Abstract
Chalcogenide phase change materials (PCMs) have been extensively applied in data storage, and they are now being proposed for high resolution displays, holographic displays, reprogrammable photonics, and all-optical neural networks. These wide-ranging applications all exploit the radical property contrast between the PCMs’ different structural phases, extremely fast switching speed, long-term stability, and low energy consumption. Designing PCM photonic devices requires an accurate model to predict the response of the device during phase transitions. Here, we describe an approach that accurately predicts the microstructure and optical response of phase change materials during laser induced heating. The framework couples the Gillespie Cellular Automata approach for modelling phase transitions with effective medium theory and Fresnel equations. The accuracy of the approach is verified by comparing the PCM’s optical response and microstructure evolution with the results of nanosecond laser switching experiments. We anticipate that this approach to simulating the switching response of PCMs will become an important component for designing and simulating programmable photonics devices. The method is particularly important for predicting the multi-level optical response of PCMs, which is important for all-optical neural networks and PCM-programmable perceptrons.
Similar content being viewed by others
Introduction
Chalcogenide phase change materials (PCMs) exhibit extraordinarily large changes to their optical and electrical properties when switched between their local different bonding states1,2,3. The switching is reversible and can be cycled trillions of times4. This makes PCMs attractive not just for their existing application in electrical storage5, but also for potential applications in photonics6,7,8,9, micro-electromechanical systems10, and tunable radio frequency devices11.
Chalcogenide PCMs are particularly attractive for reprogrammable photonics because they exhibit a large optical refractive index change between amorphous and crystalline phases. For example, the real component of the refractive index of Ge2Sb2Te5, which is the most famous PCMs, changes from ~4 to ~6 in the mid-infrared12, making it useful for programming mid-infrared plasmonic metamaterials13. Chalcogenide PCMs tend to have a larger refractive index in both crystalline and amorphous phases than many other tunable photonics materials, and this makes them naturally suitable for designing all-dielectric metasurface-based devices14. Another appealing characteristic of chalcogenide PCMs is that the phase transition is extremely quick; indeed amorphisation takes just 5 ps15 and crystallisation is possible in 700 ps16. Moreover, chalcogenide PCMs do not require a constant energy to hold their optical state once switched. This non-volatility makes them more energy efficient than the metal oxide PCMs, such as VO2, which require a constant energy supply to hold their optical state. Importantly, the real part of the dielectric function of many telluride-based compositions is negative in the visible spectrum, which means that the crystalline material can behave like a plasmonic metal and could further enable innovative switchable plasmonic devices17. More recently, the multiple optical states of chalcogenide PCMs are being studied, developed, and applied in multi-level optical switches18,19,20, a prerequisite for setting the weights in all-optical neural networks21,22,23.
The biggest drawback of telluride-based PCMs is their high optical absorption at visible and near-infrared frequencies12. However, in the past few years, PCMs with a wider bandgap, such as Sb2S324 and Ge2Sb2Se4Te125, have been developed to specifically programme the response of visible and near-infrared photonics devices. Prototype optical switches26,27, displays28 and metasurfaces29 have demonstrated their potential.
Designing programmable photonic devices requires an accurate model to describe the PCM switching behaviour. However, the optical properties of all materials depend on their respective crystal structures, and in the case of PCMs the crystal structure switches and transitions depending on the heating and quenching conditions. Even the crystallographic microstructure impacts optical scattering, and this may explain the large variation in measured optical constants of Ge2Sb2Te512,30,31. This variability issue is further confounded by most of the amorphous optical properties in literatures actually being for the as-deposited amorphous state, rather than the more technologically relevant melt-quenched amorphous state. To understand the evolution of a PCM photonics device optical response during switching, and the conditions that can lead to multi-level optical devices18,19, it is important to know not only the initial and final states, but also how the optical constants evolve during nucleation, crystal growth, and melt-quenching. Therefore, a model that accurately predicts the optical properties during and after phase transition will be a key enabler of successful photonic device designs, and in particular phase change multi-level devices.
Approaches to modelling the optical change of PCMs during crystallisation and amorphisation range from simple but unrealistic descriptions of the refractive index switching at a specific temperature to ab initio descriptions of the electronic band structure dependence on the local atomic coordination2 and computationally expensive density functional theory methods. However, semi-empirical methods that exploit molecular-level crystal nucleation, growth, and annihilation rates give a good compromise between accuracy, scaling, and performance. Recently, Meyer et al developed a multiphysics model that specifically describes the optical property change in a phase change metasurface perfect absorber using a phase field approach but no comparison with experiments was conducted to verify the multiphysics model32. Similarly, a phase field method was used to describe the experimental measurements observed for recrystallisation of melt quenched AgInSbTe33. But this particular model only considered crystal growth and the nucleation effects were considered negligible since AgInSbTe is a growth dominated material. Therefore, a multiphysics model capable of accurately describing experimental results during nucleation, growth, and amorphization of phase change materials needs to be developed.
Multiphysics models of Ge2Sb2Te5 and other PCMs must accurately predict crystallisation behaviour across a time span ranging by 15 orders of magnitude because photonic memories must be stable at room temperature for years yet crystallise in nanoseconds at slightly elevated temperatures. This dichotomy is possible because the PCM viscosity depends non-linearly on temperature34,35,36,37. However, typical models that simulate the laser and electric heating pulses do not consider this non-linearity and thus they can only be used over narrow range of temperatures and heating rates.
The Gillespie Cellular Automata (GCA)-based phase-change model was developed by Ashwin to describe isothermal crystallisation of PCM alloys and phase transitions in electrical devices38. In the GCA model, each unit cell is considered as a PCM molecule with physically meaningful characteristics, and they can be directly related to microscopic density functional theory models. Therefore, the GCA approach was suggested as a bridge between hundred-atom-order density functional theory models and device-level performance models38. The GCA approach has been used to model electrical phase change memory devices and to study the PCM crystallisation process39,40. Although the electrical switching performance predicted from these models is in reasonable agreement with device measurements, the predicted crystallographic microstructure has not been verified by experiments. For photonics applications and especially multi-level photonics19,20, it is important to know the influence of the crystal domain size and density on the PCM optical properties. Until now, however, a complete GCA-thermo-optical model that can be used to design photonics devices remains unreported.
