Abstract
Emission control of colloidal quantum dots (QDs) is a cornerstone of modern high-quality lighting and display technologies. Dynamic emission control of colloidal QDs in an optoelectronic device is usually achieved by changing the optical pump intensity or injection current density. Here we propose and demonstrate a distinctly different mechanism for the temporal modulation of QD emission intensity at constant optical pumping rate. Our mechanism is based on the electrically controlled modulation of the local density of optical states (LDOS) at the position of the QDs, resulting in the modulation of the QD spontaneous emission rate, far-field emission intensity, and quantum yield. We manipulate the LDOS via field effect-induced optical permittivity modulation of an ultrathin titanium nitride (TiN) film, which is incorporated in a gated TiN/SiO2/Ag plasmonic heterostructure. The demonstrated electrical control of the colloidal QD emission provides a new approach for modulating intensity of light in displays and other optoelectronics.
Similar content being viewed by others
Introduction
Tailoring light emission of quantum emitters, such as semiconductor quantum dots (QDs), is a central theme of nanotechnology1. The spontaneous emission decay rate of a solid state emitter can be modified by coupling the emitter to a nanostructured environment with a tailored local density of optical states (LDOS)2,3. Previously this phenomenon, also known as the Purcell effect, has yielded a 540-fold increase of the emission decay rate and a simultaneous 1900-fold increase of total emission intensity for colloidal QDs coupled to a plasmonic nanocavity4. Typically, the properties of the nanostructured environment are fixed at the time of fabrication, which also sets the spontaneous emission decay rate of the emitter. Conventionally, the power radiated from an array of quantum emitters is dynamically modulated (actively controlled) by changing the optical5 or electrical6 pump intensity within a given nanostructured environment. On the other hand, the coupling of emitters to a local environment with tunable optical properties, as done in this study, enables the modulation of the emitter decay rate while keeping the optical pump power constant. Previous experiments have demonstrated the tunability of the narrowband emission of an epitaxial QD, which is coupled to a high-quality factor dielectric cavity7,8. However, these experiments can be performed only at cryogenic temperatures, making them less amenable for immediate practical applications.
Recently, there has been considerable interest in studying active nanophotonic structures with tunable optical responses9. Active plasmonic structures are especially interesting candidates for tuning the emission of room temperature broadband solid state emitters. This is due to the fact that they offer small optical mode volumes and relatively low-quality factors, thus eliminating the necessity of careful alignment of cavity and emitter resonances. Previous works have reported field-effect tuning of the carrier density and Fermi level in graphene10, transparent conducting oxides11, and silicon12 to modulate transmittance and reflectance of plasmonic structures in the near- and mid-infrared wavelength range. Previous work has adopted this tuning mechanism to electrically modulate the 1.5 μm wavelength emission of trivalent erbium ions coupled to a graphene sheet13. In an alternative approach, a previous study has used the optically induced phase transition in vanadium dioxide to modulate near-infrared emission of erbium ions coupled to Salisbury-screen-type heterostructure14. However, field effect modulation of the optical response of a nanophotonic structure has not been demonstrated at visible wavelengths. This is primarily due to the relatively low carrier concentrations of previously used doped oxides and semiconductors11,12 that limit their epsilon-near-zero (ENZ) wavelengths to the near- or mid-infrared wavelength range.
Here we use degenerately doped n-type titanium nitride (TiN)15,16,17,18,19,20, with an ENZ wavelength in the visible spectrum, to demonstrate the field effect tunable optical response of a gated TiN/SiO2/Ag heterostructure at visible wavelengths. We embed InP/ZnS core–shell colloidal QDs in the SiO2 layer of the tunable TiN/SiO2/Ag heterostructure and study emission properties of the QDs while biasing the TiN and Ag layers with respect to each other. We observe a temporal modulation of the QD spontaneous emission rate, far-field emission intensity, and quantum yield that occurs due to the modulation of the LDOS at the position of the QDs. The optoelectronic device fabricated in this work exemplifies how conventional electronic components, in our case, a metal-oxide-semiconductor capacitor, can be adapted to the field of nanophotonics to yield the bias-controlled modulation of the PL intensity of fluorophores. Our proof-of-principle experiment demonstrates an active plasmonic mechanism for modulating visible light that is extensible to other types of quantum emitters.
