Abstract
Commonly available heat-storage materials cannot usually store the energy for a prolonged period. If a solid material could conserve the accumulated thermal energy, then its heat-storage application potential is considerably widened. Here we report a phase transition material that can conserve the latent heat energy in a wide temperature range, T<530 K and release the heat energy on the application of pressure. This material is stripe-type lambda-trititanium pentoxide, λ-Ti3O5, which exhibits a solid–solid phase transition to beta-trititanium pentoxide, β-Ti3O5. The pressure for conversion is extremely small, only 600 bar (60 MPa) at ambient temperature, and the accumulated heat energy is surprisingly large (230 kJ L−1). Conversely, the pressure-produced beta-trititanium pentoxide transforms to lambda-trititanium pentoxide by heat, light or electric current. That is, the present system exhibits pressure-and-heat, pressure-and-light and pressure-and-current reversible phase transitions. The material may be useful for heat storage, as well as in sensor and switching memory device applications.
Similar content being viewed by others
Introduction
Phase transition phenomena, such as metal-insulator, ferroelectric ferromagnetic, and spin transitions, are attractive issues in the fields of physics, chemistry and materials science. Phase transitions are controlled not only by temperature change but also by other external stimuli such as pressure, light-irradiation or electric current flow. For example, for pressure-induced phase transitions, pressure-induced metal-semiconductor transition in a molybdenum disulphide1, pressure-induced superconductor transition in a fulleride2 and pressure-induced ferroelectric–antiferroelectric transition in a perovskite system3 have been reported. For light-induced phase transitions, light-induced crystalline-amorphous transitions in chalcogenides4,5, light-induced metal-semiconductor transition in a trititanium pentoxide6 and insulator-metal transition in perovskite manganites7,8, light-induced spin-crossover transitions in metal complexes9,10,11,12 and light-induced charge-transfer transition in organic molecules13,14 and metal complexes15 have been reported. Furthermore, for current-induced phase transitions16,17,18, current-induced insulator-metal transition in organic compound and current-induced magnetic-domain-wall switching in gallium manganese arsenide have been reported.
In recent years, heat-storage materials have been attracting attention from the viewpoint of energy saving. Development of high-performance heat-storage materials is important for the effective use of waste heat from blast furnaces in factories. Phase transition materials are considered to be useful as latent heat-storage materials. These are divided into solid–liquid and solid–solid phase transition types. In the former, the phase transition at the melting point (m.p.) is used for the heat storage. For example, water (320 kJ L−1 at m.p.=0 °C), paraffin (140 kJ L−1 at m.p.=64 °C)19 and polyethylene glycol (165 kJ L−1 at m.p.=20 °C)20 are known. In these cases, there are concerns of liquid spill from the system and mixing (or reaction) with the surrounding media. From this angle, a solid–solid phase transition material is stiff and its form is maintained without support, while at the same time it has chemical stability against the surrounding media. Well-known solid–solid phase transition materials for heat-storage usage include copolymers (for example, hyperbranched polyurethane: 150 kJ L−1 at 67 °C)21, organic compounds (for example, neopentylglycol: 165 kJ L−1 at 48 °C and pentaerythritol: 360 kJ L−1 at 188 °C)22,23 and organometallic compounds (for example, bis(n-hexadecylammonium) tetrachlorozincate: 120 kJ L−1 at 103 °C and bis(n-decylammonium) tetrachlorocuprate: 60 kJ L−1 at 34 °C)19,24,25. In general, such phase change heat-storage materials cannot store the energy for a prolonged period below the phase transition temperature. If a solid material could conserve the accumulated thermal energy and release it only on demand, then its heat-storage application potential is considerably widened. From this angle, our work focused on a phase transition where the latent heat of thermal phase transition could be stored.
In this paper, we report a heat-storage material composed of lambda-trititanium pentoxide. The solid–solid phase transition of this material can be controlled by heat, pressure application, light-irradiation and current flow. This heat-storage material can conserve a high accumulation of energy and release it by the application of a remarkably small external pressure.
Results
Material and morphology
The sample of the titanium oxide, a new series of lambda-trititanium pentoxide (λ-Ti3O5), was produced by sintering rutile-TiO2 particles in a hydrogen atmosphere (see Methods). Elemental analysis using inductively coupled plasma mass spectrometry confirms that the formula of the material is Ti3O5. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images of the obtained sample show a coral-like morphology with particle size of ∼4 × 1 μm (Supplementary Fig. 1), composed of aggregates of rectangular-shaped nanorods, of which the majority are ∼200 × 30 nm dimensions (hereafter called ‘stripe-type-λ-Ti3O5’, Fig. 1a). The high-resolution TEM (HRTEM) image is shown in Fig. 1b. The Fourier transform analysis of the HRTEM image showed that the growth direction of the nanorods is along the crystallographic b axis. The atomic level image from HRTEM corresponds to the visualized electron density distribution map on the bc plane calculated by the maximum entropy method (MEM; Fig. 1c), described later.
