Abstract
For the upsurge of high breakdown strength (\({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\)), efficiency (\({{{{{\rm{\eta }}}}}}\)), and discharge energy density (\({{{{{{\rm{U}}}}}}}_{{{{{{\rm{e}}}}}}}\)) of next-generation dielectrics, nanocomposites are the most promising candidates. However, the skillful regulation and application of nano-dielectrics have not been realized so far, because the mechanism of enhanced properties is still not explicitly apprehended. Here, we show that the electric field cavity array in the outer interface of nanosieve-substrate could modulate the potential distribution array and promote the flow of free charges to the hole, which works together with the intrinsic defect traps of active Co3O4 surface to trap and absorb high-energy carriers. The electric field and potential array could be regulated by the size and distribution of mesoporous in 2-dimensional nano-sieves. The poly(vinylidene fluoride-co-hexafluoropropylene)-based nanocomposites film exhibits an \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) of 803 MV m−1 with up to 80% enhancement, accompanied by high \({{{{{{\rm{U}}}}}}}_{{{{{{\rm{e}}}}}}}\) = 41.6 J cm−3 and \({{{{{\rm{\eta }}}}}}\,\)≈ 90%, outperforming the state-of-art nano-dielectrics. These findings enable deeper construction of nano-dielectrics and provide a different way to illustrate the intricate modification mechanism from macro to micro.
Similar content being viewed by others
Introduction
With the development of power system and energy system dominated by renewable energy, new requirements for advanced electrical and energy materials are continuously being put forward1,2,3. Exploiting high electric field breakdown performance (\({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\)) engineering insulating materials is of great significance for the design and manufacture of power equipment insulation system in the third-generation power grid;2 developing high-energy-density (\({{{{{{\rm{U}}}}}}}_{{{{{{\rm{e}}}}}}}\)) and high-energy-efficiency (\({{{{{\rm{\eta }}}}}}\)) electrostatic capacitor dielectric is prominence for reducing the volume and weight of energy storage devices4,5. Since the concept of nano-dielectrics is first proposed by T. J. Lewis in 1994, numerous efforts show that the incorporation of nanoparticles (NPs) could significantly improve the electrical, thermal, and mechanical properties of dielectric materials due to their nano “interface” effect is more vital than itself structure4,5,6,7,8,9,10,11,12,13,14,15,16,17. Therefore, nanocomposites dielectric is one of the most promising candidates for advanced functional insulation and electrostatic energy storage material.
Polymer is both an integral part of many insulating devices, such as cable, and a critical component of electrostatic energy storage devices, such as metallized film capacitor, which is widely applied in electrical and energy territory18,19,20. Poly(vinylidene fluoride-co-hexafluoropropylene) (P(VDF-HFP)) has the advantages of high dielectric constant (\({{{{{\rm{K}}}}}}\)), stable structure, corrosion resistance, and heat resistance, etc., and is a promising competitor as insulating energy storage material21,22. So, it is adopted as the substrate in this experiment.
Polymer-based nano-dielectric is a research hotspot in the film capacitor field in the past decade and quite a few efforts report excellent modified performance13,18,19,20,21,22,23,24,25. However, the modification mechanism is still not been understandably clarified, resulting in us not being able to regulate it maturely and realize rational construction of the nanocomposites. Trap theory is well recognized as a way to depict the essential features of charge carrier transport, with shallow traps assisting charge transport and deep traps holding charge for long-lasting time10,26. The depth of the trap is determined by the location of the trap energy level between the conduction and valence band, depending on the natural defect of the material itself. It is a micro-level theoretical explanation27. We call these kinds of traps as “intrinsic charge traps” (eV) in this paper. But, the interconnection from microscopic charge trapping and de-trapping to macroscopic free charge carriers’ transport and dielectric local discharge is not well investigated since the failure process is complicated. The application of density functional theory (DFT)28 and finite element simulation (FES)29 benefited from advanced computer technology provides the possibility to build a “bridge” between them for the illustration of the mechanism, while little attention has been paid to this aspect in the past. Meanwhile, most of the papers on these two technologies are sometimes too coarse or simplified to embody the experimental results precisely. For example, the high external electric field (\({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\)) application context of the insulating materials is rarely considered in the DFT, and the dealing of interface layer parameters is unrefined in FES. Experimentally, most of the nanocomposites are carried out on the basis of NPs, and some works on 1D and 2D nanomaterials have emerged in recent years13,30,31. Most nanofillers are coarse or purchased from the market. After simple treatment, such as surface decoration, etc., they are incorporated into the insulating substrate. 2D nanomaterial is a rising star due to its huge specific surface, and unique electrical, thermal, optical, and electromagnetic properties13,32. But the lack of nanomaterials’ synthesis and regulation techniques leads to the scarcity of systematic structural research, resulting in a disconnected understanding of the modification mechanism.
In this work, we synthesize homogeneous nano-sieves of different pore sizes and incorporate them uniformly into P(VDF-HFP)-based films with low doping. It is found that the DC breakdown field improvement has never been so high, and by some distance. Such a large breakdown electric field is achieved. Theoretical calculations reveal that the electric field cavity array and sub-macro potential trap array in the outer interface layer allure the free-charged ions or electrons toward the holes of nano-sieves, making them effectively captured by the deep intrinsic defect traps on the active Co3O4 surface. Meanwhile, the dielectric loss is suppressed, even comparable to that of linear dielectrics. The close-knit connection (F-Co3+) between nano-sieves (large specific surface area) and polymers significantly affects the polarization of P(VDF-HFP).
