Abstract
We report on the high thermoelectric performance of p-type polycrystalline BiCuSeO, a layered oxyselenide composed of alternating conductive (Cu2Se2)2− and insulating (Bi2O2)2+ layers. The electrical transport properties of BiCuSeO materials can be significantly improved by substituting Bi3+ with Ca2+. The resulting materials exhibit a large positive Seebeck coefficient of ∼+330 μV K−1 at 300 K, which may be due to the ‘natural superlattice’ layered structure and the moderate effective mass suggested by both electronic density of states and carrier concentration calculations. After doping with Ca, enhanced electrical conductivity coupled with a moderate Seebeck coefficient leads to a power factor of ∼4.74 μW cm−1 K−2 at 923 K. Moreover, BiCuSeO shows very low thermal conductivity in the temperature range of 300 (∼0.9 W m−1 K−1) to 923 K (∼0.45 W m−1 K−1). Such low thermal conductivity values are most likely a result of the weak chemical bonds (Young’s modulus, E∼76.5 GPa) and the strong anharmonicity of the bonding arrangement (Gruneisen parameter, γ∼1.5). In addition to increasing the power factor, Ca doping reduces the thermal conductivity of the lattice, as confirmed by both experimental results and Callaway model calculations. The combination of optimized power factor and intrinsically low thermal conductivity results in a high ZT of ∼0.9 at 923 K for Bi0.925Ca0.075CuSeO.
Similar content being viewed by others
Introduction
As thermoelectric materials are capable of creating electricity from waste heat, they are relevant to sustainable energy solutions and thus receive a significant amount of scientific attention. The efficiency of thermoelectric devices is determined by a dimensionless figure of merit (ZT), which is defined as ZT=(S2σ/κ)T, where S, σ, κ, and T are the Seebeck coefficient (thermopower), electrical conductivity, thermal conductivity and absolute temperature, respectively.1 Efforts to enhance the ZT involve either increasing the power factor (S2σ) or decreasing the thermal conductivity (κ).2 Examples of these efforts include modifying the band structure by creating electronic resonance states,3 designing quantum confinement effects,4 and using electron energy barrier filtering5 to increase the Seebeck coefficient; synthesizing parent nanocrystalline materials,6 in situ forming nanoscale dots,7 precipitating nano-phases,8 and artificially introducing nano-particles9 to reduce the lattice thermal conductivity. Alternatively, high-performance single-phase thermoelectric materials can be obtained using materials with intrinsically low lattice thermal conductivities. Typical materials included in this class are as follows: AgSbTe2 (κ∼0.39 W m−1 K−1, ZT∼1.6 at 673 K),10, 11 Ag9TlTe5 (κ∼0.22 W m−1 K−1, ZT∼1.2 at 700 K),12 Ag0.95GaTe2 (κ∼0.20 W m−1 K−1, ZT∼0.7 at 850 K),13 Ag3.9Mo9Se11 (κ∼0.75 W m−1 K−1, ZT∼0.6 at 800 K),14 Cu3SbSe4 (κ∼0.50 W m−1 K−1, ZT∼0.8 at 650 K),15 Cu2Ga4Te7 (κ∼0.67W m−1K−1, ZT∼0.6 at 940 K),16 Cu2.1Zn0.9SnSe4 (κ∼0.50 W m−1K−1, ZT∼0.9 at 860 K),17 Cu2Ga0.07Ge0.93Se3 (κ∼0.67 W m−1 K−1, ZT∼0.5 at 745 K),18 CsBi4Te6 (κ∼0.50 W m−1 K−1, ZT∼0.8 at 275 K),19 and K2Bi8Se13 (κ∼0.80 W m−1 K−1, ZT∼0.4 at 400 K).20 Recently, we reported a quaternary BiCuSeO compound that exhibits very low thermal conductivity.21, 22, 23, 24, 25 High ZT values were achieved using this system by optimizing the electrical transport properties. Specifically, electrical conductivity was increased by Sr doping, introducing Cu deficiencies and Ba heavy metal doping.21, 22, 23, 24, 25
Although promising thermoelectric properties have been observed with BiCuSeO compounds,21, 22, 23, 24, 25 surprisingly little is known about their microstructure and the main cause of their low thermal conductivity. In this paper, we perform a systematic evaluation of the BiCuSeO system, including the structural, transport, optical and elastic properties, using a combination of electron microscopy observations and electronic structure calculations. Furthermore, Ca2+ is added as a hole dopant for the Bi3+ sites to improve the electrical transport properties (S2σ) and to reduce the lattice thermal conductivity by introducing point defects. A ZT of ∼0.9 is observed for a Bi0.925Ca0.075CuSeO sample at 923 K. These results indicate that the BiCuSeO system should be investigated further for future applications in medium-temperature thermoelectric devices.
Experimental procedures
Synthesis
Samples with a chemical composition of Bi1-xCaxCuSeO, (x=0, 0.025, 0.05, 0.075, and 0.10) were synthesized using a two-step, solid-state reaction process.21, 22, 23, 24, 25 Stoichiometric mixtures of Bi2O3 (3 N), Bi (4 N), CaO (3 N), Cu (3 N) and Se (5 N) powders were thoroughly ground up by hand and then heated to 973 K for 12 h in a sealed evacuated quartz tube. The total sample mass was maintained at ∼10 g; for example, when x=0.075 Ca, 3.8778 g of Bi2O3, 2.1622 g of Bi, 0.1135 g of CaO, 1.7195 g Cu, and 2.1269 g of Se are used. Next, the powders were reground and then cold-pressed at a pressure of 250 MPa using a Φ 13 mm × 20 mm cylindrical mold. Finally, the cylinders were heated again to 993 K for 24 h in a sealed evacuated quartz tube. All sample preparation processes, including the weighing out of raw materials and grinding of powders, were performed in air.
