Abstract
Some Bravais lattices have a particular geometry that can slow down the motion of Bloch electrons by pre-localization due to the band-structure properties. Another known source of electronic localization in solids is the Coulomb repulsion in partially filled d or f orbitals, which leads to the formation of local magnetic moments. The combination of these two effects is usually considered of little relevance to strongly correlated materials. Here we show that it represents, instead, the underlying physical mechanism in two of the most important ferromagnets: nickel and iron. In nickel, the van Hove singularity has an unexpected impact on the magnetism. As a result, the electron–electron scattering rate is linear in temperature, in violation of the conventional Landau theory of metals. This is true even at Earth’s core pressures, at which iron is instead a good Fermi liquid. The importance of nickel in models of geomagnetism may have therefore to be reconsidered.
Similar content being viewed by others
Introduction
Iron and nickel are two of the most well-known ferromagnets, that is, conducting materials with a permanent magnetization1. Their importance comes primarily from the invaluable technological uses, ranging from invars with low thermal expansion, permalloys having high permeability, to maraging steel, high-resistance nichrome and corrosion-resistant coatings. Iron is also a cardinal ingredient of Earth’s magnetism and its transport properties at high pressure are presently the object of a lively debate2,3,4,5,6. At first sight, nickel should not play a role in generating the Earth’s magnetic field as it originates in the outer core, which is made of liquid iron. In current models, however there seems to be not enough energy to sustain the geodynamo through heat convection. Therefore, the importance of the inner core, ∼20% of which is believed to be made of nickel, is being critically reconsidered7.
Surprisingly, we still lack a complete theoretical comprehension of these two textbook materials. The reason can be ascribed to the intrinsic quantum many-body nature of their electronic structure, which makes a standard treatment in terms of independent electrons and conventional band theory inapplicable. The calculated Coulomb interaction is large and comparable in size in iron and nickel, which instead differ in the number of 3d electrons filling the bands close to the Fermi level. Iron is not too far from half filling, where the Coulomb interaction has the strongest effect and can easily drive a system Mott insulating. On the contrary, nickel has an almost full shell, a situation in which the Landau theory of Fermi liquids is in general recovered, even if the Coulomb interaction is significant. Yet, nickel was originally considered the more correlated of the two, because of photoemission satellites far away from the Fermi level, believed to originate from spectral weight transfer due to the Coulomb interaction8,9. A theoretical study by one of us10 put the two materials on a similar level, stressing the existence in both of them of well-formed local moments, despite their marked itinerant character.
Here we go a step further and perform electronic structure calculations including the full local Coulomb interaction. This way we demonstrate that nickel would not be a strong-coupling quantum magnet without the van Hove singularities of its fcc density of states (DOS). In fact, it turns out that only the combined influence of its peculiar DOS11 and of the electron–electron interaction can explain the Curie behaviour of its local spin susceptibility. This reflects in what we call pre-localized moments and a scattering rate, which is unexpectedly linear in temperature. The most important implication of our results for nickel comes from the observation that even at a pressure of hundreds of GPa, the position and the shape of these sharp features in the DOS do not change dramatically. Nickel remains in its fcc structure up to even larger pressures12,13,14 and its magnetic moments, though smaller, are much more robust than those of iron15. Consequently, this physics is still active at the pressures of the inner Earth’s core, at which instead iron is already a perfect Fermi liquid5,6. The non-Fermi-liquid mechanism identified here hence calls for including nickel in the current models of geomagnetism.
Results
Ferromagnetic transition temperatures
The Curie temperature (TC) of iron and nickel has been the object of several studies, in particular using the merger of density functional theory and dynamical mean-field theory (DFT+DMFT)17,18,19. This theoretical approach gives reliable results for three-dimensional materials with large coordination number, and is able to access the magnetic as well as the non-ordered phase above TC. The latter is described by DFT+DMFT as non-vanishing local magnetic moments with strong quantum fluctuations, which is crucial for the physics of correlated itinerant magnets20,21,22,23. Our DFT+DMFT spectra are consistent with previous calculations of similar kind10,24,25,26 and agree reasonably well with angular-resolved photoemission data (see Supplementary Note 5 and Supplementary Figs 2–5). They also reproduce the known signatures of correlation in both materials, in particular the visible spin-polarized photoemission satellite around −6 eV for nickel. Single-site DMFT describes dynamical local correlations via a k-independent self-energy. This gives rise to the non-Fermi-liquid physics discovered in this paper. Yet, non-local exchange can also play an important role here and have a visible impact on the spectral function. It can be accounted for by quasiparticle self-consistent GW (QSGW)27 and leads to a k-dependence of the self-energy. QSGW gives good results for iron but it does not fully capture the band structure of nickel28. A combination of both is possible in the GW+DMFT29 or QSGW+DMFT method28,30, but for the present extensive analysis such calculations are numerically too costly.