The aim of this work is to develop an accurate framework for simulating PCM photonics devices. To quantify the accuracy, we must be able to simulate and measure the PCM microstructures and optical response of photonics devices. For this reason, we will apply the framework to a programmable thin-film optical stack. In what follows, we describe how combining nanosecond non-isothermal laser heating, non-linear and probabilistic GCA, effective medium theory and the Fresnel Equations can be used to accurately model the switching process of PCMs and the transient optical response of the programmable optical stack during nanosecond pulsed laser irradiation. Laser switching experiments and transmission electron microscopy (TEM) were performed to show that the model is highly accurate and can predict the final optical state, the crystallographic microstructure evolution, the transient optical response, and multilevel optical reflectivity and transmissivity which corresponds to partial crystallisation of the PCM film. Thus, this model is important because it can be used to optimise the PCM films, device structures, and laser pulse parameters to achieve multi-level switching. We foresee the model being widely applied to optimising the interconnection weights in all-optical neural network schemes41, controllable metamaterial phase arrays42,43, and displays28,44. Moreover, the thermodynamic parameters used in the code can be edited to study the influence of doping on the performance of different programmable photonic devices45. For this reason, the code is publicly available at the GitHub website46, and we encourage others to use it.
Results
Multiphysics modelling
The active structures in many PCM photonics devices consist of a PCM multilayer stack. Therefore, here we simulate the time-dependent optical response of such a stack during nanosecond laser heating. Note, however, the model can be easily adapted to other more complicated devices, such as waveguides and memories. The multi-physics scheme that we developed is shown in Fig. 1. The optical response and microstructure of the stack used in experiments, can be easily measured, which makes this particular device ideal for validating the accuracy of the multi-physics model. The model starts by calculating the heat distribution due to laser heating. The temperature as a function of space and time was obtained by solving the heat conduction equation with an explicit finite difference method. Non-uniform meshing and time-step alternation strategies were adopted to increase the calculation efficiency. The phase-transition of the PCM molecules was simulated using a modified GCA model. In contrast to ref. 38, here, the probabilities of nucleation, growth and dissociation are directly deduced from the classical nucleation and growth theory, and these probabilities are combined with a piecewise viscosity model to simulate phase transitions. This step is important for handling the highly non-linear crystallisation rates which allow PCMs to crystallise from nanoseconds to years by only moderately changing the temperature. Due to the differences in dimensionality for the heat conduction and GCA grids, the 3D temperature distribution was re-sampled onto the 2D GCA grid, i.e., the calculation is assumed to occur in the top surface of the PCM film. This is acceptable because generally the thickness of PCM films in photonics devices is thinner than the PCM crystal grain size47.
The proposed multi-physics GCA model can predict the transient optical response, crystallographic microstructures and multilevel response of an arbitrary PCM device by circularly calculating the temperature distribution through solving the heat transfer equation, the phase of each PCM cell via a modified GCA model, the effective optical constants by the effective medium theory and the real-time reflectivity, transmission and absorption using the Fresnel equations.
PCMs can exist in an intermediate phase, which simultaneously consists of crystalline and amorphous domains. Therefore, the crystallised fraction was computed as the ratio of crystalline molecules to the total number of molecules within the full width of half maximum (FWHM) of the Gaussian laser beam. The effective permittivity and optical constants of the crystalline grains within the amorphous matrix were calculated using the Lorentz-Lorenz relation and effective medium theory. The reflectivity and transmissivity of the device was updated by taking advantage of characteristic matrix method and Fresnel equations. The new absorption and reflection coefficients were further used to calculate the laser-induced heat distribution as the model iterates. Then, the multilevel responses of the PCM reprogrammable photonics device can be predicted. Further modelling details are described in the Methods section.
Simulation
The multi-physics GCA model was applied to analyse the entire crystallisation process of a Ge2Sb2Te5 sample under laser irradiation. The programmable thin film optical stack is shown in Fig. 2a. It consists of a 30 nm thick Ge2Sb2Te5 film on top of a 50 nm thick silicon nitride (Si3N4) membrane. Again, this particular structure was simulated because of the ease at which the microstructure evolution can be measured. Indeed, the entire thickness of the stack is 80 nm, which is sufficiently thin for TEM imaging of the microstructure. Note that the current model can be easily adjusted to model crystallisation and amorphisation of any samples with a layered structure.
We simulated the crystallisation and melting processes of amorphous Ge2Sb2Te5 with a focused Gaussian laser beam. The beam radius (1/e2 intensity) was 600 nm and the peak power was changed from 0 mW to 5.0 mW, whilst the pulse duration was varied from 100 ns to 1000 ns. These parameters were chosen by considering the accessible parameters of our laser testing system48, which will be used to compare the modelled and measured change in transmission due to the laser pulse. In this system, the temporal waveform of the laser pulse is an isosceles trapezoid function with rise and fall time of 8 ns. Due to the thinness of the Ge2Sb2Te5 layer, the divergence of the laser beam in the Ge2Sb2Te5 was ignored. At the 660 nm laser wavelength, the complex refractive indices of amorphous and crystalline Ge2Sb2Te5 are Na = 4.36–1.79i and Nc = 4.61–4.01i, respectively12.
The crystallisation process of the programmable optical device was simulated using a 3.0 mW and 300 ns laser pulse. Fig. 2b and c show the peak temperature in the sample, the crystallised fraction, and the sample’s transmissivity and reflectivity as a function of time, respectively. The peak temperature continuously rises during the laser pulse and then quickly quenches when the laser pulse ends. Figure 2b clearly shows that the crystallisation incubation time is 80 ns, at which time the peak temperature is 566 K. The crystallised fraction appears to stop growing after 260 ns because at this time the diameter of the crystallised area matches the FWHM of the laser spot. These characteristic times are also seen in the transmissivity and reflectivity curves, see Fig. 2c. Despite the crystallised fraction being close to 100% at 260 ns, the crystal is still growing. This effect is due to the crystallised fraction being computed under the FWHM of gaussian laser spot, which after 260 ns is smaller than crystal diameter. In addition, the rate that the peak temperature increases becomes slightly higher at 110 ns (see Supplementary Fig. 4), which is due to the higher single-pass absorption of the crystalised film in comparison to the amorphous background. The crystallographic microstructure of the Ge2Sb2Te5 film at any time during crystallisation was also monitored. Figure 2d shows snapshots of the microstructure at 0, 100, 200, 300 and 600 ns. The blue background represents the amorphous phase, whereas other colours represent different orientations of crystalline grains. We see that the crystallised region is polycrystalline and consists of many small grains, indicating that the crystallisation of Ge2Sb2Te5 is nucleation-dominated. Additionally, the crystallised region increases in size during the laser heat pulse and keeps almost constant once the laser pulse ends. This is important for understanding how to programme a photonics device with a multi-level optical response. The diameter of the crystallised region was 810 ± 10 nm at 600 ns. Note that for these pulse conditions the grain size at the centre of the crystallised area is similar to that at the area’s perimeter; we will see later that this is not always the case. The evolution of the microstructure is best seen using Supplementary Video 1.