(a) TEM image of stripe-type-λ-Ti3O5. The scale bar below the TEM image indicates 50 nm. (b) HRTEM image of the surface of stripe-type-λ-Ti3O5 showing the atomic arrangement on the bc plane. The scale bar below the TEM image indicates 1 nm. (c) Visualized electron density maps on the bc plane of stripe-type-λ-Ti3O5 obtained by the MEM (isosurface 0.8e Å−3). The scale bar below the electron density map (left) indicates 1 nm. (d) Pressure (P) and temperature (T) dependence of the XRPD patterns (λ=1.5418 Å). The ambient-temperature XRPD pattern of the as-prepared sample at atmospheric pressure (P=0.1 MPa) is shown in the front, followed by XRPD patterns of the pellet samples pressurized by P=15−530 MPa, measured after pressure release. These are followed by the XRPD patterns of pressure-produced β-Ti3O5 with increasing temperature from 300 K to 510 K. (e) Pressure evolution of the phase fractions of λ-Ti3O5 (blue) and β-Ti3O5 (red). The pressure where the fraction of λ-Ti3O5 becomes 50% (P1/2) is an extremely small value of ∼60 MPa. (f) Temperature evolution of the phase fractions of λ-Ti3O5 (blue) and β-Ti3O5 (red) in the heating process.
Pressure-induced phase transition
X-ray powder diffraction (XRPD) measurements were performed to investigate the pressure (P) dependence of the crystal structure of the stripe-type-λ-Ti3O5. The XRPD pattern at 300 K under atmospheric pressure (P=0.1 MPa) is shown in Fig. 1d and Supplementary Fig. 2. Rietveld analysis indicates that this sample is composed of 80.0(2)% λ-Ti3O5 and 20.0(2)% β-Ti3O5. λ-Ti3O5 adopts a monoclinic crystal structure (space group C2/m) with lattice parameters of a=9.83119(19) Å, b=3.78798(7) Å, c=9.97039(19) Å and β=91.2909(7)˚, and a unit cell volume, V=371.207(12) Å3. λ-Ti3O5 has three symmetry-inequivalent Ti sites, Ti(1), Ti(2) and Ti(3), and five-symmetry-inequivalent O sites, O(1) to O(5). All the Ti sites form a six-coordinate structure. In the previous investigation6 of the same polymorph prepared from anatase-TiO2 nanoparticles, we observed some indications of a pressure effect. In the present research, the sample was pressed at various external pressures with a pellet press, and XRPD patterns were measured for the pellets after pressure release. With increasing P, the intensity of the XRPD peaks of λ-Ti3O5 decreased and those of β-Ti3O5 increased (Fig. 1d and Supplementary Fig. 3). The pressure where the fraction of λ-Ti3O5 becomes 50% (P1/2) is ∼60 MPa as shown in Fig. 1e. The crystal structure of β-Ti3O5 is monoclinic (space group C2/m; a=9.75252(18) Å, b=3.80034(6) Å, c=9.44413(19) Å, β=91.5322(10)˚ and V=349.902(11) Å3) (Supplementary Fig. 4). After pressurizing the sample and releasing the pressure at room temperature, heating the sample causes β-Ti3O5 to revert back to λ-Ti3O5 at 470 K (Fig. 1d,f and Supplementary Fig. 5a). Above 530 K, λ-Ti3O5 further transforms to α-Ti3O5. On the other hand, in the cooling process from 620 to 300 K, α-Ti3O5 returns to λ-Ti3O5 (Supplementary Fig. 5b). This λ-Ti3O5 is very stable in the wide temperature range of 0<T<530 K. Furthermore, when external pressure was applied to this recovered λ-Ti3O5 sample, λ-Ti3O5 exhibited again the phase transition to β-Ti3O5 (Supplementary Figs 6 and 7).
The visualized electron density distributions of λ-Ti3O5 and β-Ti3O5 obtained using MEM from the XRPD patterns, are shown in Fig. 2a. The MEM image of λ-Ti3O5 shows that the electron density is spread between both Ti and O atoms, while in β-Ti3O5, the electron density is localized around each atom. This result indicates the electron delocalized character of λ-Ti3O5 and localized character of β-Ti3O5, which are consistent with the fact that λ-Ti3O5 is a metallic conductor and β-Ti3O5 is a semiconductor. In addition, the visualized electron density distribution of λ-Ti3O5 in the bc plane well reproduces the HRTEM image, as mentioned in Figs 1b and c.
(a) Visualized electron density maps (isosurface 0.45e Å−3) of λ-Ti3O5 (upper) and β-Ti3O5 (lower) obtained using MEM from the XRPD patterns. (b) Phonon density of state (DOS) for λ-Ti3O5 (upper) and β-Ti3O5 (lower). Blue, light blue and grey areas indicate the contributions from phonons due to Ti, O, and the total phonon DOS, respectively for λ-Ti3O5 (upper). Red, orange and grey areas indicate the contributions from phonons due to Ti, O and the total phonon DOS, respectively, for β-Ti3O5 (lower). (c) Schematic illustration of the Bu phonon mode at 445.8 cm−1 for λ-Ti3O5 (upper) and the Bu phonon mode at 226.7 cm−1 for β-Ti3O5 (lower). Arrows and their lengths indicate the direction of the movement of the atoms and the relative amplitude of oscillation, respectively (see Supplementary Movies 1 and 2).
First-principles calculation of phonon mode
To elucidate the pressure-induced phase transition, first-principles phonon mode calculations were conducted. Figure 2b shows the phonon density of states (DOS) based on the lattice vibrations for λ-Ti3O5 and β-Ti3O5. The phonon dispersion and phonon frequencies at the Brillouin zone centre, Γ point, for each of the phonon dispersions are listed in Supplementary Fig. 8. Comparison of the two crystal structures shows that the coordination geometry of Ti(3) is different between λ-Ti3O5 and β-Ti3O5; Ti(3) is connected to O(5) in λ-Ti3O5, while it bonds to O(4) in β-Ti3O5. Therefore, in the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5, the Ti(3)−O(5) bond is considered to break, and the Ti(3)−O(4) bond to form. The corresponding phonon modes of λ-Ti3O5 lie at 248.6, 318.5 and 445.8 cm−1. For example, for the Bu phonon mode at 445.8 cm−1, Ti(3) vibrates significantly toward O(4) and moves further away from O(5) (Fig. 2c (upper) and Supplementary Movie 1). On the contrary, in the course of the thermal phase transition (that is, heat-storage process) from β-Ti3O5 to λ-Ti3O5, the Ti(3)−O(4) bond is broken and the Ti(3)−O(5) bond is generated. The corresponding phonon modes now lie at 226.7 and 339.3 cm−1. For example, visualization of the Bu phonon mode at 226.7 cm−1 shows that Ti(3) significantly vibrates towards O(5) (Fig. 2c (lower) and Supplementary Movie 2).