Results
Field effect modulation of dielectric permittivity of TiN
The schematic of our TiN/SiO2/Ag heterostructure is shown in Fig. 1a. As seen in the high-resolution transmission electron microscopic image, the fabricated heterostructure consists of an optically thick Ag, a 9 nm-thick insulating SiO2 spacer, and a 7 nm-thick conductive TiN layer (Fig. 1b). Visible-emitting colloidal QDs with diameters of 4–5 nm are embedded in the insulating SiO2 spacer (Fig. 1c). In our work, we use InP/ZnS core–shell colloidal QDs (hereafter, InP QDs), which are of greater application interest because they are free of heavy metals and may be beneficial in considering health and environmental concerns. When a bias is applied between TiN and Ag, a charge depletion or accumulation layer is formed in the TiN at the TiN/ SiO2 interface (Fig. 1d and Supplementary Fig. 1). This results in a modulation of the complex refractive index of TiN and, therefore, also modulation of the LDOS at the position of QDs embedded in the SiO2 layer. Depending on the deposition conditions, TiN can either be in an optically dielectric phase (Re(ɛ) > 0) or in an optically plasmonic phase (Re(ɛ) < 0) in the visible wavelength range (Fig. 2). Moreover, one can identify a carrier concentration that yields ENZ-TiN (−1 < Re(ɛ) < 1), which is crucial for observation of reflectance modulation (Supplementary Fig. 4).
Dynamic control of emission rate of QD via LDOS modulation
The optical measurements performed on the ENZ-TiN/SiO2/Ag heterostructures at the QD emission wavelength of λ = 630 nm show a relative reflectance modulation of 18% (normalized to the reflectance at zero bias) when the gate voltage is varied between −1 and +1 V (Fig. 3a). Additionally, we demonstrate that the device has a modulation speed exceeding 20 MHz (Supplementary Fig. 5). The reflectance is modulated by changing the carrier density under field effect gate control in the TiN layer. This in turn modulates the real part of dielectric permittivity of the TiN from positive to negative values through the so-called ENZ regime, which marks the borderline between dielectric and plasmonic media (Fig. 3b). Moreover, when we replace the top TiN electrode by a titanium (Ti) electrode of identical thickness, we observe no reflectance modulation under an applied bias (Fig. 3c, d). This shows that the TiN plays a crucial role in the observed optical modulation (for reflectance calculations, see Supplementary Fig. 6).
Having established gate-tunable reflectance, we study emission modulation of InP QDs embedded in the SiO2 spacer layer of the TiN/SiO2/Ag plasmonic heterostructure (Fig. 1a). The dependence of the photoluminescence (PL) intensity on applied bias at the QD peak emission wavelength of λ = 630 nm is shown in Fig. 4a (for optical setup, see Methods). As seen in Fig. 4a, the PL intensity monotonically increases with positive bias and monotonically decreases with negative bias. At λ = 630 nm, the PL intensity change (normalized to the PL intensity at zero bias) is as high as 15% when gate voltage is varied between −1 and +1 V. On the other hand, for QDs embedded in the Ti/SiO2/Ag passive heterostructure (the same device was used for Fig. 3c), no PL intensity modulation is observed under applied bias (Fig. 4b). In our experiments, we observe no shift of the wavelength of PL peak intensity under applied bias in both cases when QDs are embedded in a tunable TiN/SiO2/Ag or passive Ti/SiO2/Ag heterostructure (Supplementary Figs. 7 and 8). Hence, at applied electric fields of 1.1 MV cm−1, our InP QDs show no quenching or red-shift of emission, which is characteristic for cadmium-based core–shell colloidal QDs21,22. This is attributable to the large bandgap difference between InP core and ZnS shell materials21. Thus the electron and hole wave functions are well confined to the core of the core/shell QDs with an external electric field. The fact that we observe both an increase and decrease of PL intensity, depending on the polarity of the electric field, provides additional evidence that the observed modulation of PL intensity is not caused by the change of the internal state of the QDs under applied bias. If this were the case, the observed modulation of the PL intensity would depend only on the magnitude of the electric field and not on its direction.
