Abstract
The interplay between electron correlation and topology of relativistic electrons may lead to a fascinating stage of the research on quantum materials and emergent functions. The emergence of various collective electronic orderings/liquids, which are tunable by external stimuli, is a remarkable feature of correlated electron systems, but has rarely been realized in the topological semimetals with high-mobility relativistic electrons. Here, we report that the correlated Dirac electrons in perovskite CaIrO3 show unconventional field-induced successive metal–insulator–metal crossovers in the quantum limit accompanying a giant magnetoresistance (MR) with MR ratio of 3500 % (18 T and 1.4 K). In conjunction with the numerical calculation, we propose that the insulating state originates from the collective electronic ordering such as charge/spin density wave promoted by electron correlation, whereas it turns into the quasi-one-dimensional metal at higher fields due to the field-induced reduction of chemical potential, highlighting the highly field-tunable character of correlated Dirac electrons.
Similar content being viewed by others
Introduction
The quantum phenomena of relativistic electron (Dirac/Weyl electron) in solids have been a subject of great interest in modern materials physics. Topological semimetals offer a fertile field of materials to study various quantum transport phenomena of high-mobility relativistic electrons, presenting the chiral anomaly or various topological phases1. Most of them have been understood in the scheme of single particle physics so far, but there is growing interest in the strong electron correlation as one of the promising routes to realize the emergent collective topological phenomena2,3,4,5,6. According to conventional wisdom, the Landau–Fermi liquid picture tends to collapse in the low-dimensional correlated materials, resulting in or from various charge/spin correlations. Indeed, various kinds of exotic electronic liquids or charge/spin ordering have been identified in conventional quasi-two/one dimensional correlated systems7,8. In this context, the spatial confinement of high-mobility relativistic electron under the strong electron correlation may be a promising pathway to find emergent collective topological phenomena.
In the case of bulk topological semimetals, the quasi-one-dimensional (1D) confinement of relativistic electrons is typically realized in the quantum limit (QL) under a sufficiently strong magnetic field B. Electrons in the lowest Landau level with the index n = 0 are confined in a scale of magnetic length \(l_{{{\mathrm{B}}}} = \sqrt {\hbar /eB}\) within a plane perpendicular to the magnetic field, whereas the momentum along the magnetic field is preserved. Previous theoretical studies proposed that nontrivial phases such as the axion charge density wave (CDW) and excitonic insulator are induced, if the QL of the Dirac/Weyl electron can be realized in materials with the strong electron correlation9,10,11. However, the experimental realization of quantum limit in the strongly correlated electron material is a challenge and hence it has rarely been explored so far.
In this context, the correlated Dirac semimetal of perovskite CaIrO3 provides an ideal arena to study the collective phenomena of high-mobility relativistic electrons in the QL. In CaIrO3, due to the strong spin–orbit coupling and electron correlation, the nominally half-filled jeff = 1/2 band, which lies near the Fermi energy (EF), constitutes the nearly compensated semimetal state with a few electron- and hole-pockets. It has been proposed that the electron pocket emerging around U-point in the Brillouin zone is caused by the Dirac band dispersion with a closed line-node protected by the nonsymmorphic crystalline symmetry (Pbnm) as illustrated in the inset to Fig. 1a12,13,14. Recently, it has been shown that the line node is precisely tuned close to EF (~10 meV below EF) and yields the Dirac electrons with dilute carrier density (less than 2 × 1017 cm−3), and high mobility exceeding 60,000 cm2 V−1 s−1 due to strong electron correlation in the proximity to the Mott criticality15,16,17,18. In particular, due to the small size of nodal loop, the Fermi surface is expected to be of anisotropic elliptical or butterfly-type shape15 rather than of the torus shape in the conventional nodal line semimetal. Specifically, the Fermi velocity is renormalized to a moderately small value (vF ~ 8 × 104 m s−1) compared to other topological materials19,20,21,22. Consequently, the correlated Dirac electrons reach the QL at a modest magnetic field less than 10 T. However, the transport property in the QL of this material has not been explored so far, and a possibly striking feature of collective phenomena of the Dirac electrons remains elusive. Here, by magneto-transport measurements and theoretical modeling, we show that the two successive metal-insulator crossovers accompanying a giant magnetoresistance are induced by moderate magnetic field (10–30 T) in the QL region of CaIrO3. The field dependence of activation energy, which agrees with the model of density wave state in the quantum limit, suggests that one is a crossover from semimetallic state to the charge/spin density wave and that the other is a reentrance to the quasi-1D metallic state of correlated Dirac electrons.