The hitherto published results differ in the Coulomb matrix elements Uijkl and in the approximation in which they are treated in the many-body part of the algorithm (DMFT)10,24,31. To calculate TC, we use ab-initio-estimated Uijkl and go beyond the ‘density–density’ and ‘Kanamori’ parametrizations (see ‘Methods’ section, Supplementary Note 1, Supplementary Table 1, as well as ref. 32). This allows us not only to improve the agreement with the experimental transition temperatures but, even more importantly, to take a step forward in the understanding of the differences between these two itinerant magnets. In Fig. 1a,b, we show the DFT+DMFT magnetization curves. The agreement with the experimental TCs is good (for the overestimate of TC in iron, see Supplementary Note 2 and Supplementary Table 2, as well as ref. 33). There is however, a substantial dependence on the parametrization of the Coulomb interaction, which reflects the big influence of electron–electron interaction in iron and nickel. However, since the two materials have different fillings of the d-shell and different band structures, the impact of correlations on their physics is profoundly contrasting. In Fig. 1c,d, we show the local self-energy , a complex function describing the correction to the non-interacting propagation of an electron added to the system (Green’s function) due to electron–electron interactions.
highlights already many of the dissimilarities: Unlike in nickel, the eg orbitals in iron display strong scattering (proportional to the imaginary part of the self-energy at small frequencies) and large quasiparticle renormalization34. Notwithstanding the smaller scattering rate in nickel (Fig. 1d), we reveal a surprisingly large deviation from the T2-behaviour predicted by the Landau theory of Fermi liquids. The scattering rate of nickel is indeed strongly non-quadratic in a large range of temperatures, as we will see in Fig. 4c.
Ferromagnetic order parameter in bcc iron (a) and in fcc nickel (b) as a function of temperature, whereas N↑ (N↓) are the total number of spin-up (-down) electrons in the correlated d orbitals. The Curie temperature TC is signalled by the magnetization dropping to zero. For nickel, we obtain TC=600 K, very close to the experimental value of 633 K (ref. 16), indicated by the black arrow in b. Our estimated TC for iron is around 1,500 K, that is, roughly 30% larger than the experimental one of 1,043 K (ref. 16), marked by the black arrow in a (for a discussion, see ‘Methods’ section, where also a description of the three parametrization used for the Coulomb interaction is given). Imaginary part of the Matsubara self-energies of iron (c) and nickel (d) at β=30 eV−1 in the paramagnetic phase. The curves with filled circles show one of the degenerate t2g orbitals, with empty circles one of the degenerate eg orbitals. The lifetime of the quasiparticles is inversely proportional to
. Contrary to nickel, the scattering rate in iron at ambient pressure is large, even though the insulating-like shape of the density–density eg-self-energy is replaced by an upturn at small frequencies in Kanamori and full Coulomb.
(a) Temperature dependence of the local spin susceptibility in iron, calculated with DFT+DMFT. Calculations are performed following the non-ordered magnetic solution, also below the ferromagnetic transition temperature TC at which the uniform (Q=0) susceptibility diverges (not shown).
in iron displays a marked 1/T Curie–Weiss behaviour, above as well as below TC, indicating the existence of robust local magnetic moments. The fits are least-square fits with fit function
. For density–density, we obtain an effective local moment of
and a Kondo temperature of TK=35 K, for Kanamori
and TK=227 K. The DFT+DMFT data are compared to the uncorrelated and ‘bubble’ susceptibilities, that is, calculated, respectively, from the bare and ‘dressed’ Green’s functions, neglecting the effect of vertex corrections. Figure b shows the decay in imaginary time τ of the local spin susceptibility at two temperatures β=4 eV−1 (dashed lines) and β=30 eV−1 (full lines), for density–density (red) as well as Kanamori (blue). The fact that
is going to zero much more slowly than β implies the presence of persistent local moments at these temperatures.
(a) Temperature dependence of the static local spin susceptibility of nickel in DFT+DMFT, compared to the ‘bubble’ approximation and to the non-interacting one. To show that the characteristic temperature dependence of the non-interacting susceptibility originates from the t2g sector and its van Hove singularity, we also plot the intra-orbital contribution to the full
(‘full’), considering the cases where either the five orbital-diagonal terms of
are summed (‘
’), or only the two eg terms are retained (‘eg only’). This shows the more conventional Pauli spin response of the eg part is in agreement with the fact that the eg DOS is much smoother around EF=0. (b) Inverse susceptibility for the non-interacting and DFT+DMFT case. This illustrates the main peculiarity of nickel, namely that already the non-interacting spin response is characterized by a 1/T law. As explained in the text, this is due to pre-localized moments arising from the vicinity to the van Hove singularity. (c) Electronic band dispersion of nickel on the hexagonal face of the Brillouin zone, close to the L point. The colors indicate the energy of the band relative to the Fermi level, which is located at zero energy. The extended flat region around the shallow maximum at L is responsible for the van Hove singularity. (d) t2g and eg DOS for energies close to EF=0. In the inset, the electronic state dispersion of nickel, close to the W-L-K region and to the top of the band is shown. The distance of the sharp step in the t2g orbitals at E=0.17 eV corresponds to the kink of the non-interacting susceptibility in b at T=2,000 K. (e)
for β=4 eV−1 (dashed) and 30 eV−1 (solid). (f) Instantaneous (τ=0) and long-time (
) values of
. From the latter one can clearly see that the moment is eventually screened at temperatures much lower than TC. The comparison with the non-interacting and with the ‘bubble’ results shows also that vertex corrections are important and the DFT+DMFT result cannot be obtained by using ‘dressed’ quasiparticle propagators (see also b).