Multilevel switching modelling
To show how our model can be used to find the conditions for multi-level switching, we used it to simulate the crystallisation dependence on laser power. Figure 3a–c shows the transient evolution of the crystallised fraction, reflectivity and transmissivity for 300 ns laser pulses with powers varying from 0 to 5.0 mW. The crystallised fraction, reflectivity and transmissivity exhibit a similar trend. We have also included the peak temperature evolution in Supplementary Fig. 5. More importantly, we see that there are four distinct phases of evolution. Firstly, for laser powers below 2.0 mW, crystallisation cannot happen because the peak temperature is too low for the crystallites to grow. Indeed, less than 1% of the irradiated area has crystallised. Secondly, partial crystallisation is easily obtained for laser powers between 2.0 and 2.9 mW, which allows the crystallised percentage of material to be varied from 1% to 98%. This result is particularly significant for multi-level, or even programmable analogue optical states. Thirdly, complete crystallisation is realised within a power range of 3.0 to 3.8 mW; we see that 100% of the material that is irradiate by the laser has crystallised. Finally, when the laser power is greater than 3.8 mW, after the film crystallises, it melts and then quickly re-crystallises. This effect occurs because the dissociation probability of a GCA cell is higher than the growth probability for temperatures greater than 788 K (see Supplementary Fig. 2). Since crystallised percentage gradually decreases during dissociation (melting), the transmissivity increases and reflectivity decreases. In the model, we assumed that the molten phase of Ge2Sb2Te5 has the same optical constants as the amorphous phase49. Recrystallisation of the molten phase takes up to twenty nanoseconds, and we see that the recrystallisation rate is higher than the crystallisation rate from an amorphous phase. This is due to the molten area being surrounded by a crystalline matrix; hence recrystallisation can occur from pre-existing crystal templates and there is no need to nucleate a crystal, which is time consuming. This is also reminiscent of high recrystallisation rates that are possible in GeTe-Sb2Te3 superlattice interfacial phase change materials, where crystallisation rates are high due to Sb2Te3 templating effects50,51,52. The melt-recrystallisation effect also verifies that pre-treating a PCM device can significantly increase the rate of phase transformations53. Note, the melt-quenched amorphous phase does not appear at high powers due to the low thermal conductivity of the floating Si3N4 membrane. Figure 2d showed the microstructure for crystallisation using 3.0 mW laser pulses, which didn’t melt the Ge2Sb2Te5. For comparison the crystal’s microstructure evolution for 5 mW laser pulses is also given in Supplementary Fig. 6. The Figure clearly shows melt-recrystallisation, and crystal growth from pre-existing templates causing large domain sizes at the centre of the irradiated mark.
So far, we have presented a model that predicts the time dependent change in optical transmissivity and reflectivity of a Ge2Sb2Te5-based thin film programmable optical stack. We have shown that four switching regimes can take place which result in four distinct microstructural phases, and that the model can predict partial crystallisation which in turn can lead to multi-level optical switching. We now evaluate the accuracy of these predictions by laser switching a 30 nm thick Ge2Sb2Te5 film on a Si3N4 membrane. Figure 3d shows the measured relative optical transmissivity change of the structure as a function of laser power and time for a fixed laser pulse width of 300 ns. The measured switching time and laser powers can be directly compared with the simulated results in Fig. 3c. There appears to be an excellent agreement. We see that the measured minimum laser power for crystallisation is 1.7 ± 0.1 mW, which is similar to the model. Partial crystallisation appears to be possible in a power range of 1.8 to 2.7 mW, and the model predicts 2.0 to 2.9 mW; once again there is a good agreement. Complete crystallisation is achieved for laser powers greater than 2.7 mW and the model predicts 3.0 mW. Qualitatively, we also see that the crystallisation time is shorter for higher power pulses. Indeed, at 5.0 mW, the crystallisation process starts at 40 ± 3 ns, which agrees well with the minimum predicted value (35 ± 3 ns). There is evidence of some small differences between the simulation and experiment results. The current model does not consider laser ablation. Ablation causes a substantial increase in the transmissivity, which is observed in the measurement when the laser power is raised above 5.5 mW (see Supplementary Figs. 9 and 10). We also assumed that molten Ge2Sb2Te5 had the same refractive index as amorphous Ge2Sb2Te5, which was mentioned in reference49. This means melting and recrystallisation can be distinguished in the transient transmissivity simulation. However, in the experiment this distinction cannot be observed, which may be due to molten Ge2Sb2Te5 actually having similar optical properties to the crystalline Ge2Sb2Te5. The optical properties of molten Ge2Sb2Te5 need to be studied further. Practically, the optical properties of the molten Ge2Sb2Te5 can be readily updated in the simulation framework.