Results and discussion
Magneto-transport properties
As shown in Fig. 1a, the resistivity along the a-axis, ρzz, shows a metallic behavior above 150 K, but a peak is observed around 20 K; here we take the Cartesian coordinate with respect to the orthorhombic axes as x||b, y||c and z||a throughout this paper. The peak is attributed to the competition between the reduction of thermally excited carriers and enhancement of carrier mobility15. Figure 1b shows the low field region of longitudinal magnetoresistivity measured with the electric current and magnetic field parallel to the a-axis (B||I||a, z||a). With increasing magnetic field, ρzz initially increases up to 2 T, and then moderately decreases up to 10 T accompanying the Shubnikov-de Haas (SdH) oscillations due to the electron pocket around the line node15. The frequency of the SdH oscillations is 10.5 T [see Supplementary Fig. 1]. Due to the small Fermi surface, the Dirac electron reaches QL at the modest field of BQL = 6 T, which is defined as the field of SdH oscillation peak due to the Landau index n = 1 [see Supplementary Fig. 1].
The magnetoresitivity ρzz (B||I||a) up to 55 T is shown in Fig. 1c. At 1.4 K, ρzz steeply increases above the threshold magnetic field (Bth) of 10 T, and is nearly saturated around 18 T with the MR-ratio \(\left[ {\rho _{zz}(B) - \rho _{zz}\left( 0 \right)} \right]/\rho _{zz}\left( 0 \right)\) of 35. Above 18 T, the magnetoresistivity monotonically decreases up to 55 T. With increasing temperature, the peak in ρzz around 18 T is gradually smeared out, while shifting toward higher magnetic field. On the contrary, the magnetoresistivity in transverse configuration ρxx (B||a, I||b) monotonically increases, and at low temperature, a small kink emerges at Bth [see Fig. 1c]. Here, we used two different samples for the longitudinal and transverse configurations but they have almost the same carrier density [see Supplementary Note 2].
To quantify the anisotropy of transport properties in the QL, we compare the magnetoconductivity in the longitudinal configuration (B||I||a, σzz) and that in transverse configuration (B||a, I||b, σxx) in Fig. 2a. Here, σzz is defined as the inverse of ρzz in the longitudinal configuration (B||I) and σxx as \(\rho _{xx}/( {\rho _{xx}^2 + \rho _{yx}^2} )\) with ρxx and ρyx being the resistivity measured in transverse configuration (\({{{\mathbf{B}}}} \bot {{{\mathbf{I}}}}\); B||a and I||b(x)) and the Hall resistivity [see Supplementary Fig. 3], respectively. With increasing the magnetic field, σzz initially increases, steeply drop around Bth, and shows an upturn at 18 T. In particular, σzz at 55 T is enhanced to about ten times compared to that at 18 T. On the contrary, σxx monotonically decreases with increasing magnetic field with a small drop at Bth. Around BQL, σzz is about ten times as large as σxx in agreement with the quasi-one-dimensional confinement of electrons along B||z. On the other hand, σzz falls down to a value comparable to or even less than σxx around 18 T, but becomes larger than σxx again in high magnetic field above 30 T. Since σxx shows no clear anomaly around 18 T, the enhancement of conductivity at high field is likely attributed to the change in the electronic state on the n = 0 LL rather than the decay of the LL itself.
