Abstract
Dendrite growth of alkali metal anodes limited their lifetime for charge/discharge cycling. Here, we report near-perfect anodes of lithium, sodium, and potassium metals achieved by electrochemical polishing, which removes microscopic defects and creates ultra-smooth ultra-thin solid-electrolyte interphase layers at metal surfaces for providing a homogeneous environment. Precise characterizations by AFM force probing with corroborative in-depth XPS profile analysis reveal that the ultra-smooth ultra-thin solid-electrolyte interphase can be designed to have alternating inorganic-rich and organic-rich/mixed multi-layered structure, which offers mechanical property of coupled rigidity and elasticity. The polished metal anodes exhibit significantly enhanced cycling stability, specifically the lithium anodes can cycle for over 200 times at a real current density of 2 mA cm–2 with 100% depth of discharge. Our work illustrates that an ultra-smooth ultra-thin solid-electrolyte interphase may be robust enough to suppress dendrite growth and thus serve as an initial layer for further improved protection of alkali metal anodes.
Similar content being viewed by others
Introduction
Lithium anode has received considerable attention, as it is regarded as the most promising anode candidate for the next generation high-energy-density rechargeable batteries such as Li–sulfur and Li–air batteries1,2,3,4,5,6. Recently, sodium and potassium anodes are also gaining popularity because of their abundance and more attractive cathode chemistry in Na–air7 and K–air8 batteries. However, anodes made of these alkali metals, also denoted as MA, suffer from intrinsic and induced dendrite growth upon charge–discharge cycling, resulting in low Coulombic efficiency, short-circuiting and thus short lifetime of batteries9,10,11,12,13. Continuous efforts have been devoted to improve the long-term stability of Li anodes, ranging from traditional soaking-based method that passively forms a solid-electrolyte interphase (SEI)14,15,16,17,18,19, strategies to improve Li deposition/dissolution behaviors including preferential adsorption20, employment of ultrahigh Li salt concentration21 and asymmetric cycling protocols22, to currently overwhelming artificial approaches23,24,25,26,27,28 that form micrometer scale artificial SEI layers by heavy reactions with Li surface or application of physical isolating layers. However, up to date, the long-term stability of Li anodes, especially under high-current density and with reasonable depth of discharge (DOD), is still far from satisfactory (see Supplementary Table 1). Most of the works have to employ Li foils as anode material because of low utilization of Li source, or only limited cycle numbers can be maintained in the case of anode-free type cells. The situation is even less optimistic for Na and K anodes29,30 (see Supplementary Table 2).
Looking into the origins of dendrite growth, the microscopic protrusions, non-uniform electric field distribution, as well as uneven supply of metal ion flux are detriment factors that promote dendrite growth2,3. These factors are inherently correlated with the roughness of surface as well as inhomogeneity of SEI that is inevitably formed on the MA surfaces as a result of chemical and/or electrochemical reductions of electrolyte14,31,32,33. The rough surface morphology boosts the intrinsic growth of long dendrites at Li anode, while inhomogeneous and unstable SEI induces dendrite growth at all of the three metal alkali anodes, especially Na and K anodes because of their more reactive chemistry than Li (Fig. 1a). However, it is important to emphasize that SEI is a double-edged sword depending on its physical and chemical properties: A coarse and inhomogeneous SEI, such as the disordered mosaic type of SEI prepared by soaking-based method34, promotes preferential growth through the cracks of mosaic SEI or at the locations where SEI is thinner or broken; while a fine and smooth SEI where the localized defects are largely eliminated would suppress both intrinsic and induced dendrite growth of all the three MA anodes.
Ideally, SEI layers for alkali metal anodes must be chemically stable and metal ion-conductive for batteries to operate; they should also be compact in general and uniform laterally to avoid localized effects for dendrite growth; last but not least, they should have well-defined structure both in lateral and vertical directions with mechanical property of coupled rigidity and elasticity to accommodate the volume change upon cycling2,35. Of particular attention is that the achievement of such ideal SEIs relies strongly on the smoothness of the metal surface19,36. Thus, creation of atomically smooth surface, onto which a near-ideal SEI can be formed, is an ultimate goal that would lead to a near-perfect metal alkali anode. This has been pursued for long time, but is so challenging that has not been achieved by currently available approaches. However, it is well-known that electrolytes can be reduced to various oxidation states37,38 depending on potential and MA+ concentration. Hence, the fundamental surface electrochemistry could play important and unique roles that other approaches cannot provide in terms of facile control of electrode kinetics.
Here, we report a general non-conventional electrochemical approach to create near-perfect Li, Na, and K metal anodes, based on electrochemical polishing of the alkali metal surfaces down to atomic-flatness as well as manipulation of electrolyte reduction processes to construct ultra-smooth ultra-thin (USUT) SEI with designable structure. By combined extensive characterizations by chemically, structurally as well as mechanically sensitive techniques, we reveal that the SEIs on MA anodes can be facilely tuned to have alternating inorganic-rich (I) and organic-rich/mixed (O) multi-layer structures in appropriate electrolytes. These types of multi-layer SEI structures are on contrary to the traditional mosaic model of SEI, and bear mechanical property of coupled rigidity and elasticity. With these features and merits, a significant step forward has been achieved for all the three alkali metal anodes in cycling stability under high-current density with high DOD.