Microstructure predictions
The modelled laser-crystallised marks quantitively and qualitatively agree with the measured laser crystallised marks. The crystal microstructures after crystallisation at different laser powers with the same 300 ns pulse width are shown in Fig. 4a. The crystallised regions can clearly be seen to increase in diameter from 0.68 um to 1.39 um as the laser power is increased from 2.8 mW to 4.9 mW. We see that for laser powers between 4.4 mW and 4.9 mW, the grain sizes are much larger at the centre of the crystallised area than at the perimeter, and this effect is caused by crystal growth from pre-existing crystalline surroundings without the need to nucleate. These larger grains were also verified by selected area electron diffraction (see Supplementary Fig. 11). By comparing simulations and measured TEM images, we know that for these laser powers, the centre of the irradiated area melts and then recrystallises. The larger grains at the centre of the mark do not appear at low power and short pulse widths because crystallisation occurs directly from the amorphous phase without melting. The simulated grains at the centre of the laser written mark are elongated relative to the measured grains. This small difference in microstructures may be caused by volume-change-induced stress interfering with the crystal growth direction54, an effect which is not included in the model. The diameters of the crystallised region at laser power larger than 3.3 mW are larger than the FWHM of laser beam (0.7 μm) because of the radial flow of heat outward from the laser spot. The predicted diameter of the crystallised marks shows excellent agreement with the measured diameters, see Fig. 4b. Across the entire range of laser pulse powers studied, we see that the predicted diameter is within the measurement error. The simulations were repeated ten times and the mean diameter of the crystallised region for each simulation is given in Fig. 4b. The error bars show the standard deviation in the mark diameter. A histogram of the mark diameters at 3.8 mW is given in Fig. 3c. The mean mark diameter is 1.125 μm with a standard deviation of just 1.9 nm. Clearly, the reproducibility of the GCA model is very high and the small spread in mark diameters (see Supplementary Fig. 12) stems from the intrinsic stochasticity of the GCA model. Therefore, the model accurately predicts the polycrystalline microstructure, grain size distribution, and the diameter of the crystallised region. This is useful because we can now be confident that this GCA model can predict the laser pulse parameters for multilevel switching.
a Crystallographic microstructures at different laser power. First row: simulation; Second row: experiments. The scale bar is 200 nm. b Mean diameters of crystallised regions at different laser powers. The dashed green line indicates the FWHM of the laser beam. c Histogram of the crystallised mark diameters, which was simulated for an incident laser power of 3.8 mW.
Partial crystallisation and multilevel switching
Multilevel switching can be achieved using a fixed pulse width and controlling the laser pulse power. Indeed, Rios et al used this method to control the output of a Ge2Sb2Te5-programmable on-chip photonics device with four different transmission levels20. A second method to achieve multilevel switching involves using a fixed pulse power and changing the pulse duration (τ). We can see that this is possible by selecting a fixed power in Fig. 3 and noting how the reflectivity and transmissivity change. Here, we simulated and measured partial crystallisation at a fixed laser power of 5.4 mW for different pulse widths. The total simulation time was 500 ns. Figure 5a shows the crystal percentage, reflectivity, and transmissivity after the applied laser pulse. Once again, there are four distinct steps to the phase transformation (also see Supplementary Fig. 7): (i) τ < 10 ns, crystallisation can be ignored due to too little heating; (ii) 10 ns<τ < 60 ns, partial crystallisation with the crystallised percentage being tuneable from 1% to 99%; (iii) 60 ns<τ < 100 ns, complete crystallisation is obtained; (iv) τ > 100 ns, melting and fast re-crystallisation appear during crystallisation. Importantly, we conclude that when the pulse duration is less than 60 ns, the reflectivity can be controlled using the pulse width.
The measured and simulated crystal microstructures after irradiating with 5.4 mW and varying pulse widths are shown in Fig. 5b. The diameter of the crystallised region increases with the laser pulse duration. Longer duration pulses caused melting and subsequent re-crystallisation into marks with large grains in the centre and smaller grains around the perimeter. Again, the agreement between the experiment and the simulation is good.
Multilevel switching laser parameter prediction
Achieving multiple optical states using Ge2Sb2Te5 is challenging due to the rather abrupt optical response to heat pulses. Although multiple reflectivity levels have been achieved using picosecond laser pulses, generally reliably setting intermediate optical states with single nanosecond pulses is difficult. This is because the energy is delivered to the PCM over a similar period to that required for the phase transition, and because more heat is trapped in the surrounding structure. Hence, experimentally optimising the pulse conditions for different optical states is time consuming. Here, however, we found that the GCA Multi-physics modelling approach could accurately predict the pulse conditions for different optical reflectivity levels.
In the previous simulations and experiments, an implicit condition that both pump and probe lasers have the same beam size was used. Hence, a relatively narrow multilevel switching range was obtained due to the crystallised regions easily exceeding the FWHM of the probe laser. This issue can be mitigated by setting the probe laser spot size to be larger than the pump laser spot. We used the GCA multiphysics model to simulate the transmission change of the Ge2Sb2Te5 thin-film programmable optical stack that is switched with different laser power and pulse widths. Here, the beam radii (1/e2 intensity) of the pump and probe lasers were 0.8 μm and 1.1 μm, respectively. Figure 6a shows the normalised transmissivity change. Partial crystallisation and multi-level switching were realised for a power range of 2.4 mW to 5.0 mW, 2.6 times larger than results in Fig. 3. Complete crystallisation was obtained for laser power > 5.0 mW. In experiments, the beam sizes were finely tuned to those used in the simulation. We can see from Fig. 6a that the measured normalised transmission change has similar trend to that simulated. Similarly, the normalised transmission change induced by a 3.5 mW laser pulse with different widths was conducted in simulation and experiments, shown in Fig. 6b. The results also exemplify the accuracy of our multiphysics GCA model. The small differences may be caused by the deviation from the isosceles trapezoid of the temporal waveform of our laser pulses.
Discussion
Crystallisation in PCMs is either nucleation or growth dominated. In nucleation driven materials, an incubation time is required for the material to create stable crystal nuclei. After incubation, a high density of nuclei form and each crystal domain tends to be small. Contrastingly, growth dominated materials do not readily nucleate, and tend to extend the crystalline regions from a nucleus that forms stochastically after a long incubation period. Consequently, the crystal domains in growth dominated materials tend to be larger than those of nucleation dominated materials. AgInSbTe and Ge2Sb2Te5 are commonly referred to as growth and nucleation dominated materials, respectively55. However, it is also possible for Ge2Sb2Te5 to exhibit a growth-dominated crystallisation behaviour because at high temperature, the growth probability of Ge2Sb2Te5 is much larger than the nucleation probability (see Supplementary Figure 2), meaning that if pre-existing nuclei exist in the amorphous background, then Ge2Sb2Te5 crystallisation becomes growth dominated. Indeed, at high laser powers and long pulse widths, we see that the grain sizes at the centre of the heated region are clearly larger than those at the border. These larger grains are due to melting and subsequent re-crystallisation from the crystalline surroundings. This also indicates that the re-crystallisation process is growth dominated. From a device perspective, this finding is significant because if an amorphous mark is created within a crystalline surrounding, the optical constants of the material will not evolve by increasing the nuclei concentration but growing from pre-existing crystalline surroundings. This could be exploited to crystallise Ge2Sb2Te5 in short times. Note, experimentally a good method of distinguishing nucleation and growth dominated materials is to measure the crystallisation time as a function of the amorphous mark area56. The crystallisation time of growth dominated materials shows a strong dependence on the amorphous area, whereas the crystallisation time of nucleation dominated materials is insensitive to the amorphous mark area. Indeed, in the Supplementary Note 15 we show that crystallisation of Ge2Sb2Te5 is dominated by nucleation at moderate temperatures and dominated by growth at higher temperatures.