Electrical properties
The electrical transport properties were examined using bar samples obtained by cutting along the longitudinal direction of the cylindrical samples discussed above. In this manner, 10 × 3 × 2 mm bars were obtained. These bars were used for the simultaneous measurement of the Seebeck coefficient as well as electrical conductivity using an Ulvac Riko ZEM—3 (Ulvac, Yohohama, Japan) instrument under a helium atmosphere in the temperature range of 300–923 K. Heating and cooling cycles generated reproducible electrical properties. In addition, the electrical properties of different slices obtained from the same ingot were similar, indicating that the samples exhibited a significant degree of homogeneity. Hall coefficients were measured using a home-built system with the four-contact Hall-bar geometry. The measurements were performed using both negative and positive polarities to eliminate Joule resistive errors using magnetic fields in the range of 0–1.25 T.
Thermal conductivity
Thermal diffusivity measurements were performed on coins of Ø 8 mm and a thickness of ∼2 mm prepared by cutting along the longitudinal direction of the cylinder. The samples were coated with a thin layer of graphite to minimize errors in determining the emissivity of the material. The thermal conductivity was calculated using the following equation: κ=D × Cp × ρ, where the thermal diffusivity coefficient D was measured using laser flash diffusivity on a Netzsch LFA457 (Netzsch, Selb, Germany) (wherein the heating and cooling cycles produced reproducible diffusivity measurements for a given sample); Cp is the specific heat capacity, which was indirectly derived using a standard sample (Pyroceram 9606) in the range of 300–923 K; and the density ρ of the sample was determined using sample dimension and mass and confirmed using gas pycnometer (Micromeritics Accupyc1340, Norcross, GA, USA) measurements. All measured densities exhibit a value that is ∼90% of the theoretical density, 8.903 g cm−3, for BiCuSeO.
Elastic properties
The longitudinal and transverse acoustic velocities were measured using an ultrasonic instrument (Ultrasonic Pulser/Receiver Model 5900 PR, Panametrics, Waltham, MA, USA). The elastic constants and Poisson ratio were then calculated using the measured velocities.26
Electron microscopy and X-ray diffraction
Transmission electron microscopy (TEM) investigations were performed using a JEOL 2100F (JEOL, Tokyo, Japan) microscope operating at 200 kV. The TEM specimens were prepared by conventional standard methods. The procedures were performed including the cutting, grinding, dimpling, polishing and Ar-ion milling in a liquid nitrogen environment. For powder X-ray diffraction, samples were pulverized with an agate mortar and were then subjected to Cu Kα (λ=1.5418 Å) radiation in the reflection geometry using an Inel diffractometer equipped with a position-sensitive detector and operating at 40 kV and 20 mA.
Electronic structure calculation
CASTEP based on the plane-wave ultrasoft pseudopotential method was used to calculate the total energy.27 In this manner, the local density approximation (LDA) and the generalized gradient approximation (GGA) plus the Hubbard parameter (U) (Coulomb-interaction-corrected LDA and GGA) were calculated. The density-functional theory based on LDA suffers from a well-known gap problem, which is caused by the highly correlated nature of the system that leads to strong effective Coulomb interactions between the electrons. In this manner, the LDA may treat some states incorrectly, such as the d-states in materials containing three-dimensional transition metals, and especially when determining electron energy gap values. However, the plus Hubbard parameter (U) method has been shown to resolve this problem in compounds,28 such as CuO, CuAlO2 and CuAl2O4, where the U is an on-site Coulomb repulsion parameter. The Cu 3d104s1, Se 4s24p4, Bi 6s26p3 and O 2s22p4 electrons are explicitly treated as valence electrons. In these calculations, a plane-wave cutoff energy of 450 eV, 6 × 6 × 3 Monkhorst–Pack k points as well as an energy conversion threshold of 5.0 × 10–6 eV per atom were used.29
Band gap measurement
The reflectance versus wavelength data were used to estimate the band gap by converting the reflectance measurement to an absorption value as described by the Kubelka–Munk equations: α/S=(1−R)2/2R, where R is the reflectance, and α and S are the absorption and scattering coefficients, respectively.
Results and discussion
Structural and thermoelectric properties
The crystal structure of BiCuSeO belongs to the ZrSiCuAs-type structure with the tetragonal P4/nmm space group that constitutes the (Cu2Se2)2− layers alternating with (Bi2O2)2+ layers along the c-axis of the tetragonal cell, as shown in Figure 1a.30, 31 Figure 1b shows the typical samples used in this study, as well as the bar and coin that are used for electrical and thermal transport properties measurements, respectively. These materials were cut along the same longitudinal direction of the cylinder sample in case there is anisotropy in the layered crystal structure of BiCuSeO, even though this material is polycrystalline. Figure 1c shows the powder X-ray diffraction patterns of Bi1-xCaxCuSeO samples. All major Bragg peaks exhibit an excellent match with the simulation results for BiCuSeO (PDF # 82-0464), which can be indexed as a ZrSiCuAs-type structure. Figure 1d shows the diffraction pattern and Rietveld refinement of the Bi0.925Ca0.075CuSeO sample. There is a good fit between the experimental data (black circle) and the calculations (red line), as confirmed by typical R values for all refinements of the Rwp (weighted residual error, black line) factor of ∼6.7%, Rp∼5.9% and RBragg∼2.1%.
The change in lattice parameters as a function of the Ca doping level is shown in Supplementary Figure S1(SI), wherein both a- and c-axes increase slightly with increasing Ca content, which is related to the radius of the Ca2+ ions (0.99 Å) being larger than that of the Bi3+ ions (0.96 Å). The Hall carrier concentrations (nH) at 300 K increase rapidly from 1.1 × 1018 cm−3 for pure BiCuSeO to 8.94 × 1020 cm−3 for the sample with x=0.1 Ca, as shown in Figure 1e. Collectively, the lattice parameter variation and carrier concentration indicate that Ca2+ is successfully incorporated into the BiCuSeO lattice. The electronic absorption of the BiCuSeO sample corresponds to a band gap of ∼0.82 eV, Figure 1f, which shifts to a lower energy value when the Ca doping level fraction is within x=0.05. A further increase in the Ca doping level to x=0.075 and 0.10 results in a structure with no clear band-edge, which indicates that the absorption of metallic conduction electrons decreases the Fermi energy in the valence band due to heavy Ca doping. This result is consistent with the change in the carrier concentrations as a function of Ca doping content in Figure 1e.