Figure 2b shows the temperature dependence of σzz below 15 K. With decreasing temperatures, σzz monotonically increases at 0 T, but monotonically decreases at 18 T, implying that the ground state changes from a metal to an insulator or a charge-gapped state. On the other hand, the metallic behavior is recovered at 55 T, while σzz shows a modest temperature dependence. To quantify the insulating behavior at 18 T, we fitted σzz by the Arrhenius model \(\sigma _{zz} = \sigma _0 + \sigma _1\exp \left( { - {\Delta}_{\exp }/2k_BT} \right)\) and derived the activation energy Δexp with σ0 and σ1 being the temperature independent parameters; here σ0 (= 0.17σ1) represents the small residual conductivity likely coming from another hole pocket [see Supplementary Note 2]. The temperature dependence of σzz below 6 K is well described by the Arrhenius model [see Fig. 2c] and Δexp is deduced to be 1.2 meV at 18 T. We conducted the similar analyses at various magnetic fields and plotted Δexp as a function of magnetic field in Fig. 2d. The result shows a peak around 18 T in agreement with the behavior of MR at 1.4 K [see Fig. 1c]. This suggests that the large peak structure in MR (dip structure of σzz) originates from the field variation of Δexp.
Numerical calculation of Landau levels
To get insights into the electronic states under the magnetic field, we numerically calculate the field dependence of the Landau levels (LLs). We construct a tight binding model for the electronic structure around the line node, which takes into account the Zeeman term (g-factor of 2)23. Figure 3a shows the energy dispersion of band structure around the U-point at 0 T along the kz-direction. The Fermi energy is set to be 5.0 meV above the band crossing point, i.e., the line node15. Under the magnetic field, the energy band splits into the LLs, and in the QL (B > BQL = 6 T), only the n = 0 LLs cross the Fermi energy, which are degenerate at kz = 0 and split into two doubly degenerate states at kz ≠ 0 mainly due to Zeeman term [see Fig. 3b–d]. Since the splitting of n = 0 LLs is small, the effect of Zeeman term is not likely significant. Figure 3e displays the density of states (DOS) at various magnetic fields. At a small magnetic field (0.1 T), the DOS around EF is small as is expected from the small size of the line node15. At 10 T, the DOS in the low energy region (−6 meV ≤ E ≤ 6 meV), which is governed by the n = 0 LL, is flat and several peaks due to the n ≠ 0 LLs are discernible above 6 meV as well as below −6 meV [see Fig. 3b]. At 50 T, the DOS in the region −10 meV ≤ E ≤ 10 meV is governed by n = 0 LL and becomes fairly large due to the increased LL degeneracy. As shown in Fig. 3f, the DOS at EF linearly increases as a function of magnetic field. We note that the charge transfer between these LLs and hole pockets nearby the Γ-point is negligible and hence the carrier density in the LLs is likely conserved at least below 55 T [Supplementary Note 2]. This suggests that the energy difference (ΔEF) between the Fermi energy and the band crossing point, as well as the Fermi wave number kF, decreases as a function of magnetic field [see Fig. 3g].
Origin of the non-monotonic field dependence of MR
The calculated results suggest that the electronic state of n = 0 LL is described by the four Weyl bands, which subsist even at sufficiently high magnetic field. This is consistent with the experimental result that the resistivity deep in the QL region at 55 T shows a metallic behavior. In more detail, the conductivity at 55 T shows the power-law type temperature dependence \(\left( {\sigma _{zz} \propto T^\alpha ,\alpha \sim 0.24} \right)\) in accord with the picture of the Tomonaga-Luttinger liquid [see Supplementary Fig. 6]24. On the contrary, the insulating behavior with the finite gap around 18 T is far from clear in terms of the numerical calculation.