The modelling allowed us to successfully optimise the laser parameters to achieve more than 8 optical transmittivity levels in Ge2Sb2Te5. Finding these parameters experimentally would be extremely time consuming due to the abrupt nature of the Ge2Sb2Te5 phase transition. Other PCMs and multilayer PCM structures can make this response more gradual, and thus widen the window of pulses that can be used to achieve multilevel switching.18,19 If one must use Ge2Sb2Te5 in a multi-level switching photonics device, our simulations suggest that controlling both the pulse time and pulse power together will provide a wider window of possible partially crystallised states.
In the GCA model, a 2D lattice grid was used to discretize the PCM layer, i.e., it is a 2D crystallisation model. Typically, for visible and near-infrared photonics the PCM films are kept thin to minimise absorption20,57 and thermal mass, which is important for amorphisation. Therefore, a 2D crystallisation model will, in most cases be acceptable. However, films thicker than 30 nm are likely to form multiple grains across the film thickness, and therefore the GCA model will need to be extended to 3D. This will increase the computational resources required to run the model.
The melt-quenched amorphous samples of PCMs generally have a shorter crystallisation start-up time and a higher crystallisation rate than the as-deposited amorphous samples. This makes them attractive for ultrafast storage memory and reprogrammable photonics devices. Density functional calculations show that as-deposited Ge2Sb2Te5 lacks ABAB squares (A = Ge, Sb; B = Te), which in melt-quenched Ge2Sb2Te5 act as nucleation seeds and result in shorter crystallisation times58. Experimental results have found that the sub-critical nuclei (crystalline embryos) existing in the melt-quenched state accelerates the crystallisation start-up time and rate53,56. In GCA model, the melt-quenched amorphous materials can be dealt with by randomly adding a fraction of crystalline cells into the amorphous matrix. Further studies should be conducted to determine whether other thermodynamic parameters of the melt-quenched amorphous state are the same as the as-deposited amorphous state.
In summary, a Gillespie cellular automata-based multiphysics model was developed to accurately predict the transient optical response of phase change material programmable photonics devices. We have used this model to simulate entire transient changes to the transmissivity and reflectivity of a programmable optical structure. By including the non-linear dependence of the viscosity with temperature, we were able to accurately predict the optical and microstructural properties of Ge2Sb2Te5. Somewhat surprisingly, we found that laser pulses with relatively high intensities and long widths can cause Ge2Sb2Te5 to exhibit growth dominated crystallisation, rather than nucleation dominated crystallisation, which is usual for Ge2Sb2Te5. These results were confirmed by TEM measurements on laser switched Ge2Sb2Te5. We also showed that the simulation tool can be used to accurately predict multilevel switching, and therefore we believe it will become a powerful tool to design and optimise programmable PCM photonic devices. For this reason, we have made the code open for others to use46.
Methods
Growth velocity and nucleation rate
Measurements of crystallisation kinetics for prototypical PCMs at low heating rates59,60 showed that the growth velocity conforms to an Arrhenius exponential relation with reciprocal temperature, and typically this Arrhenius relationship is assumed in previously reported models of PCMs. Recently, however, ultrafast differential scanning colorimetry studies and laser and electrical heating experiments34,35,36,37 showed that the growth velocity deviates strongly from the Arrhenius model at high temperatures due to the high fragility of the PCMs, which flattens the viscosity and growth velocity at high temperatures. The PCMs are in the super-cooled liquid state and the glass state when the temperature is above and below the glass transition temperature Tglass, respectively. The viscosity of this super-cooled liquid state is given by the Mauro-Yue-Ellison-Gupta-Allan model61, whereas the viscosity of the glass state follows the Arrhenius relationship (see Supplementary Note 2).
The crystal growth velocity (i.e., the growth rate of the radius of a crystal cluster per unit time) is modelled as
where, r and Rh are the atomic radius and the hydrodynamic radius, respectively, kB is the Boltzmann constant, T is the temperature, λj is the diffusional jump distance, η(T) is the viscosity, Δg is the bulk Gibbs energy difference per monomer between the liquid and crystalline phase. According to Thompson-Spaepen model62, Δg is calculated as
where, vm is the volume of one monomer, ΔHf is the enthalpy of fusion at the melting temperature Tm. According to the classical growth theory, the two terms of Eq. (1) correspond to the growth (vgr) and dissociation (vdi) velocity, respectively, which means that Eq. (1) represents the net growth velocity.
Based on the classical nucleation theory, the nucleation rate is written as63
where, nc = f(θ)·32π/3·vm2σ3/Δg3 is the number of monomers contained in the critical crystal clusters, ΔGc = f(θ)·16π/3·vm2σ3/Δg2 is the critical energy barrier for nucleation, σ is the interfacial energy, f(θ) = (2-3cosθ + cos3θ)/4 is the factor that indicates the degree of the heterogeneous nucleation, θ is the wetting angle, γ is the molecular jump frequency which is modelled by the Stokes-Einst31ein relation63 as γ = kBT/3πλj3η. Here, the nucleation rate means the number of newly generated nuclei per unit volume and time. Typical parameters for Ge2Sb2Te5 were extracted from four different publications; for the interested reader, this data is compiled in Supplementary Table 1.