Results
Electrochemical polishing for alkali metal surfaces
Basically, our electrochemical approach is based on the electrochemical stripping-plating (ESP) strategy as shown in Fig. 1b, including a potentiostatic stripping, during which concurrent MA dissolution and electrolyte reduction takes place, and a follow-up galvanostatic plating, during which concurrent MA deposition and further reduction of the electrolyte occurs. The potential for stripping is sufficiently anodic for high-rate MA dissolution (up to ~200 mA cm–2 in the initial stage), yet within the potential window for electrolyte reduction. An exceedingly high MA+ surface concentration (~11 mol L–1) is created during stripping (see Supplementary Fig. 1, Supplementary Notes 1 and 2 and Supplementary Table 3), which forms a viscous MA+ liquid layer that is crucial to achieving a smooth metal surface and meanwhile promoting electrolyte reduction and formation of a primary MA+-rich SEI. The cathodic current density for plating is kept low, which allows MA to deposit back slowly to smooth out the surface and SEI formation to complete at the same time.
As revealed by atomic force microscopy (AFM) images, large-scale close to atomic-flatness surfaces were created for the three alkali metals after application of the ESP processes. The flat terraces can reach a size of as large as ~30 μm wide with roughness of only ~1.5 nm, approaching the quality of single crystalline surfaces (Fig. 2b–h), in contrast to the rough pristine surfaces with height variation of ~1 μm (Fig. 2a and Supplementary Fig. 2a, b). Remarkably, the SEI films of the three alkali metals are also ultra-smooth with molecular-scale roughness of e.g., ~0.6 nm within an area of 5 × 5 μm2 on the metal surface (Fig. 1d, f, h). The large-scale flat surfaces can also be obtained on Li and Na thin films introduced onto modified Cu substrates (Supplementary Fig. 3), which facilitates easy characterizations and enables battery performance tests with reasonable DOD.
Tunable structure and mechanical property of SEI
To probe the vertical structure and mechanical property39,40,41 of the ultra-smooth SEIs, AFM force curve measurements were performed, mainly on Li anodes. For convenience of discussion, we begin with inspection of the force-piezo displacement curve recorded for soaked Li surface (Fig. 3a and Supplementary Fig. 5a, d). It can be seen intuitively that the cantilever deflects steeply until the tip reaches the Li substrate so that only a dip is seen. This implies the SEI on the soaked sample is rather stiff and lacks of flexibility against tip pressing so that cracking occurs upon force accumulation, as discerned by the fragmentation of surface after the measurements (Fig. 3b and Supplementary Fig. 6a, d).
However, the situation is totally different for the polished surfaces. A single potential step into the potential region preferential for reduction of 1,3-dioxolane (DOL) in the stripping process can create an SEI with coupled rigidity and elasticity. This can be viewed with linear deflection of cantilever followed by levering off until reaching the Li substrate (Fig. 3d and Supplementary Fig. 5b, d). This behavior is just like an elastic-plastic deformation process and suggests a soft inner layer and a stiff outer layer, i.e., soft-stiff SEI structure, which is robust against pressing as discerned by the smooth surface after force curve measurements (Fig. 3e and Supplementary Fig. 6b, e). By applying multiple potential steps sequentially to the regions for bis(trifluoromethanesulfonyl)imide (TFSI) reduction at lower potential and for DOL reduction at higher potential and then back to the region for reduction of TFSI, two types of force curves are observed for such an SEI, either with two elastic-plastic deformation-like processes (Supplementary Fig. 5c, d) or an elastic-plastic deformation-like process in the outer region followed by an elastic-cracking process in the inner region (Fig. 3g, h and Supplementary Fig. 5c, d). Both situation indicating the presence of an additional stiff inner layer, i.e., an alternating stiff-soft-stiff multi-layered SEI has been formed.
To understand the origin of the different mechanical behaviors of the three types of SEIs, depth-dependent characterization of chemical composition was performed by X-ray photoelectron spectroscopy (XPS) profile analysis. For soaked sample (Fig. 4a, b and Supplementary Fig. 8a), inorganic species of LiF, LiNSO2CF3, and Li3N are the major components in the inner region, while LiCF3, LiNSO2CF3, and Li2S2O4 in the surface region. Only very little organic moieties exist, mostly from high-oxidation state reduction products such as CH3OCH2CH2OLi as the C 1s signal is weak, broad and random, largely from the aliphatic C; this is further corroborated by the broad signals of amorphous organic salts of Li observed by X-ray absorption near-edge structure (XANES)42 (Supplementary Fig. 10). There is a cut of signals on the spectra between etching time of 30 and 60 s, dividing the SEI film into two inorganic-rich layers, which is denoted as an I–I structure or all-inorganic structure (Supplementary Fig. 9a). Interestingly, such I–I type of SEI structure is in contrast to the traditional I–O double layer model of SEI34,43, a picture that has been widely adopted for SEI for a long time.
