Abstract
Herein we report a 3D heterostructure comprising a hierarchical macroporous carbon foam that incorporates mesoporous carbon nanotubes decorated with cobalt oxide nanoparticles as an unique and highly efficient electrode material for the oxygen evolution reaction (OER) in electrocatalytic water splitting. The best performing electrode material showed high stability after 10 h, at constant potential of 1.7 V vs. RHE (reversible hydrogen electrode) in a 0.1 M KOH solution and high electrocatalytic activity in OER with low overpotential (0.38 V vs RHE at 10 mA cm−2). The excellent electrocatalytic performance of the electrode is rationalized by the overall 3D macroporous structure and with the firmly integrated CNTs directly grown on the foam, resulting in a large specific surface area, good electrical conductivity, as well as an efficient electrolyte transport into the whole electrode matrix concurrent with an ability to quickly dispose oxygen bubbles into the electrolyte. The eminent properties of the three-dimensional structured carbon matrix, which can be synthesized through a simple, scalable and cost effective pyrolysis process show that it has potential to be implemented in large-scale water electrolysis systems.
Similar content being viewed by others
Introduction
The imminent threat of global warming and climate change brought by carbon dioxide associated with the extensive use of fossil fuels has turned academic and industrial attention towards hydrogen, known as a clean fuel and could function as an excellent alternative to traditional fossil fuels1,2,3,4. Water electrolysis is one of the most important non-polluting methods to obtain hydrogen from water, in particular when coupled to a renewable energy source such as solar energy5,6,7,8. The water electrolysis technology is based on the generation of hydrogen at cathode and oxygen at anode by passing an electric current through water. One of the biggest problems in the electrocatalytic water splitting process is the sluggish kinetics frequently observed for the oxygen evolution reaction (OER) on the anode7, 9. Today, ongoing research efforts focus on the development of effective catalysts in order to speed up the reaction rate, lower the overpotential and to exhibit good stability. Noble metal oxide based catalysts such as IrO2 and RuO2 have a documented high electrocatalytic activity in OER7, 10 however the high cost and scarcity of these noble metals limit their application, especially in large scale. Consequently, transition metal oxide catalysts based on non-precious and more abundant metals such as iron, nickel, cobalt and manganese have been proposed as viable alternatives to noble metals11,12,13,14. Among them, cobalt oxide (CoOx) catalyst have been widely studied as an alternative for noble metals based catalysts due to its low cost, low environmental foot print and good catalytic activity in OER11, 15, 16.
Upon electrode fabrication, powder form CoOx is typically attached onto conductive substrates using polymeric binders such as Nafion®. However, the employment of any binder can deteriorate the overall performance of the catalyst by (1) reducing the contact area between the electrolyte and active sites; (2) limiting carrier transport within the electrode; (3) hampering electrode stability, thus resulting in compromised electrocatalytic performance of the electrode12, 17. To further improve the electrode characteristics, especially considering the poor conductivity of most metal oxides, an intimate integration of metal oxide nanoparticles with different substrates such as mesoporous silica, nickel foam and carbon materials have been developed11, 15,16,17, with a focus on achieving a good electrical conductivity and high surface area. More recently, 3D electrodes fabricated from materials such as nickel foam, graphene, carbon cloth and carbon paper have been developed to retain all above characteristics as well as to allow for swift and unhindered penetration of electrolytes into the whole electrode matrix11, 12, 16, 18. Further development of such electrode materials that are flexible, low-weight and that can be produced from abundant materials by methods that enable upscaling is thus highly motivating.
Here we introduce a new hierarchically 3D structured, low-weight carbon foam with high surface area and high compressibility, synthesized directly from a commercially available, low-cost melamine foam (Supplementary Fig. S1a)19. Additionally, due to the simple and cost effective synthesis methods (pyrolysis and activation), the melamine based carbon foam has great potential for large-scale applications. Comparing to other carbon foam materials e.g. carbon paper and carbon aerogel, these above-mentioned characteristics indicate that the melamine based carbon foam has at least equal or even better potential to be used as electrode material for OER. The most conductive carbon foam introduced in our previous study19 (denoted as A800) also possesses the highest surface area and was used as a reference material in this study. Herein we demonstrate that the new carbon foam (denoted as P900) exhibits excellent properties as a hybrid electrode for oxygen evolution reactions (OER). The material was obtained after a heat treatment process to increase its electrical conductivity and carbon nanotubes (CNTs) were grown in the pores and on the surface of P900 to further increase its surface area. Finally, after subsequent decoration of the CNTs/P900 support by CoOx nanoparticles a material with excellent properties was obtained. We further show that despite heat treatment and integration of CNTs into the carbon foam, the overall scaffold-like structure with its flexible characteristics is fully preserved. The (CoOx@CNTs/P900) electrode could be implemented directly as for OER and displays a low overpotential of 0.38 V vs RHE at 10 mA cm−2 and a good stability (~10 h at constant potential of 1.7 V vs RHE) in a 0.1 M KOH solution.
