Abstract
Suzuki cross-coupling reactions catalyzed by palladium are powerful tools for the synthesis of functional organic compounds. Excellent catalytic activity and stability require negatively charged Pd species and the avoidance of metal leaching or clustering in a heterogeneous system. Here we report a Pd-based electride material, Y3Pd2, in which active Pd atoms are incorporated in a lattice together with Y. As evidenced from detailed characterization and density functional theory (DFT) calculations, Y3Pd2 realizes negatively charged Pd species, a low work function and a high carrier density, which are expected to be beneficial for the efficient Suzuki coupling reaction of activated aryl halides with various coupling partners under mild conditions. The catalytic activity of Y3Pd2 is ten times higher than that of pure Pd and the activation energy is lower by nearly 35%. The Y3Pd2 intermetallic electride catalyst also exhibited extremely good catalytic stability during long-term coupling reactions.
Similar content being viewed by others
Introduction
Palladium-catalyzed Suzuki cross-coupling reactions have drawn considerable attention as a powerful tool for carbon-carbon bond formation, and are extensively used in organic synthesis chemistry1,2,3,4. To overcome the high activation barriers of the substrates, electron-rich active sites have been proposed in most homogeneous palladium catalysts by the introduction of electron-donating ligands5. However, the use of costly and potentially toxic palladium complexes and ligands remains a controversial issue with respect to sustainable chemical industry6. In contrast, heterogeneous catalysts are preferred over homogeneous catalysts due to their facile reusability and compatibility with flow systems7,8,9,10,11. There have been numerous efforts to develop heterogeneous catalysts for Suzuki cross-coupling reactions, and most of them are based on the design of palladium clusters or nanoparticles with highly electron-donating supports, photogenerated electrons or hot electrons in heterojunctions9,10,11,12,13,14. In particular, Pérez-Ramírez et al. recently developed single-atom catalysts, in which isolated Pd atoms anchored into the exfoliated graphitic carbon nitride, attract considerable attention due to its excellent activity and stability towards Suzuki cross-coupling reaction, surpassing the performance of state-of-the-art homogeneous catalysts and other conventional heterogeneous catalysts15. Electron-rich isolated palladium sites with high electron donation ability generally exhibit excellent catalytic activity for Suzuki cross-coupling reactions16,17,18,19,20. However, the stability issue for the loaded palladium catalyst particles has not yet been resolved; severe particle aggregation and/or leaching of active Pd sites on the catalyst surface during the reaction leads to poor recyclability21,22,23. There are few approaches to significantly enhance the activity and stability of heterogeneous palladium-based catalysts because the electron density of the active metal is not easily stabilized.
Recently, Nørskov and colleagues reported active and stable cathode catalysts of Pt alloyed with early transition metals, such as lanthanum, scandium, or yttrium for electrocatalytic oxygen reduction reaction24,25,26,27. When these alloys are used, the binding energy of the oxygen containing species on Pt can be modified moderately by changing the electronic structure of the active Pt sites28,29,30,31. Our group recently reported that ternary intermetallic compounds (LaCu0.67Si1.33 and LaCoSi) have a unique activation ability for H2 and N2 molecules, and thus exhibit excellent catalytic activity for the chemoselective hydrogenation reaction and ammonia synthesis, respectively32,33. These intermetallic compounds host solid active sites, high carrier densities, and low work functions (LWFs). The combination of rare earth metal and active transition metal can also induce charge transfer from the rare earth metal to the transition metal, which results in negatively charged active sites. As a consequence, electron transfer from the catalyst to the lowest unoccupied molecular orbitals (LUMOs) of absorbed molecules can be realized, which leads to weakening of the chemical bonds of the absorbed molecules and enables molecular dissociation with lower activation energy (Ea)34,35,36,37. Inspired by these developments, we have attempted to design a Pd-based intermetallic electride that should have both solid Pd sites and strong electron donation ability associated with a high carrier density and a LWF.
Herein, we propose a Pd-based electride, Y3Pd2, as an efficient catalyst for Suzuki cross-coupling reactions. The work function of Y3Pd2 (ΦWF ≈ 3.4 eV) is comparable to that of metallic yttrium (ΦWF ≈ 3.3 eV); however, Y3Pd2 is stable in air and under the reaction conditions for Suzuki cross-coupling. The measured carrier density is ne ≈ 1 × 1022 cm−3, which is much higher than that for oxide and carbon supports. Together with the negatively charged Pd, associated with different electronegativity between yttrium and palladium, Y3Pd2 exhibits stable and high catalytic activity for Suzuki cross-coupling reactions. The high carrier density and LWF for Y3Pd2 enable the activation of aryl halides with a significantly reduced Ea (about 35% less) compared with that for a pure Pd catalyst, and the turnover frequency (TOF) and recycle number exceed those for other reported Pd-based heterogeneous catalysts under similar reaction conditions. We consider that the electron transfer from the negatively charged Pd to aryl halides could be the key factor for the dissociation of aryl halides and the intrinsic catalytic ability of the active Pd sites involved was significantly enhanced in the Y3Pd2 intermetallic electride material.
Results
The crystal and electronic structures of Y3Pd2
Y3Pd2 crystallizes with a trigonal structure (Fig. 1a), and can be synthesized using arc-melting and subsequent annealing (Supplementary Fig. 1). The obtained powder are ductile and air-water stable. One specific feature of Y3Pd2 is the presence of interstitial sites. As depicted as X1, X2, and X3 in Fig. 1, yttrium atoms form Y4 tetrahedral and Y6 octahedral cages. The Y–Y distances for the Y6 octahedra and Y4 tetrahedra are 3.73 and 3.80 Å, respectively, which is very close to that of the Y5Si3 electride (3.78 Å)38. Consequently, large volumes of Y4 tetrahedral and Y6 octahedral cages are realized in Y3Pd2, and thus the X1, X2, and X3 sites can be considered as periodically distributed cavities. Bader charge analysis using pseudo atoms of these interstitial sites revealed that 0.87, 1.05, and 1.05 electrons are confined in the X1, X2, and X3 sites to give a formal valence state of [Y3Pd2]+:e‒, which is consistent with the electride concept. Motivated by the presence of interstitial sites, we conducted DFT calculations to clarify the electronic structure. Figure 1b shows that Y3Pd2 exhibits a metallic band structure. The electronic bands near the Fermi level are partially associated with empty X1, X2, and X3 sites (Supplementary Fig. 2). The chemical environments of the X2 and X3 sites are similar; therefore, these components (green and blue dots) occupy the same positions in the band structure (Supplementary Fig. 3). Partial electron density analysis also shows that the interstitial sites accommodate anionic electrons (Supplementary Fig. 3). These results indicate that the X1, X2, and X3 sites are electrically active, which supports the electride concept in Y3Pd2. The DFT calculation also showed the electron transfer from yttrium to palladium, pushing down the d-band center of Y3Pd2 (Supplementary Fig. 2). Thus, by combing with ductile nature, the co-existence of ionic and metallic bond interactions can be expected in Y3Pd2, which should benefit to realize a solid Pd sites.
