Abstract
Indirect excitons (IXs) are explored both for studying quantum Bose gases in semiconductor materials and for the development of excitonic devices. IXs were extensively studied in III–V and II–VI semiconductor heterostructures where IX range of existence has been limited to low temperatures. Here, we present the observation of IXs at room temperature in van der Waals transition metal dichalcogenide (TMD) heterostructures. This is achieved in TMD heterostructures based on monolayers of MoS2 separated by atomically thin hexagonal boron nitride. The IXs we realize in the TMD heterostructure have lifetimes orders of magnitude longer than lifetimes of direct excitons in single-layer TMD and their energy is gate controlled. The realization of IXs at room temperature establishes the TMD heterostructures as a material platform both for a field of high-temperature quantum Bose gases of IXs and for a field of high-temperature excitonic devices.
Similar content being viewed by others
Introduction
An indirect exciton (IX) is composed of an electron and a hole confined in spatially separated quantum well layers. Long lifetimes of IXs allow them to cool below the temperature of quantum degeneracy giving the opportunity to create and study quantum Bose gases in semiconductor materials1,2. Furthermore, IXs are explored for the development of excitonic devices with energy-efficient computation and seamless coupling to optical communication3. IXs were extensively studied in III–V and II–VI semiconductor heterostructures. However, their range of existence has been limited so far to low temperatures due to low IX binding energies in these materials. IXs in van der Waals transition-metal dichalcogenide (TMD) heterostructures4 are characterized by high binding energies making them stable at room temperature and giving the opportunity for exploring high-temperature quantum Bose gases in materials and for creating excitonic devices operational at room temperature, the key for the development of excitonic technology5,6,7.
Experimental studies of quantum degenerate Bose gases of IXs were performed so far in GaAs coupled quantum well (CQW) structures where quantum degeneracy was achieved in the temperature range of few Kelvin. The findings include spontaneous coherence and condensation of excitons8, long-range spin currents and spin textures9, spatially modulated exciton state10, and perfect Coulomb drag11. Furthermore, IX energy, lifetime, and flux can be controlled by voltage that is explored for the development of excitonic devices. Excitonic devices with IXs were demonstrated so far at temperatures below ~100 K. These devices include traps, lattices, conveyers, and ramps, which are used for studying basic properties of cold IXs, as well as excitonic transistors, routers, and photon storage devices, which hold the potential for creating excitonic signal processing devices and excitonic circuits, a review of excitonic devices can be found in ref. 3.
A finite exciton binding energy Eex limits the operation temperature of excitonic devices. Excitons exist in the temperature range roughly below Eex/kB (kB is the Boltzmann constant)12. Furthermore, the temperature of quantum degeneracy, which can be achieved with increasing density before excitons dissociation to electron–hole plasma, also scales proportionally to Eex5. These considerations instigate the search for material systems where IXs have a high-binding energy and, as a result, can provide the medium for the realization of high-temperature coherent phenomena and excitonic devices.
IXs were explored in various III–V and II–VI semiconductor QW heterostructures based on GaAs2,3,8,9,10,11,12,13,14, AlAs15,16, InGaAs17, GaN18,19,20, and ZnO21,22. Among these materials, IXs are more robust in the ZnO structures where their binding energy is about 30 meV21. Proof of principle for the operation of IX switching devices was demonstrated at temperatures up to ~100 K in AlAs/GaAs CQW16 where the IX binding energy is about ~10 meV15. Studies of IXs in III–V and II–VI semiconductor materials continue to attract intense interest.
Van der Waals structures composed of atomically thin layers of TMD offer an opportunity to realize artificial materials with designable properties, forming a new platform for studying basic phenomena and developing optoelectronic devices4. TMD heterostructures allow IXs with remarkably high binding energies5,6,7, much higher than in III–V or II–VI semiconductor heterostructures. Therefore, IXs in TMD heterostructures open the opportunity to realize room-temperature excitonic devices and explore high-temperature quantum degenerate Bose gases of IXs.
The experimental approaches to the realization of IXs in TMD materials involve two kinds of heterostructures. In type I TMD heterostructures with direct gap alignment, the electron and hole layers are spatially separated by a barrier layer. Such type I structures with MoS2 forming the QW layers and a hexagonal boron nitride (hBN) forming the barrier were considered in refs. 5,23. These heterostructures are similar to GaAs/AlGaAs CQW heterostructures where GaAs forms QW layers and AlGaAs forms the barrier2,3,8,9,10,11,12,13,14. In type II TMD heterostructures with staggered band alignment, the electron and hole layers form in different adjacent TMD materials such as single-layer MoSe2 and WSe224,25,26,27, MoS2 and WSe228,29, MoS2 and WS230,31, MoSe2 and WS232, and MoS2 and MoSe233. These heterostructures are similar to AlAs/GaAs CQW heterostructures where electrons and holes are confined in adjacent AlAs and GaAs layers, respectively15,16.