Experimental
Materials
Melamine foam (Basotect® G) was purchased from BASF. Cobalt (II) acetate tetrahydrate (Co(C2H3O2)2. 4H2O) and thiophene (C4H4S, 99%) were purchased from Sigma Aldrich. Silver paint was purchased from PELCO®. All chemicals were used as received.
Synthesis of carbon foam
The activated carbon foam sample (denoted as A800, where A stands for activated and the number denotes the treatment temperature) was synthesized following a procedure reported in ref. 18. Briefly, melamine-based polymer foam (BASF, Basotect® G, used as received) was pyrolyzed at 800 °C (1 hour with the ramping rate of 1 °C/min, under N2 flow (50 ml/min)) in a quartz reactor. Immediately after the pyrolysis, an activation gas mixture (2% CO2 in N2, 50 ml/min) was introduced into the system for 2 hours at the same temperature (at 800 °C). On the other hand, P900 sample (where P stands for pyrolyzed and the number denotes the treatment temperature) was produced by the pyrolysis of the polymer foam at 900 °C (6 hours, the ramping rate of 5 °C/min) in a quartz reactor under N2 flow (50 ml/min). After completed heat treatment and activation process, the system was allowed to cool to room temperature under inert (nitrogen) atmosphere.
Synthesis of CNTs on carbon foam
CNTs were grown on the carbon foam substrate by means of catalytic chemical vapor deposition (CCVD). In this study, only cobalt decorated P900 sample was used as a substrate to grow CNTs. The sample was placed on a quartz boat which then was inserted into a horizontal quartz tube. The system was purged with the Varigon gas (5% hydrogen in argon gas, 180 mL/min) for 20 minutes and then heated to 670 °C with 20 min heating time. When the desired temperature was reached, acetylene was introduced into the system (~3.8 ml/min) for 30 minutes (while the Varigon gas flow was also maintained). The system was then allowed to cool down to room temperature under argon atmosphere (180 mL/min). The final product (CNTs/P900) was stored in Falcon tubes for further use.
Synthesis of catalyst material
In a typical process, 20 mg of cobalt (II) acetate tetrahydrate was dissolved in 5 ml of dimethyl formamide (DMF) and sonicated for 3 minutes. The carbon foam sample (20 mg) which can be either A800 or P900 or CNTs/P900, was submerged into the mixture together with 65 μL of thiophene. The mixture was then sonicated for 20 minutes, followed by a drying at 125 °C under nitrogen flow. Finally, the obtained sample was annealed at 400 °C for 2 h in nitrogen atmosphere to facilitate the formation of CoOx. Depending on the initial carbon foam (A800, P900 and CNTs/P900), the final products were denoted as CoOx@A800, CoOx@P900 and CoOx@CNTs/P900, respectively. It is important to note that, a similar procedure (but without annealing step) was used to decorate cobalt on P900 which was later used to synthesis CNTs/P900.
Characterization
Scanning electron microscopy (SEM) was carried out using a Zeiss Merlin FEG-SEM instrument. High-resolution transmission electron microscopy (HRTEM) image was obtained using a JEOL 2100 F instrument operating at 200 keV. Thermogravimetric analysis (TGA) was conducted on a Mettler Toledo equipment (TGA/DSC 1LF) operated at a heating rate of 10 °C/min up to 950 °C in air. The surface chemistry of the samples was examined by the means of X-ray photoelectron spectroscopy (XPS). The photoelectron spectra were collected with a Kratos Axis Ultra DLD electron spectrometer using monochromated Al Kα source operated at 120 W. An analyzer pass energy of 160 eV for acquiring wide spectra and a pass energy of 20 eV for individual photoelectron lines were used. The surface potential was stabilized by the spectrometer charge neutralization system. Processing of the spectra was accomplished with the Kratos software. Raman spectroscopy was performed on a Renishaw InVia Raman spectrometer using a laser excitation wavelength of 633 nm. The CoOx particle size distribution was determined by counting around 70 particles per sample based on SEM images. The content of cobalt element in the electrolyte was detected by using an Inductively Coupled Plasma Optical Emission Spectrometer (ICP/OES) Optima 2000 DV (Perkin Elmer Instruments).
The samples used in the current-voltage studies measurements were cut to a size of ~12 × 5 × 2 mm3 with a surgical blade. The samples were placed over copper electrodes made from a circuit board (electrode size of 24 × 3 mm2 and spacing of ~0.3 mm between adjacent electrodes). To ensure an intimate contact with the electrodes, the sponges were slightly pressed against the substrate by placing a weight (1.5 g) on the top. The copper electrodes were connected to a potentiostat (Metrohm Autolab, PGSTAT302N). Current-voltage sweeps were performed from −1.0 V to 1.0 V at scan rate of 0.1 V/s in air at room temperature. The resistance was estimated based on the I-V curve with 95% confidence interval.