a Crystal structure of stoichiometric Y3Pd2. Y and Pd atoms are depicted as gray and orange balls, respectively. X1, X2, and X3 sites are indicated using black solid arrows. b Calculated band structure of stoichiometric Y3Pd2. The contributions of X1, X2, and X3 sites are indicated using red, green and blue dots, respectively. c Calculated work functions for the most stable surface, Y3Pd2(0001). The inset shows the 0001 surface of Y3Pd2. d Comparison of the Fermi level for Y3Pd2 and the unoccupied (LUMO) states for aryl halides, iodobenzene, and bromobenzene.
As predicted by the DFT calculations, Y3Pd2 exhibits metallic conductivity, and the carrier density was estimated to be ne ≈ 1 × 1022 cm−3, which is much higher than that for traditional oxides and carbon supports (Supplementary Fig. 4). Furthermore, the work function of Y3Pd2 (0001), the most stable surface, was calculated to be 3.4 eV (Fig. 1c, Supplementary Fig. 5), which is much smaller than that for pure Pd metal (ΦWF ≈ 5.1 eV, Supplementary Fig. 6), although very close to that for yttrium metal (ΦWF ≈ 3.3 eV, Supplementary Fig. 6). It should be noted that the oxidative addition of aryl halides is the first and the most important step in Suzuki cross-coupling reactions. As typical aryl halides, the estimated LUMO positions of iodobenzene and bromobenzene are around 4.2 eV and 4.4 eV below the vacuum level, respectively, and thus deeper than the Fermi level for Y3Pd2, but much shallower than that for pure Pd metal (see Fig. 1d). Therefore, the combination of active Pd sites and strong electron donation ability of Y provides surface electrons that are efficiently donated from Y3Pd2 to the LUMOs of adsorbed aryl halides molecules, which is expected to lower Ea for the breaking of C−X bonds (X = I and Br).
Catalytic performance evaluation for Suzuki coupling reactions
The couplings of phenylboronic acid with iodobenzene and bromobenzene are used as model reactions to study the reaction kinetics and catalytic activity. The data in Fig. 2a, b show the Suzuki coupling activity of Y3Pd2 and pure Pd metal catalysts. For both reactions, the Y3Pd2 catalyst exhibited rather higher reaction rates than those of pure Pd metals (Supplementary Fig. 7). This can be attributed to the introduced Y species that surrounds the Pd sites, which would significantly improve the catalytic activity. Due to the high quantities of the total Pd amount in the bulk of Y3Pd2, the turnover frequencies (TOFs) based on total Pd was firstly calculated to be 7.6 h−1, which is several times higher than that of pure Pd metal (0.9 h−1) with comparable particle size under the same conditions (Table S1, Supplementary Fig. 8). Ullmann homo-coupling of aryl halides can be excluded through the inactive solely iodobenzene coupling reaction and the carbon balance of both catalysts for Suzuki coupling reactions were estimated to be >98% (Supplementary Tables 1, 2). It should be noted that the catalytic reaction process often takes place on the surface of the catalyst and the activity solely depends on the surface exposed active sites. Here, the active ensembles of Pd-Y unit should be regarded as the surface active sites, which can be confirmed by our DFT calculations (see below Supplementary Fig. 14). Therefore, the TOFs were calculated based on each exposed Pd-Y sites. It is evident that the calculated TOFs for Y3Pd2 are one order of magnitude higher than those for the pure Pd metal catalyst (Supplementary Table 1). Impressively, in terms of TOFs, Y3Pd2 even outperforms other benchmarked commercial heterogeneous Pd catalysts (Pd/C, Pd/Al2O3, and Pd-Pb/CaCO3) by an order of magnitude (Supplementary Table 3). Such TOF values are also much higher than those of the most reported Pd-based heterogeneous catalysts, including Pd-based photon-assisted catalysts in Suzuki coupling systems under similar reaction conditions (Supplementary Tables 4, 5). Although the highest TOF value was kept by Pd2+-exchanged graphite oxide as a heterogeneous catalyst, the deactivation problem still cannot be avoided in heterogeneous system due to the agglomeration of the Pd nanoparticles9. However, in Y3Pd2, the incorporated Pd sites in the crystalline lattice can solve the re-deposition and agglomeration problems in Suzuki coupling reactions which will be discussed below.
a, b Suzuki coupling reaction rates (blue bars) and TOFs (red bars) over Y3Pd2 and pure Pd metal catalysts. c, d Apparent Eas for the Suzuki coupling reaction over Y3Pd2 and pure Pd metal catalysts. Reaction conditions: Pd (40 mol% relative to organohalide); 0.5 mmol organohalide, 0.8 mmol phenylboronic acid, 1.5 mmol K2CO3, 5 ml solvent, iodides 30 °C, bromides 60 °C.