The measured PL intensity spectrum shows significant modulation only around the central emission wavelength of λ = 630 nm. This seems to contradict the theoretical prediction of the broadband LDOS modulation under applied bias (Fig. 4d). The apparent contradiction is resolved by recalling that the measured PL intensity spectrum originates from an inhomogeneously broadened QD ensemble. Note that the relative PL intensity modulation of each QD does not depend on the emission wavelength (Supplementary Fig. 7c). In the measured ensemble, the size distribution of the QDs is such that a large fraction of the individual QDs emits around the wavelength of λ = 630 nm, yielding a brighter PL signal at λ = 630 nm.
Once we have demonstrated the PL intensity modulation of the QDs, we perform time-resolved PL measurements to identify the lifetime of the QDs embedded in the TiN/SiO2/Ag heterostructures. When no electrical bias is applied, the measured lifetime of the InP QDs is 390 ps. This shows that embedding the QDs into the TiN/SiO2/Ag plasmonic heterostructure results in 28-fold reduction of the QD lifetime as compared to the lifetime of the QDs on bare silicon (Supplementary Fig. 10). At applied electrical bias of +1 V, the lifetime of the QDs decreases by 12%, while at the bias of −1 V, the lifetime increases by 18% (Fig. 4c). Our calculations indicate that the optical frequency electric field radiated by a QD is tightly confined in the SiO2 layer and shows a considerable enhancement at the interface with TiN (Fig. 4d). As a result, the LDOS in the middle of the SiO2 layer is sensitive to the modulation of the complex refractive index of the TiN film (Supplementary Fig. 11). The observed lifetime as well as the PL intensity and reflectance modulation reported in our work cannot be fully explained by changing the carrier concentration in the Drude term of the Drude–Lorenz model that describes the dielectric permittivity of TiN. At high carrier concentrations (N = 1.8 × 1022 cm−3 for ENZ-TiN), a number of different effects may contribute to the observed optical modulation, such as the dependence of the electron effective mass on the applied voltage due to the nonparabolicity of the conduction band and the dependence of the electron mobility on the applied bias. In our theoretical calculations (Fig. 4d), we assume that the dielectric permittivity of the 1 nm-thick accumulation layer of TiN is given by the measured dielectric permittivity of the TiN film with carrier concentration of N = 4.1 × 1022 cm−3 (Fig. 2). Strictly speaking, this assumption is not accurate; however, it allows us to estimate the sensitivity of the calculated LDOS with respect to the variation of the refractive index of the 1 nm-thick accumulation layer (Fig. 4d).
To summarize, in our experiment we observe either a simultaneous increase of the PL intensity and total decay rate of emission Γ tot or a simultaneous decrease of the PL intensity and Γ tot. However, the observed PL intensity modulation it not necessarily caused the actively changed LDOS. For example, variation of excitation field intensity under applied bias could also result in modulation of PL intensity. To investigate this possibility, we measure the absorbance spectrum of the ENZ-TiN/SiO2/Ag plasmonic heterostructure at a laser excitation wavelength of λ = 375 nm as a function of applied voltage (Supplementary Fig. 13). We observe a slight decrease of the absorbance at positive voltages that implies increased excitation intensity, and consequently, increased PL intensity. The observed PL intensity modulation can also be attributed to the reduction or increase of the absorbance of the ENZ-TiN/SiO2/Ag plasmonic heterostructure at QD emission wavelengths (Supplementary Fig. 13). However, we would like to point out that the absorbance modulation at the QD emission wavelength and modulation of the total decay rate of a QD are interrelated since the QDs are placed in the immediate vicinity of the TiN layer (Fig. 1). In what follows, we further investigate how the LDOS modulation contributes to the observed PL modulation.