Accumulated heat energy and pressure-released energy
To investigate the heat-storage process from pressure-produced β-Ti3O5 to λ-Ti3O5 and the amount of accumulated thermal energy in the system, heat capacity measurements were performed. First, we investigated the heat capacity of the pressure-produced β-Ti3O5. In the temperature region from 5 to 300 K, specific heat was measured by the relaxation technique using the physical properties measurement system (Fig. 3a), and above 300 K, specific heat accompanying the thermal phase transition from pressure-produced β-Ti3O5 to λ-Ti3O5 was measured by differential scanning calorimetry (DSC; Fig. 3b). By combining the results from the physical properties measurement system and DSC measurements and integrating with temperature, the experimental enthalpy (H) curves of λ-Ti3O5 and β-Ti3O5 versus temperature were obtained up to 600 K (Fig. 3c; see Methods). The transition enthalpy (ΔH) associated with the first-order phase transition from β-Ti3O5 to λ-Ti3O5 was 230±20 kJ L−1 (12±1 kJ mol−1). In the temperature decreasing process of the DSC measurement, there was no peak, indicating that the accumulated heat energy of the phase transition from β-Ti3O5 to λ-Ti3O5 was conserved in the system.
(a) Molar heat capacity of λ-Ti3O5 (blue) and β-Ti3O5 (red) as a function of temperature. Experimental data were fitted with a Debye model (see Methods). (b) DSC charts of the pressure-produced β-Ti3O5 with increasing temperature and λ-Ti3O5 with decreasing temperature. A peak due to the latent heat of the first-order phase transition from β-Ti3O5 to λ-Ti3O5 (230 kJ L−1) was observed in the heating process, whereas no peak was observed in the cooling process. (c) Temperature dependence of the enthalpy (H) for λ-Ti3O5 (blue) and β-Ti3O5 (red). When pressure is applied to λ-Ti3O5, the accumulated heat energy is released as shown in the lower enlarged figure (see Supplementary Movie 3). (d) Pressure-released heat energy accompanying the pressure-induced phase transition from stripe-type-λ-Ti3O5 to β-Ti3O5. Pressure was applied at t=0.
Next the released energy of the pressure-induced phase transition from stripe-type-λ-Ti3O5 to β-Ti3O5 was measured using a high-pressure micro-DSC measurement system at room temperature. After applying pressure, heat energy of 240±40 kJ L−1 was released, which almost corresponds to the heat accumulated energy (Fig. 3d). Therefore, this material conserves the heat energy of the phase transition from pressure-produced β-Ti3O5 to λ-Ti3O5 and releases the accumulated heat energy by applying low pressure through the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5 (Supplementary Movie 3).
Thermal conductivity and sensible heat-storage performance
Bricks and concrete are useful as sensible heat-storage materials20,26,27,28 since they release thermal energy slowly. Thermal conductivity measurements were performed for the stripe-type-λ-Ti3O5 and pressure-produced β-Ti3O5. The thermal conductivities were 0.20±0.02 W m−1 K−1 and 0.41±0.02 W m−1 K−1 for λ-Ti3O5 and β-Ti3O5, respectively, which are similar to the values of bricks (for example, 0.16 W m−1 K−1)26 and concrete (for example, 0.57 W m−1 K−1)28.
Current-induced and light-induced phase transitions
Electric current was flowed to the pressure-produced β-Ti3O5 sample at 298 K. By flowing a current of 0.4 A mm−2, the colour of the sample changed from brown to dark blue (Fig. 4a). The XRPD patterns before and after flowing the current indicate that β-Ti3O5 is transformed into λ-Ti3O5 (Fig. 4b and Supplementary Movie 4). The electric current dependence on the conversion from the pressure-produced β-Ti3O5 to λ-Ti3O5 shows that the threshold current value of the current-induced phase transition is 0.2 A mm−2 (Supplementary Fig. 9). The origin of this current-induced phase transition is regarded as breaking of charge ordering or (and) Joule heat16,17,18. The mechanism by breaking of charge ordering is considered as follows: β-Ti3O5 is a charge-localized state whose charge is localized on Ti3+(3) with empty orbital on Ti4+(2). In contrast, λ-Ti3O5 is a charge-delocalized state whose charge is delocalized on Ti(2) and Ti(3). By flowing electric current to β-Ti3O5, the localized charge on Ti(3) is forcedly moved to the empty orbital on of Ti(2), resulting in a transition to metallic λ-Ti3O5.
An electric current of 0.4 A mm−2 flowed through the pressure-produced β-Ti3O5 at 298 K. (a) Photographs of the pressure-produced β-Ti3O5 before (left) and after the application of an electric current of 0.4 A mm−2 (right). (b) XRPD pattern in the 2θ range of 16.0–22.5° of the pressure-produced β-Ti3O5 (left) and after the application of the electric current (right). Blue and red areas mark the peaks of λ-Ti3O5 and β-Ti3O5, respectively.