While the coupling reaction of chlorobenzene with phenylboronic acid was also tested (Supplementary Table 6), the activity for forming diphenyl was lower than that of bromobenzene and iodobenzene. As widely known in Suzuki coupling reactions, the lower catalytic activity can be attributed to the stronger C−Cl bond of chlorobenzene than that of C−Br and C−I13. Thus, breaking C−Cl bond of chlorobenzene needs higher temperature, leading to a low activity between chlorobenzene and phenylboronic acid at mild condition. Here, used Y3Pd2 is the bulky material, and its specific surface area was much lower than previously studied catalytic system. However, we found the surface area of Y3Pd2 can be elevated by 8 times through a ball-mill treatment, and accordingly the reaction rate increased in proportion while TOFs remains largely unchanged (Supplementary Table 7 and Supplementary Figs. 9–11). This tendency revealed a very promising potential that the performance may be further improved, e.g., by supporting the material and/or nanocrystallization adjustment of the particle size.
Kinetic analysis
The kinetics of the Suzuki coupling over Y3Pd2 and pure Pd metal catalysts were then examined. Based on the organic halide conversion at the start of each reaction, Y3Pd2 always exhibited higher TOF values than pure Pd metal catalysts (Fig. 2), which implied high activity. Based on the initial reaction rate (r0) values at different reaction temperatures, a set of Arrhenius plots were produced by plotting lnr0 as a function of 1/T. The slope of the Arrhenius plot was used to calculate the apparent Ea for Y3Pd2 to be 48.4 kJ mol−1 for the Suzuki coupling of iodobenzene and phenylboronic acid (Fig. 2c), which was an Ea reduction of around 35% compared to that for pure Pd metal catalysts (74.2 kJ mol−1), which provides evidence that the Suzuki coupling reaction is highly promoted over Y3Pd2. Similarly, Ea for the coupling of bromobenzene (Fig. 2d) with phenylboronic acid over Y3Pd2 follows the same trend, with a reduction of Ea by about 30% compared with that for pure Pd metal catalysts. Furthermore, the dependence of r0 on the concentration of aryl halides and phenylboronic acid was examined to determine the kinetic reaction order. As shown in Supplementary Fig. 12, both reactions exhibited a first order relationship with respect to the aryl halide (iodo and bromo) concentration and almost a zero order dependence on the phenylboronic acid concentration. Therefore, the activation of aryl halides (iodo and bromo) acted as the rate controlling step over Y3Pd2. This is a commonly observed phenomenon for Suzuki cross-coupling reactions over both homogeneous and heterogeneous Pd based catalysts, i.e., the oxidative addition of the aryl halide is the rate-determining step for the catalytic cycle39,40,41. From these kinetic studies, the distinct apparent Ea values and reaction kinetic orders suggest that the enhanced activity for the Y3Pd2 catalyst compared to that for pure Pd metal exclusively originates from the promoted activation of the aryl halides. Corresponding DFT simulations was also examined to investigate the activation behaviors of aryl halides on the Y3Pd2 (0001) surface. The activation process of bromobenzene molecule proceeds with the calculated energy gain of 0.11 eV on Y3Pd2 (0001), much lower than that of 0.53 eV on Pd (111) (Supplementary Figs. 13, 14). It should be noted that the difference between the calculated and experimental values could be due to the effects which were not taken into account such as solvent effect42. Nevertheless, the distinct calculated activation energy difference reasonably agree with the experimental observations. Furthermore, the Bader charge analysis indicates an obvious charge transfer (~0.12 e−) from the Y3Pd2 (0001) surface to the adsorbed aryl halides via the active Pd site (Supplementary Table 8), which is favored for the electron donation to the antibonding orbitals of aryl halides. These results predicted that the activation step of carbon halogen bond on Y3Pd2 catalyst is remarkably enhanced, explaining the high performance on Suzuki coupling reactions.
Other different Y-Pd binary intermetallic compounds such as Y3Pd, Y3Pd4, and YPd3 were also investigated (Supplementary Fig. 15). It is noted that their Pd active sites were also negatively charged with low work function features (Supplementary Figs. 16, 17). We found that all of Y3Pd, Y3Pd4, and YPd3 show moderate reaction rates per catalyst weight for Suzuki coupling reaction. Unfortunately, they are much harder to crash than Y3Pd2, leading to lower surface area and reaction rates. On the other hand, their calculated TOFs are comparable to that of Y3Pd2, and nearly one order of magnitude higher than pure Pd metal (Supplementary Table 9). Kinetic study also demonstrated that these Y-Pd binary catalysts exhibit the similar activation energies for the Suzuki coupling reactions (Supplementary Fig. 18). These results well suggest the importance of the combination between Y and Pd species in terms of electron density modification, resulting in the significant enhancement of the catalytic activity.
Spectroscopy characterizations
To determine the origin of the superior activation of aryl halides on Y3Pd2, the electronic structure of the Pd species was further analyzed using X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopy. The results indicated that the absorption edge for the Pd species in intermetallic compounds was located at an even lower energy relative to that for the Pd foil, which implies that Pd is negatively charged in Y3Pd2 (see Fig. 3a). The EXAFS spectrum of the sample was also fitted well by the Y3Pd2 structure (Supplementary Fig. 19). The intrinsic loss factor S02 was obtained to be 1.2 showing that the sample consists of bulky Y3Pd2. This EXAFS fitting result is consistent with the powder X-ray diffraction (XRD) patterns (Supplementary Fig. 1). One might think why long range peaks at around 4 Å are missing. EXAFS FT simulations by FEFF calculations were performed for the ideal Y3Pd2 structure to check long range interactions43,44. The amplitude of each path has a fair value, and the sum of the amplitudes shows a strong peak at ~4 Å (Supplementary Fig. 20). However, when an experimental EXAFS FT is compared with calculated paths, the phases of the paths should be considered. The envelop function of the imaginary parts corresponds to the real EXAFS FT data. The sum of the imaginary parts of the paths and its envelop function are shown in Supplementary Fig. 21. It was revealed that the phases of long range paths are different each other, and the intensities of long range interactions are weakened.