Active control of quantum yield of QDs
Once a QD has been excited by absorbing a photon, it may undergo a transition to the ground state either by far-field photon emission (radiative pathway) or via non-radiative processes, such as energy transfer via non-radiative dipole–dipole coupling23. An important metric to quantify the emission properties of fluorophores is the quantum yield, which is the probability of an excited QD to relax via the radiative pathway. When no electrical bias is applied, the estimated quantum yield of the InP QDs embedded in the SiO2 layer of plasmonic heterostructure is 15% (Supplementary Fig. 12).
Our measurements show that under positive bias the radiative emission decay rate (Γ rad) increases by 15%, while under negative bias Γ rad decreases by 11% (Fig. 5a). This amounts to a relative modulation of Γ rad of 26% when the applied gate voltage varies between −1 and +1 V (see Methods for further details). The measured voltage-dependent total emission decay rate (Fig. 4c) and radiative decay rate can be used to determine the variation of QD quantum yields η = Γ rad/Γ tot under applied bias. We observe a 35% relative increase of the quantum yield at an applied bias of +1 V and 21% relative decrease of the quantum yield at an applied bias of −1 V (Fig. 5b). This in situ control of quantum yield is a unique consequence of the bias-induced modulation of LDOS. We emphasize that the LDOS, radiative emission decay rate, and quantum yield do not depend on the absorbance at the excitation wavelength of λ = 375 nm.
To summarize, we observe that at positive bias the increase in the PL intensity is always accompanied by increases in both total and radiative emission decay rates: Γ tot and Γ rad (Figs. 4 and 5). This implies that the LDOS modulation also contributes to an increase in PL intensity under applied bias along with reduced absorption of the ENZ-TiN/SiO2/Ag plasmonic heterostructure at the QD emission wavelength λ = 630 nm and slightly increased excitation intensity at λ = 375 nm. Although, as mentioned above, at the QD emission wavelength the LDOS modulation and the absorbance modulation cannot be fully decoupled. In previously reported cases of bias-induced LDOS modulation, an increase of the LDOS has always been accompanied by a decrease in the PL intensity, which implies that the applied bias primarily affects the non-radiative decay rate13,23. In contrast, in our work we observe a simultaneous increase in LDOS and PL intensity.
Discussion
The ability to electrostatically control the spontaneous emission rate, intensity, and quantum yield of colloidal QDs via modulation of LDOS may lead to a number of applications, since this represents a means to dynamically modulate emitted intensity without electrical injection of carriers into the QD emitters. Thus more optimized structures featuring electrostatic LDOS modulation of optically pumped QDs have potential for application in optically efficient ultrathin displays with long durability, reduced pixel size, and large viewing angle. We note that modern commercially available QD displays typically use blue light emitting diodes (LEDs) to optically pump colloidal QDs, which down-convert the blue LED emission into red and green light24. The resulting QD light emission is used for backlighting, while the image is formed by the same principles as in regular liquid crystal displays25. Using colloidal QDs with narrowband emission at controllable wavelengths has enhanced the color gamut of modern displays, enabling generation of more realistic and vivid colors. The proof-of-concept experiment demonstrated here suggests that emission control of optically pumped QDs may be directly used for image formation, potentially eliminating necessity of the liquid crystal light modulator. Unlike the case of QD-LEDs, where both QD excitation and emission intensity modulation are achieved via current injection into the QDs, our approach decouples the excitation and modulation mechanisms. As a result, our method does not lead to deterioration of the emission properties of QDs typically observed in QD-LEDs. Moreover, due to capacitive nature of the device architecture used for our modulation mechanism, there is no need to place QDs between p- and n-type materials. This eliminates the necessity of the careful band alignment of the constituent materials.