Next, the soft-stiff SEI formed after ESP process with a single potential step for stripping displays a dramatically different chemical structure. No passive layer is present as no signals from Li2O and carbonyl species (CO32−) are observed by XPS and XANES (Supplementary Figs. 8b and 10) and no signal from hydroxyl (–OH) by Fourier transform infrared spectroscopy (FTIR) (Supplementary Fig. 11). This leaves with a fresh Li surface for SEI formation. Remarkably, however, in the inner region (sputtering time between 30 and 150 s), the signal of C–O moieties clearly indicates the presence of an ordered low oxidation state polymeric ROLi that is rich of C–O–C, C–C–O, O–C–O, in contrast to the almost absence of such moieties in the I–I structured SEI of soaked sample. In the surface region, however, the high-oxidation state ROLi is present judged from the appearance of aliphatic C signal; meanwhile, inorganic LiCF3 and LiF become dominant with small amount of Li2NSO2CF3 and Li2S2O4 and Li2SO3 (Fig. 4c, d and Supplementary Fig. 8b). These results suggest an SEI structure with an organic-rich inner layer of ca. 10 nm thick, and an inorganic-rich outer layer of ca. 2 nm thick, estimated from the calibrated sputtering rate of 4 nm per min in Si, and we thus denote the soft-stiff SEI as O–I structured SEI (Supplementary Fig. 9b).
Finally, the stiff-soft-stiff SEI created with multiple potential step for stripping in the ESP process leads to an I–O–I structured SEI, in which an organic-mixed middle layer is sandwiched by two inorganic-rich layers in the inner and outer regions, respectively (Supplementary Fig. 9c), with total SEI thickness of ca. 26 nm. Note that each layer of the I–O–I structured SEI contains components and structure that have subtle differences from those of O–I structured SEI (Fig. 4e, f): The I-rich inner layer contains Li–C moiety as a result of exposure of freshly generated Li surface upon Li dissolution; the O-mixed middle layer contains C–O–C moiety with negligible aliphatic C signal; and the outmost region of the I-rich outer layer is rich of LiNSO2CF3 while the LiF components are buried underneath. Noteworthy is that the S-based signals also indicate the presence of substantial amount of Li2S throughout the thickness of the SEI (Supplementary Fig. 8c).
Thus, the chemical composition and structure of the three SEIs revealed by XPS profile analysis and the mechanical properties probed by AFM force curve measurements are corroborative of each other: The all-inorganic SEI is stiff, while the O–I and I–O–I structured SEI have coupled elasticity (soft) and rigidity (stiff). In particular, the combination of two chemically different O–I layers behave mechanically like a cushion layer that can resist against dendrite growth. The apparent Young’s moduli are 7.2 ± 0.7 GPa for the O–I SEI and 3.5 ± 0.9 GPa for the combined O–I part of the I–O–I SEI. These values are smaller than that of the all–I SEI (10.9 ± 5.7 GPa), but are within the scope for rigid inorganic materials41,44,45 (Fig. 3c, f, i and Supplementary Note 3). Statistical analysis on thickness reveal total thickness of 22 ± 10 , 11 ± 2 , and 21 ± 3 nm for the all–I SEI, O–I SEI and I–O–I SEI, respectively, after correction of Li deformation (Supplementary Note 4 and Supplementary Fig. 5e). These values are on the smaller side given the reason that the organic-rich layer is deformed elastically and not penetrated upon pressing. The coupled elasticity and rigidity presented by the ultra-thin ultra-smooth I–O–I SEI are similar to the favorable mechanical property possessed by much thicker polymeric artificial SEIs that have been demonstrated to accommodate the interfacial fluctuation during the Li plating/stripping processes46,47,48.
MA +-rich SEI for enhanced conductivity
The exceedingly high MA+ surface concentration generated upon stripping of MA surface favors the reduction of TFSI or trifluoromethanesulfonate (OTf) anion to low oxidation states; in the case of Li electrode, it also provides the possibility for DOL to reduce and form Li-incorporated oligomer of (ROLi) n , rather than only the Li-ending ROLi chain, where R denotes for polymeric (CH3CH2OCH2O–) n or (CH3OCH2CH2O–) n moiety. Thus, it is feasible to create MA-rich SEIs in all cases, and a network-like framework incorporated with the polymeric (CH3CH2OCH2O–) n or (CH3OCH2CH2O–) n moiety in the case of Li electrode. In the following, we focus on Li electrode for further discussion on the SEI structure.
FTIR measurements disclose differences among the three types of SEIs (Fig. 4g and Supplementary Table 4), which supports the Li+-rich network-like structure of the O–I and I–O–I SEIs. First, the signal of band at 575 cm–1, attributed to the rocking mode of vibration of Li–O, increases in a sequence of I–O–I SEI > O–I SEI > all–I SEI, implying the amount of Li+ in the same sequence. Second, the overwhelmingly strong bands at ~625 cm–1, largely contributed by various stretching modes of the LiF clusters49, reveal that all the three types of SEIs contain substantial amount of LiF clusters. Furthermore, the broad background-like feature in the region of 1000–1400 cm–1 from C-based bands of organic components (e.g. C–C, C–O, and C–H) observed on O–I and I–O–I structured SEIs is an indication of presence of a cross-linked structure in these SEIs. These features suggest that Li+-rich oligmeric (ROLi) n moieties, more preferential than the Li-ending chain-like ROLi moiety, are formed in the I–O–I and O–I SEI (see Supplementary Note 5 and Supplementary Fig. 13). Hence, a network structure composed of oligmeric (ROLi) n incorporated with small inorganic molecules and clusters such as LiF and Li2S is proposed (see Supplementary Note 6), in which the rich amount of Li sites in the network is expected to provide channels that facilitate Li ion conduction. A conclusion can be reached based on the above analysis that the O–I and I–O–I types of SEI structures are not only on contrary to the I–I structure of the SEI of the soaked sample and disordered mosaic type of model for SEI, but also expected to exhibit fast transport of Li+ ions.