Light irradiation experiment was also conducted on a pressure-produced β-Ti3O5. The reverse phase transition from β-Ti3O5 to λ-Ti3O5 was observed by irradiation of 410-nm laser light (Supplementary Fig. 10 and Supplementary Movie 5).
Discussion
The generation of stripe-type-λ-Ti3O5 originates from the change in the Gibbs free energy (G) of the material compared with the bulk or single crystal Ti3O5. This change in the G value is considered to be due to the interface (and/or surface) energy of the nanoscale domain. It is noted that there is no oxygen vacancy, which was confirmed by electron spin resonance. To understand why the stripe-type-λ-Ti3O5 undergoes a pressure-induced phase transition to β-Ti3O5, we considered the thermodynamics of the present phase transition phenomena using the mean-field model, developed by Slichter and Drickamer29. In this model, G is described by ΔH, the transition entropy (ΔS) and the interaction parameter between λ-Ti3O5 and β-Ti3O5 phases. The calculation shows that at atmospheric pressure (P=0.1 MPa), the sample exists as λ-Ti3O5 (Supplementary Movie 6). This is because λ-Ti3O5 is synthesized by sintering at a high temperature, and it remains as λ-Ti3O5 with decreasing temperature due to the energy barrier between λ-Ti3O5 and β-Ti3O5 as shown in the G versus fraction (x) of λ-Ti3O5 curves (Fig. 5a (i)). On the contrary, on applying external pressure, the G versus x curves change; for example, the energy barrier disappears <400 K when P is 60 MPa, and hence, λ-Ti3O5 transforms into β-Ti3O5 on applying pressure (Fig. 5a (ii)). The x versus temperature curves of P=0.1 MPa and P=60 MPa are shown in Fig. 5b. As shown in Fig. 5c, x versus pressure plots indicate the threshold of the pressure-induced phase transition. The origin of the pressure-induced phase transition is the PΔV term of ΔH(=ΔU+PΔV), where ΔU and ΔV are the changes of internal energy and volume, respectively. At such a low pressure, the pressure-induced change on ΔU is very small and negligible. In fact, the phonon mode calculation under external pressure shows that the pressure-induced change of ΔU is ∼1 × 10−3 kJ mol−1 at 60 MPa, which is two orders smaller compared with PΔV=0.19 kJ mol−1. The pressure-induced change on ΔS is also very small and cannot contribute to the pressure-induced phase transition in the present system (see Methods, Supplementary Fig. 11 and Supplementary Tables 1, 2). It is noted that the observed x versus P plots of Fig. 1e is somewhat gradual. This is explained by the presence of a distribution in the transition pressure of the Slichter and Drickamer model, which may be due to the crystal size distribution. We have simulated this gradual pressure-induced phase transition with a distribution of transition pressures (Supplementary Fig. 12).
(a) Gibbs free energy (G) versus λ-Ti3O5 fraction (x) for every 10 K between 250 K to 500 K calculated using the Slichter–Drickamer mean-field model at P=0.1 MPa (i) and 60 MPa (ii). Blue and red circles indicate λ-Ti3O5 and β-Ti3O5, respectively. λ-Ti3O5 undergoes a pressure-induced phase transition to β-Ti3O5 because the energy barrier (shown by brown shadows) disappears by the application of external pressure above ∼60 MPa as shown in the insets (see Supplementary Movie 6). (b) Calculated x versus temperature curves at P=0.1 MPa (blue) and 60 MPa (red). (c) Calculated x versus pressure curve at 300 K indicating a threshold pressure of ∼60 MPa.
In summary, we report the first metal oxide capable of conserving the accumulated heat energy of a phase transition. Stripe-type-λ-Ti3O5 can store a large heat energy of 230 kJ L−1, and this energy can be released by applying external pressure only when demanded. The magnitude of the required pressure is extremely small, ∼60 MPa. This value is remarkably smaller than the typical pressures observed in the pressure-induced phase transitions in metal oxide materials30,31,32,33,34,35 and metallic compounds36,37,38,39,40,41, for example, the pressure-induced phase transition from rutile-TiO2 to baddeleyite-type TiO2 at 1,043 K occurs at 20,000 MPa (=20 GPa)30. From the viewpoint of the energy balance of the thermodynamic cycle, pressure of 60 MPa corresponds to ∼10 kJ L−1, which is <5% of the pressure-releasing heat energy. Pressure of ∼60 MPa can be realized even by the water pressure of a high-pressure washing machine, and hence, λ-Ti3O5 has the potential to be employed as pressure-sensitive sheets or reusable portable heating pads. In addition, since λ-Ti3O5 is a metallic conductor and β-Ti3O5 is a semiconductor, it has possibilities as a pressure-sensitive conductivity sensor or pressure-sensitive optical sensor. Furthermore, because λ-Ti3O5 is composed of common elements (titanium and oxygen), it is safe and environmentally friendly. λ-Ti3O5 could be useful for heat-retaining systems for residential use and may realize more efficient uses of industrial waste heat generated from furnaces (Supplementary Fig. 13)42,43. In addition, light-induced and current-induced phase transitions from pressure-produced β-Ti3O5 to λ-Ti3O5 are also observed, that is, stripe-type-λ-Ti3O5 shows reversible pressure-and-light-induced phase transition and reversible pressure-and-current-induced phase transition. These effects are also attractive phenomena from the viewpoint of advanced electronic devices.