Three samples (BiCuSeO, Bi0.975Ca0.025CuSeO and Bi0.925Ca0.075CuSeO) were examined in more detail using TEM. Rod-like grains were mainly observed without any nanoscale precipitates. Figure 2a shows the typical low-magnification TEM image of the BiCuSeO sample. Lamellar structures with an average width of 0.5 μm and length of 4.0 μm are shown in the image. Figure 2b shows an electron diffraction pattern with a selected area aperture of only one grain, which is marked as a circle in Figure 2a and does not show split Bragg spots. The electron diffraction pattern can be easily indexed as the [110] direction of the BiCuSeO sample. The TEM images also reveal a variety of relative orientations, including coherent, semicoherent and incoherent, between the lamellar grains. Different types of grain boundaries will affect electron and phonon scattering differently because of their dissimilar scattering properties.1, 8 Very flat and sharp boundaries can be observed between the lamellar grains in Figure 2c. In the left part of Figure 2c, the [001] directions of the two grains are parallel to the coherent or semicoherent boundary, but they exhibit an ∼70° rotation with the right part of Figure 2c. Figure 2d is an high-resolution TEM image of the Bi0.975Ca0.025CuSeO sample along the [001] direction. No nanoscale precipitates were observed along this direction as well. The relative electron diffraction pattern (inset) shows no split spots along the [001] axis, instead revealing two sub-lattices (CuSe and doped BiO) that are commensurate rather than incommensurate. These data suggest that BiCuSeO is not a misfit compound. Figure 3a is a typical lattice image of a grain boundary, which shows a sharp and bright interface. The upper grain image is obtained along the [100] direction, although the direction of the bottom grain is along the [110] direction. Figure 3b is the atomic model based on the high-resolution TEM image in Figure 3a, which clearly shows the mismatch and misfit dislocation at the interface, while it may be hard to see the mismatch in the real image. Fast Fourier transforms of images in Figures 3a and b are provided in Figures 3c and d, respectively. The fast Fourier transform images reveal similar spot distributions to those of the parent images. However, a careful comparison shows split spots along the c direction only in Figure 3c, but not in Figure 3d, which indicates that the strain is partially relaxed in these two grains.1, 8
The electronic band structure of BiCuSeO can be determined using the LDA+U (U=9.0 eV) along the high symmetry directions in the Brillouin zone, as shown in Figure 4a. The conduction band minimum is at point Z, and the valence band maximum is on the M–Γ line. The effective mass of BiCuSeO is obtained by fitting the actual E−k diagram around the conduction band minimum and the valence band maximum, and the effective mass m* is defined as1, 2:
where ħ is the reduced Planck constant. The calculated effective mass of the valence bands is ∼0.54 mo for BiCuSeO by LDA+U. The GGA+U (generalized gradient approximation+Hubbard parameter) calculation indicates an indirect band gap of 0.66 eV for BiCuSeO, which can be comparable to the measured value of 0.82 eV for BiCuSeO (Supplementary Figure S1). Figure 4b shows the total and partial density of states for BiCuSeO. The valence bands consist of three parts: the first is located at lower energies, which is mainly the O-2 s states. The middle valence bands are dominated by Se-4s and Bi-6s states. The strong contributions to the upper valence bands are coming from the O-2p, Cu-3d and Se-4p states. The conduction bands edge is described by Bi-6p states.
Figure 5 shows the thermoelectric properties as a function of temperature for Bi1-xCaxCuSeO samples. As shown in Figure 5a, BiCuSeO exhibits low electrical conductivity over the entire temperature range and a semiconducting electrical transport behavior. After doping with Ca, the electrical transport changes to a metallic-like behavior and the electrical conductivity shows a significant increase with increasing Ca fraction, from ∼1.12 S cm−1 (BiCuSeO) to ∼270 S cm−1 (Bi0.90Ca0.10CuSeO) at 300 K. The electrical conductivity of Bi0.90Ca0.10CuSeO is higher than that of BiCu0.975SeO22 and is comparable to that of Bi0.90Sr0.10CuSeO.21 This result indicates that Ca doping can effectively enhance the electrical conductivity of BiCuSeO by introducing holes in the valence band. Similar to the LaFeAsO superconductors,32, 33 the BiCuSeO compounds consist of (Cu2Se2)2− conducting layers separated by insulating (Bi2O2)2+, which act as charge reservoirs. Therefore, the enhanced electrical conductivity of Bi1-xCaxCuSeO can be explained by the carriers introduced to the (Cu2Se2)2− layers in response to the negative charges in the insulating (Bi2O2)2+ layers through partial substitution of Bi3+ by Ca2+.21 The substitution of Ca2+ for Bi3+ leads to a transfer of holes (h+) from the charge reservoir (Bi2O2)2+ layers to the conducting (Cu2Se2)2− layers in the following manner:
where h+ is the produced holes introduced by Ca doping. If we assume that each Ca promotes one hole h+ to the valence band, when x=0.1 Ca, there are 0.2 holes per unit cell (2 BiCuSeO units per unit cell). The volume of the unit cell is approximately 138 Å3 (from X-ray diffraction), which should lead to a carrier concentration of ∼1.45 × 1021 cm−3. Indeed, the obtained carrier concentration of 8.94 × 1020 cm−3 is observed for the sample with x=0.1 Ca doping, which indicates that the small amount of Ca is not introduced into the structure or that the carrier concentration difference comes from the starting powers purity, experimental measurement error and composition homogeneity, among other effects.