Indeed, the electrochemical impedance spectroscopy (EIS) measurements (Fig. 4h and Supplementary Table 5) show that the O–I and I–O–I types of SEIs have considerably smaller SEI resistance (21 and 28 Ω) as well as charge transfer resistance (23 and 30 Ω), compared with those of soaked sample (87 and 50 Ω), respectively. This illustrates that not only the Li+ transport through the thin SEI layer, but also the electron transfer across the Li–SEI interface, are significantly enhanced in the SEIs formed on the fresh and flat Li surfaces. Furthermore, given the thickness of 12 and 26 nm, conductivity of 3 × 10–8 and 5 × 10–8 S cm–1 are estimated for the O–I and I–O–I SEIs, respectively, which are of about ten times enhancement compared to those reported for SEI50.
Enhanced electrochemical performance of polished Li anodes
The Li-rich USUT SEI with the O–I and I–O–I multi-layered structures on flat Li surface bear all features for an ideal SEI. Of particular significance is the coupled rigidity and elasticity of these SEIs, which is a highly desirable mechanical property for stabilizing Li anodes (Fig. 5 and Supplementary Figs. 14–18). With these features and merits, Li thin-film anodes with the I–O–I SEIs can run over 500 and 300 stable cycles with 10% DOD (Fig. 5e) and 50% DOD (Supplementary Fig. 16c), respectively, at 10 mA cm–2. To separately evaluate the capability of the as-prepared I–O–I SEI for working on a foreign substrate, asymmetric Cu||Li cells were employed (see Methods section). As shown in Fig. 5g, the Cu||Li cell can run for over 200 cycles with 100% DOD under current density of 2 mA cm–2 and areal capacity of 1 mAh cm–2 with an average Coulombic efficiency of ~99% in an electrolyte with ordinary concentration of Li salt (1 M LiTFSI/DME-DOL) and without additives, approaching the performance achieved by employing high Li salt concentration and cycling protocol51.
Optimizing the ESP process can further enhance the performance of MA anodes for specific purposes. To accommodate Li–S batteries, additional 2 wt.% LiNO3 was added to the electrolyte of 1 M LiTFSI dissolved in 1,2-dimethoxyethane (DME) and DOL for polishing Li electrodes. The I–O–I SEI thus prepared significantly enhances the capability to withstand the reaction of Li surface with sulfur so that at least 450 cycles was maintained in the absence of LiNO3 with Li DOD of as high as 30% (see Methods section for the detailed DOD calculation) and Coulombic efficiency of nearly 100% (Supplementary Fig. 19). To further probe the potential application of the SEIs prepared in DOL-based electrolyte in Li metal batteries involving carbonate-based electrolyte, Li||LiCoO2 full cells in the electrolyte of 1 M LiPF6 in EC-DMC-EMC (V/V/V, 1/1/1) were constructed. The full cell using Li anode coated with I–O–I structured SEI exhibits a promising reversibility with Columbic efficiency of 99.7% and capacity retention of 83% after 200 cycles (Supplementary Fig. 20).
The above results demonstrate that despite of the large Young’s modulus of the SEI, the coarse all-inorganic structured SEI promotes dendrite growth; on contrary, the USUT multi-layered SEI with coupled rigidity and elasticity, even in the free-standing like state on Cu substrate, can suppress dendrite growth for long-term stability of Li anodes.
Enhanced stability of polished Na and K anodes
Na and K anodes created by ESP processes have all-inorganic type of SEI structure, which has been confirmed by the results of XPS, FTIR, and AFM (Supplementary Figs. 21–23), due to the reason that the currently adopted electrolytes compatible with Na and K anodes, NaOTf/diglyme and KTFSI/DME, respectively, do not contain DOL that would otherwise be an essence for creating organic-rich moieties. Nevertheless, compared with the all-inorganic SEI on the soaked Li anode, these SEIs are thinner, ca. 15 and 7 nm with apparent Young’s moduli of ca. 1.3 and 14.2 GPa for Na and K anodes, respectively. Importantly, however, since the primary problems for Na and K anodes arise from the poor quality of SEIs which then induces dendrite growth and causes excessive electrolyte consumption, the compact and stable Na+-rich and K+-rich SEIs on smooth Na and K surfaces may be adequate to circumvent the problems. Hitherto unreported cycling stability was achieved for Na anodes with 100% DOD for the Cu||Na cell, which can run for at least 550 cycles with Columbic efficiency close to 100% (Fig. 6d, e). Optical images show that the surface of polished Na remains metallic luster and relatively flat after 400 cycles (Fig. 6f). As for K anodes, symmetric cells were assembled with two polished K foil electrodes. A preliminary try of the ESP process leads to enhanced stability of at least 200 cycles (0.1 mA cm–2 with 0.02 mAh cm–2 in 1 M KTFSI/DME) (Supplementary Fig. 24).