Iron as a typical strong-coupling ferromagnet
The onset of ferromagnetic long-range order is signalled by a divergence of the Q=0 spin susceptibility at the Curie temperature. For a ferromagnetic metal, such as nickel or iron, the local spin susceptibility is instead a regular function of T. The latter is defined as , that is, the ω=0-Fourier component of the spin–spin response function
, where
is the local spin operator for the orbital i on nickel or iron, at the imaginary time τ. g denotes the electron spin gyromagnetic factor. By studying
, the formation of local magnetic moments can be inferred. A Stoner-like ferromagnet does not have pre-formed local moments, whereas a strong-coupling ferromagnetic instability can be pictured as the emergence of localized spin moments at high temperatures, which acquire phase coherence and order throughout the crystal on cooling. With DFT+DMFT, we can access
also below the Curie temperature, as if magnetism was not present (paramagnetic solution). This is useful to study the intrinsic local spin response, independently of the actual long-range order. If the local moments are created by the electron–electron interaction,
must behave, at sufficiently high temperatures, as 1/T (Curie law). This clearly happens in iron (Fig. 2a) for both parametrizations of the Coulomb interaction used in this case. Plotted on the same scale of the interacting one, the Uijkl=0-susceptibility (green dots), as well as the dressed convolution of two DMFT Green’s functions (‘bubble’ approximation, grey squares), are small and weakly temperature dependent. They are completely overwhelmed by the pronounced Curie behaviour obtained, as soon as the Coulomb interaction is considered.
In the paramagnetic phase, iron is therefore a bad metal with a strong electron–electron scattering and robust local magnetic moments. The local susceptibility nicely fits to Wilson’s formula35
![](http://media.springernature.com/lw310/springer-static/image/art%3A10.1038%2Fncomms16062/MediaObjects/41467_2017_Article_BFncomms16062_Equ1_HTML.gif)
as shown in Fig. 2a,b. Here μeff is the local moment and, indeed, the estimated values are in excellent agreement with the experimentally ordered ferromagnetic moment. TK is the Kondo temperature and indicates the screening of the local moment, as well as the onset of a Fermi liquid behaviour. As our results show, this would only occur far below TC, if no long-range order would set in. At TC, the paramagnetic phase of iron is therefore still closer to a local moment than to an itinerant electron description. This indicates that electronic correlations are much more important around TC than for the low temperature spin-polarized ferromagnetic solution, which is not too far from a single-electron Slater determinant.
Nickel as a van Hove magnet
The situation in nickel is shown in Fig. 3 and it is totally different. The absolute value of the local spin susceptibility (Fig. 3a) is way smaller than in iron. Also for nickel, it follows the Wilson law and, surprisingly, this is already the case for the non-interacting susceptibility. We can explain this by the particular shape of the DOS of nickel with its van Hove singularity, appearing in the t2g sector (see Fig. 3d) slightly below the Fermi level (EF=0). As shown in Fig. 3c, the corresponding band forms a hollow on the hexagonal face of the Brillouin zone, inside which the dispersion is essentially flat, except for a slow modulation between the six minima and the shallow maximum around the L point. Though this singularity is integrable in three dimensions, it induces a pre-localization effect of the Bloch electrons which, for geometrical reasons, have a band velocity close to zero. This reflects directly in an apparent Curie law of the non-interacting spin susceptibility, governed by the distance in energy from the flat band11,36. Including electronic correlations, the local susceptibility in Fig. 3b keeps its 1/T behaviour but is strongly enhanced (by a factor of 2–3). We stress that such enhancement is much stronger than what is to be expected from the quasiparticle renormalization Z∼0.8 (Z=(1−α)−1 with
in Fig. 1d). This indicates the fundamental importance of vertex corrections to the susceptibility of nickel, despite its large filling.
The second fingerprint of pronounced band effects in nickel is the kink in the spin susceptibility. This is present in the Uijkl=0 as well as in the interacting case (see Fig. 3a,b, Supplementary Note 10 and Supplementary Fig. 9) and separates two Wilson-like behaviours with different slopes of . The kink can be traced back to the fact that the chemical potential is ∼0.17 eV below the sharp upper edge of the t2g DOS and ∼0.05 eV above the van Hove singularity (see Fig. 3c,d). The former acts as a source of pre-localization too (for a demonstration, see the analysis under pressure and the inset to Fig. 4b). Since the two singularities are different, their influence to
is not symmetric, resulting in two different 1/T behaviours: decreasing T from high temperatures, we switch from one to the other when the larger of the two energy scales, that is, ∼1,700 K, is crossed (see Fig. 4a).
(a) The t2g DOS of nickel at different values of the pressure. The van Hove peak and the sharp edge are smoothed with increasing pressure, but the Fermi level (EF=0) remains close to these two singular points. The cross at temperature T1 marks the beginning of the DOS steps, whereas the square at T2 marks is its ending. Their evolution with pressure is shown in the inset to b. (b) Non-interacting local spin susceptibility versus temperature at high pressures. The dashed lines are least-square fits of the high- and low-temperature region, which uncover the separation between the two Wilson-like behaviours, shifting towards higher temperatures compared to ambient pressure. The position of this kink (shown as hexagons in the inset) scales with the energy distance between EF and the sharp edge of the t2g DOS. (c) A consequence of the sharp features at the top of the band is the deviation of the quasiparticle scattering rate from the T2 law predicted by the Landau theory. Here this is shown for pure nickel, by plotting the scattering rates of one of the degenerate t2g and one of the degenerate eg orbitals, both at ambient pressure and at 330 GPa. The error bars come from averaging over different fit parameters (number of Matsubara frequencies and order of fit-polynomial).
It is important to note that the inclusion of interactions does not alter this picture, apart from lifetime effects and broadening, which make the kink much smoother and its position slightly renormalized. The kink in the local susceptibility directly translates via the Bethe–Salpeter equation to a kink in the ferromagnetic susceptibility. It clarifies the experimentally observed kink at ∼1,200 K (ref. 37), reported almost 80 years ago but so far, to the best of our knowledge, without explanation.