Doping with Ca also produces a significant effect on the Seebeck coefficient of BiCuSeO system, as shown in Figure 5b. A positive Seebeck coefficient indicates p-type electrical transport behavior. The Seebeck coefficients for BiCuSeO are large, for example, +330 μV K−1 at 300 K and +410 μV K−1 at 923 K, and decrease with increasing Ca doping fractions but still remain high over the entire temperature range of +120 μV K−1 at 300 K to +198 μV K−1 at 923 K for the Bi0.90Ca0.10CuSeO sample. The increase in the Seebeck coefficient may be related to the layered crystal structure wherein insulating (Bi2O2)2+ and conductive (Cu2Se2)2− layers alternate forming a natural superlattice with a two-dimensional confinement of charge carriers. The natural layered structure of (Bi2O2)2+/(Cu2Se2)2−/(Bi2O2)2+ is very similar to the two-dimensional electron gas structure of SrTiO3/SrTi0.8Nb0.2O3/SrTiO3, containing artificial insulating/conductive/insulating layers, which exhibits a high Seebeck coefficient.34 The calculation of the electronic density of states for BiCuSeO indicates a large Seebeck coefficient resulting from a large effective mass (m*). To further verify this assumption, the effective mass (m*) was also calculated according to the following equations using the observed carrier concentration (n) and Seebeck coefficient (S) values35:
where Fn(η) is the n-th order Fermi integral, kB is the Boltzmann constant, e is the electron charge, h is the Planck constant and r is the scattering factor. Usually, this calculation is assumed based on a single parabolic band with three-dimensional transport character. In this study, BiCuSeO polycrystalline samples were examined at a random grain orientation because it is difficult to extract the directional dependence of the physical properties for a polycrystalline sample. Therefore, all values provided in this paper are averaged estimates. The scattering factor (r) is −1/2 as the acoustic phonon scattering is independent of the grain size and is generally assumed to be the main scattering mechanism at room temperature.8, 36 The reduced Fermi energy η was determined based on the fitting of respective Seebeck values (the details are provided in the SI). The calculation provides an effective mass (m*) of ∼0.60 mo, which is consistent with 0.54 mo determined by density of state calculations and higher than that of PbTe (0.24 mo)37 and PbS (0.40 mo)8 with a rock salt structure. The combined electrical conductivity and positive temperature-dependent Seebeck coefficient result in a power factor (S2σ) peak at a high temperature of 923 K. As shown in Figure 5c, the highest power factor is ∼4.74 μW cm−1 K−2 for the Bi0.925Ca0.075CuSeO sample at 923 K, which is higher than ∼4.10 μW cm−1 K−2 at 923 K for the BiCu0.975SeO sample.22
Figure 5d shows the total thermal conductivity as a function of temperature for Bi1-xCaxCuSeO samples. The total thermal conductivity of undoped BiCuSeO decreases with increasing temperature from 0.89 W m−1 K−1 at 300 K to 0.45 W m−1 K−1 at 923 K (heat capacity (Supplementary Figure S2) and thermal diffusivity (Supplementary Figure S3)). This total thermal conductivity is very low and comparable to other high-performance thermoelectric materials,1, 2, 3 even lower than that of nanostructured Bi–Sb–Te.6 The total thermal conductivity increases with increasing Ca content but still maintains low over the entire measuring temperature range, for example, 1.05 W m−1 K−1 at 300 K and 0.52 W m−1K−1 at 923 K for the Bi0.90Ca0.10CuSeO sample. Generally, the lattice thermal conductivity κlat can be estimated by directly subtracting the electronic thermal conductivity κele from the total thermal conductivity κtot. The electronic part κele is proportional to the electrical conductivity σ through the Wiedemann–Franz relation, κele=LσT, where L is the Lorenz number obtained from fitting the respective Seebeck coefficient values with an estimate of the reduced chemical potential (η),38, 39 as shown in Supplementary Figure S4 (Lorenz number calculation details can be found in the SI; the electronic thermal conductivity κele is shown in Supplementary Figure S5). Figure 4e shows the lattice thermal conductivity as a function of temperature for Bi1-xCaxCuSeO samples. BiCuSeO shows a very low lattice thermal conductivity of 0.88 W m−1 K−1 at 300 K and 0.43 W m−1 K−1 at 923 K, which is much lower than those of PbTe-based thermoelectrics.3, 7, 8, 36 The possible origin of the intrinsically low thermal conductivity of BiCuSeO will be discussed later in this paper. As the thermal conductivity values are very low, it is worth comparing them with the calculated minimum lattice thermal conductivity κlat,min for BiCuSeO to assess if there is still room for improvement. The lattice thermal conductivity κlat can be estimated by the following relationship11, 14, 18:
where the Cv is the molar specific heat at constant volume, l is the mean free path of phonons, and va is the average sound velocity, which is defined as follows12, 40:
va is determined using the longitudinal (vl) and transverse (vs) sound velocities provided in Table 1. The minimal lattice thermal conductivity κlat has been estimated by the minimum l to be the interatomic distance11, 14, 18 of ∼3.0 Å for the BiCuSeO system. Using equation (6), κlat,min of 0.47 W m−1K−1 is obtained at 300 K, it is much lower than the value of 0.88 Wm−1K−1 obtained in this study, suggesting a possibility for further reduction of κlat in BiCuSeO.