Results
Characterization of nanofillers and nanocomposite films
Co3O4 is a p-type antiferroelectric semiconductor with multiple metal valence states33, and is adopted as the additive. Uniformly belt-like Co3O4 nano-sieves (NSIs) with four different pore sizes (5, 15, 25, 50 nm) are synthesized by regulating hydrothermal reaction and calcination conditions (Fig. 1a, Supplementary Note 1, and Methods section). It can be seen from the scanning electron microscope (SEM) images (Fig. 1a, Supplementary Fig. 1 and 2) that the NSIs have a quasi-one-dimensional (1D) nanobelt morphology, with a width of 200–400 nm and a length of 2–3 um. High-resolution transmission electron microscope (HRTEM) image (Fig. 1b) and fast Fourier transform pattern (inset) show the preferential exposure of (110) facet of spinel Co3O4. In addition, NPs (16 nm) are obtained from our previous work for controlled experiments (Supplementary Fig. 3). At the same test conditions, the XRD peak of Co3O4 NPs is higher and narrower than that of NSIs, showing that NPs have better crystallinity while NSIs have a higher specific surface area and more defects34. In order to quantify the specific surface area, nitrogen adsorption and desorption isotherms based on Brunauer–Emmett–Teller (BET) theory are tested. As shown in Supplementary Fig. 5, the specific surface area of NSIs is generally ~385.5 m2/g, which is 5.7 times larger than that of NPs (67.6 m2/g). These results show that we have successfully synthesized NSIs with large specific surface area and distinct pore sizes.
P(VDF-HFP) (10 mol% HFP) with higher K of 9–10 at 1 kHz is selected as the matrix to investigate the nano-modification mechanism and performance. Using the serial dilution method to obtain low doping concentration (0.0008, 0.008, 0.08 wt%) nano-suspensions and the classic casting method to fabricate thin films (Fig. 1c, Supplementary Note 2). The fabricated films are highly flexible and translucent. In the case of 0.0008 and 0.008 wt% doping, equal to “impurity” level content, the naked eye cannot distinguish any difference from the pure film; the film turns black gradually as the further increase of nanofillers (Fig. 1c, and Supplementary Fig. 6). Each nanocomposites film is uniquely labeled as X@NSIs-Y wt% (X denoted as pore size, and Y denoted as doping amount). The surface SEM images of films intuitively reflect their crystalline state (Supplementary Fig. 7). Pure P(VDF-HFP) film has a spherulite structure (Supplementary Fig. 7a). After the addition of NSIs, the surface crystalline state of the film presents fibrous and smooth, which indicates NSIs might affect the nucleation of growth process and lead to the increment of β-phase content (Supplementary Fig. 7b–d)35. But when NSIs are excessive, it would hinder the growth of crystal domains (smaller grains), resulting in the increase of α-phase content (Supplementary Fig. 7e, f). Front high-angle annular dark-field scanning TEM (HAADF-STEM) and cross-sectional SEM images of 15@NSIs-3wt% film display that NSIs are randomly and uniformly distributed in the ~18 um thick film, and no agglomeration occurred (Fig. 1d and Supplementary Fig. 8). It can be seen from HRTEM images of 15@NSIs-3wt% (Fig. 1e) and pure film (Supplementary Fig. 9) that P(VDF-HFP)-based films contain polycrystalline and amorphous regions, and NSIs are in direct contact with the amorphism region. Fourier-transform infrared (FTIR) and XRD techniques are employed to characterize the α, β, and γ phases of the films (Fig. 1f, and Supplementary Figs. 11–15). The results before and after heat treatment, the pure film’s β content decreased by 16% (42.3 → 35.65%), while that of 15@NSIs-0.008 wt% only reduced by 8% (47.3 → 43.5%) (Supplementary Fig. 11), illustrates that NSIs facilitate the formation of β-phase during polymer crystal growth, and inhibit the conversion of β to α during heat treatment36. With the increase of the doping mass fraction, the β-phase content increases first and then decreases (Supplementary Table 1), which is consistent with the previous film’s surface SEM images (Supplementary Fig. 7). In a typical 15@NSIs-0.008 wt% film, the relative content of α, β, and γ phases is 20.1%, 43.5%, and 36.4%, respectively (Supplementary Fig. 14). The nanocomposites films with different pore sizes have nearly identical XRD and FTIR results at the same doping mass, which shows that the pore size has little effect on the phases component of P(VDF-HFP)-based film (Supplementary Fig. 15, and Supplementary Table 1).