Methods
Material
A new series of λ-Ti3O5 nanocrystallites was produced by sintering rutile-TiO2 particles in a hydrogen atmosphere (flow rates of 0.7 dm3 min−1) at 1,117 °C for 2 h, followed by a slow cooling process of ∼9 h from the sintering temperature to room temperature (Supplementary Fig. 14). Elemental analysis using inductively coupled plasma mass spectrometry confirms that the formula is Ti3.00(1)O5.00(6); Calc.: Ti, 64.2%. Found: Ti, 64.2(1)%. The experimentally obtained density is 4.000±0.048 g cm−3, which is consistent with the theoretical value of 4.00 g cm−3 from the crystal structure of λ-Ti3O5 as determined by XRPD measurements. SEM and TEM images of the obtained sample show a coral-like morphology with particle size of ∼4 × 1 μm, composed of rectangular-shaped nanorods, of which the majority are ∼200 × 30 nm dimensions (Supplementary Fig. 1a). The Fourier transform analysis of the HRTEM image showed that the growth direction of the nanorods is along the crystallographic b axis. This new series of λ-Ti3O5 have larger crystal size than the previous series, which were prepared from anatase-TiO2 (ref. 6; Supplementary Fig. 1b).
XRPD measurements
XRPD measurements were performed with a Rigaku Ultima IV diffractometer with Cu Kα radiation (λ= 1.5418 Å). The temperature-dependent XRPD measurements were undertaken using a high-temperature chamber with atmosphere control (RIGAKU-OAT003S) under N2 flow. The RIETAN-FP computer programme was used for the Rietveld analyses, while Dysnomia was used for the MEM analyses. The refined crystal structures and charge densities were visualized by the computer programme VESTA. Although both λ-Ti3O56 and its high-temperature phase44,45 can be considered as candidates of the present material with C2/m crystal structure, we assigned the present material to λ-Ti3O5 because it is obtained by a very slow cooling process taking of ca. 9 h from the sintering temperature to room temperature, and it is thermally stable.
Heat capacity measurements
To investigate the temperature dependence of the lattice specific heat, C(T), in the temperature range of 5–300 K, we carried out curve fitting of the observed plots with the equation based on the two-Debye model46 expressed by , where R is gas constant, ci is coefficient, θi is Debye temperature, x is
, ħ is the reduced Planck constant, ω is phonon frequency and kB is Boltzmann constant, with the fit parameters of c1=3.2(1), c2=5.6(1), θ1=4.1(1) × 102 K and θ2=9.3(1) × 102 K for λ-Ti3O5, and c1=2.7(1), c2=5.8(1), θ1=4.3(1) × 102 K and θ2=9.3(2) × 102 K for β-Ti3O5. We then developed the temperature dependence curve of the specific heat in the temperature range of 5–600 K using both the fitted curve and the anomalous specific heat associated with the first-order phase transition from β-Ti3O5 to λ-Ti3O5 obtained from the DSC measurement.
Released heat energy on pressure application
Released heat energy on pressure application was measured with a high-pressure DSC measurement system (μDSC VII, SETARAM Instrumentation) at 300 K. Pressure application of 40 MPa was achieved by instant injection of N2 gas into the sample cell.
Thermal conductivity measurements
The specific heat and thermal diffusivity of λ-Ti3O5 and β-Ti3O5 pellet samples were measured with a DSC measurement system (DSC200F3 Maia (NETZSCH), NSST Co., Ltd.) and Light Flash Apparatus (LFA447NanoFlash, NSST Co., Ltd.), respectively.
First-principles phonon mode calculations
First-principles calculations based on the density functional theory were carried out for λ-Ti3O5 and β-Ti3O5 using the VASP (Vienna ab initio simulation package) code. The wavefunctions based on plane waves and potentials of the core orbitals were represented by the projector-augmented wave of Blöchl, and the exchange-correlation term was evaluated by the generalized gradient approximation by Perdew, Burke, and Ernzerhof. The crystal structures of λ-Ti3O5 and β-Ti3O5 obtained from the XRPD measurements were used for computed models as the initial structures. The lattice parameters and atomic positions were optimized under no pressure and 1000 MPa with an energy cutoff of 500 eV and 3 × 7 × 3 k-mesh until satisfying 10−5 eV pm−1 force tolerance. Supercells (1 × 3 × 1) of the optimized structures were used to calculate the phonon modes and thermodynamic functions of λ-Ti3O5 and β-Ti3O5, which were calculated by the direct method implemented in Phonon code with 2 pm displacements using the optimized structures.
Thermodynamic analysis
In the Slichter and Drickamer mean-field model, the Gibbs free energy of the system is described as G=x(ΔH)+γx(1−x)+T{R[x lnx+(1−x)ln(1−x)]−x(ΔS)}+Gβ, where x is the ratio of the charge-delocalized unit of Ti(1)3.3+−Ti(2)3.3+−Ti(3)3.3+ corresponding to λ-Ti3O5, γ is the interaction parameter between λ-Ti3O5 and β-Ti3O5 phases, Gβ is Gibbs free energy of β-Ti3O5 set as the origin of the energies, and R is the gas constant. The observed phase transition was considered to be a metal-semiconductor phase transition between charge-delocalized Ti(1)3.3+−Ti(2)3.3+−Ti(3)3.3+ and charge-localized Ti(1)3.0+−Ti(2)3.7+−Ti(3)3.3+ systems, which were regarded as λ-Ti3O5 and β-Ti3O5, respectively. The values of ΔH=11.5 kJ mol−1 and ΔS=25.2 J K−1 mol−1, and a suitable value of γ=γa+γb f(T ), where γa=14 kJ mol−1 and γb=1.08 × 10−2 J K−1 mol−1 to be consistent with the observation results, were used. When the external pressure is applied to the sample, ΔH is perturbed by the pressure-induced change on the ΔU and PΔV terms. Compared with the pressure-induced change on the PΔV term, for example, 0.19 kJ mol−1 at P=60 MPa, the change on ΔU evaluated by the first-principles phonon mode calculations is negligibly small, for example, 1 × 10−3 kJ mol−1 at P=60 MPa. Thus, ΔH is controlled by the PΔV term in the present system. The pressure-induced change on ΔS is also very small, for example, −0.067 J K−1 mol−1 at P=60 MPa, from the results of first-principles phonon mode calculations.