The lattice thermal conductivity κlat is presumably reduced by point defect scattering through Ca doping. Indeed, a clear trend can be readily observed where the lattice thermal conductivity κlat decreases with increasing Ca content. Namely, the lattice thermal conductivity κlat at 300 K decreases from 0.88 W m−1 K−1 for the undoped BiCuSeO to 0.75 W m−1 K−1 for the Bi0.90Ca0.10CuSeO sample. To understand the role of point defects in reducing the κlat of Bi1-xCaxCuSeO, we performed theoretical calculations based on the Callaway model,40, 41 wherein point defect scattering in a solid solution system originates from both mass difference (mass fluctuations) as well as differences in size and interatomic coupling forces (strain field fluctuations) between the impurity atom and the host lattice. Herein, we present a phonon scattering model based on the Callaway model40, 41 and try to describe the effect of Ca doping on the lattice thermal conductivity κlat.
At temperatures above the Debye temperature, the ratio of the lattice thermal conductivities of a material containing point defects with that of the parent material can be written in the following manner:40, 41
where κlat and κlat,p are the lattice thermal conductivities of the doped and parent materials, respectively, and the parameter u is defined as follows:40, 41
where h, Ω, va and θD are the Planck constant, the average volume per atom, the average sound velocity, and the Debye temperature, respectively. The imperfection scaling parameter Γ in equation (9) represents the strength of point defects phonon scattering, which includes two components: the scattering parameter due to mass fluctuations ΓM and the scattering parameter due to strain field fluctuations ΓS. A phenomenological adjustable parameter ɛ is always included; because of the uncertainty of ΓS, one writes Γ=ΓM+ɛΓS. The calculation of point defect scattering based on the Callaway model (calculation details can be found in the SI), exhibits excellent agreement between the calculated and measured values, as shown in the inset of Figure 5e. Thus, the reduction in the lattice thermal conductivity by Ca doping is confirmed by both experimental results and theoretical calculations.
Using the electrical and thermal transport properties, the dimensionless figure of merit (ZT) is calculated as shown in Figure 5f. The ZT shows an increasing trend with temperature, and a maximum ZT value of 0.9 is achieved at 923 K for the Bi0.925Ca0.075CuSeO sample, which is higher than that of 0.8 at 923 K for BiCu0.975SeO.22 The ZT value of Bi0.925Ca0.075CuSeO at 873 K is also higher than that of 0.7 for Bi0.90Sr0.10CuSeO at 873 K.21 The present ZT of 0.9 is higher than most thermoelectric materials with intrinsically low thermal conductivity reported so far.13, 14, 15, 16, 17, 18, 19, 20 Therefore, it can be concluded that the higher thermoelectric performance of BiCuSeO is mainly due to the intrinsically low thermal conductivity of the material.
Origin of the low thermal conductivity
Our results suggest that the electrical transport properties of the BiCuSeO system are actually significantly lower than those of other thermoelectrics, for example, Bi2Te3-based,6, 9, 36 PbTe-based,3, 7, 8 skutterudites,42 and metallic-based layered misfit sulfides.43 Thus, the high thermoelectric performance of the BiCuSeO system is mainly due to the intrinsically low thermal conductivity. To clarify the origin of the intrinsically low thermal conductivity, the elastic properties of BiCuSeO compounds were analyzed. Young’s modulus (E) value of BiCuSeO was extracted from the longitudinal (vl) and transverse (vs) sound velocities.23 Young's modulus is related to the stiffness of a material's individual atomic bonds.12, 36 Weaker interatomic bonding generally results in lower stiffness and a lower Young's modulus. The materials with a low Young's modulus are considered to have ‘soft’ bonding, which will result in a slow transport of phonons, and thus a lower lattice thermal conductivity.44 Indeed, BiCuSeO exhibits a lower sound velocity,23 Young’s modulus and lattice thermal conductivity at 300 K than other oxides,40, 45 namely, BiCuSeO (2107 ms−1, 76.5 GPa, 0.9 W m−1 K−1) are lower than those of Ba2YbAlO5 (2901 m s−1, 109.4 GPa, 1.4 W m−1 K−1), those of Ba2DyAlO5 (3078 m s−1, 116.5 GPa, 1.8 W m−1 K−1) and those of Gd2Zr2O7 (3832 m s−1, 234.3 GPa, 2.2 W m−1 K−1).
In addition to the analysis of Young’s modulus (E), which is related to the chemical bonding strength, the Gruneisen parameter (γ) is also relevant in evaluating the intrinsically low thermal conductivity.11, 18 The Gruneisen parameter (γ) is often referred to as a temperature-dependent anharmonicity parameter that reflects how much phonon vibrations in a crystal lattice deviate from harmonic oscillations. Anharmonicity of the chemical bond drives the phonon–phonon umklapp and normal processes that limit the lattice thermal conductivity.46 In this paper, the Gruneisen parameter (γ) of BiCuSeO has been calculated using the following relationship:47
where the Poisson ratio (υp) can be derived from the longitudinal (vl) and transverse (vs) sound velocities using the following relationship40, 47:
The Gruneisen parameter (γ) was calculated to be ∼1.5 for BiCuSeO, which is a fairly large value for a compound with the potential to be a low thermal conductivity material, indicating a high degree of anharmonicity in the crystal lattices of the BiCuSeO system. This value is comparable to or even a bit higher than that (1.45) of PbTe.44 The large Gruneisen parameter (γ) value of PbTe likely results from octahedral atomic coordination in the rock salt crystal structure and a high coordination number. The associated high anharmonicity results from a rather low value of κlat.46, 48 This behavior was recently explained in terms of local structural distortions in PbTe, which is close to its ferroelectric phase transition, leading to bonding anharmonicity.49