Here, we report on the realization of IXs in TMD heterostructures at room temperature. This was achieved using the previously demonstrated approach with MoS2/hBN type-I CQW23 combined with an improved structure design and detected using time-resolved optical spectroscopy.
The structure studied here was assembled by stacking mechanically exfoliated two-dimensional crystals on a graphite substrate, which acts as a global backgate (Fig. 1a). The top view of the device showing the contours of different layers is presented in Fig. 1c. The CQW is formed where the two MoS2 monolayers, separated by three hBN layers, overlap. IXs are formed from electrons and holes in different MoS2 layers (Fig. 1b). The top and bottom 5 nm thick hBN serve as dielectric cladding layers. Voltage Vg applied between the top graphene layer and the backgate is used to create the bias across the CQW structure. The thickness of hBN cladding layers is much smaller than in our previous CQW TMD device23. This allowed us to achieve a much higher electric field across the structure for the applied voltage and, in turn, realize effective control of IX energy by voltage as described below.
Results
Long-lifetime emission
IXs dominate the emission spectrum measured after the laser excitation pulse (Fig. 2). At the time delays exceeding the DX recombination times, most of DXs have recombined, and so the recombination of IXs, which have a much longer lifetime, is not masked by the DX recombination. Both short-lifetime DX and long-lifetime IX emission lines are observed in the spectrum measured in the time window between the laser pulses and the first ≈2 ns of the laser pulse (Fig. 2). As the fraction of time corresponding to the laser pulse grows, the relative intensity of the DX emission increases. In the cw regime, where the laser is permanently on, DXs dominate the spectrum due to their higher oscillator strength (Fig. 2). Supplementary Figure 2 shows similar spectra at 2 K (Supplementary materials present kinetics at different Vg and low-temperature spectra).
The IX emission kinetics is presented in Fig. 3. The time resolution of the experimental system including the pulse generator, the laser, the photomultiplier, and the time-correlated photon counting system is ~0.5 ns as seen from the laser decay kinetics measured at Eex=3.07 eV. The DX decay kinetics measured at the DX line peak EDX=1.89 eV closely follows the excitation laser decay indicating that the DX lifetime is shorter than the 0.5 ns experimental resolution. The decay kinetics in the IX spectral range 1.46–1.65 eV shows a double-exponential decay (Fig. 3). Its faster component is determined by the decay of low-energy DX states, which appear in the IX spectral range due to the spectral broadening of the DX line (Fig. 2) (similar localized DXs at low energies in the spectral range of IXs were studied in GaAs/AlAs CQW in ref. 34). The slower component is determined by the IX decay (Fig. 3). The IX lifetime ~10 ns (Fig. 3) is orders of magnitude longer than the DX lifetime35 and is controlled by gate voltage Vg over a range of several ns (Fig. 3, inset). The voltage dependence of the IX lifetime has two characteristic features. First, it reduces at positive Vg where the IX energy approaches the DX energy (section: “Control of Energy by Voltage”). Second, it has a local maximum around Vg=0 (Supplementary Fig. 1) (Supplementary materials present kinetics at different Vg and low-temperature spectra). Both these features are characteristic of IXs16. The former can be attributed to the increase of the overlap of electron and hole wave functions with approaching the direct regime. The latter may result from the suppression of the leakage currents through the CQW layers at zero bias. The realization of the indirect regime, where the IXs are lower in energy than DXs, already at Vg=0 indicates an asymmetry of the device, presumably due to unintenional doping.
Transport
Figure 4 shows the spatial profiles of IX emission. The width of the emission profiles determined by a fit to Lorentzian distribution (dashed lines in Fig. 4) is shown in inset to Fig. 4 as a function of time. The emission profiles after the laser excitation pulse have wider spatial distributions than during the pulse. During the laser excitation pulse, the low-energy tail of short-lifetime DX emission strongly contributes to the emission in the IX spectral region (Fig. 2). After the pulse, DXs decay quickly and the emission is dominated by the long-lifetime IXs. Diffusion of IXs away from the laser excitation spot during their long lifetime contributes to the wider spatial profiles of IX emission. The increase in emission width after the pulse end l can be used for estimating an upper bound on the IX diffusion coefficient D. For l~1 μm (Fig. 4) and IX lifetime τ ~ 10 ns (Fig. 3) this gives D ~ l2 / τ ~ 1 cm2/s.
Control of energy by voltage
Figure 5 shows control of the IX energy by gate voltage. The energy of the long-lifetime emission line shifts by about 120 meV at cryogenic temperatures and by about 60 meV at room temperature. No leakage current or sample damage was detected at cryogenic temperatures in the measurements at applied voltages up to ±6 V, which is typical for thin hBN that can withstand electric fields of about 0.5 V/nm36. However, at room temperature, applying ±3 V led to the appearance of leakage current through the device and the reduced device resistivity persisted after lowering Vg. This limited the maximum applied voltage and, in turn, the IX energy shift at room temperature.