Since in nickel, the Wilson-like behaviour is already present in at Uijkl=0, a direct interpretation in terms of a Kondo effect is difficult. Let us hence turn to the imaginary time τ dependence of the local susceptibility, shown in Fig. 3e,f. Without interaction, there is a rapid drop of
for τ→β/2. This indicates the absence of long-lived local moments. A drop is present with interaction as well, but on much larger timescales and from larger
values. This confirms the presence of correlation-enhanced38,39 local moments in nickel and the τ dependence reveals their screening properties. Since there remains a finite unscreened moment
even at β=30 eV−1 (370 K), the screening is not complete. Only at much lower temperatures (of the order of 100 K), this moment eventually gets completely screened, see inset of Fig. 3f. The existence of such a two-stage screening can be clarified invoking the few charge carriers available for screening, as in Nozières exhaustion scenario40,41. Also the local spin being larger than 1/2 (ref. 42) and the fact that d electrons act both as localized moments and itinerant ones can contribute. The latter screen the former. This leads to different energy scales for the onset of screening and for complete screening43, with the range in-between strongly affected by the van Hove peak in the d electron spectral function.
A unified picture
A van Hove singularity is actually also present in the bcc DOS of iron (see Supplementary Note 8 and Supplementary Fig. 7). The reason why this does not influence the physical properties as for nickel is the different occupation of the d shell of the two materials. Due to the proximity to half filling, in iron the physics is dominated by correlation-induced band renormalization and strong electron–electron scattering. This means that, even though the van Hove singularity does give a 1/T behaviour for the non-interacting as well as a kink visible on a small scale (see Supplementary Fig. 7), this has hardly any influence in the actual behaviour in the presence of the interaction.
Nickel is instead close to nine d electrons and moreover the individual occupation of its five d orbitals is almost maximized. Hence, the entire manifold of electronic states is practically occupied and the majority of the active electrons lives close to van Hove singularity and to the sharp feature at the top of the t2g DOS. As a result, its physics is distinct from the more common case of a strongly correlated metal with sharp features in the DOS located far away from the band edges (bcc iron).
This difference between iron and nickel does not only concern the formation of local moments but it also leads to different microscopic mechanisms for ferromagnetism. In the case of iron, ferromagnetism is driven by Hund’s rule coupling, which forms a large local moment of the d electrons that are close to half filling. These Hund’s moments then only need a bit of hopping to order44. For nickel on the other side, its peculiar DOS is essential not only for the formation of the local moments, but also for their ferromagnetic long-range order. This is the flat band45, or more generally asymmetric DOS route46,47, to ferromagnetism. In contrast to the aforementioned work, Hund’s coupling plays also an important role in nickel. It enhances the local moments and strongly affects TC (see Supplementary Note 2 and Supplementary Table 2). Such a mixture of Hund’s rule and flat band ferromagnetism has recently also been observed in BaRuO3 (ref. 48).
Nickel at Earth’s core pressures
Inspired by our improved understanding of the different nature of magnetism in iron and nickel, we discuss now the physics of Ni under high pressures. Indeed, if the non-Fermi-liquid properties of nickel survive the extreme conditions of the Earth’s core, our conclusions would be also important to the recent debate about geomagnetism. The key observation is that the van Hove singularity in nickel does not dramatically change its position with pressure. As shown in Fig. 4a, it gets gradually smoothed out but it survives pressures of even hundreds of GPa (see Supplementary Fig. 1, Supplementary Tables 4 and 5, as well as Supplementary Note 4 for the equations of state used to obtain the pressure–volume relationships for fcc Ni). At the same time, the sharp edge of the t2g DOS moves away from the Fermi level but its influence can be clearly observed in the non-interacting at all values of the pressure considered here. In Fig. 4b, the kink is indeed still visible at high pressure. In the inset, we compare the kink position with the distance—converted in temperature—between EF and the edge of the t2g DOS (see Fig. 4a). They scale the same way with pressure, confirming our interpretation in terms of sharp features of the DOS.
We now analyse the electron–electron scattering rate , as possible non-quadratic temperature dependencies of this quantity signal deviations from the Landau theory description of Fermi liquids. Γ of pure fcc nickel is shown in Fig. 4c as a function of temperature at ambient pressure and 330 GPa, characteristic of the Earth’s inner core. In both cases, we observe non-Fermi-liquid behaviour in a large interval of temperatures. A technical comment is in order here: extracting the scattering rate from the Matsubara axis at these elevated temperatures poses well-known difficulties6. We therefore first checked that a three-orbital model with the same filling of nickel, the same bandwidth of the ambient pressure case and no singularity and no asymmetry in the DOS gives a nicely T2 Fermi-liquid scattering rate (not shown). This confirms that it is possible to reliably extract the scattering rate from our DFT+DMFT calculations—at least for temperatures up to 2–3,000 K—without artefacts (see Supplementary Note 9 and Supplementary Fig. 8). As a matter of fact, even by considering error bars estimated from several polynomial fits to
(denoted by the vertical bars in Fig. 4c), the non-quadratic temperature behaviour is clearly recognizable.
Hence we find that, even though judging from the self-energy nickel may seem to be a much more conventional metal than iron (see Fig. 1c,d), its scattering rate has a non-Fermi-liquid behaviour at ambient pressure as well as at 330 GPa. This deviation from the standard linear temperature dependence is caused by the van Hove singularity36 and it is so robust that it is still visible at Earth’s core pressures, where the sharp features in the DOS are weakened but not yet completely gone.