A large Gruneisen parameter (γ) leads to a lower thermal conductivity, along with a larger Seebeck coefficient, resulting in improved performance of PbTe in comparison with other thermoelectrics.1, 2 Morelli et al.11 reported that the intrinsically low thermal conductivity of AgSbTe2 results from an extremely high Gruneisen parameter (γ) value of 2.05. The high Gruneisen parameter (γ), linked to the anharmonicity, may originate from the presence of non-bonding valence electrons in the sp-hybridized bonding orbital.11, 15 These non-bonding electrons, originating from the valence shell of Sb, give rise to electron clouds surrounding the Sb atoms that cause nonlinear repulsive forces, which is manifested as an anharmonicity.11, 15 As it is in the same group as V, Bi exhibits a larger atom radius than that of Sb, making its valence shell and the electron clouds surrounding the Bi atoms larger than those of Sb,11, 15, 46 Similarly low lattice thermal conductivity should be observed in the Bi-based compounds,50 in which the Bi ion formally adopts a trivalent state as in the case of Sb in AgSbTe2. The connection between the nature of the bonding and the Grüneisen parameter (γ) has been explored in detail theoretically by Huang et al.,51 who clearly show the effect of large electron clouds on anharmonicity. In addition, the lone pair of electrons on Bi possibly lead to more asymmetric electron density and a stronger lattice vibration energy.52 We speculate that the very low thermal conductivity and high Gruneisen parameter (γ) of 1.5 in the BiCuSeO system are due in part to the increased bond anharmonicity associated with the presence of trivalent Bi.50
In addition to the Young’s modulus and Gruneisen parameter (γ) for the BiCuSeO system, other possible reasons include the layered structure, as the phonons can be confined to scattered layer interfaces,53 and the presence of heavy elements,1, 2 among others. All of these features can be summarized as involving heavy atoms with ‘soft’ bonding, which meet the requirements for a low thermal conductivity selection, as suggested by Clarke.54
Concluding remarks
High-performance thermoelectric devices based on the BiCuSeO system were achieved due to an intrinsically low thermal conductivity of the materials, which was further reduced by Ca doping. The elastic properties indicate that the intrinsically low thermal conductivity is most likely a result of the weak chemical bonding between the two different layers and the strong anharmonicity of the bonding arrangement in the BiCuSeO crystal structure. The figure of merit, ZT, increased significantly from 0.53 for pure BiCuSeO to 0.9 for Bi0.925Ca0.075CuSeO at 923 K, which is higher than that of most thermoelectric materials with intrinsically low thermal conductivity reported thus far.13, 14, 15, 16, 17, 18, 19, 20 These results suggest that the BiCuSeO system is a robust candidate for medium-temperature thermoelectric applications. Further improvement in the ZT may be achieved by increasing the electrical conductivity via heavy hole doping either using conductive (Cu2Se2)2− layers or insulating (Bi2O2)2+ layers and/or by improving the carrier mobility.
References
Kanatzidis, M. G. Nanostructured thermoelectrics: the new paradigm? Chem. Mater. 22, 648–659 (2010).
Li, J. F., Liu, W. S., Zhao, L. D. & Zhou, M. High-performance nanostructured thermoelectric materials. NPG Asia Mat. 2, 152–158 (2010).
Heremans, J. P., Jovovic, V., Toberer, E. S., Saramat, A., Kurosaki, K., Charoenphakdee, A., Yamanaka, S. & Snyder, G. J. Enhancement of thermoelectric efficiency in PbTe by distortion of the electronic density of states. Science 321, 554–557 (2008).
Harman, T. C., Taylor, P. J., Walsh, M. P. & LaForge, B. E. Quantum dot superlattice thermoelectric materials and devices. Science 297, 2229–2232 (2002).
Heremans, J. P., Thrush, C. M. & Morelli, D. T. Thermopower enhancement in lead telluride nanostructures. Phys. Rev. B 70, 115334 (2004).
Poudel, B., Hao, Q., Ma, Y., Lan, Y., Minnich, A., Yu, B., Yan, X., Wang, D., Muto, A., Vashaee, D., Chen, X., Liu, J., Dresselhaus, M. S., Chen, G. & Ren, Z. F. High-thermoelectric performance of nanostructured bismuth antimony telluride bulk alloys. Science 320, 634–638 (2008).
Hsu, K. F., Loo, S., Guo, F., Chen, W., Dyck, J. S., Uher, C., Hogan, T., Polychroniadis, E. K. & Kanatzidis, M. G. Cubic AgPbmSbTe2+m: bulk thermoelectric materials with high figure of merit. Science 303, 818–821 (2004).
Zhao, L. D., Lo, S., He, J., Li, H., Biswas, K., Androulakis, J., Wu, C. I., Hogan, T. P., Chung, D. Y., Dravid, V. P. & Kanatzidis, M. G. High performance thermoelectrics from earth-abundant materials: enhanced figure of merit in PbS by second phase nanostructures. J. Am. Chem. Soc. 133, 20476–20487 (2011).
Zhao, L. D., Zhang, B. P., Li, J. F., Zhou, M., Liu, W.-S. & Liu, J. Thermoelectric and mechanical properties of nano-SiC-dispersed Bi2Te3 fabricated by mechanical alloying and spark plasma sintering. J. Alloys Compd 455, 259–264 (2008).
Wang, H., Li, J. F., Zou, M. M. & Sui, T. Synthesis and transport property of AgSbTe2 as a promising thermoelectric compound. Appl. Phys. Lett. 93, 202106 (2008).
Morelli, D. T., Jovovic, V. & Heremans, J. P. Intrinsically minimal thermal conductivity in cubic I-V-VI2 semiconductors. Phys. Rev. Lett. 101, 035901 (2008).
Kurosaki, K., Kosuga, A., Muta, H., Uno, M. & Yamanaka, S. Ag9TITe5: a high-performance thermoelectric bulk material with extremely low thermal conductivity. Appl. Phys. Lett. 87, 061919 (2005).
Yusufu, A., Kurosaki, K., Kosuga, A., Sugahara, T., Ohishi, Y., Muta, H. & Yamanaka, S. Thermoelectric properties of Ag1-xGaTe2 with chalcopyrite structure. Appl. Phys. Lett. 99, 061902 (2011).