Electrical properties
The electrical properties of P(VDF-HFP) and its nanocomposites with Co3O4 nanomaterials are estimated at room temperature (Fig. 2, Supplementary Note 3). The dielectric spectrums as a function of frequency are measured (Fig. 2a, Supplementary Figs. 16–17). In the case of “impurity-level” doping (0.0008 and 0.008 wt%), the introduction of Co3O4 NSIs with higher \({{{{{\rm{K}}}}}}\) (\({{{{{{\rm{\varepsilon }}}}}}}_{{{{{{\rm{r}}}}}}}\), ~20)37 actually leads to a decreased \({{{{{\rm{K}}}}}}\) of the nanocomposites film compared to pure film, which is inconsistent with conventional cognition. When the filler fraction is further increased, the \({{{{{\rm{K}}}}}}\) value is mounting and exceeding that of pure film (Fig. 2a). The spectrum of loss factor and conductivity has similar variation pattern, which first decreases and then increases with the rising of doping concentration (Supplementary Fig. 16). The nanocomposites with different pore sizes NSIs have almost the same dielectric spectrum at 0.008 wt% (Supplementary Fig. 17). Combined with aforementioned XRD and FTIR results (Supplementary Fig. 15), it can be deduced that pore size has little influence on nanocomposites’ properties films at low voltage. The two-parameters Weibull plots are employed for statistical analysis of the breakdown field strength (\({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\)) data (Fig. 2b, Supplementary Figs. 18–20). Impressively, the \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) of 15@NSIs-0.008 wt% is 803.3 MV m−1, which is 40% higher than for the NPs/P(VDF-HFP)-0.008 wt% (575 MV m−1), >80% higher than for pure film (~445 MV m−1). The elevation magnitude is superior to state-of-the-art reported works (Fig. 2b,c, Supplementary Table 2). The Co3O4 NSIs have various modification states to \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) when the filler fraction is less than 3 wt%, which also contributes to high-energy storage performance. Here, the pore size of NSIs exhibits obviously diversity in \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) (Supplementary Figs. 19, and 20). It can be clearly seen that 15@NSIs-0.008 wt% has higher \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) than other pore sizes-based films. The pore size has significant domination on breakdown strength which is a sharp contrast to previously obtained conclusion at low voltage, indicating that there are other key factors are crucial to the breakdown process in high electric field.
We next evaluate the energy storage properties of the films from their unipolar electric displacement-electric field (D-E) loops under room temperature (Fig. 2d–f, Supplementary Note 4). The discharge energy density (\({{{{{{\rm{U}}}}}}}_{{{{{{\rm{e}}}}}}}\)) reaches a maximum of 41.6 J cm−3 for 15@NSIs-0.008 wt% at 800 MV m−1 because of the excellent dielectric strength (Fig. 2d). The value is 3.4 times as large as the 12.2 J cm−3 for pure P(VDF-HFP) film. An overall upgraded energy efficiency (\({{{{{\rm{\eta }}}}}}\), ~90%) is discovered, which is superior to the great majority of electrostatic energy storage capacitors (Fig. 2e)9,11,15. As shown in Fig. 2d, a set of concentration control experiments, the D-E loops of 15@NSIs-0.0008 wt% and 15@NSIs-0.008 wt% are located below that of pure film, corroborated with aforementioned reduced \({{{{{\rm{K}}}}}}\), suggesting the interaction between the NSIs and macromolecule inhibits partial polymer polarization. While the NSIs are overdosed, the loop shifts to the upper left with increasing loss, which is probably due to the polarization action of Co3O4 NSIs itself structure far exceeding the inhibition effect of the interface38. The polarization of 15@NSs-3wt% continues to increase after the maximum electric field is reached, creating a bloated shape of the D-E loop. This demonstrates that significant leakage currents are present in 15@NSs-3wt%39. All of those merits demonstrate that the P(VDF-HFP)-based film modified by the nano-sieves with suitable pore size at low doping is a promising candidate for electrostatic storage application because of combined great \({{{{{{\rm{U}}}}}}}_{{{{{{\rm{e}}}}}}}\) and high \({{{{{\rm{\eta }}}}}}\), which surpasses the bulk P(VDF-HFP)-based film and nano-modified dielectrics (Fig. 2f, Supplementary Table 2)4,40,41,42,43,44,45,46,47,48.