When considering display applications, it is crucial to have large relative modulation of PL intensity. An obvious improvement would be to replace SiO2 by a gate dielectric with higher DC permittivity, such as Al2O3 or HfO2. The relative modulation strength of our device can further be improved by incorporating a TiN layer into a plasmonic cavity that can be formed, for instance, by placing an appropriately designed patch antenna on top of the Ag/SiO2/TiN heterostructure4,26. Previous research has shown that the lifetime of a quantum emitter embedded in the dielectric gap of the patch antenna resonator is very sensitive to gap thickness26. If the resonant wavelength of the cavity is aligned with the emission wavelength of the emitter, this configuration will yield a large modulation of the PL intensity under an applied bias. Moreover, using a patch antenna resonator can increase emission intensity by orders of magnitude4, thus making the whole device more energy efficient. The energy efficiency of our device can be further improved by using QDs with a higher quantum yield and by using a QD ensemble with narrower spectral width of PL intensity (for a more detailed discussion, see Supplementary Note 7).
Our findings can be readily used for visible light communication systems such as Li-Fi, a counterpart of Wi-Fi that utilizes the visible spectral range27,28. Li-Fi denotes the proposed future visible light communication scheme, in which temporally modulated LED lamps are likely candidates as sources for an optical wireless communication system to transmit information encoded via intensity variations in the emitted light. Cadmium-free QDs are currently used for improving the quality of light of LED light bulbs by making the emitted light more pleasant for the human eye. In many lighting devices, QDs absorb blue LED light and re-emitted as light downshifted in wavelength to achieve a desired lamp emission color characteristic. It has been suggested that light intensity modulations could be achieved by varying the intensity of the blue LED pump27,28. Instead of varying the intensity of the LED pump light source, we propose to dynamically control the emission properties of QDs via LDOS modulation. Our proposed approach would enable the realization of a more flexible visible light communication system, where, for example, an actively tunable wavelength multiplexing device could be enabled by separately modulating the emission intensity of QDs with different emission wavelengths. We would like emphasize that, within the context of visible light communication systems, a large amplitude modulation of the emitted light is not necessary27,28.
Methods
Sample fabrication
We formed a dilute solution of commercially available InP/ZnS core–shell QDs (2 mgmL−1 in toluene) in isopropanol, with a volume ratio of 1:20 and a quantum yield of 17%. Next, we fabricated TiN/SiO2/Ag plasmonic heterostructures with QDs embedded in the SiO2 layer by depositing 80 nm of Ag, followed by 4 nm of SiO2 on a mica substrate via electron-beam evaporation at a chamber pressure of 10−7 torr. We then spin-coated the diluted QD solution for 30 s at 4000 rpm to spread the solution evenly and subsequently deposited another 4 nm of SiO2 via electron-beam evaporation. In this way, we obtained a layer of QDs embedded in the SiO2 layer. As a final step, we sputtered 7 nm TiN film with DC magnetron sputtering at a chamber pressure of 7.5 × 10−7 torr and at room temperature. In accordance with previously reported results16,17,18, varying argon/nitrogen flow rate, DC power, growth temperature, and growth substrate strongly influenced the optical properties of the deposited films. Using Hall measurements, we identified the growth conditions enabling the carrier concentration of the fabricated TiN films to lie between N = 5.9 × 1020 cm−3 and N = 4.1 × 1022 cm−3, while the mobility ranged from 0.059 to 5.8 cm2 V−1 s−1 (Supplementary Tables 1 and 2). Each deposition step was undertaken with an appropriate face mask made of stainless steel to permit easy bias application configuration in the final device. The working area of the device was 1 × 1 mm2. The thicknesses of the constituent layers in the fabricated TiN/SiO2/Ag heterostructure were determined via cross-sectional transmission electron microscopic analysis. To prepare the sample for the electron microscopic analysis, we used dual-beam focused gallium ion-beam (FIB, FEI model Nova 200) to FIB-cut the heterostructure normal to the interface. The diameter of the QDs was 4–5 nm, as determined by high-resolution transmission electron microscopy (FEI Tecnai TF20 STEM). To determine the material parameters of the sputtered TiN films, we fabricated additional large-area control samples that consisted of 35 nm of SiO2 and about 30 nm of TiN deposited on Si substrate under the same growth conditions as the ones used to fabricate our final devices. We used large-area control samples for both Hall and ellipsometry (J.A.Woollam Co. model VASE) measurements. Since the optical properties of TiN film sensitively depend on the choice of the substrate19, our control samples used for both ellipsometry and Hall measurements were deposited on SiO2.