Disordered iron/nickel alloy
The inner Earth’s core contains about 20% nickel in addition to solid iron and, at these extreme pressure and temperature conditions, they form a disordered alloy. Therefore, to understand whether or not nickel should actually be considered in theories of geomagnetism, one has to study a disordered iron/nickel alloy under pressure. In particular, it should be seen if, even under extreme conditions, the electronic scattering rate is large and non-Fermi liquid, as in pure fcc Ni where the van Hove singularity mechanism is active. The electronic properties of an alloy are fundamentally different from those of a perfect crystal. To take the nontrivial disorder effects into account, we performed calculations for nickel alloys of various concentrations at the Earth’s pressure within a coherent potential approximation (CPA)+DMFT scheme. The details of our implementation are described in the Supplementary Note 6.
The identification of the correct crystalline structure of iron at Earth’s core conditions is still a subject of debate (see ref. 5 and references therein, as well as ref. 49). In this work we will consider an hcp Fe/Ni alloy, since hcp Fe (ɛ-Fe) emerges as the most stable structure, according to several studies14,50,51. The blue curve in Fig. 5a shows the DOS of hcp iron at core pressure. The vertical dashed lines in the case under pressure show the position of the local levels, after the shift of the CPA+DMFT algorithm that simulates the presence of the dopant atoms. For the iron/nickel alloy, the shift is towards the top of the hcp band and brings the local levels of Ni close to the sharp structures resembling those of pure fcc nickel (shown in Fig. 4a). We also considered the alloy with manganese for reference purposes. In that case, the CPA shift has the opposite sign and it does not bring the energy levels close to any special structure in the DOS, therefore the alloy with Mn is expected to have more standard electronic properties than that with Ni.
(a) DOS of the ɛ (hcp) phase of iron at ambient and Earth’s core pressure (green and blue lines, respectively). E=0 corresponds to the chemical potential of hcp iron. The vertical dashed lines indicate the energies at which the local levels of Ni and Mn are shifted within the CPA+DMFT scheme. In contrast to the shift for the Fe/Mn alloy (used here as a reference example), that for Fe/Ni brings the local levels of nickel close to the peak at the top of the hcp band. Since the latter is similar to the sharp features of pure fcc nickel (shown in Fig. 4a), the non-Fermi-liquid effects observed in the pure fcc material are expected to survive in the iron/nickel alloy. (b) Non-interacting local spin susceptibility for pure hcp iron and for the alloys of hcp iron with Mn and Ni, all at Earth’s core pressure, that is, 330 GPa. The iron/nickel alloy strongly deviates from standard Pauli behaviour of good Fermi liquids. The example of Mn is on the contrary much closer to the Fermi-liquid result of hcp iron. (c) The scattering rate (averaged over all d orbitals) of the nickel alloy at high temperatures within CPA+DMFT is remarkably similar to the corresponding one of pure fcc nickel at these pressures and much larger than that of the Fe/Mn alloy, taken here as a reference.
The first indication that the hcp iron/nickel alloy shares part of the anomalous behaviour of fcc nickel comes from its non-interacting spin susceptibility (Fig. 5b). While pure hcp iron, as well as the alloy with Mn, displays a Pauli-like spin susceptibility in the absence of electron–electron interaction, the alloy with nickel (both with 5 and 20% nickel content) shows the Wilson-like behaviour which characterizes pure fcc nickel (see Fig. 4b). Note that the absolute values of depend mainly on the filling, as already observed for pure iron and nickel. Figure 5c confirms that, when taking the electron–electron interaction into account, 20% nickel leads to a linear and large quasiparticle scattering rate at high temperatures. This confirms the close resemblance of the iron/nickel disordered alloy to pure fcc nickel, for what concerns the non-Fermi-liquid nature of the scattering. The red solid circles shown in Fig. 5c approach the grey curve at high temperatures (or even go somewhat above it), which refers to pure fcc nickel at 330 GPa. This demonstrates that the anomalous effect of nickel is relevant also in the case of the alloy at the Earth’s core conditions.
Discussion
The disorder, that we have treated here at the CPA level, turned out to have a crucial effect. A comparable amount of nickel combined with hcp iron in a translationally invariant crystalline structure gives more Fermi-liquid results, as interestingly pointed out in a recent paper by Vekilova et al.52. The latter approach has the advantage over CPA+DMFT that non-local changes to the band-structure induced by the presence of the nickel atoms are fully taken into account. By going beyond the state-of-the-art implementation of CPA+DMFT, which is the one we followed here, it will be possible in the future to fully describe this difficult interplay between many-body and disorder effects.
The linear in T scattering rate of the iron/nickel alloy at core pressure in a large window of temperatures suggests a small thermal conductivity. Molecular dynamics followed by real-space DMFT calculations of large nickel supercells, shows that the van Hove singularity in the spectrum and the scattering rate are not dramatically modified by the inclusion of thermal disorder (for details, see Supplementary Note 7 and Supplementary Fig. 6). Our results may therefore play a role in models of the geodynamo, recently questioned because of the large thermal conductivity of iron2. Whether or not this can be reconciled with iron alone is at the moment under debate6,7, but according to the current understanding there would be too little energy left for convection in the total heat budget4. In light of our results, it will be interesting to reconsider the contribution of nickel to the total thermal conductivity of the core. The next challenge will thus be to include electronic correlations also in the ab initio study of the liquid phase of iron and nickel and determine if a more consistent explanation of the geodynamo can be obtained.
Methods
Density functional theory and projections
Density functional calculations within the local-density approximation were performed using the projector-augmented-wave53 based Vienna ab initio simulation package54,55. We used the experimentally determined lattice parameters for both materials, that is, 2.87 Å for iron and 3.52 Å for nickel. The local Hamiltonian for the subsequent many-body calculations was constructed using the projection on local orbitals as described in refs 56, 57. Here we included the 3d bands as well as the 4s band of both metals.