The catalytic process only occurs on the surface of the catalyst; therefore, we also supplied the surface properties as determined by XPS. Figure 3b shows the XPS Pd 3d spectra with respect to the binding energy of Y3Pd2 and pure Pd metal. The obvious shifts of typical Pd 3d XPS peaks to lower energy further indicate the elevated electron density of Pd sites, while the Y 3d peaks gave a significant shift to higher energy compared to that for Y0 3d (Supplementary Fig. 22). Here, it should be noted that the generation of surface yttrium oxides can also be ruled out by the absence of Y–O bonds from the XPS O 1 s spectra of Y3Pd2 (Supplementary Fig. 23). The slightly larger full width at half maximum (FWHM) of Pd 3d XPS peaks in Y3Pd2 compared to pure Pd metal can be ascribed to the co-existence of lowly and fully coordinated Pd species on the surface and in the bulk respectively (Supplementary Fig. 24) which is also confirmed by the Bader charge analysis in Supplementary Table 8, in which the oxidation states of bulk Pd and surface Pd are –1.88 and –1.77, respectively. Bader charge analysis also indicate the oxidation states of the Pd and three different Y atoms (i.e., Y1, Y2, Y3) are –1.88 and +1.19, +1.19, +1.23, respectively, indicating an obviously electron transfer from Y to Pd in the Y3Pd2 intermetallic (see Supplementary Table 8). These observation combined with the XANES analysis results demonstrate the key role of the rare earth metal (Y) as an electron donor in modifying the electron density and thus the final catalytic activity of the Pd species.
Infrared (IR) spectroscopy has been reported to be a powerful technique for understanding the electronic effects related to adsorbed molecule activation processes on a solid catalyst. Therefore, to elucidate the interaction between the aryl halides and the catalyst, diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) spectra were measured for iodobenzene adsorbed on Y3Pd2 and pure Pd metal. The typical C–C stretching in the aromatic vibration bands (νC–C) are in the range of 1400–1600 cm−145,46. In the low-frequency region, the main peaks at around 996, 1014, and 1060 cm−1 can be assigned to trigonal ring breathing, out-of-plane C–H (γC–H) deformation and halogen-sensitive vibration, respectively46. Compared to pure Pd metal, the two frequencies at 1575 and 1473 cm−1 involved with the admixture of C–I deformation on Y3Pd2 exhibited an obvious redshift (see Fig. 3c). Moreover, a clear redshift was also observed for the C–I stretching vibration (1060 cm−1) for Y3Pd2 (see Fig. 3d). Both of these the redshifts imply that C–I bonds in the iodobenzene molecules are weakened by electron donation from Y3Pd2. Electropositive Y metal generally acts as an electron-donating ligand that increases the electron density of Pd, thereby favoring the back-donation of electrons to the antibonding orbitals of C–I, which accounts for the carbon halogen bond weakening.
Proposed reaction mechanism
Figure 4 shows our proposed mechanism for the Suzuki cross-coupling process catalyzed by Y3Pd2, based on the experimental results. Here, Y3Pd2 with high electron density of Pd and positively charged Y act as the adsorption sites for the aryl halide (iodobenzene or bromobenzene). Next, the C–X group with an electron withdrawing element X (X = I, Br) of the aryl halide molecules can be preferentially adsorbed on Yδ+-Pdδ− sites through strong electrostatic interaction. The negatively charged Pd served as the electron donation sites to weaken the C–X bond, resulting in a significantly suppressed Ea, which is confirmed to be the rate-determining step for the reaction. The subsequent reductive elimination and transmetallation processes are followed by the formation of the final coupling products. Although the detailed mechanism remains undetermined at this stage, it is important to emphasize that electron transfer from the negatively charged Pd to the aryl halide could be the key factor for activation of the aryl halide that results in high catalytic activity for the Suzuki coupling reactions.
Catalytic Stability
The recyclability of catalysts is one of the most important properties for practical applications. It is worth noting that bare Pd nanostructures or even supported Pd nanoparticles in conventional Suzuki coupling reactions typically suffer from a significant loss in activity because traditional heterogeneous Pd-based catalysts act by the release of small amounts of soluble Pd with the dissolution and re-deposition process, which often induced an aggregation of the loaded Pd species47,48,49. Thus far, recently studied Pd based heterogeneous catalysts could only be reused less than 10 times under mild alkaline conditions50,51. In the present work, under the same reaction conditions, Y3Pd2 could be recycled 20 times without loss of activity, which indicates much higher stability than other reported Pd-based heterogeneous catalysts (see Fig. 5a, Supplementary Tables 4, 5, stability test at low conversion level is also shown in Supplementary Fig. 25). Moreover, significant activity loss was observed on other benchmarked heterogeneous Pd catalysts (Supplementary Fig. 25) and a characteristic Pd particle size change on Pd/C evidenced degradation of the catalyst via metal agglomeration effect (Supplementary Fig. 26), which highlights the obstacle of the sustainability by using heterogeneous catalysts for Suzuki couplings in large scale. In Y3Pd2, XRD patterns for the used catalyst indicated no obvious change in the crystal structure (Fig. 5b). Most importantly, the XPS results also showed that the Pd species still existed in a negatively charged state, which suggests that the surface electronic structure of Y3Pd2 is extremely stable (Fig. 5c). Note that the reaction proceeds only in the presence of Y3Pd2, and no more coupling products can be produced after removal of the catalyst during the reaction process (Supplementary Fig. 27). Inductively coupled plasma (ICP) spectroscopy also revealed that Y and Pd species in the filtrate were below the detection limit (0.007 ppm). Scanning electron microscopy (SEM) observations and energy dispersive X-ray spectroscopy (EDX) analysis also revealed that Y3Pd2 did not undergo a change in morphology or composition (Supplementary Fig. 28). To shed light on the intrinsic stability of the Y3Pd2 system, d-band center shift, segregation energy and island formation energy were calculated based on DFT with the well-established methodology52. As shown in Supplementary Fig. 29, there is an obvious down-shift of the d-band center (–2.31 eV) for Y3Pd2 (0001) as compared with Pd (111) (–0.95 eV), indicating a relative lower dissolution potential of the Pd species in Y3Pd2, which accounts for the high stability during the catalytic reaction53. Moreover, the segregation of a Pd atom from the bulk towards the surface requires 1.79‒2.67 eV for Y3Pd2 (0001) (Supplementary Fig. 30), which is comparable to the values in Pd3S system54. Also, the formation of Pd islands is also not favored in our case, because the energies required for the exchange of Pd/Y atoms are sufficiently high (0.71‒2.25 eV), as shown in Supplementary Fig. 31. These large segregation and island formation energies are consistent with our initial assessment to Y3Pd2, in which Pd sites could be stabilized through ionic and metallic bonding within the Y3Pd2 lattice. These results well explain the excellent stability of the Y3Pd2 intermetallic electride catalyst.