One possible scenario is the magnetic freeze-out, i.e., electron localization by disorders promoted by the quasi-1D confinement. Indeed, the magnetic freeze-out often occurs in the QL of semiconductors such as Hg1−xCdxTe and InSb25,26, which manifests itself as the non-saturating positive MR. In general, the strength of localization is determined by the ratio of impurity potential to the kinetic energy of electron or equivalently the Fermi energy. Under the magnetic field, the Fermi energy monotonically decreases due to the Landau level degeneracy, resulting in the enhancement of localization under the magnetic field. To explain the reentrant metallic behavior at higher field, therefore, the additional mechanism to suppress the magnetic freeze-out would be necessary. However, as previously mentioned, the effect of Zeeman splitting or intervalley charge transfer may not be remarkable and thus there is no clear mechanism to suppress the magnetic freeze-out in the present material. Here, we speculate that the density of charged impurities, possibly arising from the deficiency of Ir, is on the order of the Dirac electron density (2 × 1017 cm−3) or smaller, judging from the high mobility at low temperatures15, [see also Supplementary Note 3]. Furthermore, the qualitatively different behavior for ρzz and ρxx cannot be simply explained by the scenario of magnetic freeze-out [see Fig. 1c].
A more plausible scenario would be the field-induced collective electronic ordering promoted by the quasi-one-dimensional confinement and field-enhancement of the density of states. It is known that the Fermi surface of quasi-1D metal is unstable towards a charge-gapped state such as the CDW, spin density wave (SDW) or excitonic insulator27,28,29,30,31,32,33. Although there are several possible candidates of electronic orderings for the quasi-1D state composed of the n = 0 LL, we focus here on the fieldinduced CDW. By taking into account the long-range Coulomb interaction within the Hartree–Fock approximation, Fukuyama27 showed theoretically that the electron gas in the QL turns into the charge density wave at low temperatures, as later experimentally observed for graphite28,29,30,31. We calculated the magnetic field dependence of Tc following Fukuyama’s theory27 and estimated the charge gap Δcal (=3.5kBTc) [Supplementary Note 6]. In Fig. 2d, we show the field dependence of Δcal [see also Supplementary Fig. 10]. Δcal shows a peak around 18 T which is consistent with the experimental results within the difference of factor of 3. In more detail, the non-monotonic field dependence of Δcal can be understood from the balance between the field variation of the LL degeneracy and EF; the transition temperature, or equivalently the order parameter, initially increases due to the enhancement of the LL degeneracy, but is counterbalanced by the decrease of EF at the higher magnetic field. In this context, the non-monotonic field dependence of magnetoresistivity and Δexp can be explained by the field induced CDW formation and its subsequent suppression by higher magnetic fields. We note that the theory considering electron–phonon interaction also gives a qualitatively similar result32, [Supplementary Note 6].