Discussion
In conclusion, we have established a simple, but more than simple, ESP-based electrochemical approach to create near-perfect MA anode with near-ideal SEIs of the three alkali metal anodes. The methodology for lateral as well as vertical characterization of structure and property of the USUT SEI by AFM-based imaging and force spectroscopy and XPS depth profile analysis provide corroborative evidence that elucidate novel well-defined O–I and I–O–I types of multi-layered SEI structure. Such Li anodes have exhibited significantly enhanced cycling stability under high-current density with high DOD, and allow Li–S battery to operate in the absence of LiNO3 additive under high DOD. Also, such Li anodes with SEIs prepared in DOL-based electrolyte could be extended to match LiCoO2 cathodes in carbonate-based electrolytes. The prolonged cycling stability of Na anode with 100% DOD provides solid foundation for its practical applications. Our work illustrates that an ultra-smooth and ultra-thin SEI of near-perfect alkali metal anodes may be robust enough to protect the MA anodes for superior long-term cycling stability. The near-perfect alkali metal surfaces also provide tremendous opportunities in diverse fields including surface science, nanotechnology, and materials and energy sciences and technologies.
Methods
Electrochemical polishing and SEI formation of MA metal foil surface
The electrochemical polishing of MA anodes, employing a stripping-plating strategy, was conducted in a two-electrode cell that employed a larger alkali metal foil as the counter electrode before half cells or full cells were assembled. To facilitate simultaneous creation of flat MA surface and formation of smooth SEI, a potential which is sufficiently anodic of MA equilibrium potential yet within the potential window for electrolyte reduction was applied in the stripping step, during which MA dissolution and electrolyte reduction occurred concurrently. For Li anode, the potential range for stripping was chosen to be between 0.6 and 1.4 V in DOL-DME-LiTFSI electrolyte (Supplementary Fig. 1) and lasted for a period of 90 – 150 s to obtain a flat Li surface, which meanwhile supplies high concentration of Li+ near the surface to facilitate the initial stage of SEI formation. Multiple potential steps were applied between 0.6 and 1.0 V (vs. Li/Li+) to create multi-layered SEI. A galvanostatic cathodic polarization at low-current density is immediately followed as the plating step for a prolonged time, during which Li deposition and electrolyte reduction take place, which further smoothens the Li surface and completes the SEI formation. For Na and K anodes the stripping potentials were 0.8 V (vs. Na/Na+) and 0.2 V (vs. K/K+), respectively, which was followed by the plating step.
Electrochemical polishing of Li and Na thin-film electrodes
To test the electrochemical performance of Li and Na anodes with practical concern, thin film electrodes were prepared by a modified lithophilic or sodiophilic approach initially reported by the group of Yi Cui52. The procedure is described as follows: Cu foils (Ф13.0 × 0.024 mm, ≥99.7%, Power long) were washed by immersing in 0.1 M sodium oxalate for 5 min, followed by successive rinsing with deionized water, acetone and ethanol. After drying, the Cu foils were transferred to a thin film deposition platform (Explorer-14, Denton Vacuum) and sputtered with 50 nm Au to form lithophilic or sodiophilic Cu@Au foils. The Cu@Au foils were then transferred to Ar-filled glove box for Li or Na infiltration by dipping in a Li or Na melt obtained by heating a piece of metallic Li to over 250 °C or metallic Na to over 150 °C, until the melt was entirely entrapped. After cooling down to room temperature, Li or Na thin-film electrodes were obtained. The amount of the Li or Na melt was quantified depending on purposes. The Li or Na thin-film electrodes were subject to electrochemical polishing, following the same procedure for Li or Na foils, to obtain flat metal surfaces and to achieve desirable SEIs. To obtain free-standing like SEIs on modified Cu substrates for constructing anode-free type of Cu||Li and Cu||Na cells, respectively, the residual Li or Na on the corresponding thin film electrodes after electrochemical polishing were removed by electrochemical dissolution.