To prepare electrodes, different electrode materials (A800, CoOx@A800, P900, CoOx@P900, CNTs/P900 and CoOx@CNTs/P900) were cut to an appropriate form from the bulks of the respective materials by a surgical blade. The thickness of samples was controlled at around 1.7 mm. A copper wire was attached to an electrode material using silver paste (Supplementary Fig. S1b) and allowed to dry overnight. A platinum coil and Ag/AgCl (1 M KCl) were used as the counter and reference electrodes, respectively, in a three-electrode electrochemical cell (Supplementary Fig. S1c). Linear sweep voltammery (LSV) was performed at a scan rate of 2 mV/s in a 0.1 M KOH solution. Note that 0.1 M KOH solution was used as electrolyte in all electrocatalytic activity tests including stability test in this study. For the stability test, chronoamperometry data were recorded at a constant potential of 1.7 V vs RHE. After 5 hours, the old electrolyte inside the electrochemical cell was replaced with a fresh electrolyte. Another type of stability test was also performed in this study where the sample was tested by 100 consecutive LSV scans (scan rate 5 mV/s). A potentiostat (Metrohm Autolab, PGSTAT302N) connected with FRA32M module (for impedance spectroscopy) was used for all of the electrochemical tests.
Results and Discussions
The results in Table 1 indicate that there is a relation between the electrical conductivity of the carbon foam samples and the carbon content on the surface which is in agreement with the study of Ramos et al. about the electrical properties of activated carbon cloths20. Our previous study19 also showed that the carbon content at the surface of carbon foam as well as their electrical conductivity are directly proportional with the pyrolysis temperature. For example, A800 which was pyrolyzed and activated at 800 °C was found as the most conductive carbon foam compared with other samples which were treated at lower temperature. Due to the electrical conductivity and the high surface area brought by the activation process, A800 was selected as a reference material in this study. On the other hand, as can be seen in the XRD pattern of P900 sample (Fig. 1d), a broad peak appears at 2θ ~26° which can be assigned to C (002) reflection. Thus, even though P900 is still lacking long-range crystal order as shown by the broadened C (002) reflection, it has higher graphitization degree than that of A800 showing no reflection at all for C (002) planes19. Higher treatment temperature for P900 sample can facilitate the formation of sp2 π bonded carbon volume fraction21 leading to dramatic increase of P900 conductivity compared with A800 sample. Moreover, the high amount of nitrogen found on the surface of A800 (more than 16 at. %, Table 1) can also hinder the charge transfer by the forming of insulating phase at high concentration of nitrogen22, 23. Additionally, due to the treatment at higher temperature and longer time than in the case of the A800 sample, a higher extent of shrinkage was observed for the P900 sample. In this sample, more than 90 wt. % and around 55% in terms of volume of the precursor polymer foam was lost after completion of the pyrolysis process (compared with around 80 wt.% and 40% in terms of volume for the A800 sample19). The increased shrinkage of the P900 sample resulted in a smaller sample void volume that could also contribute to a better electrical conductivity of P900 sample. As shown in Supplementary Fig. S2, the electrical conductivity of P900 is far better than that of A800. The estimated resistances of P900 and A800 are 518 ± 1 Ω and 64.7 ± 0.2 kΩ, respectively which is in agreement with the assumption above. Thus, based on these results we expected that the P900 would be the most promising material as the catalyst support for OER. Further evidence for this hypothesis will be presented in the following paragraph.
Structure and composition of the hierarchical carbon foam-nanotube structure decorated with CoOx nanoparticles. (a) Low and (b) high magnification scanning electron micrographs, (c) TEM image and (d) XRD patterns of P900 and CoOx@CNTs/P900 sample, (e) HRTEM image and (f) Electron diffraction pattern of ‘fresh’ CoOx@CNTs/P900 electrode.
The electrocatalytic activities of CoOx@A800 and CoOx@P900 together with “blank” reference (A800 and P900) samples were tested in alkaline electrolyte (0.1 M KOH). As shown in Fig. 2a, the bare P900 electrode has shown much better electrocatalytic activity compared with that of the bare A800 electrode which further confirmed for our initial conclusion in the previous paragraph. Moreover, at a lower nitrogen content (Table 1 and Supplementary Fig. S3a), some certain type of nitrogen such as pyridinic and quaternary nitrogen (Supplementary Fig. S3b) on the surface of P900 can also contribute to the OER performance of the sample24, 25. Cobalt oxide was successfully decorated on carbon foam samples, A800 and P900, as shown in Supplementary Figs S4 and S5a, respectively. At a similar catalyst loading (17 and 16 wt. % for CoOx@A800 and CoOx@P900, respectively), while finely dispersed cobalt oxide nanoparticles were formed on the CoOx@A800 surface, a semi-thin film of cobalt oxide was found on the surface of CoOx@P900. It is evident that the introduction of cobalt oxide on carbon foam gives rise to a better electrocatalytic activity with a lower overpotential and a higher anodic current. For example, the CoOx@P900 electrode demonstrated a higher anodic current (around 2.5 times higher than that of P900) and also a lower overpotential compared with the bare P900 electrode (0.53 V and 0.70 V, respectively). However, in the case of the A800 material, the introduction of the cobalt oxide could neither improve the overpotential nor the anodic current. Therefore, A800 is completely unsuitable for the application in question. The low electrocatalytic activity of A800 and CoOx@A800 also confirmed that the contribution of silver and copper (if any) to the performance of the electrodes is small. Generally, based on the electrocatalytic performance, we came up with a conclusion that the material P900 is the most suitable one to be used as an electrode in OER.