Nonlinear transport measurements
It is instructive to compare these results with the case of graphite28,29, which is a canonical system showing the field induced insulating state in the QL. In graphite, the insulating state due to 2kF instability is observed as a phase transition accompanying a clear jump of magnetoresistivity at a certain threshold field, which is enhanced at higher temperatures. Moreover, the insulating state returns into a metallic state in the higher magnetic field31. There is a similarity between the both cases, graphite and CaIrO3, in terms of overall behavior of meatal-insulator-metal transition (crossover), but the sharpness of the transition is obviously different. To characterize the possible CDW state in CaIrO3, we investigated the current–voltage (I–V) characteristics in the QL. It has been known that the long-range ordered CDW slides over the underlying lattice with a current excitation larger than a certain threshold value, which manifests itself as the non-Ohmic I–V characteristics34. On the contrary, the disordered or short-range ordered CDW does not show a clear onset of sliding motion. As shown in the inset to Fig. 4a, even at the sufficiently large current of 100 μA, which corresponds to the electric field about 45 mV cm−1, the I–V property measured at 2 K and 14 T does not show any clear threshold or jump characteristic of the sliding motion of long-range ordered CDW35,36. Alternatively, we found that the I–V property already includes the non-Ohmic component even in the weak current region by measurements of third-harmonic voltage response Vzz3ω [see the inset to Fig. 4a, Supplementary Note 5]. In Fig. 4a, we show the third-harmonic resistivity Rzz3ω, which is defined as −Vzz3ω/I, as well as that normalized by the linear component of resistivity (Rzz3ω/Rzz 1ω). Both Rzz3ω and Rzz3ω/Rzz1ω steeply increases above Bth, suggesting that the non-Ohmic behavior is inherent to the QL state. Specifically, the Rzz3ω/Rzz1ω reaches 6 × 10−4 at 14 T. Such a higher harmonic of resistance is often observed in disordered metal or correlated electron systems and typically originates from the spatially inhomogeneous electronic state37,38,39. In this context, the non-Ohmic I–V property without clear threshold field suggests that the CDW state in the present system is not spatially homogeneous, or equivalently, is not of long-range nature. From the value of 2kF, the period of the CDW is estimated to be about 50 nm at 18 T, and hence the long-ranged CDW formation would require the extremely clean sample, which may not be obtained in the present study.
Comparison with conventional semimetals
On the basis of these results, we constructed the electronic phase diagram as shown in Fig. 4b. In the low-field regime below Bth, the metallic state extends over a wide temperature range. In the intermediate field regime above Bth, the insulating state as characterized by the disordered CDW emerges at low temperatures, but gradually turns into the quasi-1D metallic state perhaps with the nature of Tomonaga-Luttinger liquid in a higher field regime. Although we focus on the CDW model here, the possibility of other electronic orderings, such as SDW or interband CDW cannot be excluded due to the multi-band structure of n = 0 LLs and the strong electron correlation. However, we anticipate that the CDW picture gives a good starting point to capture the field induced insulating state in the present system. Moreover, we note here that the threshold magnetic field of the insulating state (Bth) is as small as 10 T. Except the case of ZrTe5 with exceptionally small BQL (~2 T)40, Bth is much smaller than the value of other semimetals, such as graphite (Bth = 25 T)28,29,30 and TaAs (Bth = 80 T)41, regardless of similar value of the BQL [see Table 1]. The theoretical model of CDW as presented above also demonstrates that Bth decreases as vF decreases through the enhancement of density of state, when vF is in the range of 104–106 m s−1 [see Supplementary Fig. 11 and Supplementary Note 6]. In this context, the moderate renormalization of vF due to the strong electron correlation15 may be one of the key ingredients for the small value of Bth in CaIrO3.
In this study, we have investigated the QL transport of correlated Dirac electrons in the perovskite CaIrO3 by means of magneto-transport measurements and theoretical calculations. In the QL, the magnetoresistivity steeply increases around 10 T (= Bth) and the insulating state with a finite energy gap emerges around 18 T. By further increasing the magnetic field, both the gap and resistivity dramatically decrease, resulting in the quasi-1D metallic state in the deep QL regime. The non-monotonic field dependence of the gap suggests that the field induced insulating state originates from the collective electronic ordering, likely the charge density wave or spin density wave driven by the Fermi surface instability inherent to the quasi-one-dimensional n = 0 Landau levels with the enhanced density of states under the magnetic field. Furthermore, the weak non-linear transport observed in the QL above 10 T suggests that the density wave state is not of long-range nature but spatially inhomogeneous. The field-induced crossover between the metallic state and the gapped state occurs in the fairly low magnetic field regime (10–30 T) among the conventional semimetals, highlighting the highly field-sensitive character of strongly correlated Dirac electrons relevant to the Mott criticality.
