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.