a Recycling experiment for the Suzuki cross-coupling reaction over Y3Pd2. Reaction conditions: Pd (40 mol% relative to organohalide); 0.5 mmol iodide, 0.8 mmol phenylboronic acid, 1.5 mmol K2CO3, 5 ml solvent, 30 °C. b Powder XRD patterns for as-prepared and used (after 5, 10, 15, and 20 cycles) Y3Pd2 catalyst. c XPS Pd 3d spectra for the as-prepared and used (after 20 cycles) Y3Pd2 catalyst.
Scope of Suzuki coupling reaction
Aromatic and Aliphatic Alcohols. The reaction protocol was further extended to various aryl halides and boronic acids to verify the scope and activity of Suzuki coupling reactions catalyzed by Y3Pd2 (Table 1). All of the substituted iodobenzenes and bromobenzenes with varied functional groups could be converted to the corresponding coupled products in high yields, regardless of whether electron-donating (CH3, OCH3, and OH) or electron-withdrawing (F and CF3) substituents were present (Supplementary Figs. 32−41). The general applicability of Y3Pd2 for the coupling of three different types of arylboronic acids bearing electron-donating or electron-withdrawing substituents was also tested (Table 2). It is well known that boronic esters are also applicable to the Suzuki coupling reaction in place of boronic acids because of its high thermal stability and high solubility in organic solvents55. Y3Pd2 catalyst also exhibited a relatively high yield (88%) of biphenyl for the coupling of bromobenzene with phenylboronic acid pinacol ester (Supplementary Table 7 and Supplementary Fig. 42). The calculated TOFs (411.1 h−1) were comparable to that of reported Pd single-atom catalyst tested in flow system, while much higher than those of other reported heterogeneous catalysts tested in a batch reactor15. The results confirmed the general applicability of the Y3Pd2 catalyst with high chemoselectivity and functional group tolerance.
Discussion
Guided by the active sites integrated in the intermetallic electride concept, an intermetallic electride catalyst, Y3Pd2, was developed for Suzuki cross-coupling. The in situ stable intermetallic electride Y3Pd2 possesses both high carrier density and a LWF, and thus exhibit much higher catalytic activity than Pd metals and other conventional Pd based supported catalysts. Mechanistic studies demonstrated that negatively charged Pd sites induce electron injection into the antibonding orbitals of C–X, significantly promoting the activation of aryl halides, which is the rate-determining step for the investigated Suzuki cross-coupling reactions. Given the heterogeneous nature of the catalyst, Y3Pd2 could be easily separated and recycled for more than twenty cycles without significant loss in activity. Our results show the possibility of tailoring the electronic structure of active transition metals such as Pd by the formation of intermetallic compounds with early transition elements—an approach that should be broadly applicable for the tuning of catalytic properties.
Methods
Sample preparation
Elemental yttrium (ingot) and palladium (ingot and powder) used in this study were purchased from Kojundo Chemical Lab. Co., Ltd. (Japan), and directly used without any pretreatments. Y3Pd2 was directly synthesized by arc-melting yttrium and palladium ingots with the ratio of 3.1: 2 under an argon atmosphere. The ingot obtained was grounded using an agate motor in Ar filled glove box. The obtained powder was then pelletized and sealed into an argon filled stainless tube, and annealed at 900 °C for 90 h. Stainless tubes were sintered in nitrogen atmosphere in order to prevent their oxidation. Y3Pd, Y3Pd4, and YPd3 were prepared by arc-melting method similar with that for the preparation of Y3Pd2. Ball-milling of Y3Pd2 was conducted using heptane and ethanol as solvents under argon atmosphere, and the rotation rate was set to 150 rpm. In order to avoid overheating, Y3Pd2 was milled for 10 min with 10 min of interval, and this sequence was 10 times repeated. Pd/C, Pd/Al2O3, and Pd–Pb/CaCO3 used in this study were purchased from Sigma-Aldrich, and directly used without any pretreatments.
Physical property measurements
The electronic transport properties, magnetic susceptibility and heat capacity were measured using a physical property measurement system (PPMS) and a superconducting quantum interference device (SQUID) vibrating sample magnetometer (SVSM) from Quantum Design.
General procedure for Suzuki cross-coupling reactions
All reactions were conducted in a 25 ml stainless steel autoclave fitted with a glass mantel and a magnetic stirrer. In a typical reaction, 0.5 mmol organohalide, 0.8 mmol phenylboronic acid, 1.5 mmol K2CO3, and Pd (40 mol% relative to organohalide) catalyst were mixed in 5 ml of solvent. The autoclave was then flushed three times with Ar and reactions were performed in the autoclave at about 30–70 °C. The products were analyzed using gas chromatography (GC) and product identification was further confirmed from gas chromatography-mass spectrometry (GC-MS) measurements. The TOF was calculated from the reaction rate at a low conversion level derived from the number of Pd atoms exposed to the catalyst surface (Eqs. 1 and 2):
where n0 is the initial number of moles of substrate, C is the conversion of the substrate at reaction time t, ncat is the number of moles of Pd atoms exposed on the surface, mcat is the weight of the catalyst, NPd sites is the amount of exposed Pd atoms per gram of catalyst, and NA is Avogadro’s constant.