Methods
Sample preparation and characterization
Single crystalline samples of perovskite CaIrO3 were synthesized under high pressures using the cubic-anvil type facility. The samples were treated at pressure of 1 GPa and temperature of 1200 °C. The materials were kept under this condition for 10 min and then quenched to room temperature. The typical size of the sample is about 0.5 × 0.3 × 0.3 mm3. We have determined the crystal orientation by an in-house X-ray diffractometer. The crystal structure is identified as the orthorhombic (GdFeO3-type) perovskite with the space group of Pbnm.
Transport measurement under pulsed high magnetic field
The resistivity (ρzz) in longitudinal configuration and the resistivity (ρxx) and Hall resistivity (ρyx) in transverse configuration were measured by a four- or five-probe method with indium electrode. Epo-tek H20S silver epoxy and 50-μm-diameter gold wires were used to form electrical contacts. The magnetic field was applied along the a-axis and the current was applied along the a-axis and b-axis of the crystal for a longitudinal and transverse configuration, respectively. The magnetotransport measurements up to 55 T in a temperature range from 1.4 to 40 K were done under pulsed high magnetic fields using nondestructive magnets installed at The Institute for Solid State Physics, The University of Tokyo. The magnetic fields up to 55 T (pulse durations of 36 ms) were generated using bipolar pulse magnets, which can generate both positive and negative fields. We used numerical lock-in technique at a frequency of 100 kHz. The resistivity and Hall resistivity are symmetrized and antisymmetrized with respect to the magnetic field, respectively.
Nonlinear transport measurement
Measurements of the third-harmonic voltage response have been performed by standard four-terminal geometry in the longitudinal configuration (B||I||a). An ac current \(I = I_0\sin \omega t\) is applied to the sample and the linear (V1ω) and nonlinear response (V3ω) in the total voltage signal \(V = V^{1\omega }\sin \omega t + V^{3\omega }\sin 3\omega t + \cdots\) are detected simultaneously by two digital lock-in amplifiers. The magnetic fields up to 14 T is applied and the sample was cooled down to the temperature of 2 K using the Physical Property Measurement System (Quantum Design). The measurements were done in a frequency range from 3 to 4000 kHz.
Numerical calculation on Landau levels of line node
We constructed a low-energy effective model of the band structure around the U point, where the line node resides, based on the previous works13,23 on SrIrO3, which has the same crystal symmetry as the perovskite CaIrO3 [see Supplementary Note 7 for detail]. Using the Landau quantization for B||a, we derived coupled secular equations similar to those derived in ref. 23. for B||c. We then numerically solved these equations, to obtain the LLs. The DOS is calculated by integrating the weight (∝B) of the LLs over −0.48/a < kz < 0.48/a around the U point.
Data availability
All data needed to evaluate the conclusions in the paper are present in the paper and/or the supplementary materials. Additional data requests should be addressed to the corresponding authors.
References
Armitage, N. P., Mele, E. J. & Vishwanath, A. Weyl and Dirac semimetals in three-dimensional solids. Rev. Mod. Phys. 90, 015001 (2018).
Wei, H., Chao, S.-P. & Aji, V. Excitonic phases from Weyl semimetals. Phys. Rev. Lett. 109, 196403 (2012).
Moon, E.-G., Xu, C., Kim, Y. B. & Balents, L. Non-Fermi-liquid and topological states with strong spin-orbit coupling. Phys. Rev. Lett. 111, 206401 (2013).
Wang, Z. & Zhang, S.-C. Chiral anomaly, charge density waves, and axion strings from Weyl semimetals. Phys. Rev. B 87, 161107(R) (2013).
Sekine, A. & Nomura, K. Axionic antiferromagnetic insulator phase in a correlated and spin-orbit coupled system. J. Phys. Soc. Jpn. 83, 104709 (2014).
Gooth, J. et al. Axionic charge-density wave in the Weyl semimetal (TaSe4)2I. Nature 575, 315–319 (2019).
Keimer, B., Kivelson, S. A., Norman, M. R., Uchida, S. & Zaanen, J. From quantum matter to high-temperature superconductivity in copper oxides. Nature 518, 179–186 (2015).