Modified GCA model
In the GCA models38, the PCM is divided into a two-dimensional matrix. Each site (i, j) has a phase variable rij to indicate whether it is in crystalline (rij = 1) or amorphous (rij = 0) phase, and an orientation variable ϕij with a range of [0, π) to represent the infinite possible orientations of the crystalline grain. Three possible events can impact the state of each site: (a) Nucleation; an amorphous cell transforms into a crystalline cell to form a new crystal nucleus with a probability of Pnu(i, j). Then, rij = 1 and ϕij is the orientation of the nucleus; (b) Growth; an amorphous cell grows onto an adjacent crystallite with an orientation ψ with a probability of Pgr(i, j, ψ). Then, rij = 1 and ϕij = ψ; (c) Dissociation; a crystalline site detaches from its parent crystallite and becomes amorphous phase with a probability of Pdi(i, j). Then, rij = 0 and ϕij becomes a random value meaning a random orientation. The GCA model uses a stochastic Gillespie-type algorithm to simultaneously compute the time step and the state of the site using the probabilities of all events.
In contrast to Ref. 38, here the probabilities of the three events were directly deduced from the above growth velocity and nucleation rate equations, and this allowed accurate predictions of the phase transition across a wide range of temperatures. Considering the influence of neighbours on a site as a linear approximation, the nucleation probability Pnu(i, j) for an amorphous site to nucleate is written as
where, \(n_{ij}^{am}\) is the number of amorphous neighbours of a site. The growth probability Pgr(i, j, ψ) for an amorphous site to crystallise according to an adjacent crystallite with an orientation ψ is written as
and the dissociation probability Pdi(i, j) for a crystalline site to become amorphous is written as
where, nij is the total number of neighbours of a site which is equal to 8 in the two-dimensional matrix, \(n_{ij}^\psi\) is the number of crystalline neighbours with an orientation ψ of a site, and D is the distance between two adjacent sites.
Laser-induced heat distribution
A laser pulse can increase the temperature of PCMs and induce crystallisation, melting, and/or amorphisation. The transient temperature profile is obtained by calculating the unsteady heat conduction equation,
where, T(x, y, z, t) is the temperature at a location of (x, y, z) and a certain time t, ρ is the density, c is the specific heat capacity, k is the heat conduction coefficient, Q(x, y, z, t) is the heat source brought by the laser pulse. Considering the laser beam’s Gaussian transverse profile, the laser-induced heat is modelled as
where, Pin is the optical power, α is the absorption coefficient, ω is the gaussian beam radius, R is the reflectivity, and f(t) is the temporal waveform. An isosceles trapezoid function with rising and falling edges of 8 ns was assumed for f(t) in simulations to reflect the laser waveforms in experiments.
An explicit finite difference method was used to compute Eq. (7) to obtain the transient temperature profile of a given sample structure. However, the maximum time step is limited to Δtmax = ρch2/6k in three-dimensions in order to satisfy the stability requirements, where h is the space step. To increase the efficiency of the calculation while maintaining high precision, a non-uniform meshing technique was exploited by dividing more grid points at laser heating regions and fewer grid points at regions far from the laser beam (see Supplementary Note 4). Additionally, a time-step alternation strategy was adopted to further accelerate the calculation (see Supplementary Note 5).
Optical model
During laser pulse irradiation on the PCM sample, the temperature rapidly increases, and many PCM sites transform to new phases, leading to the formation of an intermediate phase which simultaneously consists of crystalline and amorphous phases. According to the effective medium theory, the effective permittivity εeff(λ) of this intermediate PCM is calculated based on Lorentz-Lorenz relation64,
where, Xf is the crystallised fraction which is defined as the ratio of crystalline sites to the total sites. εc(λ) and εa(λ) are the wavelength-dependent dielectric functions for the crystalline and amorphous phases, respectively. Then, the effective refractive index (neff) and extinction coefficient (keff) are given by
where, ε1 and ε2 are the real and imaginary parts of εeff(λ), respectively.
Using the characteristic matrix approach and the Fresnel equations, the reflectivity and transmissivity of a PCM sample at normal incidence are calculated as65
where, ns is the complex refractive index of substrate, Re(ns) means the real part of ns, mij (i, j = 1, 2) are the elements of the characteristic matrix of the PCM sample.
Sample preparation and characterisation
A 50 nm thick silicon nitride membrane window (TED Pella, No. 21509) supported by a 0.5 mm silicon substate was chosen as substrate due to the window’s good electron transmission characteristics. A 30 nm thick amorphous Ge2Sb2Te5 film was deposited on the substrate by radio frequency magnetron sputtering from a Ge2Sb2Te5 target at 30 W for 67 seconds in an argon atmosphere at a pressure of 0.5 Pa. Our inhouse-built static tester48 was used to make crystallisation marks on the as-deposited amorphous Ge2Sb2Te5 film. In short, the system consists of a low-power 638 nm probe laser and a relatively high-power 660 nm pump laser. The system can simultaneously measure the reflection and transmission of the probe laser from the sample whilst pump laser pulses heat the sample. The focused laser spot has a beam size of 0.6 μm (1/e2 intensity) on the sample. Here, we used the static tester to make a matrix of crystallisation marks under different pulse widths and intensities. Simultaneously, the transient transmission change was measured. The absolute value of the relative transmissivity change cannot be directly compared with the simulated transmissivity change because there is a DC offset on the amplified detector and because the photodetector does not collect all the transmitted light.
The size and microstructure of the crystallised marks on the as-deposited Ge2Sb2Te5 film were then measured by Transmission Electron Microscopy (FEI Titan with Gatan OneView camera) using an acceleration voltage of 200 kV and a rather small 40 μm objective aperture to enhance the contrast of the crystallised regions. The beam current was kept sufficiently low so that the PCM state was unaffected by the heating. A schematic of the TEM sample and its preparation is given in Supplementary Figure 8.
Data availability
All the simulating data in this article was generated by our home-made multiphysics GCA code. We have also made all data available through a public GitHub repository46.
Code availability
We have made the code open for others to use through a public GitHub repository46.
References
Lee, T. H. & Elliott, S. R. Chemical bonding in chalcogenides: the concept of multicenter hyperbonding. Adv. Mater. 32, 2000340 (2020).
Martinez, J. C. et al. The origin of optical contrast in Sb2Te3-based phase-change materials. Phys. Status Solidi RRL 257, 1900289 (2020).
Zhu, M. et al. Unique bond breaking in crystalline phase change materials and the quest for metavalent bonding. Adv. Mater. 30, 1706735 (2018).