The number of moles of Pd atoms exposed on the surface was estimated by experimental measurement and theoretical prediction, respectively. For experimental measurement, the CO-pulse chemisorption (BELCAT-A, BEL, Japan) was measured at 50 °C using a He flow of 30 ml min−1 and pulses of 0.36 ml (9.88% CO in He). Prior to the analysis, the catalyst was treated with flowing Ar (50 ml min−1) at 400 °C for 30 min and then flowing He (50 ml min−1) at 400 °C for 15 min. To calculate the metal dispersion, a stoichiometry of Pd/CO = 1 was assumed. Because each Pd site was isolated by the surrounded Y atoms in the most stable surface Y3Pd2 (0001). The nearest separation between surface isolated Pd sites is ~0.43 nm, sufficiently longer than the bond length of CO molecule (~0.11 nm). In addition, the CO adsorption to Y powder was below the detection limit at the same condition. Therefore, it is reasonably assume each active ensemble of Pd-Y corresponds to one CO molecule. For theoretical prediction, both of the Pd atom numbers in one unit cell of Y3Pd2 crystal and surface area of the corresponding unit cell were calculated. Then the number of the Pd atoms per unit cell’s surface area were extended to the measured specific surface area of the experimentally prepared Y3Pd2 powder.
For the recycling study, the Suzuki coupling reaction was performed with organohalide and phenylboronic acid, maintaining the same reaction conditions as described above except using recycled catalyst. After each completion of the reaction, the catalyst powder was washed by ethanol with a certain amount of water several times to remove the organic and inorganic impurities from the used catalyst. Finally, the resultant powder was dried in a vacuum at room temperature, weighed, and reused in the next run.
Sample characterization
The crystal structure was analyzed using an X-ray powder diffractometer (D8 ADVANCE, Bruker) with monochromated Cu Kα radiation (λ = 0.15418 nm). Nitrogen sorption measurements (BELSORP-mini II, BEL) were performed to evaluate the Brunauer–Emmett–Teller surface area of the catalysts. The surface morphology of the catalyst samples was investigated using high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM; JEM-2010F, Jeol). XPS (ESCA-3200, Shimadzu) measurements were performed using Mg Kα radiation at <10−6 Pa (8 kV bias voltage applied to the X-ray source). Nuclear magnetic resonance (NMR) spectra were recorded on a Bruker Ultrashield Plus 400 instrument (Bruker Corporation) using tetramethylsilane as an internal standard (400 and 100 MHz for 1H NMR and 13C NMR, respectively). X-ray absorption fine-structure (XAFS) measurements were performed on the AR-NW10A beamline of the Photon Factory Advanced Ring at the Institute of Materials Structure Science, High Energy Accelerator Research Organization, Tsukuba, Japan. A Si (311) double-crystal monochromator was used to obtain a monochromated X-ray beam, and spectra were obtained in transmission mode. Y3Pd2 with BN (dried at 300 °C) were mixed in an argon-filled glovebox and the mixture was pressed with a hand press apparatus to obtain a pellet sample, which was sealed in a plastic bag for measurement. XAFS spectra were analyzed using the Athena and Artemis software packages43. The FEFF6 code44 was used to calculate the theoretical spectra.
DFT calculations
DFT calculations were performed using the generalized gradient approximation (GGA) with the Perdew−Burke−Ernzerhof (PBE)56 functional and the projector augmented plane-wave method implemented in the VASP 5.4 code57. The plane-wave cutoff energy was set to 500 eV. Γ-centered k-meshes with a k-spacing of 0.1 Å–1 were employed to sample the Brillouin zones. The bulk structures were relaxed until the total force on each atom was less than 0.01 eV Å–1. A Bader charge analysis was conducted using the Bader program58. Calculations for slab supercell models, which consist of atomic layers with thicknesses of around 10 Å and a vacuum layer with a thickness of 15 Å, were performed to determine the work functions and formation energies for different surfaces. The energy barriers of the activation of aryl halides were calculated using the nudged elastic band method implemented in the Vienna Ab initio Simulation Package with 10 replicas, which included initial and final structures and 8 nudged intermediate images.
FT-IR measurements
DRIFT spectra were measured using a spectrometer (FT/IR-6100, Jasco) equipped with a mercury–cadmium–tellurium detector at a resolution of 4 cm−1. An alumina sample cup containing approximately 30 mg of catalyst was introduced into a water-cooled stainless steel heat chamber equipped with KBr windows (STJ-0123-HP-LTV, S.T. Japan). The sample was heated at 200 °C under vacuum for 2 h and then cooled to room temperature. After the pretreatment, iodobenzene was supplied into the system. The infrared spectrum of the sample at room temperature prior to the adsorption of substrates was used as the background for the difference spectra obtained by subtraction of the background from the spectra of the catalyst samples with adsorbed substrate.
Data availability
The data that support the findings of this study are available from the corresponding authors on reasonable request.
References
Miyaura, N. & Suzuki, A. Palladium-catalyzed cross-coupling reactions of organoboron compounds. Chem. Rev. 95, 2457–2483 (1995).
Fihri, A., Bouhrara, M., Nekoueishahraki, B., Basset, J.-M. & Polshettiwar, V. Nanocatalysts for Suzuki cross-coupling reactions. Chem. Soc. Rev. 40, 5181–5203 (2011).
Molnár, Á. Efficient, selective, and recyclable palladium catalysts in carboncarbon coupling reactions. Chem. Rev. 111, 2251–2320 (2011).
Glasspoole, B. W. & Crudden, C. M. The final frontier. Nat. Chem. 3, 912–913 (2011).
Buchwald, S. L. Cross coupling. Acc. Chem. Res. 41, 1555–1564 (2008).
Yin, L. X. & Liebscher, J. Carbon−carbon coupling reactions catalyzed by heterogeneous palladium catalysts. Chem. Rev. 107, 133–173 (2007).
Grirrane, A., Corma, A. & Garcıá, H. Gold-catalyzed synthesis of aromatic azo compounds from anilines and nitroaromatics. Science 322, 1661–1664 (2008).
Kesavan, L. et al. Solvent-free oxidation of primary carbon-hydrogen bonds in toluene using Au-Pd alloy nanoparticles. Science 331, 195–199 (2011).
Scheuermann, G. M., Rumi, L., Steurer, P., Bannwarth, W. & Mulhaupt, R. Palladium nanoparticles on graphite oxide and its functionalized graphene derivatives as highly active catalysts for the Suzuki2Miyaura coupling reaction. J. Am. Chem. Soc. 131, 8262–8270 (2009).