Measurements of electrochemical behaviors of alkali electrodes
Galvanostatic cycling and cathodic polarization behaviors were examined on LANHE CT2001A battery testing system (LAND Electronics) or VMP-300 multi Potentiostat (Bio-Logic Science). Both metal foil electrodes and metal thin-film electrodes were employed for evaluation of charge–discharge cycling behavior as well as the behavior against prolonged unidirectional galvanostatic polarization. For Li metal electrodes, Li foils were assembled into symmetric coin cells (CR2025-type) with soaked Celgard-2400 separator and 1 M LiTFSI/DME-DOL (1/1, V/V) electrolyte, or otherwise indicated. For galvanostatic cycling using Li thin-film electrodes at fixed DOD, typical 10 ± 10% mg of Li was entrapped onto Cu@Au foil (1.3 cm2), which can provide a total capacity of 38.6 mAh, based on the consideration of theoretical specific capacity of 3860 mAh g–1 for metallic Li. Cycling at a current density of 10 mA cm–2 (3 mAh cm–2) results in an charge–discharge capacity of 3 mAh cm–2 × 1.3 cm2 = 3.9 mAh, which is equivalent of 10% DOD. Cycling tests with Cu||Li cells were carried out by first depositing 1 mAh of Li onto the Cu@Au surface with free-standing SEI, followed by Li stripping up to 1.0 V vs. Li/Li+. For Na and K anodes, the configurations of coin cells were almost the same as Li anodes except the glass fiber separator. The electrolyte for Na-based cells and K-based cells are 1 M NaOTf in diglyme and 1 M KTFSI in DME, respectively.
Measurements of performances of Li–S batteries
Galvanostatic charge–discharge cycling was performed on LANHE CT2001A battery testing system. Li thin-film electrodes prepared by the lithophilic approach were used as the anodes for Li–S coin cells (CR2016-type). The amount of the metallic Li for entrapping was based on the actual loading of active materials for cathodes. For an example, the weight of Li was calculated according to the stoichiometric ratio of Li and S of the reaction 2Li + S → Li2S. The actual DOD for Li thin-film electrodes was 30%. The metal–organic-framework/sulfur composite5 was employed as cathode material. The composite contains a three-dimensional porous cobalt and nitrogen-doped graphitic carbon with 70 wt% sulfur loading (S@Co–N-GC). The cathode was prepared by mixing Co–N-GC/S composite powder, acetylene black, water-soluble polymer n-lauryl acrylate (LA) with a weight ratio of 7:2:1 onto Al foils and then dried at 60 °C under vacuum overnight. The electrolyte for battery testing was 1 M LiTFSI/DME-DOL (1/1, V/V), without any additives including LiNO3. Cycling was performed in the voltage range of 1.7−2.7 V. The geometric areas of all electrodes were 1.3 cm2 (13 mm in diameters) and the areal mass loading on the electrode was about 1.5 mg cm–2.
Measurements of performances of Li||LiCoO2 batteries
To test the potential application of polished Li anodes, having SEI prepared in the DOL-based electrolyte, in full cells in carbonate-based electrolytes, LiCoO2 (Power long) was used as a cathode material. The LiCoO2 cathode was prepared by mixing the active material LiCoO2, super carbon, and LA at a weight ratio of 8:1:1 in deionized water and ethanol to form a slurry. The slurry was pasted on Al foil and dried at 60 °C under vacuum overnight. The electrolyte for battery testing was 1 M LiPF6/EC-DMC-EMC (1/1/1, V/V/V). The electrode were 1.3 cm2 (13 mm in diameters) with LiCoO2 loading mass of approximately 6 mg cm−2, corresponding to the areal capacity of 1 mAh cm−2. Cells were cycled at 0.5 C (calculated based on the LiCoO2 cathode) in the potential range of 2.5–4.3 V.
Data availability
The data that support the plots within this paper and other finding of this study are available from the corresponding author upon reasonable request.
References
Bruce, P. G., Freunberger, S. A., Hardwick, L. J. & Tarascon, J. -M. Li-O2 and Li-S batteries with high energy storage. Nat. Mater. 11, 19–29 (2011).
Xu, W. et al. Lithium metal anodes for rechargeable batteries. Energy Environ. Sci. 7, 513–517 (2014).
Lin, D., Liu, Y. & Cui, Y. Reviving the lithium metal anode for high-energy batteries. Nat. Nanotech. 12, 194–206 (2017).
Kim, H. et al. Metallic anodes for next generation secondary batteries. Chem. Soc. Rev. 42, 9011–9034 (2013).
Li, Y.-J., Fan, J.-M., Zheng, M.-S. & Dong, Q.-F. A novel synergistic composite with multi-functional effects for high-performance Li-S batteries. Energy Environ. Sci. 9, 1998–2004 (2016).
Aurbach, D., McCloskey, B. D., Nazar, L. F. & Bruce, P. G. Advances in understanding mechanisms underpinning lithium–air batteries. Nat. Energy 1, 16128 (2016).
Hartmann, P. et al. A rechargeable room-temperature sodium superoxide (NaO2) battery. Nat. Mater. 12, 228–232 (2013).
Ren, X. & Wu, Y. A low-overpotential potassium-oxygen battery based on potassium superoxide. J. Am. Chem. Soc. 135, 2923–2926 (2013).
Aurbach, D., Gofer, Y. & Langzam, J. The correlation between surface chemistry, surface morphology, and cycling efficiency of lithium electrodes in a few polar aprotic systems. J. Electrochem. Soc. 136, 3198–3205 (1989).
Sun, Y., Liu, N. & Cui, Y. Promises and challenges of nanomaterials forlithium-based rechargeable batteries. Nat. Energy 1, 16071 (2016).
Xue, L. et al. Liquid K-Na alloy anode enables dendrite-free potassium batteries. Adv. Mater. 28, 9608–9612 (2016).