Optical measurements
Reflectance spectra were taken under normal incidence with an objective 5× (Olympus, with a numerical aperture of 0.14) focusing a supercontinuum laser (Fianium) down to a small spot of 3 μm in diameter. The reflected signal was measured by a silicon photodetector. The micro-PL and time-resolved PL measurements were taken on an inverted microscope (Zeiss, Inc.) equipped with a spectrometer consisting of a monochromator and a liquid-nitrogen-cooled CCD camera. For PL lifetime measurements, a 375 nm picosecond laser diode (70 ps pulse duration, 40 MHz repetition rate; PicoQuant) excitation source was used, and a 375 nm band pass filter was placed after laser source to purify the laser beam. A 100× objective lens with a numerical aperture of 0.9 (Zeiss, Inc.) was used to focus the pulsed laser to a small spot of 1.6 × 10−6 cm2 with an estimated peak power density of 7.5 kW cm−2. We measured QD lifetime by using a time-correlated single photon counting module (PicoHarp 300, PicoQuant) and single photon avalanche diode detector (PDM 50 T, MicroPhoton Devices)29. We used periodic pulsed laser excitation and collect photons from multiple excitation and emission cycles. This approach allowed us to construct a histogram of number of photon counts at different photon arrival times. The time resolution of our lifetime measurement setup was 200 ps. PL lifetime decays were acquired from a particular region <5 μm in diameter that was illuminated with an iris. During lifetime measurements, a 600–650 nm band-pass filter was used. When measuring the QD lifetime, we illuminated the same region of the sample that was used for PL measurements. This enabled direct comparison of the QD lifetime and PL intensity data sets and further analysis of the radiative and non-radiative recombination rate. Even though we measured slight differences in the emission spectrum depending on the part of the sample that was illuminated, we obtained reproducible data when the position of the illumination spot was fixed. We also verified that the shape of a PL intensity spectrum does not depend on pump field intensity (Supplementary Fig. 16). In addition, the voltage bias was applied to the heterostructure by a source meter (Keithley 2400 source-meter).
Electromagnetic simulations
Numerical electromagnetic simulations were performed using a finite difference time domain method. When modeling the performance of our structure under applied bias, we assumed that the complex refractive index of a 1 nm-thick TiN layer at the interface with SiO2 is modulated by the applied bias (Supplementary Figs. 6, 9 and 11).
Quantum yield measurements
To measure the quantum yield of our InP QDs, we used a standard florescence dye (Rhodamine 6G) with a known quantum yield of 95% (Supplementary Fig. 12). When calculating radiative emission decay rate, we took into account that our InP QDs were embedded in the SiO2 layer of the ENZ-TiN/SiO2/Ag heterostructure. Since the QDs were embedded in the ENZ-TiN/SiO2/Ag heterostructure, a portion of the laser excitation (λ = 375 nm) was absorbed in the top TiN layer, which affected the excitation intensity of the QDs. To estimate the effect of the possible variation of the excitation intensity, we measured the absorbance of the ENZ-TiN/SiO2/Ag plasmonic heterostructure at an excitation wavelength of λ = 375 nm under an applied bias. As seen in Supplementary Figs. 13 and 14, the absorbance stayed almost constant for negative biases and showed a slight decrease for positive biases. Since absorption primarily occurred in the TiN layer, high absorbance resulted in the reduced excitation intensity of the QDs. Taking this into account, the bias dependent radiative emission decay rate (Γ rad) given by the following formula26,30:
Here \(\Gamma _{{\mathrm{rad}}}^{\mathrm{0}}\) the radiative emission decay rate under zero bias, \(I_{\rm{PL}}^0\) the peak PL intensity under zero bias, I PL(V G) the bias-dependent PL intensity, \(A_{{\mathrm{laser}}}^0\) the absorbance in the ENZ-TiN/SiO2/Ag heterostructure at an excitation wavelength of λ = 375 nm at zero bias, and A laser(V G) the bias dependent absorbance at λ = 375 nm. V G denotes the gate voltage applied between the Ag and TiN layers in the TiN/SiO2/Ag heterostructure. We would like to emphasize that absorbance in the TiN/SiO2/Ag heterostructure primarily occurred in TiN layer. To calculate the bias-dependent quantum yield of our QDs embedded in TiN/SiO2/Ag heterostructure, we used Eq. (1) and took into account that quantum yield of the emitter η was defined as a ratio of radiative and total decay rates η = Γ rad/Γ tot.