Pressure
To simulate the effects of pressure in Ni, we calculated energy versus volume curves and fitted them with different equations of state (see Supplementary Note 4). From the fit, one obtains parameters, such as the bulk modulus, that can in turn be used to produce a pressure versus volume phase diagram for the material. From such a diagram, one can then read off the estimate the equation of state gives for the volume at any pressure. We employed different equations of state as well as different DFT functionals and created an aggregate best guess for the volume at each pressure considered. Since the equation of state of Fe is not well described within DFT, we used the volume established within the preliminary reference Earth model (see Supplementary Note 6 for futher details). Subsequently, a calculation using local-density approximation was performed using the chosen volume and a low energy model was constructed as described in the ‘Density functional theory and projections’ section.
DFT+DMFT
We combine DFT and DMFT using a localized basis constructed by means of the projection formalism as described in the ‘Density Functional Theory and projections’ section. From there we obtain a Hamiltonian matrix, which is subsequently exploited to compute the so-called hybridization function. This is used as an input for our hybridization-expansion continuous time quantum Monte Carlo (CT-HYB) impurity solver58, which solves the auxiliary Anderson impurity problem within the DMFT loop numerically exactly at each step. Since our double-counting correction is self-consistently adjusted, we needed ∼50 DMFT iterations to reach convergence. The software used to produce the DFT+DMFT results is the CT-HYB Wien–Würzburg code package ‘w2dynamics’ (ref. 32), which is available on request to the corresponding author. The results for the disordered alloys at core conditions have been obtained within a CPA scheme+DMFT and thermal disordered has been simulated also by using molecular dynamics and DMFT. The corresponding implementations are discussed in Supplementary Notes 6 and 7.
Parametrization of the Coulomb interaction
We have estimated Uijkl in a fully ab initio way including the five 3d and the 4s orbital in the target space, by means of constrained-random phase approximation (cRPA)59. In ‘w2dynamics’ (ref. 32), these matrix elements have been used here with decreasing level of complexity: The ‘full-Coulomb’ parametrization considers the full Uijkl tensor and it is applied here for the first time to iron and nickel. For a recent discussion on the role of exchange, see also ref. 60. In the other two parametrizations, some entries are instead neglected, with a consequent reduction in the numerical effort. In the ‘Kanamori’-only parametrization, the Uijkl elements compatible with full rotational invariance are left, whereas the corresponding spin–spin interaction is constrained to an Ising-like form in the case of the ‘density–density’, see Supplementary Note 1.
Double counting
The Coulomb matrix elements calculated within the cRPA contain naturally the cubic symmetry of the crystal. This means, that unlike in the usual spherically symmetric parametrization of the Coulomb matrix via Slater integrals Fk(ref. 61), the diagonal entries Uiiii are different for the t2g and eg orbitals. This poses a challenge to the so-called double-counting correction of the DFT+DMFT formalism, which is usually estimated as an orbitally averaged Coulomb interaction, see for example, ref. 62. Here we use the approach to constraint the total charge in the impurity, which is based on the Friedel sum rule63. We thus require the orbital occupancies of the interacting and non-interacting impurity Green’s functions to coincide in self-consistency64, see Supplementary Note 3 and Supplementary Table 3 for details.
Data availability
The data that support the findings of this study are available from the corresponding author on reasonable request.
Additional information
How to cite this article: Hausoel, A. et al. Local magnetic moments in iron and nickel at ambient and Earth's core conditions. Nat. Commun. 8, 16062 doi: 10.1038/ncomms16062 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Aristoteles. De Anima, 405, a20–22 (384–322 BC).
Pozzo, M., Davies, C., Gubbins, D. & Alfè, D. Thermal and electrical conductivity of iron at Earths core conditions. Nature 485, 355–358 (2010).
Cohen, R. E., Mazin, I. I. & Isaak, D. G. Magnetic collapse in transition metal oxides at high pressure: implications for the earth. Science 275, 654–657 (1997).
Olson, P. The new core paradox. Science 342, 431–432 (2013).
Pourovskii, L. V. et al. Electronic properties and magnetism of iron at the Earth’s inner core conditions. Phys. Rev. B 87, 115130 (2013).
Pourovskii, L. V., Mravlje, J., Georges, A., Simak, S. I. & Abrikosov, I. A. Fermi-liquid behavior and thermal conductivity of ɛ-iron at Earth’s core conditions. Preprint at http://arxiv.org/abs/1603.02287 (2016).
O’Rourke, J. G. & Stevenson, D. J. Powering Earth’s dynamo with magnesium precipitation from the core. Nature 529, 387–389 (2016).
Hüffner, S. & Wertheim, G. K. Multielectron effects in the XPS spectra of nickel. Phys. Lett. A 51, 299–300 (1975).
Tanaka, A., Jo, T. & Sawatzki, G. A. Configuration interaction in Ni metal and Ni alloys and high-energy spectroscopy. J. Phys. Soc. Jpn 61, 2636–2639 (1992).
Lichtenstein, A. I., Katsnelson, M. I. & Kotliar, G. Finite-temperature magnetism of transition metals: an ab initio dynamical mean-field theory. Phys. Rev. Lett. 87, 067205 (2001).
Vonsovskii, S. V., Katsnelson, M. I. & Trefilov, A. V. Localized and itinerant behavior of electrons in metals. Phys. Met. Metallogr. 76, 247–299 (1993).
Mohammed, Y. S., Yan, Y., Wang, H., Li, K. & Du, X. Stability of ferromagnetism in Fe, Co, and Ni metals under high pressure with GGA and GGA+U. J. Magn. Magn. Mat. 322, 653–657 (2010).