Current-induced phase transition study
Stainless electrodes are attached to β-Ti3O5 pellet by Ag paste with an adhesion area of 5 mm2 and electric current of 2 A was flowed (0.4 A mm−2) at 298 K. After that, the XRPD pattern of the surface of the pellet was measured.
Additional information
How to cite this article: H Tokoro et al. External stimulation-controllable heat storage ceramics. Nat. Commun. 6:7037 doi: 10.1038/ncomms8037 (2015).
References
Nayak, A. P. et al. Pressure-induced semiconducting to metallic transition in multilayered molybdenum disulphide. Nat. Commun. 5, 3731 (2014).
Takabayashi, Y. et al. The disorder-free non-BCS superconductor Cs3C60 emerges from an antiferromagnetic insulator parent state. Science 323, 1585–1590 (2009).
Avdeev, M. et al. Pressure-induced ferroelectric to antiferroelectric phase transition in Pb0.99(Zr0.95Ti0.05)0.98Nb0.02O3 . Phys. Rev. B 73, 064105/1–14 (2006).
Kolobov, A. V. et al. Understanding the phase-change mechanism of rewritable optical media. Nat. Mater. 3, 703–708 (2004).
Wuttig, M. & Yamada, N. Phase-change materials for rewriteable data storage. Nat. Mater. 6, 824–832 (2007).
Ohkoshi, S. et al. Synthesis of a metal oxide with a room-temperature photoreversible phase transition. Nat. Chem. 2, 539–545 (2010).
Miyano, K., Tanaka, T., Tomioka, Y. & Tokura, Y. Photoinduced insulator-to-metal transition in a perovskite manganite. Phys. Rev. Lett. 78, 4257–4260 (1997).
Fiebig, M., Miyano, K., Tomioka, Y. & Tokura, Y. Visualization of the local insulator–metal transition in Pr0.7Ca0.3MnO3 . Science 280, 1925–1928 (1998).
Gütlich, P., Hauser, A. & Spiering, H. Thermal and optical switching of iron(II) complexes. Angew. Chem. Int. Ed. 33, 2024–2054 (1994).
Létard, J. F. et al. Light induced excited pair spin state in an iron(II) binuclear spin-crossover compound. J. Am. Chem. Soc. 121, 10630–10631 (1999).
Ohkoshi, S. et al. 90-degree optical switching of output second-harmonic light in chiral photomagnet. Nat. Photonics 8, 65–71 (2014).
Ohkoshi, S., Imoto, K., Tsunobuchi, Y., Takano, S. & Tokoro, H. Light-induced spin-crossover magnet. Nat. Chem. 3, 564–569 (2011).
Koshihara, S., Tokura, Y., Mitani, T., Saito, G. & Koda, T. Photoinduced valence instability in the organic molecular compound tetrathiafulvalence-p-chloranil (TTF-CA). Phys. Rev. B 42, 6853–6856 (1990).
Collet, E. et al. Laser-induced ferroelectric structural order in an organic charge-transfer crystal. Science 300, 612–615 (2003).
Ohkoshi, S. & Tokoro, H. Photomagnetism in cyano-bridged bimetal assemblies. Acc. Chem. Res. 45, 1749–1758 (2012).
Yamanouchi, M., Chiba, D., Matsukura, F. & Ohno, H. Current-induced domain-wall switching in a ferromagnetic semiconductor structure. Nature 428, 539–542 (2004).
Ikeda, S. et al. A perpendicular-anisotropy CoFeB–MgO magnetic tunnel junction. Nat. Mater. 9, 721–724 (2010).
Asamitsu, A., Tomioka, Y., Kuwahara, H. & Tokura, Y. Current switching of resistive states in magnetoresistive manganites. Nature 388, 50–52 (1997).
Farid, M. M., Khudhair, A. M., Razack, S. A. K. & Al-Hallaj, S. A review on phase change energy storage: materials and applications. Energ. Convers. Manage. 45, 1597–1615 (2004).
Sharma, A., Tyagi, V. V., Chen, C. R. & Buddhi, D. Review on thermal energy storage with phase change materials and applications. Renew. Sust. Energ. Rev. 13, 318–345 (2009).
Cao, Q. & Liu, P. Hyperbranched polyurethane as novel solid-solid phase change material for thermal energy storage. Eur. Polym. J. 42, 2931–2939 (2006).
Benson, D. K., Burrows, R. W. & Webb, J. D. Solid state phase transitions in pentaerythritol and related polyhydric alcohols. Sol. Energ. Mater. 13, 133–152 (1986).
Barrio, M., López, D. O., Tamarit, J. L., Negrier, P. & Haget, Y. Molecular interactions and packing in molecular alloys between nonisomorphous plastic phases. J. Solid State Chem. 124, 29–38 (1996).
Busico, V., Carfagna, C., Salerno, V., Vacatello, M. & Fittipaldi, F. The layer perovskites as thermal energy storage systems. Sol. Energy 24, 575–579 (1980).