Noël, T., Kuhn, S., Musacchio, A. J., Jensen, K. F. & Buchwald, S. L. Suzuki-miyaura cross-coupling reactions in flow: multistep synthesis enabled by a microfluidic extraction. Angew. Chem. Int. Ed. 50, 5943–5946 (2011).
Yuan, B., Pan, Y., Li, Y., Yin, B. & Jiang, H. A highly active heterogeneous palladium catalyst for the suzuki–miyaura and ullmann coupling reactions of aryl chlorides in aqueous media. Angew. Chem. Int. Ed. 49, 4054–4058 (2010).
Sarina, S. et al. Enhancing catalytic performance of palladium in gold and palladium alloy nanoparticles for organic synthesis reactions through visible light irradiation at ambient temperatures. J. Am. Chem. Soc. 135, 5793–5801 (2013).
Leyva-Pérez, A., Oliver-Meseguer, J., Rubio-Marqués, P. & Corma, A. Water-stabilized three- and four- atom palladium clusters as highly active catalytic species in ligand-free C-C cross-coupling reactions. Angew. Chem. Int. Ed. 52, 11554–11559 (2013).
Wang, F. et al. A polyphenylene support for Pd catalysts with exceptional catalytic activity. Angew. Chem. Int. Ed. 53, 8645–8648 (2014).
Chen, Z. et al. A heterogeneous single-atom palladium catalyst surpassing homogeneous systems for Suzuki coupling. Nat. Nanotechnol. 13, 702–707 (2018).
Fu, G. C. The development of versatile methods for palladium-catalyzed coupling reactions of aryl electrophiles through the use of P(t-Bu)3 and PCy3 as Ligands. ACC Chem. Res. 41, 1555–1564 (2008).
Mitchell, S., Vorobyeva, E. & Pérez-Ramírez, J. The multifaceted reactivity of single-atom heterogeneous catalysts. Angew. Chem. Int. Ed. 57, 15316–15329 (2018).
Li, X. H., Baar, M., Blechert, S. & Antonietti, M. Facilitating room-temperature Suzuki coupling reaction with light: Mott-Schottky photocatalyst for C-C-coupling. Sci. Rep. 3, 1743 (2013).
Raza, F. et al. Structuring Pd nanoparticles on 2H-WS2 nanosheets induces excellent photocatalytic activity for cross-coupling reactions under visible light. J. Am. Chem. Soc. 139, 14767–14774 (2017).
Guo, J. et al. Boosting hot electrons in hetero-superstructures for plasmon-enhanced catalysis. J. Am. Chem. Soc. 139, 17964–17972 (2017).
MacQuarrie, S. et al. Visual observation of redistribution and dissolution of palladium during the suzuki–miyaura reaction. Angew. Chem. Int. Ed. 47, 3279–3282 (2008).
Shao, L. D. et al. Nanosizing intermetallic compounds onto carbon nanotubes: active and aelective hydrogenation catalysts. Angew. Chem. Int. Ed. 50, 10231–10235 (2011).
Wan, Y. et al. Ordered mesoporous Pd/silica−carbon as a highly active heterogeneous catalyst for coupling reaction of chlorobenzene in aqueous media. J. Am. Chem. Soc. 131, 4541–4550 (2009).
Greeley, J. et al. Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat. Chem. 1, 552–556 (2009).
Escudero-Escribano, M. et al. Tuning the activity of Pt alloy electrocatalysts by means of the lanthanide contraction. Science 352, 73–76 (2016).
Stephens, I. E. L., Bondarenko, A. S., Grønbjerg, U., Rossmeisl, J. & Chorkendorff, I. Understanding the electrocatalysis of oxygen reduction on platinum and its alloys. Energy Environ. Sci. 5, 6744–6762 (2012).
Stamenkovic, V. R. et al. Improved oxygen reduction activity on Pt3Ni(111) via increased surface site availability. Science 315, 493–497 (2007).
Zhang, J., Sasaki, K., Sutter, E. & Adzic, R. R. Stabilization of platinum oxygen-reduction electrocatalysts using gold clusters. Science 315, 220–222 (2007).
Hernandez-Fernandez, P. et al. Mass-selected nanoparticles of PtxY as model catalysts for oxygen electroreduction. Nat. Chem. 6, 732–738 (2014).
Wang, S. J. et al. Role of electronic perturbation in stability and activity of Pt-based alloy nanocatalysts for oxygen reduction. J. Am. Chem. Soc. 134, 19508–19511 (2012).
Roy, C. et al. Scalable synthesis of carbon-supported platinum–lanthanide and− rare-earth alloys for oxygen reduction. ACS Catal. 8, 2071–2080 (2018).
Gong, Y. et al. Ternary intermetallic LaCoSi as a catalyst for N2 activation. Nat. Catal. 1, 178–185 (2018).
Ye, T. N. et al. Copper-based intermetallic electride catalyst for chemoselective hydrogenation reactions. J. Am. Chem. Soc. 139, 17089–17097 (2017).
Kitano, M. et al. Ammonia synthesis using a stable electride as an electron donor and reversible hydrogen store. Nat. Chem. 4, 934–940 (2012).
Kitano, M. et al. Electride support boosts nitrogen dissociation over ruthenium catalyst and shifts the bottleneck in ammonia synthesis. Nat. Commun. 6, 6731 (2015).
Ye, T. N., Li, J., Kitano, M., Sasase, M. & Hosono, H. Electronic interactions between a stable electride and a nano-alloy control the chemoselective reduction reaction. Chem. Sci. 7, 5969–5975 (2016).
Ye, T. N., Li, J., Kitano, M. & Hosono, H. Unique nanocages of 12CaO·7Al2O3 boost heterolytic hydrogen activation and selective hydrogenation of heteroarenes over ruthenium catalyst. Green. Chem. 19, 749–756 (2017).
Lu, Y. F. et al. Water durable electride Y5Si3: electronic structure and catalytic activity for ammonia synthesis. J. Am. Chem. Soc. 138, 3970–3973 (2016).