Discussion
Regarding the physical mechanism that governs the IX lifetime in the studied heterostructure we can say the following. In general, this lifetime is limited by tunneling through the hBN spacer. However, direct tunneling across the entire thickness 3 × 0.33=1 nm of the spacer should be prohibitively slow. The tunneling action and tunneling probability can be estimated to be S ~ 12 and exp(−2S) ~ 10−11, respectively, for the potential barrier of height 2 eV and the carrier mass mb ~ 0.5 inside the barrier (similar to ref. 5). Therefore, we surmise that the IX recombination involves transmission through some midgap defects in the spacer36 (specific properties of these defects beyond their ability to facilitate tunneling through the hBN layer, relevant to the experiment, are unclear).
In summary, IXs were observed at room temperature in van der Waals MoS2/hBN heterostructure. The IXs have long lifetimes, orders of magnitude longer than lifetimes of direct excitons in single-layer MoS2, and their energy is controlled by voltage at room temperature.
Methods
Experimental setup
The excitons were generated by a semiconductor laser with excitation energy Eex=3.07 eV. In continuous wave (cw) experiments, photoluminescence (PL) spectra were measured using a spectrometer with resolution 0.2 meV and a liquid-nitrogen-cooled CCD. In all time-resolved experiments, the laser pulses had a rectangular shape with the duration 10–50 ns, period 40–200 ns, and edge sharpness ~0.5 ns (Fig. 2). The laser was focused to a ~2 μm spot with a power of 0.8 mW. In time-resolved PL kinetics and spectrum measurements, the emitted light was filtered by an interference filter or diffracted by the spectrometer, respectively, and then detected by a photomultiplier tube and time-correlated photon counting system. In time-resolved imaging experiments, the emitted light was filtered by an interference filter and detected by a liquid-nitrogen-cooled CCD coupled to a PicoStar HR TauTec time-gated intensifier. The measurements were performed in a 4He atmosphere at room temperature (T≈300 K) and in a liquid 4He cryostat at 2 K.
Data availability
All relevant data are available from the authors.
References
Lozovik, Yu. E. & Yudson, V. I. A new mechanism for superconductivity: pairing between spatially separated electrons and holes. Sov. Phys. JETP 44, 389–397 (1976).
Butov, L. V. et al. Stimulated scattering of indirect excitons in coupled quantum wells: signature of a degenerate Bose-gas of excitons. Phys. Rev. Lett. 86, 5608–5611 (2001).
Butov, L. V. Excitonic devices. Superlattices Microstruct. 108, 2–26 (2017).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Fogler, M. M., Butov, L. V. & Novoselov, K. S. High-temperature superfluidity with indirect excitons in van der Waals heterostructures. Nat. Commun. 5, 4555 (2014).
Ye, Z. et al. Probing excitonic dark states in single-layer tungsten disulphide. Nature 513, 214–218 (2014).
Chernikov, Alexey et al. Exciton binding energy and nonhydrogenic Rydberg series in monolayer WS2. Phys. Rev. Lett. 113, 076802 (2014).
High, A. A. et al. Spontaneous coherence in a cold exciton gas. Nature 483, 584–588 (2012).
High, A. A. et al. Spin currents in a coherent exciton gas. Phys. Rev. Lett. 110, 246403 (2013).
Yang, S., Butov, L. V., Simons, B. D., Campman, K. L. & Gossard, A. C. Fluctuation and commensurability effect of exciton density wave. Phys. Rev. B 91, 245302 (2015).
Nandi, D., Finck, A. D. K., Eisenstein, J. P., Pfeiffer, L. N. & West, K. W. Exciton condensation and perfect Coulomb drag. Nature 488, 481–484 (2012).
Chemla, D. S. et al. Room temperature excitonic nonlinear absorption and refraction in GaAs/AlGaAs multiple quantum well structures. IEEE J. Quantum Electron. 20, 265–275 (1984).
Islam, M. N. et al. Electroabsorption in GaAs/AlGaAs coupled quantum well waveguides. Appl. Phys. Lett. 50, 1098–1100 (1987).
Alexandrou, A. et al. Electric-field effects on exciton lifetimes in symmetric coupled GaAs/Al0.3Ga0.7As double quantum wells. Phys. Rev. B 42, 9225–9228 (1990).
Zrenner, A. et al. Indirect excitons in coupled quantum well structures. Surf. Sci. 263, 496–501 (1992).
Grosso, G. et al. Excitonic switches operating at around 100 K. Nat. Photonics 3, 577–580 (2009).