Kim, W. et al. Ald-based confined pcm with a metallic liner toward unlimited endurance. 2016 IEEE International Electron Devices Meeting (IEDM), San Francisco, CA, USA, p 4.2.1-4.2.4 (2016).
Hoddeson, L. & Garrett, P. The discovery of Ovshinsky switching and phase-change memory. Phys. Today 71, 44–51 (2018).
Cao, T., Wang, R., Simpson, R. E. & Li, G. Photonic Ge-Sb-Te phase change metamaterials and their applications. Prog. Quantum Electron. 74, 100299 (2020).
Rudé, M. et al. Optical switching at 1.55 μm in silicon racetrack resonators using phase change materials. Appl. Phys. Lett. 103, 141119 (2013).
Rudé, M., Simpson, R. E., Quidant, R., Pruneri, V. & Renger, J. Active control of surface plasmon waveguides with a phase change material. ACS Photonics 2, 669–674 (2015).
Wang, Q. et al. Optically reconfigurable metasurfaces and photonic devices based on phase change materials. Nat. Photon. 10, 60–65 (2016).
Wilhelm, E., Richter, C. & Rapp, B. E. Phase change materials in microactuators: Basics, applications and perspectives. Sens. Actuators, A 271, 303–347 (2018).
Champlain, J. G. et al. Examination of the temperature dependent electronic behavior of GeTe for switching applications. J. Appl. Phys. 119, 244501 (2016).
Chew, L. T. et al. Chalcogenide active photonics; SPIE, 2017.
Dong, W. et al. Tunable mid-infrared phase-change metasurface. Adv. Opt. Mater. 6, 1701346 (2018).
Leitis, A. et al. All-dielectric programmable huygens’ metasurfaces. Adv. Funct. Mater. 30, 1910259 (2020).
Waldecker, L. et al. Time-domain separation of optical properties from structural transitions in resonantly bonded materials. Nat. Mater. 14, 991–995 (2015).
Rao, F. et al. Reducing the stochasticity of crystal nucleation to enable subnanosecond memory writing. Science 358, 1423–1427–1423–1427 (2017).
Gholipour, B. et al. Phase-change-driven dielectric-plasmonic transitions in chalcogenide metasurfaces. NPG Asia Mater. 10, 533–539 (2018).
Meng, Y. et al. Design of a 4-level active photonics phase change switch using vo2 and Ge2Sb2Te5. Appl. Phys. Lett. 113, 071901 (2018).
Meng, Y. et al. Ultrafast multilevel optical tuning with CSb2Te3 thin films. Adv. Opt. Mater. 6, 1800360 (2018).
Ríos, C. et al. Integrated all-photonic non-volatile multi-level memory. Nat. Photon. 9, 725–732 (2015).
Li, X. et al. Fast and reliable storage using a 5 bit, nonvolatile photonic memory cell. Optica 6, 1–6 (2019).
Wuttig, M., Bhaskaran, H. & Taubner, T. Phase-change materials for non-volatile photonic applications. Nat. Photonics 11, 465–476 (2017).
Teo, T. Y., Lu, L. & Simpson, R. E. Reconfigurable multi-bit phase change material silicon photonics directional couplers. Preprint at https://arxiv.org/abs/2106.01169 (2021).
Dong, W. et al. Wide bandgap phase change material tuned visible photonics. Adv. Funct. Mater. 29, 1806181 (2019).
Zhang, Y. et al. Broadband transparent optical phase change materials. Conference on Lasers and Electro-Optics, San Jose, California, p JTh5C.4 (2017).
Zhang, Y. et al. Broadband transparent optical phase change materials for high-performance nonvolatile photonics. Nat. Commun. 10, 4279 (2019).
Delaney, M., Zeimpekis, I., Lawson, D., Hewak, D. W. & Muskens, O. L. A new family of ultralow loss reversible phase-change materials for photonic integrated circuits: Sb2S3 and Sb2Se3. Adv. Funct. Mater. 30, 2002447 (2020).
Liu, H. et al. Rewritable color nanoprints in antimony trisulfide films. Sci. Adv. 6, eabb7171 (2020).
Zhang, Y. et al. Electrically reconfigurable non-volatile metasurface using low-loss optical phase-change material. Nat. Nanotechnol. 16, 661–666 (2021).
Shportko, K. et al. Resonant bonding in crystalline phase-change materials. Nat. Mater. 7, 653–658 (2008).
Gemo, E. et al. Simple technique for determining the refractive index of phase-change materials using near-infrared reflectometry. Opt. Mater. Express 10, 1675–1686 (2020).
Meyer, S., Tan, Z. Y. & Chigrin, D. N. Multiphysics simulations of adaptive metasurfaces at the meta-atom length scale. Nanophotonics 9, 675–681 (2020).
Tabatabaei, F., Boussinot, G., Spatschek, R., Brener, E. A. & Apel, M. Phase field modeling of rapid crystallization in the phase-change material aist. J. Appl. Phys. 122, 045108 (2017).
Orava, J., Greer, A. L., Gholipour, B., Hewak, D. W. & Smith, C. E. Characterization of supercooled liquid Ge2Sb2Te5 and its crystallization by ultrafast-heating calorimetry. Nat. Mater. 11, 279–283 (2012).
Salinga, M. et al. Measurement of crystal growth velocity in a melt-quenched phase-change material. Nat. Commun. 4, 2371 (2013).
Sebastian, A., Le Gallo, M. & Krebs, D. Crystal growth within a phase change memory cell. Nat. Commun. 5, 4314 (2014).
Chen, B., ten Brink, G. H., Palasantzas, G. & Kooi, B. J. Crystallization kinetics of GeSbTe phase-change nanoparticles resolved by ultrafast calorimetry. J. Phys. Chem. C. 121, 8569–8578 (2017).
Ashwin, P., Patnaik, B. S. V. & Wright, C. D. Fast simulation of phase-change processes in chalcogenide alloys using a Gillespie-type cellular automata approach. J. Appl. Phys. 104, 084901 (2008).
Wright, C. D., Hosseini, P. & Diosdado, J. A. V. Beyond von-neumann computing with nanoscale phase-change memory devices. Adv. Funct. Mater. 23, 2248–2254 (2013).
Diosdado, J. A. V., Ashwin, P., Kohary, K. I. & Wright, C. D. Threshold switching via electric field induced crystallization in phase-change memory devices. Appl. Phys. Lett. 100, 253105 (2012).