Data availability
The data sets analyzed during this study are available from the corresponding author on reasonable request.
References
Shirasaki, Y., Supran, G. J., Bawendi, M. G. & Bulovic, V. Emergence of colloidal quantum-dot light-emitting technologies. Nat. Photon. 7, 13–23 (2013).
Novotny, L. & Hecht, B. Principles of Nano-optics, 2nd edn (Cambridge University Press, Cambridge, 2012).
Pelton, M. Modified spontaneous emission in nanophotonic structures. Nat. Photon. 9, 427–435 (2015).
Hoang, T. B., Akselrod, G. M. & Mikkelsen, M. H. Ultrafast room-temperature single photon emission from quantum dots coupled to plasmonic nanocavities. Nano Lett. 16, 270–275 (2016).
Grandidier, J. et al. Gain-assisted propagation in a plasmonic waveguide at telecom wavelength. Nano Lett. 9, 2935–2939 (2009).
Colvin, V. L., Schlamp, M. C. & Alivisatos, A. P. Light-emitting-diodes made from cadmium selenide nanocrystals and a semiconducting polymer. Nature 370, 354–357 (1994).
Jin, C. Y. et al. Ultrafast non-local control of spontaneous emission. Nat. Nanotechnol. 9, 886–890 (2014).
Laucht, A. et al. Electrical control of spontaneous emission and strong coupling for a single quantum dot. New J. Phys. 11, 023034 (2009).
Ferrera, M. et al. Dynamic nanophotonics [Invited]. J. Opt. Soc. Am. B 34, 95–103 (2017).
Brar, V. W., Jang, M. S., Sherrott, M., Lopez, J. J. & Atwater, H. A. Highly confined tunable mid-infrared plasmonics in graphene nanoresonators. Nano Lett. 13, 2541–2547 (2013).
Huang, Y. W. et al. Gate-tunable conducting oxide metasurfaces. Nano Lett. 16, 5319–5325 (2016).
Olivieri, A. et al. Plasmonic nanostructured metal-oxide-semiconductor reflection modulators. Nano Lett. 15, 2304–2311 (2015).
Tielrooij, K. J. et al. Electrical control of optical emitter relaxation pathways enabled by graphene. Nat. Phys. 11, 281–287 (2015).
Cueff, S. et al. Dynamic control of light emission faster than the lifetime limit using VO2 phase-change. Nat. Commun. 6, 8636 (2015).
Boltasseva, A. & Atwater, H. A. Low-loss plasmonic metamaterials. Science 331, 290–291 (2011).
Naik, G. V., Shalaev, V. M. & Boltasseva, A. Alternative plasmonic materials: beyond gold and silver. Adv. Mater. 25, 3264–3294 (2013).
Naik, G. V., Kim, J. & Boltasseva, A. Oxides and nitrides as alternative plasmonic materials in the optical range [Invited]. Opt. Mater. Express 1, 1090–1099 (2011).
Wang, Y., Capretti, A. & Dal Negro, L. Wide tuning of the optical and structural properties of alternative plasmonic materials. Opt. Mater. Express 5, 2415–2430 (2015).
Zgrabik, C. M. & Hu, E. L. Optimization of sputtered titanium nitride as a tunable metal for plasmonic applications. Opt. Mater. Express 5, 2786–2797 (2015).
Patsalas, P., Kalfagiannis, N. & Kassavetis, S. Optical properties and plasmonic performance of titanium nitride. Materials 8, 3128–3154 (2015).