Bayley, P. M., Trease, N. M. & Grey, C. P. Insights into electrochemical sodium metal deposition as probed with in Situ 23Na NMR. J. Am. Chem. Soc. 138, 1955–1961 (2016).
Yan, K. et al. Selective deposition and stable encapsulation of lithium through heterogeneous seeded growth. Nat. Energy 1, 16010 (2016).
Xu, K. Electrolytes and interphases in Li-ion batteries and beyond. Chem. Rev. 114, 11503–11618 (2014).
Lu, Y., Tu, Z. & Archer, L. A. Stable lithium electrodeposition in liquid and nanoporous solid electrolytes. Nat. Mater. 13, 961–969 (2014).
Miao, R. et al. Novel dual-salts electrolyte solution for dendrite-free lithium-metal based rechargeable batteries with high cycle reversibility. J. Power Sources 271, 291–297 (2014).
Basile, A., Bhatt, A. I. & O’Mullane, A. P. Stabilizing lithium metal using ionic liquids for long-lived batteries. Nat. Commun. 7, 11794 (2016).
Tang, S. et al. An electrochemical surface-enhanced Raman spectroscopic study on nanorod-structured lithium prepared by electrodeposition. J. Raman Spectrosc. 47, 1017–1023 (2016).
Cheng, X.-B. et al. Implantable solid electrolyte interphase in lithium-metal batteries. Chem 2, 258–270 (2017).
Ding, F. et al. Dendrite-free lithium deposition via self-healing electrostatic shield mechanism. J. Am. Chem. Soc. 135, 4450–4456 (2013).
Suo, L., Hu, Y.-S., Li, H., Armand, M. & Chen, L. A new class of Solvent-in-Salt electrolyte for high-energy rechargeable metallic lithium batteries. Nat. Commun. 4, 1481 (2013).
Zheng, J. et al. Highly stable operation of lithium metal batteries enabled by the formation of a transient high-concentration electrolyte layer. Adv. Energy Mater. 6, 1502151 (2016).
Zheng, G. et al. Interconnected hollow carbon nanospheres for stable lithium metal anodes. Nat. Nanotech. 9, 618–623 (2014).
Huang, C. et al. Manipulating surface reactions in lithium-sulphur batteries using hybrid anode structures. Nat. Commun. 5, 3015 (2014).
Kozen, A. C. et al. Next-generation lithium metal anode engineering via atomic layer deposition. ACS Nano 9, 5884–5892 (2015).
Kim, J. -S., Kim, D. W., Jung, H. T. & Choi, J. W. Controlled lithium dendrite growth by a synergistic effect of multilayered graphene coating and an electrolyte additive. Chem. Mater. 27, 2780–2787 (2015).
Li, N. W., Yin, Y. X., Yang, C. P. & Guo, Y. G. An artificial solid electrolyte interphase layer for stable lithium metal anodes. Adv. Mater. 28, 1853–1858 (2016).
Lin, D. et al. Layered reduced graphene oxide with nanoscale interlayer gaps as a stable host for lithium metal anodes. Nat. Nanotech. 11, 626–632 (2016).
Hartmann, P. et al. A comprehensive study on the cell chemistry of the sodium superoxide (NaO2) battery. Phys. Chem. Chem. Phys. 15, 11661–11672 (2013).
Wibowo, R., Aldous, L., Jacobs, R. M. J., Manan, N. S. A. & Compton, R. G. Monitoring potassium metal electrodeposition from an ionic liquid using in situ electrochemical-X-ray photoelectron spectroscopy. Chem. Phys. Lett. 509, 72–76 (2011).
Seh, Z. W. & Sun, J., Sun, Y. & Cui, Y. A highly reversible room-temperature sodium metal anode. ACS Cent. Sci. 1, 449–455 (2015).
Luo, W. et al. Ultrathin surface coating enables the stable sodium metal anode. Adv. Energy Mater. 7, 1601526 (2017).
Ren, X. et al. Understanding side reactions in K-O2 batteries for improved cycle life. ACS Appl. Mater. Interfaces 6, 19299–19307 (2014).
Gauthier, M. et al. Electrode-electrolyte interface in Li-ion batteries: current understanding and new insights. J. Phys. Chem. Lett. 6, 4653–4672 (2015).
Verma, P., Maire, P. & Novák, P. A review of the features and analyses of the solid electrolyte interphase in Li-ion batteries. Electrochim. Acta 55, 6332–6341 (2010).
Gireaud, L., Grugeon, S., Laruelle, S., Yrieix, B. & Tarascon, J. M. Lithium metal stripping/plating mechanisms studies: A metallurgical approach. Electrochem. Commun. 8, 1639–1649 (2006).
Aurbach, D. et al. On the surface chemical aspects of very high energy density, rechargeable Li-sulfur batteries. J. Electrochem. Soc. 156, A694–A702 (2009).
Howlett, P. C., Brack, N., Hollenkamp, A. F., Forsyth, M. & MacFarlane, D. R. Characterization of the lithium surface in N-Methyl-N-alkylpyrrolidinium bis(trifluoromethanesulfonyl)amide room-temperature ionic liquid electrolytes. J. Electrochem. Soc. 153, A595–A606 (2006).