Electrochemical performance of the carbon foam-based electrodes. (a) polarization curves for OER on different carbon foam based electrodes at a scan rate of 2 mV/s, (b) Polarization curves of CoOx@CNTs/P900 under iR compensation at a scan rate of 2 mV/s (~19 ohms, identified by impedance spectroscopy, Complementary Fig. S9a). (c) Chronoamperometric reponses of CoOx@/P900 and CoOx@CNTs/P900 at a constant potential of 1.7 V vs. RHE and (d) 100 consecutive polarization scans obtained with CoOx@CNTs/P900 electrode (at a scan rate of 5 mV/s). All of the tests were performed in 0.1 M KOH solution.
As discussed earlier, the high electrical conductivity of P900 renders it suitable as a catalyst support for OER. However, its low surface area (Table 1) limits the electrocatalytic performance. Thus, in order to increase the surface area, CNTs were directly grown on the P900 surface (Fig. 1 and Supplementary Fig. S6) using the CCVD method without destroying the carbon body of the foam. It is clear that the carbon foam was densely covered by CNTs with some parts being less covered (Fig. 1a) and some fraction could containing fiber-like material. The successful growth of well-entangled CNTs onto the carbon foam (P900) was manifested by an increase in the B.E.T. surface area from 4 m2/g for P900 to 122 m2/g for CNTs/P900. The electrical conductivity of the CNTs/P900 was slightly improved compared to P900 (Supplementary Fig. S2). The estimated resistances were 412 ± 1 and 518 ± 1 Ω for CNTs/P900 and P900, respectively. The measured impedance of both P900 and CNTs/P900 electrode materials in the frequency range of 0.01 to 105 Hz was shown as the Nyquist plots in the Supplementary Fig. S9b. As shown in the figure, the ohmic resistance of the electrolyte and the internal resistance of the electrode described as RS were represented by the value at the intersection point on the real axis (Z’) at high frequency26. Thus based on the the RS value of P900 and CNTs/P900 (which were estimated as 26.20 Ω and 19.07 Ω, respectively) we can conclude that the internal resistance of CNTs/P900 electrode is slightly beter than that of P900 electrode. This conclusion is also in agreement with the measured bulk resistance of these materials (Supplementary Fig. S2). On the other hand, in the case of CNTs/P900 electrode a stepper slope in the high frequency region, which also means a faster ion mobility than that of P900 electrode for the double layer formation26, was observed. The faster ion mobility could be facilitated by the higher electrical conductivity of the CNTs/P900 sample brought by the excellent electrical conductivity of CNTs. Figure 1b showed that after applying the capping agent (thiophene)27 a homogenous decoration of CoOx nanoparticles in the range of 4–14 nm (Supplementary Fig. S7) was achieved (CoOx@CNTs/P900).
The chemical nature of the cobalt oxide catalyst on CoOx@CNTs/P900 were revealed by different techniques such as XRD, HRTEM, Raman spectroscopy and XPS. The survey X-ray photoelectron spectrum of as synthesized CoOx@CNTs/P900 catalyst is shown in Supplementary Fig. S3a and reveals strong signals from cobalt, carbon and oxygen as well as a small nitrogen and sodium signal, as expected from the synthesis process of the carbon foam19. It is noteworthy that no signal of sulfur can be detected suggesting that thiophene was decomposed completely upon the annealing process. Figure 3a and b show the X-ray photoeletron spectra of CoOx@CNTs/P900, before and after OER testing. The presence of a doublet at 780.5/796.0 eV for Co 2p3/2 and Co 2p1/2, respectively is in line with the expected binding energies of Co 2p doublet in cobalt (II) oxide28, 29. Moreover, high intense satellite structures at 786.2 and 802.4 eV for Co 2p3/2 and Co 2p1/2, respectively suggests the presence of high-spin Co (II) ions at the surface. Interestingly a shoulder peak at around 778 eV can be attributed to metallic cobalt on the surface of the CNTs/P900 sample likely due to a reduction of cobalt to lower oxidation states at the high temperature treatment in inert atmosphere29,30,31. XRD and HRTEM analysis of the lattice fringes in the catalyst nanoparticles (Fig. 1d and e, respectively) suggests both CoO and Co3O4 phases present in the samples, in excellent agreement with electron diffraction measurements (Fig. 1f)32, 33. The Raman spectrum of CoOx@CNTs/P900 is vastly dominated by characteristic vibrations of crystalline Co3O4 with clear peaks at 482 cm−1 (Eg), 519 and 621 cm−1 (F2g) and 690 cm−1 (A1g) (Supplementary Fig. S8b)34,35,36. Due to the strong Raman cross section of the Co3O4 peaks37, 38 and the much smaller Raman cross section of Co(II) oxides, the peaks at 455 and 675 cm−1 are almost fully hidden in the envelopes of the stronger Co3O4 signals34. In overall, based on these aforementioned evidences we can conclude that the CoOx@CNTs/P900 comprises a mixture of CoO, Co3O4 and very minute fraction of metallic cobalt on the surface of the sample after the annealing process.