Density functional theory
To figure out why is that the NSIs modified film has lower polarization loss and higher \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\), the interfacial molecular model of Co3O4 and P(VDF-HFP) is established for first-principles calculation (Fig. 3a–h). Nowadays, most of the studies on DFT so far are carried out under simplified vacuum background without considering actual operational environment for insulation dielectrics materials that are long-term exposed to high \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\), which might lead to inaccurate results4. So, DFT is used to study the polymer adsorption on the Co3O4(110) surface with the electric field effects. In the Fig. 3a, Co2+ and Co3+ are in the tetrahedral and octahedral oxygen surrounding, respectively. Co2+ and Co3+ are in the top layer of the stable Co3O4(110) in the Fig. 3c and d. To simplify the polymer and Co3O4(110) surface interaction, only one unit molecule as shown in Fig. 3b is used for the adsorption study. The F atom is the electron donor comparing with H and C atom. We first find the binding site at 0.00 eV/Å. The molecule binds with Co2+ with F-Co bond distance 2.18 Å in Fig. 3e, f. For the Co3+ binding, the F atom of the molecule is shared by two Co3+ with F-Co distance 2.602 and 2.885 Å (Fig. 3g, h). The adsorption energy (\({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ads}}}}}}}\)) are −0.79 and −1.08 eV with F atom binding with Co2+ and Co3+, respectively. Generally, the shorter binding distance, the stronger binding. In our case, the molecule prefers to bind with Co3+. We speculate there are two reasons, one is the positive charge on metal atom, the other is unsaturated coordination. The positive charge on the Co3+ is of course bigger than the Co2+. The coordination number of Co2+ and Co3+ are 4 and 6 in the bulk, respectively. Once, in the top layer of surface, the coordination number of Co2+ and Co3+ change to 3 and 4. The internal electric field is formed with a large electrostatic potential difference ΔE 12.33 eV in Fig. 3i, signifying the active charge transfer4. The disordered macromolecular chain in the amorphous phase of the P(VDF-HFP) film is more susceptible to steering polarization, which is the main part of polarization loss49. It is obtained that nanofillers are in direct contact with the amorphous polymer molecular chains from the previous characterization. The formation of F-Co3+ bond results in enhanced binding between nanofiller and macromolecule (» the van der Waals force). This allows the orientation polarization loss to be well suppressed, which well accounted for the introduction of high \({{{{{\rm{K}}}}}}\) inorganic nanofillers at low doping content leading to the reduction of polarization losses. Supplementary Table 4 demonstrates that there are electrons transfer (7.3 \({{{{{\rm{\mu }}}}}}\)C/m2) from Co3O4(110) surface to the adjoining polymer molecular layer (denoted as inner interface layer) when the \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\) = 0 MV/m. An increase in the charges on the polymer molecules results in enhanced molecular polarization. However, there are differences in charge transfer between them under different intensities and orientations of \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\), which leads to various magnitudes of molecular polarization in the inner interface layer (Fig. 3j). Based on the DFT calculation results, we revise the interface model in the next FES work. Furthermore, there are abundant deficiencies such as unsaturated/broken bonds on the surface of the Co3O4 NSIs. If the new energy levels introduced by these defects exist in the energy gap between valence band and conduction band, it will trap electrons or holes. Shallow traps are formed near the bottom of the conduction band or the top of the valence band27. As illustrated in Supplementary Fig. 23, the surface of Co3O4 nanomaterials contains both deep and shallow traps.
Finite element simulation
The above analysis provides a well interpretation for the suppressed polarization loss of the nanocomposites, but it is still ambiguous why the 15@NSIs-0.008 wt% film has the highest \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\). It is generally accepted that the charge carrier transport and \({{{{{\rm{E}}}}}}\) distortion are essential factors in the performance of insulating materials50. So, we simulate the steady-state internal \({{{{{\rm{E}}}}}}\) and potential (\({{{{{\rm{V}}}}}}\)) distribution of the interfacial corrected dielectric model by using finite element computations (Fig. 4, and Supplementary Note 6). The potential contours and \({{{{{\rm{E}}}}}}\) distribution in the selected vertical cross-section surface at the NSIs centrum (Supplementary Fig. 26) are plotted in P(VDF-HFP) substrate excited by a \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\) = 200 MV m−1. Compared to the nanosheet and nanoparticle, it can be seen that the equipotential lines close to nano-sieve boundary are meandering due to the existence of mesoporous, which indicates the \({{{{{\rm{V}}}}}}\) and \({{{{{\rm{E}}}}}}\) distributions are intricate in this area (Fig. 4a, b, Supplementary Figs. 25b and 27). The non-uniform \({{{{{\rm{E}}}}}}\) and \({{{{{\rm{V}}}}}}\) distribution could produce crucial electric stress on charges and change their transport paths. In order to visually understand the potential trap and \({{{{{\rm{E}}}}}}\) distribution near NSIs surface, the \({{{{{\rm{normE}}}}}}\) and \({{{{{\rm{V}}}}}}\) data of local horizontal plane (0.5 nm from the inner interface layer, Supplementary Fig. 28) are extracted and three-dimensional (3D) plotted. As shown in Fig. 4d, the \({{{{{\rm{E}}}}}}\) in the region matched up with the sieve pores is weakened, while the \({{{{{\rm{E}}}}}}\) in the surface region corresponding to the Co3O4 skeleton is enhanced, resulting in a 3D tubular-like cavity array of electric field. The \({{{{{\rm{E}}}}}}\) cavity distribution makes the potential in the outer interface layer present a sub-macroscopic potential distribution array (Fig. 4e). The \({{{{{\rm{E}}}}}}\) cavity effect is effective in the range of 0–10 nm around the interface (Supplementary Figs. 30, and 31). When a positive ion transport from positive to negative electrode, the ion would move toward the pore of nano-sieves, acting like a trap. The same is true for negative charges. To distinguish it from the intrinsic defect trap, the potential distribution caused by uneven \({{{{{\rm{E}}}}}}\) are called “sub-macro potential trap array” (V). A series of comparative 3D graphs of \({{{{{\rm{normE}}}}}}\) and \({{{{{\rm{V}}}}}}\) of NPs, nanosheets, and nano-sieves with different pore sizes are shown in Supplementary Fig. 25. The15@NSIs in polymer substrate excited by external \({{{{{\rm{E}}}}}}\) generates the largest and most sophisticated interface area with alternating configuration of suitable deep and shallow potential traps array, which might be the critical element why the 15@NSIs-0.008 wt% has the highest \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) performance. Relative potential difference (\({{{{{{\rm{V}}}}}}}_{{{{{{\rm{r}}}}}}}\)) and electric field distortion rate (\({{{{{\rm{\xi }}}}}}\)) are employed to provide a quantitative description of potential traps depth and \({{{{{\rm{E}}}}}}\) deformity, respectively. The \({{{{{{\rm{V}}}}}}}_{{{{{{\rm{r}}}}}}}\) and \({{{{{\rm{\xi }}}}}}\) generated by the nanoparticle are 0.31 V and 40%. The \({{{{{{\rm{V}}}}}}}_{{{{{{\rm{r}}}}}}}\) generated by the 2D nanomaterials is reduced to ~0.21 V, but the \({{{{{\rm{\xi }}}}}}\) value is decreased by half. \({{{{{{\rm{V}}}}}}}_{{{{{{\rm{r}}}}}}}\) and \({{{{{\rm{\xi }}}}}}\) are negatively correlated. What we pursue is more potential traps and lower \({{{{{\rm{\xi }}}}}}\). At this point, the emergence of 2D porous sieve nanomaterials could satisfy these two demands. This could be the critical factor for the world-leading insulation performance modification of 15@NSIs-0.008 wt% in this experiment.