Wang, F. et al. Plasmonic harvesting of light energy for Suzuki coupling reactions. J. Am. Chem. Soc. 135, 5588–5601 (2013).
Zhang, X. et al. C–C coupling on single-atom-based heterogeneous catalyst. J. Am. Chem. Soc. 140, 954–962 (2018).
Xiao, Q. et al. Visible light-driven cross-coupling reactions at lower temperatures using a photocatalyst of palladium and gold alloy nanoparticles. ACS Catal. 4, 1725–1734 (2014).
Proutiere, F. & Schoenebeck, F. Solvent effect on palladium-catalyzed cross-coupling reactions and implications on the active catalytic species. Angew. Chem. Int. Ed. 50, 8192–8195 (2011).
Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2005).
Zabinsky, S. I., Rehr, J. J., Ankudinov, A., Albers, R. C. & Eller, M. J. Multiple-scattering calculations of x-ray-absorption spectra. Phys. Rev. B 52, 2995 (1995).
Wu, W., Liao, L., Lien, C. & Lin, J. FTIR study of adsorption, thermal reactions and photochemistry of benzene on powdered TiO2. Phys. Chem. Chem. Phys. 3, 4456–4461 (2001).
Whiffen, D. H. Vibrational frequencies and thermodynamic properties of fluoro-, chloro-, bromo-, and iodo-benzene. J. Chem. Soc. 273, 1350−1356 (1956).
Kohler, K., Kleist, W. & Prockl, S. S. Genesis of coordinatively unsaturated palladium complexes dissolved from solid precursors during heck coupling reactions and their role as catalytically active species. Inorg. Chem. 46, 1876–1883 (2007).
Zhao, F. Y., Shirai, M., Ikushima, Y. & Arai, M. The leaching and re-deposition of metal species from and onto conventional supported palladium catalysts in the Heck reaction of iodobenzene and methyl acrylate in N-methylpyrrolidone. J. Mol. Catal. A 180, 211–219 (2002).
Davies, I. W., Matty, L., Hughes, D. L. & Reider, P. J. Are heterogeneous catalysts precursors to homogeneous catalysts? J. Am. Chem. Soc. 123, 10139–10140 (2001).
Soomro, S. S., Ansari, F. L., Chatziapostolou, K. & Köhler, K. Palladium leaching dependent on reaction parameters in Suzuki–Miyaura coupling reactions catalyzed by palladium supported on alumina under mild reaction conditions. J. Catal. 273, 138–146 (2010).
Siamaki, A. R., Khder, A. E. R. S., Abdelsayed, V., El-Shall, M. S. & Gupton, B. F. Microwave-assisted synthesis of palladium nanoparticles supported on graphene: a highly active and recyclable catalyst for carbon–carbon cross-coupling reactions. J. Catal. 279, 1–11 (2011).
López, N. & Vargas-Fuentes, C. Promoters in the hydrogenation of alkynes in mixtures: insights from density functional theory. Chem. Commun. 48, 1379–1391 (2012).
Jinnouchi, R., Toyoda, E., Hatanaka, T. & Morimoto, Y. First principles calculations on site-dependent dissolution potentials of supported and unsupported Pt particles. J. Phys. Chem. C. 114, 17557–17568 (2010).
Albani, D. et al. Selective ensembles in supported palladium sulfide nanoparticles for alkyne semi-hydrogenation. Nat. Commun. 9, 2634 (2018).
Kitamura, Y. et al. Heterogeneous Pd/C-catalyzed ligand-free Suzuki-Miyaura coupling reaction using aryl boronic esters. Tetrahedron 63, 10596–10602 (2007).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
Tang, W., Sanville, E. & Henkelman, G. A grid-based Bader analysis algorithm without lattice bias. J. Phys. Condens. Matter 21, 084204 (2009).
Acknowledgements
This work was supported by funds from a Kakenhi Grant-in-Aid (No. 17H06153) from the Japan Society for the Promotion of Science (JSPS) and the MEXT (Ministry of Education, Culture, Sports, Science and Technology) Element Strategy Initiative to form a research core. XAFS measurements were performed under the approval of PF-PAC No. 2016S2–004. T.Y. is supported by a JSPS fellowship for International Research Fellows (No. P18361). Y.L. is supported by a JSPS fellowship for young scientists (No. 18J00745). Prof. M. Hara (Tokyo Institute of Technology) is acknowledged for conducting XPS measurements.
Author information
Authors and Affiliations
Contributions
H.H. proposed the idea behind the research and supervised the project. T.Y., Y.L., J.L., and M.K. performed the synthesis, characterization, and catalytic measurements. Z.X., T.N., and T.T. carried out the model construction and DFT calculations. H.A. and Y.N. helped with the XAFS measurements. T.Y., Y.L., Z.X., and H.H. co-wrote the paper. All authors discussed the results and commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ye, TN., Lu, Y., Xiao, Z. et al. Palladium-bearing intermetallic electride as an efficient and stable catalyst for Suzuki cross-coupling reactions. Nat Commun 10, 5653 (2019). https://doi.org/10.1038/s41467-019-13679-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-13679-0
This article is cited by
-
Berry curvature contributions of kagome-lattice fragments in amorphous Fe–Sn thin films
Nature Communications (2023)
-
Highly efficient and recyclable amorphous Pd(II)/crystal Pd(0) catalyst for boosting Suzuki reaction in aqueous solution
Nano Research (2022)
-
Tellurium-Ligated Pd(II) Complex of Bulky Organotellurium Ligand as a Catalyst of Suzuki coupling: First Report on In Situ Generation of Bimetallic Alloy ‘Telluropalladinite’ (Pd9Te4) Nanoparticles and Role in Highly Efficient Catalysis
Catalysis Letters (2022)
-
Insight into rare-earth-incorporated catalysts: The chance for a more efficient ammonia synthesis
Journal of Advanced Ceramics (2022)
-
Nitrogen-bonded ultrasmall palladium clusters over the nitrogen-doped carbon for promoting Suzuki cross-coupling reactions
Advanced Composites and Hybrid Materials (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.