Fernandes, R. M., Chubukov, A. V. & Schmalian, J. What drives nematic order in iron-based superconductors? Nat. Phys. 10, 97–104 (2014).
Roy, B. & Sau, J. D. Magnetic catalysis and axionic charge density wave in Weyl semimetals. Phys. Rev. B 92, 125141 (2015).
Li, X., Roy, B. & Sarma, S. D. Weyl fermions with arbitrary monopoles in magnetic fields: Landau levels, longitudinal magnetotransport, and density-wave ordering. Phys. Rev. B 94, 195144 (2016).
Pan, Z. & Shindou, R. Ground-state atlas of a three-dimensional semimetal in the quantum limit. Phys. Rev. B 100, 165124 (2019).
Zeb, M. A. & Kee, H.-Y. Interplay between spin-orbit coupling and Hubbard interaction in SrIrO3 and related Pbnm perovskite oxides. Phys. Rev. B 86, 085149 (2012).
Chen, Y., Kim, H. S. & Kee, H.-Y. Topological crystalline semimetals in nonsymmorphic lattices. Phys. Rev. B 93, 155140 (2016).
Chen, Y., Lu, Y.-M. & Kee, H.-Y. Topological crystalline metal in orthorhombic perovskite iridates. Nat. Commun. 6, 6593 (2015).
Fujioka, J. et al. Strong-correlation induced high-mobility electrons in Dirac semimetal of perovskite oxide. Nat. Commun. 10, 362 (2019).
Masuko, M., Fujioka, J., Nakamura, M., Kawasaki, M. & Tokura, Y. Strain-engineering of charge transport in the correlated Dirac semimetal of perovskite CaIrO3 thin films. APL Mater. 7, 081115 (2019).
Yamada, R. et al. Large variation of Dirac semimetal state in perovskite CaIrO3 with pressure-tuning of electron correlation. Phys. Rev. Lett. 123, 216601 (2019).
Fujioka, J., Yamada, R., Okawa, T. & Tokura, Y. Dirac polaron dynamics in the correlated semimetal of perovskite CaIrO3. Phys. Rev. B 103, L041109 (2021).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Zhang, Y., Tan, Y.-W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Qu, D.-X., Hor, Y. S., Xiong, J., Cava, R. J. & Ong, N. P. Quantum oscillations and Hall anomaly of surface states in the topological insulator Bi2Te3. Science 329, 821–824 (2010).
Liang, T. et al. Ultrahigh mobility and giant magnetoresistance in the Dirac semimetal Cd3As2. Nat. Mater. 14, 280–284 (2015).
Rhim, J.-W. & Kim, Y. B. Landau level quantization and almost flat modes in three-dimensional semimetals with nodal ring spectra. Phys. Rev. B 92, 045126 (2015).
Zhang, X.-X. & Nagaosa, N. Tomonaga-Luttinger liquid and localization in Weyl semimetals. Phys. Rev. B 95, 205143 (2017).
Robert, J. L., Raymond, A., Aulombard, R. L. & Bousquet, C. Magnetic freeze-out in doped semiconductors the metal non-metal transition in n-type InSb. Philos. Mag. B 42, 1003–1025 (1980).
Shayegan, M., Goldman, V. J. & Drew, H. D. Magnetic-field-induced localization in narrow-gap semiconductors Hg1-xCdxTe and InSb. Phys. Rev. B 38, 5585–5602 (1988).
Fukuyama, H. CDW instability of electron gas in a strong magnetic field. Solid State Commun. 26, 783–786 (1978).
Iye, Y. et al. High-magnetic-field electronic phase transition in graphite observed by magnetoresistance anomaly. Phys. Rev. B 25, 5478–5485 (1982).
Iye, Y., Beglund, P. M. & McNeil, L. E. The magnetic field dependence of the critical temperature for the electronic phase transition in graphite in the quantum limit. Solid State Commun. 52, 975–980 (1984).