X-ray photoelectron spectrum of the CoOx@CNTs/P900 after OER testing, as shown in Fig. 3b, reveals a significant change in oxidation state of cobalt manifested by a sharpening of the Co 2p3/2 and Co 2p1/2 peaks and the disappearance of the metallic cobalt signal as well as a dramatic loss in the intensity of the satellite peaks. This observation is similar with the phenomenon observed by Petitto and his coworkers in their XPS study of the transformation of Co (II) oxide to Co3O4 at high temperatures under oxygen atmosphere28. The oxidation of cobalt during the OER tests was further evidenced by comparing the O 1 s spectra of the”fresh” and”spent” catalysts (Supplementary Fig. S3c and d), revealing a clear increase in the intensity of the O 1 s component corresponding to Co = O bond at 529.7 eV for the sample subjected to 100 OER sweeps. It was further confirmed by smaller Cototal/O(529.7 eV) atomic ratio of the “spent” catalyst compared with that of the “fresh” catalyst (1.1 and 1.5, respectively). Thus, it is plausible that both the surface metallic cobalt and cobalt (II) oxide were further oxidized to form Co3O4 by newborn oxygen atoms formed during the OER process. Generally, after the electrochemical reaction, Co3O4, as also confirmed by the Raman spectroscopy (Supplementary Fig. S8b), was the dominant phase on the surface of the CoOx@CNTs/P900 electrode.
The electrocatalytic activities of CoOx@CNTs/P900 electrode and the “blank” reference (CNTs/P900) were tested in alkaline electrolyte (0.1 M KOH). As illustrated in Fig. 2a, the higher current density of the “blank” CNTs/P900 electrode clearly indicates that the electrode possesses a higher surface area compared to the “blank” P900. After growing CNTs, there is no sign of cobalt on the surface of CNTs/P900 sample (Supplementary Fig. S3a) indicating that the cobalt catalyst particles were completely covered by carbon. Thus, we can conclude that the contribution of the cobalt metal which was used as catalyst in CNTs growing process to the OER performance of CNTs/P900 and also CoOx@CNTs/P900 sample is very minor. On the other hand, the electrocatalytic activity of the CoOx@CNTs/P900 electrode was much better than that of the CoOx@P900 electrode giving rise to a lower overpotential (0.42 V compared with 0.53 V, at 10 mA/cm2, no iR corrected) as well as to a much higher current density. After growing CNTs, compared with the original bulk density of P900, the bulk density of the CNTs/P900 was almost doubled. Thus the absolute weight of cobalt oxide catalyst on CNTs/P900 sample, which has the same catalyst loading (16 wt. %) with CoOx@P900 sample, is two times higher than the amount of cobalt oxide on P900 sample. This could explain for the higher OER performance of CoOx@CNTs/P900 sample over CoOx@P900. Besides, the introduction of cobalt oxide nanoparticles on CNTs (Fig.1b and c) brought along a significantly higher active surface area and, consequently, a higher catalytic activity compared to the cobalt oxide film found on the CoOx@P900 electrode (Supplementary Fig. S5). Ahn et al. found that the OER activity and the bubble genesis behavior of a catalyst are dependent on the surface morphology39. Metal oxide catalysts with film-like morphology do not perform well upon electrolysis of water due to their low catalytic activity (low surface area) and the platelet morphology also hampers the bubbles ability to detach from a surface (increasing hydrophobicity). Consequently, a higher electrocatalytic activity was observed for the CoOx@CNTs/P900 electrode. As showed in the Table 2, eventhough the overpotential of CoOx@CNTs/P900 electrode (at 10 mA/cm2) is higher than some reported value in the literature, which used better catalysts e.g. NiFe or different material e.g. nickel foam, comparing with the results which based on cobalt oxide catalyst, our material showed a high OER performance (0.38 V vs. RHE) after iR compensation (Fig. 2b). Moreover, it is important to emphasis that the aim of our work was to introduce a robust carbon foam based electrocatalyst platform rather than finding the ultimate electrocatalyst for OER.