McMahan, A. K. & Albers, R. C. Insulating nickel at a pressure of 34 TPa. Phys. Rev. Lett. 49, 1198–1201 (1982).
Kuwayama, Y., Hirose, K., Sata, N. & Ohishi, Y. Phase relations of iron and ironnickel alloys up to 300 GPa: implications for composition and structure of the Earth’s inner core. Earth Planet. Sci. Lett. 273, 379–385 (2008).
Torchio, R., Mathon, O. & Pascarelli, S. XAS and XMCD spectroscopies to study matter at high pressure: probing the correlation between structure and magnetism in the 3d metals. Coord. Chem. Rev. 277–278, 80–94 (2014).
Wohlfarth E. P. in Ferromagnetic Materials Vol. 1 (North-Holland Publishing Company, 1980).
Georges, A., Kotliar, G., Krauth, W. & Rozenberg, M. J. Dynamical mean-field theory of strongly correlated fermion systems and the limit of infinite dimensions. Rev. Mod. Phys. 68, 13–125 (1996).
Kotliar, G. et al. Electronic structure calculations with dynamical mean-field theory. Rev. Mod. Phys. 78, 865–951 (2006).
Held, K. Electronic structure calculations using dynamical mean field theory. Adv. Phys. 56, 829–926 (2007).
Lichtenstein, A. I., Katsnelson, M. I., Antropov, V. P. & Gubanov, V. A. Local spin density functional approach to the theory of exchange interactions in ferromagnetic metals and alloys. J. Magn. Magn. Mater. 67, 65–74 (1987).
Ruban, A. V., Khmelevskyi, S., Mohn, P. & Johansson, B. Temperature-induced longitudinal spin fluctuations in Fe and Ni. Phys. Rev. B 75, 054402 (2007).
Kudrnovský, J. et al. Spin-disorder resistivity of ferromagnetic metals from first principles: the disordered-local-moment approach. Phys. Rev. B 86, 144423 (2012).
Drchal, V., Kudrnovský, J. & Turek, I. Effective magnetic Hamiltonians from first principles. Eur. Phys. J. Web Conf. 40, 11001 (2013).
Belozerov, A. S., Leonov, I. & Anisimov, V. I. Magnetism of iron and nickel from rotationally invariant Hirsch-Fye quantum Monte Carlo calculations. Phys. Rev. B 87, 125138 (2013).
Sánchez-Barriga, J. et al. Strength of correlation effects in the electronic structure of iron. Phys. Rev. Lett. 103, 267203 (2009).
Schickling, T., Bünemann, J., Gebhard, F. & Boeri, L. Quasiparticle bands and structural phase transition of iron from Gutzwiller density-functional theory. Phys. Rev. B 93, 205151 (2016).
Kotani, T., van Schilfgaarde, M. & Faleev, S. V. Quasiparticle self-consistent GW method: a basis for the independent-particle approximation. Phys. Rev. B 76, 165106 (2007).
Sponza, L. et al. Self-energies in itinerant magnets: a focus on Fe and Ni. Phys. Rev. B 95, 041112 (2017).
Biermann, S., Aryasetiawan, F. & Georges, A. First-principles approach to the electronic structure of strongly correlated systems: combining the GW approximation and dynamical mean-field theory. Phys. Rev. Lett. 90, 086402 (2003).
Tomczak, J. QSGW+DMFT: an electronic structure scheme for the iron pnictides and beyond. J. Phys. Conf. Ser. 592, 012055 (2015).
Leonov, I., Poteryaev, A. I., Anisimov, V. I. & Vollhardt, D. Electronic correlations at the α-γ structural phase transition in paramagnetic iron. Phys. Rev. Lett. 106, 106405 (2011).
Parragh, N., Toschi, A., Held, K. & Sangiovanni, G. Conserved quantities of SU(2)-invariant interactions for correlated fermions and the advantages for quantum Monte Carlo simulations. Phys. Rev. B 86, 155158 (2012).
Katanin, A., Belozerov, A. & Anisimov, V. Nonlocal correlations in the vicinity of the α-γ phase transition in iron within a DMFT plus spin-fermion model approach. Phys. Rev. B 94, 161117 (2016).
Katanin, A. et al. Orbital-selective formation of local moments in α-iron: First-principles route to an effective model. Phys. Rev. B 81, 045117 (2010).
Wilson, K. G. The renormalization group: critical phenomena and the Kondo problem. Rev. Mod. Phys. 47, 773–840 (1975).
Dzyaloshinskii, I. Extended Van-Hove singularity and related non-Fermi liquids. J. Phys. I 6, 119–135 (1996).
Sucksmith, W. & Pearce, R. R. The paramagnetism of the ferromagnetic elements. Proc. R. Soc. Lond. A 167, 189–204 (1938).
Prokopjev, Y. I. & Reser, B. I. A single-site spin correlation function in paramagnetic iron. J. Phys. Condens. Matter 3, 6055–6067 (1991).
Toschi, A., Arita, R., Hansmann, P., Sangiovanni, G. & Held, K. Quantum dynamical screening of the local magnetic moment in Fe-based superconductors. Phys. Rev. B 86, 064411 (2012).
Nozières, P. Magnetic impurities and Kondo effect. Ann. Phys. 10, 19–35 (1985).
Burdin, S., Georges, A. & Grempel, D. R. Coherence scale of the Kondo lattice. Phys. Rev. Lett. 85, 1048–1051 (2000).
Nevidomskyy, A. H. & Coleman, P. Kondo resonance narrowing in d- and f-electron systems. Phys. Rev. Lett. 103, 147205 (2009).