Zhou, T., Lenoir, B., Colin, M., Dauscher, A., Orabi, R. A. R. A., Gougeon, P., Potel, M. & Guilmeau, E. Promising thermoelectric properties in AgxMo9Se11 compounds (3.4 <= x<=3.9). Appl. Phys. Lett. 98, 162106 (2011).
Skoug, E. J., Cain, J. D. & Morelli, D. T. High thermoelectric figure of merit in the Cu3SbSe4-Cu3SbS4 solid solution. Appl. Phys. Lett. 98, 261911 (2011).
Plirdpring, T., Kurosaki, K., Kosuga, A., Ishimaru, M., Harnwunggmoung, A., Sugahara, T., Ohishi, Y., Muta, H. & Yamanaka, S. High-temperature thermoelectric properties of Cu2Ga4Te7 with defect zinc-blende structure. Appl. Phys. Lett. 98, 172104 (2011).
Liu, M. L., Chen, I. W., Huang, F. Q. & Chen, L. D. Improved thermoelectric properties of Cu-doped quaternary chalcogenides of Cu2CdSnSe4. Adv. Mater. 21, 3808–3812 (2009).
Cho, J. Y., Shi, X., Salvador, J. R., Meisner, G. P., Yang, J., Wang, H., Wereszczak, A. A., Zhou, X. & Uher, C. Thermoelectric properties and investigations of low thermal conductivity in Ga-doped Cu2GeSe3. Phys. Rev. B 84, 085207 (2011).
Chung, D. Y., Hogan, T., Brazis, P., Rocci-Lane, M., Kannewurf, C., Bastea, M., Uher, C. & Kanatzidis, M. G. CsBi4Te6: a high performance thermoelectric material for low temperature applications. Science 287, 1024–1027 (2000).
Chung, D. Y., Choi, K. S., Iordanidis, L., Schindler, J. L., Brazis, P. W., Kannewurf, C. R., Chen, B., Hu, S., Uher, C. & Kanatzidis, M. G. High thermopower and low thermal conductivity in semiconducting ternary K-Bi-Se compounds. Synthesis and properties of b-K2Bi8Se13 and K2.5Bi8.5Se14 and their Sb analogs. Chem. Mater. 9, 3060–3071 (1997).
Zhao, L. D., Berardan, D., Pei, Y. L., Byl, C., Pinsard-Gaudart, L. & Dragoe, N. Bi1-xSrxCuSeO oxyselenides as promising thermoelectric materials. Appl. Phys. Lett. 97, 092118 (2010).
Liu, Y., Zhao, L. D., Liu, Y. C., Lan, J. L., Xu, W., Li, F., Zhang, B. P., Berardan, D., Dragoe, N., Lin, Y. H., Nan, C. W., Li, J. F. & Zhu, H. M. Remarkable enhancement in thermoelectric performance of BiCuSeO by Cu deficiencies. J. Am. Chem. Soc. 133, 20112–20115 (2011).
Li, F., Li, J. F., Zhao, L. D., Xiang, K., Liu, Y., Zhang, B. P., Lin, Y. H., Nan, C. W. & Zhu, H. M. Polycrystalline BiCuSeO oxide as a potential thermoelectric material. Energy Environ. Sci. 5, 7188–7195 (2012).
Li, J., Sui, J. H., Pei, Y. L., Barreteau, C., Berardan, D., Dragoe, N., He, J. Q. & Zhao, L. D. A high thermoelectric figure of merit ZT>1 in Ba heavily doped BiCuSeO oxyselenides. Energy Environ. Sci. 5, 8543–8547 (2012).
Barreteau, C., Berardan, D., Amzallag, E., Zhao, L. D. & Dragoe, N. Structural and electronic transport properties in Sr-doped BiCuSeO. Chem. Mater. 24, 3168–3178 (2012).
Asmani, M., Kermel, C., Leriche, A. & Ourak, M. Influence of porosity on Young's modulus and Poisson's ratio in alumina ceramics. J. Eur. Ceram. Soc. 21, 1081–1086 (2001).
Clark, S. J., Segall, M. D., Pickard, C. J., Hasnip, P. J., Probert, M. J., Refson, K. & Payne, M. C. First principles methods using CASTEP. Z. Kristallogr. 220, 567–570 (2005).
Liu, Q. J. & Liu, Z. T. First-principles generalized gradient approximation plus U study of cubic CuAl2O4. Appl. Phys. Lett. 99, 091902 (2011).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Hiramatsu, H., Yanagi, H., Kamiya, T., Ueda, K., Hirano, M. & Hosono, H. Crystal structures, optoelectronic properties, and electronic structures of layered oxychalcogenides MCuOCh (M=Bi, La; Ch=S, Se, Te): Effects of electronic configurations of M3+ ions. Chem. Mater. 20, 326–328 (2008).
Stampler, E. S., Sheets, W. C., Bertoni, M. I., Prellier, W., Mason, T. O. & Poeppelmeier, K. R. Temperature driven reactant solubilization synthesis of BiCuOSe. Inorg. Chem. 47, 10009–10016 (2008).
Quebe, P., Terbuchte, L. J. & Jeitschko, W. Quaternary rare earth transition metal arsenide oxides RTAsO (T=Fe, Ru, Co) with ZrCuSiAs type structure. J. Alloys Compd. 302, 70–74 (2000).
Kamihara, Y., Watanabe, T., Hirano, M. & Hosono, H. Iron-based layered superconductor La[O1-xFx]FeAs (x=0.05–0.12) with Tc=26 K. J. Am. Chem. Soc. 130, 3296–3297 (2008).
Ohta, H., Kim, S., Mune, Y., Mizoguchi, T., Nomura, K., Ohta, S., Nomura, T., Nakanishi, Y., Ikuhara, Y., Hirano, M., Hosono, H. & Koumoto, K. Giant thermoelectric Seebeck coefficient of two-dimensional electron gas in SrTiO3. Nature Mater. 6, 129–134 (2007).