The stability test of CoOx@CNTs/P900 and also CoOx@P900 electrodes were carried out using a chronoamperometric mode at a constant potential (1.7 V vs RHE, 3 electrodes setup) in a 0.1 M KOH solution for around 5 h/cycle (total 2 cycles). As shown in Fig. 2c, while a large drop of the current density of CoOx@P900 electrode was observed, the current density of the CoOx@CNTs/P900 electrode only showed a minor downward trend after 5hrs in the first testing cycle. The deactivation of the catalyst could be due to several reasons such as: corrosion of the carbon substrate40, 41, degradation of the electrolytes (pH and conductivity change)42. It is evident that the corrosion of the carbon substrate can be the main reason for the deactivation of CoOx@P900 where much less of catalyst was found on the surface of the sample after the test (Supplementary Fig. S5b) and cobalt (at the wavelength of 228.616 nm) was found in the electrolyte after the stability test (Supplementary Fig. S10). Moreover, the electrocatalytic performance of the 2nd round of CoOx@P900 electrode could not be recovered properly clearly implicating that irreversible corrosion of carbon happened. In the case of CoOx@CNTs/P900, there is no sign of cobalt was found in the electrolyte after stability test. The corrosion process can be remedied by the introduction of CNTs as well as cobalt oxide nanoparticles which are grown/decorated on the carbon foam surface. The fast transport of the generated electrons from the cobalt oxide nanoparticles to the CNTs/P900 surface should help to prevent charge accumulation on the surface and, subsequently, reduce unwanted corrosion reactions42. Also, cobalt oxide nanoparticles preferentially occupy most of the defective sites11 and oxygen containing groups which are more prone to the corrosion. The presence of CoOx nanoparticles should counteract corrosion processes at the electrode surface42,43,44. Noteworthy, when the electrolyte in the electrochemical cell was replaced by a fresh electrolyte after the 1st round, the chronoamperometric curve of the 2nd round of CoOx@CNTs/P900 shows a very similar trend as the 1st round (Fig. 2c) strongly indicating that the decrease in current density was most likely due to degradation of the electrolyte In summary, all of these evidences represented the excellent stability of the CoOx@CNTs/P900 electrode.
We speculate that the good electrocatalytic properties of CoOx@CNTs/P900 is rationalized by a combination of high electrical conductivity, a good charge transport in the vicinity of the active catalysts and a well-balanced morphology of the 3D electrode. The latter property is highly important since it will allow an efficient diffusion of gas bubbles throughout the whole electrode. It has been reported that attachment of gas bubbles on an electrode surface will result in lower electrocatalytic performance and the stability of electrodes, especially in case of a 2D electrode11, 12 by blocking the active catalyst sites and hindering ionic transport. As reported in the literature, the macroporous nickel foam with a pore size from 100 to 200 μm allows for a fast dissipation of large oxygen bubbles into the electrolyte12. Consequently, similar behavior can be anticipated from carbon foam which also possesses large pores, ranging from 50–100 μm (Supplementary Fig. S6a). Moreover, due to the flexibility of the carbon foam, upon wetting by water, the pores can be expanded and thus further facilitate the dissipation of oxygen bubbles. As shown in Fig. 2d, the CoOx@CNTs/P900 electrode was allowed to run for 100 LSV cycles (from 1–1.9 V vs RHE, scan rate of 5 mV/s in 0.1 M KOH solution). After 100 cycles, the anodic current manifested no decrease but even a bit higher catalytic activity than the current collected from the first cycle. The result strongly confirmed that the material is able to quickly dissipate the oxygen bubbles formed during OER of the CoOx@CNTs/P900 electrode.
Conclusions
A novel 3-D hierarchical carbon foam and carbon nanotube structure was applied as anode in OER. Depending on the nature of the heat treatment process, the electrical conductivity of the carbon foam can be easily tuned. In reality, upon comparison of the electrical conductivity and the electrocatalytic activity, the P900 matrix is considered as a suitable material to be used directly as the catalyst support for cobalt oxide catalyst which in turn can be used as oxygen electrode in the water electrolysis process. Moreover, the surface area of the P900 sample can be enhanced up to 30 times by directly growing CNTs on the surface. Owing to the advantageous approach of directly growing CNTs as well as to directly decorate cobalt oxide catalyst on the carbon foam surface, the CoOx@CNTs/P900 electrode exhibited very high electrocatalytic activity also giving a low overpotential of only 0.38 V at 10 mA/cm2 and a good stability after 2 × 5 h under the testing condition. Additionally, due to its unique macroporous frame, the electrode was also able to quickly dispose the oxygen bubbles formed during the water electrolysis process. In summary and on the basis of the results obtained, we anticipate that our carbon foam material which can be synthesized through a simple, scalable and cost effective pyrolysis process is a potent candidate in industrial or large-scale production of electrodes for the water electrolysis.
References
Turner, J. A. A realizable renewable energy future. Science 285(5428), 687–689 (1999).
Proietti, E. et al. Iron-based cathode catalyst with enhanced power density in polymer electrolyte membrane fuel cells. Nature Communications 2, 416 (2011).
Mueller-Langer, F., Tzimas, E., Kaltschmitt, M. & Peteves, S. Techno-economic assessment of hydrogen production processes for the hydrogen economy for the short and medium term. International Journal of Hydrogen Energy 32(16), 3797–3810 (2007).
Tollefson, J. Hydrogen vehicles: Fuel of the future. Nature 464(7293), 1262–1264 (2010).
Sivula, K. Le Formal F., Grätzel M. Solar water splitting: progress using hematite (α‐Fe2O3) photoelectrodes. ChemSusChem 4(4), 432–449 (2011).