Discussion
In this paper, homogeneous Co3O4 nano-sieves (NSIs) with different pore sizes and NPs are synthesized by hydrothermal method, and well-dispersed P(VDF-HFP)-based nanocomposites films with trace doping concentration are fabricated by serial dilution and casting methods. The most impressive electrical performance (\({{{{{{\rm{E}}}}}}}_{{{{{{\rm{b}}}}}}}\) = 803.3 MV m−1, \({{{{{\rm{\eta }}}}}}\,\) = 90%, and \({{{{{{\rm{U}}}}}}}_{{{{{{\rm{e}}}}}}}\) = 41.6 J cm−3) is achieved by the nanocomposites film with 15 nm pore size nano-sieves at 0.008 wt% doping amount (denoted as 15@NSIs-0.008 wt%). The 80% dielectric strength improvement is 2.7 times that of NPs-0.008 wt% film, which surpasses almost state of art reported nano-modified dielectrics. But what is more noticeable is that its \({{{{{\rm{\eta }}}}}}\) is close to 90% at any electric field, comparable with linear dielectric, which is superior to pure film (75%) and most other products in its class. First-principles calculation suggests the existence of charge transfer between F and Co3+, restraining the orientation polarization of linked macromolecules, which could be well accounted for the decreased polarization losses and \({{{{{\rm{K}}}}}}\) of the composites film after introducing high \({{{{{\rm{K}}}}}}\) nanofillers. The \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\) context is considered into insulating dielectric DFT for the first time, and it is found that the polymer chain attached to the Co3O4 (denoted as inner interface layer) receives electrons from the surface of nanomaterial to enhance the molecular polarization. While the charge transfer between them is influenced by \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\) resulting in divergence polarization at different interface sites. Based on this, we divide the inner interface layer in FES model into upper and lower layers and revise their parameters. The simulation demonstrates that the electric field (\({{{{{\rm{E}}}}}}\)) cavity array caused by the 2D nano-sieve structure and material difference produces a micron-scale non-uniform potential distribution array in the outer interface layer. This potential array plays a trap-like role in acceleration or buffering free charge carriers, causing the carriers to move toward the sieve holes, named as “sub-macro potential trap array”. Impressively, the sub-macro potential trap array could be tuned by the size and distribution of mesoporous in 2D nanomaterials. This might be the rational interpretation for the nano-sieves doped film achieving such a remarkable modification effect.
The \({{{{{\rm{E}}}}}}\) cavity array and sub-macro potential trap array is induced by nano-sieves in the outer interface layer under high \({{{{{{\rm{E}}}}}}}_{{{{{{\rm{ex}}}}}}}\) modulating the free carriers’ transport. The combination of sub-macro potential trap array with intrinsic defect traps on Co3O4 active surface diminishes high-speed moving ions or electrons in insulating dielectric, hinders the discharge channels’ formation, hugely improves the breakdown resistance of the nanocomposite films. Meanwhile, the polarization losses are suppressed since the depressed macromolecule orientation polarization in the inner interface layer and the large specific surface area of nano-sieves. The 2D nanomaterial structure design that we developed to improve overall dielectric energy storage performance should be applicable to other material systems and nanocomposites. It may also be helpful for other attempts to elucidate the modification mechanism.
Methods
Reagents
Ethylene glycol (EG) (99%, Adamas,), aqueous ammonia (NH3·H2O,) (29%, Adamas), cobalt nitrate hexahydrate (Co(NO3)2·6H2O) (99.99%, Sigma-Aldrich), sodium carbonate (Na2CO3) (99.8%, Fisher), N,N-Dimethylformamide (DMF) (99.8%, J.T.Baker), Poly(vinylidene fluoride-co-hexafluoropropylene) (P(VDF-HFP)) (Kynar Flex 2801, 10%). All the reagents are used as received. Deionized water (~18.2 MΩ cm−1) is employed throughout the study.