Butov, L. V., Zrenner, A., Abstreiter, G., Petinova, A. V. & Eberl, K. Direct and indirect magnetoexcitons in symmetric In x Ga1−xAs/GaAs coupled quantum wells. Phys. Rev. B 52, 12153–12157 (1995).
Lefebvre, P. et al. Observation and modeling of the time-dependent descreening of internal electric field in a wurtzite GaN/Al0.15Ga0.85N quantum well after high photoexcitation. Phys. Rev. B 69, 035307 (2004).
Fedichkin, F. et al. Transport of dipolar excitons in (Al,Ga)N/GaN quantum wells. Phys. Rev. B 91, 205424 (2015).
Fedichkin, F. et al. Room-temperature transport of indirect excitons in (Al,Ga)N/GaN quantum wells. Phys. Rev. Appl. 6, 014011 (2016).
Morhain, C. et al. Internal electric field in wurtzite ZnO/Zn0.78Mg0.22O quantum wells. Phys. Rev. B 72, 241305(R) (2005).
Kuznetsova, Y. Y. et al. Transport of indirect excitons in ZnO quantum wells. Opt. Lett. 40, 3667–3670 (2015).
Calman, E. V. et al. Control of excitons in multi-layer van der Waals heterostructures. Appl. Phys. Lett. 108, 101901 (2016).
Rivera, P. et al. Observation of long-lived interlayer excitons in monolayer MoSe2-WSe2 heterostructures. Nat. Commun. 6, 6242 (2015).
Rivera, P. et al. Valley-polarized exciton dynamics in a 2D semiconductor heterostructure. Science 351, 688–691 (2016).
Miller, B. et al. Long-lived direct and indirect interlayer excitons in van der Waals heterostructures. Nano Lett. 17, 5229–5237 (2017).
Nagler, P. et al. Interlayer exciton dynamics in a dichalcogenide monolayer heterostructure. 2D Mater. 4, 025112 (2017).
Fang, H. et al. Strong interlayer coupling in van der Waals heterostructures built from single-layer chalcogenides. Proc. Natl Acad. Sci. USA 111, 6198 (2014).
Latini, S., Winther, K. T., Olsen, T. & Thygesen, K. S. Interlayer excitons and band alignment in MoS2/hBN/WSe2 van der Waals heterostructures. Nano Lett. 17, 938–945 (2017).
Hong, X. et al. Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nano 9, 682–686 (2014).
Palummo, M., Bernardi, M. & Grossman, J. C. Exciton radiative lifetimes in two-dimensional transition metal dichalcogenides. Nano Lett. 15, 2794–2800 (2015).
Bellus, M. Z., Ceballos, F., Chiu, H. Y. & Zhao H. Tightly bound trions in transition metal dichalcogenide heterostructures. ACS Nano 9, 6459–6464 (2015).
Mouri, S. et al. Thermal dissociation of inter-layer excitons in MoS2/MoSe2 hetero-bilayers. Nanoscale 9, 6674–6679 (2017).
Zrenner, A. et al. Quantum dots formed by interface fluctuations inAlAs/GaAs coupled quantum well structures. Phys. Rev. Lett. 72, 3382–3385 (1994).
Korn, T., Heydrich, S., Hirmer, M., Schmutzler, J. & Schüller, C. Low-temperature photocarrier dynamics in monolayer MoS2. Appl. Phys. Lett. 99, 102109 (2011).
Britnell, L. et al. Field-effect tunneling transistor based on vertical graphene heterostructures. Science 335, 947–950 (2012).
Acknowledgements
These studies were supported by DOE Office of Basic Energy Sciences under award DE-FG02-07ER46449 and kinetics measurements were supported by NSF Grant No. 1640173 and NERC, a subsidiary of SRC, through the SRC-NRI Center for Excitonic Devices.
Author information
Authors and Affiliations
Contributions
E.V.C., M.M.F., L.V.B., S.H., A.M., and A.K.G. contributed to the work presented in this paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Calman, E.V., Fogler, M.M., Butov, L.V. et al. Indirect excitons in van der Waals heterostructures at room temperature. Nat Commun 9, 1895 (2018). https://doi.org/10.1038/s41467-018-04293-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-04293-7
This article is cited by
-
Dipolar many-body complexes and their interactions in stacked 2D heterobilayers
Nature Reviews Physics (2024)
-
Tailored plasmon polariton landscape in graphene/boron nitride patterned heterostructures
npj 2D Materials and Applications (2024)
-
Thermodynamic behavior of correlated electron-hole fluids in van der Waals heterostructures
Nature Communications (2023)
-
Tightly bound and room-temperature-stable excitons in van der Waals degenerate-semiconductor Bi4O4SeCl2 with high charge-carrier density
Communications Materials (2023)
-
Forty years of theory-inspired experiments on charge-transfer via solutions and electrodes: the Georgian accents
Journal of Solid State Electrochemistry (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.