Held, K., Peters, R. & Toschi, A. Poor mans understanding of kinks originating from strong electronic correlations. Phys. Rev. Lett. 110, 246402 (2013).
Held, K. & Vollhardt, D. Microscopic conditions favoring itinerant ferromagnetism: hund’s rule coupling and orbital degeneracy. Eur. Phys. J. B 5, 473–478 (1998).
Mielke, A. & Tasaki, H. Ferromagnetism in the Hubbard model. Commun. Math. Phys. 158, 341–371 (1993).
Ulmke, M. Ferromagnetism in the Hubbard model on fcc-type lattices. Eur. Phys. J. B 1, 301–304 (1998).
Wahle, J., Blümer,, Schlipf, N. J., Held, K. & Vollhardt, D. Microscopic conditions favoring itinerant ferromagnetism. Phys. Rev. B 58, 12749–12757 (1998).
Han, Q., Dang, H. T. & Millis, A. J. Ferromagnetism and correlation strength in cubic barium ruthenate in comparison to strontium and calcium ruthenate: a dynamical mean-field study. Phys. Rev. B 93, 155103 (2016).
Belonoshko, A. B. et al. Stabilization of body-centred cubic iron under inner-core conditions. Nat. Geosci. 10, 312–316 (2017).
Vocadlo, L. et al. Possible thermal and chemical stabilization of body-centred-cubic iron in the Earth’s core. Nature 424, 536–539 (2003).
Anzellini, S., Dewaele, A., Mezouar, M., Loubeyre, P. & Morard, G. Melting of iron at Earth’s inner core boundary based on fast X-ray diffraction. Science 340, 464–466 (2013).
Vekilova, O. Y., Pourovskii, L. V., Abrikosov, I. A. & Simak, S. I. Electronic correlations in Fe at Earth’s inner core conditions: Effects of alloying with Ni. Phys. Rev. B 91, 245116 (2015).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Hafner, J. Norm-conserving and ultrasoft pseudopotentials for first-row and transition elements. J. Phys. Condens. Matter 6, 8245–8258 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Amadon, B. et al. Plane-wave based electronic structure calculations for correlated materials using dynamical mean-field theory and projected local orbitals. Phys. Rev. B 77, 205112 (2008).
Karolak, M., Wehling, T. O., Lechermann, F. & Lichtenstein, A. I. General DFT++ method implemented with projector augmented waves: electronic structure of SrVO3 and the Mott transition in Ca2−xSrxRuO4 . J. Phys. Condens. Matter 23, 085601 (2011).
Gull, E. et al. Continuous-time Monte Carlo methods for quantum impurity models. Rev. Mod. Phys. 83, 349–404 (2011).
Şaşɩoğlu, E., Friedrich, C. & Blügel, S. Effective Coulomb interaction in transition metals from constrained random-phase approximation. Phys. Rev. B 83, 121101 (2011).
Kvashnin, Y. O. et al. Exchange parameters of strongly correlated materials: Extraction from spin-polarised density functional theory plus dynamical mean-field theory. Phys. Rev. B 91, 125133 (2015).
Slater, J. C. The theory of complex spectra. Phys. Rev. 34, 1293–1322 (1929).
Czyżyk, M. T. & Sawatzky, G. A. Local-density functional and on-site correlations: the electronic structure of La2CuO4 and LaCuO3 . Phys. Rev. B 49, 14211–14228 (1994).
Hewson, A. C. The Kondo Problem to Heavy Fermions Cambridge University Press (1997).
Karolak, M. et al. Double counting in LDA+DMFT - The example of NiO. J. Electron Spectros. Relat. Phenomena 181, 11–15 (2010).
Acknowledgements
We thank Sergio Ciuchi, Domenico Di Sante and Olle Gunnarsson for comments and useful discussions. This work was supported by the DFG through FOR 1346 (A.H., A.L. and A.T. in its FWF subproject I-1395-N16), FOR 1162 (M.K.) and SFB 1170 ‘ToCoTronics’ (G.S.). A.K. acknowledges the state assignment of FASO, Russian Federation (theme Electron, 01201463326) and Russian Foundation of Basic Research (project no. 17-02-00942) and K.H. the European Research Council under the European Union’s Seventh Framework Program (FP/2007-2013)/ERC Grant agreement no. 306447. The authors gratefully acknowledge the Gauss Centre for Supercomputing e.V. (www.gauss-centre.eu) for funding this project by providing computing time on the GCS Supercomputer SuperMUC at Leibniz Supercomputing Centre (LRZ, www.lrz.de).
Author information
Authors and Affiliations
Contributions
A.H. and M.K. performed the ab initio many-body calculations, with the cRPA matrix elements by E.S. as input. G.S. conceived and coordinated the project. All authors have contributed to the physical interpretation of the results and worked together at the writing of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Hausoel, A., Karolak, M., Şaşιoğlu, E. et al. Local magnetic moments in iron and nickel at ambient and Earth’s core conditions. Nat Commun 8, 16062 (2017). https://doi.org/10.1038/ncomms16062
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms16062
This article is cited by
-
Dual nature of magnetism driven by momentum dependent f-d Kondo hybridization
Communications Physics (2024)
-
Heavy fermions vs doped Mott physics in heterogeneous Ta-dichalcogenide bilayers
Nature Communications (2024)
-
A database of high-pressure crystal structures from hydrogen to lanthanum
Scientific Data (2024)
-
Hopping frustration-induced flat band and strange metallicity in a kagome metal
Nature Physics (2024)
-
Flat bands, strange metals and the Kondo effect
Nature Reviews Materials (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.