Synthesis of 2D Co3O4 nano-sieves with different pore sizes
In a typical preparation of Co3O4 nano-sieves with a mean pore size of 15 nm, denote as 15@Co3O4 NSIs, 12.5 ml NH3·H2O and 15 ml EG are evenly mixed in a 50 ml beaker, then 3 ml 1 M Na2CO3 solution is added and form homogeneous solution after 2 min of stirring. Afterwards, 5 ml 1 M aqueous cobalt nitride solution is added to the above mixed solution stirring for 20 min. The resulting homogeneous purple blends are transferred into a 50 ml Teflon-lined stainless steel autoclave for sealing and fixation, which is then heated in a temperature-preset oven at 170 °C for 1020 min. After the autoclave naturally cools down to room temperature, the precipitation is centrifuged and rinsed at least 4 times by deionized water and then once with ethanol. Finally, the products are dried in a 60 °C of vacuum oven overnight and calcined in a program-controlled muffle furnace at 450 °C with a ramp rate of 1 °C/min.
The amounts of precursors and calcination temperature required for the synthesis of Co3O4 nano-sieves with other pore sizes and morphology are as follows.
5@Co3O4 NSIs: 12.5 ml NH3·H2O, 16 ml EG, 2 ml 1 M Na2CO3 and 5 ml 1 M Co(NO3)2, 250 °C.
25@Co3O4 NSIs: 12.5 ml NH3·H2O, 12 ml EG, 5 ml 1 M Na2CO3 and 5 ml 1 M Co(NO3)2, 350 °C.
50@Co3O4 NSIs: 12.5 ml NH3·H2O, 11 ml EG, 7 ml 1 M Na2CO3 and 5 ml 1 M Co(NO3)2, 550 °C.
Co3O4 nanoparticles: 12.5 ml NH3·H2O, 12.5 ml deionized water, and 5 ml 1 M Co(NO3)2, 250 °C.
Film sample fabrication
The classic solution-casting method is employed in this study to prepare dielectric film. To make low-concentration nanocomposites film, 1 g of P(VDF-HFP) powers are firstly dissolved into 20 ml of DMF solvent with vigorous stirring for 2 h to obtain a homogeneous transparent solution A. 8 mg of Co3O4 nanomaterial is dispersed in 20 ml of DMF: acetone = 1:1 solvent in a 20 ml glass bottle, under sonicated for 2 h and stirred 0.5 h to form a uniform suspension B. Following that, a certain amount of X (X = 20, 200, and 2000 ul) of B is added into solution A to obtain a mixed solution with different concentrations of Co3O4 nanomaterial, corresponding to 0.0008 wt%, 0.008 wt%, and 0.08 wt% respectively. After sonication for 2 h and stirring for 12 h, the mixture is cast onto a clean and flat quartz glass plate (cleaned with isopropanol and ethanol (1:1)) and dried at 40 °C thermostat for 3 h. Afterwards, the glass plate is transferred to a 120 °C vacuum oven for 8 h to allow the solvent to evaporate completely. Finally, the flexible film is peeled off after soaking in ice water for 3 min. Film thickness is controlled by concentration of P(VDF-HFP). The thickness of all the films used for electrical tests is 15–20 um.
Pure P(VDF-HFP) and high-concentration nanocomposites films are fabricated with identical processes, except that the method of obtaining the mixed solution before casting is different. For 0.8 wt% and 3 wt% doping concentration, 8 mg and 30 mg of the Co3O4 nanomaterial are weighed and added directly to the A solution. For pure film, solution A could be used directly.
Characterization
The morphology and structure of nano-fillers and films are determined by field emission scanning electron microscopy (FSEM, JEOL JSM-7800F, 10 kV), X-ray diffraction (XRD, PANalytical X’Pert Powder with Cu Kα radiation), transmission electron microscopy (TEM, FEI, Talos F200S, 200 kV). X-ray photoelectron spectroscopy (XPS, ESCALAB250) and BET surface area measurement (BET, Quantachrome Autosorb-2MP) are adopted to analyze the surface element valence and surface area and pore size of Co3O4 nano-sieves. Fourier-transform infrared spectra (FTIR, Nicolet iS50) is performed from 400 to 4000 cm−1. Differential scanning calorimetry (DSC, Netzsch. Ltd DSC 404 F3) is conducted at a heating/cooling rate of 10 °C min−1. Thermogravimetric analysis (TGA, MERRLER TOLEDO TGA2) test is carried out with a heating rate 10 °C min−1 from ~30 °C to 700 °C under nitrogen atmosphere.
Electrical measurement
Gold electrodes of diameter 2 mm and thickness of 50 nm are sputtered on both sides of the polymer films by using a high vacuum coater (Leika EM ACE 600). Frequency-dependent dielectric spectras over the frequency range between 0.1 Hz and 1 MHz at room temperature are collected with a Concept 80 broadband dielectric spectrometer (Novocontrol Technologies GmbH & Co. KG, Hundsangen, Germany). High-field electric displacement-electric field (D-E) loops are measured using a ferroelectric test system (aixACCT-TF Analyzer 2000) with a triangular unipolar wave under 50 Hz at room temperature. Dielectric breakdown strength tests are carried out with DC voltage at a ramping rate of 200 V s−1 and a limiting current of 5 mA using a KEYSIGHT 33500B as the signal generator and a TREK P0621P as voltage amplifier.
Data availability
The data that support the findings of this study are available from the corresponding author upon request. The data and code are available on request or specifying the conditions of access. Source data are provided as a Source data file. Source data are provided with this paper.