Li, W. et al. Study of solid–solid phase change of (n-CnH2n+1NH3)2MCl4 for thermal energy storage. Thermochim. Acta 326, 183–186 (1999).
Nahas, M. K. & Constable, F. H. Thermal conductivity of mud brick. Nature 142, 837 (1938).
Gur, I., Sawyer, K. & Prasher, R. Searching for a better thermal battery. Science 335, 1454–1455 (2012).
Al-Jabri, K. S., Hago, A. W., Al-Nuaimi, A. S. & Al-Saidy, A. H. Concrete blocks for thermal insulation in hot climate. Cement Concrete Res. 35, 1472–1479 (2005).
Slichter, C. P. & Drickamer, H. G. Pressure-induced electronic changes in compounds of iron. J. Chem. Phys. 56, 2142–2160 (1972).
Sato, H. et al. Baddeleyite-type high-pressure phase of TiO2 . Science 251, 786–788 (1991).
Huang, L., Durandurdu, M. & Kieffer, J. Transformation pathways of silica under high pressure. Nat. Mater. 5, 977–981 (2006).
Karzel, H. et al. Lattice dynamics and hyperfine interactions in ZnO and ZnSe at high external pressures. Phys. Rev. B 53, 11425–11438 (1996).
Lipinska-Kalita, K. E., Kalita, P. E., Hemmers, O. A. & Hartmann, T. Equation of state of gallium oxide to 70 GPa: Comparison of quasihydrostatic and nonhydrostatic compression. Phys. Rev. B 77, 094123 (2008).
Azuma, M. et al. Colossal negative thermal expansion in BiNiO3 induced by intermetallic charge transfer. Nat. Commun. 2, 347 (2011).
Ahart, M. et al. Origin of morphotropic phase boundaries in ferroelectrics. Nature 451, 545–548 (2008).
Medvedev, S. et al. Electronic and magnetic phase diagram of β-Fe1.01Se with superconductivity at 36.7 K under pressure. Nat. Mater. 8, 630–633 (2009).
Tolbert, S. H. & Alivisatos, A. P. Size dependence of a first order solid-solid phase transition: the wurtzite to rock salt transformation in CdSe nanocrystals. Science 265, 373–376 (1994).
Hanfland, M., Syassen, K., Christensen, N. E. & Novikov, D. L. New high-pressure phases of lithium. Nature 408, 174–178 (2000).
McMahon, M. I., Nelmes, R. J., Allan, D. R., Belmonte, S. A. & Bovornratanaraks, T. Observation of a simple-cubic phase of GaAs with a 16-atom basis (SC16). Phys. Rev. Lett. 80, 5564–5567 (1998).
Mujica, A., Rubio, A., Muñoz, A. & Needs, R. J. High-pressure phases of group-IV, III-V, and II-VI compounds. Rev. Mod. Phys. 75, 863–912 (2003).
Nelmes, R. J. & McMahon, M. I. Identity of InSb-II and InSb-III. Phys. Rev. Lett. 77, 663–666 (1996).
Crabtree, G. W. & Lewis, N. S. Solar energy conversion. Phys. Today 60, 37–42 (2007).
Cartlidge, E. Saving for a rainy day. Science 334, 922–924 (2011).
Grey, I. E., Li, C. & Madsen, I. C. Phase equilibria and structural studies on the solid solution. J. Solid State Chem. 113, 62–73 (1994).
Onoda, M. Phase transitions of Ti3O5 . J. Solid State Chem. 136, 67–73 (1998).
Tomuta, D. G., Ramakrishnan, S., Nieuwenhuys, G. J. & Mydosh, J. A. The magnetic susceptibility, specific heat and dielectric constant of hexagonal YMnO3, LuMnO3 and ScMnO3 . J. Phys.: Condens. Matter 13, 4543–4552 (2001).
Acknowledgements
We are grateful to Mr Y. Kakegawa, Mr H. Tsunakawa and Mr S. Ohtsuka (The University of Tokyo) for collecting the TEM and SEM images and we also recognize the Cryogenic Research Center and the Center for Nano Lithography and Analysis, The University of Tokyo, which are supported by MEXT. We are grateful to Mr R. Uemura (Nippon Steel and Sumikin Technology Co., Ltd.) for the thermal conductivity measurement and Mr T. Tomiura and Mr Y. Okada (NIKKISO Co., Ltd.) for the knowledge of the pressure experiment. The present research was supported in part by the CREST project of JST, the Grant-in-Aid for Young Scientists (A), (B), Research Activity Start-up and the NEXT programme from JSPS, the WPI Research Center Initiative for Atoms, Molecules and Materials, SCF for Promoting Science and Technology and APSA from MEXT, Izumi Foundation and Kurata Foundation. M.Y. and N.O. are grateful to JSPS Research Fellowship for Young Scientists. M.Y. is grateful to ALPS and T.N. is grateful to MERIT from MEXT.