Yaguchi, H., Takamasu, T., Iye, Y. & Miura, N. Non-ohmic out-of-plane transport in a high-magnetic-field-induced phase of graphite. J. Phys. Soc. Jpn. 68, 181–184 (1999).
Yaguchi, H. & Singleton, J. Destruction of the field-induced density-wave state in graphite by large magnetic fields. Phys. Rev. Lett. 81, 5193–5196 (1998).
Heinonen, O. & Radi, A. A.-J. Electron-phonon interactions and charge-density-wave formations in strong magnetic fields. Phys. Rev. B 33, 5461–5464 (1986).
Fenton, E. W. Excitonic insulator in a magnetic field. Phys. Rev. 170, 816–821 (1968).
Grüner, G. The dynamics of charge-density waves. Rev. Mod. Phys. 60, 1129 (1988).
Fleming, R. M. & Grimes, C. C. Sliding-mode conductivity in NbSe3: Observation of a threshold electric field and conduction noise. Phys. Rev. Lett. 42, 1423–1426 (1979).
Iye, Y. & Dresselhaus, G. Non-ohmic transport in the magnetic-field-induced charge-density-wave phase of graphite. Phys. Rev. Lett. 54, 1182–1184 (1985).
Dubson, M. A., Hui, Y. C., Weissman, M. B. & Garland, J. C. Measurement of the fourth moment of the current distribution in two-dimensional random resistor networks. Phys. Rev. B 39, 6807–6815 (1989).
Rommel, R., Hartmann, B., Brandenburg, J., Schlueter, J. A. & Müller, J. Nonlinear electronic transport in the anomalous metallic state of quasi-2D organic superconductors κ-(BEDT-TTF)2X. Phys. Status Solidi B 250, 568–574 (2013).
Moshnyaga, V. et al. Electrical nonlinearity in colossal magnetoresistance manganite films: relevance of correlated polarons. Phys. Rev. B 79, 134413 (2009).
Tang, F. et al. Three-dimensional quantum Hall effect and metal–insulator transition in ZrTe5. Nature 569, 537–541 (2019).
Ramshaw, B. J. et al. Quantum limit transport and destruction of the Weyl nodes in TaAs. Nat. Commun. 9, 2217 (2018).
Acknowledgements
Authors thank A. Tsukazaki, M. Kawasaki, N. Nagaosa, A Yamamoto, Y. Kaneko, S. Ishiwata, Y. Fuseya, Y. Awashima, M. Masuko, and R. Kaneko for fruitful discussion. This work was supported by a Japan Society for the Promotion of Science KAKENHI (Grants No. 20J21312, 16H00981, 18H01171, 18H04214, and 16H06345) from the MEXT and by PRESTO (Grant No. JPMJPR15R5) and CREST (Grants No. JPMJCR16F1), Japan Science and Technology Japan.
Author information
Authors and Affiliations
Contributions
R.Y., J.F., and Y.T. conceived the project. R.Y., J.F., and T.O. grew the single crystalline CaIrO3 and performed the characterization with the help of D.H.; R.Y., J.F., M.K., T.S., F.K., R.K., and M.T. conducted the transport measurement and analyzed the data. S.S., M.H., and R.A. performed the theoretical calculation. R.Y., J.F., and Y.T. wrote the manuscript with contributions from all authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yamada, R., Fujioka, J., Kawamura, M. et al. Field-induced multiple metal-insulator crossovers of correlated Dirac electrons of perovskite CaIrO3. npj Quantum Mater. 7, 13 (2022). https://doi.org/10.1038/s41535-021-00418-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41535-021-00418-2
This article is cited by
-
Peculiar magnetotransport properties in epitaxially stabilized orthorhombic Ru3+ perovskite LaRuO3 and NdRuO3
Communications Materials (2024)