References
Gur, T. M. Review of electrical energy storage technologies, materials and systems: challenges and prospects for large-scale grid storage. Energy Environ. Sci. 11, 2696–2767 (2018).
Wang, W. & Li, S. Research status and development of insulation breakdown in engineering solid dielectrics. Chin. Sci. Bull. 65, 14 (2020).
Chen, X. et al. Energy-saving superconducting power delivery from renewable energy source to a 100-MW-class data center. Appl. Energy 310, 118602 (2022).
Pan, H. et al. Ultrahigh–energy density lead-free dielectric films via polymorphic nanodomain design. Science 365, 578–582 (2019).
Jiang, Y. et al. Ferroelectric polymers and their nanocomposites for dielectric energy storage applications. APL Mater. 9, 020905(2021).
Luo, H. et al. Interface design for high energy density polymer nanocomposites. Chem. Soc. Rev. 48, 4424–4465 (2019).
Behera, R. & Elanseralathan, K. A review on polyvinylidene fluoride polymer based nanocomposites for energy storage applications. J. Energy Storage 48, 103788 (2022).
Lewis, T. J. Nanometric dielectrics. IEEE Trans. Dielectr. Electr. Insul. 1, 812–825 (1994).
Feng, Q.-K. et al. Recent progress and future prospects on all-organic polymer dielectrics for energy storage capacitors. Chem. Rev. 122, 3820–3878 (2021).
Takada, T., Hayase, Y., Tanaka, Y. & Okamoto, T. Space charge trapping in electrical potential well caused by permanent and induced dipoles for LDPE/MgO nanocomposite. IEEE Trans. Dielectr. Electr. Insul. 15, 152–160 (2008).
Li, L. et al. Significant improvements in dielectric constant and energy density of ferroelectric polymer nanocomposites enabled by ultralow contents of nanofillers. Adv. Mater. 33, 2102392 (2021).
Liang, J. et al. Research Progress of In-situ Testing of the Interfacial Region in Dielectric Polymer Nanocomposites. Proc. CSEE 42, 10 (2022).
Dang, Z.-M., Zheng, M.-S. & Zha, J.-W. 1D/2D Carbon Nanomaterial-Polymer Dielectric Composites with High Permittivity for Power Energy Storage Applications. SMALL 12, 1688–1701 (2016).
Prateek, Thakur,V. K. & Gupta R. K. Recent Progress on Ferroelectric Polymer-Based Nanocomposites for High Energy Density Capacitors: Synthesis, Dielectric Properties, and Future Aspects. Chem. Rev. 116, 4260–4317 (2016).
Li, Q. et al. High-temperature dielectric materials for electrical energy storage. Annu. Rev. Mater. Res. 48, 219–243 (2018).
Yang, Y. et al. Self-healing of electrical damage in polymers using superparamagnetic nanoparticles. Nat. Nanotechnol. 14, 151–155(2019).
Xu, F. et al. Seeking optimized transformer oil-based nanofluids by investigation of the modification mechanism of nano-dielectrics. J. Mater. Chem. C. 8, 7336–7343 (2020).
Ji, S. et al. High dielectric performances of flexible and transparent cellulose hybrid films controlled by multidimensional metal nanostructures. Adv. Mater. 29, 1700538 (2017).
Liu, F. et al. High‐energy‐density dielectric polymer nanocomposites with trilayered architecture. Adv. Funct. Mater. 27, 1606292(2017).
Zhang, T. et al. A highly scalable dielectric metamaterial with superior capacitor performance over a broad temperature. Sci. Adv. 6, eaax6622 (2020).
Li, Q. et al. Flexible high-temperature dielectric materials from polymer nanocomposites. Nature 523, 576–579 (2015).
Wang, P.-J. et al. Significantly enhanced electrostatic energy storage performance of P (VDF-HFP)/BaTiO3-Bi(Li0.5Nb0.5)O-3 nanocomposites. Nano Energy 78, 105247 (2020).
Dang, Z. M., Yuan, J. K., Yao, S. H. & Liao, R. J. Flexible nanodielectric materials with high permittivity for power energy storage. Adv. Mater. 25, 6334–6365 (2013).
Tan, D. Q. The search for enhanced dielectric strength of polymer‐based dielectrics: a focused review on polymer nanocomposites. J. Appl. Polym. Sci. 137, 49379 (2020).
Yuan, C. et al. Polymer/molecular semiconductor all-organic composites for high-temperature dielectric energy storage. Nat. Commun. 11, 1–8 (2020).
Teyssedre, G., Zheng, F., Boudou, L. & Laurent, C. Charge trap spectroscopy in polymer dielectrics: a critical review. J. Phys. D: Appl. Phys. 54, 263001 (2021). (263030pp).
Ran, Z. Y., Du, B. X., Xiao, M., Liu, H. L. & Xing, J. W. Dielectric Property Improvement of Polypropylene Films Doped with POSS for HVDC Polymer Film Capacitors. IEEE Trans. Dielectr. Electr. Insul. 28, 1308–1316 (2021).
Nørskov, J. K., Abild-Pedersen, F., Studt, F. & Bligaard, T. Density functional theory in surface chemistry and catalysis. Proc. Natl Acad. Sci. 108, 937–943 (2011).