Author information
Authors and Affiliations
Contributions
S.O. designed and coordinated this study, contributed to all the measurements and calculations and wrote the paper. H.T. conducted the temperature-dependent XRPD measurements, heat capacity measurements and thermodynamic calculations. M.Y. analysed the first-principles phonon mode calculation results and partially wrote the paper. K.I. carried out the Rietveld analyses of the XRPD patterns and heat capacity data analyses. A.N. conducted the Rietveld analyses and prepared the figures. T.N. carried out the pressure- and temperature-dependent XRPD measurements. K.N. carried out the elemental analyses and background research. N.O. carried out the DSC measurements and MEM analyses. F.H. obtained the TEM and SEM images. K.T. contributed to the synthesis and Rietveld analyses. K.C. carried out the first-principles phonon mode calculations. R.M. and K.P. contributed to the interpretation of the results and to the writing of the paper. All the authors commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Figures and Supplementary Tables
Supplementary Figures 1-14 and Supplementary Tables 1-2 (PDF 2080 kb)
Supplementary Movie 1
Bu phonon mode of λ-Ti3O5 corresponding to the atomic movement of the pressure-induced transformation from stripe-type-λ-Ti3O5 to β-Ti3O5. This movie shows the Bu phonon mode of λ-Ti3O5 at 445.8 cm−1 corresponding to the movement of Ti and O atoms in the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5. Ti(3) moves away from O(5) and vibrates significantly toward O(4), suggesting breaking of the Ti(3)-O(5) bond and formation of the Ti(3)-O(4) bond. Light blue and blue balls represent Ti, and gray and ocher balls represent O. The oscillation amplitude is emphasized by two times for easier viewing. (MOV 5314 kb)
Supplementary Movie 2
Bu phonon mode of β-Ti3O5 corresponding to the atomic movement of the heat-induced phase transition from pressure-produced β-Ti3O5 to λ-Ti3O5. This movie shows the Bu phonon mode of β-Ti3O5 at 226.7 cm−1 corresponding to the movement of Ti and O atoms in the heat-induced phase transition from β-Ti3O5 to λ-Ti3O5. Ti(3) moves away from O(4) and vibrates significantly toward O(5), suggesting breaking of the Ti(3)-O(4) bond and formation of the Ti(3)-O(5) bond. Light pink and red balls represent Ti, and gray and ocher balls represent O. The oscillation amplitude is emphasized by two times for easier viewing. (MOV 5310 kb)
Supplementary Movie 3
Pressure-induced phase transition from stripe-type-λ-Ti3O5 to β-Ti3O5 and heat-induced phase transition from pressure-produced β-Ti3O5 to λ-Ti3O5. The initial part of this movie displays the pressure-induced phase transition from stripe-type-λ-Ti3O5 to β-Ti3O5, where the accumulated heat energy of stripe-type-λ-Ti3O5 is released (energy release process). In the next part, the pressure-produced β-Ti3O5 is heated and transforms to λ-Ti3O5, i.e., the heat-induced phase transition accompanying accumulation of heat energy (heat storage process). The release and accumulation of heat energy are repeatedly caused by alternating application of pressure and heat. Such a metal oxide is the first example. (MOV 11065 kb)
Supplementary Movie 4
Reversible pressure- and current-induced phase transition. This movie shows the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5 and current-induced phase transition from β-Ti3O5 to λ-Ti3O5. The initial part of this movie displays the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5, where the accumulated heat energy in λ-Ti3O5 is released (energy release process). Next, electric current is flowed to the pressure-produced β-Ti3O5 and β-Ti3O5 transforms to λ-Ti3O5, i.e., current-induced phase transition accompanying accumulation of heat energy (heat storage process). The release and accumulation of heat energy are caused repeatedly by alternating pressure application and current flow. (MOV 11065 kb)
Supplementary Movie 5
Reversible pressure- and light-induced phase transition. This movie shows the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5 and light-induced phase transition from β-Ti3O5 to λ-Ti3O5. The initial part of this movie displays the pressure-induced phase transition from λ-Ti3O5 to β-Ti3O5, where the accumulated heat energy in λ-Ti3O5 is released (energy release process). Next, the pressure-produced β-Ti3O5 is irradiated with light and transforms to λ-Ti3O5, i.e., light-induced phase transition accompanying accumulation of heat energy (heat storage process). The release and accumulation of heat energy are caused repeatedly by alternating pressure application and light irradiation. Such a metal oxide is the first example. (MOV 11065 kb)
Supplementary Movie 6
Mechanism of pressure-induced phase transition from stripe-type-λ-Ti3O5 to β-Ti3O5. This movie shows the mechanism of pressure-induced phase transition using the thermodynamic model proposed by Slichter and Drickamer. Gibbs free energy (G) versus λ-Ti3O5 fraction (x) curves show that λ-Ti3O5 phase (blue) is maintained at all temperatures due to the energy barrier originated from cooperative interaction between the two phases. Then, the 300 K curve is focused, showing its pressure dependence. At 60 MPa, the energy barrier disappears, and λ-Ti3O5 phase converts into β-Ti3O5 phase (red). Finally, heat storage process from β-Ti3O5 to λ-Ti3O5 is shown with G versus x and x versus temperature curves. Such a metal oxide is the first example. (MOV 18713 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Tokoro, H., Yoshikiyo, M., Imoto, K. et al. External stimulation-controllable heat-storage ceramics. Nat Commun 6, 7037 (2015). https://doi.org/10.1038/ncomms8037
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms8037
This article is cited by
-
Various crystalline phases of N-(2-hydroxy-4-methoxybenzylidene)-4′-n-butylaniline (OHMBBA) identified by a simultaneous measurement of DSC-XRD and DSC-Raman spectroscopy
Journal of Thermal Analysis and Calorimetry (2024)
-
Flatband λ-Ti3O5 towards extraordinary solar steam generation
Nature (2023)
-
Harnessing the flatband λ-Ti3O5: A breakthrough in solar steam generation
Science China Materials (2023)
-
Shielding Encapsulation to Enhance Fire Endurance of Phase Change Materials in Energy-Efficient Concrete
Fire Technology (2023)
-
Excellently balanced water-intercalation-type heat-storage oxide
Nature Communications (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.