Miscuglio, M., Adam, G. C., Kuzum, D. & Sorger, V. J. Roadmap on material-function mapping for photonic-electronic hybrid neural networks. APL Mater. 7, 100903 (2019).
de Galarreta, C. R. et al. Nonvolatile reconfigurable phase-change metadevices for beam steering in the near infrared. Adv. Funct. Mater. 28, 1704993–1704993 (2018).
Ruiz de Galarreta, C. et al. Reconfigurable multilevel control of hybrid all-dielectric phase-change metasurfaces. Optica 7, 476–484 (2020).
Hosseini, P., Wright, C. D. & Bhaskaran, H. An optoelectronic framework enabled by low-dimensional phase-change films. Nature 511, 206–211–206–211 (2014).
Zhou, W. et al. High thermal stability and low density variation of carbon-doped Ge2Sb2Te5 for phase-change memory application. Appl. Phys. Lett. 105, 243113 (2014).
Wang, Y., Ning, J., Lu, L., Bosman, M. & Simpson, R. E. Multiphysics GCA codes. Github https://github.com/YunzhengWang/multiphysics_GCA (2021).
Ohshima, N. Crystallization of germanium–antimony–tellurium amorphous thin film sandwiched between various dielectric protective films. J. Appl. Phys. 79, 8357–8363 (1996).
Behera, J. K., Zhou, X., Tominaga, J. & Simpson, R. E. Laser switching and characterisation of chalcogenides: Systems, measurements, and applicability to photonics [invited]. Opt. Mater. Express 7, 3741–3759 (2017).
Kuwahara, M. et al. A reversible change of reflected light intensity between molten and solidified Ge-Sb-Te alloy. Jpn. J. Appl. Phys. 46, L868–L870 (2007).
Zhou, X. et al. Avalanche atomic switching in strain engineered Sb2Te3–GeTe interfacial phase-change memory cells. Nano Futures 1, 025003 (2017).
Simpson, R. E., Fons, P., Kolobov, A. V., Krbal, M. & Tominaga, J. Enhanced crystallization of GeTe from an Sb2Te3 template. Appl. Phys. Lett. 100, 021911 (2012).
Simpson, R. E. et al. Interfacial phase-change memory. Nat. Nanotechnol. 6, 501–505 (2011).
Lee, B.-S. et al. Observation of the role of subcritical nuclei in crystallization of a glassy solid. Science 326, 980–984 (2009).
Eising, G., Pauza, A. & Kooi, B. J. Stress-induced crystallization of Ge-doped Sb phase-change thin films. Cryst. Growth Des. 13, 220–225 (2013).
Zhang, W., Mazzarello, R., Wuttig, M. & Ma, E. Designing crystallization in phase-change materials for universal memory and neuro-inspired computing. Nat. Rev. Mater. 4, 150–168 (2019).
Coombs, J. H., Jongenelis, A. P. J. M., Es‐Spiekman, W. V. & Jacobs, B. A. J. Laser‐induced crystallization phenomena in GeTe‐based alloys. II. Composition dependence of nucleation and growth. J. Appl. Phys. 78, 4918–4928 (1995).
Feldmann, J., Youngblood, N., Wright, C. D., Bhaskaran, H. & Pernice, W. H. P. All-optical spiking neurosynaptic networks with self-learning capabilities. Nature 569, 208–214 (2019).
Akola, J., Larrucea, J. & Jones, R. O. Polymorphism in phase-change materials: melt-quenched and as-deposited amorphous structures in Ge2Sb2Te5 from density functional calculations. Phys. Rev. B 83, 094113 (2011).
Kalb, J., Spaepen, F. & Wuttig, M. Atomic force microscopy measurements of crystal nucleation and growth rates in thin films of amorphous Te alloys. Appl. Phys. Lett. 84, 5240–5242 (2004).
Kooi, B. J., Pandian, R., De Hosson, J. T. M. & Pauza, A. In situ transmission electron microscopy study of the crystallization of fast-growth doped SbxTe alloy films. J. Mater. Res. 20, 1825–1835 (2005).
Mauro, J. C., Yue, Y., Ellison, A. J., Gupta, P. K. & Allan, D. C. Viscosity of glass-forming liquids. Proc. Natl Acad. Sci. USA 106, 19780–19784 (2009).
Thompson, C. V. & Spaepen, F. On the approximation of the free energy change on crystallization. Acta Metall. 27, 1855–1859 (1979).
Senkader, S. & Wright, C. D. Models for phase-change of Ge2Sb2Te5 in optical and electrical memory devices. J. Appl. Phys. 95, 504–511 (2004).
Qu, Y. et al. Dynamic thermal emission control based on ultrathin plasmonic metamaterials including phase-changing material GST. Laser Photonics Rev. 11, 1700091 (2017).
Larouche, S. & Martinu, L. OpenFilters: open-source software for the design, optimization, and synthesis of optical filters. Appl. Opt. 47, C219–C230 (2008).
Acknowledgements
This research was supported by the NSLM project (A18A7b0058). Support from A*STAR’s microscopy facility is kindly acknowledged. Ms Ning is grateful for her Singapore Ministry of Education (MoE) PhD scholarship. We are thankful for the compute time granted by the National Supercomputing Centre (NSCC) Singapore. The work was carried out under the auspices of the SUTD-MIT International Design Center (IDC).
Author information
Authors and Affiliations
Contributions
Y.Z.W. and J.N. contribute equally. Y.Z.W. was responsible for programming, computing, and laser experiments. J.N. and M.B. conducted the TEM measurements. J.N. and L.L. prepared the sample. Y.Z.W. and R.E.S. wrote the manuscript. All authors reviewed and approved the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, Y., Ning, J., Lu, L. et al. A scheme for simulating multi-level phase change photonics materials. npj Comput Mater 7, 183 (2021). https://doi.org/10.1038/s41524-021-00655-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41524-021-00655-w
This article is cited by
-
Reconfigurable optical logic in silicon platform
Scientific Reports (2024)
-
Encoding reprogrammable properties into magneto-mechanical materials via topology optimization
npj Computational Materials (2023)
-
Multiscale simulations of growth-dominated Sb2Te phase-change material for non-volatile photonic applications
npj Computational Materials (2023)