Pinder, G. F. & Gray, W. G. Finite element simulation in surface and subsurface hydrology. (Elsevier, 2013).
Huang, X., Sun, B., Zhu, Y., Li, S. & Jiang, P. High-k polymer nanocomposites with 1D filler for dielectric and energy storage applications. Prog. Mater. Sci. 100, 187–225 (2019).
Sun, Q. et al. Achieving high energy density and discharge efficiency in multi-layered PVDF-PMMA nanocomposites composed of 0D BaTiO3 and 1D NaNbO3@SiO2. J. Mater. Chem. C. 8, 7211–7220 (2020).
Chen, J. et al. Chemical adsorption on 2D dielectric nanosheets for matrix free nanocomposites with ultrahigh electrical energy storage. Sci. Bull. 67, 609–618 (2022).
Raman, V. et al. Synthesis of Co3O4 nanoparticles with block and sphere morphology, and investigation into the influence of morphology on biological toxicity. Exp. Ther. Med. 11, 553–560 (2016).
Speakman, S. A. Estimating crystallite size using XRD. MIT Cent. Mater. Sci. Eng. 2, 14 (2014).
Gu, M., Zhang, J., Wang, X., Tao, H. & Ge, L. Formation of poly (vinylidene fluoride)(PVDF) membranes via thermally induced phase separation. Desalination 192, 160–167 (2006).
Tiwari, V. & Srivastava, G. Effect of thermal processing conditions on the structure and dielectric properties of PVDF films. J. Polym. Res. 21, 1–8 (2014).
Makhlouf, S. A., Bakr, Z. H., Aly, K. I. & Moustafa, M. S. Structural, electrical and optical properties of Co3O4 nanoparticles. Superlattices Microstruct. 64, 107–117 (2013).
Roy, M. et al. Polymer nanocomposite dielectrics-the role of the interface. IEEE Trans. Dielectr. Electr. Insul. 12, 629–643 (2005).
Yan, H. et al. The contribution of electrical conductivity, dielectric permittivity and domain switching in ferroelectric hysteresis loops. J. Adv. Dielectr. 1, 107–118 (2011).
Zhang, X. et al. Giant energy density and improved discharge efficiency of solution‐processed polymer nanocomposites for dielectric energy storage. Adv. Mater. 28, 2055–2061 (2016).
Mj, K. K. & Kalathi, J. T. Investigation on the dielectric performance of PVDF-HFP/LZO composites. J. Alloy. Compd. 843, 155889 (2020).
Ma, G. et al. Improved dielectric and energy storage properties of polymer composites with BNNSs/AgNPs hybrid nanofiller. Mater. Technol. 37, 2158–2165 (2022).
Xie, X. et al. Ultralow-Content (Bi0. 5Na0. 5) TiO3–NaNbO3/PVDF-HFP Nanocomposites for Ultrahigh-Energy-Density Capacitor Applications. ACS Appl. Energy Mater. 5, 7651–7660 (2022).
Wang, H. et al. Enhanced dielectric property and energy storage density of PVDF-HFP based dielectric composites by incorporation of silver nanoparticles-decorated exfoliated montmorillonite nanoplatelets. Compos. Part A: Appl. Sci. Manuf. 108, 62–68 (2018).
Zhang, X. et al. Ultrahigh energy density of polymer nanocomposites containing BaTiO3@ TiO2 nanofibers by atomic‐scale interface engineering. Adv. Mater. 27, 819–824 (2015).
Li, H. et al. Enabling high‐energy‐density high‐efficiency ferroelectric polymer nanocomposites with rationally designed nanofillers. Adv. Funct. Mater. 31, 2006739 (2021).
Huang, X. et al. Non-intuitive concomitant enhancement of dielectric permittivity, breakdown strength and energy density in percolative polymer nanocomposites by trace Ag nanodots. J. Mater. Chem. A 7, 15198–15206 (2019).
Chen, H. et al. Enhanced energy density in sandwich-structured P (VDF-HFP) nanocomposites containing Hf0. 5Zr0. 5O2 nanofibers. Chem. Eng. J. 436, 131123 (2022).
Zhang, X. et al. Achieving high energy density in PVDF-based polymer blends: suppression of early polarization saturation and enhancement of breakdown strength. ACS Appl. Mater. Interfac. 8, 27236–27242 (2016).
Su, J., Du, B., Li, J. & Li, Z. Electrical tree degradation in high‐voltage cable insulation: progress and challenges. High. Volt. 5, 353–364 (2020).
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China (NSFC, Grant No. U19A20100, 21971027), Thousand Young Talents Program of the Chinese Central Government (Grant No. 0220002102003) and Project 111 (BP0820005).
Author information
Authors and Affiliations
Contributions
Y.W. and F.X. conceived the concept and devised the experimental program; F.X., Y. L., and Y. H. performed research; F.X. and C. L. analyzed data; all co-authors commented on the paper, F.X. and Y. W. wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Taha Abdel Mohaymen Hemaida and Wenying Zhou for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xu, F., Li, Y., Zou, Q. et al. The electric field cavity array effect of 2D nano-sieves. Nat Commun 13, 7887 (2022). https://doi.org/10.1038/s41467-022-35623-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-35623-5