Lewis, N. S. & Nocera, D. G. Powering the planet: Chemical challenges in solar energy utilization. Proceedings of the National Academy of Sciences 103(43), 15729–15735 (2006).
Walter, M. G. et al. Solar water splitting cells. Chemical Reviews 110(11), 6446–6473 (2010).
Gray, H. B. Powering the planet with solar fuel. Nature Chemistry 1(1), 7–7 (2009).
Smith, R. D. et al. Photochemical route for accessing amorphous metal oxide materials for water oxidation catalysis. Science 340(6128), 60–63 (2013).
Lee, Y. et al. Synthesis and activities of rutile IrO2 and RuO2 nanoparticles for oxygen evolution in acid and alkaline solutions. The Journal of Physical Chemistry Letters 3(3), 399–404 (2012).
Sharifi, T. et al. Comprehensive Study of an Earth-Abundant Bifunctional 3D Electrode for Efficient Water Electrolysis in Alkaline Medium. ACS Applied Materials & Interfaces 7(51), 28148–28155 (2015).
Lu, X. & Zhao, C. Electrodeposition of hierarchically structured three-dimensional nickel–iron electrodes for efficient oxygen evolution at high current densities. Nature Communications 6, 6616 (2015).
Gao, M.-R. et al. Water oxidation electrocatalyzed by an efficient Mn3O4/CoSe2 nanocomposite. Journal of the American Chemical Society 134(6), 2930–2933 (2012).
Du, P. & Eisenberg, R. Catalysts made of earth-abundant elements (Co, Ni, Fe) for water splitting: recent progress and future challenges. Energy & Environmental Science 5(3), 6012–6021 (2012).
Jiao, F. & Frei, H. Nanostructured Cobalt Oxide Clusters in Mesoporous Silica as Efficient Oxygen‐Evolving Catalysts. Angewandte Chemie International Edition 48(10), 1841–1844 (2009).
Zhao, Y. et al. Graphene-Co3O4 nanocomposite as electrocatalyst with high performance for oxygen evolution reaction. Scientific reports 5, 7629 (2015).
Ji, J. et al. Nanoporous Ni(OH)2 thin film on 3D ultrathin-graphite foam for asymmetric supercapacitor. ACS nano 7(7), 6237–6243 (2013).
Lai, J. et al. Unprecedented metal-Free 3D Porous Carbonaceous Electrodes for Water Splitting. Energy & Environmental Science 9, 1210–1214 (2016).
Pham, T. N. et al. Industrially benign super-compressible piezoresistive carbon foams with predefined wetting properties: from environmental to electrical applications. Scientific reports 4, 6933 (2014).
Ramos, M. E., Bonelli, P. R. & Cukierman, A. L. Physico-chemical and electrical properties of activated carbon cloths: effect of inherent nature of the fabric precursor. Colloids and Surfaces A: Physicochemical and Engineering Aspects 324(1), 86–92 (2008).
Maiken, E. & Taborek, P. Amorphous carbon films deposited from carbon ions extracted from a discharge in fullerene vapor. Journal of Applied Physics 87(9), 4223–4229 (2000).
Zhang, W. et al. Electrical conductivity of nitride carbon films with different nitrogen content. Solid state communications 126(3), 163–166 (2003).
Ismagilov, Z. R. et al. Structure and electrical conductivity of nitrogen-doped carbon nanofibers. Carbon 47(8), 1922–1929 (2009).
Zhang, J., Zhao, Z., Xia, Z. & Dai, L. A metal-free bifunctional electrocatalyst for oxygen reduction and oxygen evolution reactions. Nature nanotechnology. 10(5), 444–52 (2015).
Yang, H. B. et al. Identification of catalytic sites for oxygen reduction and oxygen evolution in N-doped graphene materials: Development of highly efficient metal-free bifunctional electrocatalyst. Science advances 2(4), p.e1501122 (2016).
Choi, B. G. et al. Facilitated ion transport in all-solid-state flexible supercapacitors. ACS nano 5(9), 7205–7213 (2011).
Gracia-Espino, E., López-Urías, F., Terrones, H. & Terrones, M. Self-assembly synthesis of decorated nitrogen-doped carbon nanotubes with ZnO nanoparticles: anchoring mechanism and the effects of sulfur. The Journal of Physical Chemistry C 119(1), 741–747 (2014).
Petitto, S. C., Marsh, E. M., Carson, G. A. & Langell, M. A. Cobalt oxide surface chemistry: the interaction of CoO (100), Co3O4 (110) and Co3O4 (111) with oxygen and water. Journal of Molecular Catalysis A: Chemical 281(1), 49–58 (2008).
Wang, S. et al. Valence control of cobalt oxide thin films by annealing atmosphere. Applied Surface Science 257(8), 3358–3362 (2011).
Cheng, C.-S., Serizawa, M., Sakata, H. & Hirayama, T. Electrical conductivity of Co3O4 films prepared by chemical vapour deposition. Materials Chemistry and Physics 53(3), 225–230 (1998).