Zhong, Y. X. et al. Resolving fine structures of the electric double layer of electrochemical interfaces in ionic liquids with an AFM tip modification strategy. J. Am. Chem. Soc. 136, 14682–14685 (2014).
Zhang, X. et al. Probing double layer structures of Au (111)-BMIPF6 ionic liquid interfaces from potential-dependent AFM force curves. Chem. Commun. 48, 582–584 (2012).
Zhang, J. et al. Direct observation of inhomogeneous solid electrolyte interphase on MnO anode with atomic force microscopy and spectroscopy. Nano Lett. 12, 2153–2157 (2012).
Qiao, R. et al. Distinct solid-electrolyte-interphases on Sn (100) and (001) electrodes studied by soft X-ray spectroscopy. Adv. Mater. Interfaces 1, 1300115 (2014).
Peled, E., Golodnitsky, D. & Ardel, G. Advanced model for solid electrolyte interphase electrodes in liquid and polymer electrolytes. J. Electrochem. Soc. 144, L208–L210 (1997).
Zheng, J. et al. 3D visualization of inhomogeneous multi-layered structure and Young’s modulus of the solid electrolyte interphase (SEI) on silicon anodes for lithium ion batteries. Phys. Chem. Chem. Phys. 16, 13229–13238 (2014).
Liu, X. R. et al. Single nanowire electrode electrochemistry of silicon anode by in situ atomic force microscopy: solid electrolyte interphase growth and mechanical properties. ACS Appl. Mater. Interfaces 6, 20317–20323 (2014).
Li, G. et al. Organosulfide-plasticized solid-electrolyte interphase layer enables stable lithium metal anodes for long-cycle lithium-sulfur batteries. Nat. Commun. 8, 850 (2017).
Liu, Y. et al. An artificial solid electrolyte interphase with high Li-ion conductivity, mechanical strength, and flexibility for stable lithium metal anodes. Adv. Mater. 29, 1605531 (2016).
Li, N. W. et al. A flexible solid electrolyte interphase layer for long-life lithium metal anodes. Angew. Chem. Int. Ed. 130, 1521–1525 (2018).
Oschetzki, D. & Rauhut, G. Pushing the limits in accurate vibrational structure calculations: anharmonic frequencies of lithium fluoride clusters (LiF) n , n = 2–10. Phys. Chem. Chem. Phys. 16, 16426–16435 (2014).
Zaban, A., Zinigrad, E. & Aurbach, D. Impedance spectroscopy of Li electrodes .4. A general simple model of the Li-solution interphase in polar aprotic systems. J. Phys. Chem. 100, 3089–3101 (1996).
Qian, J. et al. Anode-free rechargeable lithium metal batteries. Adv. Funct. Mater. 26, 7094–7102 (2016).
Liang, Z. et al. Composite lithium metal anode by melt infusion of lithium into a 3D conducting scaffold with lithiophilic coating. Proc. Natl Acad. Sci. USA 113, 2862–2867 (2016).
Acknowledgements
This work was supported by the MOST projects (2015CB251102, 2012CB932902) and the NSFC projects (U1305246, 21621091, 21473147, 21533006, 21673193). We thank the XAFS station (BL14W1) of the Shanghai Synchrotron Radiation Facility. We are grateful to Profs. Z.Q. Tian, H.X. Yang, X.P. Ai, N.F. Zheng, H. Li, Y.G. Guo, J.B. Zhao, and M.S. Chen for helpful discussions and advices, Dr. X.B. Lian and Mr. X.L. Li for experimental assistance, and Mr. Y. Tian for help in graphic editing.
Author information
Authors and Affiliations
Contributions
B.-W.M., Q.-F.D., and Y.G. conceived and designed the experiments, analyzed the results, and participated in writing the manuscript. W.-W.W. and Y.G. carried out AFM measurements. Y.G. and Q.-H.W. conducted XPS experiments. Y.G. and S.T. conducted FTIR experiments. Y.-J.L., W.-Q.H., and Y.G. conducted battery performance measurements. D.-Y.W. and Y.F. contributed to calculation and interpretation of IR spectra. J.-W.Y., M.-S.Z., C.-H.F., and Q.-H.Z. contributed to discussions and interpretation of results and Z.-B.C. to technical assistance.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gu, Y., Wang, WW., Li, YJ. et al. Designable ultra-smooth ultra-thin solid-electrolyte interphases of three alkali metal anodes. Nat Commun 9, 1339 (2018). https://doi.org/10.1038/s41467-018-03466-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-03466-8
This article is cited by
-
A dicarbonate solvent electrolyte for high performance 5 V-Class Lithium-based batteries
Nature Communications (2024)
-
Regulating ion transport behaviors toward dendrite-free potassium metal batteries: recent advances and perspectives
Rare Metals (2024)
-
Regulate the chemical property of the carbon nanospheres layer modified on the surface of sodium metal anode to achieve high-load battery
Nano Research (2024)
-
Nanoarchitecture factors of solid electrolyte interphase formation via 3D nano-rheology microscopy and surface force-distance spectroscopy
Nature Communications (2023)
-
Naked metallic skin for homo-epitaxial deposition in lithium metal batteries
Nature Communications (2023)