Yamamoto, M., Ohta, H. & Koumoto, K. Thermoelectric phase diagram in a CaTiO3-SrTiO3-BaTiO3 system. Appl. Phys. Lett. 90, 072101 (2007).
Zhao, L. D., Zhang, B. P., Liu, W. S. & Li, J. F. Effect of mixed grain sizes on thermoelectric performance of Bi2Te3 compound. J. Appl. Phys. 105, 023704 (2009).
Ravich, I. I., Efimova, B. A. & Smirnov, I. A. Semiconducting Lead Chalcogenides, Plenum: New York, NY, USA, (1970).
Fitsul, I. V. Heavily Doped Semiconductors, Plenum: New York, NY, USA, (1969).
Kumar, G. S., Prasad, G. & Pohl, R. O. Experimental determinations of the Lorenz number. J. Mater. Sci. 8, 4261–4272 (1993).
Wan, C. L., Pan, W., Xu, Q., Qin, Y. X., Wang, J. D., Qu, Z. X. & Fang, M. H. Effect of point defects on the thermal transport properties of (LaxGd1-x)2Zr2O7: experiment and theoretical model. Phys. Rev. B 74, 144109 (2006).
Callayway, J. & von Baeyer, H. C. Effect of point imperfections on lattice thermal conductivity. Phys. Rev. 120, 1149–1154 (1960).
Liu, W. S., Zhang, B. P., Li, J. F., Zhang, H. L. & Zhao, L. D. Enhanced thermoelectric properties in CoSb3-xTex alloys prepared by mechanical alloying and spark plasma sintering. J. Appl. Phys. 102, 103717 (2007).
Koumoto, K., Funahashi, R., Guilmeau, E., Miyazaki, Y., Weidenkaff, A., Wang, Y. & Wan, C. Thermoelectric ceramics for energy harvesting. J. Am. Ceram. Soc. 96, 1–23 (2013).
Roufosse, M. C. & Klemens, P. G. Thermal conductivity of complex dielectric crystals. Phys. Rev. B 7, 5379–5386 (1973).
Wan, C. L., Qu, Z. X., He, Y., Luan, D. & Pan, W. Ultralow thermal conductivity in highly anion-defective aluminates. Phys. Rev. Lett. 101, 085901 (2008).
Ioffe, A. F. Physics of Semiconductors, Infosearch: London, UK, (1958).
Sanditov, D. S. & Belomestnykh, V. N. Relation between the parameters of the elasticity theory and averaged bulk modulus of solids. Tech. Phys. 56, 1619–1623 (2011).
Morelli, D. T. & Slack, G. A. In: High Thermal Conductivity Materials (eds. Shinde, S. Goela, J.) Ch. 2, 37–64 Springer: New York, NY, USA, (2005).
Bozin, E. S., Malliakas, C. D., Souvatzis, P., Proffen, T., Spaldin, N. A., Kanatzidis, M. G. & Billinge, S. J. L. Entropically stabilized local dipole formation in lead chalcogenides. Science 330, 1660–1663 (2010).
Skoug, E. J., Cain, J. D. & Morelli, D. T. Structural effects on the lattice thermal conductivity of ternary antimony- and bismuth-containing chalcogenide semiconductors. Appl. Phys. Lett. 96, 181905 (2010).
Huang, B. L. & Kaviany, M. Structural metrics of high-temperature lattice conductivity. J. Appl. Phys. 100, 123507 (2006).
Payne, D. J., Egdell, R. G., Walsh, A., Watson, G. W., Guo, J., Glans, P. A., Learmonth, T. & Smith, K. E. Electronic origins of structural distortions in post-transition metal oxides: experimental and theoretical evidence for a revision of the lone pair model. Phys. Rev. Lett. 96, 157403 (2006).
Venkatasubramanian, R., Siivola, E., Colpitts, T. & O’Quinn, B. Thin-film thermoelectric devices with high room-temperature figures of merit. Nature 413, 597–602 (2001).
Clarke, D. R. Materials selection guidelines for low thermal conductivity thermal barrier coatings. Surf. Coat. Technol. 163, 67–74 (2003).
Acknowledgements
The authors (L-D Zhao and JQ He) are grateful to Professor Mercouri G Kanatzidis for helpful discussions and thermoelectric measurements performed in his group. This work is supported by the National Natural Science Foundation of China (No. 51202008) (YL Pei) and 973 program of China (No. 2013CB632503) (J-F Li). J He would like to thank the funding of a start-up research project from Xi’an Jiaotong University. The TEM work was performed at the (EPIC) (NIFTI) (Keck-II) facility of the NUANCE Center at Northwestern University. The NUANCE Center is supported by NSF-NSEC, NSF-MRSEC, Keck Foundation, the State of Illinois, and Northwestern University.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Supplementary Information accompanies the paper on the NPG Asia Materials website
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/3.0/
About this article
Cite this article
Pei, YL., He, J., Li, JF. et al. High thermoelectric performance of oxyselenides: intrinsically low thermal conductivity of Ca-doped BiCuSeO. NPG Asia Mater 5, e47 (2013). https://doi.org/10.1038/am.2013.15
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/am.2013.15
Keywords
This article is cited by
-
Role of sintering temperature in modulating the charge transport of BiCuSeO thermoelectric system: correlations to the microstructure
Applied Physics A (2024)
-
Local symmetry distortion induced anomalous thermal conduction in thermoelectric layered oxyselenides
npj Computational Materials (2023)
-
Simultaneous optimization of phononic and electronic transport in two-dimensional Bi2O2Se by defect engineering
Science China Information Sciences (2023)
-
Realizing high thermoelectric performance via selective resonant doping in oxyselenide BiCuSeO
Nano Research (2023)
-
Phase stability, mechanical properties and thermal conductivity of technetium diborides in different crystal structures
Applied Physics A (2023)