Gandia, L. & Montes, M. Effect of thermal treatments on the properties of nickel and cobalt activated-charcoal-supported catalysts. Journal of Catalysis 145(2), 276–288 (1994).
Yang, Q., Lu, Z., Sun, X. & Liu, J. Ultrathin Co3O4 nanosheet arrays with high supercapacitive performance. Scientific Reports 3, 3537 (2013).
Antón, R. L. et al. High-vacuum annealing reduction of Co/CoO nanoparticles. Nanotechnology 25(10), 105702 (2014).
Tang, C.-W., Wang, C.-B. & Chien, S.-H. Characterization of cobalt oxides studied by FT-IR, Raman, TPR and TG-MS. Thermochimica Acta 473(1), 68–73 (2008).
Llorca, J., Ramírez de la Piscina, P., Dalmon, J.-A. & Homs, N. Transformation of Co3O4 during ethanol steam-re-forming. Activation process for hydrogen production. Chemistry of Materials 16(18), 3573–3578 (2004).
Hadjiev, V., Iliev, M. & Vergilov, I. The Raman spectra of Co3O4. Journal of Physics C: Solid State Physics 21(7), 199 (1988).
Gallant, D., Pezolet, M. & Simard, S. Optical and physical properties of cobalt oxide films electrogenerated in bicarbonate aqueous media. The Journal of Physical Chemistry B 110(13), 6871–6880 (2006).
Gwag, J.-S. & Sohn, Y.-K. Interfacial natures and controlling morphology of Co oxide nanocrystal structures by adding spectator Ni ions. Bulletin of the Korean Chemical Society 33(2), 505–510 (2012).
Ahn, S. H. et al. Effect of morphology of electrodeposited Ni catalysts on the behavior of bubbles generated during the oxygen evolution reaction in alkaline water electrolysis. Chemical Communications 49(81), 9323–9325 (2013).
Wang, X. et al. Durability investigation of carbon nanotube as catalyst support for proton exchange membrane fuel cell. Journal of Power Sources 158(1), 154–159 (2006).
Sebastián, D. et al. Enhanced oxygen reduction activity and durability of Pt catalysts supported on carbon nanofibers. Applied. Catalysis B: Environmental 115, 269–275 (2012).
Lu, X. & Zhao, C. Highly efficient and robust oxygen evolution catalysts achieved by anchoring nanocrystalline cobalt oxides onto mildly oxidized multiwalled carbon nanotubes. Journal of Materials Chemistry A 1(39), 12053–12059 (2013).
Grewe, T., Deng, X. & Tüysüz, H. Influence of Fe Doping on structure and water oxidation activity of nanocast Co3O4. Chemistry of Materials 26(10), 3162-–3168 (2014).
Lu, X., Ng, Y. H. & Zhao, C. Gold nanoparticles embedded within mesoporous cobalt oxide enhance electrochemical oxygen evolution. ChemSusChem 7(1), 82–86 (2014).
Gorlin, Y. & Jaramillo, T. F. A bifunctional nonprecious metal catalyst for oxygen reduction and water oxidation. Journal of the American Chemical Society 132(39), 13612–13614 (2010).
Gong, M. et al. An advanced Ni–Fe layered double hydroxide electrocatalyst for water oxidation. Journal of the American Chemical Society 135(23), 8452–8455 (2013).
Xiaolin, Z. et al. Dual-sized NiFe layered double hydroxides in situ grown on oxygen-decorated self-dispersal nanocarbon as enhanced water oxidation catalysts. J. Mater. Chem. A 3, 24540–24546 (2015).
Acknowledgements
We thank Spinchem AB for providing us the polymeric materials. The Bio4Energy programme & the Kempe Foundations are acknowledged for funding. This work is part of the “Artificial Leaf” project funded by the Knut & Alice Wallenberg foundation. Support from the Academy of Finland (SuplaCat) is acknowledged. This work was supported by the University of Danang, University of Science and Technology, code number of project: T2017-02-101. Ajaikumar Samikannu and Umeå Core Facility Electron Microscopy (UCEM) are acknowledged for their technical assistance in capturing the SEM images.
Author information
Authors and Affiliations
Contributions
T.N.P., T.W., K.K. and J.-P.M. wrote the manuscript text. The synthesis of carbon foam and CNTs/carbon foam composites were carried out by T.N.P. The catalyst preparation, electrode fabrication and BET measurements were done by T.N.P. The electrical conductivity was measured by T.N.P. and W.S. The electrochemical tests were done by T.N.P. and T.S. The XPS analysis was carried out by A.S. The Raman analysis was performed by T.S. The T.G.A., TEM and HRTEM measurements were done by R.S. All authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pham, T., Sharifi, T., Sandström, R. et al. Robust hierarchical 3D carbon foam electrode for efficient water electrolysis. Sci Rep 7, 6112 (2017). https://doi.org/10.1038/s41598-017-05215-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-05215-1
This article is cited by
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.