Rowland, C. E. et al. Electric field modulation of semiconductor quantum dot photoluminescence: insights into the design of robust voltage-sensitive cellular imaging probes. Nano Lett. 15, 6848–6854 (2015).
Jun, Y. C., Huang, K. C. Y. & Brongersma, M. L. Plasmonic beaming and active control over fluorescent emission. Nat. Commun. 2, 283 (2011).
Reserbat-Plantey, A. et al. Electromechanical control of nitrogen-vacancy defect emission using graphene NEMS. Nat. Commun. 7, 10218 (2016).
Steckel, J. S., Ho, J. & Coe-Sullivan, S. QDs generate light for next-generation displays. Photon. Spectra 48, 55–61 (2014).
Jang, E. et al. White-light-emitting diodes with quantum dot color converters for display backlights. Adv. Mater. 22, 3076–3080 (2010).
Akselrod, G. M. et al. Probing the mechanisms of large Purcell enhancement in plasmonic nanoantennas. Nat. Photon. 8, 835–840 (2014).
Dimitrov, S. & Haas, H. Principles of LED Light Communications: Towards Networked Li-Fi (Cambridge University Press, Cambridge, 2015).
Graydon, O. View from… ECOC 2015: Lighting that talks. Nat. Photon. 9, 785–786 (2015).
Sun, S. L. et al. High-efficiency broadband anomalous reflection by gradient meta-surfaces. Nano Lett. 12, 6223–6229 (2012).
Hoang, T. B. et al. Ultrafast spontaneous emission source using plasmonic nanoantennas. Nat. Commun. 6, 7788 (2015).
Johnson, P. B. & Christy, R. W. Optical constants of the noble metals. Phys. Rev. B 6, 4370–4379 (1972).
Acknowledgements
This work was supported by Samsung Electronics, the Air Force Office of Scientific Research under grant number FA9550-16-1-0019 (device-related work), and the Department of Energy under grant number DE-FG02-07ER46405 (transparent conductor-related work). We also acknowledge use of facilities supported by the Kavli Nanoscience Institute (KNI) and the Joint Center for Artificial Photosynthesis (JCAP) at Caltech. Y.-J.L. acknowledges the support from Ministry of Science and Technology, Taiwan (Grant numbers: 104-2917-I-564-057). The authors would like to thank Wei-Hsiang Lin, Anya Mitskovets, and Panos Patsalas for useful discussions. The authors gratefully acknowledge Erin Burkett from the Hixon Writing Center at Caltech for providing feedback and guidance on writing during the revision process. The authors also deeply appreciate help in the form of the close reading of the manuscript and review responses by Kelly Mauser, Dagny Fleischman, Rebecca Glaudell, Haley Bauser, Cora Went, Phil Jahelka, and Michael Kelzenberg.
Author information
Authors and Affiliations
Contributions
Y.-J.L., R.S. and H.A.A. proposed the original idea. Y.-J.L. performed all experiments, calculations, and data analysis. R.S. proposed the theoretical model and performed calculations. R.P. and W.-H.C. helped with the optical setup. K.T., G.K.S., W.-H.C., and R.S. performed ellipsometry measurements and analyzed the ellipsometry data. A.R.D. helped in discussion. Y.-J.L., R.S., and H.A.A. wrote the paper, and all authors discussed and revised the final manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lu, YJ., Sokhoyan, R., Cheng, WH. et al. Dynamically controlled Purcell enhancement of visible spontaneous emission in a gated plasmonic heterostructure. Nat Commun 8, 1631 (2017). https://doi.org/10.1038/s41467-017-01870-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-01870-0
This article is cited by
-
High-harmonic generation in metallic titanium nitride
Nature Communications (2021)
-
Acoustic extraordinary transmission manipulation based on proximity effects of heterojunctions
Scientific Reports (2019)
-
Dynamic beam steering with all-dielectric electro-optic III–V multiple-quantum-well metasurfaces
Nature Communications (2019)
-
Dynamically tunable multifunctional QED platform
Science China Physics, Mechanics & Astronomy (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.